Patent Application
20130244004
This application claims priority under 35 USC 119 to German Patent Appl. No. 10 2012 102 290.9 filed on Mar. 19, 2012, the entire disclosure of which is incorporated herein by reference.
1. Field of the Invention
The invention relates to a mounting part for affixing a fiber composite part of a motor vehicle to at least one adjoining component of the motor vehicle. Furthermore, the invention relates to a fiber composite part, to a method for manufacturing the mounting part and to a method for manufacturing the fiber composite part.
2. Description of the Related Art
Fiber composite parts made from carbon fiber reinforced or glass fiber reinforced polymers are increasingly used in motor vehicles to achieve weight reductions. However, it is necessary to connect the fiber composite parts to at least one adjoining component of the motor vehicle. Mounting parts, or inserts, incorporated in the respective fiber composite part to connect the fiber composite parts to the adjoining component. According to the prior art, these mounting parts incorporated in a fiber composite part are metallic, and usually aluminum.
The metallic mounting part used for affixing the fiber composite part to an adjoining component of the motor vehicle must be coated with an adhesion promoter and an anti-corrosion agent prior to being introduced into the fiber composite part. As a result, manufacturing expenses are increased.
Fiber composite parts used with metallic mounting parts are disclosed in WO 2011/051227 A1.
An object of the present invention is to provide an innovative mounting part for affixing a fiber composite part of a motor vehicle to at least one adjoining component of the motor vehicle, an innovative fiber composite part and a method for manufacturing the mounting part and the fiber composite part.
The invention relates to mounting parts that are incorporated or embedded in a fiber composite part for affixing the fiber composite part to an adjoining component. The mounting parts of the invention are made from a fiber composite material. As a result, and unlike the prior art, there is no need to coat the mounting parts with an adhesion promoter and an anti-corrosion agent prior to being incorporated, thereby reducing manufacturing expenses. Moreover, the fiber composite mounting parts ensure an integral bond between the mounting parts and the fiber composite part.
The mounting part is made from a carbon fiber reinforced or a glass fiber reinforced polymer with relatively short fibers between 3 mm and 100 mm in length, and preferably between 20 mm and 80 mm in length. This defined length of the relatively short fibers for the mounting part allows on the one hand the guarantee of a sufficient strength of the mounting part, and on the other hand the provision of a three-dimensional shape analogous to that of metallic mounting parts.
The mounting part preferably comprises between 30% by volume and 70% by volume, in particular between 40% by volume and 65% by volume, fibers and furthermore between 70% by volume and 30% by volume, in particular between 60% by volume and 35% by volume, a thermosetting polymer. This composition of the mounting part of fibers and thermosetting polymer is advantageous for guaranteeing a high strength of the mounting parts.
The mounting part preferably is manufactured by preparing a liquid or flowable mixture of polymer and fibers. The mixture then is filled into a three-dimensionally shaped mold for the mounting part. The mold then is closed and the mounting part is cured for a defined period of time at a defined temperature and a defined pressure. The aforementioned method enables the manufacturing of three-dimensionally shaped mounting parts with sufficient strength from a fiber composite material with simple means. In this context the term “flowable” does not mean that the mixture has to be “flowable” already at room temperature. Rather, the mixture may take the form of a sheet at room temperature and an appropriately weighed amount may be filled into the mold. The mixture conforms to the three-dimensionally shaped mounting part once the mold has been closed on the basis of temperature and pressure.
The mounting part preferably is cured in the mold for a period of between 0.5 min and 10 min at a temperature between 100° C. and 200° C. and at a pressure of more than 100 bar. The abovementioned process parameters are advantageous, with the tool preferably being heated isothermally during the curing of the mounting part.
Exemplary embodiments of the invention are explained with reference to the drawing, without being limited to this.
The invention relates to a mounting part for affixing a fiber composite part of a motor vehicle to at least one adjoining component of the motor vehicle. The mounting part is incorporated or embedded in the respective fiber composite part and is referred to as an insert. The invention also relates to a fiber composite part of a motor vehicle with at least one such mounting part and to a method for manufacturing the mounting part and the fiber composite part.
A recess 12 with an internal thread 13 is cut into the mounting part 11 to allow a direct screw connection of the fiber composite part 10 via the mounting part 11 to an adjoining component. Alternatively, an internally threaded bush can be inserted into the recess 12 so that the fiber composite part 11 can be screwed indirectly via the threaded bush to an adjoining component.
