Fe-Ni based permalloy and method of producing the same and cast slab

Abstract
A Fe—Ni based permalloy comprises Ni: 30-85 wt %, C: not more than 0.015 wt %, Si: not more than 1.0 wt %, Mn: not more than 1.0 wt %, P: not more than 0.01 wt %, S: not more than 0.005 wt %, O: not more than 0060 wt %, Al: not more than 0.02 wt % and, if necessary, not more than 15 wt % of at least one selected from the group consisting of Mo, Cu, Co and Nb within a range of not more than 20 wt % in total.
Description
BACKGROUND OF THE INVENTION

1. Field of the Invention


This invention relates to a Fe—Ni based permalloy suitable for use in a magnetic head, a magnetic shielding material, an iron core of a transformer or the like and having excellent magnetic properties and a method of producing the same as well as a cast slab.


2. Description of Related Art


As the Fe—Ni based high magnetic permeability alloy or so-called permalloy, there are usually typified PB material (40-50 wt % Ni), PC material (70-85 wt % Ni—Mo—Cu), PD material (35-40 wt %-Ni—Fe) and the like, which are defined according to IS C2531. Among these alloys, the PB material is mainly used in applications utilizing the characteristic that saturated magnetic flux density is large, such as stator in a watch, pole piece in an electromagnetic lens and the like, while the PC material is used as a high sensitivity transformer or a magnetic shielding material at a high frequency zone utilizing an excellent permeability. Among these alloys, it is designed to cope with applications such as a magnetic head, a shield case and the like by adding an additional element such as Nb, Cr or the like to provide the abrasion resistance and corrosion resistance (for example, JP-A-60-2651).


As another example of improving the properties of these alloys, JP-A-62-142749 and the like disclose that the permeability and the punching property are improved by adjusting impurity elements such as S, O and the like. Recently, the movement from PC material to PB material or from PB material to PD material is observed for reducing the cost, or there is adopted a method of supplementing for the lack of material properties by designing a fabricator.


In the material makers, therefore, it is strongly noticed to develop materials such as PB material having properties corresponding to those of PC material or PD material having properties corresponding to those of PB material, This increases a degree of freedom in the design of fabricator and hence is effective to give products having higher performances to markets.


SUMMARY OF THE INVENTION

It is, therefore, an object of the invention to provide a Fe—Ni based permalloy satisfying the above demand. That is, the invention is to improve the magnetic properties of PB material and PD material to grade up to the magnetic properties corresponding to those of PC material and PB material and to further improve the magnetic properties of PC material and to develop materials capable of coping with applications of high sensitivity and frequency.


The inventors have made various studies in order to achieve the above object and found that Fe—Ni based permalloys having the following constructions are preferable and as a result the invention has been accomplished.


The invention lies in a Fe—Ni based permalloy comprising Ni: 30-85 wt %, C: not more than 0.015 wt %, Si: not more than 1.0 wt %, Mn: not more than 1.0 wt %, P: not more than 0.01 wt %, S: not more than 0.005 wt %, O: not more than 0.006 wt %, Al: not more than 0.02 wt % and the remainder being Fe and inevitable impurities, provided that Ni segregation amount CNiS represented by the following equation is not more than 0.15 wt %, preferably 0.10 wt %. CNis=analytical value of Ni component (wt %)×CiNis (c.p.s.)/CiNiave. (c.p.s.) wherein CiNis is a standard deviation of X-ray intensity (c.p.s.) and CiNiave. is an average intensity of all X-ray intensities (c.p.s.).


In addition to the above constitutional components, the alloy according to the invention is favorable to contain not more than 15 wt % of at least one selected from the group consisting of Mo, Cu, Co and Nb within a range of not more than 20 wt % in total.


And also, the alloy according to the invention is favorable to control an amount of non-metallic inclusion having a diameter corresponding to a circle of not less than 0.1 μm to not more than 20 particles/mm2, preferably not more than 10 particles/mm2.


Furthermore, the alloy according to the invention is favorable to have the following constructions:


(1) The alloy containing 35-40 wt % of Ni exhibits such magnetic properties that a maximum magnetic permeability μm is not less than 50000, an initial magnetic permeability μi is not less than 10000 and a coercive force Hc is not more than 0.05 (Oe);


(2) The alloy containing 40-50 wt % exhibits such magnetic properties that a maximum magnetic permeability μm is not less than 100000, an initial magnetic permeability μi is not less than 30000 and a coercive fore Hc is not more than 0.02 (Oe);


(3) The alloy containing 70-85 wt % exhibits such magnetic properties that a maximum magnetic permeability μm is not less than 400000, an initial magnetic permeability μi is not less than 20000 and a coercive force Hc is not more than 0.006 (Oe).


And also, the invention proposes a method of producing a Fe—Ni based permalloy, which comprises continuously casting an alloy comprising Ni: 30-85 wt %, C: not more than 0.015 wt %, Si: not more than 1.0 wt %, Mn: not more than 1.0 wt %, P: not more than 0.01 wt %, S: not more than 0.005 wt %, O: not more than 0.0060 wt %, Al: not more than 0.02 wt %, and, if necessary, not more than 15 wt % of at least one selected from the group consisting of Mo, Cu. Co and Nb within a range of not more than 20 wt % in total and the remainder being Fe and inevitable impurities into a slab, and subjecting the continuously cast slab to a homogenizing heat treatment and further to a hot rolling.


