Patent Application
20120255643
1. Field of the Invention
This invention relates generally to the technology field of textile, and in particular, it relates to a fabric material and manufacturing methods thereof.
2. Description of the Related Art
Conventional terry or pile fabrics do not have a good sense of layers. These fabrics usually are made of natural fibers. However, natural fibers have their own characteristics. For example, cotton has poor size stability; linen has high stiffness; silk is hard to maintain and store, etc. All of these make their fabric products imperfect. For example, 100 percent cotton terry or pile fabrics have shortage in fluff and softness; moreover, they are not easy to wash and tend to become tough to the feel after repeated washes.
It is an object of the present invention to provide a fabric that is fluffy, has a good sense of layers, is soft and comfortable, offers durable performance, and is resistant to mildew.
Additional features and advantages of the invention will be set forth in the descriptions that follow and in part will be apparent from the description, or may be learned by practice of the invention. The objectives and other advantages of the invention will be realized and attained by the structure particularly pointed out in the written description and claims thereof as well as the appended drawings.
To achieve these and other advantages and in accordance with the purpose of the present invention, as embodied and broadly described, the present invention provides a fabric, including ground fabric and a double layer terry and/or a double layer pile on its surfaces.
In one embodiment, the ground fabric has a double layer terry on a single side of its surface.
In another embodiment, the ground fabric has a double layer terry on each of the two sides of its surface.
In another embodiment, the ground fabric has a double layer terry on one side of its surface and a double layer pile on the other side of its surface.
In another embodiment, the ground fabric has a double layer pile on a single side of its surface.
In another embodiment, the ground fabric has a double layer pile on each of the two sides of its surface.
In one embodiment, the double layer terry includes an outer, higher terry and an inner, lower terry lower than the outer terry.
In another embodiment, the double layer pile includes an outer, higher pile and an inner, lower pile lower than the outer pile.
In one embodiment, the outer high terry or pile is made of a natural fiber which may include cotton, wool, silk, linen, soy fiber or bamboo pulp fiber or a blend yarn; the inner low terry or pile is made of a microfiber. The microfiber is fiber of single component or multi-components, whose single fiber line density is less than 0.55 dtex. Such fabrics made by natural fibers or blend yarn and microfibers have outstanding performance in moisture absorption, gas permeability, softness, comfort and durability.
In one embodiment, the ground fabric is made of synthetic filament or/and natural fiber.
The fabric may be a woven fabric or a knitted fabric. In a knitting process, the microfiber terry alternate with the natural fiber terry or blend yarn terry. Ground stitch materials are synthetic filament or/and natural fiber or/and blend yarn. In a weaving process, the terry warp is a natural fiber or a blend yarn and single component fiber or multi-component fibers which have one component or two components in a single-fiber. For example, superfine polyester fiber is a single component fiber and PET/PA composite fiber is a multi-component fiber. The weft and ground warp are natural fiber or blend yarn or synthetic filament.
In one embodiment, the arrangement ratio of the terry warp and ground warp in the woven fabric is 1:1 or 2:1 or 1:2 or 2:2; the fabric organization is 2/1 fancy warp-backed weave or 3/1 fancy warp-backed weave or 2/2 fancy warp-backed weave. The arrangement ratio of the natural fiber and microfiber in the terry/pile is 1:1 or 1:2 or 2:1.
In one embodiment, the terry or pile of the knitted fabrics is interwoven by microfiber filament and natural fiber yarn or filament or blend yarn, and the ground organization employs chemical fiber filament or blend yarn or natural fiber yarn or filament.
In one embodiment, the manufacturing process includes a single-side pile cutting treatment on the terry fabrics. After post-processing, single-side pile fabric or one-side terry and one-side pile fabrics are produced. The manufacturing process may also include a double-side pile cutting treatment on the terry fabrics. After post-processing, double-side pile fabrics are produced. The post-processing may include unwinding, splitting process, washing, dyeing and setting.
Embodiments of the present invention provide a new fabric, where the double layer terry and/or double layer pile enhance the sense of layers in fabric, makes the fabric more colorful in style, and more comfortable, soft and durable.
It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are intended to provide further explanation of the invention as claimed.
The invention will be fully understood, while still further objects and advantages will become apparent, in the following detailed description of preferred embodiments with reference to the accompanying drawing, in which:
In these drawings, 1 refers to a ground fabric; 2 refers to an outer high terry; 3 refers to an inner low terry; 4 refers to a high pile; and 5 refers to a low pile.
