Patent Application
20090239058
Embodiments described herein generally relate to erosion systems and components having improved erosion resistance. More particularly, embodiments herein generally describe erosions systems for use on components that can provide from about a 50% increase to about a 400% increase in erosion resistance to the underlying component per layer of the erosion system.
In gas turbine engines, such as aircraft engines, air is drawn into the front of the engine, compressed by a shaft-mounted compressor, and mixed with fuel in a combustor. The mixture is then burned and the hot exhaust gases are passed through a turbine mounted on the same shaft. The flow of combustion gas expands through the turbine, which in turn spins the shaft and provides power to the compressor. The hot exhaust gases are further expanded through nozzles at the back of the engine, generating powerful thrust, which drives the aircraft forward.
In recent years composite materials have become increasingly popular for use in a variety of aerospace applications because of their durability and relative lightweight. Because engines operate in a variety of conditions, engine components often come into contact with foreign objects, such as hailstones, ice, sand, and dirt. Over time, contact with such foreign objects can damage and erode the surface of the composite engine components.
To help protect the composite components from exposure to such harsh environments, the surface of the component is often coated with external, secondarily applied materials. By “secondarily applied” it is meant that the composite component is cured prior to the application of the coating. These secondarily applied materials may include polymer coatings that are sprayed, painted, or otherwise bonded to the composite component. Other secondarily applied materials may include metal foils or sheets that are preformed and bonded to the composite component. In general, this approach can require considerable labor and expense for preparation and processing, typically requiring sanding and/or priming of the cured composite component prior to the application of the coating.
In addition, to ensure that the finished component satisfies dimensional constraints, each component must be inspected after the protective coating is applied. For example, non-destructive evaluation techniques, such as the use of a coordinate-measuring machine, a hand gauge, or ultrasonic inspection, can be used to determine if defects are present. If it is determined that there is significant coating thickness variation, which there often is, the coating must be stripped and reapplied. Even if the dimensions are found to be accurate, additional labor is often needed to ensure the desired bond integrity and surface finish are achieved.
When it is discovered that a coated surface needs to be repaired, the depth of the eroded portion can be measured to determine the extent of the wear. If the depth of erosion is small, the surface may be locally sanded, prepped, and recoated by spraying or painting a new coating onto the eroded surface. If the depth of erosion is large, entire sections of the composite component may be removed and replaced with patches of material attached using epoxy or other suitable matrix material.
Accordingly, there remains a need for erosion systems for components exposed to harsh environments that can be produced using less labor, improve erosion protection, extend performance life, and improve the ease of inspection.
Embodiments herein generally relate to erosions systems comprising a toughened resin for improving erosion resistance, the toughened resin including a resin and a toughening agent, and a support for retaining the toughened resin wherein at least one layer of the erosion system is applied to a component to provide from about a 50% increase to about a 400% increase in erosion resistance to the component per layer of the erosion system.
Embodiments herein also generally relate to components comprising an erosion system including a toughened resin for improving erosion resistance, the toughened resin including a resin and a toughening agent, and a support for retaining the toughened resin wherein at least one layer of the erosion system is applied to the component to provide from about a 50% increase to about a 400% increase in erosion resistance to the component per layer of the erosion system.
Embodiments herein also generally relate to gas turbine engine components comprising a plurality of layers of an erosion system, each layer of the erosion system including a toughened resin for improving erosion resistance, the toughened resin including a resin and a toughening agent and a support for retaining the toughened resin and for providing a color to the erosion system wherein each layer of the erosion system comprises a different color and provides from about a 50% increase to about a 400% increase in erosion resistance to the gas turbine component per layer of the erosion system.
These and other features, aspects and advantages will become evident to those skilled in the art from the following disclosure.
While the specification concludes with claims particularly pointing out and distinctly claiming the invention, it is believed that the embodiments set forth herein will be better understood from the following description in conjunction with the accompanying figures, in which like reference numerals identify like elements.
Embodiments described herein generally relate to erosion systems and components having improved erosion resistance. The erosion systems, components comprising the same, and methods for making the same described herein may generally include a component and at least one layer of an erosion coating system. Also described are improved methods of inspection for articles comprising the erosion coating system.
Referring to
For example, in one embodiment, component 10 may comprise a composite made from a material including organic or non-organic fibers, and a resin matrix. More particularly, as used herein, “material” can refer to any woven, braided, or non-crimp fabric or fibers capable of being treated and cured with a resin to produce a composite. In one embodiment, the material may comprise carbon fibers, graphite fibers, glass fibers, ceramic fibers, aramid polymer fibers (e.g. Kevlar®), and combinations thereof. As shown in
Component 10 may take any shape desired to carry out its intended purpose. By way of example, some acceptable turbine engine components suitable for use herein may include, but should not be limited to, vanes, blades, struts, ducts, spacers, and the like. Those skilled in the art will understand that although the examples provided herein relate to turbine engines, “component” may be used to refer to any part matching the previous description.
