Ex-situ presulfuration in the presence of a hydrocarbon molecule

Information

  • Patent Application
  • 20020037806
  • Publication Number
    20020037806
  • Date Filed
    April 12, 2001
    23 years ago
  • Date Published
    March 28, 2002
    22 years ago
Abstract
The invention relates to a process for the ex-situ presulfuration of a catalyst for the hydroconversion of hydrocarbons in the presence of hydrogen and of at least one sulfurated compound. It is characterized in that the catalyst is also brought into contact with at least one hydrocarbon compound.
Description


FIELD OF THE INVENTION

[0002] The invention relates to a process for the ex-situ presulfuration of a catalyst for the hydroconversion of hydrocarbons in the presence of hydrogen and of at least one sulfurated compound.



BACKGROUND OF THE INVENTION

[0003] Catalysts for the hydroconversion of hydrocarbons and particularly for the hydro-treatment of petroleum cuts generally contain at least one element of group VIII or group VI of the periodic classification or a combination of several elements from these same groups, deposited on an amorphous oxide support, for example zeolithic such as for example the designated solids CoMo/Al2O3, NiMo/Al2O3 or NiW/Al2O3. To enable the catalysts to be active for different hydrotreatment reactions, i.e. hydrodesulfuration, hydrodenitrogenization, demetallation or demetallization and certain types of hydrogenation, it is desirable to carry out a sulfuration of the metals with the aim of creating an active phase of the mixed sulfur type. This pre-conditioning stage must be carried out with the greatest care as it conditions the future activity of the product in its subsequent use It can be carried out according to two different methods. The conventional technique, called in-situ sulfuration, consists of carrying out this pretreatment after loading the catalyst into the hydrocarbons conversion reactor.


[0004] The other method of activating this type of catalyst is to carry out an ex-situ sulfuration, i.e. outside the hydrotreatment reactor as described in various patents of the Applicant, for example U.S. Pat. Nos. 4,719,195, 5,139,983, 5,397,756, EP-A 785022.



SUMMARY OF THE INVENTION

[0005] The object of the present invention is to carry out an ex-situ presulfuration of the catalyst in the presence of hydrogen and at least one sulfurated compound which can be sulfurated hydrogen or any other compound containing sulfur. The invention is characterized in that, with the aim of improving the sulfuration or presulfuration, the catalyst is brought into contact with at least one hydrocarbon compound. This hydrocarbon compound is added either preferably at a stage before the presulfuration stage, or also before and during the said presulfuration stage.



DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

[0006] Thus, the catalyst, is preferably brought into contact with the hydrocarbon compound during a stage before the presulfuration stage. In this case, the hydrocarbon compound can be deposited using any method, for example using the method of dry impregnation of the catalyst by the hydrocarbon compound. This impregnation takes place cold, i.e. at normal temperature. It will most often be enough to introduce the hydrocarbon compound into the porosity of the catalyst at least superficially. It is not necessary to go “to pore volume”. Thus, the pore volume of the catalyst is filled completely or at least in part. Preferably, during this treatment, 10 to 100% of the total pore volume of the catalyst is impregnated for example, and more particularly 30 to 100%, by the said hydrocarbon compound.


[0007] The said hydrocarbon compound is chosen from the group constituted by the liquid hydrocarbons, but more particularly the compounds containing oxygen, and particularly alcohols, acids, ketones, aldehydes and other compounds containing oxygen. Vegetable oils, nitrogenous compounds, sulfurated compounds, polysulphides (in particular organic), and more particularly also oil bases or base lube oil, for example 150 Neutral (150 N) type, diesel oils and possibly white spirits can also be used. The latter have already been used in earlier catalyst presulfuration procedures, but they were used as vector solvents of sulfurated compounds with which the catalysts (in particular organic polysulfurs) were presulfurated, whereas here the catalyst is firstly impregnated in its porosity with these white spirits.


[0008] The sulfuration phase can be carried out at atmospheric pressure in a rotary system heated to between approx. 200 and 500° C. In the case of a gaseous hydrogen/sulfurated hydrogen mixture, the partial sulfurated hydrogen pressures can vary within the range of 0.05 to 0.7. The introduction of the reagents can be carried out at the point of injection of the initial solid or at the point of ejection of the final solid, the sulfuration is thus respectively called co-current sulfuration or counter current sulfuration.


