The present invention relates generally to gas pressurization of metal particles and more specifically to the pressurization in the presence of deuterium of metal nanoparticles 2 nm or less in size in an oxide matrix.
The study of dispersed metals has a long history because of their use as catalysts. It is well-known in the art that as the size of the metal particles decrease, the activity increases. Mainly papers concerning the ratio of hydrogen to palladium atoms and the heats of adsorption of hydrogen into palladium are referenced herein. The rate of organic chemical bond-forming and cracking reactions also vary with particle size, as is well-known in the art. However, that art does not concern the present application. Much of the art references hydrogen reactions, but for the purpose of the present application, hydrogen and deuterium are considered identical in chemical nature for the ratios of uptake with a metal catalyst. For example, others have shown that the uptake of hydrogen increases rapidly when the particle size of the dispersed palladium in an oxide matrix decreases to 1 nm or less. See, e.g., Shu-Chin Chou et al., “lsosteric Heat of Sorption of Dihydrogen on Alumina-supported Palladium,” J. Chem. Soc. Faraday Trans., 91, 949-951 (1995); Sheng-Yang Huang et al., “Chemical Activity of Palladium Clusters: Sorption of Hydrogen,” J. Phys. Chem. B, 110, 21783-21787 (2006), the entire contents of each are incorporated herein by reference. Although, they did not state the particle size specifically, data from Huang, et al., can be used to estimate the particle size and the approximate ratio of H:Pd as shown in Table 1. The heat of adsorption also increased with decreasing particle size. Others have studied a number of supports and preparation conditions and have also showed that the heat of adsorption and loading ratio increased with decreasing particle size. Pen Chou et al., “Calorimetric Heat of Adsorption Measurements on Palladium I. Influence of Crystallite Size and Support on Hydrogen Adsorption,” J. of Catalysis, 104, 1-16 (1987), the entire contents of which is incorporated herein by reference. The estimated particle size in Chou's work was greater than 1.6 nm. Aben showed that hydrogen absorption could be used to estimate particle size and that the H:Pd ratio also increased with decreasing particle size, reaching a maximum H:Pd ratio of 0.83 in his study using ion exchanged silica. P. C. Aben, “Palladium areas in supported catalysts: Determination of palladium surface areas in supported catalysts by means of hydrogen chemisorption,” Journal of Catalysis, 10 224-229 (1968), the entire contents of which are incorporated herein by reference. The smallest size that Aben measured was 2.5 nm. He also showed that high pretreatment temperatures increased particle growth, which would be detrimental to the present invention.
As the particle size must be small for high H:Pd ratios, one must disperse the particles on a support to keep them from sintering and growing too large. As noted by P. A. Sermon, even heating palladium black (a non-supported form of nano-sized palladium) to 98° C. would cause sintering of the particles. P. A. Sermon, “Characterization of palladium blacks: I. A novel hydrogen pretreatment and surface area determination of palladium,” J. of Catalysis, 24, 460-466 (1972), the entire contents of which are incorporated herein by reference.
Arata (Arata et al., Formation of Condensed Metallic Deuterium Lattice and Nuclear Fusion. Proc. Jpn. Acad., Ser. B, 78 (Ser. B): p. 57 (2002), the entire contents of which is incorporated herein by reference) has claimed excess heat when pressurizing a specially-prepared Pd—ZrO2 or Pd—Ni—ZrO2 matrix (Shin-ichi Yamaura et al., “Hydrogen absorption of nanoscale Pd particles embedded in ZrO2 matrix prepared from Zr—Pd amorphous alloys,” J. Mater. Res., 17, 1329-1334 (2002), the entire contents of which are incorporated herein by reference). His particles (ca. 5 nm) are on the size level of commercial catalysts. See Yoshinori Arachi et al., “Alternation of the Pd Lattice in Nano-Sized-Pd/ZrO2 Composite during Hydrogen Absorption,” X-ray Absorption Fine Structure—XAFS13, edited by B. Hedman and P. Pianetta, 2007 American Institute of Physics, pp. 740-742 (2007); Yoshinori et al., “Structural analysis of nano-sized-Pd/ZrO2 composite after H(D) absorption,” Solid State Ionics 177, 1861-1864 (2006), the entire contents of each are incorporated herein by reference. Furthermore, they sinter during use. Others have attempted to put palladium in zeolites and expose it to deuterium to generate excess enthalpy. See I. Parchamazad et al., “Investigations of Nanoparticle Palladium/Deuterium Systems in Zeolites,” Abstract for 14th International Conference on Condensed Matter Nuclear Science”, Hyatt Regency, Washington, D.C. Aug. 10-15, 2008, the entire contents of which are incorporated herein by reference. The incorporation of the palladium was through an organic palladium precursor and the support was calcined before use—removing the organics and likely growing the particles. Parchamazad et al. made no mention of the particle size, cycling, nor amount of excess enthalpy was made.
