The application claims priority to Chinese Application No. 202111356393.6, filed on Nov. 16, 2021, entitled “ethylene degradation catalyst and preparation method and use thereof”, which is herein specifically and entirely incorporated by reference.
The present disclosure relates to the technical field of catalytic degradation of ethylene, and in particular to an ethylene degradation catalyst and a preparation method and a use thereof.
Volatile Organic Compounds (VOCs) are important precursors for the formation of PM2.5 and O3. In order to further improve air quality, the comprehensive treatment of the coal chemical industry and other key industries of emission of VOCs should be enhanced. The current technologies for treatment of VOCs are mainly divided into three categories, namely adsorption recovery technology, combustion technology, adsorption concentration+combustion technology, wherein the combustion technology is used for treatment of VOCs lacking a recovery value. For example, volatile organic compounds from the coal chemical industry are mainly derived from coal gasification process, and the process of washing tail gas with low temperature methanol; the VOCs have the characteristics such as a wide variety of VOCs, low recovery value, and high air volume. The combustion technology can oxidize VOCs to harmless emissions of CO2 and H2O.
Catalytic combustion is one of the key means in the combustion technology, wherein the key nodes of catalytic combustion technology include the design and preparation of catalysts for oxidation of VOCs. The catalysts for oxidation of VOCs are typically composed of two parts, namely a carrier and an active ingredient (noble metal). Ethylene is a common VOC gas of the coal chemical industry, the commercially available catalysts for the oxidation of ethylene are mainly Pt/γ-Al2O3 catalysts. However, the active ingredient noble metal is expensive and requires a long supply cycle, and is essentially dependent on imports from foreign countries. In addition, the commercially available Pt/γ-Al2O3 catalysts suffer from the defects such as undesired thermal stability, poor resistance to catalyst poisoning.
To sum up, it is imperative to develop a novel, low cost, anti-poisoning, stable and environmentally friendly catalyst that effectively reduces the atmospheric pollutants VOCs.
An object of the present disclosure is to overcome the problem in the prior art that the ethylene degradation catalyst requires a noble metal as an active ingredient, and the present disclosure provides an ethylene degradation catalyst and a preparation method and a use thereof, wherein the ethylene degradation catalyst can achieve a high catalytic activity for ethylene.
The inventors of the present disclosure have discovered during the course of research that, when the composition of an ethylene degradation catalyst comprises K2O and Na2O, and TiO2 crystals have an anatase type, and the surface of TiO2 crystals is covered with a TiO2 disordered layer containing surface hydroxyl groups and Ti3+, the catalyst can effective decompose ethylene into CO2 and H2O, without using a noble metal contained in the catalyst as an active ingredient, thus obtain the present disclosure.
In order to achieve the above object, a first aspect of the present disclosure provides an ethylene degradation catalyst, comprising TiO2 crystals and auxiliary agents; wherein the crystalline form of TiO2 crystal is an anatase type, and the surface of TiO2 crystal is covered with a TiO2 disordered layer containing surface hydroxyl groups.
In a second aspect, the present disclosure provides a method of preparing an ethylene degradation catalyst, comprising the following steps:
(1) mixing a titanium source powder with an acid, and roasting an obtained mixture;
(2) subjecting a product obtained from the roasting to water leaching, and subsequently to a solid-liquid separation to obtain a Ti-containing filtrate;
(3) subjecting the filtrate to hydrolysis and aging to obtain a metatitanic acid colloid comprising auxiliary agent elements which contain Na and K;
(4) subjecting the metatitanic acid colloid to water washing, drying and calcination, to obtain nano-TiO2 powder;
(5) subjecting the nano-TiO2 powder to hydrogenation, so as to prepared the ethylene degradation catalyst;
wherein the titanium source powder is selected from the group consisting of spent SCR denitration catalysts containing Na2O and K2O.
In a third aspect, the present disclosure provides an ethylene degradation catalyst prepared with the aforesaid method.
In a fourth aspect, the present disclosure provides a use of the aforesaid ethylene degradation catalyst in the degradation of ethylene.
Through the aforementioned technical scheme, the present disclosure has the favorable effects as follows:
(1) The preparation method of the ethylene degradation catalyst of the present disclosure uses the spent SCR catalyst containing Na2O and K2O auxiliary agents as raw materials, can rationally utilize the elements contained in the obtained anatase type TiO2 prepared with the sulfuric acid method, so as to provide the acidic site for hydrogenation of TiO2. In addition, the structural defect of the prepared TiO2 crystal can rationally regulate its oxidation-reduction property.
