Abstract
The present invention relates to a thickened aqueous solution, or gel solution, for use in providing fiber to a cement composition. Additionally, the present invention relates to a method for mixing fibers with cement.
Description
FIELD OF INVENTION
[0001] The present invention relates to a gel or thickened aqueous composition containing fibers, with the composition intended for use in cement and similar compositions. The gel mixture serves as a conduit for facilitating the introduction and mixing of the fibers with the cement.
BACKGROUND OF INVENTION
[0002] It is known that adding fibers to cement, mortar, concrete, or similar compositions (referred to throughout as cement) will increase the flexular and tensile strength of the cured product. Additionally, the fibers prevent, minimize, or inhibit, cracking in the cured cement. Cement is defined as any mixture of fine-ground lime, alumina, and silica that will set to a hard product by admixture of water which combines chemically with other ingredients to form a hydrate. Mortar is defined as a type of adhesive or bonding agent that may be either inorganic or organic, soft and workable when fresh but sets to a hard, infusible solid on curing, either by hydraulic action or by chemical crosslinking. The chief ingredients of inorganic mortars are cement, lime, silica, sulfur, and sodium or potassium silicate. Concrete is defined as a conglomerate of gravel, pebbles, sand, broken stone, and blast-furnace slag or cinders, termed the aggregate, imbedded in a matrix of either mortar or cement, usually standard Portland cement in the United States.
[0003] The addition of fibers to a cement mixture, prior to pouring, will minimize or inhibit cracking in the cured cement product. Minimization and inhibition of cracks is one of the primary reasons for adding fibers to cement. As such, it is well known and desired to add various synthetic fibers or other fibrous materials to cement compositions, as the fibers result in a more desired cured cement product.
[0004] Fibers are typically added to cement mixers prior to pouring at a construction site. The fibers are available in bags that are added directly to the mixer, whereby the bags will dissolve in the cement mixture found in the mixer. As such, the bags are added by hand, by workers. Unfortunately, there is no verification concerning whether the proper number of bags were added to the cement mixture. For example, if a bag is dropped on the ground prior to mixing, it is likely that it or a replacement will not be added to the mix. Whether the fibers have been added in the correct amount cannot generally be verified. For this reason, it is desired to have a way to better control and monitor the addition of the fibers.
[0005] The method for adding the fibers is not automated, which contributes to the inaccurate addition of the fiber material to the cement material. For this reason, it is desired to have a method that allows for more accurate metering and addition of the fibers to the cement.
[0006] Typically, a cement truck must be directed to a staging area other than where the cement is added for the bags of fibers to be added thereto. The fibers are added at a location away from where the cement is added. As such, the cement trucks line up and have cement added thereto, with the fibers then added at a different location for safety reasons. This can be time consuming and inefficient. It is desired to have a more efficient method for adding the fibers.
[0007] The fibers to be added to the cement typically have a low density and, as such, they tend to float. Conversely, some fibers are of a density such that they sink. Such characteristics make it difficult to readily mix the fibers into a water-based, aqueous solution. Consequently, the fibers are not pre-mixed with water prior to the addition of the fibers to the cement. For this reason, it is desired to have a carrier for use with the fibers, which allows for the suspension of the fibers and easy mixing in the cement. The carrier form should be other than a dry mix to ensure easier addition to the cement. It is especially desired to have fibers available in an aqueous form, whereby the fibers are suspended.
[0008] Thus, it is desired to have a fiber composition which can be more easily added to cement. It is further desired to have a composition that can be easily metered and controlled by an automated process to ensure accurate addition. It is further desired to eliminate manual addition by workers of the fibers to the cement.
SUMMARY OF INVENTION
[0009] The present invention relates to an aqueous gel solution, which is a fiber carrier, that can be mixed with cement. In particular, the present invention relates to an aqueous solution containing fibers for use in cement. The present invention further relates to an uncured cement composition containing an amount of cement, fibers, and an aqueous gel composition. The invention further relates to a method for adding fibers to cement.
