Patent Application
20140041230
This invention relates to the manufacture of improved fabrication members, in particular, the manufacturing of fabrication members having properties to create more effective and efficient fabrication members.
Frame members are made from a variety of materials used for many different applications. Fabrication members are used in applications where increased load is exerted in a structure. For example, such loads in buildings may comprise the gravitational load exerted by the weight of the building, the loads exerted by the manner in which the building is used, and loads exerted by the environment, such as from wind and seismic activity. For further example, such loads in vehicles may be exerted by the weight of the vehicle, by the cargo carried by the vehicle, or the manner in which the vehicle is used; additionally, such loads may be exerted by collisions. In each instance, the structure has to be reinforced, compared to less-load-bearing areas, in order to maintain the structural integrity of the building or vehicle.
It is customary for the designer of structures to specify the load-bearing qualities which must be exhibited by each of the components comprised in the structure. Special attention is paid to the special load-bearing components. Typically these load-bearing components are formed from a single strip of raw material having relatively uniform thickness and substantially uniform properties across the entire sheet. Examples of such members used in structures include cold-formed steel metal studs used in walls, metal building purlins used in roofs and walls, or curtainwall members or large windows. Such structures have been customarily made from a single piece of metal strip material which is cold-formed through a series of mechanical passes in order to shape them into the desired structure. As a result, the previous cold-formed fabrication members have a relatively uniform thickness throughout the entire structure, including areas of the structure which carry less load. These previous fabrication members, therefore, comprise more material than is necessary to perform their desired function.
These fabrication members often comprise one or more web portions and one or more flange portions. Generally, the web-portion having different mechanical properties to bear shear and torsional forces along the length of the web portion and between flange portions. Tube-shaped fabrication members often comprise two web portions connecting two flange portions. Generally, these fabrication members are formed from a single metal strip with the web portions the same dimensions and mechanical properties as the flanges. The specifications of the flange members providing for a desired material and desired dimensions of the fabrication members. Generally, however, the loads applied to the web portions require less material than the loads applied to the flange portions. There is, therefore, a need for a fabrication member meeting the desired load-bearing requirements, while also having a more effective and efficient structure.
Presently disclosed is a method of making a composite tube-shaped fabrication member comprising the steps of: providing in a coil a first planar member having a desired cross-sectional shape and a desired first set of mechanical properties suitable to form a flange of a tube-shaped fabrication member; providing in coils two second planar members having a desired cross-sectional shape and a desired second set of mechanical properties different from the first planar member suitable to form web portions of a tube-shaped frame member; providing in coils two third planar members each having a desired cross-sectional shape and a desired third set of mechanical properties suitable to form a portion of a flange of the tube-shaped member; uncoiling and passing through accumulators a third planar member, a second planar member, the first planar member, a second planar member, and a third planar member, the accumulators allowing sufficient delay to permit for welding of end portions of coils to enable continuous flow of first planar member, second planar members, and third planar members; aligning side portions of first planar member and second planar member and side portions of the first planar member and third planar member for attachment; attaching side portions of the first planar member and the two third planar members to respective side portions of two second planar members by induction welding to form a composite intermediate product as a continuum of a third planar member, a second planar member, the first planar member, a second planar member and a third planar member, suitable for forming a tube-shaped composite fabrication member; and cold-forming the composite intermediate product to form a composite fabrication member of a tube-shape with the first planar member forming flange portions, the second planar members forming web portions, and the two third planar members forming a flange portion of the tube-shaped composite fabrication member. The method may also comprise attaching the two third planar members together by welding to form a continuous flange of the tube-shaped fabrication member.
In some embodiments the step of cold-forming imparts bends in the first and third planar members adjacent transitions between the first and second planar members and the second and third planar members to form a box-shaped fabrication member. In other embodiments the step of cold-forming may impart a profile into the first, second and third planar members to form a curvilinear-shaped tubular fabrication member. Furthermore, in embodiments, the step of attaching the first and third planar members to the second planar members is performed with the step of cold-forming to form a composite fabrication member having a tube-shape. Alternatively, or in addition, the step of attaching the two third planar members by welding to form the tube-shaped composite fabrication member may be performed with the step of cold-forming to form a composite fabrication member having a tube-shape.
The presently disclosed method of making a composite fabrication member may further comprise the step of forming perforations, embossments, or knurling in the composite intermediate product and/or the composite fabrication member.
Also disclosed is a method of making a composite intermediate fabrication product comprising the steps of: providing in a coil a first planar member having a desired cross-sectional shape and a desired first set of mechanical properties suitable to form a flange of a tube-shaped fabrication member; providing in coils two second planar member having a desired cross-sectional shape and a desired second set of mechanical properties different from the first planar members suitable to form a web portion of a tube-shaped frame member; providing in coils two third planar members each having a desired cross-sectional shape and a desired third set of mechanical properties suitable to form a portion of a flange of the tube-shaped member; uncoiling and passing through accumulators a third planar member, a second planar member, the first planar member, a second planar member, and a third planar member, the accumulators allowing sufficient delay to permit for welding of end portions of coils to enable continuous flow of first planar member, second planar members, and third planar members; aligning side portions of first planar member and second planar member and side portions of the first planar member and third planar member for attachment; and attaching side portions of the first planar member and the two third planar members to respective side portions of two second planar member by induction welding to form a composite intermediate product as a continuum of a third planar member, a second planar member, the first planar member, a second planar member and a third planar member, suitable for forming a tube-shaped composite fabrication member.
The disclosed method of making a composite fabrication member and the disclosed method of making a composite intermediate product may both have side portions of the first and third planar members overlap with side portions of the second planar members prior to induction welding. The second planar members may have thicknesses less than the thicknesses of the first and third planar members. Alternatively, the third planar members may have thicknesses less than the thicknesses of the first and second planar members.
The first and third planar members may be made from a material suitable for making a composite intermediate such as steel or aluminum or alloys thereof having different compositions. Alternatively the first and third planar members are made of a steel or aluminum or alloy thereof composition different from the second planar members.
