Patent Application
20170113971
The present invention relates generally to the field of composite materials and, more particularly, to extruded cement-based materials.
Cement-based materials are generally produced using large amount of water to form a slurry that is too wet to extrude.
The present invention provides an extrudable cement-based material formed from a mixture that includes cement, water, gypsum, secondary materials, reinforcement fibers and rheology modifying agent. Note that the cement may contain the gypsum such that gypsum is not added to the mixture. The extrudable cement-based material is a lightweight material that has a density in the range of about 1.4 to 2.4 g/cm3, a compressive strength in the range of about 5 to 100 MPa, and a flexural strength in the range of about 5 to 35 MPa.
In addition, the present invention provides an extrudable cement-based material that is formed from a mixture that includes cement in the range of about 0.1 to 90% by wet weight percent, water in the range of about 10 to 60%, gypsum in the range of about 0.1 to 90% by wet weight percent, a secondary material (e.g., sand, rock, fly ash, slag, silica fume, calcium carbonate, etc.) in the range of about 0.1 to 50% by wet weight percent, a reinforcement fiber in the range of about 1 to 20% by wet weight percent and a rheology modifying agent in the range of about 0.5 to 10% by wet weight percent. Note that the cement may contain the gypsum such that gypsum is not added to the mixture.
Moreover, the present invention provides a method for manufacturing an extrudable cement-based material by mixing cement, gypsum, a secondary material, a reinforcement fiber and a rheology modifying agent with water, extruding the mixture through a die using an extruder, and allowing the extruded mixture to set. Note that the cement may contain the gypsum such that gypsum is not added to the mixture.
Furthermore, the present invention provides a method of making the extrudable cement-based material (composite) by the following steps: (1) mixing about 0.1 to 90% Wt. wet cement and 0.1 to 90% Wt. wet gypsum with about 10 to 60% Wt. wet water; (2) blending the cement-gypsum-water mixture with about 0.1 to 50% Wt. wet secondary material (e.g., sand, rock, fly ash, slag, silica fume, calcium carbonate, etc.), and about 1 to 20% Wt. wet reinforcement fiber; and (3) adding about 0.5 to 10% Wt. wet rheology modifying agent to the mixture. The resulting extrudable cement-based material can then be extruded and cured (e.g., allowed to sit, heating, steam, etc.). Note that the cement may contain the gypsum such that gypsum is not added to the mixture.
The above and further advantages of the invention may be better understood by referring to the following description in conjunction with the accompanying drawings, in which:
None.
While the making and using of various embodiments of the present invention are discussed in detail below, it should be appreciated that the present invention provides many applicable inventive concepts that can be embodied in a wide variety of specific contexts. The specific embodiments discussed herein are merely illustrative of specific ways to make and use the invention and do not delimit the scope of the invention.
Ordinary Portland cement (OPC), calcium aluminate cement (CAC), Sorel cement (magnesium oxide and magnesium chloride cements), CSA cement (calcium sulphate aluminate cement), phosphate cement or other cement type known in the State-of-the-Art, in its wet state with water added before setting, can be rheologically modified into a clay-like material, which allows the use of the conventional clay production method known as extrusion.
The cement can be used as a binder with water in a composite composition in combination with a multitude of materials such as fine limestone, sand, gypsum, silica fume, fumed silica, plaster of Paris, fly ash, slag, rock, cellulose fiber, glass fiber, plastic fiber, PVA fiber, Dolanit fiber, etc., which when rheologically modified can be extruded as described above. Note that the cement may contain small amounts of gypsum (e.g., 0.3%, etc.), so adding gypsum to the mixture may not be necessary when the desired gypsum content is in the lower end of the range (see below).
The cement-gypsum-water mixture is stabilized by the addition of a rheology modifying agent typically in an amount of about 0.5 to 10% Wt. wet.
The rheology-modifying agents fall into the following categories: (1) polysaccharides and derivatives thereof, (2) proteins and derivatives thereof, and (3) synthetic organic materials. Polysaccharide rheology-modifying agents can be further subdivided into (a) cellulose-based materials and derivatives thereof, (b) starch based materials and derivatives thereof, and (c) other polysaccharides.
Suitable cellulose-based rheology-modifying agents include, for example, methylhydroxyethylcellulose, hydroxymethylethylcellulose, carboxymethylcellulose, methylcellulose, ethylcellulose, hydroxyethylcellulose, hydroxyethylpropylcellulose, etc.
Suitable starch based materials include, for example, wheat starch, pre-gelled wheat starch, potato starch, pre-gelled potato starch, amylopectin, amylose, seagel, starch acetates, starch hydroxyethyl ethers, ionic starches, long-chain alkylstarches, dextrins, amine starches, phosphate starches, and dialdehyde starches.
The currently preferred rheology-modifying agent is hydroxypropylmethylcellulose, examples of which are Methocel 240 and Methocel 240S.
