Fiber reinforced magnesium alloy

BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention relates in general to a fiber reinforced magnesium alloy as a material for automotive parts, machine parts or aerospace devices which are required to have heat resistance at elevated temperatures and to be lightweight, with excellent mechanical properties. The present invention relates more particularly to an alumina fiber reinforced magnesium alloy using alumina fiber as reinforcement and magnesium alloy as a matrix.
2. Description of the Prior Art
In recent years, the study of composite materials has become more and more advanced. There have been developed and utilized many composite materials such as fiber reinforced plastics (FRP), fiber reinforced ceramics (FRC) and fiber reinforced metals (FRM).
As in the case of fiber reinforced metals, some alloys which belong to so-called light metals such as aluminum alloy or magnesium alloy have been also used as a matrix. As for the latter, magnesium alloys such as MDC1A classified by JIS (AZ91A by ASTM standard), MC7 (ZK61A by ASTM standard) or MC8 (EZ33A by ASTM standard) and magnesium alloys such as AM60A, AS41A or QE22A classified by ASTM standard are supposed to have been available.
It is well known that alumina fibers are characterized by high strength, heat stability at high temperatures and low thermal expansion. Furthermore, manufacturing costs can be reduced when utilizing them as the reinforcement, because of their relative inexpensiveness.
However, composite materials, for example, formed by hot melt forging, generally exhibit low heat resistance when using alumina fibers as the reinforcement and the above magnesium alloys as the matrix alloy. Therefore, these alloys are not preferred for use at elevated temperatures such as 200.degree. C. or over.
SUMMARY OF THE INVENTION
It is an object of the present invention to provide a short alumina fiber reinforced magnesium alloy having excellent mechanical properties and heat resistance at relatively high temperatures, for example, at least 200.degree. C.
It is another object of the present invention to provide a short alumina fiber reinforced magnesium alloy having low thermal expansion.
The present invention has been achieved based on the following information recognized by the present inventors as a result of a variety of experiments and research on heat resistance and the mechanical properties of alloy composition. That is, the heat resistance and mechanical properties of alloys are highly improved when neodymium is contained in the magnesium alloy.
A short alumina fiber reinforced magnesium alloy is composed of 70 to 95 vol % of magnesium alloy consisting of 2 to 15 wt % of neodymium and the balance essentially of magnesium, and 30 to 5 vol % of short alumina fibers. More preferably, the magnesium alloy may contain 4 to 7 wt % of neodymium. The neodymium component may be composed of neodymium-containing metals such as didymiums containing at least 70 wt % of neodymium.
The magnesium alloy may contain at least one constituent selected from the groups consisting of less than 3 wt % of manganese, less than 1.5 wt % of yttrium, less than 5 wt % of samarium, less than 5 wt % of praseodymium, less than 5 wt % of gadolinium, less than 5 wt % of scondium, and less than 8 wt % of cerium. The cerium component may be composed of cerium-containing metals such as mischmetals containing at least 50 wt % of cerium. The magnesium component may contain a small amount of impurities which comprise a total of less than 0.5 wt % of zinc, silicon, iron, copper and/or nickel.
A process for forming a short alumina fiber reinforced magnesium alloy comprises the following steps; forming and placing alumina fiber preform, injecting molten magnesium alloy containing 2 to 15 wt % of neodymium and the balance essentially of magnesium into the fiber preform, saturating the alumina fiber preform with the molten alloy, and solidifying the magnesium alloy saturated alumina fiber preform.
According to the present invention, heat resistance and mechanical properties at relatively high temperatures are highly improved by the addition of neodymium to the matrix. Furthermore, when the matrix is reinforced by alumina fibers, the fabricated composite material exhibits high strength, stability at high temperatures and low thermal expansion resulting from the properties of the alumina fibers. The composite materials so obtained combine these characteristics by using magnesium alloy containing neodymium as the matrix and short alumina fibers as the reinforcement. Moreover, composites according to the present invention can be used in fabricating lightweight articles, and manufacturing costs can be kept low as alumina fibers are inexpensive.

