Patent Grant
8911825
1. Technical Field of the Invention
The present invention relates to a fiber-reinforced heat-resistant sound-absorbing material used for the exhaust nozzle and the like of a jet engine and a process for producing the material.
2. Description of the Related Art
Conventional sound-absorbing materials used for the exhaust nozzle and the like of a jet engine have a honeycomb structure. The sound-absorbing material having a honeycomb structure is comprised of a honeycomb made of a heat resistant alloy, a perforated plate, and a rear plate and it has a reactive structure like a Helmholtz resonator, and sound is diminished by the counteractive offset by the reflection, on the rear plate, of sound waves incident from the perforated plate.
In such a sound-absorbing material having a honeycomb structure, the perforated plate, inner honeycomb and rear plate of the material are overheated by a high temperature exhaust gas (for example, from 700 to 800 K or greater) and sometimes change their shape greatly. For example, since the perforated plate is made of a stainless or aluminum panel, the plate may be damaged or deformed by heat, and the brazed portion between the plate and honeycomb may peel.
Furthermore, a sound-absorbing material having the above-described structure can absorb only sound in a narrow frequency band so that noise in a wide frequency band (for example, from 1000 to 4000 Hz) produced by a jet engine cannot be absorbed satisfactorily.
A variety of sound-absorbing materials equipped with both heat resistance and capacity of absorbing sound in a wide frequency band have been proposed (for example, refer to Patent Documents 1 to 3).
According to “a lightweight ceramic sound-absorbing material and a process for producing the same” of Patent Document 1, a sound-absorbing material having both thermal shock resistance and sound-absorbing performance heightened by stacking a dense layer containing ceramic fibers over the surface of a porous foamed ceramic is disclosed.
According to “a lightweight CMC sound-absorbing material and a process for producing the same” of Patent Document 2, the absorbing material is a porous material made of an alumina-based ceramic containing SiC whiskers and having a porosity of from 80 to 92%. It has an improved sound absorption coefficient by controlling its flow resistance by adding silicon carbide fibers without changing the bulk density.
“A porous sound-absorbing material and a process for producing the same” of Patent Document 3 is characterized in that it has a skeleton made of an aggregate having pores and the porous sound-absorbing material has a porosity of from 75% to 85%.
The lightweight ceramic sound-absorbing material according to Patent Document 1 has many layers of several sound-absorbing materials stacked one after another so that its production cost is high. Moreover, since the sound-absorbing material is manufactured by foaming ceramics and its porosity is therefore not constant, it is difficult to expand the sound absorption effect even to a wide frequency band.
The lightweight CMC sound-absorbing material according to Patent Document 2 is also produced by foaming ceramics and its porosity is therefore not constant so that a satisfactory sound-absorbing effect in a wide frequency band cannot be attained.
The porous sound-absorbing material according to Patent Document 3 is composed of porous ceramics having a porosity of from 75% to 85% so that it is characterized in that it has adequate strength as a sound-absorbing material while maintaining a predetermined sound absorbing effect, and exhibits high sound absorbing effect against noise in a wide frequency band such as noise of a jet engine.
When it is exposed to a high-temperature high-speed exhaust gas, however, the porous ceramic is worn away and at last it loses its function.
As described above, conventional sound-absorbing materials having a honeycomb structure cannot achieve the sound absorbing performance in a wide frequency band which is a property necessary for the reduction of a jet noise and at the same time, when they are exposed to a high-temperature high-speed exhaust gas, they do not fulfill their function because the honeycomb material is damaged by it.
In addition, ordinarily used glass wool has low heat resistance (300° C. or less), while the sound-absorbing materials disclosed in Patent Documents 1 to 3 have problems that in spite of having high heat resistance, they cannot provide stable sound absorbing performance in a wide frequency band which is a property necessary for the reduction of jet noise, are worn away easily by a high-temperature high-speed exhaust gas, and are not light in weight.
The present invention has been made in order to overcome the above-described problems. An object of the present invention is to provide a fiber-reinforced heat-resistant sound-absorbing material which remains undamaged for a long period of time even exposed to a high-temperature high-speed exhaust gas of a jet engine or the like, has a sound absorbing performance in a wide frequency band which is a property necessary for the reduction of jet noise, and is light in weight; and a production process of the material.
The present invention makes it possible to provide a fiber-reinforced heat-resistant sound-absorbing material comprising a fiber preform made of silicon carbide short fibers having heat resistance of 1000° C. or greater and a heat resistant compound having heat resistance of 1000° C. or greater and applied onto the surface of the fibers; and having a porosity of 90% or greater.
