Patent Grant
7960493
The present invention relates to a process to prepare polyol esters from tertiary alkyl acid with reduced homo-polymerisation of the polyols. Esters of trialkyl acetic acids are known to have high hydrolytic resistance, and to enhance the hydrolytic stability of adjacent ester. They are therefore well suitable for coating and or structural end use applications, where resistance against hydrolysis is desired. This property is due to steric hindrance provided by the trialkyl group of the acid. Partially esterified polyols with trialkyl acetic acid are therefore appreciated as building-block in the synthesis of resins for coatings or structural applications.
The esterification of an alcohol with a trialkyl acetic acid is difficult, and therefore such an acid has even been used as catalyst to promote the esterification reaction of a less sterically hindered acid with an alcohol (WO 01 44156).
The use of traditional esterification catalysts for the esterification of a sterically hindered acid with alcohol or polyol is known from Jour. Am. Oil. Chem. Soc., Vol 45, 5-10, January 1968. The conditions used are in the opinion of the authors more rigorous than for non-sterically hindered acid or alcohol and in the case of polyols they worked with an excess of acid to achieve a complete esterification of the alcohol functions.
The esterification of highly branched (sterically hindered) acids was also known by use of non traditional esterification catalysts. The use of chlorosilanes (Bull. Chem. Soc. Jpn, 54, 1267-1268) is efficient in case of a mono alcohol due to the formation of the alkoxysilanes as active species. However, not any technology is given as to the use of this method for partial esterification of polyols.
From said cited publications it can be derived that the prior art solutions suffer from disadvantages such as the use of expensive catalysts, or that the conditions could not be used to promote a partial esterification of a polyol to yield predominantly mono ester of polyols with only small amounts of higher molecular weight compound resulting from etherification side reactions.
A process that could use conventional esterification catalysts to produce predominantly mono-ester of polyols is strongly needed by the industry; as such a monomer is seen as a valuable building block to be used in further resin synthesis.
As result of extensive research and experimentation, it has now surprisingly been found that a selection of specific process conditions in combination with a specific of catalyst enables the predominant formation of low viscosity hydroxyl functional mono-ester from tertiary alkyl carboxylic acids with polyols.
Surprisingly, it has been found now that use of sulfonic acid derivatives under mild thermal conditions is an efficient combination to the production of a mono-ester of a polyol without significant formation of polyethers. Said polyethers are regarded as undesired homopolymer side products and believed to be the reaction product between alcohol functions; this reaction is a competition reaction when esterification is slow or when the alcohol is used in excess over the acid functions. The present invention provides a solution for the problem encountered i.e. an improved selective preparation of mono ester from polyols and sterically hindered carboxylic acids.
The process for the above selective esterification reaction is obtained in the presence of acid catalyst at a temperature below 180° C.
Suitable polyols can be selected from ethylene glycol, propylene glycol, oligomer of glycols (n from 2 to 10), glycerol, neopentyl glycol, trimethylolpropane, pentaerythritol, and combination thereof. In one embodiment, the polyols are selected from ethylene glycol, neopentyl glycol, trimethylolpropane, pentaerythritol. In another embodiment, the polyols are selected from neopentyl glycol, trimethylolpropane.
The acid derivative is selected from an acid corresponding to the general formula (I),
in which R1 and R2 are independently aliphatic alkyl radicals of 1 to 10 carbon atoms, the total carbon atoms of the three radicals (CH3+R1+R2) being 3 to 20. In another embodiment, the total carbon atoms of the three radicals (CH3+R1+R2) being 3 to 13.
The acid catalyst is selected from a sulphonic acid derivative such as methane sulphonic, ethane sulphonic, trifluoromethane sulphonic, para toluene sulphonic, xylene sulphonic acids. In one embodiment, the acid catalyst is selected from methane sulphonic acid or para-toluene sulphonic acid. These acids are used in a range of 0.05 to 4 weight % relative to the weight of acid and polyol. In another embodiment, the range is 0.10 to 2.5 weight % on acid and polyol. In one embodiment, the catalyst is methane sulphonic acid.
The hydroxyl ester derived from the above polyol and the alkyl acid of formula (I) can further be used as building blocks in the preparation of a polyester resin with improved chemical resistance.
The resins so obtained are oligomers that may be used advantageously in coating compositions, in compositions for fiber impregnation and for lube oil application.
Test Description and Analytical Methods:
Viscosity of Newtonian systems using a Brookfield viscometer: ISO 2555-89.
The invention is illustrated in more detail in the following examples, however without restricting its scope to these specific embodiments. All percentages are contents by mass weight and all parts are parts by mass weight, unless expressly stated otherwise.