In the production method according to the invention, it is favorable that the continuous casting is carried out without applying an electromagnetic agitation and that a cast slab for the permalloy having an area ratio of equiaxed crystal in a cast texture of a continuously cast slab of not more than 1% is used.


As the homogenizing heat treatment, it is favorable that the continuously cast slab is treated at a temperature of 1100-1375° C. under a condition that Ni diffusion distance DNi represented by the following equation is not less than 39:

DNi=(Dt)1/2/μm

wherein


D: diffusion coefficient, D=D0×exp(−Q/RT),


D0: vibration number item=1.63×108/μm2 s−1


Q: activation energy of Ni diffusion=2.79×105/J mol1


R: gas constant=8.31/J mol1 K−1


T: temperature/K


t: annealing time/s


Furthermore, a cold rolling is carried out to produce a product after the hot rolling step, if necessary. And also, it is favorable to conduct a magnetic beat treatment of 1100-1200° C. after the cold rolling step. Such a magnetic heat treatment is favorable to be carried out in a hydrogen atmosphere.


Moreover, the cold rolling step may include usually used steps such as annealing, BA, pickling and the lie. And also, the cast slab used herein may include a cast ingot for the formation of usual ingot in addition to the continuously cast slab.




BRIEF DESCRIPTION OF THE DRAWINGS

The invention will be described with reference to the accompanying drawings: wherein



FIG. 1 is a schematic view illustrating a method of measuring Ni segregation amount of Ni;



FIG. 2 is a graph showing found data of results measured on Ni segregation amount in PB material; and


FIGS. 3(a) and 3(b) are diagrammatically section views of a cast slab.




DETAILED DESCRIPTION OF THE INVENTION

As a result that the inventors have made many experiments, it has been found that it is effective to adopt the following means for solving the above matters, and the invention has been developed.


That is, the invention is characterized in that an alloy comprising Ni: 30-85 wt %, C: not more than 0.015 wt %, Si: not more than 1.0 wt %, Mn: not more than 1.0 wt %, P: not more than 0.01 wt %, S: not more than 0.005 wt %, O: not more than 0.0060 wt %, Al: not more than 0.02 wt %, and, if necessary, 1-15 wt % of at least one selected from the group consisting of Mo, Cu, Co and Nb within a range of not more than 20 wt % in total and the remainder being Fe and inevitable impurities is shaped into a slab through a continuous casting, and then the continuously cast slab is subjected to a homogenizing heat treatment and further to a hot rolling after a surface treatment to render Ni segregation amount CNis into not more than 0.15 wt %, preferably not more than 0.12 wt %, more particularly not more than 0.10 wt %.


The reason why the Ni segregation amount is particularly noticed in the invention is due to the fact that Ni is a most important component among the constitutional components and is slow in the diffusion rate in the alloy and serves as a rate-determining of the homogenizing,


In the invention, therefore, the continuously cast slab is subjected to a homogenizing heat treatment at a higher temperature for a long time as mentioned later as a method of providing a desired Ni segregation amount.


Moreover, when the slab is hot rolled without being subjected to the homogenizing heat treatment, the Ni segregation amount of the hot rolled material is usually about 0.4%.


According to the inventors' studies, it has been found that when the homogenizing heat treatment is carried out so as to satisfy the following temperature and time conditions, there can be obtained materials having the segregation amount lower than the initially anticipated value. That is, according to the inventors' various experiments, it has been found that the Ni segregation amount of the hot rolled material after the hot rolling can be decreased to 0.15 wt % by conducting the homogenizing heat treatment under conditions that the value (D·t)1/2 of the Ni diffusion distance DNi represented by the following equation (1) is not less than 39 and the heat treating temperature T is within a range of 1100-1375° C.:

Ni diffusion distance DNi=(D·t)1/2/μm (1)

wherein


D: diffusion coefficient, D=D0×exp(−Q/RT),


D0: vibration number item=1.63×108/μm2 s−1


Q: activation energy of Ni diffusion=2-79×105/J mol−1


R: gas constant=8.31/J mol1 K−1


T: temperature/K


t: annealing time/s.


In the above equation (1), the value (D·t)1/2 is an indication showing a degree of decreasing Ni segregation. As the temperature becomes higher and the time becomes longer, the value becomes larger and the segregation becomes decreased.


Moreover, as an indication showing the degree of Ni segregation, a standard deviation is determined from the data of Ni concentration distribution obtained by linear analysis of EPMA (X-ray microanalyzer), which is used as Ni segregation amount.


In the above homogenizing heat treatment, when the temperature is lower than 1100° C., the treating time becomes undesirably too long, while when it exceeds 1375° C., the yield is lowered due to the oxidation loss and there is caused a risk of brittle crack through heating. In the invention, therefore, the heat treating temperature is within a range of 1100-1375° C.


And also, non-metal inclusions included in the alloy are noticed in the invention, and the size and number thereof are defined. That is, the ratio of the non-metal inclusion having a diameter of not less than 0.1 μm is controlled to not more than 20 particles/mm2, preferably not more than 15 particles/mm2, more particularly not more than 10 particles/mm2.


As a method of controlling the distribution of the non-metal inclusions, it is advantageous to use a high cleaning technique such as smelting through dissolution under vacuum, deoxidizing with C or the like.


