The properties of a material are affected by the processing used to form and shape the material. Processing includes heat treatment, deformation, and casting. Heat treatment is the process of subjecting a metal or alloy to a particular schedule of heating and cooling that causes desirable physical or chemical changes. Deformation is the process of forcing a piece of material to change its thickness or shape, and some deformation techniques include forging, rolling, extruding, and drawing. Casting is the pouring of melted metal into a mold so that the metal conforms to the shape of the mold when it solidifies. Heat treatment, deformation, and casting can be used in combination, and in some cases particular alloying elements are added to influence such processing in a desirable way.
Seamless metal tubing, such as copper tubing, is typically manufactured using various methods such as cast-and-roll, up-casting, or extrusion processes. To lower the cost of manufacturing metal tubing produced by conventional extrusion and casting techniques, manufacturers increase the size of billets used for forming the metal tubing. These billets are typically 100 to 1,000 pounds or more. Manufacturers thus require very large facilities to house the specialized large-scale machinery needed to processes the billets to form metal tubing. The sheer size of the equipment, and the billets processed by the equipment, causes the extrusion process to have large start-up and maintenance costs. Furthermore, limitations of the processes, such as extruding only one billet at a time, lead to manufacturing inefficiencies including limits on the amount of tubing produced per run and system component wear caused by the constant start-up and shut-down of the manufacturing process with respect to separate runs for each billet.
Disclosed herein are systems, devices, and methods for extruding materials. In certain embodiments, the systems, devices, and methods allow for continuous extrusion of a plurality of billets. Such continuous extrusion allows for relatively smaller billets to be used to produce a desired quantity of extruded material, and therefore the scale of such continuous extrusion press systems can be smaller than conventional extrusion processes. The systems, devices, and methods allow for continuous seamless extrusion of the plurality of billets.
In one aspect, the systems, devices, and methods of the present disclosure include a method for continuously loading and extruding a plurality of billets, the method comprising loading a first billet at a receiving end of an elongate mandrel bar, transporting the first billet along the mandrel bar and through gripping elements that secure in place and prevent rotation of the mandrel bar, wherein at any given time at least one gripping element is gripping the mandrel bar, and extruding the first billet to form an extruded material by pressing the first billet through a rotating die, wherein the first billet is followed by an adjacent second billet that forms a part of the extruded material. The rotating die heats the billet as the billet advances through the rotating die. In certain implementations, a substantially constant pushing force is provided against the first billet in a direction towards the rotating die. In certain implementations, the rotation speed of the rotating die may be adjusted.
In certain implementations, the method further includes transporting the first billet along the mandrel bar and through cooling elements that clamp to the mandrel bar and deliver cooling fluid to the mandrel bar, wherein at any given time at least one cooling element is clamped to the mandrel bar. The billet may be transported along the mandrel bar via a track that intermittently moves depending on the position of the first billet relative to the gripping elements and the cooling elements. In certain implementations, the cooling fluid is transported to a mandrel bar tip provided on a second end of the mandrel bar opposite the receiving end, and the cooling fluid is returned to the cooling elements after passing through the mandrel bar tip. The mandrel bar tip may be positioned within the rotating die prior to receiving the first billet. In certain implementations the cooling fluid is water.
In certain implementations, continuously loading the plurality of billets further comprises the gripping elements alternately gripping the mandrel bar to allow one or more billets to pass through the gripping elements. In certain implementations, a downstream gripping element grips the mandrel bar and an upstream gripping element is open, and the method includes loading the one or more billets onto the mandrel bar and past the open upstream gripping element, closing the open upstream gripping element, and advancing the one or more billets to the downstream gripping element. In certain implementations, the method then includes opening the downstream gripping element, advancing the one or more billets past the open downstream gripping element, and closing the downstream gripping element.
In certain implementations, continuously loading the plurality of billets further comprises the cooling elements alternately clamping the mandrel bar to allow one or more billets to pass through the cooling elements. In certain implementations, a downstream cooling element clamps the mandrel bar and delivers cooling fluid to the mandrel bar, and an upstream cooling element is open, and the method includes loading the one or more billets onto the mandrel bar and past the open upstream cooling element, closing the open cooling gripping element, and advancing the one or more billets to the downstream cooling element. In certain implementations, the method then includes opening the downstream cooling element, advancing the one or more billets past the open downstream cooling element, and closing the downstream cooling element.
In certain implementations, the method further includes, during the extruding, preventing a portion of the first billet that has not yet entered the rotating die from rotating. A centering insert may grip the portion of the first billet to prevent rotation of said portion, and the centering insert may have an adjustable position relative to the rotating die. The centering insert may be cooled with a cooling fluid.
In certain implementations, the method further includes quenching the extruded material when the extruded material exits the rotating die. The extruded material may be quenched using water. In certain implementations, the water contacts the extruded material within approximately 1 inch of the rotating die. In certain implementations, the rotating die comprises a plurality of stacked die plates. In certain implementations, the material is copper, or the material is selected from the group consisting of copper, aluminum, nickel, titanium, brass, steel, and plastic. The plurality of billets may extend along substantially the entire length of the mandrel bar. In certain implementations, the method includes flooding the interior of the extruded material with nitrogen. Each of the plurality of billets may be loaded onto the mandrel bar by a human or by an automated loading device.
In one aspect, there is provided a method for continuously loading and extruding a plurality of billets, the method comprising receiving a first billet at a receiving end of an elongate mandrel bar, transporting the first billet along the mandrel bar and through cooling elements that clamp to the mandrel bar and deliver cooling fluid to the mandrel bar, wherein at any given time at least one cooling element is clamped to the mandrel bar, and extruding the first billet to form an extruded material by pressing the first billet through a rotating die, wherein the first billet is followed by an adjacent second billet that forms a part of the extruded material.
In certain implementations, the first billet is transported along the mandrel bar via a track that intermittently moves depending on the position of the first billet relative to the cooling elements. In certain implementations, the cooling fluid is transported to a mandrel bar tip provided on a second end of the mandrel bar opposite the receiving end, and the cooling fluid is returned to the cooling elements after passing through the mandrel bar tip. The mandrel bar tip may be positioned within the rotating die prior to receiving the first billet. In certain implementations, the cooling fluid is water.
