Patent Application
20060108619
The present invention relates to a single-crystal ferromagnetic group IV-based semiconductor or a single-crystal ferromagnetic group III-V-based or II-VI-based compound semiconductor, which has ferromagnetic properties achieved by adding at least one rare-earth metal element selected from the group consisting of Ce, Pr, Nd, Pm, Sm, Eu, Gd, Th, Dy, Ho, Er, Tm, Yb and Lu, to a group IV-based semiconductor or a group III-V-based or group II-VI-based compound semiconductor, which is transparent to light having a wavelength in the range of the infrared to ultraviolet regions, so as to form a mixed crystal of them. The present invention also relates to a method for adjusting a ferromagnetic characteristic of the ferromagnetic semiconductor.
The realization of a single-crystal ferromagnetic thin film having both light transparency and ferromagnetic properties will open the way for obtaining optical isolators or optically assisted high-density magnetic recording essential for mass communication, and preparing electromagnetic materials required for future mass communication. Thus, it is desired to provide a material having both light transparency and ferromagnetic properties.
A group IV-based semiconductor, such as diamond, or a group III-V-based or group II-VI-based compound semiconductor exhibits the property of being transparent to light having a wavelength in the range of the infrared to ultraviolet regions, based on their large bandgap [diamond (Eg=5.4 eV), ZnSe (Eg=2.7 eV), ZnO (Eg=3.3 eV), ZnS (Eg=3.9 eV), GaN (Eg=3.3 eV), AlN (Eg=6.4 eV), BN (Eg=6.4 eV)], and has a high exciton binding energy. Thus, if ferromagnetic properties can be given to these semiconductors, the obtained ferromagnetic semiconductor will lead to major progress in an optical device for spin electronics, such as an optical quantum computer utilizing coherent spin states.
The inventors previously filed a patent application for invention concerning a transition metal-containing ferromagnetic ZnO-based compound and a method of adjusting ferromagnetic characteristics thereof (Japanese Patent Laid-Open Publication No. 2001-130915).
However, neither ferromagnetic states achieved in a group III-V-based or group II-VI-based compound semiconductor doped with rare-earth metal, nor ferromagnetic states achieved in a group III-V-based or group II-VI-based compound semiconductor having a high ferromagnetic transition temperature (Curie point) has been reported. Further, in the field of silicon technologies, any silicon exhibiting ferromagnetic properties has not been reported. The realization of a silicon material having ferromagnetic properties will also provide a wider application range thereof.
As mentioned above, if stable ferromagnetic properties are obtained in a group IV-based semiconductor or a group III-V-based or group II-VI-based compound semiconductor, the obtained ferromagnetic semiconductor can be used in combination with a light-emitting element, such as a semiconductor laser, comprising a group IV-based semiconductor or a group III-V-based or group II-VI-based compound semiconductor having a high exciton binding energy, and allows for a significantly extended application range of magnetooptic spin-based electronic devices utilizing magnetooptic effects.
Further, in cases where the obtained ferromagnetic semiconductor is used in a ferromagnetic memory utilizing the change in magnetization state to be induced by light irradiation, the ferromagnetic semiconductor has to be prepared to have desired ferromagnetic characteristics, for example, a ferromagnetic transition temperature (Curie temperature) adjusted at a value (slightly greater than a room temperature) which allows the magnetization state to be changed by light irradiation.
In view of the above circumstances, it is an object of the present invention to provide a ferromagnetic group IV-based semiconductor or a ferromagnetic group III-V-based or group II-VI-based compound semiconductor to be obtained using a group IV-based semiconductor or a group III-V-based or group II-VI-based compound semiconductor which is transparent to light.
It is another object of the present invention to provide a method for adjusting a erromagnetic characteristic, e.g. ferromagnetic transition temperature, of a ferromagnetic group IV-based semiconductor or a ferromagnetic group III-V-based or group II-VI-based compound semiconductor, in the process of preparing the ferromagnetic group IV-based semiconductor or the ferromagnetic group III-V-based or group II-VI-based compound semiconductor.