Also disclosed is a method for making a tube-shaped fabrication member comprising the step of: providing in a coil a first planar member having a desired cross-sectional shape and a desired first set of properties suitable to form a first part of a tube-shaped composite fabrication member; providing in a coil a second planar member having a desired cross-sectional shape and a desired second set of properties different from the first set suitable to form a second part of a tube-shaped composite fabrication member; uncoiling and passing through accumulators the first planar member and the second planar member, the accumulators allowing sufficient delay to permit for welding of end portions of coils to enable continuous flow of first planar member, and second planar member; aligning side portions of first planar member and second planar member for attachment; attaching the first and second planar members together at first side portions adjacent a transition by induction welding to form a composite intermediate product as a continuum of the first and second planar members, suitable for forming into a tube-shaped composite fabrication member; and cold-forming the composite intermediate product to bend non-joined side portions of the first and second planar members and attaching together non-joined side portions of the first and second planar members by welding along said side portions to form a tube-shaped composite fabrication member.
In some embodiments, the step of cold-forming includes imparting bends in the first planar member, the first planar member having a thickness greater than the second planar member, adjacent the non-joined side portions and the adjacent transitions between the first planar member and the second planar members and therebetween to form a box-shaped tubular fabrication member. In alternative embodiments, the step of cold-forming includes imparting bends in the second planar member, the first planar member having a thickness greater than the second planar member, adjacent the non-joined side portions and the adjacent transitions between the first planar member and the second planar members and therebetween to form a box-shaped tubular fabrication member. In further embodiments, the step of cold-forming includes imparting a profile to the first and second planar members bringing the non-joined side portions of the first and second planar members together to form a curvilinear-shaped tubular fabrication member.
Also disclosed is a method for making a composite intermediate fabrication product comprising the steps of: providing in a coil a first planar member having a desired first set of mechanical properties and a desired cross-sectional shape, suitable to form a first part of a tube-shaped fabrication member; providing in a coil a second planar member having a desired second set of mechanical properties and a desired cross-sectional shape, suitable to form a second part of a tube-shaped fabrication member; providing in a coil a third planar member having a desired third set of mechanical properties and a desired cross-section shape, suitable to form a third part of a tube-shaped fabrication member; uncoiling and passing through accumulators the first planar member, the second planar member, and the third planar member, the accumulators allowing sufficient delay to permit for welding of end portions of coils to enable continuous flow of first planar member, second planar member, and third planar member; aligning a first side portion of the first planar member with a first side portion of the second planar member and aligning a second side portion of the second planar member with a first side portion of the third planar member for attachment; and, attaching the first and third planar members to the second planar member together at respective side portions by induction welding, forming a composite intermediate product, a continuum of the first planar member, second planar member, and third planar member.
Additionally disclosed is a method of forming a tube-shaped structural fabrication member comprising the steps of: providing in a coil a first planar member having a desired first set of mechanical properties and a desired cross-sectional shape, suitable to form a first part of a tube-shaped fabrication member; providing in a coil a second planar member having a desired second set of mechanical properties and a desired cross-sectional shape, suitable to form a second part of a tube-shaped fabrication member; providing in a coil a third planar member having a desired third set of mechanical properties and a desired cross-section shape, suitable to form a third part of a tube-shaped fabrication member; uncoiling and passing through accumulators the first planar member, the second planar member, and the third planar member, the accumulators allowing sufficient delay to permit for welding of end portions of coils to enable continuous flow of first planar member, second planar member, and third planar member; aligning a first side portion of the first planar member with a first side portion of the second planar member and aligning a second side portion of the second planar member with a first side portion of the third planar member for attachment; attaching the first and third planar members to the second planar member together at respective side portions by induction welding, forming a composite intermediate product, a continuum of first planar member, second planar member, and third planar member; cold-forming the composite intermediate product bringing the non-joined side portions of first and third planar members together and attaching adjacent side portions of the first and third planar members together by welding to form a tube-shaped composite fabrication member.
In some embodiments, the step of cold-forming may include imparting bends in the second planar member to form a U-shape with returns adjacent first and third planar members. In alternative embodiments, the step of cold-forming may impart bends in the second planar member to form a U-shape and bends in the first and third planar members adjacent the second planar member. In further embodiments, the step of cold-forming may impart a profile into the first, second and third planar members to form a curvilinear-shaped tubular fabrication member.
Also disclosed is a method of making a composite fabrication member comprising the steps of: providing in a coil a first planar member having a desired cross-sectional shape and a desired first set of mechanical properties suitable to form a first part of a fabrication member; providing in a coil a second planar member having a desired cross-sectional shape with a thickness less than the first planar member and a desired second set of mechanical properties different from the first planar member suitable to form a second part of a fabrication member; uncoiling and passing through accumulators the first planar member and the second planar member, the accumulators allowing sufficient delay to permit for welding of end portions of coils to enable continuous flow of first planar member and second planar member; aligning side portions of the first planar member and second planar for attachment; attaching the first planar member and second planar member together at side portions by induction welding to form a composite intermediate product as a continuum of first planar member and second planar member; and, cold-forming to form a composite fabrication member of a desired shape, such as L-shape, or tubular shape, or other desired shapes.
The method may also include where a lip is formed on the first planar member and second planar member to form a lipped L-shaped fabrication member. Furthermore, the method of making a composite fabrication member may comprise the additional step of welding two fabrication members together each of which are L-shaped to form a box-shaped tubular fabrication member.
The side portions of the first and second planar members may overlap prior to welding. The second planar member may form a light-weight web portion of the composite fabrication member, and the first planar member may form a flange portion of the composite fabrication member.
The first and second planar members may be formed from a material suitable for forming a composite fabrication member. Examples of which materials may include steel or aluminum or alloys thereof having different compositions. Alternatively, the first and second planar members may have the same composition.
Such disclosed methods may include the step of forming perforations, embossments or knurling in the composite intermediate product or the composite fabrication member.