As shown in
Erosion system 16 can utilize a resin 22 to serve as a composite matrix. Resin 22 can comprise any conventional liquid resin known to those skilled in the art, such as, but not limited to, epoxy resin, bismaleimide resin, or polyimide resin. A toughening agent 24 can then be added to resin 22 to produce toughened resin 18 that can provide erosion resistance upon curing. Some examples of toughening agents 24 can include, but should not be limited to, fibers, nano fibers, nano particulates, and combinations thereof. Some examples of possible fibers can include carbon fibers, graphite fibers, glass fibers, ceramic fibers, aramid polymer fibers, and combinations thereof. While the amount of toughening agent 24 added to resin 22 can vary depending on the final toughness desired after curing, in general, toughened resin 18 can comprise from about 0.1% to about 25%, by weight, of toughening agent 24.
As shown in
For ease of transfer and handling, in one embodiment, erosion system 16 can be applied with the aid of a backing 26 on the side opposed to the component, as shown in
Moreover, if a plurality of layers of erosion system 16 is desired, in one embodiment, each layer may comprise the same combination of the toughened resin and the support. Alternately, in another embodiment, each layer can comprise a support having a different color. The colored layers can be stacked to reveal different depths of penetration as erosion occurs. For example, if the erosion system has three layers, a first layer 28, a second layer 30, and a third layer 32, first layer 28 can comprise support 20 that is blue in color, second layer 30 can comprise support 20 that is yellow in color, and third layer 32 can comprise support 20 that is green in color. These colors can serve and as indicator of the degree of erosion present on a component. The colors of the support can be achieved by a variety of methods, including, but not limited to, constructing the support from fibers of different colors.
Once the desired layers of erosion system 16 have been applied, component 10 comprising erosion system 16 can be co-molded using conventional techniques known to those skilled in the art, for example, compression molding, resin transfer molding, vacuum assisted resin transfer molding, or autoclaving. As used herein, “co-molding” refers to infusing resin into both the component and the layers of the erosion system concurrently. Component 10 comprising erosion system 16 can be cured concurrently using standard curing conditions known to those skilled in the art. The result is a coated component 34 wherein erosion system 16 remains as a composite film at the outermost layer, thereby providing coated component 34 with protection from the elements, as shown generally in
The previously described coating system offers several benefits over current coatings including superior erosion protection, visual identification of the coated component for maintenance issues, and the ability to co-mold.
The erosion system described herein can provide from about a 50% increase to about a 400% increase in erosion resistance to the underlying component per layer of the erosion system utilized when compared to conventional erosion protection mechanisms. This increase in erosion resistance can be measured as the mass loss of coating corresponding to a given flux of abrasive material, such as sand. Once cured, the incorporation of the previously described toughening agents into the liquid resin can allow the erosion system to serve as an integral barrier between the outside elements and the coated composite. Without intending to be limited by theory, the addition of the fibers to the resin makes the toughened resin a composite film after curing. This composite film is better able to withstand erosion attributable to elemental exposure.
Moreover the inclusion of a plurality of layers of the erosion system, each having a different colored support, can provide for visual identification of erosion. As the erosion system erodes from exposure to the elements, different colored layers of the support are revealed. By visually inspecting the colors of the exposed mesh, it can be determined how deep into the erosion system the erosion has penetrated. This visual inspection can increase the efficiency of making assessments of the integrity of the erosion system for purposes of maintenance or repair, as compared to conventional techniques.
In addition, the ability to co-mold the present embodiments can provide net shaped coated components displaying more dimensional consistency and less variation between coated components. In this way, the sanding, priming, and painting steps generally required by conventional manufacturing can be substantially eliminated. Co-molding can also help reduce the cost and time involved in manufacturing such coated components. In addition, a variety of erosion resistance improvements can be achieved in a single component by applying a different number of layers of material to the component, by selectively positioning the placement of the material about the component, or a combination thereof. Moreover, the ability to selectively improve erosion in specific portions of the component can further help save costs by eliminating the need to coat the entire component.
This written description uses examples to disclose the invention, including the best mode, and also to enable any person skilled in the art to make and use the invention. The patentable scope of the invention is defined by the claims, and may include other examples that occur to those skilled in the art. Such other examples are intended to be within the scope of the claims if they have structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal language of the claims.
This Application claims priority to Provisional Application Ser. No. 61/037,524, filed Mar. 18, 2008, which is herein incorporated by reference in its entirety.