[0010] The aqueous gel solution is of a density and viscosity such that the fibers are suspended, whereby the fibers will not readily sink or float. Also, the gel solution has sufficient flow characteristics to be easily metered into the cement. The gel viscosity will be increased or decreased, dependent upon the density of the particular fiber selected. The aqueous gel solution is formed from water and a thickener, with the amount of thickener varied according to the desired viscosity. Also, different types of thickeners or thickening agents impart different viscosities. As such, the thickener is selected from any of a variety of constituents and mixed with water. Importantly, a gel mixture is formed that will hold fibers for a sufficient period of time in a suspended state so that the fibers won't readily sink or float.
[0011] The fibers are added in an amount equal to between 0.1 and 15 lbs. of dry fiber to one gallon of gel. Most synthetic fibers, such as polypropylene, will be added in an amount equal to between 0.5 to 2 lbs. of dry fiber, to one gallon of gel. Heavier fiber materials, such as steel fiber, will be added in an amount equal to between 8 and 12 lbs. of fiber per one gallon of gel. The amount of fiber added to the gel will depend on the desired finished characteristics of the cement, the type of fiber added, and the constituent used to form the gel. The fibers can be selected from any of a variety of constituents, as long as the cured concrete properties are improved. In particular, the fiber material should inhibit cracking. The fibers range in length between 0.0625 inches and 2.5 inches. It is preferred to have a length ranging between 0.25 inches and 0.75 inches. Any length can be used as long as the cement properties are improved, and the fibers are adequately mixed into the cement. The available fibers include polypropylene, polyester, nylon, steel, and combinations thereof. The gel with the fibers is added to the cement in an amount equal to between 1 quart and 20 gallons per cubic yard of cement.
[0012] The method includes adding fibers to cement, with the method initiated by forming a gel composition from fibers and a thickened aqueous composition. Next, the method includes adding the gel composition to cement prior to pouring. As such, a method for adding fibers to cement is provided.
[0013] The present invention is advantageous because a method for the controlled and monitored addition of fibers to cement is provided. Additionally, the gel composition is preferred, because it enhances dispersion and addition of the fibers in the cement.
DETAILED DESCRIPTION
[0014] The present invention relates to a gel composition, or thickened aqueous composition, containing an amount of a fiber constituent, with the aqueous gel composition for use in cement. The gel composition is a carrier for the fiber constituent. The present invention also relates to a cement composition, which includes the gel composition containing the fibers. Additionally, the present invention relates to a method for adding fibers to cement prior to the pouring and curing of the cement. Thus, the present invention relates to a gel composition containing an amount of a fiber constituent suspended within the gel composition, whereby the gel facilitates the mixing of the fibers with the cement.
[0015] The gel composition, also known as the thickened aqueous composition, is formed by mixing an amount of the fiber constituent with an amount of a gel constituent. Any of a variety of fibers may be used in the present invention as the fiber constituent, as long as the fibers are readily suited for use with cement, concrete, mortar, or similar compositions. The fibers are added to inhibit or prevent cracking in the cured cement products, and to preferably increase tensile and flexular strength. As such, the fibers should be of a character, whereby once added to cement, cracking is inhibited or prevented. Preferably, the fiber constituent is selected from the group, which includes polypropylene, polyester, nylon, steel, cotton, wool, iron shavings, rubber, aluminum, and combinations thereof. Any synthetic or natural fiber, which does not readily degrade in the cement and which imparts the desired improvements to the cement, can be used. The fibers will range in length between 0.0625 inches and 2.5 inches; however, other lengths can be used, as long as the fibers readily mix with the cement. More preferably, the fibers will have a length ranging between 0.25 and 0.75 inches. Additionally, the fibers will need to impart the desired characteristics. The fibers generally have a density equal to between 0.5 and 9.0. Any density may be used as long as the fiber material can be suspended. Synthetic fibers generally have a specific gravity ranging between 0.5 and 1.5. Steel fibers generally have a specific gravity ranging between 7.4 and 9.0. Ultimately, the fibers will be added to the cement in an amount equal to between 0.1 lbs. of dry fiber to 15 lbs. of dry fiber per gallon of gel. The gel is then added in an amount ranging between 1 quart and 20 gallons per cubic yard of cement.
