Patent Grant
8236885
The present invention relates to polymer resins. More particularly, the present invention relates to paints having a nanoparticle based pigment and a plurality of binders.
Traditionally consumers have had to choose between the superior durability offered by latex paints and the superior hiding properties of oil-based paint. Conventional latex or emulsion paints require an underlying primer coat prior to their application to provide an adequate level of blocking and to prevent bleed-through, such as of tannins. In addition, many conventional latex paints require a primer coat to provide adequate adhesion and durability for specific applications. Often, even when a primer is applied, multiple coats of the prior art paints are required to prevent an alteration of color due to the presence of the primer or bleed through of dyes and pigments from the underlying substrate. In fact, multiple applications of prior art paint will not prevent bleed-through on substrates such as cedar since the dyes and pigments, such as tannins contained in the substrates, are often water soluble and diffuse through each layer of the latex paint.
Paint typically contains four essential ingredients, namely pigment, binder, liquid and additives. Any or all of these ingredients may be a single component or may comprise multiple items. Pigment provides color to paint and also makes paint opaque, and pigment is usually of mineral or organic origin although some pigments are artificially produced. Some pigments possess little or no bulk and must be fixed on a more solid, but at the same time transparent, substance or base. “Prime” pigments provide color and opacity (opaque coverage). The most common prime pigment is titanium dioxide, which is white and is used in latex and oil-based paints.
Traditionally, pigments have also added hiding properties to paint. Specialty or extender pigments may also be used and provide bulk to the paint at a low cost. The extender pigments are often chosen for their impact on properties like scrub resistance, stain resistance and chalk resistance. Alum or clay are frequently used for this purpose. These pigments are added to the paint to provide certain characteristics such as thickness, a certain level of gloss and durability. They are usually naturally occurring products which originally were in the earth and were mined and purified for use in paint. Such pigments as calcium carbonate, talc and clay are, for example, used extensively in paints.
The binder holds the pigment and also adheres it to a surface, and a binder composition may have more than one component. In latex paint, the latex resin is the binder. Most commonly in latex paint, the binder is 100% acrylic, vinyl acrylic (polyvinyl acetate), or styreneated acrylic. The pigment particles are insoluble and merely form a suspension in the binder. The binder “binds” the pigment into a tough, continuous film and as noted above helps the paint adhere to the surface. In addition, it has been found previously that the use of 100% acrylic binder provides for maximum adhesion when wet and also provides for resistance to blistering and peeling, resistance to mildew and dirt, and alkali resistance for paint applied over fresh masonry.
Liquids carry the pigment and binders, and this liquid is the part of the paint or coatings product which evaporates. The role of the fluid is to keep the paint in a fluid form for ease of application. Once applied to the surface it evaporates leaving a uniform film which then dries to form a protective coating. The liquid used is primarily determined by the solubility of the binder. In oil-based and alkyd paints, the liquid is typically a paint thinner, and in latex paints, the liquid is typically water. Traditionally, top quality paints have less liquid and more solids (i.e. pigment & binders) as measured by percent solid.
Additives are ingredients used at low levels to provide key properties, such as but not limited to: mildew resistance, better flow and leveling, and splatter resistance. Common additives used in conventional paint formulations include rheology modifiers, surfactants, defoamers, coalescents, and biocides. Other numerous additives are well-known in the art and may be utilized as required to formulate a paint having the desired properties.
Various techniques are known in the art for producing paints having various types of sheens, i.e. “shine” or gloss. For example, by incrementally increasing pigment levels and/or by using larger pigment particles, various gloss levels can be achieved including, but not limited to flat, satin, and semi-gloss. Pigment volume concentration (PVC) is often associated with the paint finish, although various finishes may have overlapping ranges of PVC. PVC is the unit volume of pigments as a percentage of the volume of pigments plus the volume of the binder. PVC represents the relationship between durability of the coating and the amount of pigment.
Thus, there is a need for a paint composition and method of making the same to replace the traditional role of a primer and topcoat system and which is capable of providing a coating having improved properties such as, tannin blocking, hiding power, stain removal, and corrosion resistance.
The present invention relates generally to a binder composition and a paint system with superior tannin blocking, stain removal, corrosion resistance, adhesion, and various other improved properties. The present invention preferably includes a two binder system with an inorganic nano-particle pigment and with a pigmentary titanium dioxide. In one embodiment, a paint composition in accordance with the principles of the present invention further includes additives for formulating paint. In another embodiment, the present invention relates to a coating on a substrate that provides improved coverage through the use of at least two binders, an inorganic nano-particle pigment and a pigmentary titanium dioxide.
