Extruded, open-cell alkenyl aromatic polymer foam and process for making

Abstract

Disclosed is an extruded, open-cell alkenyl aromatic polymer foam useful in insulating applications. The foam has an open cell content of about 30 to about 80 percent. The foam further has in minor dimension and cross-section of greater than 0.25 inches. The foam has a high heat distortion temperature, and is particularly useful in roofing applications. Further disclosed is a process for making the open-cell foam.

Description

BACKGROUND OF THE INVENTION

This invention relates to an extruded, open-cell alkenyl aromatic polymer foam and a process for making.

Alkenyl aromatic polymer foams have been employed extensively in a variety of insulating applications. The most common types employed are closed-cell extruded foams and expanded bead foams. Extruded foams are made by forming a gel of a polymer melt and a blowing agent under heat and pressure, and extruding the gel through a die into a region of lower pressure. The lower pressure causes the gel to expand, cool, and solidify to form the foam. Bead foams are made by charging a mold with solid, expandable polymer beads containing an imbibed blowing agent or pre-expanded beads, and exposing the beads to heated air or steam to effect their expansion, coalescence, and adherence to form a unitary foam mass or article.

Heat distortion temperature of an alkenyl aromatic foam is very important when the foam is being used in a relatively high temperature application close to the service temperature limit (about 165.degree. F. for a conventional polystyrene foam) of the foam. If the heat distortion temperature of a foam is too low, it may be subject to disfigurement and/or rupture.

Extruded, closed-cell foams are more vapor-resistant, more water-resistant, and mechanically stronger than expanded bead foams. Extruded, closed-cell foams have these advantages because they are made in a solid, cellular form. Expanded bead foams, in contrast, are formed in a coalesced mass of discrete, expanded foam beads.

Expanded bead foams typically better maintain their shape in a high temperature environment than extruded, closed-cell foams because they typically have better bowing characteristics. Their bowing characteristics are better because the coalesced expanded beads allow for greater mechanical relaxation compared to the solid, cellular form of extruded, closed-cell foams.

A common high temperature application for alkenyl aromatic foams is in roofing. In roofing, the foam is typically employed below a roofing membrane, which is dark and rubber-like, and may reach service temperature limits when underneath a membrane exposed to direct sunlight in the summer months. If the foam becomes distorted, the membrane and the foam may separate to form void pockets, which leaves the membrane with less mechanical support on its undersurface. The lack of undersurface support renders the membrane more subject to rupture, which results in water leaking in the roof.

It would be desirable to have an alkenyl aromatic foam which had a vapor resistance, water resistance, and mechanical strength similar to that of extruded, closed-cell foams and bowing characteristics similar to that of expanded bead foams.

SUMMARY OF THE INVENTION

According to the present invention, there is an extruded, open-cell alkenyl aromatic polymer foam. The foam comprises an alkenyl aromatic polymer material having greater than 50 percent by weight alkenyl aromatic monomeric units. The foam has an open cell content of about 30 to about 80 percent according to ASTM D2856-87. The foam has a minor dimension in cross-section (thickness) of greater than 0.25 inches (6.4 millimeters) or more. The foam preferably has a density of about 1.5 pounds per cubic foot (pcf) to about 6.0 pcf (about 24 to about 96 kilograms per cubic meter (kg/m.sup.3)) according to ASTM D1622-88. The foam preferably has an average cell size of from about 0.08 millimeters (mm) to about 1.2 mm according to ASTM D3576-77. The foam preferably has a heat distortion temperature of from about 175.degree. F. to about 210.degree. F. according to ASTM D-2126-87. The foam is useful in a variety of insulating, cushioning, and protective applications. Since the foam has a relatively high heat distortion temperature, it is particularly useful in high-temperature insulating applications such as in roofing.