The inventors have been dedicated to researches for obtaining a single crystal with ferromagnetic properties using a group IV-based semiconductor or a group III-V-based or group II-VI-based compound semiconductor which has a wide bandgap suitable, particularly, as a material transparent to light.
During the course of these researches, the inventors found that even if about 1 to 25 at % of metal ion, such as Si in a group IV-based semiconductor, Ga in a group III-V-based compound semiconductor or Zn in a group II-VI-based compound semiconductor, is substituted with at least one rare-earth metal element selected from the group consisting of Ce, Pr, Nd, Pm, Sm, Eu, Gd, Th, Dy, Ho, Er, Tm, Yb and Lu (to form a mixed crystal of them), at a low temperature through a nonequilibrium crystal growth process, a single crystal can be adequately obtained.
The inventors also found that when at least one rare-earth metal element selected from the group consisting of Ce, Pr, Nd, Pm, Sm, Eu, Gd, Th, Dy, Ho, Er, Tm, Yb and Lu is added to a group IV-based semiconductor or a group III-V-based or group II-VI-based compound semiconductor to form a mixed crystal of them, a hole or electron is doped into the semiconductor (the number of electrons is increased or reduced) due to the change in electronic state, so as to allow the semiconductor to have ferromagnetic properties.
Further, the inventors found that while a group III-V-based compound semiconductor exhibits no ferromagnetic property by means of the formation of a mixed crystal of Gd added thereto by itself, desired ferromagnetic properties can be obtained therein by co-doping a donor, such as oxygen.
Furthermore, the inventors found that the formation of a mixed crystal by means of adding at least one rare-earth metal element selected from the group consisting of Ce, Pr, Nd, Pm, Sm, Eu, Gd, Th, Dy, Ho, Er, Tm, Yb and Lu to a group IV-based semiconductor or a group III-V-based or group II-VI-based compound semiconductor provides the same effects as those to be obtained by adding a hole to 4f electrons.
As above, at least one rare-earth metal element selected from the group consisting of Ce, Pr, Nd, Pm, Sm, Eu, Gd, Th, Dy, Ho, Er, Tm, Yb and Lu can be simply added to a group IV-based semiconductor or a group III-V-based or group II-VI-based compound semiconductor to form a mixed crystal of them, so as to allow the semiconductor to be put into a stable ferromagnetic state.
Through the subsequent continuous researches, the inventors found that each of the rare-earth metals consisting of Ce, Pr, Nd, Pm, Sm, Eu, Gd, Th, Dy, Ho, Er, Tm, Yb and Lu is put into a high spin state having an electronic spin s=1/2, 1, 3/2, 2, 5/2, 3 or 7/2, and a ferromagnetic transition temperature of a ferromagnetic semiconductor to be obtained can be adjusted by changing a combination of or the ratio between two or more of these elements, or adding n-type and/or p-type dopants.
The inventors also found that the above technique can be used to provide a more stabilized ferromagnetic state than antiferromagnetic and paramagnetic states, and adjust energy in the ferromagnetic state (for example, an energy for allowing the ferromagnetic state to be generally maintained although a slight difference in the energy causes a spin glass state analogous to an antiferromagnetic state).
Further, the inventors found that the lowest transmission wavelength of the obtained ferromagnetic semiconductor is varied depending on the kind of the aforementioned rare-earth metal elements, and thereby one or more of these elements can be selectively formed as a mixed crystal to allow the obtained ferromagnetic semiconductor to have a desired filter function.
Thus, the concentration and/or mixing ratio of the rare-earth metal elements can be adjusted to provide a single-crystal ferromagnetic group IV-based semiconductor or a single-crystal ferromagnetic group III-V-based or group II-VI-based compound semiconductor, which has desired magnetic characteristics.
Specifically, the present invention provides a ferromagnetic group IV-based semiconductor or a ferromagnetic group III-V-based or group II-VI-based compound semiconductor, comprising a group IV-based semiconductor or a group III-V-based or group II-VI-based compound semiconductor, which contains at least one rare-earth metal element elected from the group consisting of Ce, Pr, Nd, Pm, Sm, Eu, Gd, Th, Dy, Ho, Er, Tm, Yb and Lu.
