Patent Application
20160083645
A variety of granular particles are widely used as propping agents to maintain permeability in oil and gas formations. Three grades of proppants are conventionally employed: sand, resin-coated sand, and ceramic proppants. Conventional proppants exhibit exceptional crush strength but also extreme density. A typical density of ceramic proppants exceeds 100 pounds per cubic foot. Proppants when used in oil and gas wells are materials pumped into oil or gas wells at extreme pressure in a carrier solution (typically brine) during the hydrofracturing process. Once the pumping-induced pressure is removed, proppants “prop” open fractures in the rock formation and thus preclude the fracture from closing. As a result, the amount of formation surface area exposed to the well bore is increased, enhancing recovery rates. Proppants also add mechanical strength to the formation and thus help maintain flow rates over time. Proppants are principally used in gas wells, but do find applications in oil wells.
Relevant quality parameters, especially when proppants are used to enhance oil or gas production, include: particle density (low density is desirable), crush strength and hardness, particle size (value depends on formation type), particle size distribution (tight distributions are desirable), particle shape (spherical shape is desired), pore size (value depends on formation type and particle size, generally smaller is better), pore size distribution (tight distributions are desirable), surface smoothness, corrosion resistance, temperature stability, and hydrophilicity (hydro-neutral to phobic is desired). Lighter specific gravity proppants can be desirable, since they are easier to transport in the fracturing fluid and therefore can be carried farther into the fracture before settling out and which can yield a wider propped fracture than higher specific-gravity proppants.
Proppants used in the oil and gas industry are often sand and man-made ceramics. Sand is low cost and a moderate density compared to other proppant materials, but has low strength. Man-made ceramics, mainly bauxite-based ceramics or mullite-based ceramics, are much stronger than sand, but are far more dense and more costly than sand. Ceramic proppants dominate sand and resin-coated sand on the critical dimensions of crush strength and hardness. They also offer some benefit in terms of maximum achievable particle size, corrosion, and temperature capability. Extensive theoretical modeling and practical case experience suggest that conventional ceramic proppants offer compelling benefits relative to sand or resin-coated sand for most formations. Ceramic-driven flow rate and recovery improvements of 20% or more relative to conventional sand solutions are not uncommon.
Current ceramics proppants are typically employed in wells of intermediate to deep depth. Shallow wells typically employ sand or use no proppants. Ceramic proppants were initially developed for use in deep wells (e.g., those deeper than 7,500 feet) where sand's crush strength is inadequate. In an attempt to expand their addressable market, ceramic proppant manufacturers have introduced products focused on wells of intermediate depth.
Resin-coated sands offer a number of advantages relative to conventional sand. First, resin coated sand exhibits higher crush strength than uncoated sand given that resin-coating disperses loads over a wider area, reducing stresses within the proppant. Second, resin-coated sands are “tacky” and thus exhibit reduced “proppant flow-back” relative to conventional sand proppants. In other words, the resin-coated sand proppant is more likely to remain in the formation. Third, the resin coating typically increases sphericity and roundness of the proppant, thereby reducing flow resistance through the proppant pack.
Recent developments in ceramic proppants have sought to maintain crush strength while reducing proppant density. As an example, porosity has been introduced into proppant bodies. The introduction of pores into proppant bodies have generally corresponded with reduced strength.
In each application of proppants to an oil or gas formation, some proppants are crushed. Porous ceramic proppants tend to generate significant amounts of fine particles which can be carried from the formation. Fines must be filtered and can abrade the equipment used during well production.
Ceramic proppants are typically formed using a standard series of processes:
Traditional processes to produce ceramic particles such as proppants are time consuming and costly. Raw materials are typically pre-ground to size. Then the sized materials are transferred to a mixer having medium to intensive shear in order to form a uniform dispersion or green body material. The green body material is then formed into particles by another process such as spray drying, compaction, or milling The formation process may be repeated several times if a multi-layer ceramic particle configuration is desired. The stable, unsintered particle that is formed whether in a single or multi-layered process is called a “green body.” Finally, the green body is sintered to produce a finished ceramic, glass-ceramic, or composite. The multiple steps in this process require many pieces of equipment, a large manufacturing area, and the need to transfer material from one piece of equipment to the next. Most of the steps in the traditional process are batch operations.
