Patent Application
20170282156
This application claims the benefit of priority to an Iran patent application having a serial number 139550140003000539 filed on Apr. 09, 2016, which is incorporated by reference herein in its entirety.
The present disclosure relates generally to a method for determination of residual solvents in pharmaceutical and, in particular, relates to a method to synthesize a fiber by an electrochemical polymerization (EP).
Organic residuals in pharmaceutical products, which may be the solvent or byproducts of chemical synthesis or separation processes, have caused a great deal of concern. Developing fast, reliable and cost effective separation techniques for the organic residuals is therefore crucial. In recent years, Solid Phase Microextraction (SPME) techniques have attracted attention due to their simplicity and sensitivity. However, there are some disadvantages associated with the SPME. The disadvantages may include fiber delicacy, costly commercial fibers, and restricted sorption capacity. Hence, there is a need to prepare a more reliable, less expensive and less fragile SPME fiber to overcome the drawback of the available commercial fibers.
In one general aspect, the instant application describes a method to synthesize polyaniline/multiwall carbon nanotube (PANI/MWCNT) nanocomposite. The method includes decanting MWCNT and aniline into an electrolyte solution to prepare a PANI/MWCNT nanocomposite sorbent; coating a stainless-steel wire with platinum to create a substrate for coating the PANI/MWCNT nanocomposite sorbent thereon; inserting the platinum coated stainless-steel wire into the electrolyte solution; and coating the platinum coated stainless-steel wire with the PANI/MWCNT nanocomposite sorbent by applying a voltage to the platinum coated stainless-steel wire.
The above general aspect may include one or more of the following features. The platinum coated stainless-steel wire inserted into the electrolyte solution may be used as an anode. The method may further include inserting another wire into the electrolyte solution as a cathode. Coating the platinum coated stainless-steel wire with the PANI/MWCNT nanocomposite sorbent may include coating the platinum stainless-steel wire with the PANI-MWCNT nanocomposite sorbent by applying the voltage between the anode and the cathode to create a fiber.
Decanting MWCNT and aniline into the electrolyte solution may include decanting 0.1 g MWCNT and 0.05 M aniline into 30 mL of 0.05 M SDS electrolyte solution inside a 40 mL SPME vial with an aluminum cap to prepare the nanocomposite sorbent. The aniline may be kept in darkness and distilled prior to reaction. The applied voltage between anode and cathode may be 1.4 V for 300 seconds. The fiber may be coupled to Gas Chromatography-Flame Ionization Detector (GC-FID).
Coating the platinum coated stainless-steel wire with the PANI/MWCNT nanocomposite sorbent includes coating the platinum coated stainless-steel wire with the PANI/MWCNT nanocomposite sorbent while the anode is rotating at 200 rpm.
Coating the stainless-steel wire with platinum includes coating the stainless-steel wire with platinum via a two-electrode technique in an electrolyte solution comprising 0.42 g K2PtCl6 and 0.2 g H3BO3 in 20 mL water. The two-electrode technique may include using the stainless-steel wire as an anode and another stainless steel wire as a cathode in a platinum solution. The platinum solution may be ultra-sonicated for 10 min and added in a 25-mL container, which may be used as an electrochemical cell in a water bath at 80° C. A 1 mA current may flow between the anode and cathode for 5 seconds. The anode and cathode may be at 2 cm distance from each other.
The method may further include heat-treating the PANI/MWCNT for approximately 1 hour at 200° C. The sorbent may be configured for microextraction of the organic solvents of Benzene-Toluene-Ethyl Benzene-Xylene (BTEX) in penicillin.
Features of the subject technology are set forth in the appended claims. However, for purpose of explanation, several implementations of the subject technology are set forth in the following figure.
In the following detailed description, various examples are presented to provide a thorough understanding of inventive concepts, and various aspects thereof that are set forth by this disclosure. However, upon reading the present disclosure, it may become apparent to persons of skill that various inventive concepts and aspects thereof may be practiced without one or more details shown in the examples. In other instances, well known procedures, operations and materials have been described at a relatively high-level, without detail, to avoid unnecessarily obscuring description of inventive concepts and aspects thereof
The instant application describes a method to synthesize polyaniline/multiwall carbon nanotube (PANI/MWCNT) nanocomposite configured for sampling and deliver analyte e.g. complicated particulate matters to an analytical device e.g. gas chromatograph. The nanocomposite sorbent of the present application may be used to extract the organic compounds of Benzene-Toluene-Ethyl Benzene-Xylene (BTEX) in penicillin. The results confirm the ability of the nanocomposite sorbent of the present application in extracting volatile organic compounds (VOCs) from pharmaceutical products.