According to the present invention, there is a process for making an extruded, open-cell alkenyl aromatic polymer foam having a minor dimension and cross-section of greater than 0.25 inches (6.4 millimeters) or more. The process comprises: a) heating an alkenyl aromatic polymer material comprising more than 50 percent by weight alkenyl aromatic monomeric units to form a melt polymer material; b) incorporating into the melt polymer material an amount of a nucleating agent sufficient to result in a foam having from about 30 percent to about 80 percent open cell content; c) incorporating into the melt polymer material at an elevated pressure a blowing agent to form a foamable gel; d) cooling the foamable gel to a suitable foaming temperature; and e) extruding the foamable gel through a die into a region of lower pressure to form the foam. The foaming temperature ranges from about 118.degree. C. to about 145.degree. C. wherein the foaming temperature is from about 3.degree. C. to about 15.degree. C. higher than the highest foaming temperature for a corresponding closed-cell foam. Preferred foaming temperature is about 33.degree. C. or more higher than the glass transition temperature (according to ASTM D-3418) of the alkenyl aromatic polymer material.

DETAILED DESCRIPTION

Extruded alkenyl aromatic foams of relatively high open-cell content (about 30 to about 80 percent), relatively high cross-section thickness (greater than 0.25 inches), and relatively low density (about 1.5 pcf to about 6.0 pcf) have previously been difficult to prepare. Problems encountered included small cross-section, small cell size, low compressive strength, and higher density.

Preparing the above foams is difficult because the need for a small average cell size is incongruous with the need for desirable levels of density, cross-section thickness, and compressive strength. In making an open-cell foam, cell walls must be sufficiently thin upon expansion of the foam such that a certain proportion of them rupture so that the desired open-cell content is attained. Making sufficiently thin cell walls requires that the average cell size be relatively small, since cell wall thickness is proportional to cell size. Making a foam with a sufficiently small average cell size typically requires that relatively large amounts of a nucleating agent be employed. The large degree of nucleation to achieve small average cell size results in foam expansion which is too rapid. The rapid expansion causes premature cooling of the expanded foam, which results in small cross-section and high density.

In the prior art, open-cell polystyrene foam sheet of up to 0.25 inches (6.4 millimeters) have been prepared. Such foams range from 10 percent to 40 percent open cell, and range in density from 3 pcf to 6 pcf (48 kg/m.sup.3 to 96 kg/m.sup.3). Such foams are typically produced with an annular die, and are slit to shape. Such foams are typically employed in packaging applications, and are too thin for roofing applications.

In the present process, a relatively high foaming temperature is employed along with a nucleating agent to make the desired open-cell foams. The relatively high foaming temperature enables the open-cell foam to be made with a lower degree of nucleation than with a lower foaming temperature. The relatively higher foaming temperature results in the polymer material in the cell wall being less viscous than at a lower foaming temperature. A less viscous cell wall is more likely to rupture upon expansion of the foam, and, thus, is more likely to form a foam with higher open-cell content. The less viscous the cell wall during foam expansion, the thicker the cell wall, and, thus, the larger the cell size that may be employed in the open-cell foam.

In the present process, the foaming temperature, which is relatively higher than that for making closed-cell foams (less than 10 percent open-cell according to ASTM D2856-87), may vary from about 118.degree. C. to about 145.degree. C. Foaming temperature will vary according to nucleating agent composition and concentration, blowing agent composition and concentration, polymer material characteristics, and extrusion die design. The foaming temperature for the present open-cell foam varies from about 3.degree. C. to about 15.degree. C. and preferably about 10.degree. C. to about 15.degree. C. higher than the highest foaming temperature for a corresponding closed-cell foam (less than 10 percent open-cell according to ASTM D2856-87) of substantially equivalent density and cell size made with a substantially equivalent composition (including polymer material, nucleating agent, additives, and blowing agent) in a substantially equivalent process. A preferred foaming temperature is at about 33.degree. C. or more higher than the glass transition temperature (according to ASTM D-3418) of the alkenyl aromatic polymer material. A most preferred foaming temperature is from 135.degree. C. to 140.degree. C.

The amount of nucleating agent employed to prepare the present open-cell foam will vary according to desired cell size, foaming temperature, and composition of the nucleating agent. Open-cell content increases with increasing nucleating agent content. Useful nucleating agents include calcium carbonate, calcium stearate, talc, clay, titanium dioxide, silica, barium stearate, diatomaceous earth, mixtures of citric acid and sodium bicarbonate, and the like. Preferred nucleating agents are talc and calcium stearate. The amount of nucleating agent employed may range from about 0.01 to about 5 parts by weight per hundred parts by weight of a polymer resin. The preferred range is from 0.4 to about 3.0 parts by weight.