BRIEF DESCRIPTION OF THE DRAWINGS
The present invention will be understood more clearly from the preferred embodiments described herebelow and from the appended drawings which illustrate detailed construction of the embodiments, which, however, should not be taken to limit the invention but are for explanation and understanding only.
In the drawings:
FIG. 1 is a right-half broken away side view of an article cast of short alumina fiber reinforced magnesium alloy according to the present invention;
FIG. 2 is a partial sectional view of cavity of the vertical die cast machine used for casting the short alumina fiber reinforced magnesium alloy of the present invention;
FIG. 3 is a graph showing the relationship between neodymium content in the magnesium alloy and tensile strength or elongation;
FIG. 4 is a graph showing the relationship between fiber volume fraction (%) in the magnesium alloy and tensile strength, 0.2% yield strength or elongation.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
In the present invention, the matrix magnesium alloy contains neodymium or corresponding neodymium-containing metals in a range from 2 to 15 wt %. Here, neodymium-containing metals may include didymium containing principally neodymium, by at least 70 wt %, purified from bastonaesite ore, for example, by the back extraction method. Furthermore, if required, the alloy may additionally contains at least one of the following: less than 3 wt % of manganese, less than 1.5 wt % of yttrium, less than 5 wt % of samarium, less than 5 wt % of praseodymium, less than 5 wt % of gadolinium, less than 5 wt % of scandium, less than 8 wt % of cerium or corresponding cerium-containing metals. Cerium-containing metals may be mischmetals containing principally cerium, by at least 50 wt %, purified from monozidte ore, for example, by the concentration method. The balance consists essentially of magnesium. The fiber reinforced magnesium alloy of the invention is composed of the above matrix of 70 to 95 vol % and the above reinforcement of 30 to 5 vol %. The composition example of didymium and mischmetal is shown in the following Table 1.
TABLE 1______________________________________Composition example ofdidymium and mischmetal (wt %)Elements Didymium Mischmetal______________________________________Nd 72.3 18.2Pr 7.9 6.4La 8.8 22.6Ce 0.8 50.6Cr 0.75 0.03Si 0.56 0.16Fe 7.05 0.59Impurities 1.84 1.42Sum of rare earth 89.8 97.8elements______________________________________
Additionally, the above magnesium may contains less than 0.5 wt % of impurities, such as zinc, silicon, iron, copper, nickel and so on.
When neodymium is contained in the alloy, it acts to increase the heat resistance and to improve the mechanical properties of the alloy. However, no desirable effects are obtained in amounts of less than 2 wt %. On the other hand, amounts exceeding the upper limit of 15 wt % causes embrittlement of the resulting alloy, and tend to cause breaking of the resulting composite materials at relatively small loads. Therefore, the preferred amount of neodymium in the magnesium matrix is determined in a range from 2 to 15 wt %, preferably from 4 to 7 wt %. Didymium as the neodymium-containing may be used, but in this case, the amount of didymium containing neodymium is determined in a range so as to provide enough neodymium to the magnesium alloy to be within the desired neodymium range of 2 to 15 wt %.
In the present invention, short alumina fiber tows are the most preferable reinforcing fiber. It is well known that short alumina fibers show high strength, high stability at high temperatures, and low thermal expansion. Moreover, it is relatively inexpensive fiber while compared with other reinforcing fibers. Generally, silicon dioxide (SiO.sub.2) is contained in short alumina fibers. Silicon dioxide reacts with magnesium in the alloy and forms silicon according to the following reaction formula:
SiO.sub.2 +2Mg=Si+2MgO
However, silicon formed in this reaction acts to decrease the strength of the magnesium alloy containing neodymium. Therefore, short alumina fibers containing minimum amounts of silicon dioxide are preferred.