Extrusion processes are well known as methods to form ceramics. U.S. Pat. No. 3,112,184 describes a method to make thin-walled ceramic honeycomb structures for use in regenerators, recuperators, radiators, catalyst carriers, filters, heat exchangers, and the like. Such ceramic extrusions are useful for producing large, structural articles. U.S. Pat. No. 5,227,342 describes a method for making metal oxide ceramics, such as pellets or plugs, by an extrusion process. U.S. Pat. No. 7,160,584 describes a method for manufacturing a ceramic glow pin that is formed of more than two layers and manufactured by a co-extrusion process. Such ceramic extrusions can produce smaller shapes, such as pellets. However, these methods are not useful for articles, such as proppants, because proppants must be generally spherical in shape. When bisected by three mutually perpendicular planes, a sphere has a circular cross section in each plane. Extrusions can produce spherical cross sections in only one plane perpendicular to the direction of the extrudate as it exits the die. Furthermore, proppants with multiple layers must enclose or encapsulate the inner layers in the generally spherical proppant. In co-extrusions, multiple, adjacent layers, or regions are extruded simultaneously. If the extrudate from a coextrusion was cut perpendicular to the flow of material, inner layers or regions of material would not be completely encapsulated as all materials present in the coextrusion are visible in the extrudate when viewed in the direction perpendicular to the extruder die. Pellets cut from a coextrusion expose the inner layers of the structure at the surface where the pellet is cut.
A feature of the present invention is a process to produce a wide variety of ceramic particles suitable for use as proppants in a continuous and efficient manner.
A further feature of the present invention is a process capable of producing proppants with one or a plurality of material, layers, or regions.
A further feature of the present invention is the use of one or multiple green body materials, each associated with a layer, or region within the final proppant.
A further feature of the present invention is the use of a co-extrusion step where a plurality of green body materials come into contact and flow or move in substantially the same direction.
A further feature of the present invention is partial encapsulation of at least one material with another during a co-extrusion step.
A further feature of the present invention is the creation of higher density and lower density distribution green bodies.
A further feature of the present invention is the improvement of interfaces between multiple materials within green bodies.
A further feature of the present invention is the formation of proppants with a significantly narrower particle size distribution with respect to conventional proppants.
A further feature of the present invention is the ability to have the different layers or regions create a desired internal stress profile within the proppant bodies.
A further feature of the present invention is to provide a method for making strong, tough, and lightweight ceramics, glass or glass-ceramics matrix composites through a self-toughening structure generated by viscous reaction sintering of a complex mixture of oxides within at least one layer or region of a proppant.
A further feature of the present invention is to provide a multi-layer or multi-region ceramics, glass or glass-ceramics composite, such as in the form of a proppant, with superior crush strength.
A further feature of the present invention is to provide a proppant having a superior balance of crush strength and/or buoyancy as shown by specific gravity.
A further feature of the present invention is to provide a proppant that can overcome one or more of the disadvantages described above.
To achieve one or more features of the present invention, the present invention relates to a method to produce a material, such as a ceramic, glass-ceramic, or composite, by bringing multiple green body materials together into a stable multi-layered or multi-region arrangement in the form of a green body. The green body can be formed from several green body materials.
The method can include forming a green body from green body materials. The green body materials can include multiple mixtures of materials that can take the form of powders, slurries, pastes, liquids, and other forms. The materials in those mixtures can include one or more of the following classes of materials:
The method can include an extrusion process to shape and form the green body material into a final shape suitable for a proppant or into an intermediate shape that can be subsequently transformed into a shape suitable for a proppant. Extrusion is accomplished by pushing or drawing the green body material through a die or other shaping device of the desired cross-section shape and size. The energy required to push or draw the green body material may be provided by a piston in a cylinder, a rotating screw in a cylinder, a twin rotating screw in co-linear cylinders, cylinder peristalsis, vibration, centrifugal forces, similar methods, or any combination thereof.
The method can include shaping the proppant subsequent to the extrusion to form the green body material into a final shape suitable for a proppant. The subsequent shaping may be accomplished by tumbling, rolling, grinding, milling, casting, die pressing, die forging, impingement, sand blasting, partial dissolving, and the like, or any combination thereof.
The method can include sintering the green body to produce a sintered ceramic, glass, glass-ceramic, or composite, such as a proppant. Sintering is accomplished with pressure or without pressure by increasing the temperature of the green body to effect inter-particle adherence in the green body. The required temperature increase for sintering may be produced by radiant heating, infra-red heating, plasma heating, microwaves, induction heating, RF heating, lasers, self-propagating combustion, and the like.
The present invention provides a process for making new and improved proppants that overcome the above-referenced problems and others. The proppant can be used in any application suitable for a proppant. The present invention accordingly relates to a method to prop open subterranean formation fractions using the proppant.
The present invention relates to a process that includes preparing precursor ceramic, glass, glass-ceramic, or composite materials; combining precursor materials to form a green body material; bringing those materials together within an extrusion head, which can be a co-extrusion head; parting sections of the combined materials to form a green body; optionally altering the shape of the green body; and sintering the green body.