For extrusion, the cement-based composite with approx. 10-60 Wt. % water of the total wet material and a suitable rheology modifying admixture is made to feel and behave similar to plastic clay. The material feels plastic/deformable to the touch and can be extruded similar to clay with the use of a clay extruder where the material is conveyed forward by an auger through a barrel and is formed continuously through a die into a final shape with form stability.
Depending on the water content and the amount of rheology modifying admixture, the extruded material can have more or less form stability.
By adding a reinforcement fiber to the material increased stability will be achieved before setting of the cement. Further, the fiber addition has been found to reduce or eliminate material shrinkage and drying shrinkage cracks during the drying phase of the production process, and further provide increased flexural strength and toughness of the dry material. The preferred type of fiber is cellulose (hardwood or softwood), plastic (based on poly vinyl alcohol or acrylic) and glass fiber; cellulose and plastic fiber is primarily used for insulation intended for below freezing or ambient temperatures, whereas glass fiber is primarily used for insulation intended for temperatures above ambient or where fire resistance is required. Also, combinations of fiber types can be applied. The preferred fiber length is from about 1 to 2 mm for the cellulose fiber, about 4 to 10 mm for the plastic fiber and about 6 to 20 mm for the glass fiber. The preferred fiber diameter is about 10 to 40 microns.
To increase the time that the cement-based material can be extruded before setting (hardening), the setting time can be retarded up to several hours with the use of small additions of suitable conventional concrete set retarder (e.g., Delvo from the company BASF). The cement-based material can be extruded by conveying the mixture through a barrel using an auger, and continuously forming the mixture into a final shape having form stability through the die using the extruder. Following extrusion, the material will within a few hours develop the initial and final setting of the finished product.
To develop the final 28 days strength of products made from OPC cement, the product is either allowed to sit around for 28 days in a humid environment, or the strength development can be accelerated within 24-48 hours by heating either by its own internal (exothermic) heat development or by steam curing such as is conventional in the State-of-the-Art.
Products made from CAC cement, Sorel cement, CSA cement, phosphate cement or other cement types will achieve its final strength in 24 hours and does not necessarily require additional curing.
After achieving the final strength development, the product is dried to generate the finished composite material. Following hardening, the hardened material can be finished as desired (e.g., cut to size, sanded, trimmed, painted, sealed, textured, imaged, etc.).
In one embodiment, the finished product can be made water repellent by spraying the product with water or solvent based silane. Such product, Protectosil BHN, is typically sold by BASF. The finished product can also be sprayed with anti-fungal or anti-microbial coatings. Moreover, the finished product can be painted, stained or textured.
The finished lightweight cement-based composite will have a density in the range of about 1.4 to 2.4 g/cm3, a compressive strength in the range of about 5 to 100 MPa, and a flexural strength in the range of about 5 to 35 MPa.
The compositional ranges are shown below:
The cement can be 0.1%, 0.2%, 0.3%, 0.4%, 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1.0%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 11%, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21%, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31%, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41%, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51%, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59%, 60%, 61%, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69%, 70%, 71%, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81%, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89% or 90% by weight or other incremental percentage between.
The water can be 10%, 11%, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21%, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31%, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41%, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51%, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59% or 60% by weight or other incremental percentage between.
The gypsum can be 0.1%, 0.2%, 0.3%, 0.4%, 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1.0%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 11%, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21%, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31%, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41%, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51%, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59%, 60%, 61%, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69%, 70%, 71%, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81%, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89% or 90% by weight or other incremental percentage between.
The secondary material can be 0.1%, 0.2%, 0.3%, 0.4%, 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1.0%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 11%, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21%, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31%, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41%, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49% or 50% by weight or other incremental percentage between.
The reinforcement fiber can be 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1.0%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 11%, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19% or 20% by weight or other incremental percentage between.
The rheology modifying agent can be 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1.0%, 1.1%, 1.2%, 1.3%, 1.4%, 1.5%, 1.6%, 1.7%, 1.8%, 1.9%, 2.0%, 2.1%, 2.2%, 2.3%, 2.4%, 2.5%, 2.6%, 2.7%, 2.8%, 2.9%, 3.0%, 3.1%, 3.2%, 3.3%, 3.4%, 3.5%, 3.6%, 3.7%, 3.8%, 3.9% 4.0% 4.1%, 4.2%, 4.3%, 4.4%, 4.5%, 4.6%, 4.7%, 4.8%, 4.9%, 5.0%, 5.1%, 5.2%, 5.3%, 5.4%, 5.5%, 5.6%, 5.7%, 5.8%, 5.9%, 6.0%, 6.1%, 6.2%, 6.3%, 6.4%, 6.5%, 6.6%, 6.7%, 6.8%, 6.9%, 7.0%, 7.1%, 7.2%, 7.3%, 7.4%, 7.5%, 7.6%, 7.7%, 7.8%, 7.9%, 8.0%, 8.1%, 8.2%, 8.3%, 8.4%, 8.5%, 8.6%, 8.7%, 8.8%, 8.9%, 9.0%, 9.1%, 9.2%, 9.3%, 9.4%, 9.5%, 9.6%, 9.7%, 9.8%, 9.9% or 10% by weight or other incremental percentage between.
