Fibrous batts impregnated with aqueous dispersions based on heat-hardenable phenolic resins

The invention relates to aqueous dispersions based on heat-hardenable phenolic resins. More particularly, the invention relates to aqueous dispersions of heat-hardenable phenolic resins, which are characterized by excellent stability and by a low pollution index, and which are capable of being infinitely diluted with water. In view of the properties noted above and, also, in view of the excellent adhesion to glass, when cured, the aqueous dispersions of this invention have particular utility in applications wherein mineral fibers are sprayed with the aqueous dispersions and subsequently formed into mineral fiber batts and other such compacted structures.
Mineral fiber batts and other such compacted structures, which have found wide acceptance in the fields of thermal and acoustical insulation, have been produced by first blowing a stream of molten glass or slag with high pressure steam in such a manner that the glass or slag stream is drawn into fibers of random lengths. The fibers, while in transit in a forming hood or blow chamber, and while still at elevated temperatures from the drawing operation, have then been sprayed with an aqueous solution of a heat-hardenable phenolic resin and thereafter allowed to settle into a continuous mat on an endless foraminous conveyor belt. Generally, there is sufficient residual heat in the mineral fibers to volatilize substantially all of the water from the "phenolic" binder, leaving the binder on the fibers in a viscous or semi-viscous state. The sprayed fibers, in the form of a batt, have been transferred to a curing oven, heated by air which is at relatively high temperatures, about 400.degree.F and which is blown through the batt. The relatively high temperatures involved effect a cure of the binder to an infusible state.
At the relatively high temperatures employed in this process, the low molecular weight components of the water-soluble phenolic resin tend to volatilize, escape to, and polute the atmosphere. Consequently, the use of water-soluble, heat-hardenable phenolic resins as binders in the production of fiber batts, is being severely restricted in view of the current pollution standards now in effect in may areas of the country.
Attempts to utilize phenolic resins made up of molecules of higher molecular weight, in the form of aqueous dispersions, in order to minimize volatilization have not proved to be particularly successful. Such dispersions have poor stability characteristics as the phenolic resin thereof settles out within a few minutes after preparation, coalescing into a continuous resin phase. Furthermore, such dispersions cannot be diluted with water to a consistency suitable for use in spray applications.
The present invention provides aqueous dispersions which can be successfully used in the production of mineral fiber batts by a spray operation, the dispersions being characterized by excellent bonding and application efficiency. The aqueous dispersions of this invention exhibit a tensile strength of at least about 300 psi when tested according to the Glass Adhesion Test described subsequently in this specification. Also, the aqueous dispersions remain stable for periods of time in excess of about 2 weeks, that is, the phenolic resin particles thereof do not settle out into a continuous resin phase. Consequently, the dispersions can be prepared, shipped to the ultimate user, and stored for extended periods of time. Further, the aqueous dispersions of this invention can be infinitely diluted with water to any desired concentration of phenolic resin solids with substantially no change in the size and uniformity of the dispersed resin particles. Furthermore, the aqueous dispersions of this invention retain the excellent properties discussed above, and also retain their flow and gel properties for extended periods of time, in contrast to the water-soluble phenolic resins. Also, the aqueous dispersions of this invention have a pollution index of less than about 6 percent, which is acceptable from an environmental standpoint, based on standards currently in force.
The aqueous dispersions of this invention contain a heat-hardenable phenolic resin having a weight average molecular weight of at least about 400, generally about 500 to about 3000, and preferably about 500 to about 2000.
Particularly desirable aqueous dispersions are those having a gel time of not more than about 180 seconds, generally about 10 to about 170 seconds, preferably about 20 to about 150 seconds, and more preferably about 30 to about 100 seconds, wherein the heat-hardenable phenolic resin thereof has a weight average molecular weight as defined above and wherein substantially all of the resin particles have a diameter of less than about 60 microns. Even more desirable aqueous dispersions are those as defined in the preceding paragraph wherein the resin particles have a diameter on average of about 5 to about 20 microns with substantially all resin particles having a diameter less than about 40 microns.
The heat-hardenable phenolic resins, used to produce the aqueous dispersions of this invention are resole resins obtained by condensing a phenol with an aldehyde in the presence of an alkaline catalyst.
Among suitable phenols which can be condensed with an aldehyde to produce phenol-aldehyde "resole" resins are the monohydric as well as the polyhydric phenols.