The present foam has a density of about 1.5 pcf to about 6.0 pcf (about 24 kg/m.sup.3 to about 96 kg/m.sup.3) and preferably a density of about 1.8 pcf to about 3.5 pcf (about 32 kg/m.sup.3 to about 48 kg/m.sup.3) according to ASTM D-1622-88.

The present foam has an average cell size of from about 0.08 millimeters (mm) to about 1.2 mm and preferably from about 0.10 mm to about 0.9 mm according to ASTM D3576-77.

In the present invention, the foam is particularly suited to be formed into a plank, desirably one having a minor dimension in cross-section (thickness) of greater than 0.25 inches (6.4 millimeters) or more and preferably greater than 0.375 inches (9.5 millimeters) or more. Further, preferably, the foam has a cross-sectional area of 30 square centimeters (cm) or more.

The present foam has an open cell content of about 30 to about 80 percent and preferably about 40 to about 60 percent according to ASTM D2856-87.

The present foam is generally prepared by heating an alkenyl aromatic polymer material to form a plasticized or melt polymer material, incorporating therein a blowing agent to form a foamable gel, and extruding the gel through a die to form the foam product. Prior to mixing with the blowing agent, the polymer material is heated to a temperature at or above its glass transition temperature or melting point. The blowing agent may be incorporated or mixed into the melt polymer material by any means known in the art such as with an extruder, mixer, blender, or the like. The blowing agent is mixed with the melt polymer material at an elevated pressure sufficient to prevent substantial expansion of the melt polymer material and to generally disperse the blowing agent homogeneously therein. A nucleating agent is blended in the polymer melt or dry blended with the polymer material prior to plasticizing or melting. The foamable gel is typically cooled to a lower temperature to optimize or attain desired physical characteristics of the foam. The gel may be cooled in the extruder or other mixing device or in separate coolers. The gel is then extruded or conveyed through a die of desired shape to a zone of reduced or lower pressure to form the foam. A preferred die design is a rectangular or slit die, which are advantageous for making plank products. The zone of lower pressure is at a pressure lower than that in which the foamable gel is maintained prior to extrusion through the die. The lower pressure may be superatmospheric or subatmospheric (evacuated or vacuum), but is preferably at an atmospheric level.

Blowing agents useful in making the present foam include inorganic agents, organic blowing agents and chemical blowing agents. Suitable inorganic blowing agents include carbon dioxide, nitrogen, argon, water, air, nitrogen, and helium. Organic blowing agents include aliphatic hydrocarbons having 1-9 carbon atoms, aliphatic alcohols having 1-3 carbon atoms, and fully and partially halogenated aliphatic hydrocarbons having 1-4 carbon atoms. Aliphatic hydrocarbons include methane, ethane, propane, n-butane, isobutane, n-pentane, isopentane, neopentane, and the like. Aliphatic alcohols include methanol, ethanol, n-propanol, and isopropanol. Fully and partially halogenated aliphatic hydrocarbons include fluorocarbons, chlorocarbons, and chlorofluorocarbons. Examples of fluorocarbons include methyl fluoride, perfluoromethane, ethyl fluoride, 1,1-difluoroethane (HFC-152a), 1,1,1-trifluoroethane (HFC-143a), 1,1,1,2-tetrafluoro-ethane (HFC-134a), pentafluoroethane, difluoromethane, perfluoroethane, 2,2-difluoropropane, 1,1,1-trifluoropropane, perfluoropropane, dichloropropane, difluoropropane, perfluorobutane, perfluorocyclobutane, and the like. Partially halogenated chlorocarbons and chlorofluorocarbons for use in this invention include methyl chloride, methylene chloride, ethyl chloride, 1,1,1-trichloroethane, 1,1-dichloro-1-fluoroethane (HCFC-141b), 1-chloro-1,1-difluoroethane (HCFC-142b), chlorodifluoromethane (HCFC-22), 1,1-dichloro-2,2,2-trifluoroethane (HCFC-123) and 1-chloro-1,2,2,2-tetrafluoroethane (HCFC-124), and the like. Fully halogenated chlorofluorocarbons include