The terry fabric is a woven fabric; the arrangement ratio of terry warp and ground warp in the woven fabric is 1:1 or 2:1 or 1:2 or 2:2, and the fabric organization is 2/1 fancy warp-backed weave or 3/1 fancy warp-backed weave or 2/2 fancy warp-backed weave.
The pile fabric is a knitted fabric. The pile organization of the knitted fabric is interwoven by microfiber filament and natural fiber yarn or filament or blend yarn, and the ground organization employs chemical fiber filament or natural fiber yarn or filament or blend yarn.
The terry fabric is a woven fabric; the arrangement ratio of terry warp and ground warp in the woven fabric is 1:1 or 2:1 or 1:2 or 2:2, and the fabric organization is 2/1 fancy warp-backed weave or 3/1 fancy warp-backed weave or 2/2 fancy warp-backed weave.
The terry/pile fabric is a knitted fabric. The terry or pile organization of the knitted fabric is interwoven by microfiber filament and natural fiber yarn or filament or blend yarn, and the ground organization employs chemical fiber filament or natural fiber yarn or filament or blend yarn.
The pile fabric is a woven fabric; the arrangement ratio of pile warp and ground warp in the woven fabric is 1:1 or 2:1 or 1:2 or 2:2, and the fabric organization is 2/1 fancy warp-backed weave or 3/1 fancy warp-backed weave or 2/2 fancy warp-backed weave.
In the above embodiments, the blend yarn may contain chemical fiber of less than 40 percent; for example, it may be a blend of 65 percent cotton with 35 percent polyester.
The manufacturing processes for the fabric of the various embodiments are described below. While details of the processes are provided, the invention is not limited to specific steps or parameters given below.
This manufacturing method may be used to produce the fabric shown in
The method employs a knitting process, which includes the following steps: preparing packages, warping, preparing warp beam, knitting, unwinding, splitting, washing, dyeing and setting.
The terry materials on the first bar and on the third bar are 150D/72F DTY of PET/PA composite fiber and 32S cotton yarn. Materials on the second bar are 150D/72F DTY of PET/PA composite fiber. Materials on the fourth bar are 200D/96F FDY of PET fiber. The ratio of terry materials on the first bar and the third bar is 1:1. After warping and knitting the grey fabrics are produced. The finished fabrics are produced after post-processing.
The post-processing includes unwinding, splitting, washing, dyeing and setting.
Beam warping is used on warping machine DS21/30.
The fabrics may be knitted on warp knitting machine HKS4-1 which is E24 106 inch tricot. The specific process is as follows: GB1 and GB3: 0-0/2-2//5100 mm/Rack, GB2:5-5/0-0//3450 mm/Rack, GB4:0-1/1-0//3260 mm/Rack.
The dyeing process includes:
(1) Unwinding, preparing fabrics.
(2) Splitting process. The fabrics are kept in a 100° C. 7 g/L sodium hydroxide solution for 80 minutes.
(3) Washing: The fabrics are washed in 40° C. water 10 minutes. Then 1% acetic acid is put in water in order to make the PH of solution to 7.
(4) Dyeing: Disperse dyes are used. The dyeing auxiliary include 1.2 g/L deoiling agent, 0.5 g/L leveling agent and 0.3% peregal. The temperature is increases from 30° C. to 125° C. with 1° C. m increase rate. The fabrics kept in the solution for 30 minutes. Then the temperature is reduced to 60° C. with 2° C./m cooling speed.
(5) Reduction cleaning: Fabrics are kept in 60° C. solution which includes 1 g/L sodium hydrosulfite and 0.5 g/L soda for 20 minutes.
(6) Washing: Fabrics are kept in 40° C. water which includes 3% cleaning agent for 10 minutes.
(7) Post-process: Fabrics are kept in 40° C. water which includes 1.5% Hydrophilic silicone Oil for 20 minutes.
(8) Setting: The setting is done on STB501 machine with the speed of 28 m/minute and temperature is 165° C.
In one embodiment, single-side pile cutting treatment is done on the terry fabrics. After post-processing, single-side pile fabric or one-side terry and one-side pile fabrics are produced. In another embodiment, double-side pile cutting treatment is done on the terry fabrics. After post-processing, double-side pile fabrics are produced. The resulting pile includes high pile 4 and low pile 5.
This manufacturing method may be used to produce the fabric shown in
The method employs a weaving process, which includes winding, warping, weaving, dyeing and setting.
300D DTY of PET/PA composite fiber terry alternate with 20S cotton yarn terry in warp terry. The ground warp is 300D DTY of PET/PA composite fiber. The weft is 300D FDY of PET fiber. After warping and weaving the grey fabrics are produced. The finished fabrics are produced after post-processing.