Some embodiments of the present method may produce composite fabrication members of a desired cross-sectional shape at 300-500 ft/min, or up to 800 ft/min, or 1000 ft/min dependent, in part, on the size and desired cross-section shape. In other embodiments the present method may produce composite fabrication members of a desired cross-sectional shape in excess of 200 ft/min.
Presently disclosed is a system for forming a composite intermediate product by the herein disclosed methods. Additionally, presently disclosed is a system for forming a composite fabrication member by the herein disclosed methods.
The composite fabrication members have reduced cost in starting materials and reduced weight, and reducing associated transportation costs of raw materials, intermediary products, and finished products. Composite structural components formed by the present method are lighter, reducing the weight of the vehicles, reducing manufacturing expenses, and increasing fuel efficiency in operation of the vehicles. An L-shape formed from such methods shall have a more effective and efficient use of material, selecting the second planar member to provide a more effective and efficient amount of material used while having mechanical properties to provide the desired load-bearing capacity for the composite structural member, maintaining the composite fabrication member to required mechanical strength and design specifications.
The composite intermediate product and subsequent cold-formed structural fabrication member may be desirable in a number of industries. Such industries may include, but not be limited to, the building, automotive, piping, plumbing, gutter, mechanical, and oil & gas industries.
a is a perspective view of a composite fabrication member formed from the intermediate product shown in
b is a perspective view of a lipped composite fabrication member formed from the intermediate product shown in
a is a schematic view of a continuous welding apparatus for attaching by induction welding a third planar member, a second planar member, a first planar member, a second planar member and a third planar member together to form a composite intermediate product for forming a tube-shaped composite fabrication member.
b is a schematic view of a continuous welding apparatus for attaching by induction welding a first planar member and a second planar member to form a composite intermediate product for forming a composite fabrication member.
c is a schematic view of a continuous welding apparatus for attaching by induction welding first, second, and third planar members to form a composite intermediate product for forming a composite fabrication member.
a is a perspective view of a cold forming apparatus for cold rolling the composite intermediate product, comprised of third planar member, second planar member, first planar member, second planar member and third planar member, for forming a tube-shaped fabrication member.
b is a perspective view of a cold forming apparatus for cold rolling the composite intermediate product, comprised of first planar member and second planar member, for forming an composite fabrication member having an L-shape.
Referring to
As used herein, adjacent includes touching and overlapping. For example a first planar member adjacent a second planar member includes the first and second planar members touching at side portions and overlapping at side portions. A planar member as used herein is generally a substantially flat or curvilinear metal sheet of a desired cross-section. The planar members may be provided in coils, each planar member provided as a separate coil.
Furthermore, each planar member provided in coils formed from metal sheet may have a variety of coatings, such as coatings permissible by Table 1 of ASTM A1003/A1003M-12 Standard Specification for Steel Sheet, Carbon, Metallic and Nonmetallic Coated for Cold Formed Framing Members.
In some embodiments, the first planar member 11 may have the same mechanical properties as the third planar members 17 and 17′. Further, the second planar members 14 and 14′ may have a set of mechanical properties, different from the mechanical properties of the first and third planar members. In other embodiments, the mechanical properties of the second planar members 14 and 14′ may be the same as the mechanical properties of the first planar member 11 and/or the third planar members 17 and 17′.
The first planar member 11 has a selected thickness d11, the second planar members 14 and 14′ have a selected thickness d14, generally thinner than the thickness d11. The third planar members 17 and 17′, have a selected thickness d17, generally of the same thickness d11 as the first planar member 11, but the thickness d17 may be different than thickness d11. Generally, the second planar members 14 and 14′, having thicknesses d14 less than the thicknesses of the first and third planar members, d11 and d17. Alternatively, the third planar members 17 and 17′ may have thicknesses less than the thicknesses of the first and second planar members.
Each planar member may be made from any suitable material to form a composite fabrication member having a desired shape. Examples of which may be metal strip or sheet, such as steel, aluminum, other metal alloys thereof, or composite metal strips. Each planar member may be of the same composition. In other embodiments each planar member or some of the planar members may have different compositions and mechanical properties. In further embodiments the first and third planar members are made of a steel or aluminum or alloys thereof composition being different composition from the steel or aluminum or alloys thereof composition of the second planar members.
A composite intermediate product 10 as a continuum of first, second, and third planar members may be formed by attaching side portions the first planar member 11 and the two third planar members 17 and 17′ to respective side portions of the second planar members 14 and 14′ by welding to form a composite intermediate product 10 as a continuum of a third planar member 17, a second planar member 14, the first planar member 11, a second planar member 14′ and a third planar member 17′, suitable for forming a tube-shaped composite fabrication member. Specifically, the first side portion 12 of the first planar member may be attached to the first side portion 15 of the second planar member 14 and the second side portion 16 of the second planar member 14 may be attached to the first side portion 18 of the third planar member 17. Additionally, the second side portion 13 of the first planar member 14 may be attached to the first side 15′ of the other second planar member 14′, and the second side portion 16′ of the other second planar member 14′ may be attached to the first side portion 18′ of the other third planar member 17′. Thereby forming a composite intermediate product 10, as a continuum of a third planar member, a second planar member, the first planar member, a second planar member, and a third planar member, adapted to be used in the formation of a tube-shaped composite fabrication member meeting customer specifications.
The attaching of side portions may be performed by continuous induction welding. In other embodiments, attaching of side portions may be performed by discrete induction welding at discrete intervals along respective side portions at each weld site. Induction welding is where a conductive material (metal) passes through an electromagnetic field producing localized currents which heat the 2 edges of material through resistance and hysteresis to the point at which they can be fused. The electromagnetic field can be produced by passing an electrical current through a coil of conductive material or by inducing currents though contacts contact applied to the 2 material edges. As used herein, “induction welding,” as used herein, may also include high frequency contact welding where weld current is transferred to the formed steel through contacts that ride on the strip. In high frequency contact welding the welding current is applied directly to a workpiece, such as a tube.