Among suitable monohydric phenols can be noted; phenol and those phenols having the general formula:
FORMULA I ##SPC1##
wherein x is an integer having a value of 1 to 2 inclusive, each R, which can be the same or different, is an alkyl radical containing from 1 to 9 carbon atoms inclusive, an alkoxy radical containing from 1 to 9 carbon atoms inclusive, or a halogen, e.g., chlorine, bromine and iodine; with the proviso that at least three positions other than meta to the hydroxyl group are unsubstituted.
Specific phenols falling within the scope of Formula I are: alkylated phenols, exemplary of which are m-cresol, m-ethylphenol, m-propylphenol, m-isopropylphenol, m-sec-butylphenol, m-amylphenol, m-hexylphenol, m-nonylphenol and other like phenols, as well as the commercially available meta-cresol which contains small amounts of both the para and the ortho isomers; alkoxylated phenols, exemplary of which are m-methoxyphenol, m-ethoxyphenol, m-propoxyphenol, m-hexoxyphenol, 3,5-dimethoxyphenol, and the like; halogenated phenols such as meta-chlorophenol, meta-bromophenol, and the like.
Among suitable polyhydric phenols can be noted resorcinol, and the like, as well as polyhydric, polynuclear phenols having the formula:
FORMULA 2 ##SPC2##
wherein Z is a divalent radical, as for example, sulfur, oxygen, alkylidene, alkylene and the like; and also substituted derivatives of phenols falling with the scope of Formula 2.
Exemplary of specific polyhydric, polynuclear phenols are the following: bis(hydroxyphenyl)alkanes such as 2,2-bis(4-hydroxyphenyl)propane, commonly referred to as Bisphenol A, 2,4'-dihydroxyldiphenylmethane, dihydroxydiphenyl sulfone and the like.
Also small amounts of di- and/or mono-functional phenols such as p-nonylphenol and 2,5-di-tert-butylphenol can be used in conjunction with tri and higher functional phenols, illustrated above, to produce suitable phenolic resins for purposes of this invention.
Examples of aldehydes which can be condensed with the phenols listed above to produce the phenol-aldehyde resins are: formaldehyde in any of its available forms, i.e., formalin and para-formaldehyde; furfural, and the like.
The amount of aldehyde used to prepare the heat-hardenable or resole resins of this invention is at least about 0.9 mole per mole of phenol, generally about 1 to about 3 moles, and preferably about 1.2 to about 2.5 moles per mole of phenol.
As previously stated, the condensation of a phenol and an aldehyde is carried out in a reaction medium containing an alkaline catalyst. Illustrative of suitable catalysts are the following: alkali metal and alkaline earth metal hydroxides or oxides, as for example, sodium hydroxide, potassium hydroxide, calcium hydroxide, calcium oxide, barium hydroxide, barium oxide and the like, or an amine such as hexamethylenetetramine or ammonia.
Particularly desirable resins for purposes of this invention are those produced using barium hydroxide as a catalyst. An aqueous dispersion of such resin when applied to mineral fibers and cured, exhibits an unusually high degree of adhesiveness thereto.
The amount of catalyst used in producing the resole resins is about 0.01 to about 0.1 mole per mole of phenol, preferably about 0.02 to about 0.05 mole per mole of phenol. For a detailed discussion of condensates produced from a phenol and an aldehyde and methods for the production thereof, reference is made to the following:
"Phenolic Resins" by W. A. Keutgen ENCYCLOPEDIA OF POLYMER SCIENCE & TECHNOLOGY Volume 10, pages 1-73 Published by Interscience, John Wiley - 1969
The preparation of the aqueous dispersions of this invention can be carried out by a number of convenient methods, for example by condensing a phenol with an aldehyde in a reaction mixture containing an alkaline catalyst to produce a heat-hardenable phenolic resin, adding to the mixture a mixture of "gums", as will be described subsequently, and adjusting the pH of the resultant mixture, if necessary, to less than about 8, generally to a pH of about 3 to about 7.5, and preferably to a pH of about 4.5 to about 6.5, and then condensing (bodying) the resin, if necessary, to a weight average molecular weight as previously described.
Alternatively, the pH of the mixture can be adjusted, if necessary, prior to the addition of the gums, the gums then added and the resin then bodied as indicated above. Also, the gums can be added, along with the phenol, aldehyde, and alkaline catalyst, into the reaction flask, and this mixture can then be condensed and bodied, as described above.
With each of the methods described, the aqueous dispersion produced has a pH of less than about 8 generally about 3 to about 7.5 and preferably about 4.5 to about 6.5.