[0016] The fiber constituent can be suspended in any of a variety of aqueous gel constituent compositions, or similar type aqueous carriers. The gel compositions should have a viscosity such that the selected fibers do not readily float to the top, or settle to the bottom of the solution. Water has a density of about 1 centipoise at 20° C. This is the standard from which the gel will be measured. As such, the gel should have a viscosity greater than 1.0 centipoise. The selected viscosity is dependent upon the selected fiber. The fibers should remain suspended in the solution. Typically, the aqueous solution will have a viscosity sufficient that the fibers will be suspended. Also, the solution should be of a sufficient flowability to ensure addition to cement. It is preferred for the aqueous solution to be water-based, as water mixes well with cement. Most importantly, the solution must be such that it can be readily mixed with cement without any adverse effects. Preferably, the aqueous solution is formed from water and a thickening agent to form a colloid suspension. A gel is defined as a colloid. In a colloid, the disperse phase has combined with the continuous phase to produce a viscous jelly-like product. A colloid solution is a system intermediate between a true solution and a suspension. Compositions suitable for use as thickeners for use in forming the gel include xanthan gum, locust bean gum, guarana gum, tragacahth gum, Arabic gum, cassia tora gum, sodium alginate potassium alginate, ammonium alginate, calcium alginate, alginate ester, carrageen, alpha cellulose, powdered cellulose, microcristilline cellulose, cologel, ethal cellulose, hydroxpropyl cellulose, carboxymetil cellulose, agar-agar, bentonite, cellulosit, attapulgate clay, actigel 150, bentone, gelatin, acacia, acaten, gum Arabic, cellulose dextran, furcellaran, ghatti, guar gum, karaya, konjac, locust bean, pectin, psyllium, tamarine, and tragacanth. It should be noted that the aqueous solution should be one that is readily used under ambient conditions, and can be easily mixed so that heating is generally not required to blend the fibers with the gel.
[0017] The fiber and gel will be mixed in a ratio of 0.1 to 15 lbs. of dry fiber to about one gallon of gel. The ratio will be dependent on the density of the fiber and the viscosity of the gel. A more preferred range is as follows: 1 lb. of dry fiber to 1 gallon of gel.
[0018] Once the gel composition has been formed, it can be added to the cement composition. The gel composition can be added to any of a variety of compositions, including cement, concrete, mortar, and similar compositions. It is preferred to add the gel composition at the station where cement is placed into concrete trucks. Thus, the gel composition is added simultaneously with, or shortly thereafter, the addition of the cement to the cement mixer truck. Advantageously, the gel composition can be added via a metering system at the cement plant, whereby fibers are added without human input or responsibility. As such, the system for adding the fibers can be automated which will, in turn, reduce the possibility of human error.
[0019] The final fiber solution will be pumped with a progressive cavity pump from a storage container into a weigh chamber, and then gravity fed into the ready mix truck or water scale. Other pumps could include a single or double diaphragm pump, progressing cavity pump, peristaltic pump or lobe pump. The weigh chamber could be omitted, and the fiber solution could be verified with a flow meter, or other measuring device. The final fiber solution could be verified volumetrically. Any device can be used, as long as the device allows for accurate metering of the gel into the cement, for tracking the amount of gel metered, and is of a design such that the fibers do not get stuck in the device.
Example 1
[0020] A cement mixture was prepared for use in comparing a cured cement product with a cement product having fibers added thereto.
[0021] The below list describes the starting materials, equipment, and characteristics:
1|
|
Mix ID No. 1
|
|
Description:5 Sack MixW/C ratio: 0.64
Strength (fc):N/A psiSack Content: 5.00 sk.
