1. Field of the Invention
The invention relates to a field emission cathode and method for fabricating the same and, particularly, to a carbon nanotube-based field emission cathode and a method for fabricating the same.
2. Description of Related Art
Carbon nanotubes (CNTs) are a novel carbonaceous material discovered by lijima, a researcher of NEC Corporation, in 1991. Typically, carbon nanotubes have tube-shaped structures with small diameters (less than 100 nanometers) and large aspect ratios (length/diameter). They have excellent electrical properties as well as excellent mechanical properties. The electronic conductance of carbon nanotubes is related to their structures. Because the carbon nanotubes can transmit extremely high electrical current and emit electrons easily, at a low voltage of less than 100 volts, they are considered to be promising for use in a variety of display devices, such as field emission display (FED) devices.
Generally, a CNT field emission display device includes a cathode electrode and a carbon nanotube array formed on the cathode electrode. The methods adopted for forming the carbon nanotube array on the cathode electrode mainly include mechanical methods and in-situ synthesis methods. One mechanical method is performed by using an atomic force microscope (AFM) to place the synthesized carbon nanotube array on the cathode electrode and to then fix the carbon nanotube array on the cathode electrode, via a conductive paste or adhesive. The mechanical method is easy and straightforward. However, the precision and efficiency thereof are relatively low. Furthermore, the electrical connection between the cathode electrode and the carbon nanotube array tends to be poor because of the limitations of the conductive adhesives/pastes used therebetween. Thus, the field emission characteristics of the carbon nanotube array are generally unsatisfactory.
One in-situ synthesis method is performed by coating metal catalysts on the cathode electrode and directly synthesizing the carbon nanotube array on the cathode electrode, by means of chemical vapor deposition (CVD). In principle, a carbon source gas is thermally decomposed at a predetermined temperature in the presence of metal catalyst, thereby forming the carbon nanotube array. The in-situ synthesis method is relatively easy. Furthermore, the electrical connection between the cathode electrode and the carbon nanotube array is typically good because of the direct engagement therebetween.
The rear substrate where the carbon nanotube array is formed is usually made of metal materials, thus displaying good conductivity and the ability to carry high current loads. However, the metal materials are generally limited to metals such as aluminum (Al) or nickel (Ni) or alloys thereof. This limitation is necessary to prevent the material of substrate from adversely affecting formation of the carbon nanotube array. Such an adverse effect could be created by a reaction of the substrate material with the metal catalysts or by a decomposition reaction with the carbon source gas to form amorphous carbon. In addition, because the metallic substrate, such as the aluminum substrate, may be weakened due to erosion by, e.g., acid and/or alkali, it is less compatible with the micromaching techniques used in forming the cathode electrode.
What is needed, therefore, is a field emission cathode and a method for fabricating the same that can overcome the above-mentioned problems and still yield a well-aligned carbon nanotube array.
A field emission cathode is provided. In one embodiment, the field emission cathode includes a substrate, a metal electrode, an aluminum transition layer, and a carbon nanotube array. The metal electrode is disposed directly upon the substrate. The aluminum transition layer is disposed upon the metal electrode. The carbon nanotube array is formed upon the aluminum transition layer. In this case, a thickness of the aluminum transition layer is in an approximate range from 5 nm to 40 nm.
A method for fabricating a field emission cathode is also provided. In one embodiment, the method includes the following steps: providing a substrate; forming a metal electrode on the substrate; depositing an aluminum transition layer on the metal electrode; depositing a catalyst layer on the aluminum transition layer; annealing the substrate, on which the metal electrode, the aluminum transition layer and the catalyst layer are disposed in order, the annealing being performed in air so that the catalyst layer reacts to form a plurality of oxidized catalyst particles on the aluminum transition layer; heating the treated substrate in a reactor to a first temperature in the presence of a protective gas; and introducing a mixture of a carbon source gas and a protective gas in the reactor and heating the treated substrate to a second temperature, whereby a carbon nanotube array is formed and extends from the aluminum transition layer via the oxidized catalyst particles.
Other advantages and novel features of the present field emission cathode and the method for fabricating the same will become more apparent from the following detailed description of preferred embodiments when taken in conjunction with the accompanying drawings.
Many aspects of the present field emission cathode and the method for fabricating the same can be better understood with reference to the following drawings. The components in the drawings are not necessarily to scale, the emphasis instead being placed upon clearly illustrating the principles of the present field emission cathode and the method for fabricating the same.
Corresponding reference characters indicate corresponding parts throughout the several views. The exemplifications set out herein illustrate at least one preferred embodiment of the present field emission cathode and the method for fabricating the same, in one form, and such exemplifications are not to be construed as limiting the scope of the invention in any manner.
Reference will now be made to the drawings to describe embodiments of the present field emission cathode and method for fabricating the same, in detail.
Referring to
In the present embodiment, the substrate 222 is composed of, for example, silicon or silicon dioxide (SiO2). Thus, this nonmetallic substrate 222 can act as a supporter to allow the field emission display device using the substrate 222 to have a higher resolution and to be capable of forming an addressing matrix.
The metal electrode 224 has a thickness in an approximate range from 60 nm to 200 nm and is made of gold (Au), silver (Ag), copper (Cu), or molybdenum (Mo), or of alloys incorporating such metals. Usefully, the metal electrode 224 is made of molybdenum, which has the merits, at least, of a high melting point and significant corrosion resistance, in particular, against hydrogen fluoride (HF), so as to have better compatibility with the micromaching techniques often used in forming a triode field emission display device.