The gums which are used to prepare the aqueous dispersions are a mixture of gum arabic and one or more of the following gums: (1) a polysaccharide having mannose and galactose units, particularly desirable examples of such polysaccharides being a guar gum, a locust bean gum, and the like (Guar gums are available commercially from Stein Hall & Co. under the designation "Jaguar" gums); (2) a polysaccharide having D-mannuronic acid and L-guluronic acid units, particularly desirable examples of such polysaccharides being algin gum, and the like; and (3) gum carageenan.
The combined weight of the gums used in producing the aqueous dispersions is about 0.5 to about 12, preferably about 0.5 to about 10 and more preferably about 1.2 to about 4.5 parts by weight, based on each 100 parts by weight "phenol" used in producing the heat-hardenable phenolic resin. The weight ratio of gum arabic to the other recited gums is about 0.5 to about 20 to 1, preferably about 0.5 to about 16 to 1 and more preferably about 1 to about 5 to 1.
The production of the dispersions of this invention is further exemplified by the Examples noted in the specification wherein the gums are utilized in the form of aqueous solutions or in the dry form.
In utilizing the dispersions of this invention for mineral fiber bonding by a "spray" application wherein the solid resin content is of the order of about 2 to about 20 percent by weight, it is customary to add thereto such additives as flame-retardants, exemplary of which are urea and the like, silane coupling agents and other additives well known in the art. Silane coupling agents are generally used in amounts of about 0.1 percent to about 0.5 percent by weight based on the solids content of the aqueous dispersion. Among suitable silanes are the trialkoxy amino alkyl silanes wherein a nitrogen atom thereof is separated from a silicon atom by a least three sequential carbon atoms. Specific silanes are the following: ##EQU1##
A particularly desirable silane is one used in carrying out the Glass Adhesion Test.
Although the aqueous dispersions of this invention have been described primarily in relation to "spray" applications to produce mineral fiber batts suitable as thermal and acoustical insulation, the aqueous dispersions can be used as laminating varnishes, additives to paper and other cellulosic pulp and in general, in bonding applications, to bond together organic and inorganic particles and fibers.
In the following examples, which are illustrative of the present invention, properties noted therein were determined by the following procedures.
Gel Time - determined by placing a two gram sample of the aqueous dispersion on a hot plate which was at a temperature of 150.degree.C. The resin was stroked with a spatula and the time required to reach a "no string" condition noted and reported as the Gel Time. A "no string" condition is reached when there is no pulling of strings of the material, by the spatula, from the main body of the resin.
Pollution Index - determined by weighing a two gram sample of the dispersion into a weighed tin. To the sample, there was then added 15 ml. analytical grade methanol and the contents of the tin thoroughly mixed. The tin, containing the sample, was placed in a 300.degree.F oven for 2 hours. At the end of the two hour period, the tin was removed from the oven and placed in a desiccator where the tin and the residue cooled to room temperature. The tin, containing the residue, was weighed and the weight of the residue recorded. Tin and residue were then placed in a 450.degree.F oven for 20 minutes. The tin, with the residue therein, was removed from the oven, cooled to room temperature in a desiccator and reweighed. Percent weight loss of the residue, resulting from the heating cycle in the 450.degree.F oven was calculated and reported as the Pollution Index. A pollution Index below about six percent is acceptable from an environmental standpoint.
Glass Adhesion Test - the composition to be tested, based on the aqueous dispersion of Example I had the following formulation:
GRAMS______________________________________dispersion of Example I 34.38ammonium sulfate 0.2 (accelerator)urea 3.6silane 0.54water 6.82______________________________________
The composition was prepared by weighing the water into a 100 ml. beaker and adding the ammonium sulfate thereto. The mixture was stirred to solution and to this solution there was then added in sequence, the aqueous dispersion, the urea and silane. The pH of the ultimate mixture was adjusted to 8.2 by the addition thereto of ammonium hydroxide. The composition was charged into a Hobart mixer which contained 582 grams of small glass beads (designated as P-93 Glass Spheres by the supplier, Cataphote Corp.). The materials were thoroughly mixed and the mixture then poured into a mold, having a number of dog-bone shaped cavities, which had been preheated in a 450.degree.F oven. The filled mold was placed in the 450.degree.F oven for 5 minutes. Test specimens were then removed from the mold, half placed in a desiccator and the other half placed in a humidity chamber wherein the relative humidity was 100% and the temperature was 120.degree.F.