(2) The ethylene degradation catalyst of the present disclosure does not require a use of transition metals or noble metals as active ingredients, thereby eliminating the need to deal with problems of catalyst poisoning and aging during the process of catalytic degradation of ethylene, and the catalyst can be easily regenerated after deactivation.
1. TiO2 powder
2. ethylene degradation catalyst
The terminals and any value of the ranges disclosed herein are not limited to the precise ranges or values, such ranges or values shall be comprehended as comprising the values adjacent to the ranges or values. As for numerical ranges, the endpoint values of the various ranges, the endpoint values and the individual point value of the various ranges, and the individual point values may be combined with one another to produce one or more new numerical ranges, which should be deemed have been specifically disclosed herein.
A first aspect of the present disclosure provides an ethylene degradation catalyst, comprising TiO2 crystals and auxiliary agents; wherein the crystalline form of TiO2 crystal is an anatase type, and the surface of TiO2 crystal is covered with a TiO2 disordered layer containing surface hydroxyl groups.
The ethylene degradation catalyst provided by the present disclosure comprises TiO2 crystals having a specific structure and auxiliary agents, it does not comprise a noble metal as an active ingredient, and can produce better effect of catalytic degradation of ethylene.
In some embodiments of the present disclosure, it is preferable that the catalyst comprises TiO2 in an amount of 99.9-99.99 wt %, based on the total weight of the catalyst.
In some embodiments of the present disclosure, the catalyst further comprises auxiliary agents, which can advantageously promote the technical effect of increasing the catalytic degradation of ethylene. Preferably, the auxiliary agents comprise K2O and Na2O, the catalyst comprises K2O in an amount of 0.002-0.006 wt % and Na2O in an amount of 0.006-0.098 wt %, based on the total weight of the catalyst.
In some embodiments of the present disclosure, the catalyst may further comprise a pore structure that is favorable for catalytic degradation reaction of ethylene. Preferably, the catalyst has a specific surface area of 80-120 m2/g, a pore volume of 0.2-0.8 cm3/g, and a pore diameter of 8-13 nm.
In some embodiments of the present disclosure, it is preferable that the TiO2 disordered layer has a thickness of 1.8-3 nm. The structural defects formed by TiO2 crystals in the catalyst may form the TiO2 disordered layer on the surface of the TiO2 crystals, and can contain the surface hydroxyl group.
In some embodiments of the present disclosure, it is preferable that a molar percentage of the Ti3+ of the TiO2 disordered layer in Ti elements is within a range of 2.15%-10.37%, more preferably 5.15%-8.66%. The TiO2 crystals of the present disclosure contain the above-mentioned defects and the amount of the defects is calculated based on Ti3+, and when the molar percentage falls in the above range, those skilled in the art may control the catalyst to more appropriately match the above-mentioned auxiliary agents, and exhibit desired catalytic activity for catalytic degradation reaction of ethylene. The amount of Ti3+ can be determined by X-ray photoelectron energy spectrum analysis method.
In the present disclosure, the surface hydroxyl groups are hydroxyl groups attached to Ti3+, and may be represented as Ti—OH.
In the present disclosure, the ethylene degradation catalyst has an appearance of an earth yellow color and a morphology of a spherical shape.
In a second aspect, the present disclosure provides a method of preparing an ethylene degradation catalyst, as shown in
(1) mixing a titanium source powder with an acid, and roasting an obtained mixture;
(2) subjecting a product obtained from the roasting process to water leaching, and subsequently to a solid-liquid separation to obtain a Ti-containing filtrate;
(3) subjecting the filtrate to hydrolysis and aging to obtain a metatitanic acid colloid comprising auxiliary agent elements which contain Na and K;
(4) subjecting the metatitanic acid colloid to water washing, drying and calcination, to obtain nano-TiO2 powder;
(5) subjecting the nano-TiO2 powder to hydrogenation, so as to prepared the ethylene degradation catalyst;
wherein the titanium source powder is selected from the group consisting of spent SCR denitration catalysts containing Na2O and K2O.
In some embodiments of the present disclosure, steps (1) and (2) can be used to extract mainly Ti elements and to obtain the soluble Ti-containing compounds, and can extract Na and K elements as well. Preferably, the acid is concentrated sulfuric acid; preferably, the acid has a concentration of 85-92 wt %, more preferably 88-91 wt %. The requirement of extracting the beneficial elements dominated by Ti elements is fulfilled.