The group IV-based semiconductor herein is Si, diamond or Ge. The group III-V-based compound semiconductor is a compound, such as GaAs, GaSb, GaP, GaN, AlN, InN or BN, which is a combination of a group III atom of B, Al, Ga, In or TI, and a group V atom of N, P, As, Sb or Bi. The group II-VI-based compound semiconductor is a compound, such as ZnSe, ZnS, ZnTe, ZnO, CdS or CdSe, which is a combination of a group II atom of Be, Mg, Zn, Cd, Hg, Ca, Sr or Ba, and a group IV atom of O, S, Se or Te.
Each of the aforementioned rare-earth metal elements has an ionic radius relatively close to that of Zn, Cd, Ga, Al or In. Thus, even if these rare-earth metal elements are added to the semiconductor as a solid solution in an amount of 1 at % to 25 at % at a low temperature through a nonequilibrium crystal growth process, a single-crystal structure of the semiconductor serving as a matrix can be maintained, and the matrix semiconductor can exhibit ferromagnetic properties while maintaining the transparency thereof.
Each of the above rare-earth metal elements selected from the group consisting of Ce, Pr, Nd, Pm, Sm, Eu, Gd, Th, Dy, Ho, Er, Tm, Yb and Lu is different in the atomic level of their 4f atom and the amplitude of p-f hybridization. Thus, when at least two or more of these rare-earth metal elements are contained in the above semiconductor, the ferromagnetic characteristics of the semiconductor can be more directly varied as compared with hole-doping or electron-doping, so as to adjust a ferromagnetic characteristic, such as ferromagnetic transition temperature.
While the doping of at least one of an n-type dopant and a p-type dopant does not provide a direct effect as that between the rare-earth metal elements because it is incorporated into the matrix of the group IV-based semiconductor or the group III-V-based or group II-VI-based compound semiconductor, the dopant can act on a 4f electron adjacent to an atom constituting the group IV-based semiconductor or group III-V-based or group II-VI-based compound semiconductor so as to change the state of hole or electron to adjust the ferromagnetic characteristic.
The present invention also provides a method of adjusting a ferromagnetic characteristic of a ferromagnetic group IV-based semiconductor or a ferromagnetic group III-V-based or group II-VI-based compound semiconductor, which comprises adding either one of:
(1) at least two rare-earth metal elements selected from the group consisting of Ce, Pr, Nd, Pm, Sm, Eu, Gd, Th, Dy, Ho, Er, Tm, Yb and Lu;
(2) the at least two rare-earth metal elements, and at least one metal element selected from the group consisting of Th, Pa, U, Np, Pu, Am, Cm, Bk, Cf, Es, Fm, Md, No and Lr; and
(3) the above (1) or (2), and at least one of an n-type dopant and a p-type dopant, to a group IV-based semiconductor or a group III-V-based or group II-VI-based compound semiconductor so as to adjust the ferromagnetic characteristic according to a combination of the rare-earth metal elements.
Further, the present invention provides a method of adjusting a ferromagnetic characteristic of a ferromagnetic group IV-based semiconductor or a ferromagnetic group III-V-based or group II-VI-based compound semiconductor, which comprises adding either one of:
(1) at least one rare-earth metal element selected from the group consisting of Ce, Pr, Nd, Pm, Sm, Eu, Gd, Th, Dy, Ho, Er, Tm, Yb and Lu;
(2) the at least one rare-earth metal element, and at least one metal element selected from the group consisting of Th, Pa, U, Np, Pu, Am, Cm, Bk, Cf, Es, Fm, Md, No and Lr; and
(3) the above (1) or (2), and at least one of an n-type dopant and a p-type dopant, to a group IV-based semiconductor or a group III-V-based or group II-VI-based compound semiconductor, and controlling the concentration of one of the at least one rare-earth metal element, the at least one metal element selected from the group consisting of Th, Pa, U, Np, Pu, Am, Cm, Bk, Cf, Es, Fm, Md, No and Lr, and the at least one of an n-type dopant and a p-type dopant so as to adjust the ferromagnetic characteristic.