The process described herein, of the present invention can include one or more of the following steps:
The materials used to form the green body materials in the present invention can include one or more of the following:
Sacrificial materials in the present invention can include one or more of the following:
Reactive materials in the present invention can include one or more of the following:
Riders, materials that remain substantially the same during the process, in the present invention can include one or more of the following:
Pore and/or microsphere formers in the present invention can include one or more of the following:
Flow agents in the present invention can include one or more of the following:
Appropriate flow (or material movement) and pressure (or force) can be delivered to the co-extrusion chamber described herein using one or more of the following methods, and/or combinations thereof:
The methods of the present invention can comprise at least one extruder, such as shown in
The extrusion chamber (e.g.,
The co-extrusion chamber in the present invention includes at least one volume (e.g., space, flow path, flow area) for each single precursor material, wherein only that precursor material is stored, flows, or moves. Those volumes can be shaped to direct the flow or movement of each precursor in some combination toward and in parallel to other precursor materials. As one example, the flow or movement of a material in Region 2 in
When a co-extrusion method is used, such as shown in
The composition of the green body materials within any one or more volumes of the extrusion chamber can vary with time.
The shape of the volumes for each green body material, the flow rates of each green body material, and/or the flow rate of the combined green body materials contribute to a co-extrusion process wherein the cross section of the extrudate (output of the co-extrusion chamber) can vary with time. In a co-extrusion process, each green body material is made to occupy a certain region within the cross section of the extrudate. As an example, the width or cross-sectional area of the extrudate and/or the width or cross-sectional area of material regions, within the extrudate can be varied with time.
In the present invention, green bodies can be formed by dividing the flow or material movement created in the co-extrusion chamber into discrete, disconnected units. The means of dividing the material movement or flow can include the following separately or in any combination:
The combination of varying extrudate cross sections and parting methods allows outer regions of extrudate to partially encapsulate or completely encapsulate inner regions. In other words, green bodies formed by the present invention can have inner extrudate layers that have limited or no exposure to the surface of the green body even after a parting and/or shaping operation.
Varying flow rates can also be used to increase the sphericity of green bodies, as assessed immediately after the parting operation. Without varying the combined flow rate, the green bodies would exhibit a roughly cylindrical shape.
The formation of green bodies in the present invention can include, in addition to the dividing or separating activity described above, shaping, coating, hardening, heating, and/or other processes that improve the process, improve the sintering process step or improve the features of the proppants.
The present invention further relates to other methods of making proppants which have a strengthened spherical structure with reduced defects. For instance, a slurry paste (e.g., ceramic slurry paste) can be forced under pressure through an extrusion die to form a green body extrudate, such as a cylindrical tube (e.g., hollow cylindrical tube), which is sectioned into predetermined lengths, for instance, by crimping, to form sectional green bodies (e.g., tube sections) which can have sealed ends, such as conical or hemispherical ends. The ends can be rounded off, such as by tumbling or other methods. The sectional green bodies or the resulting proppant can have one or more other layers.
Another method of the present invention for making the strengthened spherical particles can comprise an extrusion process wherein a slurry paste is forced under pressure through an extrusion die configured to form an extrudate which comprises a continuous cylinder shape which has a substantially cylindrical-shaped (or other shape) cross-sectional profile, and then intermittently crimping and dividing/cutting the tube to form discrete tube-shaped particles which have opposite crimped tube ends, and then tumbling the cut tube-shaped particles with crimped ends in a spheronizer to round off the cylinder ends to form a more spherical shaped hollow particle.
In an extrusion molding process of the present invention, a slurry paste can be forced under pressure through an extrusion die to form a hollow cylindrical-shaped tube of predetermined inside and outside dimensions. As shown in
In order to seal the ends on the tube (or any green body material exiting the extruder) prior to subsequent processing, the green body can be separated or cut via a crimping method, such as using a double acting crimping tool. The active faces of the crimping tool can have an included angle of about 90 degrees, and can form a conical section (or other shaped end) at the end of each section.
The spheronizer which is used can operate on conventional principles for such a device adapted for rounding off the ends of the described ceramic, glass, or metal oxide type extrudates. For example, the basic spheronizer machine can have a rotating friction disk, designed to increase friction with the product, which spins at high speed at the bottom of a cylindrical pan or bowl. The spinning friction disc can have a groove pattern on the processing surface. This is most often crosshatched, but several sizes and other types are available. After the cylindrical extrudate segments are separated or cut into segments, the extrudate segments can be charged to the spheronizer and fall on the spinning disc. These cylindrical segments are gradually rounded by the collisions with the bowl wall, the plate and each other. The ongoing action of particles colliding with the wall and being thrown back to the inside of the plate creates a “rope-like” movement of product along the bowl wall. The continuous collision of the particles with the wall and with the friction plate gradually turn the cylindrical segments into spheres, provided that the granules are plastic enough to allow the deformation without being destroyed. When the particles have obtained the desired spherical shape, the discharge valve of the chamber is opened and the granules are discharged by the centrifugal force.