Moreover, the Ni segregation amount CNis (wt %) at section of plate is calculated according to the following equation (2) based on FIG. 1 after the section of the plate is subjected to mirror polishing in usual manner and analyzed through EPMA (X-ray microanalyzer) under conditions shown in Table 1. In this case, the scanning distance is substantially a full length of the plate in thickness direction:

CNis (wt %)=analytical value of Ni component (wt %)×CNiS (c.p.s.)/CiNiave. (c.p.s.)  (2)

wherein CiNis: standard deviation of X-ray intensity at section of plate (c.p.s.) represented by
CiNiS=1nn(CiNi-CiNiave.)2


CiNiave.: average intensity of total X-ray intensities at section of plate (c.p.s.).


The above analytical value of Ni component (wt %) is a Ni content included in the starting material and an analytical value by a chemical or physical method



FIG. 2 is a graph of found data showing results measured on Ni segregation amount of PB material in a hot rolled plate having a thickness of 5 mm. The same measurement is carried out with respect to cold rolled sheet or magnetic heat-treated sheet having a thickness of about 0.2 mm.

TABLE 1Probe diameter1 μmIrradiated current5.0 × 10−7 AAcceleration voltage20 kVMeasuring time0.5 sec/pointMeasuring interval2 μmSpectrocrystalLIF


And also, the measurement of the number of non-metal inclusions is carried out by the following method. Firstly, a surface of a product is subjected to a mechanical polishing and finished by buffing and thereafter the polished surface is subjected to an electrolysis at a constant potential field (Speed process) in a nonaqueous solvent (10 v/v % acetylacetone+1 w/v % tetramethyl ammonium chloride+methanol solution). The electrolysis is carried out in a potential field of 10 C (Coulomb)/cm2 at 100 mV. As the observation is conducted by a scanning type electron microscope (SEM), non-metal inclusions having a diameter corresponding to circle of not less than 0.1 μm are counted at 1 mm2. Moreover, the term “diameter corresponding to circle” means a diameter when individual inclusion is converted into a true circle.


As seen from the above, the invention lies in a point that the characteristics of the alloy are considerably improved without largely changing the component composition. This can be considered as follows. That is, there are various factors dominating the soft magnetic properties of the alloy. For example, there are well-known size of crystal grain, crystal orientation, impurity component, non-metal inclusion, vacancy and the like. In the silicon steel sheets, however, it is known that the soft magnetic properties in a particular direction are considerably improved to highly improve power efficiency of al alternating current transformer by controlling the crystal orientation.


On the contrary, according to the invention, it has been found that the magnetic properties of the Fe—Ni based permalloy can largely be improved by noticing the segregation of Ni, which has never been considered up to the present time, and controlling it. And also, adequate production conditions are found out therefore


In the invention, the alloy characteristics are controlled by controlling the segregation of Ni, which is particularly slow in the diffusion rate among segregations of the components. However, as a result of various examinations, it has been found that it is effective to simultaneously control the non-metal inclusions and crystal grain size for improving the characteristics to desirable levels.


The control of such non-metal inclusions is carried out by rationalizing vacuum dissolution and deoxidation method and reducing elements producing elements producing oxide and sulfide. On the other hand, the control of the crystal grain (coarsening) can be realized by mitigating the component segregation and decreasing the amount of the non-metal inclusion such as sulfide, oxide and the like, for example, MnS, CaS and so on. In this case, the control of the non-metal inclusion is effective in view of two points such as the improvement of magnetic properties by reducing the inclusion itself and the improvement of magnetic properties by controlling the crystal grain.


Moreover, the degree of influence differs in accordance with the components of the alloy in these control factors. For example, the influence of grain size, segregation is large in the PD material and PB material while the influence of non-metal inclusion and component segregation is large in the PC material.


As a method of reducing Ni segregation, which is inevitable for realizing the function and effect of the invention, it is effective to conduct a diffusion heat treatment at a high temperature for a long time as previously mentioned. According to the inventors' studies, it has been found that the segregation of Ni is closely related to a dendrite arm interval of solidification texture and it is advantageous to mitigate Ni segregation as the dendrite arm interval is small. In this case, it has been confirmed that when the continuously cast material is compared with the usual ingot material, the dendrite arm interval is as very small as ⅕- 1/10 and in case of using the continuously cast material, Ni segregation can be mitigated at a small energy.


In case of the alloys according to the invention satisfying the above crystal grain size and the amount and shape of the non-metal inclusion, when the magnification of Ni segregation amount is restricted to not more than 0.15 wt %, the permeability can be made to 2-5 times that of the conventional alloy and the coercive force can be made to about ½- 1/7 thereof and hence the improving effect becomes higher as the Ni segregation amount becomes small.


As a result, the invention can provide PB material as a substitute of PC material, PD material as a substitute of PB material, or PC material having higher magnetic properties.


That is, it is a preferable embodiment that the following characteristics are required in the PB material (40-59 wt % Ni) as a substitute of PC material:


1. Higher permeability: at least maximum permeability μm=not less than 100000, initial permeability μi=not less than 30000;


2. Small coercive force: at least coercive force Hc=not more than 0.02 (Oe);


3. Excellent high frequency characteristic: effective permeability μe at, for example, a thickness of 0.35 mm, 1 Khz=not less than 4000. Moreover, as to the high frequency characteristic, even when there is no difference in the effective permeability μm at the same thickness, the magnetic flux density in PB material is larger (about 2 times) than that of PC material, so that the thickness can be more thinned, which is advantageous in view of design of magnetic circuit, weight reduction and reduction of cost.


