20160032152
Composite plastic parts are of great value in industry because of their high strength and light weight. Tubular, simple, and complex structures are produced by laying on, wrapping, or coating a core mold, form, or mandrel, with the composite plastic and curing the composite at appropriately high temperature.
For some configurations, the composite material must be pressed into areas of the form or mold which is accomplished by placing the form or mold with overlaying composite material into an enclosing bag, followed by vacuum evacuation of the bag so that the outside pressure against the bag forces consolidation of the composite material and conformation with the form or mold shape. Failure to get sufficient consolidation and conformation of the composite into depressed areas of the form or mold results in unacceptable defect in the product.
Bag/breather elongation and bridging deficiencies account for the majority of defect issues in composite curing and is normally due to the fact that the outside consolidation force is not able to make intimate contact with the composite material that is to be consolidated. The insufficient force for compressing (consolidating) composite material in problem areas is mitigated by applying the expandable medium of the present invention to the problem areas so that sufficient pressure is applied during consolidation and curing.
The expandable tacky tape invention relates to a room temperature high viscosity medium such as butyl rubber or silicone, etc. that serves as a carrier for thermally expandable material such as microspheres or graphite. The thermally expandable microspheres are selected based both on the required expansion volume-duration and also the required temperature-duration that is needed for the material on which it is imparting force. If expandable graphite is utilized, the size and intercalent can be selected to define the expansion volume. Once the thermally expandable material is dispersed in the expansion medium, the material is then applied to difficult to fill or press areas that occur in the processing of plastic materials. When subsequently cured at increased temperature, the expansion within the tacky tape effectively transmits pressure sufficient to consolidate the composite material to adequately conform to the form, mold, or mandrel resulting in the desired product.
The expandable tacky tape of this invention is a material comprised of a high viscosity medium incorporating thermally expandable material, such as thermally expandable microspheres or exfoliating graphite, in sufficient volume to effectively transmit pressure to consolidate composite material to adequately conform to a form or mold when heated and cured.
For example, in an epoxy composite type curing process it is important for the thermal expansion material to apply force as the composite material is heated above 80° C. and then continue to apply force for anywhere from 5 minutes to several hours. The expandable microspheres incorporated in the viscous medium are selected from groups that start to expand anywhere from 70° C. to 220° C. and then also when they pop, depressurize, ranging from 90° C. to 250° C. In addition, the duration that the sphere is expanded can be affected by the wall thickness of the microsphere so that it is able to support the application of force for a longer period, as needed. By selecting both the type of expandable microsphere and the relative concentration that will be added to the high viscosity medium, a controlled volume material is produced that exhibits the desired thermal expansion-duration profile for the required cure cycle.
Selected expandable microspheres are incorporated into a viscous medium such as, but not limited to, butyl rubber or silicone. The concentration of microspheres is sufficient to effectively transmit sufficient pressure to consolidate the composite material to conform to the form or mold when heated under the appropriate curing conditions.
Typically, the mold or mandrel coated with composite and expandable tacky tape applied over selected areas of difficult to achieve conformation is placed into an enclosing bag and vacuum evacuated and sealed. This assembly is then cured at a higher temperature, as appropriate for the composite. The expansion of microspheres during curing transmits sufficient pressure to consolidate the composite and conform the composite to the mold, form, or mandrel.
One embodiment of the invention is comprised of a high viscosity medium such as butyl rubber within which is dispersed more than about 1%, alternatively about 2% or more, Expancel by weight. The Expancel is selected to activate at about 120° C. and not depressurize until it reaches a temperature of 180° C. The viscous medium containing dispersed Expancel is placed over raw fiber reinforced composite that overlays a mandrel. This assembly is placed into a bag, vacuum evacuated and sealed, then placed into a curing oven or autoclave and heated to an appropriate curing temperature in excess of 120° C. and less than about 140° C. The Expancel expands during the curing, applying uniform and sufficient pressure on the composite, consolidating and conforming the composite to the mandrel form.
This invention improves the accuracy of conformation to the desired shape and reduces defects in products.
The tacky tape of this invention can include any effective viscous material, including without limitation, butyl rubber, latex, urethane, urea, silicone, neoprene, or other materials known to those skilled in the art.
The tacky tape, in one example, contains heat-expanding microspheres in a concentration of about 0.1 percent to about 60 percent by weight. Depending on the viscosity of the combined viscous material with microspheres, this combination can be applied over the raw composite directly, as caulking, poured on, or sprayed to accomplish a sufficient density of microspheres to be effective.
Exfoliating graphite includes graphite and intercalent. Exfoliating graphite expands at temperatures greater than the transition temperature of the intercalent, typically greater than 185° C.
When the curing temperature for the composite is in excess of 185° C., it may be desirable to utilize exfoliating (expandable) graphite as the thermally expandable material dispersed within the viscous medium. This exfoliating graphite can be combined with the viscous medium over a range of 0.1% to about 1% or more up to about 70% by weight. At greater than 70%, the mixture becomes brittle and difficult to use. The exfoliating graphite is selected based on the use and curing conditions needed. As the graphite loading (content) of the dispersion in viscous medium increases, so does the viscosity of the mixture. A typical concentration would be 30% by weight graphite with 70% butyl rubber or silicone. This tacky tape mixture is placed over the area of composite where it is desired to produce increased pressure on the composite during curing, utilizing a resin barrier that will survive the curing temperature to separate the tacky tape from the composite. Upon heating above the transition temperature of the intercalent, the graphite begins to exfoliate layers of graphite/grapheme and the material expands. This pressure resulting from expansive force of exfoliating graphite to surrounding materials or occupation of a desired volume creates pressure transference from an outer vacuum bag or autoclave.
Depending on the viscosity of the mixture of viscous medium and exfoliating graphite, the mixture can be applied directly, as caulking, poured on, or sprayed on to achieve sufficient density of expandable material to effectively consolidate the composite and to conform the composite as required to the mandrel or form.
Examples are intended to illustrate the invention and are not limiting.
This application claims the benefits of U.S. Provisional Application 62/030,157, filed Jul. 29, 2014.