Specifically, according to the above methods, a ferromagnetic transition temperature as one of ferromagnetic characteristics can be adjusted.
In the above method, at least one or more of the rare-earth metal elements and at least one or more of the actinide elements described in the (2) may be added to form a mixed crystal so as to adjust an energy in a ferromagnetic state, and allow the energy to be reduced as a whole according to a kinetic energy of a hole or electron introduced from the rare-earth metal elements by themselves, to stabilize said ferromagnetic state.
Further, at least one or more of the rare-earth metal elements and at least one or more of the actinide elements described in the (2) may be added to form a mixed crystal so as to control the magnitude and the positive/negative sign of the magnetic interaction between the rare-earth metal atoms according to a hole or electron introduced from the rare-earth metal elements by themselves, to stabilize said ferromagnetic state.
Furthermore, at least one or more of the rare-earth metal elements and at least one or more of the actinide elements described in the (2) may be added to form a mixed crystal so as to control the magnitude and the positive/negative sign of the magnetic interaction between the rare-earth metal atoms and a light transmission characteristic to be obtained from the mixed crystallization of the rare-earth metal elements and the actinide elements, according to a hole or electron introduced from the rare-earth metal elements by themselves, to provide a desired light filter characteristic in the ferromagnetic group IV based semiconductor the ferromagnetic group III-V-based or the group II-VI-based compound semiconductor.
The rare-earth metal-containing magnetic semiconductor of the present invention can emit sharp light reflecting the magnetic states without variation in temperature, and the emission may be utilized to generate circularly polarized light.
In observation of a temperature dependence of the wavelength of emission induced by excitation using ultraviolet light, the emission wavelength is not varied at all in the range of liquid helium temperatures to room temperatures. The no-variation with the temperature would result from a sharp energy level in the ground state and in the excited state of electrons in the 4-f shell, and negligible influences of lattice vibrations and a humidity dependence of the matrix semiconductor. In conventional optical communications using emission from an AlGaSb light-emitting element, it is required to use a Peltier element or the like because of occurrence of variation in wavelength due to temperature change. The semiconductor of the present invention capable of generating light emission without any variation in wavelength due to temperature change is suitable for high-performance optical communications.
The 4f-electron state of a rare-earth metal ion belonging to lanthanoid elements except for La having no 4f electron has a large electronic spin in a high spin state, and an orbital angular momentum spin based on orbital angular momentum. Further, there is 1 eV (equivalent to 8000 K) of strong ferromagnetic spin interaction between 4f electrons and 5d electrons which are valence electrons. Thus, such a rare-earth metal can be added to the semiconductor as a solid solution to stabilize a ferromagnetic state, in which an impurity band formed in the bandgap of the semiconductor and partly occupied by electrons to have a narrow bandwidth and a large electron correlation energy is utilized to achieve a ferromagnetic state based on the gain of band energy.
According to the present invention, the kind and/or concentration of the rare-earth elements can be adjusted to obtain a transparent ferromagnetic semiconductor which allows visible light to pass therethrough and has a high ferromagnetic transition temperature of greater than room temperatures or 400 K or more, using AlN or GaN. The phenomenon that the circular polarization direction of light is rotated by ferromagnetism when the light passes through a transparent material is referred to as “Kerr effect”. A ferromagnetic semiconductor providing a larger rotation angle is more excellent in performance as a device, such as optical isolators, utilizing magnetooptic effects. In Eu-doped or Gd+O-doped GaN or AlN, the following large Kerr rotation angle (at room temperatures, 3 mm thickness) can be obtained in the visible region.
For example, Eu substituted for Ga site of GaN or Al site of AIN becomes Eu3+, and a ferromagnetic transition temperature can be largely controlled through such electron-doping. The value of Kerr rotation angle can also be controlled in the range of zero to about 150 degrees by adjusting the concentration of Eu impurity and the amount of electron-doping.