[0009] A possible explanation of the benefit brought about by sulfuration in the presence of a carbon compound consists of a thermal effect. The reactions transforming these oxide phases into sulfur phases are very exothermic. If this production of heat is poorly controlled, it can lead to significant heatings of the catalyst bed which, apart from the obvious problems of the safety of the process, can lead to the formation of poorly dispersed sulfur phases. This fritt of the active phase would lead to mediocre catalytic properties. One of the means of improving the control of the temperature at the time of sulfuration consists of impregnating the oxide catalyst with a hydrocarbon compound preferably before the sulfuration stage proper. This addition probably acts as a heat store during the exothermic sulfuration stage and permits an appreciable diminution of the increase in temperature, in particular in the core of the particle. The choice of this hydrocarbon compound will be made from the wide range of organic compounds containing or not containing a functional group.


[0010] Another possible explanation of the benefit brought about by this invention can be the following: the mechanism of the sulfuration of an oxide phase like the mixture of MoO3/CoO or NiO oxides supported on alumina involves a complete recomposition and a migration of species to the surface of the support. The structures of the initial and final phases are fully described in the literature. The oxide phase is comprised of well dispersed species at the surface of the alumina such as polymolybdates or tungstates associated with cobalt or nickel oxides. The active phase is structurally very different from this oxide phase. It is in the form of polygonal sheets of molybdenum or tungsten sulfur, generally stacked in a small number from 1 to 5 for conventional preparations, with cobalt or nickel atoms, so-called promoters, being situated on the periphery of these sheets. It is assumed that the catalytic activity is a function of the fine structure of this mixed phase and more precisely of the location of these border atoms, be this in an edge or corner position of these often hexagonal sheets. It is possible to imagine that the necessary migration of species can be influenced by the presence or not of hydrocarbon species on the surface of the solid, thus slightly modifying the structure of the mixed phase. Another hypothesis which can be proposed is that the carbon itself can be part of the active phase and thus directly modify the catalytic properties. This role of the carbon would obviously be different from that, better known, of depositing coke during the product utilization cycle, provoking the progressive reduction in catalyst performance values.


[0011] The entire disclosure of all applications, patents and publications, cited above and below, and of corresponding French application 98/12.739, filed Oct. 12, 1998, are hereby incorporated by reference.


[0012] Notwithstanding the above description and the following examples, a catalyst can be impregnated with the hydrocarbon liquid at not only ambient temperature, but also at substantially ambient temperatures, i.e. at higher or lower temperatures as convenient. For example, at lower temperatures, the viscosity of the hydrocarbon liquid will increase and therefore the rate of impregnation will be slower. Conversely, at higher temperatures, the hydrocarbon liquid may become excessively volatile. Thus, the term “substantially ambient temperature” encompasses the practicalities involved in the selection of the temperature of impregnation. In any case the impregnation step will be conducted at a lower temperature than 200° C. rather than at higher temperatures in the manner of GB, 533,616.


[0013] Also, the present invention can be conducted without the function of an oxygen-containing hydrocarbon in the manner of the U.S. Pat. No. 5,990,037 to Seamans et al. To this extent, applicant's hydrocarbon.liquid is substantially devoid of oxygenated hydrocarbons. Likewise, the present invention does not contemplate the use of an intermediate step of incorporating elemental sulfur into the pores of the catalyst, in the same manner as Seamans et al. U.S. Pat. No. 4,943,547. Still further, the present invention does not require a step of coating to catalyst with a paraffin wax as in U.S. 3,453,217 to Kozlowski.


[0014] Conversely, it is contemplated that the benefits of the present process obtained by presulfurisation can be achieved by the use of any overall presulfuriation system wherein the present process would achieve at least 60% of the presulfurization thereof. For example, whereas it is unnecessary in the present invention for the hydrocarbon liquid which is impregnated into the catalyst at substantially ambient temperature to contain other sulfurizing agents, the hydrocarbon liquid should not in any case contain sulfurizing agents which would cause more than 60% of the presulfurization, more preferably not more than 40%, especially not more than 20% of the presulfurization. The step of contacting the hydrocarbon impregnated catalyst at a temperature of 200-500° C. will account for the remaining presulfurization of the catalyst. Thus, it is contemplated that the hydrocarbon liquid be substantially devoid of sulfurizing agents, or optionally contain any quantity of sulfurizing agents Up to the point wherein not more than 60% of the presulfurization is accounted for by the use of presulfurization agents, e.g. sulfur and/or sulphides.