In one aspect, an extrusion press system comprises a mandrel bar having a first end and a second end, the first end for receiving a billet having a hole therethrough and the second end coupled to a mandrel bar tip, a cooling element coupled to the mandrel bar, the cooling element having a port through which cooling fluid is delivered into the interior of the mandrel bar for cooling the mandrel bar tip, a gripping element coupled to the mandrel bar, the gripping element comprising moveable grips for securing in place and preventing rotation of the mandrel bar, and a rotating extrusion die configured to receive the billet from a centering insert having a plurality of notches that frictionally engage the billet to prevent the billet from rotating prior to entry of the billet into the rotating extrusion die, wherein the mandrel bar tip is positioned within the rotating die.
In certain implementations, the extrusion press system further includes a press-ram element having moveable first and second arms that together grip the billet and provide a substantially constant pushing force in the direction of the rotating die. The substantially constant pushing force may cause the billet to enter the rotating die at a predetermined rate. In certain implementations, the extrusion press system further comprises a motor coupled to a spindle that controls the rotation speed of the rotating extrusion die.
In certain implementations, the mandrel bar comprises an opening proximate to the cooling element ports, which opening receives the cooling fluid. The mandrel bar may further comprise notches about the mandrel bar on either side of the opening, wherein the notches are configured to receive an o-ring to substantially prevent the cooling fluid from leaking. The mandrel bar may further comprise a mandrel bar sleeve about the opening that substantially prevents the cooling fluid from leaking. In certain implementations, the mandrel bar comprises a grip portion that is correspondingly shaped to mate with the gripper of the gripping element. In certain implementations, the mandrel bar comprises an inner tube therein that receives the cooling fluid from the cooling element and through which the cooling fluid is delivered to the mandrel bar tip. The cooling fluid may be returned to the cooling element from the mandrel bar tip along a space within the mandrel bar between the outer surface of the inner tube and the inner surface of the mandrel bar. In certain implementations, the cooling fluid is water.
In certain implementations, the extrusion press system further comprises a track along which the billet is transported, wherein the track intermittently moves depending on the position of the billet relative to the gripping elements and the cooling elements. The track may include upper rolling wheels located above the track and configured to contact an upper surface of the billet. In certain implementations, the extrusion press system further comprises a quench tube provided at an exit of the rotating extrusion die. The quench tube quenches the extruded material when the extruded material exits the rotating extrusion die. In certain implementations, the extruded material is quenched using water. The water may contact the extruded material within approximately 1 inch of the rotating extrusion die.
In one aspect, a system is provided for controlling at least in part the extrusion of a plurality of billets, and the system includes a processor configured to provide instructions to an extrusion press system for loading a first billet at a receiving end of an elongate mandrel bar, transporting the first billet along the mandrel bar and through gripping elements that secure in place and prevent rotation of the mandrel bar, wherein at any given time at least one gripping element is gripping the mandrel bar, and extruding the first billet to form an extruded material by pressing the first billet through a rotating die, wherein the first billet is followed by an adjacent second billet that forms a part of the extruded material.
In certain implementations, the processor is further configured to provide instructions to an extrusion press system for intermittently moving a track upon which the first billet is placed based on the location of the first billet with respect to the gripping elements. In certain implementations, the processor is further configured to provide instructions to an extrusion press system for adjusting a rotation speed of the rotating die. In certain implementations, the processor is further configured to provide instructions to an extrusion press system for monitoring a cooling fluid delivery system. In certain implementations, the processor is further configured to provide instructions to an extrusion press system for adjusting the advancing and retraction speeds of press-rams that deliver the plurality of billets to the rotating die.
In one aspect, a non-transitory computer-readable medium is provided for controlling at least in part the extrusion of a plurality of billets, the non-transitory computer-readable medium comprising logic recorded thereon for loading a first billet at a receiving end of an elongate mandrel bar, transporting the first billet along the mandrel bar and through gripping elements that secure in place and prevent rotation of the mandrel bar, wherein at any given time at least one gripping element is gripping the mandrel bar, and extruding the first billet to form an extruded material by pressing the first billet through a rotating die, wherein the first billet is followed by an adjacent second billet that forms a part of the extruded material.
In certain implementations, the non-transitory computer-readable medium further comprises logic recorded thereon for intermittently moving a track upon which the first billet is placed based on the location of the first billet with respect to the gripping elements. In certain implementations, the non-transitory computer-readable medium further comprises logic recorded thereon for adjusting a rotation speed of the rotating die. In certain implementations, the non-transitory computer-readable medium further comprises logic recorded thereon for monitoring a cooling fluid delivery system. In certain implementations, the non-transitory computer-readable medium further comprises logic recorded thereon for adjusting the advancing and retraction speeds of press-rams that deliver the plurality of billets to the rotating die.
In one aspect, an extrusion press system comprises a mandrel bar having a first end and a second end, the first end for receiving a billet having a hole therethrough and the second end coupled to a mandrel bar tip, cooling means for delivering cooling fluid into the interior of the mandrel bar for cooling the mandrel bar tip, gripping means for securing in place and preventing rotation of the mandrel bar, and rotating extrusion means for extruding the billet, wherein the rotating extrusion means receives the billet from centering means having a plurality of notches that frictionally engage the billet to prevent the billet from rotating prior to entry of the billet into the rotating extrusion means, wherein the mandrel bar tip is positioned within the rotating extrusion means.
In certain implementations, the extrusion press system further includes pressing means for gripping the billet and providing a substantially constant pushing force in the direction of the rotating extrusion means. The substantially constant pushing force may cause the billet to enter the rotating extrusion means at a predetermined rate. In certain implementations, the extrusion press system further includes means for controlling the rotation speed of the rotating extrusion means.
In certain implementations, the mandrel bar comprises an opening proximate to the cooling means, which opening receives the cooling fluid. The mandrel bar may further comprise notches about the mandrel bar on either side of the opening, wherein the notches are configured to receive an o-ring to substantially prevent the cooling fluid from leaking. The mandrel bar may further comprise a mandrel bar sleeve about the opening that substantially prevents the cooling fluid from leaking. In certain implementations, the mandrel bar may further comprise a grip portion that is correspondingly shaped to mate with the gripping means. In certain implementations, the mandrel bar comprises an inner tube therein that receives the cooling fluid from the cooling means and through which the cooling fluid is delivered to the mandrel bar tip. The cooling fluid may be returned to the cooling means from the mandrel bar tip along a space within the mandrel bar between the outer surface of the inner tube and the inner surface of the mandrel bar. In certain implementations, the cooling fluid is water.
