Patent Application
20080255674
This document relates to the manufacture of a ceramic-metal composite, and more particularly to a ceramic-composite for a medical device.
Total hip arthroplasty, or total hip replacement, is an orthopedic procedure in which a surgically implanted device replaces a worn, damaged, or diseased hip joint. The surgically implanted device assumes the functions of the replaced hip joint, including support and joint articulation. The components of the surgically implanted device typically include an acetabular cup, a femoral head, and a femoral stem. The acetabular cup is a socket implanted into the hip that receives the femoral head having a smooth hemispherical surface adapted for articulation with the acetabular cup. The opposite end of the femoral head is attached to a fitting on the femoral stem, which is attached at its other end to the femur of a patient.
The implanted device should be biocompatible, structurally strong, tough, and wear-resistant. Further, the articulation between the acetabular cup and the femoral head should produce relatively low frictional engagement. These requirements, often conflicting, affect the choice of materials used to construct implanted devices. In particular, the femoral head should possess a hard and wear-resistant articulating outer surface, while also possessing tough, crack-resistant material properties in the region where the femoral head attaches to the femoral stem.
Therefore, a need exists in the art for an articulating structure to be used in an implanted orthopedic device that simultaneously possesses high hardness at the joint articulating surface, and high toughness where the structure joins to the underlying attachment structures.
In one embodiment, a ceramic-metal composite is manufactured having an exterior ceramic layer with a relatively narrow thickness that may be bonded to a metal layer in a hot pressing process.
In another embodiment, a medical device may include a first articulating component made from a ceramic-metal composite with an exterior ceramic layer bonded to an inner metal core with the first articulating component adapted to engage a second articulating component. The first articulating component may have a hemispherical configuration in which the exterior ceramic layer is used as an articulating surface adapted to rotatably engage the second articulating component.
In yet another embodiment, the medical device may include a femoral head adapted to engage an acetabular cup for use in total hip arthroplasty. The femoral head may have a multi-layered body made of a ceramic-metal composite with a ceramic exterior layer as an articulating surface bonded to an inner metal core. The inner metal core may define an inner bore adapted to engage a femoral stem taper, while the ceramic exterior layer may be rotatably engaged to the acetabular cup in an articulating relationship.
In one embodiment, the femoral head may include a multi-layered body having a metal inner core bonded to a ceramic outer layer, the ceramic layer having an interface layer and an exterior ceramic layer. The interface layer may include one or more sub-layers made from a graded mixture of ceramic and metal materials.
In a further embodiment, a method for manufacturing an orthopedic implant component made from a ceramic-metal composite may include cold-pressing powdered metal and ceramic materials to form a compressed powder body, followed by hot pressing to consolidate and sinter the compressed powder body.
Additional objectives, advantages and novel features will be set forth in the description which follows, or will become apparent to those skilled in the art upon examination of the drawings and detailed description which follows.
Corresponding reference characters indicate corresponding elements among the view of the drawings. The heading used in the figures should not be interpreted to limit the scope of the claims
Referring to the drawings, an embodiment of the femoral head is illustrated and generally indicated as 10 in
In one embodiment, the inner metal core 12 may be made of metal or metal alloys, such as Nb, Zr, Ti, Ta, Co, V, Cr, Al, alloys thereof, stainless steel, and combinations thereof. Any metal or metal alloy may be used to fabricate the metal core 12, so long as the material is biocompatible, bonds strongly to the ceramic material in the outer layer, and possesses adequate tensile strength and toughness to bear the loads experienced on the prosthetic joint during normal activities such as walking, running, standing, and jumping. The diameter of the metal inner core may range between about 10 mm and about 40 mm, and more preferably between about 25 mm and about 30 mm. The dimensions of the inner metal core 12 may be sized to assure that the metal material absorbs nearly all of the tensile stresses acting on the femoral head 10 via the metal taper 20, as determined by structural analysis techniques such as finite element modeling.