Binder content of each specimen was 3 percent by weight.
Specimens were aged and tested for tensile strength which is indicative of "bonding" strength, using a Baldwin Tensile Tester with the cross-head speed set at 0.2 inch per minute.
The silane used in the formulation had the following structure:
H.sub.2 NC.sub.2 H.sub.4 NHC.sub.2 H.sub.4 NHC.sub.3 H.sub.6 Si(OCH.sub.3).sub.3
Molecular Weight Distribution = Mw/Mn
Number Average Molecular Weight = (Mn) and
Weight Average Molecular Weight = (Mw) : determined
according to procedure described in J. Polymer Science, Part A, 2, 835, 1964 by J. Moore.
Particle Size of Resin in the Aqueous Dispersion - determined using a Coulter Counter.

EXAMPLE 1
Into a five-liter, round bottom flask, equipped with a reflux condenser, agitator, thermometer and heating mantle, there was charged 1200 grams of phenol, 1668 grams aqueous formaldehyde (40%), and a slurry of 30 grams of barium hydroxide monohydrate in 60 grams of water. The mixture was then heated to a temperature of 75.degree.C., whereupon the heating mantle was removed and the mixture was allowed to reach a stage of atmospheric reflux through its exothermic heat of reaction. The mixture was then allowed to reflux for about forty-five minutes. At the end of the forty-five minute period, a water solution, made up of 24 grams of gum arabic, 6 grams of guar gum, and 720 grams of water, was added to the contents of the flask. After the addition of the gum there was then added, to the flask, a water solution, made up of 12 grams of sulfuric acid (96.6%) and 48 grams of water, to neutralize the barium hydroxide. The contents of the flask were then brought to a temperature of about 85.degree.C. and maintained at this temperature for about 10 minutes. At the end of the 10 minute period, the contents of the reaction flask were cooled to a temperature of about 50.degree.C. and discharged into a container as a resin-in-water dispersion having a solids content of 42 percent by weight.
Solids content of the aqueous dispersions, as noted in this specification, was determined by placing a weighed sample of the dispersion in a 300.degree.F. oven for 2 hours and weighing the residue after the 2 hour period. Percent solids was calculated by dividing the weight of the residue by the weight of the sample and multiplying by 100.
______________________________________Properties of the phenol-formaldehyde resin:______________________________________Mole ratio of reactants - formaldehyde to phenol = 1.75 to 1Number average molecular weight = 360Weight average molecular weight = 760Molecular weight distribution = 2.1Free phenol = 6.2 percent by wt.Amount of resin made up of one ring compounds = 22 percent by wt.Amount of resin made up of one and two ring compounds = 46 percent by wt.Gel time = 75 secondsParticle size (diameter) of the resin in the dispersion, on average = 10 micronsDiameter of substantially all of particles of resin in the dispersion, less than = 30 microns______________________________________
The particles were excellently dispersed in the aqueous medium, as determined by microscopic examination.
______________________________________pH of the aqueous dispersion = 5.7Pollution Index of the aqueous dispersion = 2.9 percent______________________________________
The aqueous dispersion had excellent stability characteristics - no visual settling of particles after two weeks storage at a temperature of about 23.degree.C. Also, the dispersion could be infinitely diluted with water without significant change as to particle size.
______________________________________Glass Adhesion Test______________________________________Average value of 6test specimens(aged 1 hr. in desiccator) = 700 psiAverage value of 6test specimens(aged 16 hours in humiditychamber) = 600 psi______________________________________
On the basis of 100 parts by weight phenol changed into the reaction flask, the amount of gum arabic in the dispersion was 2 parts by weight, and the amount of guar gum was 0.5 part by weight.
The guar gum noted in this and in subsequent examples is a commercial product sold by Stein-Hall under the designation Jaguar J2S1.
EXAMPLE 2
Into a five-liter, round bottom flask, equipped with a reflux condenser, agitator, thermometer and heating mantle, there was charged 720 grams of water, 24 grams of gum arabic, and 6 grams of guar gum. The materials were mixed for 15 minutes, and to the mixture there was then added 1200 grams of phenol, 1668 grams of aqueous formaldehyde (40%), and 48 grams of aqueous sodium hydroxide (25%). The mixture was then heated to a temperature of 75.degree.C., whereupon the heating mantle was removed and the mixture was allowed to reach a stage of reflux through its exothermic heat of reaction. The mixture was then allowed to reflux for about forty-five minutes. At the end of the forty-five minute period, the reacted mixture was cooled to a temperature of 85.degree.C., and an aqueous mixture, made up of 15.6 grams of aqueous phosphoric acid (85%) and 36 grams of water, was added. After 1.5 hours at a temperature of 85.degree.C., the contents of the flask were discharged into a container as a resin-in-water dispersion having a solids content of 42.2 percent by weight.