Extremely high magnetooptic effects to be obtainable through the Kerr effect have potential for providing a higher performance in memories or computers using magnetooptic light or optical isolators. In cases where a transition metal is contained in the aforementioned semiconductor, the transition between 3d electrons provides light emission having a wide continuous energy spectrum and a wavelength to be largely varied according to temperature change. By contrast, in case of the rare-earth metals, the transition occurs between 4f electrons, and thereby the resulting emission advantageously has a sharp spectrum and a wavelength to be never varied relative to temperature, which is significantly valuable to future data communication utilizing spin electronics.
With reference to the drawings, a ferromagnetic group IV-based semiconductor or a ferromagnetic group III-V-based or group II-VI-based compound semiconductor of the present invention, and a method for adjusting a ferromagnetic characteristic thereof, will now be described. A ferromagnetic group IV-based semiconductor or a ferromagnetic group III-V-based or group II-VI-based compound semiconductor of the present invention comprises a group IV-based semiconductor or a group III-V-based or group II-VI-based compound semiconductor, which contains at least one rare-earth metal element selected from the group consisting of Ce, Pr, Nd, Pm, Sm, Eu, Gd, Th, Dy, Ho, Er, Tm, Yb and Lu.
The following description will be made, mainly, in connection with a case where Si is used as IV-based semiconductor. In a process for obtaining a ferromagnetic material using Si as IV-based semiconductor, a 4f electron of the rare-earth metal element, such as Gd, Th or Dy, is strongly p-f-hybridized with the 3p electron of Si serving as a matrix semiconductor. Thus, as seen in
A cell 2a receiving therein Si as a material (source) constituting a compound to be grown, a cell 2b receiving therein at least one rare-earth metal element selected from the group consisting of Ce, Pr, Nd, Pm, Sm, Eu, Gd, Th, Dy, Ho, Er, Tm, Yb and Lu (while
Each of the cells 2a to 2d receiving therein the respective solids (elemental substances) is provided with means (not shown) for heating the solid source to vaporize it in an atomic state. The radical cell 3a is designed to activate the atomized sources using an RF (high-frequency) coil 8. Each of the Si, rare-earth metal element and n-type dopant is use after vaporizing a corresponding solid source having a purity of 99.99999%, in an atomic state. The atomic state of the Si or the rare-earth metal element may be obtained by irradiating a corresponding molecular gas with an electromagnetic wave in the microwave region.
Then, a Si thin film 6 is grown at a temperature of 350 to 800° C. while supplying the n-type dopant of P, Sb or As at a flow volume of 1.33×10−5 Pa, the p-type dopant of B, Al or Ga in an atomic state at a flow volume of 6.65×10−5 Pa, and the rare-earth metal element, such as Gd, Th or Dy, in an atomic state at a flow volume of 1.33×10−5 Pa, all together onto the substrate 5, to provide a Si thin film 6 formed as a mixed crystal containing the rare-earth metal element.
In the above example, the n-type and p-type dopants are doped. By contrast, in the aforementioned example of
As seen in
While the rare-earth metal element is doped in Si in the above example, it may also be doped in a group III-V-based nitride, such as GaN, to obtain a ferromagnetic single crystal, because GaN is different from Si only in that its bandgap energy is greater than that of Si, and any group III-V-based nitride other than GaN has a four-coordinate structure similar to and difference only in bandgap energy from that of GaN.
However, in a case where 5 at % of Gd is doped in the semiconductor, a desired ferromagnetic material can be obtained only if 1 at % or more, preferably 3 at % or more of oxygen is doped as a donor to dope an n-type carrier in the semiconductor. Further, in a case where 10 at % of Gd is doped in the semiconductor, a desired ferromagnetic material can be obtained only if 2 at % or more, preferably 5 at % or more of oxygen is doped as a donor to dope an n-type carrier in the semiconductor.