When the volume fraction (Vf) of short alumina fibers to magnesium alloy is less than 5 vol %, the reinforcing effect of short alumina fibers is insufficient to attain a substantial increase in strength and lower thermal expansion. On the other hand, the Vf exceeding the upper limit of 30 vol % causes large infiltration resistance when alumina fibers are immersed in molten magnesium alloy. Therefore, sound castings cannot be obtained easily, so it is preferably to determine the volume fraction of short alumina fibers in a range from 5 to 30 vol %. The strength of the composites proportionally increases along with Vf increases in the range of the above-mentioned amounts of short alumina fibers.
The present invention will now be described in further detail in the following examples including some examples for comparison.
EXAMPLES
Examples 1 to 5, Comparisons 1 to 5
Alloys of comparisons 1 to 5 were, according to the name of ASTM standards, AZ92, AZS1010 (manufactured by Ube Industries Ltd.), AS21, EX33A and QE22A, and alloys of examples 1 to 5 were Mg-5 wt % of Nd, Mg-5 wt % of Nd-1 wt % of Mn, Mg-5 wt % of Nd-1 wt % of Y, Mg-5 wt % of Nd-4 wt % of mischmetal, and Mg-4 wt % of Nd-2 wt % of Sm. Respective compositions of these comparisons and examples are shown in the following Table 2.
TABLE 2__________________________________________________________________________Compositions of magnesium alloys for the composite material matrix Alloy Elements (wt %)Sample Alloy Al Zn Si Mn MM* Di** Nd Y Sm Ag Zr Mg__________________________________________________________________________Comp. 1 AZ92 9.1 2.0 -- 0.25 -- -- -- -- -- -- -- balanceComp. 2 AZS1010 9.3 0.6 0.59 0.19 -- -- -- -- -- -- -- balanceComp. 3 AZ21 2.3 0.5 0.80 0.60 -- -- -- -- -- -- -- balanceComp. 4 EZ33A -- 2.5 -- -- 3.2 -- -- -- -- -- 0.6 balanceComp. 5 QE22A -- -- -- -- -- 2.5 -- -- -- 2.1 0.5 balanceExam. 1 Mg--5% Nd -- -- -- -- -- -- 5.1 -- -- -- -- balanceExam. 2 Mg--5% Nd--1% Mn -- -- -- 0.80 -- -- 4.9 -- -- -- -- balanceExam. 3 Mg--5% Nd--1% Y -- -- -- -- -- -- 4.7 1.2 -- -- -- balanceExam. 4 Mg--5% Nd--4% MM* -- -- -- -- 4.1 -- 5.0 -- -- -- -- balanceExam. 5 Mg--4% Nd--2% Sm -- -- -- -- -- -- 4.2 -- -8 -- -- balance__________________________________________________________________________ Comp.: comparison, Exam.: example *Rare earth metals added by mischmetal addition **Rare earth metals added by didymium addition
On the other hand, short alumina fiber preforms (having about 100 mm diameter, 20 mm thickness, and about 10 vol % of Vf) were formed disc-like by the suction method in which short alumina fibers (manufactured by IMPERIAL CHEMICAL INDUSTRIES PLC; less than 5 wt % Si content) were suspended in water then suctioned. The direction of these fibers were arranged randomly parallel to the disc surface of the fiber preform.
Casting was performed using a vertical die cast machine having a diagrammatical structure as shown in FIG. 2. Referring now to FIG. 2, die cavity 1 is defined by a fixed mold 3 fixing to a platen 2 and a movable mold 4. Sleeve 5 is fixed within fixed mold 3. Core 6 is spaced on the upper end of the sleeve 5, and a plunger 6 is movable spaced to contact with ceramic paper (sold by the name of Fine Flex Paper) 7 fitted within the sleeve 5.
Molten magnesium alloy 10 having a composition as previously shown in Table 1 was supplied to the inside of the ceramic paper 7 within the sleeve 5. The die cavity 1 was opened by upwardly moving the movable mold 4, a dish-like preform of compressed short alumina fibers 8 was placed on the core 6, then the die cavity was closed by securing the movable mold 4 to the fixed mold 3. After the closing was completed, molten magnesium alloy 10 in the sleeve 5 was injected upwardly into the die cavity 1 by the plunger 9 to infiltrate the preform. The molten magnesium alloy 10 cast in the die cavity 1 and the saturated fiber preform 8 were solidified. Thus, casting article 11 formed of short alumina fiber reinforced magnesium alloy as previously shown in FIG. 1 was obtained. The casting conditions are shown in the following Table 3.