The mounting part 11 incorporated in the fiber composite part 10 is a three-dimensionally shaped structure with ribs, and/or webs and/or protrusions and/or depressions.
The mounting parts 11, 11′ or 11″ for a fiber composite part are made from a fiber composite material, namely from a carbon fiber reinforced or a glass fiber reinforced polymer with relatively short fibers. The carbon fiber reinforced or glass fiber reinforced polymer is preferably a thermosetting polymer, in particular an epoxy resin or a vinyl-ester resin or polyurethane.
The relatively short fibers of the mounting part 11, 11′ or 11″ have a length of between 3 mm and 100 mm. Preferably, the length of the relatively short fibers of the mounting part 11, 11′ or 11″ is between 20 mm and 80 mm.
The mounting part 11, 11′ or 11″ may have fibers of exclusively one length, such as short fibers exclusively of a length of 25 mm or 70 mm or 75 mm. Alternatively, the respective mounting part 11, 11′ or 11″ may have relatively short fibers of at least two different lengths, for example first fibers of a length of 25 mm and second fibers of a length of 50 mm. Likewise it is possible that the mounting part 11, 11′ or 11″ has first fibers of a length of 10 mm and second fibers of a length of 75 mm.
The use of fibers of different lengths for the mounting part advantageously enables both a sufficient strength of the respective mounting part 11, 11′ and 11″ and any desired three-dimensional shaping of the part.
The respective mounting part 11, 11′ or 11″ preferably has between 30% by volume and 70% by volume fibers and between 70% by volume and 30% by volume thermosetting polymer.
The mounting part 11, 11′ or 11″ preferably comprises between 40% by volume and 65% by volume fibers and between 60% by volume and 35% by volume thermosetting polymer, in particular epoxy resin.
The mounting parts 11, 11′ or 11″ for a fiber composite part 10 of a motor vehicle themselves uniquely are made from a fiber composite material. In this context relatively short fibers in a defined mixing ratio with a polymer are used in the respective mounting part 11, 11′ or 11″. Thus, three-dimensionally shaped mounting parts made from a fiber composite material are provided with a three-dimensional shape typically associated with metallic mounting parts and with a sufficiently high strength.
The fiber composite parts 10 and the mounting parts 11, 11′ or 11″ incorporated therein preferably are made from a fiber composite material, with identical fiber material of different lengths and with an identical polymer material, such as thermosetting polymer, being used in the fiber composite part 10 and in the mounting part 11, 11′ or 11″. The fibers of the fiber composite part 10 are relatively long continuous fibers, namely relatively long carbon fibers or glass fibers.
The manufacturing of the mounting part 11, 11′ or 11″ proceeds bu preparing a liquid, in particular a viscous or flowable mixture of polymer and fibers. This mixture preferably comprises between 30% by volume and 70% by volume fibers and the rest polymer, in particular thermosetting polymer. The preferred mixture comprises between 40% by volume and 65% volume fibers and the rest polymer, such as epoxy resin.
This mixture is weighed and the weighed mixture is filled into a three-dimensionally shaped mold for the mounting part. The mold for the mounting part 11, 11′ or 11″ then is closed and the mounting part is cured in a molding process with a heated mold. The curing in the mold takes place at a defined temperature and at a defined pressure over a defined period of time. In particular, the curing of the mounting part 11, 11′ or 11″ takes place in an isothermically heated mold at a temperature between 100° C. and 200° C. and at a pressure of more than 100 bar over a period of between 0.5 minutes, that is to say 30 seconds, and 10 minutes.
The manufactured mounting parts 11, 11′ or 11″ are placed in an uncured fiber composite matrix to form a semi-finished product. This semi-finished product may be a so-called prepreg of fibers and thermosetting polymer or a dry semi-finished product consisting of only fibers, into which, subsequent to the positioning of the mounting parts, thermosetting polymer, in particular epoxy resin, is injected. The fiber composite matrix with the incorporated or embedded and already cured mounting parts 11, 11′ or 11″ then is cured, and the mounting parts 11, 11′ or 11″ forming an intimate bond with the identical polymer material of the fiber composite matrix to form a composite part 10.