The present invention also makes it possible to provide a process for producing a fiber-reinforced heat-resistant sound-absorbing material, which comprises a fiber preform formation step of forming a fiber preform made of silicon carbide short fibers having heat resistance of 1000° C. or greater; a sol-gel solution preparation step of preparing a sol-gel solution containing a heat resistant compound having heat resistance of 1000° C. or greater; an impregnation-drying-calcination step of impregnating the fiber preform with the sol-gel solution, followed by drying and calcining; and a crystallization step of crystallizing the fiber preform which has finished impregnation, drying and calcination.
According to the constitution and the process of the present invention, a fiber-reinforced heat-resistant sound-absorbing material is produced using silicon carbide fibers and heat resistant compound, each having heat resistance of 1000° C. or greater so that the fiber-reinforced heat-resistant sound-absorbing material has essentially improved heat resistance. In addition, since the fiber-reinforced heat-resistant sound-absorbing material is composed of a heat-resistant compound reinforced with a fiber preform, it has strength enough to be resistant for a long period of time against exposure to a high-temperature high-speed exhaust gas of a jet engine or the like. Moreover, the impregnation-drying-calcination step and the crystallization step contribute to an increase in the porosity (90% or greater) of the material, making it possible to actualize a sound absorbing performance in a wide frequency band which is a property necessary for the reduction of jet noise, and to decrease the weight of the sound-absorbing material.
According to the preferred embodiment of the present invention, a fiber-reinforced heat-resistant sound-absorbing material having a bulk density of 0.07 g/cm3 or greater but not greater than 0.11 g/cm3 is available by repeating impregnation, drying and calcination in the impregnation-drying-calcination step.
It has been confirmed by Examples that by the above-described constitution and process, a high absorption coefficient of noise in a wide frequency band (for example, from 1000 to 4000 Hz) which becomes necessary for the reduction of jet noise and weight reduction can be attained.
The silicon carbide fibers preferably contain a metal element which is selected from the class consisting of Group II, III and IV metal atoms of the periodic table and in which a temperature at which a free energy change in the carbon reduction reaction of an oxide of the metal element becomes a negative value is higher than a temperature at which a free energy change in the carbon reduction reaction of silicon oxide becomes a negative value, and have an oxygen content falling within a range of from 1 to 13 wt. %.
Such silicon carbide fibers are commercially available from Ube Industries under the trade mark of “Tyranno fiber” which has been confirmed to have heat resistance to a temperature as high as about 1500° C.
The above-described sol-gel solution is preferably a solution in which Ba, Al, Si and Mg ions or molecules or complex ions containing, in the structure thereof, such elements have been dissolved or dispersed at a weight ratio permitting precipitation of barium osumilite crystals at the time of the crystallization treatment. The heat-resistant compound is preferably a BaO.Al2O3.SiO2.MgO oxide represented by BaMg2Al6Si9O30.
Such a BaO.Al2O3.SiO2.MgO oxide is generally called as “BMAS”. The compound has been confirmed to be resistant to a temperature as high as about 1500° C. and in addition, can be prepared by the liquid phase process.
As described above, the fiber-reinforced heat-resistant sound-absorbing material and production process thereof according to the present invention have excellent effects, for example, the material is not damaged for a long period of time even by exposure to a high-temperature high-speed exhaust gas such as a gas from a jet engine, has a sound absorbing performance in a wide frequency band which becomes necessary for reducing jet noise, and is light in weight.
Preferred embodiments of the present invention will be described referring to the accompanied drawings. In all the drawings, elements having like function will be identified by like reference numerals and overlapping descriptions will be omitted.
In the preform formation step S1, a fiber preform S2 is formed using silicon carbide short fibers 13 having heat resistance of 1000° C. or greater.
In the sol-gel solution preparation step S2, a sol-gel solution 4 containing a heat-resistant compound having resistance of 1000° C. or greater is prepared.
In the impregnation-drying-calcination step S3, the fiber preform 2 is impregnated with the sol-gel solution 4. In this impregnation-drying-calcination step, the impregnation, drying and calcination are preferably repeated until the bulk density reaches 0.07 g/cm3 or greater but not greater than 0.11 g/cm3.
In the crystallization step S4, the fiber preform 5 after impregnation, drying and calcination is subjected to crystallization treatment to complete the preparation of a fiber-reinforced heat-resistant sound-absorbing material 6.
The silicon carbide fibers 1 preferably contain a metal element which is selected from the class consisting of Group II, III and IV metal atoms of the periodic table and in which a temperature at which a free energy change in the carbon reduction reaction of an oxide of the metal element becomes a negative value is higher than a temperature at which a free energy change in the carbon reduction reaction of silicon oxide becomes a negative value; and have an oxygen content falling within a range of from 1 to 13 wt. %.