The retarder can be 0.1%, 0.2%, 0.3%, 0.4%, 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1.0%, 1.1%, 1.2%, 1.3%, 1.4%, 1.5%, 1.6%, 1.7%, 1.8%, 1.9%, 2.0%, 2.1%, 2.2%, 2.3%, 2.4%, 2.5%, 2.6%, 2.7%, 2.8%, 2.9%, 3.0%, 3.1%, 3.2%, 3.3%, 3.4%, 3.5%, 3.6%, 3.7%, 3.8%, 3.9%, 4.0%, 4.1%, 4.2%, 4.3%, 4.4%, 4.5%, 4.6%, 4.7%, 4.8%, 4.9%, 5.0%, 5.1%, 5.2%, 5.3%, 5.4%, 5.5%, 5.6%, 5.7%, 5.8%, 5.9%, 6.0%, 6.1%, 6.2%, 6.3%, 6.4%, 6.5%, 6.6%, 6.7%, 6.8%, 6.9%, 7.0%, 7.1%, 7.2%, 7.3%, 7.4%, 7.5%, 7.6%, 7.7%, 7.8%, 7.9%, or 8.0% by weight or other incremental percentage between.
As a result, the present invention provides an extrudable cement-based material formed from a mixture that includes cement, water, gypsum, secondary materials, reinforcement fibers and rheology modifying agent. The extrudable cement-based material is a lightweight material that has a density in the range of about 1.4 to 2.4 g/cm3, a compressive strength in the range of about 5 to 100 MPa, and a flexural strength in the range of about 5 to 35 MPa. Note that the cement may contain the gypsum such that gypsum is not added to the mixture. In some embodiments, a retarder can be added to the mixture.
In addition, the present invention provides an extrudable cement-based material that is formed from a mixture that includes cement in the range of about 0.1 to 90% by wet weight percent, water in the range of about 10 to 60%, gypsum in the range of about 0.1 to 90% by wet weight percent, a secondary material (e.g., sand, rock, fly ash, slag, silica fume, calcium carbonate, etc.) in the range of about 0.1 to 50% by wet weight percent, a reinforcement fiber in the range of about 0.5 to 20% by wet weight percent and a rheology modifying agent in the range of about 0.5 to 10% by wet weight percent. Note that the cement may contain the gypsum such that gypsum is not added to the mixture. In some embodiments, a retarder in the range of about 0.1 to 8% Wt. wet can be added to the mixture.
Moreover, the present invention provides a method for manufacturing an extrudable cement-based material by mixing cement, a secondary material, a reinforcement fiber and a rheology modifying agent with water, extruding the mixture through a die using an extruder, and allowing the extruded mixture to set. Note that cement may contain gypsum such that gypsum is not added to the mixture, or the gypsum is mixed with the water, or both. In some embodiments, a retarder can be added to the mixture.
Furthermore, the present invention provides a method of making the extrudable cement-based material (composite) by the following steps: (1) mixing about 0.1 to 90% Wt. wet cement and 0.1 to 90% Wt. wet gypsum with about 10 to 60% Wt. wet water, wherein the cement contains the gypsum, or the gypsum is mixed with the cement and water, or both; (2) blending the cement-gypsum-water mixture with about 0.1 to 50% Wt. wet secondary material (e.g., sand, rock, fly ash, slag, silica fume, calcium carbonate, etc.), and about 0.5 to 20% Wt. wet reinforcement fiber; and (3) adding about 0.5 to 10% Wt. wet rheology modifying agent to the mixture. The resulting extrudable cement-based material can then be extruded and cured (e.g., allowed to sit, heating, steam, etc.). In some embodiments, a retarder in the range of about 0.1 to 8% Wt. wet can be added to the mixture.
In another embodiment, the extrudable cement-based material (composite) can be made by the following steps: (1) metering all the ingredients for a batch into a mixer (e.g., Eirich intensive mixer, etc.) at the same time and mixing the ingredients; (2) dumping the mixture into a hopper and extruding the mixture through a die to form an elongated sheet; (3) rolling the elongated sheet through one or more sets of calenders (e.g., two sets, etc.) to a final thickness; (4) cutting the elongated sheet into a set of individual sheets having specified lengths; (5) picking up one or more of the individual sheets and placing them in a stack on a pallet; (6) covering the stack in a plastic and an insulating cover, and placing the stacks in a curing room for a specified period of time (e.g., 24 to 48 hours or other time period necessary to cure the individual sheets); (7) finishing each individual sheet (e.g., squaring up edges, sanding to smooth surfaces and exact dimensions; and (8) applying one or more coatings or inks to each individual sheet (e.g., UV coatings, fire resistant coatings, colors, images, texturing or a combination thereof via coating or printing processes).
Although preferred embodiments of the present invention have been described in detail, it will be understood by those skilled in the art that various modifications can be made therein without departing from the spirit and scope of the invention as set forth in the appended claims.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2015/034397 | 6/5/2015 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62007984 | Jun 2014 | US |