trichloromonofluoromethane (CFC-11), dichlorodifluoromethane (CFC-12), trichlorotrifluoroethane (CFC-113), 1,1,1-trifluoroethane, pentafluoroethane, dichlorotetrafluoroethane (CFC-114), chloroheptafluoropropane, and dichlorohexafluoropropane. Chemical blowing agents include azodicarbonamide, azodiisobutyro-nitrile, benzenesulfonhydrazide, 4,4-oxybenzene sulfonyl-semicarbazide, p-toluene sulfonyl semi-carbazide, barium azodicarboxylate, N,N'-dimethyl-N,N'-dinitrosoterephthalamide, and trihydrazino triazine, and the like.

The amount of blowing agent incorporated into the polymer melt material to make a foam-forming gel is from about 0.2 to about 5.0 gram-moles per kilogram of polymer, preferably from about 0.5 to about 3.0 gram-moles per kilogram of polymer, and most preferably from about 0.7 to 2.0 gram-moles per kilogram of polymer.

The present foam comprises an alkenyl aromatic polymer material. Suitable alkenyl aromatic polymer materials include alkenyl aromatic homopolymers and copolymers of alkenyl aromatic compounds and copolymerizable ethylenically unsaturated comonomers. The alkenyl aromatic polymer material may further include minor proportions of non-alkenyl aromatic polymers. The alkenyl aromatic polymer material may be comprised solely of one or more alkenyl aromatic homopolymers, one or more alkenyl aromatic copolymers, a blend of one or more of each of alkenyl aromatic homopolymers and copolymers, or blends of any of the foregoing with a non-alkenyl aromatic polymer. Regardless of composition, the alkenyl aromatic polymer material comprises greater than 50 and preferably greater than 70 weight percent alkenyl aromatic monomeric units. Most preferably, the alkenyl aromatic polymer material is comprised entirely of alkenyl aromatic monomeric units.

Suitable alkenyl aromatic polymers include those derived from alkenyl aromatic compounds such as styrene, alphamethylstyrene, ethylstyrene, vinyl benzene, vinyl toluene, chlorostyrene, and bromostyrene. A preferred alkenyl aromatic polymer is polystyrene. Minor amounts of monoethylenically unsaturated compounds such as C.sub.2-6 alkyl acids and esters, ionomeric derivatives, and C.sub.4-6 dienes may be copolymerized with alkenyl aromatic compounds. Examples of copolymerizable compounds include acrylic acid, methacrylic acid, ethacrylic acid, maleic acid, itaconic acid, acrylonitrile, maleic anhydride, methyl acrylate, ethyl acrylate, isobutyl acrylate, n-butyl acrylate, methyl methacrylate, vinyl acetate. The foams are preferably substantially free of rubbery or rubber-like substances such as those with C.sub.4-6 diene monomeric content, including 1,3-butadiene monomeric content. The foams are further preferably substantially free of thermoset polymers such as polyurethanes. Preferred foams comprise substantially (i.e., greater than 90 percent) and most preferably entirely of polystyrene.

The present foam optionally further comprises carbon black or another infrared absorber or reflector to enhance insulating capability. The carbon black may comprise between about 1.0 and about 25 weight percent and preferably between about 4.0 and about 10.0 weight percent based upon the weight of the alkenyl aromatic polymer material in the foam. The carbon black may be of any type known in the art such as furnace black, thermal black, acetylene black, and channel black. A preferred carbon black is thermal black. A preferred thermal black has an average particle size of about 150 nanometers or more.

Small amounts of an ethylene polymer such as linear low density polyethylene or high density polyethylene may be incorporated into the foamable gel to enhance open-cell content upon extrusion and foaming.

The present foam preferably has a heat distortion temperature of from about 175.degree. F. to about 210.degree. F. and more preferably from about 190.degree. F. to about 205.degree. F. according to ASTM D-2126-87. The present foam has excellent heat distortion characteristics due to its open-cell content.

The present foam is substantially non-crosslinked. Substantially non-crosslinked means the foam is substantially free of crosslinking, but is inclusive of the slight degree of crosslinking which may occur naturally without the use of crosslinking agents or radiation. A substantially non-crosslinked foam has less than 5 percent gel per ASTM D-2765-84, method A.