In addition, the silicon carbide fibers 1 are preferably crystalline silicon carbide fibers having a density of from 2.7 to 3.2 g/cm3, containing, in terms of a weight ratio, from 50 to 70% of Si, from 28 to 45% of C, from 0.06 to 3.8% of Al and from 0.06 to 0.5% of B, and being composed of a sintered structure of SiC.
Such silicon carbide fibers are commercially available from Ube Industries under the trade mark of “Tyranno fiber” and especially, Tyranno Lox or Tyranno ZMI fiber or Tyranno SA fiber having higher heat resistance is suited. It has been confirmed that these fibers have resistance against temperatures as high as about 1500° C.
The sol-gel solution 4 is preferably a solution having dissolved therein Ba, Al, Si and Mg ions, or molecules or complex ions containing, in the structure thereof, these elements at a weight ratio permitting precipitation of barium osumilite crystals at the time of the crystallization treatment.
Such a BaO.Al2O3.SiO2.MgO oxide is generally called as “BMAS”. It has been confirmed that the compound is resistant to high temperature of about 1500° C. and can be prepared by the liquid phase process.
No particular limitation is imposed on the heat-resistant compound insofar as it can be prepared by the liquid phase process and is equipped with heat resistance necessary for a sound-absorbing material. Specific examples include oxides of an element such as aluminum, magnesium, silicon, yttrium, indium, uranium, calcium, scandium, tantalum, niobium, neodymium, lanthanum, ruthenium, rhodium, beryllium, titanium, tin, strontium, barium, zinc, zirconium or iron, and mixed oxides of these metals.
Specific examples of the mixed oxides include LiO2—Al2O3—MgO—SiO2 oxide and LiO2—Al2O3—MgO—SiO2—Nb2Os oxide, each having β-spodumene as a main crystal phase, MgO—Al2O3—SiO2 oxide having cordierite as a main crystal phase, BaO—MgO—Al2O3—SiO2 oxide having barium osumilite as a main crystal phase, BaO—Al2O3—SiO2 oxide having mullite or hexacelsian as a main crystal phase, and CaO—Al2O3—SiO2 oxide having anorthite as a main crystal phase. These mixed oxides may have, in the crystal phase thereof, cristobalite.
(Preparation of Felt)
In the preform formation step S1, a fiber preform 2 in the felt form was prepared using “Tyranno ZMI Fiber” (Si—Zr—C—O fiber). In this Example, the fiber preform 2 in the felt form having a predetermined porosity (bulk density) was obtained by stacking short fibers (chops) having a fiber diameter of 14 μm and fiber length of 50 mm one after another at random and then applying a pressure on the stack. The bulk density was determined from the volume and weight of the preform in the felt form, while the porosity was determined from the following equation:
Porosity[%]=bulk density/true density of the constituent material×100%.
In the present invention, no particular limitation is imposed on the forming method of the fiber preform and the melt blown process for preparing a felt using continuous fibers can also be employed.
(Preparation of Solution)
In the sol-gel solution preparation step S2, the sol-gel solution 4 far producing BMAS is prepared. BMAS is a BaO.Al2O3.SiO2.MgO oxide. It has a composition represented by BaMg2Al2Si9O30 and its mineral name is barium osumilite.
The below-described raw materials are used for the preparation of the sol-gel solution.
metal barium (Ba),
ethoxymagnesium (Mg(OC2H5)2),
aluminum isopropoxide (Al (O.C3H7)3),
tetraethoxysilane (Si(OC2Hs)4),
isopropyl alcohol (CH3CH(OH)CH3), and
acetylacetone (CH3COCH2COCH3).
In the sol-gel solution preparation step S2, a three-necked flask was purged with dry nitrogen, followed by the introduction of 1200 ml of isopropyl alcohol. To it was added 8.1 g of metal barium to synthesize an alkoxide of barium. To the resulting solution were added 13.4 g of ethoxymagnesium, 144.0 g of aluminum isopropoxide and 110.2 g of tetraethoxysilane (TEOS) and the resulting mixture was stirred at 80° C. for at least 4 hours to dissolve the latter in the former. To the resulting solution was added 27.5 g of acetyl acetone as a deflocculant. The resulting mixture was stirred at 80° C. for 3 hours to prepare a sol-gel solution. The resulting solution is used as a solution 4 for producing BMAS.
The resulting solution was dried and calcined at 1250° C. for 1 hour in the air, whereby white powder was obtained. As a result of X-ray diffraction of the resulting powder, precipitation of barium osumilite crystals was confirmed.
(Production of Sound-absorbing Material)
In the impregnation-drying-calcination step S3, the fiber preform 2 in the form of a felt which had been cut into a predetermined size was impregnated in the sol-gel solution 4, followed by vacuum deaeration to sufficiently impregnate the solution in the fiber preform. The fiber preform taken out from the solution was allowed to stand for 20 minutes on a shelf plate on which an excess solution could be removed. The fiber preform from which excess solution had been removed sufficiently was dried using a drying apparatus at 80° C. for 8 hours and then calcined at 500° C. for 30 minutes in the air. The procedure of impregnation, drying and calcination was repeated until the fiber preform had a desired bulk density.