In certain implementations, the extrusion press system further comprises a track along which the billet is transported, wherein the track intermittently moves depending on the position of the billet relative to the gripping means and the cooling means. The track may include upper rolling wheels located above the track and configured to contact an upper surface of the billet. In certain implementations, the extrusion press system further comprises quenching means provided at an exit of the rotating extrusion means. The quenching means quenches the extruded material when the extruded material exits the rotating extrusion means. In certain implementations, the extruded material is quenched using water. The water may contact the extruded material within approximately 1 inch of the rotating extrusion means.
In one aspect, a method for continuously extruding a plurality of billets comprises transporting, along a non-rotating mandrel bar, the plurality of billets from a first end of the mandrel bar to a second end of the mandrel bar, and extruding the plurality of billets by pressing each of the plurality of billets through a rotating die, wherein friction from the rotation of the rotating die against the non-rotating plurality of billets generates heat for deforming the plurality of hollow billets, wherein a mandrel bar tip is positioned within the rotating die at the second end of the mandrel bar. In certain implementations, the method includes, during the extruding, preventing a portion of a respective one of the plurality of billets that has not yet entered the rotating die from rotating. In certain implementations, a centering insert grips the portion of the respective billet to prevent rotation of said portion, and the centering insert has an adjustable position relative to the rotating die. In certain implementations, the method further includes cooling the mandrel bar tip during the extruding.
In one aspect, a die for extruding a material includes a die body having a passage defining an entrance and an exit, with the diameter of the exit being smaller than the diameter of the entrance, and an interior surface extending around the passage from the entrance to the exit. A base is coupled to the die body, and rotation of the base causes the die body to rotate.
In certain implementations, the die body is configured to receive a billet of material for extrusion, and the billet is not pre-heated before entering the die body. Rotation of the die body creates friction between the interior surface and a billet advanced through the entrance and into the interior passage of the die body. The friction heats the billet to a temperature that is sufficient to cause deformation of the billet material. In certain implementations, the die body is configured to receive a mandrel tip through the entrance such that the mandrel tip is positionable within the interior passage of the die body. The interior surface of the die may include an angled portion configured to be positioned near a corresponding tapered outer surface of the mandrel tip. The die body is configured to receive a billet pressed through the interior passage of the die body to form an extruded product, the extruded product having an outer diameter corresponding to the diameter of the exit of the die body and an inner diameter corresponding to a diameter of the mandrel tip.
In certain implementations, the die body includes a plurality of die plates coupled together to form a stack. Each die plate has a circular bore through the center of the plate, and perimeters of the bores form the interior surface in the die body. The perimeter of the bores are angled at different angles with respect to an axis extending through the die body from the entrance to the exit. An angle of the perimeter near a front face of each plate in the die body is greater than an angle of the perimeter near a back face of an adjacent plate. The stack may include a non-uniform die plate having a bore perimeter angled at first angle near a front face of the plate and angled at a different second angle near a rear face of the plate. At least one of the die plates is formed from two different materials, with a first material forming a perimeter of a bore in the die plate and a second material forming an outer portion of the die plate. The first material may be a ceramic material, a steel, or a consumable material. In certain implementations, a front face of the die body near the entrance is configured to mate with a centering insert having a diameter substantially equal to the diameter of the entrance. The centering insert and a perimeter of the entrance may be formed from the same material. The centering insert does not rotate when the base and die rotate. In certain implementations, the base comprises a circular bore having a diameter greater than the diameter of the exit of the die body. A motor may supply a rotational force to the base.
In one aspect, a die includes a means for extruding a material, and the means for extruding includes a passage means defining an entrance and an exit, where the diameter of the exit is smaller than the diameter of the entrance, and an interior surface means extending around the passage means from the entrance to the exit. The die also has a means for coupling the means for extruding to a rotation means, and rotation of the means for coupling causes the means for extruding to rotate.
In certain implementations, the means for extruding is configured to receive a billet of material for extrusion, and the billet is not pre-heated before entering the die body. Rotation of the means for extruding creates friction between the interior surface means and a billet advanced through the entrance and into the passage means of the means for extruding. The friction heats the billet to a temperature that is sufficient to cause deformation of the billet material. The means for extruding is configured to receive a rod tip means through the entrance such that the rod tip means is positionable within the passage means of the means for extruding. The interior surface means of the means for extruding includes an angled portion configured to be positioned near a corresponding tapered outer surface of the rod tip means. The means for extruding is configured to receive a billet passed through the passage means of the means for extruding to form an extruded product, the extruded product having an outer diameter corresponding to the diameter of the exit of the means for extruding and an inner diameter corresponding to a diameter of the rod tip means.
In certain implementations, the means for extruding comprises a plurality of plate means coupled together to form a stack. Each plate means has a circular bore through the center of the plate means, and perimeter of the bores form the interior surface means in the means for extruding. The perimeters of the bores are angled at different angles with respect to an axis extending through the means for extruding from the entrance to the exit. An angle of the perimeter near a front face of each plate means in the means for extruding is greater than an angle of the perimeter near a back face of an adjacent plate means. The stack may include a non-uniform plate means having a bore perimeter angled at a first angle near a front face of the plate means and angled at a different second angle near a rear face of the plate means. At least one of the plate means is formed from two different materials, with a first material forming a perimeter of a bore in the plate means and a second material forming an outer portion of the plate means. The first material may be a ceramic material, a steel, or a consumable material. A front face of the means for extruding near the entrance is configured to mate with a centering means having a diameter substantially equal to the diameter of the entrance. The centering means and a perimeter of the entrance may be formed from the same material. Wherein the centering means does not rotate when the means for coupling and the means for extrusion rotate. The centering means includes gripping means that prevent rotation of a billet passing through the centering means. In certain implementations, the means for coupling comprises a circular bore having a diameter greater than the diameter of the exit of the means for extruding, and a power means may supply a rotational force to the means for coupling.
Variations and modifications of these embodiments will occur to those of skill in the art after reviewing this disclosure. The foregoing features and aspects may be implemented, in any combination and subcombination (including multiple dependent combinations and subcombinations), with one or more other features described herein. The various features described or illustrated herein, including any components thereof, may be combined or integrated in other systems. Moreover, certain features may be omitted or not implemented.