The arrangement ratio of terry warp and ground warp is 1:1 or 2:1 or 2:2. The arrangement ratio of natural fiber and microfiber in terry is 1:1 or 1:2 or 2:1.
The post-processing includes unwinding, splitting process, washing, dyeing and setting.
In one embodiment, single-side pile cutting treatment is done on the terry fabrics. After post-processing, single-side pile fabric or one-side terry and one-side pile fabrics are produced. In another embodiment, double-side pile cutting treatment is done on the terry fabrics. After post-processing, double-side pile fabrics are produced. The pile includes high pile 4 and low pile 5.
Drum warping is used on warping machine SHGA215C.
The fabrics may be woven on rapier and Jacquard loom TPS600 and CR-m-2000-230.
The terry weaves is 3/1 fancy warp-backed weaves. The ground structure is 2/2 warp-backed weaves. Two times short beating-up and two times long beating-up are finished to form a terry.
The dyeing process includes:
(1) Unwinding, preparing fabrics.
(2) Splitting process. The fabrics are kept in 100° C. 7 g/L sodium hydroxide solution for 80 minutes.
(3) Washing: The fabrics are washed in 40° C. water for 10 minutes. Then put 1% acetic acid in the water in order to make the PH of solution to 7.
(4) Dyeing: Disperse dyes are used. The dyeing auxiliary include 1.2 g/L deoiling agent, 0.5 g/L leveling agent and 0.3% peregal. The temperature is increases from 30° C. to 125° C. with 1° C./m heating rate. The fabrics are kept in the solution for 30 minutes. Then the temperature is reduced to 60° C. with 2° C./m cooling rate.
(5) Reduction cleaning: Fabrics are kept in 60° C. solution which includes 1 g/L sodium hydrosulfite and 0.5 g/L soda for 20 minutes.
(6) Washing: Fabrics are kept in 40° C. water which includes 3% cleaning agent for 10 minutes.
(7) Post-process: Fabrics are kept in 40° C. water which includes 1.5% Hydrophilic silicone Oil for 20 minutes.
(8) Setting: The setting is done on STB501 machine with the speed of 28 m/minute and temperature is 165° C.
The following points are noted for the weaving process:
(1) In order to form clear shed, the terry warp is thread though the frond dents and ground warp is thread though the back dents.
(2) The dent number should be lower; otherwise there will be more difficulties in the weaving process. The same group terry warp and ground warp are threaded though the same dents.
(3) In order to obtain good softness and high level of moisture absorption, 300D DTY of PET/PA composite fiber is selected as ground warp and internet textured yarn is selected as terry warp.
This manufacturing method may be used to produce the fabric shown in
The method employs a knitting process, where the microfiber terry alternate with the natural fiber terry or the blend yarn terry. The ground stitch materials are synthetic filament or/and natural fiber or/and blend yarn.
The post-processing contains unwinding, splitting process, washing, dyeing and setting.
In one embodiment, single-side pile cutting treatment is done on the terry fabrics. After post-processing, single-side pile fabric or one-side terry and one-side pile fabrics are produced. In another embodiment, double-side pile cutting treatment is done on the terry fabrics. After post-processing, double-side pile fabrics are produced.
This manufacturing method may be used to produce the fabric shown in
The method employs a weaving process, where the terry warp is natural fiber or blend yarn and single component fiber or multi-component fiber. The weft and ground warp are natural fiber or blend yarn or synthetic filament.
The arrangement ratio of terry warp and ground warp is 1:1 or 2:1 or 1:2 or 2:2. The arrangement ratio of natural fiber and microfiber in terry is 1:1 or 1:2 or 2:1.
The fabric structure is 2/1 or 3/1 or 2/2 fancy warp-backed weaves.
The post-processing contains unwinding, splitting process, washing, dyeing and setting.
In one embodiment, single-side pile cutting treatment is done on the terry fabrics. After post-processing, single-side pile fabric or one-side terry and one-side pile fabrics are produced. In another embodiment, double-side pile cutting treatment is done on the terry fabrics. After post-processing, double-side pile fabrics are produced.
The fabric described above combines the advantage of natural fiber with the advantage of microfiber. In use, the surface fiber which touches the skin directly is natural fiber. It can meet users' expectations that fabrics are comfortable and have high level of moisture absorption and good air permeability. At the same time, the fabrics have great advantages in softness, moisture absorption, air permeability, durability and mildew resistance.
It will be apparent to those skilled in the art that various modification and variations can be made in the fabrics of the present invention without departing from the spirit or scope of the invention. Thus, it is intended that the present invention cover modifications and variations that come within the scope of the appended claims and their equivalents.