TABLE 3______________________________________Casting Conditions______________________________________Retaining Temperature 720.degree. C.of Molten Mg AlloyPre-heating Temperature of 600.degree. C.Short Alumina Fiber PreformInjection Velocity 40 mm/secCasting Pressure 1000 kgf/cm.sup.2Cavity Temperature 150 to 250.degree. C.Lubricant HITASOL (water soluble, Graphite-type Agent)Die Closing Time 45 secondsOthers Using Core Using Ceramic paper______________________________________ article 10 cast from short alumina fiber reinforced magnesium as shown in FIG. 1 were done. Test pieces were cut from the article 11 where the fiber preform 8 were coexisting, being parallel to the disc surface of the preform. Tensile test were done at 200.degree. C. and creep rupture tests were done at 250.degree. C. according to JIS, that is JIS G 0567 and JIS Z 2272, respectively. The results are shown in the following Table 4.
It will be noted from Table 4 that Examples 1 to 5 exhibited good tensile strength at 200.degree. C. and good 0.2% yield strength, further to say excellent creep rupture strength at 250.degree. C. compared with Comparisons 1 to 5. Furthermore, very little difference was found in the strengths of composites examples 1 to 5.
Examples 6 to 12, Comparisons 6 to 8, References 1 to 11
Disc-like short alumina fiber preform 8 comprising 10 vol % Vf prepared in examples 1 to 5 were placed on the core 6 in the cavity 1 previously shown in FIG. 2. Molten magnesium alloy 10 having compositions as shown in Table 5 were injected into the cavity 1 through the alumina fiber disc. Thus comparison 6, examples 6 to 12 and comparisons 7, 8, having shapes as shown in FIG. 1, were cast into articles of short alumina fiber reinforced magnesium alloy. Test pieces were cut out then tensile tests at 200.degree. C. and creep rupture tests at 250.degree. C. were done in the same manner as examples 1 to 5. The obtained results are shown in the following Table 6.
TABLE 4__________________________________________________________________________Results of tensile test at 200.degree. C. and creep rupture test at250.degree. C. Tensile Test Creep Rupture Test *1 Tensile Strength 0.2% Yield Elongation (rupture time: h)Alloy Heating (kgf/mm.sup.2) Strength (kgf/mm.sup.2) (%) 5 kgf/mm.sup.2 7 kgf/mm.sup.2 10__________________________________________________________________________ kgf/mm.sup.2C.1 AZ92 T6 *2 15.2 12.6 0.6 10 0.8 --C.2 AZS1010 T6 *3 17.4 13.5 1.7 43 0.1 --C.3 AZ21 F *4 14.1 11.9 0.6 78 3 --C.4 EZ33A T5 *5 16.5 12.0 3.4 160 21 0.7C.5 QE22A T6 *6 20.1 13.6 3.8 321 81 12E.1 Mg--5% Nd F 22.1 15.7 2.3 889 129 23E.2 Mg--5% Nd--1% Mn F 19.5 14.3 2.1 894 131 20E.3 Mg--5% Nd--1% Y F 19.2 13.9 2.6 869 125 18E.4 Mg--5% Nd--4% MM F 18.2 13.6 1.7 923 138 28E.5 Mg--4% Nd--2% Sm F 20.4 14.8 2.7 811 117 13__________________________________________________________________________ C.: comparison, E.: example *1: Rupture Time (h:hours) *2: Quenching in water after 20 h. of retaining at 410.degree. C., then air cooling after 5 h. of retaining at 220.degree. C. *3: Quenching in water after 20 h. of retaining at 415.degree. C., then air cooling after 16 h. of retaining at 170.degree. C. *4: No heat treatment was performed after casting. *5: Air cooling after 5 h. of retaining at 215.degree. C. *6: Quenching in water after 4 h. of retaining at 530.degree. C., then ai cooling after 8 h. of retaining at 204.degree. C.