The foregoing and other objects and advantages will be apparent upon consideration of the following detailed description, taken in conjunction with the accompanying drawings, in which like reference characters refer to like parts throughout, and in which:
To provide an overall understanding of the systems, devices, and methods described herein, certain illustrative embodiments will be described. Although the embodiments and features described herein are specifically described for use in connection with continuous extrusion press systems, it will be understood that all the components, connection mechanisms, manufacturing methods, and other features outlined below may be combined with one another in any suitable manner and may be adapted and applied to systems to be used in other manufacturing processes, including, but not limited to cast-and-roll, up-cast, heat treatment, other extrusion, and other manufacturing processes. Furthermore, although the embodiments described herein relate to extruding metal tubing from hollow billets, it will be understood that the systems, devices, and methods herein may be adapted and applied to systems for extruding any suitable type of extruded product using billets.
The extrusion press system operates using frictional heat generated from a non-rotating hollow billet coming into contact with a rotating die to facilitate deformation and extrusion of the billet. There is thus no requirement of pre-heating the billets or the rotating die before the extrusion. The amount of heat generated is generally determined by the rate at which the billets are fed into the rotating die (e.g., controlled by the press-ram speed of the press-ram elements 130, 140 of
The rotating die forms the outer diameter of an extruded tube produced by the extrusion press system, and a mandrel bar tip positioned within the rotating die forms the inner diameter of the extruded tube. In certain embodiments, chilled process water, or any other suitable cooling fluid, is used to cool the process elements including the rotating die, the centering insert, the billets, and the gear box oil, as well as the extruded tubing product. Unlike conventional extrusion techniques, the extrusion press system of the present disclosure does not require any container within which to hold the billet for extrusion. Therefore the billets to be extruded preferably have sufficient column strength to withstand the pressure applied by the press-ram elements during the extrusion process. A programmable logic controller, or PLC, controls all or a subset of movements of the extrusion press system while the system is set in automatic mode.
The extrusion press systems, devices, and methods described herein may provide for continuous extrusion of a plurality of billets to produce a seamless extruded tubing product according to various seamless tubing standards including, for example, the ASTM-B88 Standard Specification for Seamless Copper Water Tube. The seamless extruded tubing of the present disclosure may also comply with the standards under NSF/ANSI-61 for Drinking Water System Components.
The mandrel grips 106, 108 comprise a mandrel bar gripping system 105 designed to hold the mandrel bar in place while allowing a plurality of billets to be continuously fed along and about the mandrel bar 100 to provide for continuous extrusion. The billets may be formed from any suitable material for use in extrusion press systems including, but not limited to, various metals including copper and copper alloys, or any other suitable non-ferrous metals such as aluminum, nickel, titanium, and alloys thereof, ferrous metals including steel and other iron alloys, polymers such as plastics, or any other suitable material or combinations thereof. The mandrel grips 106, 108 may be controlled by the PLC system to securely hold the mandrel bar 100 such that at any given time during the extrusion process, at least one of the mandrel grips 106, 108 is gripping the mandrel bar 100. The mandrel grips 106, 108 set the position of the mandrel bar 100 and prevent the mandrel bar 100 from rotating. When the mandrel grips 106, 108 are in a gripping or engaged position, thereby gripping the mandrel bar 100, the mandrel grips 106, 108 prevent billets from being transported along the mandrel bar 100 through the grips.
The mandrel grips 106, 108 operate by alternately gripping or engaging the mandrel bar 100 to allow one or more billets to pass through a respective mandrel grip at a given time. For example, the upstream mandrel grip 106 may release or disengage the mandrel bar 100 while the downstream mandrel grip 108 is gripping the mandrel bar 100. At any given time, at least one of the mandrel grips 106, 108 is preferably gripping or otherwise engaged with the mandrel bar 100. One or more billets queued or indexed near the upstream mandrel grip 106, or being transported along the mandrel bar 100, may pass through the open upstream mandrel grip 106. After a specified number of billets has passed through the open upstream mandrel grip 106, the gripper 106 may close and thereby return to gripping the mandrel bar 100, and the billets may be advanced to the downstream gripping element 108. The downstream gripping element 108 may remain closed, thereby gripping the mandrel bar 100, or the downstream mandrel grip 108 may open after the upstream mandrel grip 106 re-grips the mandrel bar 100. Although two mandrel grips 106, 108 are shown in the extrusion press system 10, it will be understood that any suitable number of mandrel grips may be provided.
The fluid clamps 102, 104 comprise a mandrel bar fluid delivery system 101 designed to supply cooling fluid along the interior of the mandrel bar 100 to the mandrel bar tip during the extrusion process. The fluid clamps 102, 104 also receive cooling fluid from the mandrel bar 100 that has returned from the mandrel bar tip. Any suitable cooling fluid may be used, including water, various mineral oils, brines, synthetic oils, any other suitable cooling fluid, including gaseous fluids, or any combination thereof. The fluid clamps 102, 104 may be controlled by the PLC system to continuously supply process cooling fluid to the mandrel bar during the extrusion process while allowing a plurality of billets to be continuously feed along and about the mandrel bar 100. The fluid clamps 102, 104 operate such that there is no or substantially no interruption to the supply of process cooling fluid to the mandrel bar tip during the extrusion process. Similar to the operation of the mandrel grips 106, 108 discussed above, when the fluid clamps 102, 104 are clamped to or engaged with the mandrel bar 100, the fluid clamps 102, 104 prevent billets from being transported along the mandrel bar 100 through the fluid clamps.
The fluid clamps 102, 104 operate such that at any given time during the extrusion at least one of the fluid clamps is clamped to or engaged with the mandrel bar 100 and thereby delivers cooling fluid into the mandrel bar 100 for delivery to the mandrel bar tip. When a billet passes through one of the fluid clamps 102, 104, the respective fluid clamp discontinues delivering (and receiving) cooling fluid and releases or disengages the mandrel bar 100 to allow the billet to pass therethrough before re-clamping the mandrel bar 100 and continuing to deliver (and receive) cooling fluid. While one of the fluid clamps 102, 104 is unclamped or disengaged from the mandrel bar 100, the other fluid clamp continues to deliver cooling fluid to the mandrel bar.