After forming the composite intermediate product 10, the welds along weld sites 24 and 25 may undergo a post-welding coating process whereby a coating, permissible by various ASTM standards, may be applied to the weld site to protect the weld from corrosion. Such process may be referred to as “metallizing welds.”
In some embodiments the induction welding is adapted to attach side portions of the planar members at a rate of 300-500 ft/min. Alternatively the welding method may be adapted to attach side portions of the planar members at a rate in excess of 200 ft/min, 800 ft/min or 1,000 ft/min. Side portions of the first and third planar members, 11, 17 and 17′, respectively, may overlap with side portions of the second planar members 14 and 14′ prior to welding. For example, the first side portions 12 and second side portions 13 of the first planar member 11 may extend over and beyond the first side portions 15 and 15′ of the second planar members 14 and 14′, respectively. Similarly, the first side portions 18 and 18′ of the third planar members 17 and 17′, respectively, may extend beyond the second side portions 16 and 16′ of the second planar members 14 and 14′, respectively. When welded, weld sites 26, 27, 28, and 29 are formed, amalgamating the material at side portions of each adjacent planar member.
In alternative embodiments, the planar members may be connected by butt welding adjacent planar members together. In such embodiments, the side portions of adjacent planar members abut. For example, the second side portion 16 of the second planar member 14 may be positioned adjacent and abutting the first side portion 18 of the third planar member 17. The second planar member 14 and the third planar member 17 may then be butt welded together, at the weld site 28, to form a contiguous composite intermediate product 10 for forming a tube-shaped composite fabrication member. Other attachments of planar members may be performed in a similar manner. Welding by butt welding may require the additional step of adding a flux material to provide sufficient material to form an attachment between adjacent planar members. Similarly, the selected method of butt-welding by induction welding may be adapted to attach side portions of the planar members together in excess of 200 ft/min, 800 ft/min, or 1,000 ft/min. In some embodiments the selected method of but-welding may be adapted to attach side portions of the planar members together at a rate of between 300 ft/min and 500 ft/min.
The composite intermediate product 10, a continuum of strips comprising first, second, and third planar members is a continuous strip of material of metal, with attachment by welding, at the weld sites 26, 27, 28, and 29, merging the second planar members 14 and 14′ with the first planar member 11 and the third planar members 17 and 17′ to form a strip of material having a contiguous cross-section formed as a continuum of the first and second and third planar members. The composite strip, comprising the composite intermediate product 10 having different cross-sectional thicknesses, d11, d14, and d17 across its width.
The strip, comprising the composite intermediate product 10, may have one surface on a substantial plane, with the top surfaces of each of the planer members positioned flush with one another, and with the bottom surface of the strip undulating, across its width, upon the transition between the first planar member 11 and the second planar members 14 and 14′, and upon the transition between the second planar members 14 and 14′ with the third planar members 17 and 17′, providing for a composite intermediate product 10 with a stepwise bottom surface. In some embodiments, the second planar members 14 and 14′, having a thickness d14 less than the thickness d11 of the first planar member 11 and less than the thickness d17 of the third planar members 17 and 17′, may be positioned, relative to the other planar members, such that the top surfaces 30, 31 and 31′, and 32 and 32′ of all the planar members are flush. Consequently, the bottom surface of the second planar members 14 will be inward, vertically, from the bottom surfaces of the other planar members. Thus, a composite intermediate product 10, a continuum of first, second, and third planar members, is formed having a substantially flat top surface, and a stepwise bottom surface, across its width, the bottom surface of the second planar member recessed relative to the bottom surface of the first and third planar members.
Alternatively, by way of example, the second planar members 14 and 14′, may be positioned vertically at any position along the thickness d11 of the first planar member 11, and vertically at any position along the thickness d17 of the third planar members 17 and 17′. In such embodiments, both the top and bottom surfaces of the composite intermediate product 10 may be stepwise, across its width, from the transitions between the first, second, and third planar members.
The strip, comprising the composite planar member 10, having different thicknesses d11, d14 and d17 across its width may be coiled by a coiler (see
Referring to
The cold-forming apparatus may be coupled with a welding apparatus for attaching the two third planar members 17 and 17′ together by induction welding to form a continuous flange 35 of the tube-shaped composite structural frame member 33. Alternatively, the welding apparatus for connecting the second sides 19 and 19′ together may be separate from the cold-forming apparatus. Induction welds are adapted to attach the two third planar members 17 and 17′ together to form a continuous flange 35 of the tube-shaped composite structural frame member 33. The second side portions 19 and 19′ of the third planar members 17 and 17′ may overlap prior to attaching by induction welding, forming a welding site 38. Third planar members 17 and 17′, which cumulatively form a flange portion 35 of the tube-shaped fabrication member 33, where the second side portions 19 and 19′ overlap, may each have a width wider than one half of the width of the first planar member 11. In other embodiments, second side portions 19 and 19′ of the third planar members 17 and 17′, respectively, may abut each other, having no overlap. Such third planar members 17 and 17′ may have a width equal to or less than one half of the width of the first planar member 11, and may be attached by induction welding at the weld site 38. Where the second side portions 19 and 19′ of the third planar members 17 and 17′, respectively, abut each other, having no overlap, a flux may be required during attachment by induction welding, to form the attachment without a reduction in the thickness of the side portions 19 and 19′. In any embodiment, the welds at the welding site 38 between the third planar members 17 and 17′ may be continuous or discrete, as described above. The induction welding may be adapted to attach by induction welding the second side portions 19 and 19′ of the third planar members 17 and 17′, respectively.
The step of attaching the first planar member 11 and third planar members 17 and 17′ to the second planar members 14 and 14′ may be performed with the step of cold-forming to form a composite fabrication member 33 having a tube-shape. Additionally, the step of attaching second side portions 19 and 19′ of the third planar members 17 and 17′, respectively, together to form a second flange portion 35, may be performed with the step of attaching the planar members together and step of cold-forming to form a composite fabrication member 33 having a tube-shape.