For reference purposes, articles were cast using molten magnesium alloy having a composition as previously shown in Table 5. These articles were not reinforced by any kind of fibers. Then tensile tests at 200.degree. C. and creep rupture tests at 250.degree. C. were preformed in the same manner as examples and comparisons 1 to 5. The obtained results are shown in Table 7.
Furthermore, tensile strength and elongation obtained during the tensile tests were summarized and shown in FIG. 3.
TABLE 5______________________________________Magnesium Alloy Compositions Composition (wt %)Sample Alloy Nd Mg______________________________________Comparison 6 Mg--1% Nd 0.9 balanceExample 6 Mg--2% Nd 2.1 balanceExample 7 Mg--3% Nd 2.9 balanceExample 8 Mg--4% Nd 3.9 balanceExample 1 Mg--5% Nd 5.1 balanceExample 9 Mg--7% Nd 6.9 balanceExample 10 Mg--10% Nd 9.5 balanceExample 11 Mg--12% Nd 12.0 balanceExample 12 Mg--15% Nd 14.8 balanceComparison 7 Mg--17% Nd 16.8 balanceComparison 8 Mg--20% Nd 19.6 balance______________________________________
TABLE 6__________________________________________________________________________Results of tensile tests (200.degree. C.) and creep rupture tests(250.degree. C.) of fiber reinforced magnesium alloy Tensile Test Creep Rupture Test Tensile Strength 0.2% Yield Elongation (rupture time: h)Sample Alloy (kgf/mm.sup.2) Strength (kgf/mm.sup.2) (%) 5 kgf/mm.sup.2 7 kgf/mm.sup.2 10 kgf/mm.sup.2__________________________________________________________________________Comparison 6 Mg--1% Nd 12.8 6.3 6.4 182 3 0.1Example 6 Mg--2% Nd 16.4 9.9 4.9 364 10 0.2Example 7 Mg--3% Nd 19.2 12.4 3.8 550 25 2Example 8 Mg--4% Nd 20.8 14.8 2.7 698 62 8Example 1 Mg--5% Nd 22.1 15.7 2.3 889 129 23Example 9 Mg--7% Nd 22.4 16.5 1.3 1080 147 32Example 10 Mg--10% Nd 21.5 17.0 0.7 1350 162 36Example 11 Mg--12% Nd 20.8 18.0 0.4 1580 175 40Example 12 Mg--15% Nd 18.7 18.3 0.3 1820 180 43Control 7 Mg--17% Nd 17.8 17.4 0.3 1830 181 40Control 8 Mg--20% Nd 16.2 16.0 0.2 1860 185 39__________________________________________________________________________
TABLE 7__________________________________________________________________________Results of tensile tests (200.degree. C.) and creep rupture tests(250.degree. C.) of unreinforced magnesium alloy Tensile Test Creep Rupture Test Tensile Strength 0.2% Yield Elongation (rupture time: h)Sample Alloy (kgf/mm.sup.2) Strength (kgf/mm.sup.2) (%) 5 kgf/mm.sup.2 7 kgf/mm.sup.2 10 kgf/mm.sup.2__________________________________________________________________________Reference 1 Mg--1% Nd 9.4 4.3 18.2 9 0.1 0.0Reference 2 Mg--2% Nd 12.8 6.6 13.4 14 0.4 0.0Reference 3 Mg--3% Nd 15.5 8.4 8.7 21 1 0.1Reference 4 Mg--4% Nd 17.3 10.8 6.4 36 3 0.4Reference 5 Mg--5% Nd 18.2 12.8 5.2 50 7 1Reference 6 Mg--7% Nd 18.9 13.4 2.6 69 20 2Reference 7 Mg--10% Nd 18.3 13.7 1.1 94 34 5Reference 8 Mg--12% Nd 17.2 15.5 0.8 110 41 8Reference 9 Mg--15% Nd 14.9 14.5 0.5 138 53 12Reference 10 Mg--17% Nd 14.6 14.2 0.6 152 62 14Reference 11 Mg--20% Nd 13.5 13.4 0.5 173 75 17__________________________________________________________________________
It will be noted from FIG. 3 that good tensile strength and creep rupture strength was obtained among samples with neodymium contents ranging from 2 to 15 wt %, further excellent results were also obtained among samples with neodymium contents range from 3 to 12 wt %. Best results were obtained with neodymium contents ranging from 4 to 7 wt %. Additionally, slight difference between the curvature of reinforced and unreinforced magnesium alloy is found in FIG. 3, it seems that the fluidity of molten magnesium alloy is increased according to increased neodymium content.