The aforementioned problems are overcome in the present invention which provides a method for producing excess enthalpy by impregnating metallic precursors on an oxide support that reduces sintering and particle growth; drying the impregnated support at a temperature where the particle growth is minimal; reducing the metallic precursors at a second temperature where the particle growth results in supported metallic particles 2 nm or less in size; and pressurizing the supported metallic particles in the presence of deuterium. The metal particles may comprise palladium, platinum, mixtures thereof, or mixtures of palladium and/or platinum with other elements. Also disclosed is a system for measuring excess enthalpy by placing a test material in a pressure vessel; heating the pressure vessel; evacuating the pressure vessel; introducing deuterium, hydrogen, or both into the pressure vessel; measuring the enthalpy generated during pressurization; again evacuating the pressure vessel; and measuring the enthalpy used during depressurization.
Gas pressurization of metal particles (palladium, platinum, etc.) 2 nm or less in size produces anomalous amounts of enthalpy in a reproducible manner. This enthalpy is produced in the presence of deuterium but not in the presence of hydrogen. Part of the observed, excess enthalpy can be calculated to be from D-H exchange—i.e. replacement of hydrogen atoms on the surface of the support with deuterium atoms, which is an exothermic reaction. Many control experiments have ruled out the excess enthalpy as being due to impurities in the deuterium that may be absent in the hydrogen. The source of the remaining excess enthalpy is unknown.
These and other features and advantages of the invention, as well as the invention itself, will become better understood by reference to the following detailed description, appended claims, and accompanying drawings.
The present invention is directed towards producing dispersed metal particles 2 nm or less in size in a support that reduces sintering and particle growth during pressurization-depressurization cycling. The present invention is also directed towards showing that such particles display an enthalpy difference between pressurization and depressurization with a gas and this difference is in the presence of deuterium and not hydrogen.
There are three general methods to prepare dispersed metals on supports. (1) Incipient wetness impregnation, where a solution of metal precursor is absorbed on the support. The amount of solution is just enough to wet the support. A variation on this method is wet impregnation where the amount of solution is greater than needed to just wet the support and the excess is removed at low temperature. (2) Ion exchange, where ions associated with the support are replaced with the metal ion of interest, generally using aqueous solutions of the metal of interest. (3) Sol-gel, where solutions of the metal are suspended in a growing polymer, which is generally inorganic in nature. After forming the supported metal precursor, the support is generally dried and calcined to remove water and organics. The heating may be done in air or an inert gas or in the presence of a reducing agent such as hydrogen. However, calcining the supports used in the present invention was found detrimental to excess enthalpy production. Finally, the metal ions are reduced to metal nanoparticles with a reducing agent such as hydrogen or deuterium. This may be done at elevated temperatures.
Elevated temperatures and high metal loading appear to increase particle size above 2 nm and should be avoided during the preparation of the supported metal particles used in the present invention. Preferably the present invention is performed at low temperatures—less than 500° C. and even more preferably at less than 300° C. Moreover, gradual heating may produce better results than quick heating.