And also, it is a preferable embodiment that the following characteristics are required in the PD material (35-40 wt % Ni) as a substitute of PB material:


1. High permeability: at least maximum permeability μm=not less than 50000, initial permeability μi=not less than 10000;


2. Small coercive force: at least coercive force Hc=not more than 0.05 (Oe);


3: Excellent high frequency characteristic: effective permeability lie at, for example, thickness of 0.35 mm, 1 kHz=not less than 3000 (Since an electric resistance value of the PD material is high, the difference of high frequency characteristic between PB material and PD material is originally small).


Furthermore, in order to improve the characteristics of the PC material (70-85 wt % Ni), it is intended to more improve the permeability and reduce the coercive force. As a numerical target value, there are maximum permeability μm=not less than 400000, initial permeability μi=not less than 200000, and coercive force Hc=not more than about 0.006 (Oe).


The reason why the composition of the alloy components according to the invention is limited to the above range will be described below.


(1) C: not more than 0.015 wt %; C is an element degrading soft magnetic properties because when the amount exceeds 0.015 wt %, carbide is formed to control the crystal growth. Therefore, the C amount is limited to not more than 0.015 wt %.


(2) Si: not more than 1.0 wt %; Si is added as a deoxidizing components but when the amount exceeds 1.0 wt %, a silicate based oxide is formed as a start point of forming sulfide such as MnS or the like. The resulting MnS is harmful for the soft magnetic properties and forms a barrier for the movement of domain wall, so that the Si amount is desirable to be as small as possible. Therefore, the Si amount is limited to not more than 1.0 wt %.


(3) Mn: not more than 1.0 wt %; Mn is added as a deoxidizing component, but when the amount exceeds 1.0 wt %, the formation of MnS is promoted to degrade the soft magnetic properties likewise Si. In the PC material or the like, however, Mn acts to control the formation of ordered lattice against the magnetic properties, so that it is desired to add it at an adequate content. Therefore, the Mn amount is limited to not more than 1.0 wt %, preferably a range of 0.01-1.0 wt %.


(4) P: not more than 0.01 wt %; When the P amount is too large, it is precipitated in the grains as a phosphoride to degrade the soft magnetic properties, so that the P amount is limited to not more than 0.01 wt %.


(5) S: not more than 0.005 wt %; When the S amount exceeds 0.005 wt %, it easily forms a sulfide inclusion and diffuses as MnS or CaS. Particularly, these sulfides have a diameter of about 0.1 μm to about few μm, which is substantially the same as the thickness of the domain wall in case of the permalloy and is harmful against the movement of the domain wall to degrade the soft magnetic properties, so that the S amount is limited to not more than 0.005 wt %.


(6) Al: not more than 0.02 wt %; Al is an important deoxidizing component. When the amount is too small, the deoxidation is insufficient and the amount of non-metal inclusion increases and the form of sulfide is easily chanced into MnS by the influence of Mn, Si to control the grain growth. On the other hand, when it exceeds 0.02 wt %, constant of magnetostriction and constant of magnetic anisotropy becomes high to degrade the soft magnetic properties. Therefore, an adequate range of Al added is not more than 0.02 wt %, preferably 0.001-0.02 wt %.


(7) O: not more than 0.0060 wt %; O is decreased by deoxidation to finally remain in steel, but it is divided into O remaining in steel as a solid solution and O remaining as an oxide of non-metal inclusion or the like. It is known that as the O amount becomes large, the amount of the non-metal inclusion necessarily increases to badly affect the magnetic properties, and at the same time it affects the existing state of S. That is, when the amount of remaining O is large, the deoxidation is insufficient, and the sulfide is easily existent as MnS to obstruct the movement of domain wall and the grain growth. From these facts, the O amount is limited to not more than 0.0060 wt %.


(8) Mo: not more than 15 wt %; Mo is an effective component for providing the magnetic properties of PC material under practical production conditions and has a function of controlling the forming condition of ordered lattice exerting upon the crystal magnetic anisotropy and magnetostriction. The ordered lattice is influenced by cooling conditions after the magnetic heat treatment. If Mo is not included, a very fast cooling, rate is required, while if Mo is included in a certain amount, maximum properties can be obtained under a practical cooling condition in industry. However, when the amount is too large, an optimum cooling rate becomes too late or the Fe content becomes small and the saturated magnetic flux density becomes low. Therefore, the Mo amount is preferable to be 1-15 wt %.


(9) Cu: riot more than 15 wt %; Cu has an action of mainly controlling the forming condition of the ordered lattice in the PC material likewise Mo, but acts to decrease the influence of the cooling rate to stabilize the magnetic properties as compared with the effect of Mo. And also, it is known that the addition of Cu in an adequate amount enhances the electric resistance and improves the magnetic properties under alternating current. However, when the Cu amount is too large, the Fe content becomes small and the saturated magnetic flux density becomes low. Therefore, the Cu amount is not more than 15 wt %, preferably 1-15 wt %.


(10) Co: not more than 15 wt %; Co enhances the magnetic flux density and at the same time acts to improve the permeability by addition of an adequate amount. However, when the Co amount is too large, the permeability lowers and also the Fe content becomes small and the saturated magnetic flux density becomes low. Therefore, the Co amount is not more than 15 wt %, preferably 1-15 wt %.