In further embodiments, the composite intermediate product, as a continuum of first and second planar members, suitable to form a tube-shaped fabrication member, may be cold-formed to form a tube-shaped fabrication member, with the thicker first planar member oriented above the thinner second planar member, such that the top portion of the tube-shaped fabrication member may withstand compression forces and the bottom portion may withstand tension forces. Additionally, the composite intermediate product may be cold-formed such that the first, second, and/or third planar members are rounded, to form a tube-shaped fabrication member having a rounded cross-section. Such tube-shaped fabrication members may be formed from two, three, or four planar members. In other embodiments, tube-shaped fabrication members may be formed from any desired number of planar members to form a more effective and efficient tube-shaped fabrication member.
The tube-shaped composite fabrication member formed by the presently disclosed method may have a square shape, rectangular, round shape, oval shape, or polygonal shape, as desired, to meet customer specification. Each planar member provided in the method may be flat or curved to meet the desired characteristics of the composite intermediate product suitable to form into a tube-shaped composite fabrication member having a desired cross-sectional shape and a desired set of mechanical properties. A curved planar member may have particular benefit during the cold-forming process, allowing particular forces to be imparted onto the plurality of planar members otherwise not available when cold-forming flat planar members. Flat planar members may have the advantage of being easier to transport and of being processed by existing cold-forming mills, and particularly suited for imparting a different set of forces when cold-forming. A polygonal-shaped, round-shaped, or oval-shaped composite fabrication member may be adapted to be used as a pipe for transportation of fluids, including liquids and gasses, with round and oval-shaped, particularly suited to the transport of fluids under pressure.
Additionally, knurling, perforations, and/or embossments may be formed in the composite intermediate product 10 and/or the tube-shaped fabrication member 33.
Referring to
Similarly to the embodiment illustrated in
A tube-shaped composite fabrication member 54 may be formed from the composite intermediate product 40 by cold-forming. The composite intermediate product 40 may be cold-formed to bend non-joined side portions of the first planar member 41 and second planar member 44 and attaching together non-joined side portions of the first planar member 41 and second planar member 44 to form a tube-shaped composite fabrication member 54. Bends 58 may be imparted during cold-forming into the first planar member 41, the first planar member 41 having a thickness greater than the second planar member 44, adjacent the non-joined side portion 42 of the first planar member 41, adjacent the transition between the first planar member 41 and second planar member 44 at the second side portion 43 of the first planar member 41, and therebetween in the first planar member 41, to form a box-shaped tubular fabrication member 54. In alternative embodiments bends 58 may be imparted during cold-forming in the second planar member 44, the first planar member 41 having a thickness greater than the second planar member 44, the bends 38 adjacent the non-joined side portions 46 of the second planar member 44, and the transition between the first planar member 41 and second planar member 44, at the first side portion 45 of the second planar member 44, and therebetween in the second planar member 44, to form a box-shaped tubular fabrication member 54.
In alternative embodiments the composite intermediate product 40 may be cold formed and a profile may be imparted into the first planar member 41 and the second planar member 44 bringing the non-joined side portions of the first and second planar members together to form a curvilinear tubular fabrication member.
Referring to
Referring to
Similarly to the embodiments illustrated in previous figures, the composite intermediate product 60 may have one flat planar surface and one stepwise surface, where the thicknesses d61 and d67 of the first and third planar members, respectively, are less than the thickness d64 of the second planar member 64. Alternatively, the composite intermediate product may have two stepwise surfaces where the first and third planar members having thicknesses less than the second planar members are positioned off-set with the second planar member.
Referring to
In all embodiments, each planar member may be made from any material suitable for a composite fabrication member. For example, each planar member may be made from metal sheet or strip, such as steel, aluminum, alloys thereof, or other metal alloys, or composite metal strips. The second planar member 94 may have a thickness d94 less than the thickness d91 of the first planar member 91, such that the second planar member 94 forms a web portion of a composite fabrication member (see
The first planar member 91 may be attached to the second planar member 94 at side portions by welding to form a composite intermediate product 90 as a continuum of the first planar member 91 and second planar member 94. Methods of welding may be continuous induction welding. Alternatively, methods of welding may be discrete induction welding forming welds at discrete intervals along the length of side portions of the planar members at the weld site 101. Such methods of induction welding may be adapted to attach side portions of planar members at a rate in excess of 200 ft/min, 300 ft/min, 500 ft/min, 800 ft/min, or 1,000 ft/min. The first side portion 92 of the first planar member 91 may extend over and beyond the first side portion 95 of the second planar member 94, where the first side portion 92 of the first planar member 91 is welded with the first side portion 95 of the second planar member 94 forming a weld site 101.
The resulting composite intermediate product 101, being a continuum of the first planar members 91 and second planar members 94, is a continuous component of material, usually metal, with welding at the weld site 101 attaching the first planar member 91 with the second planar member 94 to form a composite intermediate product 101 having a contiguous cross-section of differing thicknesses d91 and d94 formed from the first and second planar members.
The composite intermediate product 90, as a continuum of the first and second planar members, may have one surface on a constant plane. For example, the second planar member 94, having a thickness d94 less than the thickness d91 of the first planar member 91, may be positioned such that the top surface 103 of the second planar member is flush with the top surface 102 of the first planar member 91. Consequently, the bottom surface of the second planar member 94 will be stepwise, inward, from the bottom surface of the first planar member 91, providing for a composite intermediate product 90 having a flat, planar, top surface and an undulating bottom surface, across its width.
In alternative embodiments, the second planar member 94, having a thickness d94 less than the thickness d91 of the first planar member 91, may be positioned at any position on the thickness d91 of the first planar member 91. In such embodiments, both the top and bottom surfaces of the composite intermediate product 90 may be stepwise, across its width, with the transitions between the first and second planar members.