For example, the upstream fluid clamp 102 may release the mandrel bar 100 while the downstream fluid clamp 104 is clamped to the mandrel bar 100. At any given time, at least one of the fluid clamps 102, 104 is preferably clamped to the mandrel bar 100 to continuously deliver cooling fluid. One or more billets queued or indexed near the upstream fluid clamp 102, or being transported along the mandrel bar 100, may pass through the open upstream fluid clamp 102. After a specified number of billets has passed through the open upstream fluid clamp 102, the fluid clamp 102 may close and thereby return to clamping the mandrel bar 100 and delivering cooling fluid, and the billets may be advanced to the downstream fluid clamp 104. The downstream fluid clamp 104 may remain closed, thereby clamping the mandrel bar 100, or the downstream fluid clamp 104 may open after the upstream fluid clamp 102 re-clamps to the mandrel bar 100. Although two fluid clamps 102, 104 are shown in the extrusion press system 10, it will be understood that any suitable number of fluid clamps may be provided.
The billet delivery system 20 includes the billet feed track assembly 110 of
The billet feed track assembly 110 includes a chain or a track 202 positioned about sprockets 204 and 205. One or more of the sprockets 204, 205 may be coupled to a motor (not shown) that operates to move or cycle the track 202 in a loading direction, dz. The track 202 and sprockets 204, 205 are supported by a base rail 206 and a low rail 208, which together couple to a frame 210. An upper portion 210a of the frame 210 includes top roller wheels 212 that provide an upper bound for a passing billet 30. For example, as show in
Returning to
As discussed above, the extrusion press system 10 includes a platen structure section 90 having an entry platen 120 and a rear die platen 122, press-ram platens 130 and 140, a centering platen 150, and a rotating die 160 pressed against the rear die platen 122. Near the entry platen 120 is the press-ram assembly 141 that includes a first press-ram platen 130 and a second press-ram platen 140. The first and second press-ram platens 130, 140 feed billets into the centering platen 150, which grips the billets and prevents the billets from rotating prior to entering the rotating die 160, which presses against the rear die platen 122. The entry platen 120 and the rear die platen 122 are coupled by a series of tie rods 124 that act as guides for the press-ram platens 130, 140 and the centering platen 150, each of which includes bearings 126a, 126b, 126c that move along the tie rods 124. The rear die platen 122 and the entry platen 120 have mounting locations 127 through which the tie rods 124 are fixed. The entry platen 120, rear die platen 122, and tie rod structure 124 are supported by the frame 190. The frame 190 also holds the spindle 172 and motor 170. At the exit of the rotating die 160 is a quench tube 180 for rapidly cooling the extruded tubing.
The press-ram platens 130, 140 operate by gripping the billets and providing a substantially constant pushing force in the direction of the extrusion die stack 160. At any given time at least one of the press-ram platens 130, 140 grips a billet and advances the billet along the mandrel bar 100 to provide the constant pushing force. The press-ram platens 130, 140 form the final part of the billet delivery subsystem 20 before the billet enters the centering platen 150 and the rotating die 160 of the extrusion subsystem 40. Similar to the billet feed track section before the entry platen 120, the section prior to the press-ram platens 130, 140 preferably continuously indexes the billets to minimize any gaps between a billet that is gripped the press-ram platens 130, 140 and the next billet.
As discussed above, the press-rams 130, 140 continuously push billets into the rotating die 160. The press-rams 130, 140 alternate gripping and advancing billets towards and into the rotating die 160 and then ungripping the advanced billets and retracting for the next gripping/advancing cycle. There is preferably an overlap between the time when one press-ram stops pushing and the other press-ram is about to start pushing so that there is always pressure on the rotating die 160. The press-rams 130, 140 advance and retract via press-ram cylinders coupled to the respective press-ram. As shown there are two press-ram cylinders 132, 142 per press-ram. A first set of press-ram cylinders 132 is located to the left and right of the entry platen 120 (although the right-side press-ram cylinder is hidden from view by the left-side press-ram cylinder). The first set of press-ram cylinders 132 couples with the first press-ram platen 130 and is configured to move the first press-ram 130 along the tie rods 124 as the first press-ram 130 advances billets and then retracts for subsequent billets. A second set of press-ram cylinders 142 is located on the top and bottom of the entry platen 120. The second set of press-ram cylinders 142 couples with the second press-ram platen 140 and is configured to move the second press-ram 140 along the tie rods 124 as the second press-ram 140 advances billets and then retracts for subsequent billets. Although two press-ram cylinders are shown for each of the first and second press-ram platens 130, 140, it will be understood that any suitable number of press-ram cylinders may be provided. In certain embodiments, press-ram cylinders may be coupled to both press-rams 130, 140.
The centering platen 150 receives billets advanced by the press-rams 130, 140 and holds the billets to prevent their rotation during the extrusion process prior to entry of the billets into the rotating die 160. When the centering platen 150 is positioned in place for the extrusion process, the centering platen 150 becomes part of the extrusion die 160. That is, a centering insert 152 of the centering platen 150 substantially abuts the rotating die 160. The centering platen 150 itself, however, and the components therein including the centering insert 152, do not rotate with the rotating die 160. The centering platen 150 prevents billets that are no longer held by the second press-ram 150 from rotating while the die 160 rotates by gripping the billets and thereby preventing the billets from rotating prior to entry of the billets into the rotating die 160.
The rotating die 160 may have a unibody design, or may include a plurality of die plates stacked together. In certain embodiments, the die includes a base plate, a final plate, a second intermediate plate, a first intermediate plate, an entry plate, and a steel end holder, and the die plates are bolted together to form the die 160. The rotating die 160 is bolted to or otherwise coupled with the spindle 172, which is operated by the motor 170. A gear box is bolted to the rear die platen 122 and contains the spindle 172 as well as the drive chain, motor drive gear, gear oil reservoir, and gear oil heat exchanger, which are not shown in
At the extrusion end of the extrusion press system 10 is a quench box 185 bolted or otherwise coupled to the exit side of the gear box on the rear die platen 122. In certain embodiments, within the quench box 185 is a quench tube 180 for rapidly quenching or cooling the extruded material as it exits the rotating die 160. Water may be used as the quenching or cooling fluid, and the water may contact the extruded material sometime after the exit of the extruded material from the rotating die 160. For example, in certain embodiments, the extruded material is quenched with cooling fluid within approximately 1 inch of exiting the rotating die 160. Any suitable cooling fluid may be used for quenching an extruded material, including water, various mineral oils, brines, synthetic oils, any other suitable cooling fluid, including gaseous fluids, or any combination thereof. The quench tube 180 may be formed of one or more tubes having a channel therein for delivering the cooling fluid to the extruded material. In certain embodiments, the quench tube 180 further includes an end cap or other structure through which the cooling fluid is delivered to the extruded material. Any suitable quench tube may be used the extrusion press system of this disclosure, including, for example, the quench tubes described in copending, commonly-assigned U.S. patent application Ser. No. [______] (Attorney Docket No. 109965-0006-101), filed concurrently herewith, and entitled “SYSTEMS AND METHODS FOR COOLING EXTRUDED MATERIALS,” the disclosure of which is hereby incorporated by reference herein in its entirety.