(11) Nb: not more than 15 wt %; Nb is less in the effect on the magnetic properties, but enhances the hardness of the material and improves the abrasion resistance, so that it is an essential component for use in a magnetic head or the lie. And also, it is effective to reduce the magnetic degradation due to molding or the like. However, when the amount is too large, the Fe content becomes small and the saturated magnetic flux density becomes low. Therefore, the Nb amount is not more than 15 wt %, preferably 1-15 wt %.


The production method of Fe—Ni based permalloy according to the invention will be described below.


Firstly, an alloy having the above composition is melted and subjected to a continuous casting process to form a continuously cast slab. In this case, it is desirable to conduct the continuous casting without electromagnetic agitation. Then, the thus obtained continuously cast slab is subjected to a homogenizing heat treatment and further to a hot rolling after the surface treatment of the slab. In the thus obtained hot rolled sheet, the Ni segregation amount CNis can be made to not more than 0.15 wt %.


The above homogenizing heat treatment is suitable to be carried out under a condition that the value DNi(D·t)1/2 of Ni diffusion distance represented by the equation (1) is not less than 39 at a heat treating temperature T of 1100-1375° C.


It is favorable that the slab subjected to the homogenizing heat treatment is repeatedly subjected to cold rolling and annealing after the hot rolling to obtain a product. The thickness of the product is dependent upon the use application, but it is usually not more than 0.1 mm as a thin sheet for lamination in the application requiring high frequency characteristic such as coiled core or the like, and about 0.2-1.0 mm in magnetic yoke, transformer, shielding machine or the like.


As the slab to be subjected to the hot rolling, it is favorable to use a slab having an equiaxed crystal of not more than 1% as an area ratio of slab section (area of equiaxed crystal/area of slab×100) as shown in FIG. 3a because it is more easy to reduce Ni segregation. In case of a slab containing a large equiaxed crystal (20%) as shown in FIG. 3b, it is more difficult to reduce Ni segregation. As to the slab used in the invention, the reason why the use of the continuously cast slab without using the electromagnetic agitation is favorable is due to the fact that the continuously cast slab is relatively fast in the solidification rate and less in the equiaxed crystal. And also, when the electromagnetic agitation is not used, the growth of columnar dendrite texture produced in the solidification step is not obstructed and the equiaxed crystal becomes further small. Moreover, FIG. 3 is a diagrammatic view of a section perpendicular to the casting direction of the cast slab. It is possible to use slabs produced by usual ingot forming process if such a slab contains less equiaxed crystal.


The following examples are given in illustration of the invention and are not intended as limitations thereof.


In Table 2 are shown compositions of test materials-used in the examples. Among the test materials, 10 tons of a starting material-corresponding to PC material is melted under vacuum, while 60 tons of starting materials corresponding to PD and PB materials are melted in air, and then these melts are continuously cast. A part of the continuously cast slabs is subjected to a homogenizing heat treatment, and the remaining slabs are not subjected thereto, which are then hot rolled, and subjected repeatedly to cold rolling and annealing and finally to a temper rolling of few % to obtains products having a thickness of 0.35 mm. Thereafter, the thus obtained test materials are subjected to a magnetic heat treatment in a hydrogen atmosphere at 1100° C. for 3 hours to measure direct current magnetization property and alternating current magnetization property (effective permeability μe). The Ni segregation is measured in the hot rolled sheet, cold rolled sheet and magnetic heat-treated sheet at a section in a thickness direction, respectively. The degree of Ni segregation in the hot rolled sheet is approximately equal to that of the cold rolled sheet after the magnetic heat treatment. The Ni segregation amount is a measured value of the magnetic heat-treated sheet


The measurement of the direct current magnetization property is carried out by winding wire around a ring-shaped test specimen of JIS 45φ×33φ50 turns on each of primary and secondary sides and measuring through a reversed magnetic field of 20 Oe, while the alternating current magnetization property is evaluated by winding 70 turns and measuring an effective permeability at a current of 0.5 mA and a frequency of 1 kHz. As the initial permeability μi, the intensity of magnetic field is measured at 0.01 Oe in case of PB material and 0.005 Oe in case of PC material according to the definition of JIS C2531.


The test-results are shown in Table 3 for PD corresponding material (36Ni alloy: Table 2 {circle around (1)}), Table 4 for PB corresponding material (46Ni alloy: Table 2 {circle around (2)}) and Table 5 for PC corresponding material (JIS alloy: Table 2 {circle around (3)}), respectively. As seen from these tables, the cast slab having an equiaxed crystal ratio of not more than 1% is used in the alloys according to the invention, so that the Ni segregation amount is small and hence the direct current magnetization property and alternating current magnetization property are largely improved. And also, the similar tendency is observed in the alloys {circle around (4)}, {circle around (5)} of Table 2.


That is, it has been confirmed that the PD material (36Ni) has the permeability and coercive force equal to those of the PB material and also the effective permeability, is further improved as compared with that of the PB material because the electric resistance is high Further, it has been confirmed that the PB material has the permeability and coercive force equal to those of the PC material and the saturated magnetic flux density higher than that of the PC material. Moreover, it has been confirmed that the permeability is further improved and the coercive force is lowered in the PC material.