The slurry paste which can be used for the die extrusion process can comprise, for example, ceramic powder particles with sizes which can range from about 0.5 μm to about 3 μm, and specifically from about 1 μm to about 2 μm, or other sizes, mixed with a carrier fluid. The carrier fluid can be water, but may also include organic solvents, such as acetone, methanol, ethanol, and the like. Binders can be added to the slurry that allow the paste to maintain its shape after extrusion and provide enough strength to the extrudate during the crimping and spheronization processes. These binders can include paraffin wax, poly vinyl alcohol, poly methylmethacrylate, polyethylene glycol, methyl cellulose, hydroxyl propyl methyl cellulose, and any combinations thereof. In addition to the binders and carrier fluid, an optional lubricant may be added to assist with paste flow in the barrel of the extruder and in the extrusion die. These lubricants can include stearic acid, phthalic acid, oleic acid, petroleum oil, polyacrylamide, menhaden fish oil, and any combinations thereof. The resulting paste can be admitted to the barrel of an extruder and forced under pressure to the extrusion die assembly. Following the formation process, the green ceramic proppant particles can be subjected to a heat treatment cycle to bring about such processes as de-binding, and sintering.
In a further extension of the extrusion process, multiple layers of differing compositions can be simultaneously extruded through a co-axial extrusion die set to form extrudate with a layered or multi-layered structure, followed by the crimping and spheronization processes. This can yield spherical proppant particles with a layered or laminated structure which can confer additional strength, toughness and durability properties on the proppant particles. These described injection and extrusion molding processes can also be used to make template particles which can be employed in template coating processes described herein to form spherical, light weight, high strength proppant particles.
Regarding extrusion processes, in the past, the extrudate was simply cut to expose the cross-sectional area of the ends. For instance, Bortone et al. (U.S. Patent Application Publication No. 2005/034581) relates to the use of a cutting assembly for extruded materials using counter-rotating rollers with planar blades fitted to the periphery at predefined locations. Rotation of the rollers causes a cutting action to occur by way of shearing that yields cut faces of the extrudate that are more or less perpendicular to the axial direction of the extrudate. Whittingham et al. (U.S. Pat. No. 4,442,741) relates to the use of a pretensioned music wire assembly for the cutting of a minced meat extrusion, with the cutting action able to be completed on both the downward and upward strokes of the cutting wire. Again, the cut faces of the extrudate are essentially perpendicular to the axial direction of the extrudate. Fisher et al. (U.S. Pat. No. 5,251,523) takes the cutting action one step further and shows the use of a pair of cutting die bushings fitted with a thin planer blade to cut extruded plastic. The use of a rotating cutting apparatus has been described by Williams (U.S. Patent Application Publication No. 2002/0104419 and U.S. Patent Application Publication No. 2004/0035270), wherein a multiplicity of planar cutting blades are fitted to the surface of rotating cylinder, cutting action occurs by a shear mechanism. For the present invention, these cutting techniques would not work, but instead, a crimping operation would be needed when making a proppant that comprises a core and layer or a proppant with multi-layers. The above references can be modified as follows.
The mechanism of the present invention for dividing the extrudates to pre-determined lengths occurs not by shear, but, for instance, by localized compression of the extrudate between profiles blades. The profile of the blades (or dividers) may be shaped such that conical, inclined, hemispherical, or wedged shaped ends are generated by the dividing action. In other words, the dividing method of the present invention provides the separating and forming of the plurality of extrudate ends in a one step operation, and is particularly useful for achieving a uniform or substantially uniform outer surface with respect to material consistency and can be useful for the sealing of tubular or hollow extrudates during the separating/dividing operation.
The expression “reactive sintering” as used herein, can include a process wherein heat is applied to a composition, causing that composition to undergo, at least in part, a chemical reaction forming a new composition. The composition is heated to below or about its melting point.
The term “green body” or “green pellet” refers to pre-sintered material of this invention that has been shaped from the disclosed compositions but is not sintered. The mixing step typically provides an aqueous dispersion or paste, which is later dried.