EXAMPLES


Example 1 (Comparative)

[0015] here, before or during presulfuration, the catalyst is not brought into contact with a hydrocarbon compound.


[0016] An oxide catalyst containing 18.9% of MoO3 and 4.2% of CoO and an alumina support is introduced into a rotary oven supplied with a gaseous sulfur-reducing mixture of hydrogen and hydrogen sulphide at respective partial pressures of 0.8 and 0.2 bar, the gas and the solid circulating in counter current. The sulfuration of the solid is obtained by progressively increasing the temperature during the displacement of the solid inside the rotary tube, up to a maximum temperature of 330° C., the residence time inside the oven being approx. 4 hours. After cooling of the solid under reaction atmosphere and purging under nitrogen, this is brought into contact with nitrogen-diluted air so that its temperature remains below 45° C. This sulfurated catalyst can then be handled under air and re-characterized in terms of its sulfur and carbon content (LECO brand apparatus). The level of sulfuration is defined as being the relationship between the measured sulfur content, expressed on a dry basis after correcting the ignition loss at 500° C., and the theoretical content corresponding to the MoS2 and Co9S8 sulfur phases, i.e. 10.02% sulfur.


[0017] Its catalytic evaluation in hydrodesulfuration of a petroleum cut is also carried out. The catalyst test unit is supplied by a synthetic charge with a density of 0.902 and a sulfur content of 1.70% by weight, obtained by mixing equal amounts of LCO (gas oil from catalytic cracking) and direct-distillation gas oil. The hydrogen pressure is 3 MPa (30 bar) and the hourly volume rate VVH 1 h−1, the temperature 330° C. The liquid effluents are collected during a period of 40 hours in stabilized conditions and their sulfur content measured by X-ray fluorescence. The activity of order 1.5 is then calculated and compared to that obtained during a reference test. This is carried out on the oxide catalyst under the same conditions except that the start-up period includes a sulfuration stage in the presence of the direct-distillation gas oil charge to which 7% by weight of dimethyl disulphide has been added. The results are as follows:
1Level ofSulfurationLevel ofLevel ofHDSRelativeoperatingsulfurationsulfurationconversionHDSactivityTreatmentconditionbefore test %after test %%activity%ExampleEx situT = 330° C.95.299.697.004.281021gas phaseH2S-H2In situT = 330° C.100.896.904.20100liquid phaseDMDS-H2



Example 2


According to the Invention

[0018] The same CoMo/Al2O3 catalyst is impregnated at normal temperature by a gas oil (diesel oil) of direct distillation hydrocarbon cut type having initial and final boiling points 250° C. and 350° C. respectively, and a density of 0.837. The impregnated quantity is 39.0% by wt relative to the oxide weight, which corresponds to 90% of the available pore volume. After impregnation, the solid is treated in the rotary oven under the same conditions as in example 1, i.e. 330° C., 4 hours and H2/H2S mixture, then cooling under reaction atmosphere, purging under nitrogen and oxidizing passivation. The level of sulfuration of this catalyst thus obtained is 98.4% and the percentage of residual carbon expressed relative to the oxide base is 3.9% by wt. The difference between the quantity of impregnated carbon and the quantity of residual carbon represents the quantity of hydrocarbons evaporated during the sulfuration phase.


[0019] The test is carried out as described in example 1, the resulting activity for this type of preparation is improved as indicated below:
2SulfurationLevel ofLevel ofRelativeoperatingsulfurationsulfurationLevel of HDSHDSactivityTreatmentconditionbefore test %after test %conversion %activity%ExampleEx situT = 330° C.98.499.697.274.541082gas oilH2S-H2



Example 3

[0020] This example is analogous to example no 2 except that the hydrocarbon source is a 150 Neutral type base mineral oil, with a mass by volume of 0.89 g/cm3 and a viscosity of 119 mm2/s and the quantity of oil impregnated on the oxide base is 12.0% wt which corresponds to ca. 90% of the available pore volume. The analyses carried out on this catalyst show that on completion of this treatment, the solid is perfectly sulfurated and that the quantity of residual carbon is 5.2% by wt relative to the oxide base.