Examples 13 to 15
The preferred range of neodymium content was defined from the results of examples 6 to 12. In order to defined the preferable range of Vf, the following experiments were performed. Articles 11 were cast from short alumina fiber reinforced magnesium alloy using the alloy having composition of Mg-5 wt % Nd of example 1 as a matrix. Casting was performed in the same manner as example 1, except that short alumina fiber preforms of 5%, 10% (same volume as example 1), 20%, 30% and 40% Vf(vol %) instead of 10% Vf (vol %) were used. These short alumina fiber preforms were formed in the same manner as example 1. Therefore, short alumina fiber preforms having the various Vf were prepared by suspending an appropriate amount of short alumina fibers in water then suctioning, and after suctioning, pressing if necessary then binding using alumina binder.
Test pieces were cut from each cast article 11 (but heat treatment was not performed), then these pieces were subjected to tensile tests at 200.degree. C. and creep rupture tests at 250.degree. C. The obtained results are shown in Table 8. and the results of the tensile tests are shown in FIG. 4.
TABLE 8__________________________________________________________________________Results of tensile tests at 200.degree. C. and creep rupture tests at250.degree. C. at various ranges of Vf Tensile Test Creep Rupture Test Vf Tensile Strength 0.2% Yield Elongation (rupture time: h)Sample (vol %) (kgf/mm.sup.2) Strength (kgf/mm.sup.2) (%) 5 kgf/mm.sup.2 7 kgf/mm.sup.2 10 kgf/mm.sup.2__________________________________________________________________________Example 13 5 18.3 13.1 3.3 224 53 6Example 1 10 22.1 15.7 2.3 380 129 23Example 14 20 25.3 20.8 1.5 489 193 44Example 15 30 26.1 21.0 1.2 560 232 60Comparison 9 40 23.9 20.3 0.9 570 220 58__________________________________________________________________________
It will be noted from the results of Table 8 and FIG. 4 that the tensile strength of the cast articles was not increased when the Vf of short alumina fibers preform exceeded the upper limit of 30 vol %, and further to say, as at volume fractions exceeding the upper limit, magnesium alloy as a matrix cannot infiltrate short alumina fiber preforms easily, sound castings cannot be obtained. On the other hand, at a alumina short fiber Vf of less than 5 vol %, reinforcing effects cannot be obtained because the tensile strength is not so different from that of reinforced alloy. Therefore, taking all of the above mentioned into consideration, the preferable range of the Vf is determined in the range of 5 to 30 vol %.
Although the present invention has been shown and described with respect to detailed embodiments thereof, it should be understood by those skilled in the art that various changes in form and detail thereof may be made without departing from the spirit and the scope of the appended claims.

Number	Date	Country
0258178	Mar 1988	EPX
1354363	May 1974	GBX

Fiber reinforced magnesium alloy

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

Foreign Referenced Citations (2)

Non-Patent Literature Citations (3)

Entry
Tumanov et al. "Composite materials based on light alloys" Chemical Abstract No. 89(24):202392c, 1978.
Hino et al. "Mechanical properties of alumina short fiber-reinforced magnesium-neodymium alloys", Chemical Abstracts 112(24):221694n, 1990, Feb.
Hino et al., "Effect of stressing during quenching upon the thermal . . . " Chemical Abstract No. 113(12):101723v, 1990, Jan.