The sintering of the green body can occur at any temperature to achieve densification of the material forming the green body, which can include ceramic material or oxides thereof. Sintering temperatures can be, for instance, from 700° C. to about 1,700° C., or from about 800° C. to about 1,700° C. Sintering can occur by ramping up to the desired temperature. The sintering temperature is the temperature in the oven or sintering device. The green body or parts thereof can include one or more sintering aids, grain growth inhibitors, ceramic strengthening agents, glassy phase formation agents, crystallization control agents, and/or phase formation control agents. The various processes and/or materials used to form the green bodies or proppants, or post-processing steps as described in U.S. Pat. Nos. 8,075,997; 8,047,288; 8,012,533; 8,003,212; 7,914,892; 7,887,918; 7,883,773; 7,867,613; 7,569,199; 7,491,444; and 7,459,209 can be used and these patents are incorporated in their entirety by reference herein and form a part of the present application.
Furthermore, for purposes of the present application, it is understood that the shape of the proppant can be any shape, and the extrusion chamber and/or die can essentially be configured to any desired shape in order to achieve the desired proppant shape, which can be spherical, non-spherical, cylindrical, irregular, or other geometric shapes that are desirable depending upon the user's specifications.
The extrusion rate can range from 0.5 mm/min to 500 mm/min or more, or any range within these limits. The moisture content of the extrusion paste may range from 5 wt % to 20 wt % or more, such as from 5 wt % to 10 wt %. The polymeric components (binder, lubricants, dispersants, wetting agents, viscosity modifiers, defoamers, etc.) (if present) can be present in the extrusion paste(s) in an amount of from 0.5 wt % to 15 wt % or more, such as from 2 wt % to 8 wt %. The paste may be a thixotropic or rheopectic plastic non-Newtonian paste with viscosities that may range from 100,000 cP to 10,000,000 cP or more, such as from 120,000 cP to 1,000,000 cP. All weight percents provided herein are based on the total weight percent of the extrusion material or paste. Generally speaking, the amounts of one or more of the various ingredients can optionally be in the amount(s) set forth above in the identified patents, which are incorporated herein by reference.
For purposes of the present invention, the material of the present invention will be described in terms of its preferred form or shape, in terms of bodies with multiple layers or regions and namely particles that can be used in a variety of end use applications, such as for proppant uses in hydrocarbon recovery. While the preferred shape and preferred materials of the present invention are described in detail herein, it is to be understood that this is simply for exemplary purposes and in no way limits the scope of the present invention with respect to shape, materials, and/or end uses. While the term “proppant” is used at times in the application, it is understood that this term is not meant to be limited to its end use application, but for purposes of the present invention, it is to be understood that the proppant or particles, which are used as proppants, can be used in any end use application where ceramic, glass, glass-ceramics, or composites are useful.
The proppant produced by the method of the present invention may produce a solid proppant as shown in
The proppant produced by the methods of the present invention can, as an option, produce a solid proppant with a hollow core as shown in
In accordance with the methods of the present invention, the ceramic proppant produced as described herein may be used as proppants, gravel, or fluid loss agents in hydraulic fracturing, and/or frac packing. As stated above, the present invention also relates to a proppant formulation comprising one or more proppants of the present invention with a carrier. The carrier can be a liquid or gas or both. The carrier can be, for example, water, brine, hydrocarbons, oil, crude oil, gel, foam, or any combination thereof. The weight ratio of carrier to proppant can be from 10,000:1 to 1:10,000, or any ratio in between, and preferably about 0.1 g proppant/liter fluid to 1 kg proppant/liter fluid.
For the purposes of the present invention, the processes will now be described in terms of the preferred materials, preferred process steps, and the preferred process output, namely proppants. While the preferred steps, their preferred arrangements, set ups, operating conditions, geometries, control methods, and other conditions, variables and options are described herein, it is to be understood that this description is offered for exemplary purposes and in no way limits the scope of the present invention with respect to specific process steps, their arrangement, set up, operating conditions, geometries, control methods, and other conditions, variables, or options.
The ceramic, glass, glass-ceramics, or composites of the present invention can be in the form of a sphere, where the sphere is solid or hollow, or has one or more voids present within the sphere. The ceramic, glass, glass-ceramics or composites can be a sphere or similar shape, and can be hollow in the interior of the sphere.
As an option, the material of the present invention can form a shell around one or more other materials, such as a template or template material, which can be in the form of a sphere or other shape and which can be a solid material or a hollow material. For instance, the material of the present invention can form a shell around a hollow sphere, such as a cenosphere or other similar material. When the ceramic, glass, glass-ceramic, or composite of the present invention is present as a shell and encapsulates one or more other materials, such as a sphere (like a hollow sphere), the coefficient of thermal expansion between the shell and the template material can be the same or within 20% of each other, such as within 10%, within 5%, within 1%, or within 0.5% of each other.
The proppant (or sintered body) can have a hollow core or a solid core, and can have a low specific gravity, for example, a specific gravity in a range of from about 1.0 g/cc to about 2.5 g/cc, while maintaining a crush strength in a range of from about 500 psi to about 20,000 psi, and/or a flexural strength in a range of from about 1 MPa to about 200 MPa, or more.