Repeated pressurization-depressurization cycling of a supported catalyst can cause sintering and particle growth. This problem may be reduced by encapsulating the metal particles in a matrix such as a zeolite, a sol-gel, or a protective polymer. D. G. Narehooda et al., “X-ray diffraction and H-storage in ultra-small palladium particles,” International Journal of Hydrogen Energy, 34, 952-960 (2009), the entire contents of which are incorporated herein by reference. The use of zeolites as supports for metal particles is well-known in the art. For example, see K. P. Prasanth et al., “Hydrogen uptake in palladium and ruthenium exchanged zeolite X,” Journal of Alloys and Compounds, 466, 439-446 (2008); Kh. M. Minachev et al., “Deuterium Exchange with the Surface of Zeolite Catalysts 5. Palladium-Containing Zeolites,” Academy of Sciences of the USSR, Moscow. Translated from Izvestiya Akademii Nauk SSSR, Seriya Khimicheskaya, No. 12, pp. 2678-2682, December, 1978; J. Michalik et al., “Studies of the Interaction of Pd3+ and Pd+ with Organic Adsorbates, Water, and Molecular Oxygen in Pd—Ca—X Zeolite by Electron Spin Resonance and Electron Spin-Echo Modulation Spectroscopy,” J. Phys. Chem., 89, 4553-4560 (1985), the entire contents of each are incorporated herein by reference.
Many zeolites have a porous structure with defined size porous cages and are thus frequently used as catalysts supports. Zeolites are ideal for using ion-exchange methods of impregnation of the metal ion precursors as they can contain alkali-metal ions that may be easily exchanged for the metal ion of interest. If the preparation conditions for placing the ionic metal precursors in the zeolite and their reduction to metal particles are mild, the metal particles will grow inside the zeolite cage and the growth limited to the cage size. More severe metal growth conditions can cause the particles to grow outside of the zeolite cages or burst the crystal structures. See P. Gallezot et al., “X-Ray Diffraction Study of Palladium Y Zeolite Location of Palladium Acorns before and after Hydrogen Reduction,” Adv. Chem. Ser., 121, 66-73 (1973), the entire contents of which is incorporated herein by reference.
Measurements of excess enthalpy is conveniently done with using a gas loading apparatus. Gas loading experiments have the advantage that the system can be reversible—the heat generated upon pressurization due to the work of pressurization of the gas and the uptake of hydrogen/deuterium into the palladium matrix and spillover of that hydrogen to the support is released upon evacuation. An example of the reversibility of the work of pressurization and depressurization is shown by comparing the peaks sizes in
Excess energy (endothermic or exothermic) observed in a pressurization cycle may come from an irreversible chemical reaction. Typical reactions and processes to be considered are the initial reduction of the PdO to Pd metal and water, water (in the gas or generated) absorption by the matrix, oxidation of the hydrogen/deuterium by advantageous oxygen in the gas or absorbed on surfaces, the Joule-Thompson effect, a change in the matrix lattice with pressure, or D-H exchange with water in the matrix or surface hydroxyls. Most chemical reactions produce gaseous materials that can be monitored by sampling the gas in the cell or they consume the pressurization gas and cause a pressure drop and thereby signal their presence. For example, the oxidation of the hydrogen/deuterium by advantageous oxygen would show a pressure drop from consumption of the hydrogen/deuterium. All the reactions listed above should make themselves known or their effect (such as a change in lattice structure or reduction of PdO) should quickly be lost during repeated pressurization/depressurization cycles. Additionally, except for D-H exchange, pressurization with deuterium should produce similar amounts of heat as pressurization with hydrogen, i.e., any chemical isotope effect should be small.
In
The net or excess Enthalpy during a pressurization-depressurization cycle is defined as: Excess Enthalpy=Heat During Pressurization+Heat During Depressurization. The sign of the excess enthalpy is negative if the reaction is exothermic or positive for endothermic reactions.
Surprisingly and unexpectedly, the hydrogen pressurization-depressurization cycle showed a net enthalpy of approximately zero (−1.5 J) with a ratio of Enthalpy-in/Enthalpy-out of 1.04 (44.2/42.7) (see
Palladium chloride came from several sources but for large scale preparations, it was synthesized by dissolving Suisse 99.95% Pd in aqua regia and evaporating to dryness. The palladium-amine solution was prepared fresh each time by dissolving 1 g PdCl2 in 16 mL of water+4 mL of concentrated HCl and warming. To this deep red solution was slowly added 10 mL of concentrated ammonium hydroxide. A pink precipitate formed that slowly redissolved upon warming to the light yellow tetraamine. More ammonium hydroxide was added until a clear solution was produced. The percentage palladium in the zeolite was based on palladium metal where PdCl2 is assumed to be 60% Pd metal. Zeolite powder (50 g) (Aldrich Molecular Sieves 13×, Cat #283592) was placed in a 500 mL flask with 200 mL of distilled water and the required amount of palladium solution. The flask was refluxed overnight. The zeolite was filtered and washed three times with warm water. The material was air dried overnight then dried at various temperatures, generally 120° C. Air drying overnight or for several days appeared to produce material with the best characteristics, especially as the palladium concentration was decreased below 0.25%. Palladium in the support may be quantitated by extraction with concentrated HCl and a colorimetric assay as the PdI2 salt.