The present invention is directed in part to a polymer composition within a paint system which replaces the traditional role of a primer and a topcoat with improved properties such as tannin blocking, stain removal, adhesion, and corrosion resistance. In one embodiment, the present invention relates to a composition having a first binder, a second binder, inorganic nanoparticle pigments, and in some cases a third binder. This composition can be used in a conventional paint formulation as known in the art.
Binders for use in the present invention include those prepared by conventionally known methods. Suitable binders include, but are not limited to, 100% acrylic resins and styreneated, acrylic resins as manufactured. Preferably, the first binder is a 100% acrylic resin designed to be used as a primer vehicle, and the second binder is a 100% acrylic resin designed to be used in top coating applications.
Pigments for use in the present invention may comprise any suitable pigments known in the art. In one embodiment, the pigments of the present invention are titanium oxide or zinc oxide but other suitable pigments include nepheline syenite, bentonite, and calcium carbonate. Preferably, the primary pigment is titanium dioxide, such as commercially available pigments.
Metal oxide nanoparticle materials for use in a preferred embodiment of the invention have an average particle size of about 20-150 nanometers, although some embodiments can employ average sizes outside this range. In one preferred embodiment, the nanoparticle material is a zinc oxide material having an average particle size of about 60 nm.
A paint can be prepared in accordance with the principles of the present invention according to a number of known manufacturing methods. Generally, such methods involve the preparation of a binder or a multiple binder system, mixing of the additional ingredients, dispersing of the pigments, and adjusting the density and viscosity to desired levels. A variety of additives and diluents which are well known in the art can be mixed with the binders of the present invention to achieve certain properties in the paint or the coating. The additives may include, but are not limited to, surfactants, defoamers, rheology modifiers, coalescents, biocides, mildewcides, surfactants, and other additives well known in the art.
In one embodiment, a paint in accordance with the principles of the present invention is manufactured to a VOC (Volatile Organic Compounds) of 150 gr/L, including a 37% solid by volume, a 51% solid by weight, a 34 PVC, and a 1.5 pigment/binder ratio.
The PVC of paint in accordance with the principles of a preferred form of the present invention may vary between 4-55 by weight. In one embodiment of the present invention the paint is a “semi-gloss paint”, which has a relatively low PVC. In another embodiment of the present invention, the paint is a “satin paint”, which has a relatively high PVC. In another embodiment of the present invention, the paint is a “flat paint”, which has a relatively high PVC compared to satin paint.
Table 1 lists the general ranges of the main ingredients of a paint in accordance with the principles of a preferred embodiment. The total amount of polymer (i.e., binder) is preferably between about 30-60 gallons per 100 gallons. In one embodiment, the ratio of the first binder to the second binder is about 80:20. The first binder is, in one embodiment, a self-crosslinking polymer. The total amount of pigment, excluding the TiO2, is preferably between about 15 and about 150 pounds per 100 gallons. The TiO2 content is preferably between 0 pounds per gallon and about 360 pounds per 100 gallons. The preservatives comprise between about 5 and about 8 pounds per 100 gallons. Additional additives comprise approximately 50 and approximately 200 pounds per 100 gallons. Water comprises between about 50 and about 200 pounds per 100 gallons. The paint further includes additional solvent, aside from the water content of between about 30 and about 45 pounds per 100 gallons. In one embodiment, the nanoparticle metal oxide pigment particles have an average particle size of less than about 100 nanometers. In a further embodiment, the nanoparticle metal oxide pigment particles have an average particle size of between about 30 nanometers and about 65 nanometers.
The preferred formulation process consists of two conventional steps: the grind and the letdown. During the grind, the solvent (water), dispersant, defoamer, zinc oxide, ethylene glycol, amino alcohol, nepheline syenite, attapulgite clay are mixed together. During the letdown, the binder, the mildewcide, the rheology modifier, and the biocide, are added to the grind product.
The following non-limiting examples illustrate main components of the paint formulations and the paint formulations themselves. Table 2 provides the material ranges for the components of the paint formulations of Examples 1-4.
Example 1 was formulated using the basic components of Table 2, with the following specific components:
Example 2 was formulated using the basic components of Table 2, with the following specific components:
Example 3 was formulated using the basic components of Table 2, with the following specific components:
Example 4 was formulated using the basic components of Table 2, with the following specific components:
Various adhesion tests were performed to determine the adhesion properties of a paint in accordance with the principles of the present invention on different substances. The results of the tests compare a paint of the present invention to a typical, commercially-available paint and primer system sold for exterior use, and these tests are presented in Table 7.
In addition, a battery of tests were performed to evaluate the overall performance of a paint in accordance with the principles of the present invention at various sheens as compared to paints currently available in the marketplace. As shown in the results in Tables 8 and 9, the paint prepared in accordance with the principles of the present invention outperformed all of the other paints in the respective category.