In the ferromagnetic Si of the present invention which is formed as a mixed crystal containing the rare-earth metal element, while an Si atom is substituted with the rare-earth metal element, such as Gd3+, Tb3+ or Dy3+, the ferromagnetic Si matrix can be maintained in a diamond structure. In addition, the aforementioned rare-earth metal element, such as Gd, Th or Dy, has an electronic structure capable of increasing holes, and thereby stabilizes in a stable ferromagnetic state without any modification, as shown in
The variation in magnetic characteristic to be caused by changing the concentration of the rare-earth metal element was checked as follows. In addition to the aforementioned Si-based compound containing the rare-earth metal element at a concentration of 25 at %, Si-based compounds containing the rare-earth metal element at 5, 10, 15 and 20 at % were prepared, and their magnetic moment (×9.247 J/T) and ferromagnetic transition temperature (° K.) were measured. The magnetic moment and ferromagnetic transition temperature were determined by measuring a magnetic susceptibility using a SQUID (superconducting quantum interference device).
The measurement results are shown in Tables 1 and 2. As seen in Tables 1 and 2, the ferromagnetic transition temperature is apt to be increased as the mixed crystal ratio (the concentration) is increased, and is increased approximately in proportion to the mixed crystal ratio. This relationship is shown in
As described above, the rare-earth metal element is put into a high spin state which has an electronic spin s=7/2 and an orbital angular momentum L=0 for Gd, an electronic spin s=3 and an orbital angular momentum L=3 for Th, or an electronic spin s=5/2 and an orbital angular momentum L=5 for Dy. Further, as seen in Tables 1 and 2, and
The inventors also found that two or more of the rare-earth metal elements can be added to the semiconductor to form a mixed crystal of them, so as to adjust the state of holes or electrons, and obtain the respective magnetic characteristics of the two or more rare-earth metal elements together. For example, a combination of Lu and either one of Gd, Th or Dy was added to Si to form a mixed crystal of them. In a case where the conditions that the total concentration of Dy and Lu was set at 25 at %, and x was variously changed to form Dy0.25-x Lux Si0.75, the ferromagnetic transition temperature could be largely varied, and set at zero ° K. when x=0.04, as shown in
The ferromagnetic transition temperature can be set at desired value by selectively arranging x in the range of 0 to 0.10. In the same manner, a combination of Lu and Th may be added to Si to form Tb0.25-x Lux Si0.75 while variously changing x. Further, various magnetic moments can also be obtained, but not shown, by changing the mixing ratio of the above two rare-earth metal elements.
In the above examples, two or more of the rare-earth metal elements are doped to adjust the ferromagnetic characteristic. Alternatively, at least one rare-earth metal element selected from the aforementioned group, and at least one metal element selected from the group consisting of Th, Pa, U, Np, Pu, Am, Cm, Bk, Cf, Es, Fm, Md, No and Lr, which belong to actinide elements except for Ac having no 5f electron, may be doped. In this case, the magnetic moment and/or the ferromagnetic transition temperature can also be adjusted by changing the respective concentrations of the rare-earth metal element and the actinide element.
Further, an n-type dopant or a p-type dopant may be doped to change the amount of holes or electrons so as to adjust the ferromagnetic characteristic.
In this case, the n-type or p-type dopant is incorporated into the conduction band or valence band of Si to act on the 4f electron of the rare-earth metal element adjacent to the conduction or valence band. Thus, while all of added dopants do not always act on the 4f electron, at least a part of the dopants surely act on the 4f electron to change the ferromagnetic state including the ferromagnetic transition temperature.
For example, the doping of an n-type dopant is equivalent to supplying an electron. Thus, the doping of an n-type dopant in combination with the mixed crystallization of either one of Gd, Th, Dy and Lu has the same effect as that in the aforementioned example of adding Lu and either one of Gd, Th and Dy.
As seen in
Differently from the aforementioned adjustment through the mixed crystallization of two or more of the rare-earth metal elements, in the adjustment using the n-type or p-type dopant, the magnetic moment itself is maintained at a value determined by the rare-earth metal element added to Si to form a mixed crystal of them.
Either one of P, As and Sb may be used as the n-type dopant, and a compound of Si and either one of these elements may be used as a material to be doped. Preferably, the concentration of the donor is 1×1018 cm−3. For example, the donor doped at a concentration of about 1020 to 1021 cm−3 is equivalent to the aforementioned rare-earth metal element added at a mixed crystal ratio of 1 to 10 at %. As described above, either one of B, Al and Ga may be used as the p-type dopant.