The exterior ceramic layer 14 is made of a ceramic material that may have a thickness ranging between about 200 microns and about 10 mm. For example, ceramic materials that may be used to manufacture the ceramic outer layer 14 include alumina, zirconia, chromium carbide, chromium nitride, silicon carbide, silicon nitride, titanium carbide, zirconium carbide, zirconium nitride, tantalum carbide, and tungsten carbide, pure or doped with other elements, composites of these ceramics containing one or more metal or ceramic phases, and combinations thereof. The ceramic exterior layer 14 may be fabricated from any ceramic material so long as the material is biocompatible, and possesses sufficient hardness and wear resistance to withstand the loads and wear on the femoral head 10 generated by normal activities such as walking, running, standing, and jumping. The thickness of the ceramic exterior layer 14 is dimensioned to ensure that adequate material exists to provide the needed structural integrity throughout the anticipated working life of the prosthetic femoral head 10.
In order to optimize the fabrication process, the metal material used to fabricate the metal core 12 may possess a similar melting point and coefficient of thermal expansion as the ceramic material used to fabricate the ceramic exterior layer 14. If the melting points of the metal and ceramic materials are significantly mismatched, the fabrication process may be constrained to occur at the lower melting point temperature, which may lengthen the fabrication time. If the coefficients of thermal expansion are significantly mismatched, residual stresses may form in the femoral head 10 during fabrication that may need to be ameliorated through the inclusion of an interface layer 13.
As shown in
The composition and thickness of the interface layer 13, in an embodiment, are selected to minimize the presence of residual stresses within the femoral head 10 resulting from the fabrication process. In addition, the interface layer 13 provides a more gradual transition between the hard, brittle exterior ceramic layer 14, and the softer, tougher metal core 12. The composition of the interface layer 13 or discrete sub-layers (not shown) may be mixtures of the metal and ceramic materials used for the metal inner core 12 and ceramic exterior layer 14, respectively. The fraction of the total volume of the interface layer 13 or discrete sub-layers may range between about 5% and about 95% of metal material, and may range between about 95% and about 5% of ceramic material. More preferably, the fraction of the total volume of the interface layer 13 or discrete sub-layers may range between about 10% and about 90% of metal material, and may range between about 90% and about 10% of ceramic material. In embodiments that include one or more discrete sub-layers in the interface layer 13, those layers with the highest metal content may be located nearest to the metal core 12. The number of discrete sub-layers may be minimized to reduce the cost and complexity of the fabrication process. The number of discrete sub-layers, if present, may range between about 1 and about 10 sub-layers, and more preferably between about 1 and about 5 sub-layers.
The overall diameter of the hemispherical femoral head 10 is sized to closely fit with the prosthetic acetabular cup of the prosthetic hip. The diameter of the femoral head 10 may range between about 20 mm and about 55 mm, and more preferably between about 26 mm and about 36 mm. The diameter of the tapered bore 16 is sized to closely fit the metal taper 20 of the femoral stem, thereby allowing the femoral head 10 to be force fitted to the metal taper 20 of the femoral stem. The diameter of the metal taper may range between about 10 mm and about 25 mm, and more preferably may range between about 10 mm and about 18 mm.
The femoral head 10 may be fabricated using powdered metal and ceramic materials using known fabrication techniques such as cold pressing and hot pressing. In an embodiment, a powdered ceramic mixture and a powdered metal mixture are assembled into a “green body” made of the powdered materials formed into the layers of the approximate dimension of the desired end product. The “green body” is then formed into the desired end product by known hot pressing processes.
In an embodiment, the powdered ceramic mixture may include the ceramic materials listed above such as alumina or zirconia, ground to a particle size of less than about 10 microns, and more preferably less than about 1 micron. The powdered ceramic mixture may also include ceramic conditioners such as magnesium nitrate, magnesium oxide, and other magnesium compounds, ground to a particle size of less than about 10 microns, and more preferably less than about 1 micron. The powdered metal mixture may include the metal materials listed above such as niobium or titanium, with a particle size of less than about 100 microns. The powdered metal mixture may also include a sintering additive such as cobalt powder with a particle size of less than about 100 microns.
The hot pressing processes used in various embodiments may include uniaxial hot pressing or isostatic hot pressing. In alternative embodiments, the ceramic exterior layer 14 may be fabricated using powder-based methods that utilize other known alternative consolidation methods, slurry-based methods, and vapor phase deposition methods such as CVD or PECVD.
Once the desired end product such as a femoral head 10 is provided, the exterior surface may be machined to its desired exterior contour using known techniques such as grinding or computerized diamond machining. In addition, the tapered bore 16 may be preformed or machined using known methods such as drilling or electrical discharge machining (EDM).