Various additives may be incorporated in the present foam such as inorganic fillers, pigments, antioxidants, acid scavengers, ultraviolet absorbers, flame retardants, processing aids, extrusion aids, and the like.

The following are examples of the present invention, and are not to be construed as limiting. Unless otherwise indicated, all percentages, parts, or proportions are by weight.

EXAMPLES

Open-cell foams were prepared according to the present invention.

The apparatus for making the foam comprised an extruder, a mixer, a cooler, and a die in series. Two different extrusion systems were used. The foams represented in Table 1 were made with a 11/2 inch (3.8 centimeter) extruder. The foams represented in Table 2 were made with a 21/2 inch (6.4 centimeter) extruder.

A polystyrene resin and additives were dry-blended, and fed to the extruder to form a polymer melt. A blowing agent was added to the polymer melt in the mixer to form a foamable gel. The temperature of the foamable gel was reduced in the cooler to a suitable foaming temperature. The foamable gel was conveyed through the die into a region of reduced pressure to form the foam.

The polystyrene resin was of 200,000 weight average molecular weight according to size exclusion chromatography. Additives included talc, calcium stearate (CaSt), magnesium oxide (MgO), linear low density polyethylene (LLDPE), and high density polyethylene (HDPE). Talc was employed as a nucleating agent, CaSt as an acid scavenger, MgO as an extrusion aid, and LLDPE to enhance open-cell content in the resulting foam. Not all additives were used in every example.

Blowing agent content varied, and was selected from chlorodifluoromethane (HCFC-22), 1-chloro,-1,1-difluoroethane (HCFC-142b), ethyl chloride (EtCl), and carbon dioxide (CO.sub.2).

Open cell content was determined according to ASTM D2856-87. Cell size was determined according to ASTM D3576-77. Density was determined according to ASTM D-1622-88. Heat distortion temperature was determined per ASTM D-2126-87 by measuring dimensional change after exposing foam for one hour, two hours, or three days at different temperatures using .ltoreq.2.0% in any direction, or .ltoreq.5.0% in total volume as a criteria.

It was found that: as foaming temperature was increased, open-cell content increased; as cell size decreased, open-cell content increased; as die pressure drop increased, the open-cell content increased; and as open-cell content increased, the heat distortion temperature increased.