The multi-layer or multi-region proppants of the present invention provide oil and gas producers with one or more of the following benefits: improved flow rates, enhanced hydrocarbon recovery, improved productive life of wells, improved ability to design hydraulic fractures, and/or reduced environmental impact. The proppants of the present invention are designed to improve flow rates, eliminating or materially reducing the use of permeability destroying polymer gels, reducing pressure drop through the proppant pack, and/or reducing the amount of water trapped between proppants thereby increasing hydrocarbon “flow area.” Lower density enhances proppant transport into the formation, which increases the depth proppants can penetrate the formation from the well bore. This effect increases the amount of fracture-area propped, and thereby the mechanical strength of the reservoir. The low density of the present invention's proppants can reduce transportation costs. Because the proppant is lighter, less pumping force is needed, potentially lowering production costs and reducing damage to the formation.
The multi-layer structure of the present invention enables the production of proppants with a variety of beneficial property improvements which can include, but are not limited to, lower production cost, improved “flow-back” and lower particulate generation upon crushing within the formation.
Proppants of the present invention preferably enable the use of simpler completion fluids, which can be of a lower cost, and require slower or otherwise less destructive pumping. Formations packed with the lower density proppants of the present invention can exhibit improved mechanical strength/permeability and thus increased economic life. Enhanced proppant transport enabled by lower density proppants enable the placement of the proppant of the present invention in areas that were previously impossible, or at least very difficult to prop. As a result, the mechanical strength of the subterranean formations can be improved with reduced decline rates over time.
If lower density proppants are employed, water and/or brine solutions can be used in place of more exotic completion fluids. The use of simpler completion fluids can reduce or eliminate the need to employ de-crosslinking agents. Further, increased use of environmentally friendly proppants can reduce the need to employ other environmentally damaging completion techniques such as flashing formations with hydrochloric acid. The low density properties that can be exhibited by the proppants of the present invention eliminates or greatly reduces the need to employ permeability destroying polymer gels as the proppants are more capable of staying in suspension.
The present invention relates to low density proppants that can be utilized, for example, with water and/or brine carrier solutions.
The proppant can be either solid throughout or hollow within the proppant. In the present invention, a solid proppant is defined as an object that does not contain a void space in the center, although a porous material would be suitable and is optional; a fully dense material is not a requirement of a solid proppant. A hollow material is defined as an object that has at least one void space inside (e.g., generally centrally located within the proppant) with a defined size and shape.
The ceramic, glass, glass-ceramics, or composites of the present invention can have isotropic properties and/or anisotropic properties. In other words, the ceramic, glass, glass-ceramics, or composites can have measurable properties that are identical in all directions (isotropic), or can have properties that differ according to the direction of measurement (anisotropic).
The template or extrusion chamber openings can have a diameter in the size range of, for example, from about 1 nm to about 3000 μm, or from about 25 μm to about 2000 μm, or from about 80 μm to about 1500 μm, or from about 120 μm to about 300 μm, or from about 250 μm to 600 μm.
The proppants of the present application can have a specific gravity of, for example, from about 0.6 g/cc to about 3.5 g/cc. The specific gravity can be, for example, from about 2.0 g/cc to about 2.5 g/cc, from about 1.0 g/cc to about 2.5 g/cc, from about 1.0 g/cc to about 2.2 g/cc, from about 1.0 g/cc to about 2.0 g/cc, from about 1.0 g/cc to about 1.8 g/cc, from about 1.0 to about 1.6 g/cc, or from about 0.8 g/cc to about 1.6 g/cc. Other specific gravities above and below these ranges can be obtained. The term “specific gravity” as used herein is the weight in grams per cubic centimeter (g/cc) of volume, excluding open porosity in determining the volume. The specific gravity value can be determined by any suitable method known in the art, such as by liquid (e.g., water or alcohol) displacement or with an air pycnometer.
The strength properties of the proppant can be dependent on the application. It is intended that a crush strength of at least 1,000 psi is desirable. The crush strength can be from about 2,000 psi to about 25,000 psi or higher. The crush strengths can be greater than 9,000 psi, greater than 12,000 psi, or greater than 15,000 psi. Other crush strengths below or above these ranges are possible. A crush strength below 3000 psi is an option, or 500 psi to 3000 psi, or 1000 psi to 2,000 psi. Crush strength can be measured, for example, either according to American Petroleum Institute Recommended Practice 60 (RP 60) or International Standard Organization's ISO 13503-2.