The ceramic-metal materials described herein may be used to fabricate the articulating components of orthopedic implants including prosthetic hips, prosthetic knees, prosthetic shoulders, prosthetic interphalangial joints, and prosthetic vertebrae.
The following examples illustrate various iterations of the present invention.
To demonstrate the feasibility of fabricating alumina-niobium functionally graded composites in a hemispherical shape, the following experiment was conducted.
Commercially obtained ceramic and metal powdered materials were used to fabricate the hemispherical green bodies. Alumina (Al2O3) powder (Nanostructured & Amorphous Materials, Inc., 99.97%, 150 nm average particle size) was doped with 0.25% MgO by weight by combining the Al2O3 with magnesium nitrate (Mg(NO3)2.6H2O, Johnson Matthey, Materials Technology, UK). The required quantities of the magnesium nitrate were dissolved in a small amount of water and then mixed with reagent grade ethanol. Al2O3 powder was added to the magnesium nitrate-ethanol solution, and the mixture was heated at about 80° C. and stirred to evaporate the solvents. The dried sediment was ground with an agate mortar and pestle for 30 minutes and then calcined at 60020 C. for an additional hour. Prior to use, the calcined Al2O3 powder doped with 0.25% MgO by weight was ground again to a uniform consistency.
The metal powder was prepared by combining elemental niobium (Nb) powder (Cerac, 99.8%, −325 mesh) and a powdered cobalt sintering additive (Cerac, 99.9%, average particle size <4 μm). Cobalt powder was added to the niobium powder to make up 3% of the total weight of the mixture. The mixture was ground in an agate mortar for approximately one hour until a uniform powder consistency was achieved.
Due to small differences in the thermal expansion coefficients of alumina and niobium, interfacial residual stresses may be created between the two materials after the hot pressing process. To further reduce the thermal stress and to promote the interfacial thermal expansion coefficient matching between the two materials, powders for a series of transition layers were prepared. The transition layers consisted of the MgO doped alumina and Nb(3Co) mixtures with the following proportions of materials (expressed as % volume): 50% Nb(3Co):50% Al2O3, 30% Nb(3Co):70% Al2O3, and 10% Nb(3Co):90% Al2O3. All transition layer mixtures were ground with agate mortar and pestle for 30 minutes to achieve homogeneous mixtures of uniform consistency.
The laminated composite green bodies for the Al2O3 enwrapped Nb(3Co) hemispherical bearings were prepared by cold pressing the powders into a steel die in layers. The 100% Nb(3Co) powder was first pressed into a hemispherical shape, and then the transition layers were built up. The 50% Nb(3Co):50% Al2O3 was pressed onto the hemispherical shape in a layer thickness of about 1.5 mm to 2 mm, followed by the 30% Nb(3Co):70% Al2O3 powder, and then the 10% Nb(3Co):90% Al2O3 powder. A 1.5-2 mm layer of 100% MgO doped alumina powder was pressed on top of the transition layers, and the entire composite hemispherical body was subjected to cold isostatic pressing to increase the green body's density.
The green hemispherical body was transferred to a graphite die and surrounded with AIN powder for the hot pressing stage in an elevated temperature furnace with a graphite heating element in an argon atmosphere. Prior to heating, the furnace chamber was pumped down to below 100 mtorr of vacuum, then filled and refilled three times with 99.998% pure argon gas. The specimens were heated at a rate of 10° C.-15° C. per minute until a furnace temperature of about 1100° C. was achieved. The hemispherical body was then loaded with a uniaxial pressure at a rate of about 2 MPa per minute until a pressure of about 35 MPa was achieved. The furnace temperature during uniaxial pressure loading continued to increase up to a maximum of about 1400°-1450° C. The specimens were then cooled at a rate of about 10° C. per minute to a temperature of about 1200° C., and then the uniaxial pressure was slowly released from the hemispherical body down to a pressure of about 15 MPa. When the specimen had achieved a uniaxial pressure of about 15 MPa and a temperature of about 1000° C., the furnace was turned off and the uniaxial pressure was released from the hemispherical body.
After hot pressing, the outer surface of the hemispherical body was machined and polished. The Nb core was drilled using EDM machining to produce a central bore. The resulting Al2O3 enwrapped Nb(3Co) bearings had a spherical diameter of 32 mm with a tapered bore in the Nb metal core (Ø12×16).
The results of this experiment demonstrated the feasibility of fabricating a hemispherical bearing from a ceramic-metal composite materials using a technique of cold-pressing powdered materials in graded layers, followed by hot uniaxial pressing.