The aluminum transition layer 226 has a thickness in an approximate range from 5 nm to 40 nm. More suitably, the thickness of the aluminum transition layer 226 is about 40 nm. The carbon nanotube array 228 includes a plurality of well-aligned carbon nanotubes. The carbon nanotubes have an average diameter in an approximate range from 5 nm to 20 nm and have an average length in an approximate range from 2 nm to 20 nm. By disposing the aluminum transition layer 226 between the metal electrode 224 and the carbon nanotube array 228, the electric resistance therebetween is effectively minimized, and, as such, the field emission display device has a great capacity for the field emission.
Additionally, a method for fabricating the field emission cathode, according to a present embodiment, includes the following steps:
Each step of the present method is described in more detailed below, with reference to
Step 1 provides the substrate 222 advantageously made of silicon, silicon dioxide, or mixture/compound including such materials. That is, the substrate 222 in the present embodiment can be a silicon substrate, a quartz substrate, or a glass substrate.
Step 2 forms the metal electrode 224, having a thickness in an approximate range from 60 nm to 200 nm on the substrate 222. In the present embodiment, the metal electrode 224 can, advantageously, be made of a high-conductivity, corrosion-resistance metal/alloy, such as Au, Ag, Cu, or Mo, or an alloy thereof. The metal electrode 224 is formed on one surface of the substrate 222 by, e.g., photolithography, electron beam lithography in cooperation with reactive ion etching, dry etching, or wet etching. However, the way of forming the metal electrode 224 is not limited to what is mentioned above.
In Step 3, the aluminum transition layer 226 is deposited at a thickness in an approximate range from 5 nm to 40 nm directly on the metal electrode 224. In the present embodiment, the aluminum transition layer 226 is formed, for example, by evaporating or sputtering to have a thickness of about 40 nm.
Step 4 involves depositing the catalyst layer 230, having a thickness in an approximate range from 3 nm to 10 nm, on the aluminum transition layer 226. In the present embodiment, the catalyst layer 230 includes a catalyst material, beneficially selected from the group consisting of iron (Fe), cobalt (Co), nickel (Ni), and an alloy thereof. It is noted that the thickness of catalyst layer 230 is usually chosen corresponding to the type of catalyst selected. For example, when the catalyst layer 230 is made of iron, the thickness of iron catalyst layer 230 is in the approximate range from 3 nm to 10 nm and most suitably is about 5 nm.
At Step 5, the substrate 222, with the metal electrode 224, the aluminum transition layer 226, and the catalyst layer 230 disposed in order thereon, is annealed. In this step, the treated substrate is first placed in the air and then is treated by heating to a temperature substantially in an approximate range from 300° C. to 500° C. for about 10 minutes to 12 hours, with a shorter anneal time usually needed at a higher treatment temperature. As a result, the catalyst layer 230 is oxidized, thereby yielding a plurality of oxidized catalyst particles 230′ directly on the aluminum transition layer 226.
Step 6 provides for the heating of the treated substrate in a manner to form a carbon nanotube array 228. In this step, the treated substrate is placed in a reactor suitable to perform the chemical vapor deposition (CVD). Then, a protective gas is introduced into the reactor. The treated substrate is preheated to the first predetermined temperature, in the presence of the protective gas in order to prevent further oxidizing the oxidized catalyst particles 230′, as such over-oxidation could adversely affect formation of the carbon nanotube array 228. In the present embodiment, the protective gas is, usefully, an inert gas and/or nitrogen gas. Most suitably, the protective gas is argon. The first predetermined temperature is generally in an approximate range from 400° C. to 750° C. and depends on which catalyst is selected. For example, when the catalyst layer 230 is made of iron, the first predetermined temperature is preferably 650° C.
Step 7 involves introducing a mixture gas and heating the treated substrate for growing the carbon nanotube array 228. In the present embodiment, the mixture gas, composed of the carbon source gas and the protective gas, is introduced into the reactor, and the treated substrate is heated to the second predetermined temperature, substantially in an approximate range from 400° C. to 750° C. for about 0.5 minutes to 2 hours. As the result, the oxidized catalyst particles 230′ are reduced into nano-sized catalyst particles by decomposing the carbon source gas. Furthermore, the carbon nanotube array 228 is formed and extends from the aluminum transition layer 226, and then the field emission cathode 22 is formed finally. In the present embodiment, the carbon source gas can, advantageously, be a hydrocarbon, such as acetylene or ethylene. Quite usefully, the carbon source gas is acetylene. As mentioned above, the protective gas in this step can be an inert gas or nitrogen gas. Rather opportunely, the protective gas is argon.
In addition, before the step 7, the method in the present embodiment can further include a step of introducing hydrogen gas (H2) or ammonia gas (NH3) to reduce the oxidized catalyst particles 230′ into nano-sized catalyst particles. However, this step is not necessary, in practice, to achieve forming of the field emission cathode.
Referring to
In the particular present embodiment, resulting the device illustrated in
Referring to
In the present embodiment, the method includes the following steps:
Referring to
Finally, it is to be understood that the above-described embodiments are intended to illustrate rather than limit the invention. Variations may be made to the embodiments without departing from the spirit of the invention as claimed. The above-described embodiments illustrate the scope of the invention but do not restrict the scope of the invention.