TABLE 2NiMoCuNbCoFeAlloy {circle around (1)} corresponding to PD35.5bal.Alloy {circle around (2)} corresponding to PB46.5bal.Alloy {circle around (3)} corresponding to PC77.44.24.7bal.(JIS)Alloy {circle around (4)} corresponding to PC79.04.04.512.5(hard permalloy)Alloy {circle around (5)} corresponding to PC80.14.52.01.511.9(high permeability)









TABLE 3








Materials corresponding to PD (36Ni alloy)


















Homogenizing
Direct current



heat
magnetization properties













Trace components
treatment
Maximum
Initial






























O/
Temperature ·
(D · t)0.5/
permeability
permeability
Hc/




No.
C
Si
Mn
P
S
Al
ppm
Time
μm
μm
μl
Oa
B20/gauss





Example
1
0.005
0.05
0.2
0.001
0.0007
0.005
20
1350° C. × 50 hr
175.5
85000
21000
0.025
13800



2
0.004
0.06
0.3
0.002
0.0005
0.007
15
1250° C. × 45 hr
84.5
85000
15400
0.020
13600



3
0.005
0.04
0.3
0.002
0.0008
0.01 
19
1250° C. × 10 hr
39.8
55000
10500
0.035
13800



4
0.006
0.02
0.2
0.002
0.0009
0.004
25
1325° C. × 70 hr
176.6
78000
19800
0.035
13600



5
0.005
0.05
0.3
0.001
0.0012
0.009
17
1370° C. × 45 hr
188.8
90000
25400
0.015
13800



6
0.006
0.04
0.3
0.002
0.0030
0.015
45
1350° C. × 50 hr
175.5
56000
12000
0.035
13500


Comparative
7
0.005
0.03
0.3
0.002
0.0005
0.010
18
none
0
19100
5600
0.125
13500


Example
8
0.006
0.02
0.2
0.003
0.0010
0.008
15

1100° C. × 5 hr

8.4
23600
7800
0.095
13800



9
0.007
0.03
0.3
0.002
0.0009
0.011
20

1200° C. × 20 hr

38.7
35000
9800
0.075
13500



10
0.006
0.05
0.2
0.001
0.0008
0.007
21

1300° C. × 3 hr

30.9
42000
10200
0.070
13800



11
0.005
0.02
0.3
0.002
0.0007
0.009
17
1350° C. × 50 hr
175.5
27500
9500
0.080
13500



12
0.006
0.04
0.3
0.002
0.0005

0.150

15
1325° C. × 70 hr
176.6
24500
7500
0.100
13400



13
0.006
0.05
0.3
0.001

0.0066

0.005

75

1350° C. × 60 hr
192.2
22000
8900
0.105
13500



14

0.020

0.04
0.3
0.002
0.0010
0.009
12
1325° C. × 70 hr
176.6
35000
7050
0.095
13500



15
0.005

2.5

0.2
0.001
0.0012
0.010
20
1350° C. × 50 hr
175.5
24000
8900
0.100
13400



16
0.006
0.05

3.5

0.002
0.0012
0.009
22
1250° C. × 10 hr
39.6
34000
8200
0.090
13500



17
0.007
0.03
0.3

0.050

0.0006
0.010
18
1250° C. × 45 hr
84.5
28000
8500
0.095
13600



















Alternating current








magnetization





property
Number





Effective
of
Ni
Equiaxed crystal





permeability μtext missing or illegible when filed
inclusions/

text missing or illegible when filedgregation

ratio of




No.
(1 kHz)
mm2
amount(%)
slab(%)







Example
1
3500
 7.8
0.08
0  




2
3200
 8.2
0.11
0  




3
3100
10.5
0.14
0  




4
3300
 6.8
0.09
0.2




5
4000
 9.5
0.07
0  




6
3000
18.8
0.09
0.1



Comparative
7
1900
 9.5

0.45

0  



Example
8
2200
12.9

0.32

0.1




9
2500
 8.8

0.18

0  




10
2800
 8.6

0.19

0.4




11
2400
10.5

0.26


25.4





12
2200
 9.8

0.37

0.2




13
1800

60.7

0.06
0  




14
2000
10.5
0.08
0.2




15
2200
 8.9
0.10
0  




16
2400
12.6
0.13
0  




17
2400
15.8
0.12
0.1

















TABLE 4








Materials corresponding to PB (46Ni alloy)


















Homogenizing
Direct current



heat
magnetization properties













Trace components
treatment
Maximum
Initial






























O/
Temperature ·
(D · t)0.5/
permeability
permeability
Hc/




No.
C
Si
Mn
P
S
Al
ppm
Time
μm
μm
μl
Oa
B20/gauss





Example
18
0.005
0.05
0.2
0.001
0.0005
0.004
22
1350° C. × 50 hr
175.5
175000
45000
0.009
15800



19
0.006
0.02
0.2
0.002
0.0008
0.009
24
1250° C. × 45 hr
84.5
125000
35400
0.010
15900



20
0.005
0.04
0.3
0.002
0.0009
0.012
20
1250° C. × 10 hr
39.8
115000
35000
0.015
15600



21
0.004
0.08
0.3
0.002
0.0011
0.008
18
1325° C. × 70 hr
176.6
184000
39800
0.012
16000



22
0.005
0.05
0.3
0.001
0.0010
0.007
 8
1370° C. × 45 hr
188.8
184000
45400
0.009
15800



23
0.007
0.03
0.3
0.002
0.0045
0.001
35
1350° C. × 50 hr
175.5
138000
32000
0.015
15950