Alumina (50 g, Fischer Scientific Alumina Adsorption Cat # A-540) was placed in a 500 mL flask and slurried with water. The required amount of palladium solution, as prepared in Example 1, was added and the excess water removed on a RotoVapor system under aspirator pressure and at <60° C. to a semi-dry, flowing powder. This was air dried overnight and then dried at 120° C. for varying lengths of time.
Zeolite (20 g, Aldrich Molecular sieves, 13×, powder, Cat #283592) was placed in a 500 mL flask and slurried with approximately 100 mL of methylene chloride. 1 g of palladium (II) hexafluoroacetylacetonate (Aldrich Cat#401471, 20% Pd) dissolved in 11 mL of methylene chloride was added. The methylene chloride was removed on a RotoVapor system under aspirator pressure to a flowing powder containing 1% palladium metal. The powder was then dried in an air oven at 120° C. This material when pressurized remained tan in color, indicating that the particles remained very small.
Zeolite (20 g, Aldrich Molecular sieves, 13×, powder, Cat #283592) was placed in a 500 mL flask and slurried with approximately 50 mL of methylene chloride. 171 mg of palladium (II) acetate (Strem Chemical, Inc. Cat#46-1780, 47% Pd) dissolved in methylene chloride was added. The methylene chloride was removed on a RotoVapor system under aspirator pressure to a flowing powder containing 0.4% palladium metal. The powder was then dried in an air oven at 120° C.
Metal colloids may be made though standard procedures, such as the polyol synthesis, isolated, suspended in ethyl alcohol and dispersed on dried supports though sonication in ethyl alcohol.
Palladium loaded zeolite was prepared as in Example 1 but only air dried. To 10 g of palladium loaded zeolite was added 40 mL of distilled water and approximately 100 mg of rare earth nitrate salt. This was placed on a rocker at room temperature overnight. Then the sample was heated in a water bath for approximately 20 min., filtered, washed, and air dried before further processing.
A 100 g sample of Zeolite 13X was prepared as in Example 1 to contain 1% palladium. Approximately four 10 g samples were taken and heated to various temperatures in the following manner. All the samples were placed in an oven that was ramped to 200° C. in air. The oven was maintained at this temperature for two hours and one sample removed and cooled in a desiccator. The oven was then ramped to 300° C., held for two hours, and a second sample removed and cooled in a desiccator. The oven was then ramped to 400° C., held for two hours, and the third sample removed and cooled in a desiccator. The oven was then ramped to 500° C., held for two hours, and the fourth sample removed and cooled in a desiccator. The remaining zeolite was placed directly in a 120° C. oven for 118 hours and also cooled in a desiccator. The samples were loaded in separate cells and tested in the isothermal oven shown schematically in
The excess enthalpy was measured on a gas loading system, as shown schematically in
For operation, the test material (5-62 g of matrix) was placed in a pressure vessel, which was placed in a calorimeter (HCC-4-a Multi-cell Conduction calorimeter, Hart R & D, Inc., Mapleton, Utah). The calorimeter was calibrated electrically. After thermal equilibrium, the sample was evacuated with a roughing and then a turbo pump. Either deuterium or hydrogen was introduced. The enthalpy generated during pressurization (Enthalpy-out) was measured with the calorimeter and digitized and recorded using conventional means. The integrated area under the curve is the enthalpy of the reaction. The cell was then evacuated again with the roughing pump and turbo pump and the enthalpy taken up during depressurization (Enthalpy-in) was again measured with the calorimeter and digitized and recorded using conventional means. The formation of the metal nanoparticles was done in situ during the first pressurization-depressurization cycle and the amount of excess enthalpy was relatively large due to this chemistry occurring. A typical pressurization-depressurization cycle for hydrogen is shown in
Another system for measuring excess enthalpy is shown schematically in
For operation, the test material (5-15 g of matrix) was placed in a pressure vessel which was thermally equilibrated inside the isothermal oven. After thermal equilibrium, the sample was evacuated with a roughing pump. Either deuterium or hydrogen was introduced. The temperature change during pressurization (Temperature-out) was measured by the temperature increase on the bottom Negative Temperature Coefficient (NTC) thermistor and digitized and recorded using conventional means. The top NTC served as a control to measure variations in the oven temperature. The cell was then evacuated again with the roughing pump and the temperature change during depressurization (Temperature-in) was again digitized and recorded using conventional means. The integrated area under the curve is related to the enthalpy of the reaction by multiplication by a calibration constant. However, precise calibration is difficult between all the cells so that only the relative enthalpy is generally measured and is not needed to report the ratios given in Table 2 or Table 3. The formation of the metal nanoparticles is done in situ during the first pressurization-depressurization cycle and the amount of excess temperature is relatively large due to this chemistry occurring.