In some embodiments of the present disclosure, preferably, the conditions of mixing include a temperature of 20-30° C. and a time of 2-6 hours; more preferably, a temperature of 22-28° C. and a time of 3-5 hours.
In some embodiments of the present disclosure, it is preferable that the mass ratio of the titanium source powder to the acid is 1:(1.5-2). Wherein, the titanium source powder may further comprise an auxiliary agent, preferably comprising Na2O and K2O, more preferably, the titanium source powder comprises K2O in an amount of 0.1-0.3 wt % and Na2O in an amount of 0.2-0.8 wt %, based on the total weight of the titanium source powder, it can ensure that the finally prepared ethylene degradation catalyst comprises the defined amount of Na2O and K2O, to further promote the catalytic activity for catalytic degradation of ethylene.
In some embodiments of the present disclosure, it is preferable that the roasting temperature is within a range of 150-300° C. and the roasting time is 30-90 min.
In some embodiments of the present disclosure, it is preferred that the titanium source powder has an average particle size of 10-1,000 μm, preferably 50-200 μm. The above conditions can facilitate a more efficient extraction of the Ti, Na, K elements to obtain the soluble Ti-containing compounds.
In some embodiments of the present disclosure, step (2) may achieve dissolution of the Ti element, and may also dissolve auxiliary agent elements such as Na and K. Preferably, the water leaching conditions comprise a temperature of 60-120° C. and a time of 60-180 min; and more preferably, a temperature of 80-100° C. and a time of 80-120 min.
In some embodiments of the present disclosure, it is preferable that the mass ratio of the product to the water used in the water leaching is 1:(2-6), more preferably 1:(3-5).
In some embodiments of the present disclosure, step (3) may be mainly used for precipitation of Ti. Preferably, the hydrolysis temperature is within a range of 80-110° C., more preferably 85-105° C.; and the hydrolysis time is within a range of 2-5 h, more preferably 2.5-4 h.
In some embodiments of the present disclosure, the hydrolysis is followed by an aging treatment, it is preferable that the aging time is within a range of 15-30 h, more preferably 16-26 h, and the aging temperature is within a range of 10-50° C., more preferably 20-35° C.
In the present disclosure, the aged material is subjected to suction filtration, separation and water washing, to obtain a metatitanic acid colloid containing an auxiliary agent element.
In some embodiments of the present disclosure, step (4) is carried out to purify the metatitanic acid colloid, for example, the step may be used for removing impurities and dehydration. The water washing process is used to remove impurities from the metatitanic acid colloid by a process comprising mixing the metatitanic acid colloid with water, stirring the mixture, filtering and removing the filtrate. Water washing and filtering may be performed for several times. Preferably, the drying temperature is within a range of 65-95° C. and the drying time is 60-120 min.
In some embodiments of the present disclosure, it is preferable that the calcination temperature is within a range of 450-700° C., the calcination time is 2-8 h, and the temperature rise rate is 5-10° C./min. Preferably, the calcination is carried out for 5-6 h at a temperature of 500-600° C. and the temperature rise rate of 5-7° C./min, and the effect is better.
In the present disclosure, the crystalline form of the nano-TiO2 powder obtained after calcination is an anatase form.
Preferably, the nano-TiO2 powder further contains auxiliary agents, such as Na2O and K2O, which are dispersed in the nano-TiO2 powder.
In some embodiments of the present disclosure, the nano-TiO2 powder is subjected to surface hydrogenation and reduction in step (5), and the defective structures are generated after the hydrogenation process. Preferably, the hydrogenation condition comprises a hydrogenation temperature of 400-550° C., a hydrogenation temperature rise rate of 5-10° C./min, a hydrogenation time of 2-12 h, a hydrogen concentration of 90-100 vol %, and a hydrogen flow rate of 100-300 mL/min. The TiO2 powder is heated from room temperature to the hydrogenation temperature at the hydrogenation temperature rise rate in the presence of hydrogen at a set flow rate, and the hydrogenation is then performed at constant temperature. Preferably, the hydrogenation is performed at 420-460° C. under normal pressure for 4-12 h and the hydrogen flow rate of 100-150 mL/min in an atmosphere of 100 vol % H2, the effect is more desirable.
In a third aspect, the present disclosure provides an ethylene degradation catalyst prepared with the aforesaid method.