______________________________________Properties of the phenol-formaldehyde resin:______________________________________Mole ratio of reactants - formaldehyde to phenol = 1.75 to 1Number average molecular weight = 330Weight average molecular weight = 1500Molecular weight distribution = 4.5Gel time = 76 seconds______________________________________
The size of the resin particles, dispersion thereof in the aqueous medium, and the stability and the dilutability characteristics of the aqueous dispersion were comparable to those of Example 1.
______________________________________pH of the aqueous dispersion = 6.75Pollution Index of the aqueous dispersion = 3.3 percent______________________________________
On the basis of 100 parts by weight phenol charged into the reaction flask, the amount of gum arabic used was 2 parts by weight, and the amount of guar gum was 0.5 part by weight.
EXAMPLE 3
The procedure of Example 1 was repeated using the materials and amounts as noted below. This example differs from Example 1 primarily in that a smaller amount of formaldehyde was used, sodium hydroxide was the catalyst, and phosphoric acid was the neutralizing agent.
______________________________________ AMOUNT IN GRAMS______________________________________Phenol 1200Formaldehyde (40% aqueous solution) 1332Sodium hydroxide (25% aqueous solution) 48Gum arabic 24Guar gum 6Water 720Phosphoric acid (85%) 15.6Water 36______________________________________
Solids content of the resin-in-water dispersion was 45.6 percent by weight.
______________________________________Properties of the phenol-formaldehyde resin:______________________________________Mole ratio of reactants- formaldehyde to phenol = 1.40 to 1Number average molecular weight = 380Weight average molecular weight = 990Molecular weight distribution = 2.6Gel time = 58 seconds______________________________________
The size of the resin particles, dispersion thereof in the aqueous medium, and the stability and dilutability characteristics of the aqueous dispersion were comparable to those of Example 1.
______________________________________pH of the aqueous dispersion = 6.5Pollution Index of the aqueous dispersion = 2.8 percent______________________________________
On the basis of 100 parts by weight phenol charged into the reaction flask, the amount of gum arabic used was 2 parts by weight, and the amount of guar gum was 0.5 part by weight.
EXAMPLE 4
The procedure of Example 1 was repeated using the materials and amounts noted below. This example differs from Example 1 primarily in that a larger amount of formaldehyde was used, sodium hydroxide was the catalyst, and phosphoric acid was the neutralizing agent.
______________________________________ AMOUNT IN GRAMS______________________________________Phenol 1100Formaldehyde (40% aqueous solution) 1760Sodium hydroxide (25% aqueous solution) 44Gum arabic 22Guar gum 5.5Water 660Phosphoric acid (85%) 14.3Water 33______________________________________
The solids content of the resin-in-water dispersion was 42.3 percent by weight.
______________________________________Properties of the phenol-formaldehyde resin:______________________________________Mole ratio of reactants - formaldehyde to phenol = 2.01 to 1Number average molecular weight = 340Weight average molecular weight = 850Molecular weight distribution = 2.5Gel Time = 59 seconds______________________________________
The size of the resin particles, dispersion thereof in the aqueous medium, and the stability and dilutability characteristics of the aqueous dispersion were comparable to those of Example 1.
______________________________________pH of the aqueous dispersion = 6.6Pollution Index of the aqueous dispersion = 3.7 percent______________________________________
On the basis of 100 parts by weight phenol charged into the reaction flask, the amount of gum arabic used was 2 parts by weight, and the amount of guar gum was 0.5 part by weight.
EXAMPLE 5
The procedure of Example 1 was repeated using the materials and amounts noted below. This example differs from Example 1 primarily in that sodium hydroxide was used as the catalyst and hydrochloric acid was used as the neutralizing agent.