Slump:4 inchGal/sk.: 7.20
Max. Size of Agg.:1 inchUn. Wt.:146.3
|
[0022] As can be seen, the process started with 5.00 sacks or 470 pounds of cementicious material mixed with 7.2 gallons of water per sack or 36 gallons of water. All procedures outlined in ASTM C31 were used to place the cement in molds. This was a standard mix, regardless of whether fibers were added.
[0023] A cement composition was formed. The following list describes the constituents added to the mixture used to form the cement:
2|
|
Batch%Sp.
ContentsWt.UsedGr.Volume
|
|
Cement400853.152.04
Fly Ash-Class F70152.330.48
Sand1581502.629.67
1″ × #41247392.657.54
⅜″ × #8352112.652.13
Water36.0 gal.299.94.81
Entrapped Air1.25%0.34
Wt. =3950Vol. =27.00
ADMIXTURES:
None
|
[0024] As can be seen, a mixture of ash, sand, and cement, without additives, was formed. The cement was cured and then tested.
[0025] Listed below are the results of tests conducted on the cured cement product:
3|
|
Field Test ResultsCompressive Strength Results
|
|
Slump:5″ASTM C143
Concrete Temp:79° F.ASTM C231
Air Temp:90° F.ASTM C13828 day1078203814
Time:15:05ASTM C106428 day1067403776
Time Set:20:3028 day avg.1072803795
|
[0026] The results show a cement composition having characteristics similar to other known cement compositions. Example 2
[0027] A cement mixture was prepared for use in comparing a cured cement product with a cement product having fibers added thereto.
[0028] The below list describes the starting materials, equipment, and characteristics:
4|
|
Mix ID No. 2
|
|
Description:5 Sack MixW/C ratio: 0.64
Strength (fc):N/A psiSack Content: 5.00 sk.
Slump:4 inchGal/sk.: 7.20
Max. Size of Agg.:1 inchUn. Wt.:146.3
|
[0029] As can be seen, the process started with 5.00 sacks or 470 pounds of cementicious material mixed with 7.2 gallons of water per sack or 36 gallons of water. All procedures outlined in ASTM C31 were used to place the cement in molds. This was a standard mix, regardless of whether fibers were added.
[0030] A cement composition was formed. The following list describes the constituents added to the mixture used to form the cement:
5|
|
Batch%Sp.
ContentsWt.UsedGr.Volume
|
|
Cement400853.152.04
Fly Ash-Class F70152.330.48
Sand1581502.629.67
1″ × #41247392.657.54
⅜″ × #8352112.652.13
Water36.0 gal.299.94.81
Entrapped Air1.25%0.34
Wt. =3950Vol. =27.00
ADMIXTURES:
FiberFlo ™3.01.0
Gal.lb.
Fiber
|
[0031] As can be seen, a mixture of ash, sand, and cement, without additives, was formed. The cement was cured and then tested.
[0032] Listed below are the results of tests conducted on the cured cement product:
6|
|
Field Test ResultsCompressive Strength Results
|
|
Slump:5″ASTM C143
Concrete Temp:79° F.ASTM C231
Air Temp:90° F.ASTM C13828 day1200204245
Time:15:05ASTM C106428 day1299104595
Time Set:20:3028 day avg.1249654420
|
[0033] As can be seen, when compared to the cement of Example 1, the present cement had better compressive strength. Importantly, the cement was observed not to crack.
Example 3
[0034] A cement mixture was prepared for use in comparing a cured cement product with a cement product having fibers added thereto.
[0035] The below list describes the starting materials, equipment, and characteristics:
7|
|
Mix I.D. No. 3
|
|
Project:
Contractor:
Description:2000 psi Pump Mix
Strength (fc):2000 psiW/C ratio:0.68
Slump:4 inchSack Content:5.50 sk.
Max. Size of Agg.:⅜ inchGal/sk.:7.64
Un. Wt.:143.2
|
[0036] As can be seen, the process started with 5.50 sacks or 517 pounds of cementicious material mixed with 7.64 gallons of water per sack or 42.02 gallons of water. All procedures outlined in ASTM C31 were used to place the cement in molds. This was a standard mix, regardless of whether fibers were added.