The composite intermediate product 90 may be cold-formed to form a composite fabrication member 104 of a desired shape. The second planar member 94 may be selected to provide a desired lightweight web member for the composite fabrication member 104. The first planar members 01, being thicker and having different mechanical properties from the second planar member 94, usually forming flange portions of the fabrication member 104. While the mechanical properties of the first planar member 91 may differ from the mechanical properties of the second planar member 94, the planar members may be of the same composition. Alternatively, the composition of the second planar member 94, usually forming the webs of the composite fabrication member 104, may be different from the first planar member 91. The first planar member 91 and the second planar member 94 may be made of steel, or aluminum, or alloys thereof, having different, or the same, compositions.
The strip, comprising the composite planar member 90, having different thicknesses d91 and d94 across its width may be coiled by a coiler (see
In some embodiments, the step of cold-forming the strip, comprising of composite intermediate product 90 as a continuum of first planar member 91 and second planar member 94, having different thicknesses d91 and d94, across its width, may be performed with the step of attaching the first and second planar members together at respective side portions by welding to form a composite fabrication member having a desired cross-sectional shape. Alternatively, such cold forming may take place at a different time and location.
Referring now to
b illustrates an alternative embodiment of a composite fabrication member 109 having an L-shape, where a lip 107 is formed on the first planar member 91 and second planar member 94 to form a lipped L-shaped fabrication member 109. In some embodiments, the lip is formed adjacent the second side portion 93 of the first planar member 91, opposite the bend 108 adjacent the first side portion 92 of the first planar member 91, to form a lipped L-shaped member of the first and second planar members. In some embodiments, the lip 107 at the second side portion 93 of the first planar member 91 may be formed to extend in the opposite direction to the first side portion 92 of the first planar member 91, thereby forming a lipped L-shape member of the first and second planar members, where the lip extends in the opposite direction to the second planar member 94. In further embodiments, the lip 107 may be formed at any angle relative to the main portion 110 of the first planar member 91 to form a composite fabrication member 104 having a desired cross-sectional shape and mechanical properties. For example, an angled lip may be cold-formed at the second side portion 93 of the first planar member 91 to form an r-shaped member of the first planar member 91. Similar lips may be formed, as desired, in the second side portion 96 of the second planar member 94. a lip may be formed in the second edge portion 96 of the second planar member 94 at any angle relative to the main portion 111 of the second planar member 94.
In any embodiment, the first planar member 91 may overlap with the second planar member 94 with first side portions 92 of the first planar member 91 extending to or beyond first side portions 95 of the second planar member 94.
The first planar members 91 and second planar members 94 may be selected to have properties for providing a more effective and efficient amount of material used to form the composite fabrication member 104, while providing desired mechanical properties of the composite fabrication member 104. The second planar member 94 may form a light-weight web portion of the composite fabrication member 104.
In embodiments, perforations, knurling, or embossments may be formed in the composite intermediate product or the composite fabrication member by cold-forming or otherwise.
In all embodiments the cold-forming facility and welding facility for making tube-shaped composite fabrication members may be separate from the welding line for making the composite intermediate product, such the composite intermediate product may be made at one location and distributed to other locations for processing to form fabrication members having a desired cross-section shape and a desired set of mechanical properties. In alternative embodiments all processes may be performed in proximate locations such that raw material in the form of coils of planar members may be formed into composite fabrication members in the same or in proximate locations.
Referring to
Each accumulator 118 delivers respective strips 117 to a strip aligner 120, the strip aligner 120 adapted to position each strip 117, such that the third planar member 17, second planar member 14, first planar member 11, second planar member 14′, and third planar member 17′, are located adjacently aligned in desired positions for attaching together at respective side portions by induction welding in the forming and weld mill 121 to form the composite intermediate product 10. The strip aligner 120 may be adapted to be configured to change the locations in which it positions the individual planar members to achieve different desired composite intermediate products 10. Furthermore, the strip aligner 120 may be adapted to be configured while in use, so that a single composite strip, comprising a composite intermediate product as a continuum of first, second, and third planar members, having varying properties, may be achieved.
The strip aligner 120 delivers the aligned planar members, 11, 14, and 17, to the forming and weld mill 121. A strip deflector 122 may be positioned upstream from the strip aligner 120 adapted to longitudinally rotate the strip, and/or change the elevation of the strip to a desired position, to orient the strip for welding. In some embodiments, the strip deflector 122 of the middle strip, comprising the first planar member 11 may be positioned upstream of the strip aligner 120, while the strip deflector 122 for the strip comprising the other planar members may be integrated with the strip aligner 120, or positioned downstream of the strip aligner 120.
The forming and weld mill 121 may comprise a pair of set rollers 123 adapted to impart a tension onto each strip 117 in preparation for welding. In some embodiments, there may be a set of set rollers 123 adapted to impart a tension into all of the strips, simultaneously; in other embodiments, there may be one set of set rollers 123 for each individual strip, adapted to impart a desired individual tension onto each strip.
The forming and weld mill 121 comprises multiple welding stations 124, each welding station 124a, 124b, 124c, and 124d adapted to attach the first planar member 11, the second planar members 14 and 14′, and the third planar members 17 and 17′ together, at respective side portions by welding, at weld sites 26, 27, 28, and 29, to form a composite strip 125 comprising composite intermediate product 10 as a continuum of third planar member 17, second planar member 14, first planar member 11, second planar member 14′, and third planar member 17′. In some embodiments, the induction welding station(s) 124 is adapted to attach side portions of planar members at a rate in excess of 200 ft/min, 300 ft/min, 500 ft/min, 800 ft/min, or 1,000 ft/min.
The continuous welding apparatus 115 may be adapted to form composite strip 125 comprised of two, three planar, or four planar members. Alternatively the continuous welding apparatus 115 may be adapted to form composite strip 125 comprise of five, six or more planar members. For example, in situations where only a two planar member composite intermediate product is desired, the continuous welding apparatus 115 may be operated with only two strip loaders 116, two accumulators 118, and one welding station 124, performing desired functions. The other elements of the continuous welding apparatus 115 may be left dormant. Similarly, it is contemplated that the continuous welding apparatus 115 may be scaled, either up or down, for forming composite strip 125 comprised of any number of planar members, with the addition or subtraction of strip loaders, levelers, deformers, accumulators, and welding stations. The continuous welding apparatus 115 may be laid out such that the accumulators form an arc downstream of the forming and weld mill 121, as illustrated. In other embodiments, the continuous welding apparatus 115 may be laid out such that the accumulators are staggered, some forward of others, or, alternatively, stacked, one above the other, with strip deflectors, deformers, and levelers adapted to bring each strip to the desired position for passing through the forming and weld mill 121.