As seen in Table 9, the satin sheen of the present invention exhibits improved leveling, roller foam, contrast, and dry adhesion.
As illustrated in
While several embodiments have been shown and described in this application, it is understood that changes and modifications can be made to the invention without departing from the invention's broader aspects.
The present application is a divisional application of U.S. patent application Ser. No. 10/914,439, filed Aug. 9, 2004 and is incorporated herein by reference in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4771086 | Martin | Sep 1988 | A |
| 4895900 | Sukejima et al. | Jan 1990 | A |
| 4927464 | Cowie | May 1990 | A |
| 5115457 | Lewandowski et al. | May 1992 | A |
| 5338354 | Melville et al. | Aug 1994 | A |
| 5385960 | Emmons et al. | Jan 1995 | A |
| 5412019 | Roulstone et al. | May 1995 | A |
| 5424077 | Lajoie | Jun 1995 | A |
| 5509960 | Simpson et al. | Apr 1996 | A |
| 5534585 | Roulstone et al. | Jul 1996 | A |
| 5643592 | Jacobson et al. | Jul 1997 | A |
| 5650002 | Bolt | Jul 1997 | A |
| 5688853 | Salter et al. | Nov 1997 | A |
| 5741844 | Nass et al. | Apr 1998 | A |
| 5747392 | Xiao et al. | May 1998 | A |
| 5770310 | Noguchi et al. | Jun 1998 | A |
| 5886069 | Bolt | Mar 1999 | A |
| 5976237 | Halko et al. | Nov 1999 | A |
| 6005044 | Karl et al. | Dec 1999 | A |
| 6040360 | Menovcik et al. | Mar 2000 | A |
| 6040913 | Johnson | Mar 2000 | A |
| 6080800 | Frey et al. | Jun 2000 | A |
| 6080802 | Emmons et al. | Jun 2000 | A |
| 6086668 | Farneth et al. | Jul 2000 | A |
| 6143064 | Virtanen | Nov 2000 | A |
| 6200375 | Guez et al. | Mar 2001 | B1 |
| 6200674 | Kumar et al. | Mar 2001 | B1 |
| 6218012 | Rota et al. | Apr 2001 | B1 |
| 6261691 | Atarashi et al. | Jul 2001 | B1 |
| 6337362 | Reynolds et al. | Jan 2002 | B1 |
| 6492435 | Miyamoto et al. | Dec 2002 | B1 |
| 6576051 | Bardman et al. | Jun 2003 | B2 |
| 6667360 | Ng et al. | Dec 2003 | B1 |
| 6727309 | Paiva et al. | Apr 2004 | B1 |
| 6740312 | Chopin et al. | May 2004 | B2 |
| 6743286 | Wen et al. | Jun 2004 | B2 |
| 20020028867 | Cottis | Mar 2002 | A1 |
| 20020112644 | Nakamura et al. | Aug 2002 | A1 |
| 20030018103 | Bardman et al. | Jan 2003 | A1 |
| 20030024437 | Wen et al. | Feb 2003 | A1 |
| 20030089278 | Bettler et al. | May 2003 | A1 |
| 20030144399 | Matta et al. | Jul 2003 | A1 |
| 20030176550 | Rediske et al. | Sep 2003 | A1 |
| 20030212187 | Cottis | Nov 2003 | A1 |
| 20030219391 | Liew et al. | Nov 2003 | A1 |
| 20040063846 | Lettmann et al. | Apr 2004 | A1 |
| 20040068035 | Paiva et al. | Apr 2004 | A1 |
| 20040138389 | Baumgart et al. | Jul 2004 | A1 |
| 20040202601 | Wen et al. | Oct 2004 | A1 |
| 20060030656 | Tarng et al. | Feb 2006 | A1 |
| 20070221097 | Tarng et al. | Sep 2007 | A1 |
| Number | Date | Country |
|---|---|---|
| 2313765 | Jan 2001 | CA |
| 0 402 932 | Dec 1990 | EP |
| 0 549 145 | Jun 1993 | EP |
| 0 615 534 | Sep 1994 | EP |
| 0 615 535 | Sep 1994 | EP |
| 0 625 541 | Nov 1994 | EP |
| 1 070 739 | Jan 2001 | EP |
| 1 270 687 | Jan 2003 | EP |
| 1 352 618 | May 1974 | GB |
| 1 532 521 | Nov 1978 | GB |
| I333971 | Dec 2010 | TW |
| Number | Date | Country | |
|---|---|---|---|
| 20100137495 A1 | Jun 2010 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10914439 | Aug 2004 | US |
| Child | 12620226 | US |