[0037] A cement composition was formed and poured into a mold. The following list describes the constituents added to the mixture used to form the cement:
8|
|
Batch%Sp.
ContentsWt.UsedGr.Volume
|
|
Cement439853.152.23
Fly Ash-Class F78152.330.54
Sand2093702.6212.80
⅜″ × #8907302.655.49
Water42.0 gal.349.95.61
Entrapped Air1.25%0.34
Wt. =3867Vol. =27.00
ADMIXTURES:
Water Reducer3.015.5
cwt.oz.
|
[0038] As can be seen, a mixture of ash, sand, and cement, without additives, was formed. The cement was cured and then tested.
[0039] Listed below are the results of tests conducted on the cured cement product:
9|
|
Field Test ResultsCompressive Strength Results
|
|
Slump:5″ASTM C143
Concrete Temp:79° F.ASTM C231
Air Temp:90° F.ASTM C13828 day953403372
Time:15:05ASTM C106428 day942703335
Time Set:20:3028 day avg.948053354
|
[0040] As can be seen, when compared to the cement of Example 1, the present cement was similar.
Example 4
[0041] A cement mixture was prepared for use in comparing a cured cement product with a cement product having fibers added thereto.
[0042] The below list describes the starting materials, equipment, and characteristics:
10|
|
Mix I.D. No. 4
|
|
Description:2000 psi Pump MixW/C ratio:0.68
Strength (fc):2000 psiSack Content:5.50 sk.
Slump:4 inchGal/sk.:7.64
Max. Size of Agg.:⅜ inchUn. Wt.:143.2
|
[0043] As can be seen, the process started with 5.50 sacks or 517 pounds of cementicious material mixed with 7.64 gallons of water per sack or 42.02 gallons of water. All procedures outlined in ASTM C31 were used to place the cement in molds. This was a standard mix, regardless of whether fibers were added.
[0044] A cement composition was formed and poured into a mold. 51 pounds of mix were poured per mold. The following list describes the constituents added to the mixture used to form the cement:
11|
|
Batch%Sp.
ContentsWt.UsedGr.Volume
|
|
Cement439853.152.23
Fly Ash-Class F78152.330.54
Sand2093702.6212.80
⅜″ × #8907302.655.49
Water42.0 gal.349.95.61
Entrapped Air1.25%0.34
Wt. =3867Vol. =27.00
ADMIXTURES:
Water Reducer3.015.5
cwt.oz.
FiberFlo ™0.8331.00
gal.lb.
|
[0045] As can be seen, a mixture of ash, sand, and cement, without additives, was formed. The cement was cured and then tested.
[0046] Listed below are the results of tests conducted on the cured cement product:
12|
|
Field Test ResultsCompressive Strength Results
|
|
Slump:5″ASTM C143
Concrete Temp:79° F.ASTM C231
Air Temp:90° F.ASTM C13828 day955603380
Time:15:05ASTM C106428 day863603055
Time Set:20:3028 day avg.909603218
|
[0047] As can be seen, when compared to the cement of Example 3, the present cement had similar compressive strength. Importantly, the cement was observed not to crack.
Example 5
[0048] To make an exemplary gel, the following was done. Xanthan gum powder and water were mixed with a hand mixer. The xanthan powder was dispersed during this process. The powder was simply added to the water. The final solution had 0.042 pounds of dry xanthan gum added to 1 gallon of water. The solution was mixed for 15-20 minutes. The fiber was added in small amounts during mixing. The process was done under ambient conditions.
Example 6
[0049] Another gel solution was prepared as follows:
[0050] A 2% xanthan solution was made by mixing 100 lbs. xanthan powder with 150 lbs. “surcide p” (a fungicide) and 4,750 lbs. water. The mixture was mixed at 1200 rpm with a cowles style dispersing blade for 30 minutes until fully dispersed.