______________________________________ AMOUNT IN GRAMS______________________________________Phenol 1200Formaldehyde (40% aqueous 1668 solution)Sodium hydroxide (25% aqueous 48 solution)Gum arabic 24Guar gum 6Water 720Hydrochloric acid (37%) 19Water 58Solids content of resin-in-water dispersion = 41% by weight______________________________________Properties of the phenol-formaldehyde resin:______________________________________Mole ratio of reactants - formaldehyde to phenol = 1.75 to 1Number average molecular weight = 370Weight average molecular weight = 1190Molecular weight distribution = 3.2Gel time = 62 seconds______________________________________
The size and uniformity of the resin particles, dispersion thereof in the aqueous medium, and the stability of the aqueous dispersion were comparable to those of Example 1.
______________________________________pH of the aqueous dispersion = 6.7Pollution Index of the aqueous dispersion = 3.5 percent______________________________________
On the basis of 100 parts by weight phenol charged into the reaction flask, the amount of gum arabic used was 2 parts by weight, and the amount of guar gum was 0.5 part by weight.
EXAMPLES 6-8
The procedure of Example 1 is repeated, using in each instance, various amounts of gum arabic and guar gum. Amounts used, in parts by weight, based on 100 parts by weight of phenol that are charged into the reaction flask, are noted below:
Example 6 gum arabic10 guar gum0.5Example 7 gum arabic guar gum0.5Example 8 gum arabic0.5 guar gum0.5
Properties of these dispersions are comparable to the properties of the dispersion of Example 1.
EXAMPLE 9
The procedure of Example 1 was repeated using the materials and amounts noted below. This example differs from Example 1 primarily in that a mixture of phenol and p-nonylphenol was used.
______________________________________ AMOUNT IN GRAMS______________________________________Phenol 360p-Nonylphenol 40Formaldehyde (40% aqueous solution) 520Barium hydroxide monohydrate 10Gum arabic 2Guar gum 3Water 270Sulfuric acid (96.6%) 3.33Water 13______________________________________
The solids content of the resin-in-water dispersion was 42.1 percent by weight.
______________________________________Properties of the phenol-formaldehyde resin:______________________________________Mole ratio of reactants - formaldehyde to phenol = 1.75 to 1Number average molecular weight = 410Weight average molecular weight = 1440Molecular weight distribution = 3.5Gel time = 60 seconds______________________________________
The size of the resin particles, dispersion thereof in the aqueous medium, and the stability and dilutability characteristics of the aqueous dispersion were comparable to those of Example 1.
______________________________________pH of the aqueous dispersion = 6.4Pollution Index of the aqueous dispersion = 3.2 percentGlass Adhesion TestAverage value of 6 test specimens (aged 1 hr. in desiccator) = 600 psiAverage value of 6 test specimens (aged 16 hrs. in humidity chamber) = 625 psi______________________________________
The formulation of the composition tested using the aqueous dispersion of this example was as follows:
GRAMS______________________________________Aqueous dispersion 33.73Ammonium sulfate 0.2Urea 3.6Silane 0.54Water 7.4______________________________________
Amounts of glass beads used was 582 grams and the resin content of each composite or structure produced was 3 percent by weight.
On the basis of 100 parts by weight "phenols" charged into the reaction flask, the amount of gum arabic used was 0.5 parts by weight, and the amount of guar gum was 0.75 part by weight.
EXAMPLE 10
Example 1 is repeated with the exception that the mole ratio of formaldehyde to phenol is 1.89 to 1, and in lieu of the gums of Example 1, the following gums are used, in the amounts noted, based on 100 parts by weight of phenol charged:
2 parts by weight gum arabic 1 part by weight gum carageenan
The gum carageenan of this example was obtained from Marine Colloids, Inc. under the trade designation "Viscarin 402."
______________________________________Properties of the phenol-formaldehyde resin:______________________________________Mole ratio of reactants - formaldehyde to phenol = 1.89 to 1Number average molecular weight = 310Weight average molecular weight = 870Molecular weight distribution = 2.8Gel time = 145 secondsSolids content of resin-in- water dispersion = 45% by weight______________________________________
The size of the resin particles, dispersion thereof in the aqueous medium, and the stability and dilutability characteristics of the aqueous dispersion are comparable to those of Example 1.
______________________________________pH of the aqueous dispersion = 5.4Pollution Index of the aqueous dispersion = 3.4 percent______________________________________
EXAMPLE 11
Example 1 was repeated using, in lieu of the guar gum, locust bean gum in the same weight relationship.
______________________________________Properties of the phenol-formaldehyde resin:______________________________________Mole ratio of reactants - formaldehyde to phenol = 1.75 to 1Number average molecular weight = 420Weight average molecular weight = 1930Molecular weight distribution = 4.6Gel time = 75 secondsSolids content of resin-in- water dispersion = 41% by weight______________________________________
The size of the resin particles, dispersion thereof in the aqueous medium, and the stability and dilutability characteristics of the aqueous dispersion were comparable to those of Example 1.