The step of synthesis of the PANI/MWCNT nanocomposite sorbent may include three steps of: 1) treatment of a substrate (Step 110), 2) synthesis of the nanosorbent (Step 112), and 3) precipitating the nanosorbent on the substrate (Step 114). In the first step 110, a stainless-steel wire may be used as the substrate. The substrate may have high surface ratio, high porosity, high mechanical resistivity, high chemical resistivity and high adhesion properties. The substrate may further be resistive against chemical and mechanical stresses. To achieve the desired properties, the surface of the stainless-steel wire may be platinized. The stainless-steel wire may be platinized using a electrophoretic deposition (EPD) method.
In one specific example, a 4 cm long stainless-steel wire may be rinsed with distilled water twice. After drying at room temperature, the stainless-steel wire may be heat-treated in a vacuum furnace at 1100° C. for 35 min. The heat-treatment may facilitate the coating process. Upon cooling down to room temperature, the stainless-steel wire may be placed in a methanol container for a short period of time. Subsequently, the stainless-steel wire may be polished and then immersed in a solution for a few seconds. The solution may be contained 20 mL HClO4 (69%) and ethanol in water (30%). The stainless-steel wire may then be immediately rinsed with distilled water twice.
The stainless-steel wire may serve as an anode and another normal stainless steel wire as the cathode in a platinum solution. The platinum solution may contain 0.42 g K2PtCl6 and 0.2 g H3BO3 in 20 mL water. The platinum solution may be ultra-sonicated for 10 min and added in a 25-mL container, which may be used as an electrochemical cell in a water bath at 80° C. The anode may be rotated at 200 rpm. A 1 mA current may flow between the anode and cathode for 5 seconds. The anode and cathode may be at 2 cm distance from each other. To achieve desired porosity, the electrochemical process may repeat 3 times and the anode may be rinsed with distilled water twice.
In the second step 112, MWCNT and M aniline may be decanted into M SDS electrolyte solution, inside a SPME vial with aluminum cap and PTFE-silicon septum to prepare the nanocomposite sorbent. In one specific example, 0.1 g MWCNT and 0.05 M aniline may be decanted into 30 mL of 0.05 M SDS electrolyte solution, inside a 40 mL SPME vial with aluminum cap and PTFE-silicon septum to prepare the nanocomposite sorbent. The nanocomposite sorbent may be the PANI/MWCNT nanocomposite sorbent. In addition, the cap of SPME vial may be kept closed and the mixture dispersed by means of an ultrasonicator. The platinum-coated stainless-steel wire of the first step 110 and the PANI/MWCNT nanocomposite sorbent of the second step 112 may be transferred to the third step 114.
In the third step 114, the tips of a platinized and a normal stainless steel wires may be passed through the opening of the vial and immersed into the suspension. Meanwhile, the wires may be connected to a DC power supply (1.4 V) for 15 min. The normal wire may be the counter electrode and platinized stainless steel wire may be the working electrode. During EPD process, the suspension may also be continuously stirred. Next, the platinized stainless steel wire may be removed from the vial.
In order to ascertain removal of pollution and remaining monomers, the platinized stainless steel wire may be washed with water and methanol several times. The EPD process may be repeated 3 times to achieve the desired thickness of the PANI/MWCNT film on the platinized stainless steel wire to form a SPME fiber. The resulting fiber may be placed into Gas Chromatography (GC) injection port for 2 h, at 250° C. for conditioning.
To provide the reader with greater clarity,
The PANI/MWCNT-coated stainless steel wire may be coupled to an analytical device e.g. GC. The gas chromatogram of the extracted BTEX by PANI/MWCNT is illustrated in
Except as stated immediately above, nothing that has been stated or illustrated is intended or should be interpreted to cause a dedication of any component, step, feature, object, benefit, advantage, or equivalent to the public, regardless of whether it is or is not recited in the claims.
It will be understood that the terms and expressions used herein have the ordinary meaning as is accorded to such terms and expressions with respect to their corresponding respective areas of inquiry and study except where specific meanings have otherwise been set forth herein. Relational terms such as first and second and the like may be used solely to distinguish one entity or action from another without necessarily requiring or implying any actual such relationship or order between such entities or actions. The terms “comprises,” “comprising,” or any other variation thereof, are intended to cover a non-exclusive inclusion, such that a process, method, article, or apparatus that comprises a list of elements does not include only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus. An element proceeded by “a” or “an” does not, without further constraints, preclude the existence of additional identical elements in the process, method, article, or apparatus that comprises the element.
The Abstract of the Disclosure is provided to allow the reader to quickly ascertain the nature of the technical disclosure. It is submitted with the understanding that it will not be used to interpret or limit the scope or meaning of the claims. In addition, in the foregoing Detailed Description, various features are grouped together in various implementations. This is for purposes of streamlining the disclosure, and is not to be interpreted as reflecting an intention that the claimed implementations require more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive subject matter lies in less than all features of a single disclosed implementation. Thus, the following claims are hereby incorporated into the Detailed Description, with each claim standing on its own as a separately claimed subject matter.