[0051] Thus, there has been shown and described a fiber gel mixture for use in concrete which fulfills all the objects and advantages sought therefor. It is apparent to those skilled in the art, however, that many changes, variations, modifications, and other uses and applications to the fiber gel mixture are possible, and also such changes, variations, modifications, and other uses and applications which do not depart from the spirit and scope of the invention are deemed to be covered by the invention, which is limited only by the claims which follow.
Claims
- 1. A cement composition comprising:
(a) an amount of cement; (b) an amount of fiber; and (c) an amount of an aqueous gel solution.
- 2. The composition of claim 1, wherein said fibers are added to said solution in an amount equal to between 0.1 and 15 lbs. of fiber to one gallon of gel.
- 3. The composition of claim 1, wherein said aqueous gel solution has a viscosity sufficient to suspend said fibers.
- 4. The composition of claim 1, wherein a gel that forms the aqueous gel solution is formed from water and a thickener, said thickener is selected from the group consisting of xanthan gum, locust bean gum, guarana gum, tragacahth gum, Arabic gum, cassia tora gum, sodium alginate potassium alginate, ammonium alginate, calcium alginate, alginate ester, carrageen, alpha cellulose, powdered cellulose, microcristilline cellulose, cologel, ethal cellulose, hydroxpropyl cellulose, carboxymetil cellulose, agar-agar, bentonite, cellulosit, attapulgate clay, actigel 150, bentone, gelatin, acacia, acaten, gum Arabic, cellulose dextran, furcellaran, ghatti, guar gum, karaya, konjac, locust bean, pectin, psyllium, tamarine, and tragacanth.
- 5. The composition of claim 1, wherein said gel and fibers are added in an amount equal to between 1 quart and 20 gallons per cubic yard of cement.
- 6. An uncured cement composition comprising:
(a) an amount of cement; (b) synthetic fibers; and, (c) an amount of an aqueous gel solution.
- 7. A thickened aqueous composition for use in concrete, comprising:
(a) an aqueous composition; and, (b) an amount of fibers.
- 8. The composition of claim 7, wherein said aqueous composition has a viscosity such that the fibers are suspended.
- 9. The composition of claim 7, wherein said fibers range in length between 0.0625 inches and 2.5 inches.
- 10. The composition of claim 7, wherein said fibers are selected from the group consisting of polypropylene, polyester, nylon, steel, cotton, wool, iron shavings, rubber, aluminum, and combinations thereof.
- 11. The composition of claim 7, wherein said aqueous composition comprises water and an amount of thickener.
- 12. The composition of claim 7, wherein the fiber is equal to between 0.1 lb. and 15 lbs. of fiber to 1 gallon of gel.
- 13. The composition of claim 11, wherein said thickener is selected from the group consisting of xanthan gum, locust bean gum, guarana gum, tragacahth gum, Arabic gum, cassia tora gum, sodium alginate potassium alginate, ammonium alginate, calcium alginate, alginate ester, carrageen, alpha cellulose, powdered cellulose, microcristilline cellulose, cologel, ethal cellulose, hydroxpropyl cellulose, carboxymetil cellulose, agar-agar, bentonite, cellulosit, attapulgate clay, actigel 150, bentone, gelatin, acacia, acaten, gum Arabic, cellulose dextran, furcellaran, ghatti, guar gum, karaya, konjac, locust bean, pectin, psyllium, tamarine, and tragacanth.
- 14. A method for adding fibers to cement comprising:
(a) forming a gel composition from fibers and thickened aqueous composition; and, (b) adding the gel composition to cement prior to pouring.
- 15. A method for automating dispersal of fibers in concrete, comprising:
(a) forming a gel containing fibers; and, (b) using a computer controlled metering device to put the gel into uncured cement.
- 16. The method of claim 15, wherein said device comprises:
(a) means for metering the gel into the cement; (b) means for tracking the amount of gel metered; and, (c) is of a design, whereby the fibers do not get stuck in the device.
- 17. The method of claim 15, wherein said device is selected from the group consisting of a progressive cavity pump from a storage container, a single or double diaphragm pump, progressing cavity pump, peristaltic pump, or lobe pump.