TABLE 1__________________________________________________________________________Blowing AgentComposition Open Heat HCFC- Die .DELTA.P Density Cell Foaming DistortionRun 142b EtCl CO.sub.2 Talc psi pcf Cell Size Content Temp. Temp. .degree.F.Number (pph) (pph) (pph) (pph) (kPa) (kg/m.sup.3) (mm) (percent) (.degree.C.) (.degree.C.)__________________________________________________________________________ 1* 7.5 2.0 1.36 0.5 1100 (7579) 1.89 (30.2) 0.14 1.2 135 200.5 (93.6) 2* 7.5 2.0 1.36 0.5 950 (6550) 1.68 (26.9) 0.22 3.6 140 203.0 (95)3 7.5 2.0 1.36 0.5 820 (5650) 1.67 (26.7) 0.14 16.0 145 211.0 (99.4)4 7.5 2.0 1.36 0.5 1260 (8681) 1.79 (28.6) 0.15 43.8 145 218.0 (103.3)5 1.0 -- 3.3 0.0 2600 (17914) 2.42 (38.7) 0.20 52.1 145 223.0 (106.1)6 1.0 -- 3.3 0.0 2670 (18396) 2.37 (37.9) 0.25 63.9 150 222.5 (105.8)7 7.5 2.0 1.36 0.5 1080 (7441) 1.91 (30.6) 0.20 82.6 155 219.5 (104.2)8 7.5 2.0 1.36 0.5 900 (6200) 1.60 (25.6) 0.15 85.2 150 221.0 (105)9 7.5 2.0 1.36 0.5 1050 (7235) 1.66 (26.6) 0.13 92.5 154 219.5 (104.2)10 7.5 2.0 1.36 0.5 1070 (7372) 1.75 (28) 0.13 92.8 149 219.5 (104.2)11 2.5 0.5 4.3 0.0 1210 (8337) 2.26 (36.2) 0.11 92.8 150 219.5 (104.2)__________________________________________________________________________ *Not an example of the present invention TABLE 2__________________________________________________________________________Blowing Agent BA HeatComposition Loading Foaming Open Distortion(pph) (gram- Temp. Die .DELTA.P Cell Density Cell Temp.Run HCFC- moles/ .degree.C. psi Additives (pph) Size pcf Content .degree.F.Number 142b CO.sub.2 100 lbs) (.degree.F.) (kPa) Talc MgO CaSt Blue (mm) (kg/m.sup.3) (percent) (.degree.C.)__________________________________________________________________________ 12* 10.0 1.75 0.138 138 (280) 920 (6340) 0.5 0.5 0.2 -- 0.11 2.05 5.6 195 (32.8) (90.5)13 10.0 1.75 0.138 144 (291) 920 (6340) 0.5 0.5 0.2 -- 0.11 1.79 68.0 -- (28.6)14 8.25 2.5 0.139 142 (287) 970 (6680) 0.5 0.5 0.2 -- 0.17 -- 46.0 210 (98.8) 15* 8.25 1.0 0.105 137 (278) 896 (6170) 4.0 -- 0.25 0.5 0.08 2.65 21.0 -- (42.4)16 8.25 1.0 0.105 140 (284) 840 (5790) 4.0 -- 0.25 0.5 0.10 2.57 58.3 213 (101) (41.1)17 4.8 2.5 0.105 137 (278) 980 (6750) 4.0 -- 0.25 0.5 0.09 2.61 55.7 213 (1001) (41.8)18 8.25 1.0 0.105 137 (278) 880 (6060) 7.0 -- 0.25 0.5 0.07 2.68 40.1 -- (42.9)__________________________________________________________________________ BA Heat Blowing Agent Loading Foaming Open DistortionRun Composition (pph) (gram- Temp. Die .DELTA.P Cell Density Cell Temp.Num- HCFC- moles/ .degree.C. psi Additives (pph) Size pcf Content .degree.F.ber 142b EtCl CO.sub.2 100 lbs) (.degree.F.) (kPa) Talc MgO CaSt LLDPE (mm) kg/m.sup.3) (percent) (.degree.C.)__________________________________________________________________________19 10.0 -- 1.75 0.138 135 930 0.5 0.5 0.2 10.0 0.20 1.90 35.2 -- (275) (6410) (30.4)20 10.0 -- 1.75 0.138 138 950 0.5 0.5 0.2 10.0 0.22 1.77 58.0 -- (280) (6550) (28.3)21 6.1 2.5 2.5 0.157 135 960 0.5 0.5 0.2 10.0 0.20 1.81 38.2 -- (275) (6610) (28.9)22 6.1 2.5 1.6 0.136 135 880 0.5 0.5 0.2 15.0 0.3 1.93 54.7 210 (275) (6060) (30.8) (98.8) 23* 6.1 2.5 1.6 0.136 132 965 0.5 0.5 0.2 15.0 0.28 2.04 23.7 -- (269) (6670) (32.6)__________________________________________________________________________BlowingAgent BA HeatComposition Loading Foaming Open Distortion(pph) (gram- Temp. Die .DELTA.P Cell Density Cell Temp.Run HCFC- moles/ .degree.C. psi Additives (pph) Size pcf Content .degree.F.Number 22 CO.sub.2 100 lbs) (.degree.F.) (kPa) Talc MgO CaSt Blue HDPE (mm) kg/m.sup.3) (percent) (.degree.C.)__________________________________________________________________________ 24* 8.0 1.0 0.116 138 1036 0.5 0.1 0.15 -- -- 0.2 2.18 5.4 195 (280) (7138) (34.9) (90.5)25 8.0 1.0 0.116 142 922 0.5 0.1 0.15 -- -- 0.14 2.11 44.1 -- (287) (6350) (35.8) 26* 8.0 1.0 0.116 137 929 2.0 -- 0.25 0.5 -- 0.1 2.4 17.0 -- (278) (6400) (38.4)27 8.0 1.0 0.116 140 846 2.0 -- 0.25 0.5 -- 0.09 2.27 46.7 213 (284) (5830) (36.3) (101)28 8.0 1.0 0.116 138 936 0.5 0.1 0.15 -- 10.0 0.3 2.47 76.0 -- (280) (6450) (39.5) 29* 8.0 1.0 0.116 132 880 0.5 0.1 0.15 -- 10.0 0.38 2.27 9.3 -- (269) (6060) (36.3)30 8.0 1.0 0.116 135 870 0.5 0.1 0.15 -- 10.0 0.41 2.24 48.3 210 (275) (6000) (35.8) (98.8)__________________________________________________________________________ BA Heat Loading Foaming Open DistortionBlowing Agent (gram- Temp. Die .DELTA.P Cell Density Cell Temp.Run Composition (pph) moles/ .degree.C. psi Additives (pph) Size pcf Content .degree.F.Number HCFC-22 Steam 100 lbs) (.degree.F.) (kPa) Talc MgO CaSt Blue (mm) (kg/m.sup.3) (percent) (.degree.C.)__________________________________________________________________________31 9.0 -- 0.105 137 925 2.0 -- 0.25 0.5 0.05 2.68 54.1 210 (278) (6370) (42.9) (98.8)32 9.0 -- 0.105 140 837 2.0 -- 0.25 0.5 0.07 2.59 61.6 -- (284) (5770) (41.4)33 9.0 -- 0.105 137 910 2.0 -- 0.25 0.5 0.09 2.33 63.0 210 (278) (6270) (37.3) (98.8)34 9.0 yes 0.105 137 925 2.0 -- 0.25 0.5 0.07 2.69 40.5 -- (278) (6370) (43.0)35 8.0 -- 0.093 138 937 7.0 0.1 0.05 -- 0.06 2.88 40.0 -- (280) (6460) (46.1)36 8.0 -- 0.093 140 855 7.0 0.1 0.05 -- 0.06 3.09 65.0 -- (284) (5890) (49.4)__________________________________________________________________________ *Not an example of the present invention