Preferably, the ethylene degradation catalyst prepared with the above-described process comprises TiO2 crystals and auxiliary agents, wherein the catalyst comprises K2O in an amount of 0.002-0.006 wt % and Na2O in an amount of 0.006-0.098 wt %, based on the total weight of the catalyst. The crystalline form of the TiO2 crystal is an anatase form, the catalyst comprises TiO2 in an amount of 99.9-99.99 wt %, and the surface of TiO2 crystal is covered with a TiO2 disordered layer. The TiO2 disordered layer has a thickness of 1.8-3 nm; a molar percentage of the Ti3+ of the TiO2 disordered layer in Ti elements is within a range of 2.15%-10.37%, preferably 5.15%-8.66%. The catalyst has a specific surface area of 80-120 m2/g, a pore volume of 0.2-0.8 cm3/g, and a pore diameter of 8-13 nm.
In a fourth aspect, the present disclosure provides a use of the aforesaid ethylene degradation catalyst in the degradation of ethylene.
According to the present disclosure, the use specifically comprises, the catalytic degradation reaction of ethylene is performed by contacting an organic volatile gas containing ethylene with the ethylene degradation catalyst of the present disclosure.
According to the present disclosure, the use is implemented under the temperature conditions, which may be within a range of 100-500° C.
According to the present disclosure, the volume concentration of ethylene in the organic volatile gas may be within a range of 10-1,000 ppm.
According to the present disclosure, the hourly volume space velocity of the organic volatile gas is 4,000-40,000 h−1.
The present disclosure will be described in detail below with reference to examples.
In the following Examples and Comparative examples:
(1) The crystal structure of the prepared ethylene degradation catalyst was measured by the X-Ray Diffraction (XRD) analysis using the D8 ADVANCE manufactured by Bruker SA in Germany, and the testing and scanning rate was within a range of 0.5°/min to 5°/min.
(2) The pore structure and mesopore pore diameter of the prepared ethylene degradation catalyst were measured through the N2 adsorption method, using the ASAP 2020 physical adsorption instrument manufactured by the Micromeritics Corp. in USA, and the adsorption medium was N2.
(3) The morphology of the prepared ethylene degradation catalyst was measured through the Transmission Electron Microscope (TEM) using a transmission electron microscope model JEM ARM 200F manufactured by the JEOL corporation in Japan.
(4) The Electron Paramagnetic Resonance (EPR) image analysis was performed by using an electron paramagnetic resonance spectrometer.
(5) The titanium source powder was the spent SCR catalyst with an average particle size of 74 μm, and the chemical composition was determined by the XRF fluorescence analysis method (RIPP 117-90 Standard method, compiled by the Research Institution of Petroleum Processing in China), and the results were shown in Table 1. The ingredients of the catalyst and contents thereof were also measured by the XRF fluorescence analysis method.
(1) The spent SCR catalyst (with a particle size of 120 μm) and the concentrated sulfuric acid (with a concentration of 90 wt %) were blended according to a mass ratio of 1:1.8 to obtain a mixture; the mixture was subjected to roasting at a temperature of 180° C. for 1 h.
(2) The product obtained from roasting was subjected to water leaching at a temperature of 100° C. for 100 min according to a mass ratio of 1:4 between the product and water, the mixture was subjected to a solid-liquid separation to obtain a Ti-containing filtrate;
(3) Subjecting the filtrate to hydrolysis and aging in sequence, under the hydrolysis conditions consisting of a hydrolysis temperature of 100° C. and a hydrolysis time of 3 h, and the aging conditions consisting of an aging temperature of 25° C. and an aging time of 20 h, the obtained solid phase product was analyzed to be a metatitanic acid colloid comprising auxiliary agent, the auxiliary agent contained Na2O and K2O;
(4) The metatitanic acid colloid was subjected to water washing, the solid obtained from separation was subjected to drying at 80° C. for 60 min, heating at a temperature rise rate of 7° C./min and finally subjected to calcination in a muffle furnace at 500° C. for 6 h, so as to obtain the nano-TiO2 powder, upon analysis, the particle size of the nano-TiO2 powder was about 30 nm, the crystalline form the nano-TiO2 powder was an anatase type.
(5) The nano-TiO2 powder was subjected to hydrogenation in a tube furnace under a pressure of 0.1 MPa, the hydrogen concentration of 100 vol %, the hydrogen flow rate of 120 mL/min, the hydrogenation temperature rise rate of 10° C./min, so as to reach the hydrogenation temperature of 420° C., the hydrogenation with the thermal insulation was performed for 12 h, and then cooled to room temperature, the ethylene degradation catalyst was prepared and denoted as T-1.