For observing excess enthalpy, the particle size should be small—2 nm or less. The matrix supporting the particles is less critical. Commercial catalysts (lines 1-3 in Table 2) have too high a loading and/or were likely made though a calcination process and thus have larger particles. Deuterium NMR is diagnostic for particle size. The commercial Pd/BaCO3 and Pd/Al2O3 show deuterium absorbances that corresponding to deuterium in bulk palladium whereas the particles made in Examples 1, 2, and 3 show only broad absorbances at NMR positions, different than those known for deuterium in bulk palladium. The commercial, supported palladium catalysts show no excess enthalpy.
Observation of nanoparticles 2 nm or less in size in a zeolite matrix is difficult by conventional Transmission Electron Microscopy (TEM) (P. C. Aben). The size of the majority of the particles made by Examples 1 and 2 were not observable by conventional TEM indicating that they were less than 5 nm in diameter. Only a few of the larger particles, which grew outside of the zeolite matrix were visible, and they were about 1-2 nm diameter. Energy dispersive X-ray (EDX) analysis showed that palladium was throughout the matrix rather than localized as indicated by the TEM. Likewise, powder X-ray diffraction was not able to see the palladium nanoparticles, also indicating that they were less than 5 nm in diameter. Aberration-corrected TEM did show a multitude of small particles 0.5-1 nm in diameter throughout the matrix, but this instrumentation was unavailable for characterization of the majority of the samples prepared.
The materials of the present application are quite distinct from those in the literature. Arata's particles (ca. 5 nm) are much larger than the particles described in the present application (Arata et al., Formation of Condensed Metallic Deuterium Lattice and Nuclear Fusion. Proc. Jpn. Acad., Ser. B, 78 (Ser. B): p. 57 (2002)). Furthermore, they sinter during use. Using materials prepared to Arata's formula and similar matrices has failed to produce excess enthalpy when tested using our pressurization procedures (Table 2, Lines 4-8).
Lower metal loadings also favor smaller particle sizes.
The above descriptions are those of the preferred embodiments of the invention. Various modifications and variations are possible in light of the above teachings without departing from the spirit and broader aspects of the invention. It is therefore to be understood that the claimed invention may be practiced otherwise than as specifically described. Any references to claim elements in the singular, for example, using the articles “a,” “an,” “the,” or “said,” are not to be construed as limiting the element to the singular.
The present application is a divisional application of U.S. application Ser. No. 12/893,325 filed by David A. Kidwell on Sep. 29, 2010 entitled “EXCESS ENTHALPY UPON PRESSURIZATION OF NANOSIZED METALS WITH DEUTERIUM,” which was a non-provisional application that claimed the benefit of provisional application Ser. No. 61/246,619 by David A. Kidwell, filed Sep. 29, 2009 entitled “ANOMALOUS HEAT GENERATION FROM DEUTERIUM (OR PLATINUM) LOADED NANOPARTICLES,” the entire contents of each are incorporated herein by reference.
Number | Date | Country | |
---|---|---|---|
61246619 | Sep 2009 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 12893325 | Sep 2010 | US |
Child | 13921195 | US |