[0021] The level of hydrodesulfuration activity is again slightly improved compared with the references in example 1.
3SulfurationLevel ofLevel ofRelativeoperatingsulfurationsulfurationLevel of HDSHDSactivityTreatmentconditionbefore test %after test %conversion %activity%ExampleEx situT = 330° C.101.4102.097.184.451063gas oilH2S-H2



Example 4

[0022] The same CoMo/Al203 catalyst is impregnated at normal temperature by a white spirit type hydrocarbon cut having initial and final boiling points of 180° C. and 220° C. respectively, and a density of 070 The impregnated quantity is 8.1% by wt relative to the oxide weight, which corresponds to 20% of the available pore volume. After impregnation, the solid is treated in the rotary oven under the same conditions as in example 1, that is to say 330° C., 4 hours and H2/H2S mixture, then cooling under reaction atmosphere, purging under nitrogen and oxidizing passivation. The level of sulfuration of this catalyst thus obtained is 95.6% and the percentage of residual carbon expressed relative to the oxide base is 0.6% by wt. The difference between the quantity of hydrocarbons evaporated during the sulfuration phase.


[0023] The test is carried out as described in example 1, the resulting activity for this type of preparation is indicated below:
4Level ofLevel ofSulfurationLevel ofsulfurationHDSRelativeoperatingsulfurationafter testconversionHDSactivityTreatmentconditionbefore test %%%activity%ExampleEx situT = 330° C.95.6100.197.094.361044gas oilH2S-H2


[0024] The preceding examples can be repeated with similar success by substituting the generically or specifically described reactants and/or operating conditions of this invention for those used in the preceding examples.


[0025] From the foregoing description, one skilled in the art can easily ascertain the essential characteristics of this invention and, without departing from the spirit and scope thereof, can make various changes and modifications of the invention to adapt it to various usages and conditions.


Claims
  • 1. A process for ex-situ presulfurization treatment of a catalyst selected from the group consisting of CoMo/Al2O3, NiMo/Al2O3 and NiW/Al203, comprising a step-of contacting an impregnating said catalyst at substantially ambient temperature with a non-waxy liquid hydrocarbon substantially devoid of oxygen-containing hydrocarbons, and thereafter a step of contacting the hydrocarbon impregnated catalyst, at a temperature of 200-500° C., with a gaseous mixture of hydrogen and hydrogen sulfide for a sufficient time to presulfurize the catalyst, said liquid hydrocarbon optionally containing sulfurizing agents to an extent wherein not more than 60% of the total presulfurization is accounted for by said sulfurizing agents, with the remaining presulfurization being accounted for by the stage of contacting the hydrocarbon impregnated catalyst and hydrogen sulfide.
  • 2. A process according to claim 1 wherein sulfurizing agents in the liquid hydrocarbon accounts for not more than 40% of the total presulfurization.
  • 3. A process according to claim 1 wherein sulfurizing agents in the liquid hydrocarbon accounts for not more than 20% of the total presulfurization.
  • 4. A process according to claim 1 wherein sulfurizing agents in the liquid hydrocarbon accounts for not more than 5% of the total presulfurization.
  • 5. A process according to claim 1 wherein the step of contacting the hydrocarbon impregnating catalyst is conducted directly after the impregnating step.
  • 6. A process according to claim 1 wherein the presulfurization process step consists of only said impregnating and contacting steps.
  • 7. A process according to claim 1 in which the contact between the catalyst and the hydrocarbon is carried out before and during the presulfurization treatment.
  • 8. A process according to claim 1 wherein at least part of the pore volume of the catalyst is filled by impregnation with said liquid hydrocarbon.
  • 9. A process according to claim 8 in which 30 to 100% of the pore volume is filled.
  • 10. A catalyst produced according to a process of claim 1.
  • 11. A process according to claim 1 further comprising placing the resultant pre-sulfurizied catalyst in a reactor and catalytically hydroconverting a hydrocarbon feedstock in the reactor without any further sulfurization of said catalyst.
Priority Claims (1)
Number Date Country Kind
98/12 739 Oct 1998 FR
CROSS-REFERENCE TO RELATED APPLICATIONS

[0001] This application is a continuation-in-part of application Ser. No. 09/415,237 filed Oct. 12, 1999 (Attorney Docket PET-1804, priority being claimed for French Application 98/12.739 filed Oct. 12, 1998).

Continuation in Parts (1)
Number Date Country
Parent 09415237 Oct 1999 US
Child 09833215 Apr 2001 US