The lowest transmission wavelength of light to pass through the ferromagnetic material is varied depending on the kind or type of the rare-earth material to be added to the group IV-based semiconductor or a group III-V-based or group II-VI-based compound semiconductor which is a wide bandgap semiconductor, and can be adjusted by adding two or more of the rare-earth materials to the semiconductor to form a mixed crystal of them so as to provide a light filter for cutting off light having a wavelength less than a desired wavelength. For example, a ferromagnetic group III-V-based nitride (GaN) transparent to light having a desired wavelength can be obtained. The lowest wavelength of light to pass through each of ferromagnetic nitrides prepared by adding 5 at % of each of the aforementioned rare-earth metal elements to GaN to form a mixed crystal of them were measured as shown in Table 3, wherein 5 at % of oxygen is doped in the case of Gd. According to this example, a ferromagnetic magnet transparent to light having a desired wavelength can be obtained.
As mentioned above, according to the present invention, an energy in the ferromagnetic state can be changed as a whole by a kinetic energy of a hole or electron introduced from the added rare-earth metal element by themselves and others, and the level of the energy can be reduced by adjusting the concentration of the hole or electron, so as to stabilize the ferromagnetic state. Thus, the hole or electron can be introduced to controllably change the magnitude and the positive/negative sign of the magnetic interaction between the rare-earth metal atoms so as to stabilize the ferromagnetic state.
While the MBE (Molecular Beam Epitaxy) apparatus is used in the above embodiment to form a thin film containing the rare-earth metal element, an MOCVD (Metalorganic Chemical Vapor Deposition) apparatus may be used to form the same thin film. In this case, the metal material, such as Ga, Al or the rare-earth metal, is introduced in the MOCVD apparatus in the form of an organic metal compound, such as dimethyl gallium or dimethyl aluminum.
The MBE or MOCVD process can be used to form a thin film in a nonequilibrium state while doping a transition metal element or the like therein at a desired concentration. However, the thin film growth method is not limited to these processes, but the thin film may be formed through any other suitable process, such as a laser abrasion process using solid targets of solid Ga nitride, solid Al nitride and rare-earth metal to form a thin film while applying an activated dopant onto a substrate.
Further, when the rare-earth metal element or its oxide is used as the doping material, an ECR (Electron Cyclotron Resonance) plasma device adapted to electronically excite the doping material using radio wave, laser, X-ray or electron beam, to put it into an atomic state may be used. The ECR plasma device may also be used for the n-type and p-type dopants. The ECR plasma device can be advantageously used to allow such a material to be doped in an atomic state at a high concentration.
According to the present invention, at least one rare-earth metal element selected from the group consisting of Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu can be simply contained in a group IV-based semiconductor or a group III-V-based or group II-VI-based compound semiconductor to obtain a ferromagnetic single crystal having high magnetooptic effects and a high ferromagnetic transition temperature of greater than room temperatures. Thus, the obtained ferromagnetic single crystal can be combined with existing ZnO or transparent conductive oxide (TCO) for use as an n-type or p-type transparent electrode, or an optical fiber, and applied to an quantum computer or large-capacity magnetooptical recording, or to high-performance data communication or quantum computer as an optical electronic material usable in the range of the visible to ultraviolet regions.
In addition, based on the intra 4f-electron shell transition in the rare-earth metal element, the ferromagnetic semiconductor of the present invention can emit light having a constant wavelength without any variation due to temperature change up to room temperatures. Thus, the ferromagnetic semiconductor of the present invention can be adjusted to be a p-type or n-type semiconductor which is applicable to a transparent ferromagnetic semiconductor or a circularly polarized light-emitting device (spin-based semiconductor laser) which has extremely high magnetooptic effects.
| Number | Date | Country | Kind |
|---|---|---|---|
| 202-166803 | Jun 2002 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP03/07161 | 6/5/2003 | WO | 10/21/2005 |