In certain embodiments, nitrogen gas, or another suitable inert gas, is delivered to the interior of an extruded material as the material exits the rotating die. For example, nitrogen gas may be delivered to the interior of extruded tubing using a cap placed on the leading end of the extruded tubing as it exits the rotating die. Injecting gaseous or liquid nitrogen into the rotating die assembly, or the interior of the extruded material itself, can minimize oxide formation by displacing the oxygen-laden air.
Although not shown in
The various components of the extrusion press system 10 of
In certain embodiments, the clamping surfaces 314a and 318a of the blank fluid clamp 314 and the insert 318 of the inlet/outlet fluid clamp 312 are structured to mate with a corresponding portion of a mandrel bar.
The inset of the mandrel bar portion 342 shows port section 342a with an opening or port 344 for receiving and/or returning cooling fluid from the fluid clamp 102. The mandrel port 344 is sized to correspond with the respective port 320 of the fluid clamp 102. About the mandrel port 344 are a series of notches 346 receiving o-rings and thereby preventing cooling fluid from escaping or otherwise leaking from the mandrel bar 340 via the port 344. The two mandrel bar portions 342, 348 correspond, for example, to the portions of the mandrel bar that interface with the two fluid clamps 102, 104 of the extrusion press system 10 of
Also shown in
The extrusion press system 10 includes a cooling system 400 for cooling the various components of the press system 10 during operation. Although the cooling system 400 of
In certain embodiments, the top grip 510 and the bottom grip 512 are structured to mate with a corresponding portion of a mandrel bar, such as the mandrel bar portion 518 of the mandrel bar 540.
A perspective view of the portion 518 of the mandrel bar 540 is shown in
In certain embodiments, the mandrel bar extends along the length of the extrusion press system 10, terminating at a mandrel bar tip positioned within the rotating die. The mandrel bar may have a substantially continuous cross-section along its length or may have portions thereof (such as portions 342, 348, 518 and mandrel bar sleeve 360) shaped for interfacing with components of the press system such as the fluid clamps 102, 104 and the mandrel grips 106, 108. In certain embodiments, the mandrel bar may be modular and may comprise a plurality of attachable sections that together form the mandrel bar for use with an extrusion press system. For example, the mandrel bar 540 of
In certain embodiments, one or both of the first and second press-rams 130, 140 may include centering links. For example, centering links may be coupled to the link arms 622, 624 and/or the cylinder 626 of the first press-ram 130 for synchronizing movement of the respective arms of the press-ram 130 about the pivot 625. This prevents, for example, operation of the cylinder 626 from extending one arm about the pivot point 625 while the other arm remains still. When the movement of the arms 622, 624 is synchronized about the pivot 625 using the centering links, both arms move together when gripping and releasing the billets.
A billet pressed through the die 160 is extruded by heat generated from friction and forces applied to the billet by an interior surface of the die 160. Before a billet is pressed into the die 160, the die and the centering insert 152 are pressed together to form a sealed mating interface for extrusion, and this orientation is shown in
While the billet 702 and centering insert 152 do not rotate during the extrusion process, the die 160 and base 700 to which the body of the die is connected are rotated by a motor-driven spindle. As the billet 702 is advanced through the centering insert 152, it passes through the entrance 716 of the die 160 and contacts an interior surface of the die, shown in more detail in
The interior surface of the die 160 exhibits a tapered profile that narrows the interior passage through the die 160 from the entrance 716 to an exit 718. Thus, when force is applied to the billet 702 to press the billet through the die 160, the material of the billet 702 is extruded as the outer diameter of the material is forced to decrease to pass through the interior of the die 160 from entrance 716 to exit 718. The dimensions of the die 160 and interaction between the interior surface of the die 160 and the billet 702 is described in more detail below with respect to
The cross section view of the die 160 in
To reduce the cost-increasing effect of the friction wear on each of the plates in the die 160, the plates may be designed to focus the wear on one or more plates that are replaced more often than the remaining plates. Such a design may allow the die to be operated by producing multiple copies of a single plate and a single plate for the rest of the plates in the stack. For example, in the stack shown in
In addition to focusing work and stress within the die 160, mechanical and thermal properties of the billet materials may dictate the number and design of plates in a die assembly. For example, a billet material having high thermal conductivity may heat up to a deformable temperature more quickly than a material having a low thermal conductivity, and thus a shorter die with fewer plates may be used for the high conductivity material. In addition, the tapering angles of the inner surface of a die may be greater for the high conductivity material as a result of the quicker heating of the billet. In other implementations, dies of equal size having the same number of plates may be used, and the tapering angles of the dies may differ to accommodate the different thermal properties and heat the billets to a deformable temperature while still focusing work and wear to a desired area of the die surface and the surface of a mandrel tip within the die, or while spreading the work and wear over the surfaces.
Whether a unibody or die plate stack die is implemented, a billet pressed through the die 160 produces an extruded tube product through exit 718 of the die 160 having an outer diameter that is similar to the diameter d1, the diameter at the narrowest portion of interior passage 720. The inner diameter of the extruded product is selected by advancing the mandrel bar 100 into the die 160 with a mandrel bar tip, such as mandrel bar tip 800, having an end dimension selected to create the inner diameter of the tube product at the end of the mandrel bar 100.
As the billet 702 is advanced over the middle portion 732 of the mandrel bar tip 800, the taper of the interior surface 726 applies a compression force to the outer surface of the billet 702 that presses the billet 702 inwards towards the mandrel bar tip 800. Because the billet 702 is in a plastic deformation state, the material in the billet extrudes in the direction of end portion 734 of mandrel bar tip 800 as the die 160 decreases the outer diameter of the billet 702 from the original diameter d2 to a final outer diameter d3. When the billet 702 reaches the middle portion 732, the taper of the mandrel bar tip 800 towards the end portion 734 causes the inner diameter of the billet 702 to extrude and decrease from the original diameter d4 as the billet advances further over the mandrel bar tip 800. The tapered surface of the mandrel bar tip 800 in the middle portion 732 may be positioned near a sharp angled portion of the inner surface 726, for example near a first sharp angle portion 740, as discussed above with respect to second intermediate plate 712. This orientation positions the tapered middle portion 732, and the area in which the inner diameter of a billet passing over the mandrel bar tip 800 is decreased, in the same location as the greatest compression force produced by inner surface 726 over die 160.