______________________________________pH of the aqueous dispersion = 5.5Pollution Index of the aqueous dispersion = 3.5 percent______________________________________
EXAMPLE 12
Example 1 was repeated using, in lieu of the guar gum of Example 1, Jaguar 1212A, a guar gum obtained from Stein-Hall, in the same weight relationship.
______________________________________Properties of the phenol-formaldehyde resin:______________________________________Mole ratio of reactants - formaldehyde to phenol = 1.75 to 1Number average molecular weight = 410Weight average molecular weight = 1760Molecular weight distribution = 4.3Gel time = 80 secondsParticle size (diameter) of the resin in the dispersion, on average = 15 micronsDiameter of substantially all of the particles of the resin in the dispersion = 30 micronsSolids content of resin-in- water dispersion = 41% by weight______________________________________
The size of the resin particles, dispersion thereof in the aqueous medium, and the stability and dilutability characteristics of the aqueous dispersion were comparable to those of Example 1.
______________________________________pH of the aqueous dispersion = 5.75Pollution Index of the aqueous dispersion = 3.4 percent______________________________________
EXAMPLE 13
The procedure of Example 1 was repeated using the materials and amounts thereof as noted below.
______________________________________ AMOUNT IN GRAMS______________________________________Phenol 1200Formaldehyde (40% aqueous solution) 1332Barium hydroxide monohydrate 30Gum arabic 24Guar gum 6Sulfuric acid (20%) 63Water 792______________________________________
Solids content of the resin-in-water dispersion was 41 percent by weight.
______________________________________Properties of the phenol-formaldehyde resin:______________________________________Mole ratio of reactants - formaldehyde to phenol = 1.4 to 1Number average molecular weight = 330Weight average molecular weight = 857Molecular weight distribution = 2.6Free phenol = 11.9 percentAmount resin made up of one ring compounds = 31 percentAmount of resin made up of one and two ring compounds = 56 percentGel time = 132 seconds______________________________________
The size of the resin particles, dispersion thereof in the aqueous medium, and the stability and dilutability characteristics of the aqueous dispersion were comparable to those of Example 1.
______________________________________pH of the aqueous dispersion = 5.0Pollution Index of the aqueous dispersion = 3.2 percent______________________________________
EXAMPLE 14
Into a five-liter, round bottom flask, equipped with a reflux condenser, agitator, thermometer and heating mantle, there was charged 1200 grams of phenol, 1332 grams aqueous formaldehyde (40%), 30 grams of barium hydroxide monohydrate, 24 grams of gum arabic, and 6 grams of guar gum. The resultant mixture was then heated to a temperature of about 75.degree.C., whereupon the heating mantle was removed and the mixture was allowed to reach a stage of atmospheric reflux through its exothermic heat of reaction. The mixture was then allowed to reflux for about 35 minutes. At the end of the 35 minute period, 792 grams of water were added to the contents of the flask. To the flask, there was then added 61 grams of aqueous sulfuric acid (20%), and the contents of the flask were brought to a temperature of 85.degree.C. and were maintained at this temperature for about 95 minutes. At the end of this period, the contents of the flask were cooled below about 50.degree.C. and were then discharged into a container as a resin-in-water dispersion having a solids content of 42 percent by weight.
______________________________________Properties of the phenol-formaldehyde resin:______________________________________Mole ratio of reactants - formaldehyde to phenol = 1.40 to 1Number average molecular weight = 350Molecular weight distribution = 3.96Weight average molecular weight = 1390Amount of resin made up of one ring compounds = 29 percentAmount of resin made up of one and two ring compounds = 52 percentGel time = 125 seconds______________________________________
The size of the resin particles, dispersion thereof in the aqueous medium, and the stability and dilutability characteristics of the aqueous dispersion were comparable to those of Example 1.