After the composite strip 125, comprising attached planar members, exits the forming and weld mill 121, the strip may enter a strip deflector 122, adapted to rotate the strip to a desired orientation and/or change the elevation of the strip to a desired position, suitable for passing through an exit strip accumulator 126. An exit strip accumulator 126 may be positioned downstream of the forming and weld mill 121, adapted to accumulate a large amount of composite strip 125 to provide sufficient time for a filled coil at the coiling station 127 to be changed out, eliminating the requirement to continually shutdown and restart the continuous casting apparatus 115 to change out a coil. A shear may be used to cut lengths of strip for coiling. After exiting the strip exit accumulator 126 the composite strip 125, comprising the composite intermediate product 10 may be coiled at a strip coiler 127.
In other embodiments, the composite strip 125 may exit the forming and weld mill 121, and, optionally, an exit strip accumulator 122, and may enter a cold-forming mill, such as that shown in
Referring to
The continuous welding apparatus 130 may comprise a strip aligner 135 adapted to align the two strips 132 such that the strip comprised of the first planar member 91 and the strip comprised of the second planar member 94 may be positioned for welding in the forming and weld mill 136 to form a composite intermediate product 90 for forming into a composite fabrication member of a desired shape.
The forming and weld mill 136 may comprise a pair of set rollers 138 adapted to impart a tension onto each strip 132 in preparation for welding. In some embodiments, there may be a set of set rollers 138 adapted to impart a tension into all of the strips, simultaneously; in other embodiments, there may be one set of set rollers 138 for each individual strip, adapted to impart a desired individual tension onto each strip. The forming and weld mill 136 comprises one or more welding stations, each welding station for welding along a single weld site. The weld and forming mill 136 for forming an intermediate product 90 suitable to form a composite fabrication member having an L-shape may comprise a single welding station 139. In the embodiment illustrated in
As with the embodiment illustrated in
In other embodiments, the composite strip 140 may exit the forming and weld mill 135, and optionally the exit strip accumulator 141, and may directly enter a cold-forming mill (see
Referring to
The strip 147 may exit the strip accumulators 148 and enter the strip aligner 150, adapted to position each strip, such that the first planar member 61, second planar member 62, and third planar member 63 are located in the desired positions for attaching together at respective side portions by welding by the forming and weld mill 151.
The strip aligner 150 delivers the aligned planar members, 61, 62, and 63, to the forming and weld mill 151. A strip deflector 152 may be positioned upstream from the strip aligner 150 adapted to longitudinally rotate the strip, and/or change the elevation of the strip to a desired position, to orient the strip for welding.
Similarly to the embodiments illustrated in
After the composite strip 156 exits the forming and weld mill 151, the strip may enter a strip deflector 152, adapted to rotate the strip to a desired orientation and/or change the elevation of the strip to a desired position, suitable for passing through an exit strip accumulator 43. An exit strip accumulator 157 may be positioned downstream of the forming and weld mill 151, adapted to accumulate a large amount of composite strip 156 such that a shear may cut lengths of strip for coiling, eliminating the requirement to continually shutdown and restart the continuous casting apparatus 145. After exiting the strip exit accumulator 157 the composite strip 156, comprising the composite intermediate product 60 may be coiled at a strip coiler 158.
Referring to
Each individual strip alignment station 161, comprises a guide block 162 and a pair of entry rollers 163 at the entrance to the strip alignment stations 161. The guide block 162 and pair of entry rollers 163 adapted to receive the strip 117 in a desired position for passage through the strip alignment stations 161. The strip alignment stations 161 each have a plurality of guide rolls 164 and guide blocks 165, adapted to guide the strip 117 around the curve formed by the strip alignment stations 161, bringing the strip 117 in alignment with the middle strip 166, positioned at a desired position for entry into the forming and weld apparatus 121.
Referring to
Sensors 172, may be located downstream of the strip deflector 171 adapted to measure the positions of the strip 117 relative to the middle strip 166 and each other. The sensors 172 may be connected to a computer (not shown) adapted to analyze the data produced by the sensors to determine the positions of the strips 117, and also actively control the function of the strip aligner 120 and the strip deflector 171 to ensure correct positioning of the strips 117 for welding. The strips 117, and 166 pass through a first welding station 173, adapted to attach side portions of one of the outer-most strips to the adjacent strip by welding, thereby welding a first side portion 18 of one of the third planar members 17 to a first side portion 15 of one of the second planar members 14. Subsequently, the combined strip, comprised of the attached third and second planar members, and the unattached strips 117 comprised of the first planar member 11, and the other, second planar member 14′ and third planar member 17′, pass through a second welding station 174. The second welding station 174 adapted to attach the middle strip 166, comprised of the first planar member 11, to the now combined third planar member 17 and second planar member 14, at side portions by welding. As such, the second welding station 174 attaches the first side portion 12 of the first planar member 11 to the first side portion 15 of the second planar 14 member by welding. Similar welds are performed at the third welding station 175 and fourth welding station 176 until all of the individual strips 117, comprising of first, second, and third planar members, are attached at side portions by welding, to form a composite strip 140 as a continuum of first, second, and third planar members. The welding stations comprise induction welders adapted to attach side portions of planar members together at a rate in excess of 200 ft/min, 300 ft/min, 500 ft/min, 800 ft/min, or 1,000 ft/min.