When the extruding billet 702 reaches the end portion 734, the inner diameter of the billet is reduced from the original diameter d4 to the final diameter d5 of the end tubing product 728. As the billet 702 passes over the end portion 734, the outer diameter of the billet 702 continues to decrease to the final outer diameter d3 when the extruded tubing product 728 exits the die at exit 718. At the point of exit, the formation of the extruded product 728 is complete. Due to the friction and heating within the die 160, the product 728 is at a heightened temperature upon exit from the die 160, and a cooling element may be applied to prevent further deformation or increase operational safety of the extrusion press, eliminate the escape of extruded material, or maintain desired material characteristics. A bore 736 in the base plate 700 is shown in
The mandrel bar tip 800 may have any suitable diameter along the extrusion surfaces 804 as well as the terminal contact surface 806. For example, in certain embodiments, as shown by mandrel bar tip 820, the terminal contact surface 826 may have a setting diameter D2 that is relative larger than the setting diameter D1 of mandrel bar tip 800. In certain embodiments, each of the contact surfaces 804 of the mandrel bar tip 800 may correspond to the respective profile of the various die plates within the rotating die.
Process 1200 begins at step 1210, where one or more billets are loaded about the receiving end 100a of the mandrel bar near the first or upstream fluid clamp 102. Each of the billets of the present disclosure is hollow along the length of the billet, which allows the billets to be placed onto the stationary mandrel bar 100 such that the billet moves and is transported along and about the mandrel bar 100. In certain embodiments, the billet delivery subsystem 20 of the extrusion press system 10 may include a billet delivery table with a plurality of billets prepped for loading onto the extrusion press system 10. The billets may be loaded automatically by an automated process or may be loaded by hand. Once loaded, the billets may be transported along the mandrel bar by a billet feed track assembly such as the track assembly 110 shown in
At step 1220 the billets are transported along the mandrel bar and through the fluid clamps, which when engaged to the mandrel bar deliver cooling fluid to the mandrel bar tip. At any given time, at least one of the fluid clamps is preferably clamped to or otherwise engaged with the mandrel bar to provide a continuous or substantially continuous delivery of cooling fluid to the mandrel bar. The steps for passing one or more billets through the respective fluid clamps of the extrusion press system are shown in
The process 1220 with respect to the second fluid clamp is substantially similar to that performed by the PLC system for the first fluid clamp and is also shown in
Returning to process 1200 of
The process 1230 with respect to the second mandrel grip is substantially similar to that performed by the PLC system for the first mandrel grip and is also shown in
Returning to process 1200 of
At step 1250 the billets are extruded to form an extruded material. The press-rams of step 1240 advance billets through a centering insert (e.g., centering insert 152 of
At step 1260 the extruded material is quenched as it exits the rotating die. This step includes rapidly cooling the extruded material by spraying cooling fluid such as water, or any other suitable cooling fluid, at a high velocity from a quench tube onto the extruded material. Despite the temperatures generated during the extrusion process of step 1250, upon exiting the quench tube, the extruded material is relatively cool enough to the touch that it can be handled without causing burns. Furthermore, in certain embodiments, nitrogen gas, or another suitable inert gas, is delivered to the interior of the extruded material as the material exits the rotating die. For example, nitrogen gas may be delivered to the interior of extruded tubing using a cap placed on the tubing as it exits the rotating die. Injecting gaseous or liquid nitrogen into the rotating die assembly, or the interior of the extruded material itself, can minimize oxide formation by displacing the oxygen-laden air.
It will be understood that as one or more billets proceed through the process 1200 thus described, other billets may be advancing through the extrusion press system at any of the other steps of the process 1200. For example, as a first set of billets, including one or more billets, is transported through the fluid clamps at step 1220, another set of billets, including one or more billets, may be contemporaneously loaded onto the mandrel bar at step 1210 or transported through mandrel grips at step 1230 or any other step appearing in process 1200. In this way the extrusion press system is operable to continuously feed a plurality of billets into a rotating die to extrude the billets to form an extruded material.
Instructions for carrying out the methods of this disclosure for extruding a material may be encoded on a machine-readable medium, to be executed by a suitable computer or similar device to implement the methods of the disclosure for programming or configuring PLCs or other programmable devices with a configuration as described above. For example, a personal computer may be equipped with an interface to which a PLC can be connected, and the personal computer can be used by a user to program the PLC using suitable software tools.
The magnetic domains of coating 1802 of medium 1800 are polarized or oriented so as to encode, in manner which may be conventional, a machine-executable program, for execution by a programming system such as a personal computer or other computer or similar system, having a socket or peripheral attachment into which the PLC to be programmed may be inserted, to configure appropriate portions of the PLC, including its specialized processing blocks, if any, in accordance with the present disclosure.
In the case of a CD-based or DVD-based medium, as is well known, coating 1812 is reflective and is impressed with a plurality of pits 1813, arranged on one or more layers, to encode the machine-executable program. The arrangement of pits is read by reflecting laser light off the surface of coating 1812. A protective coating 1814, which preferably is substantially transparent, is provided on top of coating 1812.
In the case of magneto-optical disk, as is well known, coating 1812 has no pits 1813, but has a plurality of magnetic domains whose polarity or orientation can be changed magnetically when heated above a certain temperature, as by a laser (not shown). The orientation of the domains can be read by measuring the polarization of laser light reflected from coating 1812. The arrangement of the domains encodes the program as described above.
A PLC 1700 programmed according to the present disclosure may be used in many kinds of electronic devices. One possible use is in a data processing system 1900 shown in
System 1900 can be used in a wide variety of applications, including as instrumentation for an extrusion press system, or any other suitable application where the advantage of using programmable or reprogrammable logic is desirable. PLC 1700 can be used to perform a variety of different logic functions. For example, PLC 1700 can be configured as a processor or controller that works in cooperation with processor 1901. PLC 1700 may also be used as an arbiter for arbitrating access to a shared resources in system 1900. In yet another embodiment, PLC 1700 can be configured as an interface between processor 1901 and one of the other components in system 1900. It should be noted that system 1900 is only exemplary. For example, in certain embodiment a user terminal may be provided near the extrusion press system. In other embodiments, a networked arrangement may be provided that may allow the user terminal to be remote from the extrusion press system.