The obtained ethylene degradation catalyst was subjected to the XRD analysis, the ethylene degradation catalyst comprised TiO2 crystals with the crystalline form of an anatase type; as can be seen from the TEM diagram of
(1) The spent SCR catalyst (with a particle size of 500 μm) and the concentrated sulfuric acid (with a concentration of 88 wt %) were blended according to a mass ratio of 1:1.5 to obtain a mixture; the mixture was subjected to roasting at a temperature of 150° C. for 0.5 h.
(2) The product obtained from roasting was subjected to water leaching at a temperature of 90° C. for 80 min according to a mass ratio of 1:3 between the product and water, the mixture was subjected to a solid-liquid separation to obtain a Ti-containing filtrate;
(3) Subjecting the filtrate to hydrolysis and aging in sequence, under the hydrolysis conditions consisting of a hydrolysis temperature of 85° C. and a hydrolysis time of 2.5 h, and the aging conditions consisting of an aging temperature of 20° C. and an aging time of 16 h, the obtained solid phase product was analyzed to be a metatitanic acid colloid comprising auxiliary agent, the auxiliary agent contained Na2O and K2O;
(4) She metatitanic acid colloid was subjected to water washing, the solid obtained from separation was subjected to drying at 95° C. for 120 min, heating at a temperature rise rate of 5° C./min and finally subjected to calcination in a muffle furnace at 600° C. for 5 h, so as to obtain the nano-TiO2 powder, upon analysis, the particle size of the nano-TiO2 powder was about 20 nm, the crystalline form the nano-TiO2 powder was an anatase type.
(5) The nano-TiO2 powder was subjected to hydrogenation in a tube furnace under a pressure of 0.1 MPa, the hydrogen concentration of 100 vol %, the hydrogen flow rate of 100 mL/min, the hydrogenation temperature rise rate of 5° C./min, so as to reach the hydrogenation temperature of 430° C., the hydrogenation with the thermal insulation was performed for 4 h, and then cooled to room temperature, the ethylene degradation catalyst was prepared and denoted as T-2.
The catalyst T-2 was analyzed and the results were shown in Table 2. The comparisons of appearance, XRD, nitrogen adsorption-desorption isotherm, EPR, TEM between the catalyst and the TiO2 powder were performed, and the results obtained from the photographs or curves or spectrogram were similar to those obtained in Example 1.
(1) The spent SCR catalyst (with a particle size of 200 μm) and the concentrated sulfuric acid (with a concentration of 91 wt %) were blended according to a mass ratio of 1:2 to obtain a mixture; the mixture was subjected to roasting at a temperature of 300° C. for 1.5 h.
(2) The product obtained from roasting was subjected to water leaching at a temperature of 80° C. for 120 min according to a mass ratio of 1:5 between the product and water, the mixture was subjected to a solid-liquid separation to obtain a Ti-containing filtrate;
(3) Subjecting the filtrate to hydrolysis and aging in sequence, under the hydrolysis conditions consisting of a hydrolysis temperature of 105° C. and a hydrolysis time of 4 h, and the aging conditions consisting of an aging temperature of 35° C. and an aging time of 26 h, the obtained solid phase product was analyzed to be a metatitanic acid colloid comprising auxiliary agent, the auxiliary agent contained Na2O and K2O;
(4) The metatitanic acid colloid was subjected to water washing, the solid obtained from separation was subjected to drying at 65° C. for 100 min, heating at a temperature rise rate of 6° C./min and finally subjected to calcination in a muffle furnace at 550° C. for 5 h, so as to obtain the nano-TiO2 powder, upon analysis, the particle size of the nano-TiO2 powder was about 40 nm, the crystalline form the nano-TiO2 powder was an anatase type.
(5) The nano-TiO2 powder was subjected to hydrogenation in a tube furnace under a pressure of 0.1 MPa, the hydrogen concentration of 100 vol %, the hydrogen flow rate of 150 mL/min, the hydrogenation temperature rise rate of 8° C./min, so as to reach the hydrogenation temperature of 460° C., the hydrogenation with the thermal insulation was performed for 9 h, and then cooled to room temperature, the ethylene degradation catalyst was prepared and denoted as T-3.