Comparative
24
0.005
0.03
0.3
0.002
0.0008
0.010
18
none
0
65800
9600
0.090
15900


Example
25
0.006
0.04
0.3
0.002
0.0012
0.008
15

1100° C. × 5 hr

8.4
75500
8800
0.075
15800



26
0.006
0.04
0.3
0.002
0.0004
0.011
20

1200° C. × 20 hr

38.7
95000
20200
0.085
16050



27
0.006
0.05
0.2
0.001
0.0008
0.008
21

1300° C. × 3 hr

30.9
87000
11000
0.065
16000



28
0.005
0.04
0.3
0.002
0.0010
0.012
16
1350° C. × 50 hr
175.5
89000
9500
0.070
16050



29
0.008
0.02
0.2
0.003
0.0010

0.095

25
1325° C. × 70 hr
176.6
55000
7500
0.105
16850



30
0.008
0.05
0.3
0.001

0.0077

0.007

95

1350° C. × 60 hr
192.2
72000
9500
0.095
15950



31

0.025

0.05
0.2
0.002
0.0012
0.009
18
1325° C. × 70 hr
178.6
72000
10500
0.075
15800



32
0.004

1.8

0.2
0.001
0.0000
0.010
20
1350° C. × 50 hr
175.5
82000
9500
0.080
15900



33
0.004
0.05

2.8

0.002
0.0010
0.009
15
1250° C. × 10 hr
39.8
75000
8800
0.095
15750



34
0.005
0.03
0.3

0.075

0.0008
0.010
14
1250° C. × 45 hr
84.5
68000
7200
0.100
15850



















Alternating current








magnetization





property
Number





Effective
of
Ni
Equiaxed crystal





permeability μtext missing or illegible when filed
inclusions/

text missing or illegible when filedgregation

ratio of




No.
(1 kHz)
mm2
amount(%)
slab(%)







Example
18
5200
8.8
0.1 
0.1




19
4800
79
0.14
0  




20
4700
10.6 
0.15
0.2




21
5300
7  
0.09
0.5




22
5800
9.5
0.06
0.4




23
4500
17.5 
0.07
0.3



Comparative
24
2900
7.5

0.42

0.1



Example
25
3200
9.5

0.35

0  




26
3500
10  

0.17

0.4




27
3600
8.8

0.19

0.5




28
3000
10.5 

0.25


32.5





29
2200
11.2 
0.1 
0  




30
2800

35.6

0.05
0.2




31
3100
12.5 
0.1 
0.4




32
2900
8.7
0.09
0.3




33
3000
7.8
0.13
0.1




34
2800
9.8
0.14
0  

















TABLE 5








Materials corresponding to PC (JIS alloy)


















Homogenizing
Direct current



heat
magnetization properties













Trace components
treatment
Maximum
Initial






























O/
Temperature ·
(D · t)0.5/
permeability
permeability
Hc/
B20/



No.
C
Si
Mn
P
S
Al
ppm
Time
μm
μm
μl
Oa
gauss





Example
35
0.004
0.06
0.3
0.002
0.0005
0.002
8
1350° C. × 50 hr
175.5
650000
365000
0.0045
7900



36
0.006
0.02
0.2
0.001
0.0004
0.005
5
1250° C. × 45 hr
84.5
560000
228000
0.0050
7950



37
0.005
0.04
0.3
0.002
0.0006
0.009
6
1250° C. × 10 hr
39.8
450000
219000
0.0055
7850



38
0.005
0.05
0.2
0.001
0.0007
0.007
8
1325° C. × 70 hr
176.6
580000
334000
0.0050
8000



39
0.005
0.03
0.3
0.002
0.0008
0.008
10 
1370° C. × 45 hr
188.8
720000
495000
0.0030
7850



40
0.007
0.03
0.3
0.002
0.0025
0.010
25 
1350° C. × 50 hr
175.5
480000
205000
0.0055
7900


Comparative
41
0.005
0.05
0.3
0.001
0.0007
0.015
7
none
0
254000
76000
0.0080
7850


Example
42
0.006
0.04
0.3
0.002
0.0009
0.007
10 

1100° C. × 5 hr

8.4
278000
88000
0.0075
7900



43
0.006
0.02
0.2
0.002
0.0005
0.011
8

1200° C. × 20 hr

38.7
298000
92000
0.0070
8050



44
0.006
0.05
0.2
0.001
0.0008
0.008
10 

1300° C. × 3 hr

30.9
285000
95000
0.0070
8000



45
0.005
0.03
0.3
0.002
0.0006
0.008
8
1350° C. × 50 hr
175.5
267000
88000
0.0075
7950



46
0.006
0.04
0.3
0.002
0.0005

0.052

7
1325° C. × 70 hr
176.6
198000
63500
0.0100
7950



47
0.006
0.05
0.3
0.001

0.0060

0.005

67

1350° C. × 80 hr
192.2
220000
85000
0.0090
8000



48

0.042

0.05
0.3
0.002
0.0009
0.009
10 
1325° C. × 70 hr
176.6
248000
82000
0.0105
7900



49
0.004

2.3

0.2
0.001
0.008
0.010
9
1350° C. × 50 hr
175.5
256000
95000
0.0095
8050



50
0.005
0.04

3.2

0.002
0.0010
0.009
8
1250° C. × 10 hr
39.8
187000
79000
0.105
7950



51
0.003
0.03
0.3

0.055

0.0007
0.010
14 
1250° C. × 45 hr
84.5
215000
85000
0.115
7850



















Alternating current








magnetization





property
Number





Effective
of
Ni
Equiaxed crystal





permeability μtext missing or illegible when filed
inclusions/

text missing or illegible when filedgregation

ratio of




No.
(1 kHz)
mm2
amount(%)
slab(%)