A 11 round-bottomed glass reactor equipped with a stainless steel anchor stirrer, thermocouple, reflux condenser with a Dean Stark and N2-inlet is used. The tertiary alkyl acid and polyalcohol (see Tables 1 and 2 for the composition); with the mole ratio acid/alcohol is 1:1; are charged into the reactor. The reaction is carried out under N2 and constant stirring and heated progressively. At 130° C., the solvent (xylene) and the catalyst are added. The temperature is raised till
The temperature is kept constant till the acid value has reached a constant value. At that moment, the reaction is stopped and cooled down.
The scheme below indicates the structure of the products that have been identified by GC-MS analysis (with ionization detection, mode POS-Cl) for the examples based on trimethylol propane(TMP) as polyol. In the analyzed samples no polyethers were found.
The Catalyst Used:
The weight % reported in the Tables below for MSA is the weight of the supplied solution. pTSA supplied as solid, 95.5%, commercially available from Acros Organics, Geel, Belgium MSA supplied as solution (70% in water) commercially available from Atofina, Houston, Tex.
Polyol used as supplied: Trimethylol propane (TMP) 97%, commercially available from Sigma-Aldrich, St. Louis, Mo. Neo pentyl glycol (NPG) 99%, commercially available from Sigma-Aldrich, St. Louis, Mo. Pentaerythritol 98%, commercially available from Sigma-Aldrich, St. Louis, Mo.
Examples of Pivalic Acid (V5)
Examples of VERSATIC 10 Acid (V10)
A 1 l round-bottomed glass reactor equipped with a stainless steel anchor stirrer, thermocouple, reflux condenser and N2-inlet is used. The product of example 6 (177.8 grams) is charged with succinic anhydride (153.6 grams) in the reactor in a 1-1 mole ratio (considering the ideal adduct structure to be the mono ester). The mixture is heated under stirring until 105° C. around this temperature an exotherm occur and the temperature rose till 160° C. The reaction conditions are maintained till the acid value is reached. Then the reaction mixture is cooled down to about 140° C. before adding Cardura E10 (401 gram) the temperature is kept constant for 1 hour.
Polyester Resin Properties:
Coating Formulation
Coating Properties:
The polyesters with the compositions presented in the Table 3 were prepared in a glass reactor equipped with stirrer, heater/cooler and Dean stark. All the ingredients were heated to 160-200° C. until the desired acid value was obtained. Xylene was used to remove the reaction water by azeotropic distillation.
The polyester 14 was then evaluated as reactive diluent for an isocyanate cured coating. It was first blended in 40 wt % with an acrylic polyol. Desmodur N3600, an aliphatic isocyanate from Bayer, was used as curing agent, the catalyst was a mixture of dibutyltin dilaurate and 1,4 diazabicyclo 2,2,2 octane, and the systems were diluted to 100 mPas with butyl acetate.
This system was compared with a similar coating formulation prepared with the acrylic polyol without polyester. The mixture containing 40% had a much lower VOC than the reference material (400 versus 458 g/l) but nevertheless displayed excellent hardening speed and appearance. After less than 30 minutes at 60° C. the system was tack-free.
The temperature is kept constant till the acid value has reached a constant value. At that moment, the reaction is stopped and cooled down.
The scheme below indicates the structure of the products that have been identified by GC-MS analysis (with ionization detection, mode POS-Cl) for the examples based on trimethylol propane(TMP) as polyol. In the analyzed samples no polyethers were found.
The Catalyst Used:
The weight % reported in the Tables below for MSA is the weight of the supplied solution. pTSA supplied as solid, 95.5%, commercially available from Acros Organics, Geel, Belgium MSA supplied as solution (70% in water) commercially available from Atofina, Houston, Tex.
Polyol used as supplied: Trimethylol propane (TMP) 97%, commercially available from Sigma-Aldrich, St. Louis, Mo. Neo pentyl glycol (NPG) 99%, commercially available from Sigma-Aldrich, St. Louis, Mo. Pentaerythritol 98%, commercially available from Sigma-Aldrich, St. Louis, Mo.
| Number | Date | Country | Kind |
|---|---|---|---|
| 05076468 | Jun 2005 | EP | regional |
This application is a divisional of U.S. patent application Ser. No. 11/915,218 filed May 15, 2008, now U.S. Pat. No. 7,737,297, which is a 371 application of PCT/EP2006004070 dated May 2, 2006, which claims benefit of European Patent Application No. 05076468.7, filed Jun. 24, 2005, the entire contents of which are hereby incorporated by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5324853 | Jones et al. | Jun 1994 | A |
| 5869191 | Clemons Van Gaalen et al. | Feb 1999 | A |
| 20040030168 | Mozeleski et al. | Feb 2004 | A1 |
| Number | Date | Country |
|---|---|---|
| WO 9610009 | Apr 1996 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20100240861 A1 | Sep 2010 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11915218 | US | |
| Child | 12767591 | US |