The proppant can have any particle size. For instance, the proppant can have an average particle diameter of from about 1 nm to 1 cm, from about 1 μm to about 1 mm, from about 10 μm to about 10 mm, from about 100 μm to about 5 mm, from about 50 μm to about 2 mm, or from about 80 μm to about 1,500 μm. The optimum size of the proppant can depend on the particular application.
The proppant can also have a range of particle size distributions such as from about 0.4 to about 1.0, wherein dps=(dp90−dp10)/dp50 and wherein dp10 is a particle size wherein 10% of the particles have a smaller particle size, dp50 is a median particle size wherein 50% of the particles have a smaller particle size, and dp90 is a particle size wherein 90% of the particles have a smaller particle size. The proppant may also exhibit a dps from about 0.4 to about 0.6, a dps of 0.1 to 0.6 or 0.1 to 0.4. The percent for particle size is based on number or amount.
The present invention also relates to a proppant used to prop open subterranean formation fractions comprising a particle or particles with controlled buoyancy and/or crush strength and/or surface properties and/or fine creation with particle crushing. The controlled buoyancy can be a negative buoyancy, a neutral buoyancy, or a positive buoyancy in the medium chosen for pumping the proppant to its desired location in the subterranean formation. The medium chosen for pumping the proppant can be any desired medium capable of transporting the proppant to its desired location including, but not limited to, a gas and/or liquid, energized fluid, foam, and aqueous solutions, such as water, brine solutions, and/or synthetic solutions. Any of the proppants of the present invention can have a crush strength sufficient for serving as a proppant to prop open subterranean formation fractures.
The proppants of the present invention can comprise a single particle or multiple particles and can be a solid, partially hollow, or completely hollow in the interior of the particle. The particle can be spherical, nearly spherical, oblong (or any combination thereof), or have other shapes suitable for purposes of being a proppant. The surface of the proppant can be smooth, rough, or can have protruding structures (including whiskers), or these features in any combination. The proppant may contain filler in addition to the whiskers. The filler is a compound that does not reactively sinter with the ceramic, glass, glass-ceramics, or composites. Examples of fillers include graphite, metals (e.g., noble metals), metal oxides (e.g., cerium oxide), and metal sulfides (e.g., molybdenum disulfide).
The proppant can be spherical, oblong, nearly spherical, or any other shapes. For instance, the proppant can be spherical and have a Krumbein sphericity of at least about 0.5, at least 0.6, at least 0.7, at least 0.8, or at least 0.9, and/or a roundness of at least about 0.4, at least 0.5, at least 0.6, at least 0.7, or at least 0.9. The term “spherical” refers to sphericity and roundness on the Krumbein and Sloss Chart by visually grading 10 to 20 randomly selected particles.
As indicated, the ceramic, glass, glass-ceramics, or composites produced by the present invention can be considered a proppant or used as a proppant.
The proppant can have at least one of the following characteristics:
The proppants can be used in a method to prop open subterranean formation fractures and can involve introducing a proppant formulation that includes one or more proppants of the present invention, into the subterranean formation. The method can be for treating a subterranean producing zone penetrated by a well bore, and can include the steps of preparing or providing a treating fluid that includes a fluid, energized fluid, foam, or a gas carrier having the proppant of the present invention suspended therein, and pumping the treating fluid into the subterranean producing zone whereby the particles are deposited therein. The treating fluid can be a fracturing fluid and the proppant particles can be deposited in the fractures formed in the subterranean producing zone. The treating fluid can be a gravel packing fluid and the particles can be deposited in the well bore adjacent to the subterranean producing zone.
The present invention further relates to a matrix that includes a plurality of the proppants of the present invention and at least one solid matrix material in which the proppant is distributed.
The configuration of the glass-ceramic article being formed can take many shapes including a sphere, elliptical, doughnut shape, rectangular, or any shape necessary to fulfill a useful application. In the case of a sphere, the sphere can encapsulate a template. The template may be a hollow or solid, and may be a glassy or glass-ceramic sphere, or an organic sphere. Hollow spheres are typically used as templates in applications where it is desirable to produce particles with low specific gravity. Spheres with an overall diameter from about 90 μm to about 2000 μm are typical for proppants (e.g., 100 μm to about 2000 μm, 120 μm to about 2000 μm).
In the case of spherical glass-ceramic composite particles including a hollow template, the composition of the outer shell preferably has a coefficient of thermal expansion matching that of the template. If the expansion of the inner and outer shells is significantly different, cracks may form at the interface between the inner and outer shell and strength of the resulting particle is negatively affected.
The present invention includes the following aspects/embodiments/features in any order and/or in any combination:
The present invention can include any combination of these various features or embodiments above and/or below as set forth in sentences and/or paragraphs. Any combination of disclosed features herein is considered part of the present invention and no limitation is intended with respect to combinable features.