In this test, two products different in bulk density, that is, a low bulk density product (from 0.07 to 0.08 g/cm3) and a high bulk density product (0.11 g/cm3) were manufactured. The above-described procedure was repeated twice for the production of the low bulk density product and eight times for the production of the high bulk density product.
The sample which had finished the desired times of impregnation, drying and calcination was subjected to crystallization treatment at 1250° C. for 1 hour in the crystallization Step S4. After the completion of baking, the crystallized sample was processed into a final product of a necessary size.
The measurement results of the bulk density of the completed fiber-reinforced heat-resistant sound-absorbing material are shown in Table 1. The raw materials are added at the following weight ratio:
The completed fiber-reinforced heat-resistant sound-absorbing material has the following porosity:
High bulk density product: 0.96
Low bulk density product: 0.97.
It has been confirmed by the test which will be described later that the completed fiber-reinforced heat-resistant sound-absorbing material has a porosity of 90% or greater and has a high sound absorbing performance in a wide frequency band. In addition, a preform having a bulk density of from 0.072 to 0.11 g/cm3 can be obtained and also the weight can be reduced to about one fourth of the porous sound-absorbing material.
(Thermal Shock Test)
The sound absorbance, size and weight of the above-described two fiber-reinforced heat-resistant sound-absorbing materials 6 different in bulk density were measured before and after exposure to thermal shock.
The thermal shock test was conducted under the following cycles: the number of thermal shock cycles: 60 cycles, time per cycle: 75 minutes, maximum steady-state temperature/time: 610 K (337° C.)/35 minutes, heating to the maximum temperature: 20 minutes.
A change in the size or weight of the sample between before and after the thermal shock test was measured to find the presence or absence of a change in the shape of pores.
The measurement results of the bulk density of the sound-absorbing material after thermal shock test are shown in Table 2.
It has been understood from
(Evaluation Test of Heat Resistance)
Two fiber-reinforced heat-resistant sound-absorbing materials different in bulk density were evaluated. In this test, a test piece which had been impregnated sufficiently with kerosene, followed by removal of excess kerosene on a drain board was used as a sample. The resulting test piece was ignited with a lighter and when it was burnt out, the test was completed. The test piece was then collected. The test piece was weighed before and after the combustion test. The test was conducted at a flaming temperature of about 1700° C.
The heat resistance test results are shown in Table 3. A slight increase in weight was observed after the test, which is presumed to owe to the kerosene remaining unburned and the soot deposited on the surface of the sample. The fiber-reinforced heat-resistant sound-absorbing material 6 is not damaged at all even exposed to the flaming temperature of about 1700° C. for 10 minutes or greater, suggesting that it has heat resistance against temperatures as high as about 1500° C.
It should be noted that the present invention is not limited to the above-described Examples and Embodiments. It is needless to say that the invention can be modified to an extent not departing from the scope of the invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2004-118077 | Apr 2004 | JP | national |
This is a divisional application of U.S. patent application Ser. No. 10/599,281, which was filed on Sep. 25, 2006 as the National Phase Application in the United States of International Patent Application No. PCT/JP2005/002437 filed Feb. 17, 2005, which claims priority on Japanese Patent Application No. 118077/2004, filed Apr. 13, 2004. The entire disclosures of the above patent applications are hereby incorporated by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4464475 | Beall et al. | Aug 1984 | A |
| 5126087 | Lespade et al. | Jun 1992 | A |
| 5895897 | Sasaki | Apr 1999 | A |
| Number | Date | Country |
|---|---|---|
| 10-187163 | Jul 1998 | JP |
| 10-194864 | Jul 1998 | JP |
| 2000-154066 | Jun 2000 | JP |
| 2001-010871 | Jan 2001 | JP |
| 2002-167290 | Jun 2001 | JP |
| Entry |
|---|
| Hu Ching et al., “Investigation of Sol-Gel Processing of Ceramic Matrix Composites,” AMD-vol. 194, Mechanics in Materials Processing and Manufacturing, ASME 1994, pp. 353-360. XP009131046. |
| International Search Report corresponding to European Application No. EP 05719239.5, completed Mar. 18, 2010. |
| Search Report issued in corresponding International Application No. PCT/JP2005/002437, completed May 19, 2005 and mailed Jun. 7, 2005. |
| Number | Date | Country | |
|---|---|---|---|
| 20110012047 A1 | Jan 2011 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10599281 | US | |
| Child | 12893942 | US |