Referring to
Referring to
The cold-rolling mill 180 may comprise multiple roll sets 181, each roll set comprising a work roll 182, having a rolling face 184, rotating about a work roll axle 183, and a driving roll 185, adjacent the work roll 182, adapted to engage the work roll 182 to rotate the work roll 182, and impart lubricating oil onto the rolling face 183 of the work roll 182. Each roll face 184 may be shaped to impart a desired cross-sectional shape onto the composite strip 125 to provide a tube-shaped composite fabrication member 33. There may be successive roll sets 181, each roll set 181 adapted to further mold the composite strip 125 until the composite strip 125 has the desired cross-sectional shape. Furthermore, each consecutive roll set 181 may have work rolls 182 mounted on roll set axles 183 positioned at differing angles, such that each consecutive roll set 181 may impart an increased bend in the composite strip 125, relative to the previous roll set. Alternatively, a single roll set 181 may be sufficient to mold the composite strip 125 into the desired cross-sectional shape. Each roll set 181 may have a complimentary work roll opposite the work roll 182 shown in the figure to further assist in the shaping of the composite intermediate product 10 into a tube-shaped fabrication member 33.
Each successive work roll axis 183 positioned differently than the previous work roll axis to further form the composite intermediate product 10 into the tube-shaped fabrication member 33.
A welding station 186 may be positioned immediately subsequent to the cold-rolling apparatus 180 for attaching the second side portions 19 and 19′ of the third planar members 17 and 17′ together by welding, thus forming a flange 35 of the tube-shaped fabrication member 33. Alternatively, the welding station may be disassociated with the cold-rolling mill 180, the tube-shaped fabrication member 33 being transported from the rolling mill 180 to the welding station for final construction. Such a welding station may comprise an induction welder adapted to attach together second side portions 19 and 19′ of the third planar member 17 and 17′.
Referring to
The composite fabrication member 104, or 109, may be positioned such that a bend 108 is formed in the composite planar member 90 on the generally thicker flange member 105, as opposed to the web portion 106, to ensure that the composite fabrication member 104, or 109, meets a desired specification. Alternatively, it may be desirable to further reduce the material in the composite fabrication member 104, or 109, and position the composite strip 140 such that the bend 108 in the composite planar member 90 is positioned on the web portion 106, having less material than the flange portions 105, or at or near the transition between the web portion 106 and the flange portion 105.
The cold-rolling mill 190 may comprise multiple roll sets 191, each roll set comprising a work roll 192, having a rolling face 194, rotating about a work roll axle 193, and a driving roll 195, adjacent the work roll 192, adapted to rotate the work roll 192, and impart lubricating oil onto the rolling face 193 of the work roll 192. Each roll face 194 may be shaped to impart a desired cross-sectional shape onto the composite strip 140 to provide a composite fabrication member 104, or 109, having a desired cross-sectional shape of L-shape, or lipped L-shape. As discussed above with reference to
In alternative embodiments, the roll sets may be positioned vertically, one roll positioned above the composite strip and a second roll positioned oppositely below the composite strip. Each pair of rolls having a complimentary roll face adapted to impart a shape into the material. At each roll set, there may be a second side roll set, having axles positioned perpendicular to the axles of the first roll set. The side roll set may be adapted to provide greater precision, flexibility, further support and shaping of the composite strip, and to reduce stresses on the material. Furthermore, multiple cold-rolling mills may be utilized to provide a composite fabrication member having a desired cross-sectional shape.
In any embodiment, shears may be provided upstream of the cold-rolling mill, between cold-rolling mills, or downstream of the cold-rolling mill, adapted to cut the composite strip, or cold-formed composite strip, into discrete lengths, as desired, to form composite fabrication members, and having a desired cross-sectional shape.
In any cold-forming mill the roll sets may have a roll face adapted to impart perforations, embossments, and knurling into the planar portions of the composite fabrication members. Alternatively, perforations may be formed by a stamping apparatus, adapted to make perforations of a desired shape and dimension in the web portions of flange portions of the composite fabrication member. Such stamping may be performed simultaneously with cold-forming, prior to cold-forming, or after cold-forming. Alternatively the planar members may be provided with perforations prior the step of attaching the planar members together at respective side portions to form a composite intermediate product. Similarly, embossments and knurling may be formed by a stamping apparatus before, during, or after cold-forming, or the planar members may be provided having desired knurling and embossments prior to the step of attaching the planar members together.
A composite fabrication member may be adapted for use as an interior dry-wall stud, having perforations of a desired shape and size at desired locations to functions as conduits for plumbing and electrics. Such perforations may form any shape, for example oval-shaped, circular-shaped, square-shaped, rectangular shaped or key-hole shaped. Embossments in the web member, for example, may be adapted to provide enhanced strength to the composite fabrication member, further allowing a reduction in the material used to form a composite fabrication member having a desired set of mechanical properties. Such embossments may be diamond shaped. Embossments, such as ribs, formed in the flange portions of the composite fabrication member may increase the torsional load carrying capabilities of the composite fabrication member, further providing avenues for increasing the efficiency and effectiveness of the composite fabrication member. The composite fabrication member may undergo planking to increase the torsional strength of the composite fabrication member. Knurling may be provided in the composite fabrication member to act as guide-holes for fasteners, adapted to guide fasteners to a desired location when being placed in the fabrication member, reducing the tendency for fasteners to slide and skip on the surface of the composite fabrication member during installation of the fastener.
The features of the composite fabrication member may be provided in the individual planar members prior to attaching the planar members together. Alternatively, the composite intermediate product may be passed through a stamping or forming mill to impart desired features in the composite intermediate product. Alternatively, the cold-rolling mill adapted to form the composite fabrication member may also be adapted to impart a desired set of features into the composite fabrication member while forming the composite fabrication member.
While it has been described with reference to certain embodiments, it will be understood by those skilled in the art that various changes may be made and equivalents may be substituted without departing from scope. In addition, many modifications may be made to adapt a particular situation or material to the teachings without departing from its scope. Therefore, it is intended that it not be limited to the particular embodiments disclosed, but that it will include all embodiments falling within the scope of the appended claims.
This application claims priority to U.S. provisional application No. 61/680,777 filed Aug. 8, 2012, the contents of which are hereby incorporated in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61680777 | Aug 2012 | US |