The computing device 2200 may be configured in a distributed architecture, where databases and processors are housed in separate units or locations. The computing device 2200 may also be implemented as a server located either on site at the extrusion press facility or external to the extrusion press facility. Some such units perform primary processing functions and contain at a minimum a general controller or a processor 2202 and a system memory 2208. In such an embodiment, each of these units is attached via the network interface unit 2204 to a communications hub or port (not shown) that serves as a primary communication link with other servers, client or user computers and other related devices. The communications hub or port may have minimal processing capability itself, serving primarily as a communications router. A variety of communications protocols may be part of the system, including, but not limited to: Ethernet, SAP, SAS™, ATP, BLUETOOTH™, GSM and TCP/IP.
The CPU 2202 comprises a processor, such as one or more conventional microprocessors, and one or more supplementary co-processors, such as math co-processors, for offloading workload from the CPU 2202. The CPU 2202 is in communication with the network interface unit 2204 and the input/output controller 2206, through which the CPU 2202 communicates with other devices such as other servers, user terminals, or devices. The network interface unit 2204 and/or the input/output controller 2206 may include multiple communication channels for simultaneous communication with, for example, other processors, servers or client terminals. Devices in communication with each other need not be continually transmitting to each other. On the contrary, such devices need only transmit to each other as necessary, may actually refrain from exchanging data most of the time, and may require several steps to be performed to establish a communication link between the devices.
The CPU 2202 is also in communication with the data storage device 2214. The data storage device 2214 may comprise an appropriate combination of magnetic, optical and/or semiconductor memory, and may include, for example, RAM, ROM, flash drive, an optical disc such as a compact disc and/or a hard disk or drive. The CPU 2202 and the data storage device 2214 each may be, for example, located entirely within a single computer or other computing device; or connected to each other by a communication medium, such as a USB port, serial port cable, a coaxial cable, an Ethernet type cable, a telephone line, a radio frequency transceiver or other similar wireless or wired medium or combination of the foregoing. For example, the CPU 2202 may be connected to the data storage device 2214 via the network interface unit 2204.
The CPU 2202 may be configured to perform one or more particular processing functions. For example, the computing device 2200 may be configured, via the PLC, for controlling at least in part one or more aspects of the billet delivery subsystem 20, extrusion subsystem 40, and quenching subsystem 60.
The data storage device 2214 may store, for example, (i) an operating system 2216 for the computing device 2200; (ii) one or more applications 2218 (e.g., computer program code and/or a computer program product) adapted to direct the CPU 2202 in accordance with the present invention, and particularly in accordance with the processes described in detail with regard to the CPU 2202; and/or (iii) database(s) 2220 adapted to store information that may be utilized to store information required by the program.
The operating system 2216 and/or applications 2218 may be stored, for example, in a compressed, an uncompiled and/or an encrypted format, and may include computer program code. The instructions of the program may be read into a main memory of the processor from a computer-readable medium other than the data storage device 2214, such as from the ROM 2212 or from the RAM 2210. While execution of sequences of instructions in the program causes the CPU 2202 to perform the process steps described herein, hard-wired circuitry may be used in place of, or in combination with, software instructions for implementation of the processes of the present invention.
The term “computer-readable medium” as used herein refers to any non-transitory medium that provides or participates in providing instructions to the processor of the computing device (or any other processor of a device described herein) for execution. Such a medium may take many forms, including but not limited to, non-volatile media and volatile media. Non-volatile media include, for example, optical, magnetic, or opto-magnetic disks, or integrated circuit memory, such as flash memory. Volatile media include dynamic random access memory (DRAM), which typically constitutes the main memory. Common forms of computer-readable media include, for example, a floppy disk, a flexible disk, hard disk, magnetic tape, any other magnetic medium, a CD-ROM, DVD, any other optical medium, punch cards, paper tape, any other physical medium with patterns of holes, a RAM, a PROM, an EPROM or EEPROM (electronically erasable programmable read-only memory), a FLASH-EEPROM, any other memory chip or cartridge, or any other non-transitory medium from which a computer can read.
Various forms of computer readable media may be involved in carrying one or more sequences of one or more instructions to the CPU 2202 (or any other processor of a device described herein) for execution. For example, the instructions may initially be borne on a magnetic disk of a remote computer (not shown). The remote computer can load the instructions into its dynamic memory and send the instructions over an Ethernet connection, cable line, or even telephone line using a modem. A communications device local to a computing device (e.g., a server) can receive the data on the respective communications line and place the data on a system bus for the processor. The system bus carries the data to main memory, from which the processor retrieves and executes the instructions. The instructions received by main memory may optionally be stored in memory either before or after execution by the processor. In addition, instructions may be received via a communication port as electrical, electromagnetic or optical signals, which are exemplary forms of wireless communications or data streams that carry various types of information.
The foregoing is merely illustrative of the principles of the disclosure, and the systems, devices, and methods can be practiced by other than the described embodiments, which are presented for purposes of illustration and not of limitation. It is to be understood that the systems, devices, and methods disclosed herein, while shown for use in extrusion press systems, may be applied to systems, devices, and methods to be used in other manufacturing processes including, but not limited to, cast-and-roll and heat treatment processes. Furthermore, the disclosure could be implemented as a post-processing step of another manufacturing process, including other extrusion processes, or could be implemented concurrently with another manufacturing process.
Variations and modifications will occur to those of skill in the art after reviewing this disclosure. The disclosed features may be implemented, in any combination and subcombination (including multiple dependent combinations and subcombinations), with one or more other features described herein. The various features described or illustrated above, including any components thereof, may be combined or integrated in other systems. Moreover, certain features may be omitted or not implemented.
Examples of changes, substitutions, and alterations are ascertainable by one skilled in the art and could be made without departing from the scope of the information disclosed herein. All references cited herein are incorporated by reference in their entirety and made part of this application.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15370482 | Dec 2016 | US |
| Child | 16655084 | US | |
| Parent | 13870666 | Apr 2013 | US |
| Child | 15370482 | US |