To demonstrate the feasibility of fabricating alumina-niobium functionally graded composites in a hemispherical shape, the following experiment was conducted.
Alumina-niobium composite material samples fabricated in a disc shape using the methods described in Example 1 were sectioned by cutting along the axes of the disc using a diamond saw. The microstructures and interfaces of each of the layers of the composite bearing were investigated using scanning electron microscopy (SEM).
To further characterize the transition between the layers of the composite material sample, concentration distributions of Nb and Al atoms in the sample were detected using an EDS surface scanning technique.
To verify that no chemical reaction occurred between the materials comprising the composite, the composite material sample was subjected to XRD detection (Model D/mas 2550 v; Rigaku, Japan), Cu Kα radiation (λ=0.154056 nm)) at a scanning rate of 1.8°/min in the 2θ range of 10°-120°.
The results of this study indicated that the alumina-niobium composite material was characterized by stepwise graded layers with no third phase formation, with continuous distribution of phases between layers, indicating strong bonding between layers.
To determine the flexural strength of the alumina-niobium functionally graded composite material, the following experiment was conducted. Alumina-niobium composite material samples fabricated in a disc shape using the methods described in Example 1 were sectioned into rectangular beams, taken parallel to the sample surface to which the external pressure was applied, using a diamond saw. Beams were machined to lengths of about 25 mm, thicknesses of about 1.8 mm and widths of about 2.0 mm, as shown as
The flexural strength of the composite material samples was tested using four-point bending with an inner span of 10 mm and an outer span of 20 mm. The flexural strength was measured according to the ASTM standard of C1161-02c at a crosshead speed of 0.2 mm/min. The flexural strength (S) was calculated according the following equation:
where P is the load at fracture, L=20 mm is the outer (support) span, b is the sample width and d is the sample thickness.
Young's modulus (E) was estimated from the linear load-deflection curve under compressive stress obtained during four-point flexure testing, and was calculated according to the equation:
where m is the slope of tangent to the initial straight-time portion of the load-deflection curve (N/mm), and L, b, and dare defined as in Eq. (1).
The data in Table 1 showed that the composites combining Al2O3 and Nb together possessed higher flexural strengths than the flexural strength of either Al2O3 or Nb alone. Most likely, the higher strength of the composite material was due to the presence of the ductile Nb layer, which resulted in compressive loading of the Al2O3 layer. When a crack intersected the Nb/Al2O3 interface, plastic deformation of the Nb reduced the crack-tip stress intensity, preventing crack propagation through the Nb, thereby delaying the failure of the material samples.
The micro-hardness of the Nb(3Co) particles and Al2O3 matrix was also determined using a microhardness tester (Tukon microhardness tester, Page-Wilson Corporation) with a 200-gram load. The hardness of Nb(3Co) particles was measured to be 551 kgf/mm2 and the hardness of Al2O3 was measured to be 3097 kgf/mm2.
The results of this experiment indicated that the Al2O3-Nb layered composite material exhibited a flexural strength that was higher than either of the two materials in isolation. The addition of the Nb layer to the Al2O3 enhanced the flexural strength of the resulting material by inhibiting the propagation of cracks that originated in the more brittle, but stiffer Al2O3 layer.
To determine the fracture morphology of the alumina-niobium functionally graded composite material, the following experiment was conducted. SEM images of alumina-niobium composite samples fabricated as described in Example 1 were obtained to visualize the distribution and patterning of cracks formed in the material samples during flexural strength testing as described in Example 3.
The SEM images shown in
The results of this experiment lent further support to the conclusion that the enhanced fracture toughness of the layered Al2O3/Nb composite materials was due to the strong bonding between the composite layers, coupled with the ability of the Nb layer to inhibit crack propagation through the material.
It should be understood from the foregoing that, while particular embodiments have been illustrated and described, various modifications can be made thereto without departing from the spirit and scope of the invention as will be apparent to those skilled in the art. Such changes and modifications are within the scope and teachings of this invention as defined in the claims appended hereto.
This application claims priority from U.S. provisional patent application Ser. no. 60/922,611, entitled “Ceramic-Metal Composite Femoral Head and Method of Fabrication” filed on Apr. 10, 2007.
| Number | Date | Country | |
|---|---|---|---|
| 60922611 | Apr 2007 | US |