______________________________________pH of the aqueous dispersion = 5.3Pollution Index of the aqueous dispersion = 3.4 percent______________________________________
EXAMPLE 15
Into a 12-liter reaction flask, equipped with a reflux condenser, thermometer and agitator, there was charged 3000 grams of phenol, 3000 grams of aqueous formaldehyde (40%), and 180 grams of hexamethylenetetramine. The resultant mixture was heated to a temperature of 80.degree.C. under a pressure of 16-17 mm of Hg, and held at 80.degree.C. for about 25 minutes. At the end of the 25 minute period, 60 grams of gum arabic, 15 grams of guar gum, and 1800 grams of water were added to the flask in the order recited. The reaction mixture was held at a temperature of 85.degree.C. until the gel time of the product was about 60 seconds. At this point, 120 grams of hexamethylenetetramine were added to the flask, and the reaction continued at a temperature of 85.degree.C. to a product gel time of 25 seconds. The content of the flask were cooled rapidly to below a temperature of 50.degree.C., and were discharged into a container as a resin-in-water dispersion having a solids content of 42 percent by weight.
______________________________________Properties of the phenol-formaldehyde resin:______________________________________Mole ratio of reactants - formaldehyde to phenol = 1.26 to 1Number average molecular weight = 340Weight average molecular weight = 723Molecular weight distribution = 2.13Amount of resin made up of one ring compounds = 29.5 percent by wt.Amount of resin made up of one and two ring compounds = 53.0 percent by wt.Gel time = 25 seconds______________________________________
The size of the resin particles, dispersion thereof in the aqueous medium and the stability and dilutability characteristics of the aqueous dispersion were comparable to those of Example 1.
______________________________________pH of the aqueous dispersion = 7.6Pollution Index of the aqueous dispersion = 2.0______________________________________
EXAMPLE 16
This example illustrates the use of the aqueous dispersions of the invention in the preparation of cellulosic products.
To a mixture of 65 grams of kraft paper pulp, 85 grams of the aqueous dispersion of Example 1, and 10,000 grams of water, there was added sufficient alum to adjust the pH thereof to 4.5. The resin-pulp mixture was then collected on a 100 mesh screen to form a sheet, and was then dried at room temperature to a moisture content of about 8 percent. The dried sheet was then hot pressed for 5 minutes at a pressure of 500 psig, using platens which had been preheated to a temperature of 420.degree.F.
A hard, rigid board was obtained, evidence of excellent bonding of the paper pulp fibers by the phenolic resin.
CONTROL 1
The procedure of Example 1 was repeated using as the sole "gum", gum arabic. The actual materials used and amounts thereof are noted below.
______________________________________ AMOUNT IN GRAMS______________________________________Phenol 1200Formaldehyde (40% aqueous solution) 1668Sodium hydroxide (25% aqueous solution) 48Gum arabic 36Water 480Phosphoric acid (85%) 15.6Water 36______________________________________
The solids content of the resin-in-water dispersion was 44 percent by weight.
______________________________________Gel time = 42 seconds______________________________________
Particles of the resin were undesirably large and non-uniform, stability was poor, and the particles settled out rapidly.
On the basis of 100 parts by weight phenol charged into the reaction flask, the amount of gum arabic used was 3 parts by weight.
CONTROL 2
The procedure of Example 1 was repeated using as the sole gum, guar gum. The actual materials used and amounts thereof are noted below:
AMOUNT IN GRAMS______________________________________Phenol 1200Formaldehyde (40% aqueous solution) 1668Barium hydroxide monohydrate 30Guar gum 12Water 920Sulfuric acid (96.6%) 10Water 40______________________________________
This formulation resulted in a water-in-resin dispersion rather than a resin-in-water dispersion. Consequently, the composition obtained could not be diluted with water and used in spray coating applications.
On the basis of 100 parts by weight phenol charged into the reaction flask, the amount of guar gum used was 1 percent by weight.
CONTROL 3
Example 1 is repeated with the exception that 20 parts by weight gum arabic are used, based on 100 parts of phenol charged.
Diluting the dispersion to 10% by weight, on a solids basis, results in a rapid settling out of the particles.
CONTROL 4
Example 4 is repeated with the exception that no "gums" are used. No dispersion forms.
The term "infinitely dilutable" as used herein means that the aqueous dispersions can be diluted to a solids content of 1 percent by weight with no substantial change in the size and uniformity of the dispersed resin particles therein.

Number	Name	Date
3207652	Shannon	Sep 1965
3594268	Dahms et al.	Jul 1971
3823103	Harding	Jul 1974

	Number	Date	Country
Parent	466790	May 1974
Parent	164819	Jul 1971

Fibrous batts impregnated with aqueous dispersions based on heat-hardenable phenolic resins

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Parent Case Info

US Referenced Citations (3)

Divisions (1)

Continuation in Parts (2)