While embodiments of the foam and the process of the present invention have been shown with regard to specific details, it will be appreciated that depending upon the manufacturing process and the manufacturer's desires, the present invention may be modified by various changes while still being fairly within the scope of the novel teachings and principles herein set forth.

Claims

1. An extruded, open-cell alkenyl aromatic polymer foam, comprising:

a) an alkenyl aromatic polymer material having greater than 50 percent by weight alkenyl aromatic monomeric units,

b) a nucleating agent, the foam having an open-cell content of about 30 to about 80 percent, the foam having a minor dimension in cross-section of greater than 0.25 inches, the foam having a density of about 1.5 pcf to about 6 pcf, the foam having an average cell size of about 0.08 mm to about 1.2 mm.

2. The foam of claim 1, wherein the foam has a density of about 2.0 pcf to about 3.5 pcf.

3. The foam of claim 1, wherein the foam has an average cell size of about 0.1 mm to about 0.9 mm.

4. The foam of claim 1, wherein the foam has a heat distortion temperature of about 175.degree. F. to about 210.degree. F.

5. The foam of claim 1, wherein the foam has a heat distortion temperature of about 190.degree. F. to about 205.degree. F.

6. The foam of claim 1, wherein the foam is substantially free of rubbery polymer content and thermoset polymer content.

7. The foam of claim 1, wherein the foam has a minor dimension in cross-section of 0.375 inches or more.

8. The foam of claim 1, wherein the foam has a heat distortion temperature of about 175.degree. F. to about 210.degree. F., the foam being substantially free of C.sub.4-6 diene monomeric content and thermoset polymer content.

9. The foam of claim 1, wherein the foam has a minor dimension in cross-section of 0.375 inches or more, the foam having a density of about 2.0 pcf to about 3.5 pcf, the foam having an average cell size of about 0.1 mm to about 0.9 mm, and the foam having a heat distortion temperature of about 190.degree. F. to about 205.degree. F. the foam being substantially free of C.sub.4-6 diene monomeric content and thermoset polymer content.

10. The foam of claim 1, wherein the alkenyl aromatic polymer material consists essentially of polystyrene.

11. The foam of claim 1, wherein the alkenyl aromatic polymer material consists essentially of polystyrene.