The present invention will be further clarified by the following examples, which are intended to be exemplary of the present invention.
A ceramic powder mixture of aluminosilicate glass and alumina with a mean particle size of approximately 1.50±0.05 μm is charged into the muller of the extruder. To the powder is added 50.0±0.5 g of oleic acid as an extrusion lubricant. The resulting mixture is mulled for approximately 5 minutes, after which time 250±0.5 g of methyl cellulose is added to act as a binder. Mulling of the powder/lubricant/binder is continued for 10 minutes, after which time a quantity of water is added to wet out the powder and form a paste suitable for extrusion. The quantity of water added is typically 500±1 g. The paste is mulled for an additional 20 minutes under vacuum to de-gas the paste prior to extrusion. The paste is moved from the reservoir to the extrusion die by way of a twin screw feeder. The extrusion die has multiple circular apertures of approximately 915 μm. The paste extrudes from the die set and forms a continuous extrudate of circular cross-section with a mean diameter of approximately 915 μm. The extrudate is cut into lengths of 915 μm by way of a vertical cutting blade. The resulting cut extrudates are charged into the product chamber of an Eirich mixer to effect spheronization of the cylindrical extrudates. The pan is rotated clockwise at approximately 25 rpm with the rotor of the machine running in a counter clockwise direction at approximately 100 rpm. The process is continued until the extrudates are spherical. The now spherical extrudates are removed from the pan on the mixer and sintered in air under standard conditions (e.g., 800° C. to 1,200° C. for 10-60 minutes) to obtain a proppant of approximately 750 μm (US Mesh #20) diameter.
The paste of the same composition (and additives) as in Example 1 is prepared and is extruded through a modified die. The modified die has circular apertures with a circular mandrel of 250 μm diameter centered in each aperture of the die. The extrudate thus formed is tubular in nature with an inside diameter of approximately 250 μm and an outside diameter of approximately 915 μm. The resulting tubular extrudate is cut into lengths of 915 μm by way of a crimping action using a tool with a conical profile. The resulting crimped extrudate sections are processed in the Eirich mixer and sintered as in Example 1, yielding hollow proppant spheres of approximately 750 μm (US Mesh #20) diameter.
A ceramic polymer mixture of composition 80 vol % ceramic powder mixture with the composition of Example 1 and 20 vol % low density polyethylene is mixed in the muller for 10 minutes. The resulting ceramic-polymer mixture is heated to approximately 115° C. and mulling continued for approximately 15 minutes to melt and mix the two components together into a homogenous mix. The resulting ceramic-polymer blend is extruded through the same die as used in Example 1 and the extrudate is maintained at a temperature of approximately 75° C. and cut into lengths of 915 μm using a planar cutting blade. The cut extrudates are placed into a heated forging die of two pieces with hemispherical cavities. The forging die is maintained at approximately 100° C. The extrudates are oriented such that the axial direction of the cylindrical extrudates are perpendicular to the face of the forging die. The cylindrical extrudates are forged to spheres with a diameter of 915 μm. Heat treatment and sintering (as in Example 1) of the resulting spheres will yield a solid ceramic proppant of approximately 750 μm (US Mesh #20) diameter.
The ceramic-polymer blend of Example 3 is extruded through an extrusion die with mandrels as per the die set used in Example 2. The tubular extrudates are crimped in a manner similar to that of Example 2. The short lengths of tubular extrudates with crimped ends are forged into hollow spheres, using the forging die of Example 3, with an outside diameter of approximately 915 μm and an inside diameter of approximately 250 μm. Heat treatment and sintering (as in Example 1) of the hollow ceramic-polymer spheres will yield a hollow ceramic proppant of approximately 750 μm (US Mesh #20) diameter.
Applicants specifically incorporate the entire contents of all cited references in this disclosure. Further, when an amount, concentration, or other value or parameter is given as either a range, preferred range, or a list of upper preferable values and lower preferable values, this is to be understood as specifically disclosing all ranges formed from any pair of any upper range limit or preferred value and any lower range limit or preferred value, regardless of whether ranges are separately disclosed. Where a range of numerical values is recited herein, unless otherwise stated, the range is intended to include the endpoints thereof, and all integers and fractions within the range. It is not intended that the scope of the invention be limited to the specific values recited when defining a range.
Other embodiments of the present invention will be apparent to those skilled in the art from consideration of the present specification and practice of the present invention disclosed herein. It is intended that the present specification and examples be considered as exemplary only with a true scope and spirit of the invention being indicated by the following claims and equivalents thereof.
| Number | Date | Country | |
|---|---|---|---|
| 61435938 | Jan 2011 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13355606 | Jan 2012 | US |
| Child | 14951158 | US |