The catalyst T-3 was analyzed and the results were shown in Table 2. The comparisons of appearance, XRD, nitrogen adsorption-desorption isotherm, EPR, TEM between the catalyst and the TiO2 powder were performed, and the results obtained from the photographs or curves or spectrogram were similar to those obtained in Example 1.
The catalyst was prepared according to the same method as that of Example 1, except that the “hydrogenation temperature of 400° C.” was replaced by the “hydrogenation temperature of 420° C.”. The prepared ethylene degradation catalyst was denoted as T-4.
The catalyst T-4 was analyzed and the results were shown in Table 2. The comparisons of appearance, XRD, nitrogen adsorption-desorption isotherm, EPR, TEM between the catalyst and the TiO2 powder were performed, and the results obtained from the photographs or curves or spectrogram were similar to those obtained in Example 1.
The catalyst was prepared according to the same method as that of Example 1, except that the “hydrogenation time of 2 h” was replaced by the “hydrogenation time of 12 h”. The prepared ethylene degradation catalyst was denoted as T-5.
The catalyst T-5 was analyzed and the results were shown in Table 2. The comparisons of appearance, XRD, nitrogen adsorption-desorption isotherm, EPR, TEM between the catalyst and the TiO2 powder were performed, and the results obtained from the photographs or curves or spectrogram were similar to those obtained in Example 1.
The commercially available TiO2 was used, the parameters of the prepared catalyst were shown in Table 2.
The catalyst was prepared according to the same method as that of Example 1, except that the “hydrogenation concentration of 50 vol %” was replaced by the “hydrogenation concentration of 100 vol %”. The parameters of the prepared catalyst were shown in Table 2.
The catalyst was prepared according to the same method as that of Example 1, except that the “hydrogenation time of 0.5 h” was replaced by the “hydrogenation time of 12 h”, the “hydrogenation temperature of 200° C.” was replaced by the “hydrogenation temperature of 420° C.”. The parameters of the prepared catalyst were shown in Table 2.
As can be seen from the results of Table 2, the TiO2 without impurities was used for hydrogenation in Comparative example 1, the hydrogen gas at a low concentration was used for hydrogenation in Comparative example 2, and the hydrogenation was performed in Comparative example 3 by using the conditions that neither the hydrogenation time nor the hydrogenation temperature were within the scopes defined in the present disclosure; the results indicated that the ethylene degradation catalysts prepared in Examples 1-5 by using the preparation method of the present disclosure had a specific thickness of said disordered layer and a molar percentage of the Ti3+ of the TiO2 disordered layer in Ti elements.
The catalysts prepared in Examples 1-5 and Comparative examples 1-3 were applied in the ethylene decomposition reactions, wherein during the process of decomposing the organic volatile gases through the catalytic oxidation, the ethylene had a volume concentration of 700 ppm, the content of other gas O2 was 10 v %, nitrogen gas N2 was a balance gas, the total flow rate was 1,000 mL/min, and the hourly volume space velocity of organic volatile gas was 100,000 h−1, the results were shown in Table 3.
Wherein the degradation efficiency %=(ethylene concentration at an inlet−ethylene concentration at an outlet)/ethylene concentration at an inlet x100%.
As can be seen from the results of Table 3, the use of titanium oxide of Comparative example 1, which has not been hydrogenated, there is no degradation efficiency for ethylene; the hydrogenation time, temperature and hydrogen concentration in the Comparative examples 2 and 3 are not within the ranges, and the prepared catalysts do not have the structure of the catalysts of the present disclosure, and the catalytic degradation effect of ethylene is inferior to that of the catalysts prepared in Examples 1 to 5 of the present disclosure. In addition, the titanium oxide of Comparative example 1 is subjected to calcination under the conditions of step (4) in Example 1 to obtain an anatase type crystal, and was hydrogenated according to the method of step (5) in Example 1, but the prepared catalyst does not contain the auxiliary agents K2O and Na2O, and cannot obtain a thickness of the disordered layer and a molar percentage of the Ti3+ of the TiO2 disordered layer in Ti elements as defined in the present disclosure, thus cannot produce the desirable catalytic degradation effect of ethylene.
The above content describes in detail the preferred embodiments of the present disclosure, but the present disclosure is not limited thereto. A variety of simple modifications can be made in regard to the technical solutions of the present disclosure within the scope of the technical concept of the present disclosure, including a combination of individual technical features in any other suitable manner, such simple modifications and combinations thereof shall also be regarded as the content disclosed by the present disclosure, each of them falls into the protection scope of the present disclosure.