Example
35
8500
2.5
0.09
0.1




36
7600
1.8
0.12
0.2




37
7500
3.6
0.15
0.4




38
6500
4.2
0.09
0.1




39
9700
5.4
0.06
0.2




40
6000
7.5
0.08
0.5



Comparative
41
5400
4.5

0.39

0.4



Example
42
5500
3.8

0.32

0.2




43
5800
2.8

0.18

0  




44
5900
5.4

0.19

0.1




45
4900
5.8

0.35


46.5





46
4500
6.5

0.10

0.5




47
5200

32.5

0.06
0.1




48
4800
6.4
0.12
0.4




49
5000
6.5
0.08
0.3




50
4200
3.5
0.11
0.5




51
4000
5.4
0.12
0.2










As mentioned above, according to the invention, there can be provided Fe—Ni based permalloys having magnetic properties considerably higher than those of the conventional technique. Particularly, there can be obtained PD materials as a substitute of PB material used in a stator for watch, ball beads for electromagnetic lens and the like, PB materials as a substitute of PC material used as a magnetic head, a magnetic shielding material, a transformer core for communication equipments and the lie, and PC materials having excellent magnetic properties and indicating high sensitivity and frequency characteristics, respectively.

Claims
  • 1. A Fe—Ni based permalloy made of a hot rolled sheet comprising Ni: 70-85 wt %, C: not more than 0.015 wt %, Si: not more than 1.0 wt %, Mn: not more than 1.0 wt %, P: not more than 0.01 wt %, S: not more than 0.005 wt %, O: not more than 0.006 wt %, Al: not more than 0.02 wt % and having such magnetic properties that a maximum magnetic permeability μm is not less than 400000, an initial magnetic permeability ui is not less than 200000 and a coercive force Hc is not more than 0.006 (Oe), provided that Ni segregation amount CNis represented by the following equation is not more than 0.10 wt %: CNis=analytical value of Ni component (wt %)×CiNis (c.p.s.)/CiNiave. (c.p.s.) wherein CiNis: a standard deviation of X-ray intensity (c.p.s.) CiNiave.: an average intensity of total X-ray intensities (c.p.s.).
  • 2. A Fe—Ni based permalloy according to claim 1, wherein an amount of non-metallic inclusion having a diameter corresponding to a circle of not less than 0.1 μm is not more than 20 particles/mm2.
  • 3. A Fe—Ni based permalloy according to claim 1, wherein an amount of non-metallic inclusion having a diameter corresponding to a circle of not less than 0.1 μm is not more than 10 particles/mm2.
  • 4. A Fe—Ni based permalloy made of a hot rolled sheet comprising Ni: 70-85 wt %, C: not more than 0.015 wt %, Si: not more than 1.0 wt %, Mn: not more than 1.0 wt %, P: not more than 0.01 wt %, S: not more than 0.005 wt %, O: not more than 0.006 wt %, Al: not more than 0.02 wt %, and not more than 15 wt % of at least one selected from the group consisting of Mo, Cu, Co and Nb within a range of not more than 20 wt % in total, and having such magnetic properties that a maximum magnetic permeability μm is not less than 400000, an initial magnetic permeability μi is not less than 200000 and a coercive force Hc is not more than 0.006 (Oe), provided that Ni segregation amount CNis represented by the following equation is not more than 0.15 wt %: CNiS=analytical value of Ni component (wt %)×CiNis (c.p.s.)/CiNiave. (c.p.s.) wherein CiNis: a standard deviation of X-ray intensity (c.p.s.) CiNiave.: an average intensity of total X-ray intensities (c.p.s.).
  • 5. A Fe—Ni based permalloy according to claim 4, wherein the Ni segregation amount CNis is not more than 0.10 wt %.
  • 6. A Fe—Ni based permalloy according to claim 4, wherein an amount of non-metallic inclusion having a diameter corresponding to a circle of not less than 0.1 μm is not more than 20 particles/mm2.
  • 7. A Fe—Ni based permalloy according to claim 4, wherein an amount of non-metallic inclusion having a diameter corresponding to a circle of not less than 0.1 μm is not more than 10 particles/mm2.
Priority Claims (2)
Number Date Country Kind
2000-300632 Sep 2000 JP national
2001-23275 Jan 2001 JP national
CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of application Ser. No. 10/424,818 filed Apr. 29, 2003, which is a divisional of application Ser. No. 09/961,366, filed Sep. 25, 2001, now U.S. Pat. No. 6,656,419 B2, which applications are hereby incorporated by reference herein in their entireties. The present application claims priority under 35 U.S.C. § 119 of Japanese Application Nos. 2000-300632, filed Sep. 29, 2000 and 2001-023275, filed Jan. 31, 2001.

Divisions (1)
Number Date Country
Parent 09961366 Sep 2001 US
Child 10424818 Apr 2003 US
Continuations (1)
Number Date Country
Parent 10424818 Apr 2003 US
Child 11544601 Oct 2006 US