Patent Application
20050121066
This invention relates to novel thermoelectric compositions of the formula YbAl3-x Mnx (0<x<1), with a figure of merit greater than 0.2.
Thermoelectric or Peltier refrigerators produce only a moderate amount of cooling but have poor efficiencies when compared to compressor based refrigerators. The thermoelectric energy conversion efficiency is measured in terms of the dimensionless “figure of merit, ZT”. To maximize ZT, materials with large Seebeck coefficient, high electrical conductivity, but with low thermal conductivity are needed. The known intermetallic compound YbAl3 has a relatively high Seebeck coefficient and high electrical conductivity but its thermal conductivity is too high e.g. 12 W/μK. Usually intermetallic materials are poor thermoelectric materials but this compound exhibits unusual transport properties leading to a large Seebeck coefficient. Adding materials with very low thermal conductivity lowers the ZT, if the addition does not degrade the other inter-related parameters.
The present invention is a compound comprising:
The present invention also includes a thermoelectric refrigerator comprising a component made from the compound of this invention.
The present invention is further a thermoelectric generator comprising a component made from the compound of this invention.
Another embodiment of the present invention is a thermoelectric heater comprising a component made from the compound of this invention.
A yet further embodiment of the present invention is a process comprising
This invention provides novel intermetallic thermoelectric compositions of the formula YbAl3-x Mnx (0<x<1). When compared to YbAl3 (x=0), these compounds have a higher electrical resistivity, lower thermal conductivity, but similar Seebeck coefficient values in the temperature range 150° K-300° K. This results in an improvement in the figure of merit from 0.18 (x=0) to 0.60 (x=0.04).
The thermoelectric compositions of this invention, YbAl3-x Mnx (0<x<1), have thermoelectric properties that decreases the thermal conductivity significantly and electrical conductivity without affecting the Seebeck coefficient. This combination results in a significant improvement in ZT.
The compositions of this invention have been synthesized by the following procedure. Stoichiometric amounts of the starting materials were weighed and thoroughly mixed. The starting materials were −40 mesh size ytterbium metal, aluminum metal and manganese metal with 99.99% purity. The mixed powder of starting materials was pressed into a 1″ diameter disks. They were loaded into a carbon core vacuum furnace and pumped down to 1×10−6 torr. The sample was heated to 800° C. at 2°/min for 12 hours and, with power off, furnace cooled to room temperature. The samples were removed and pressed into desired shapes for electrical and thermal measurements and re-fired with the same temperature program in vacuum. All of the YbAl3-x Mnx phases of this invention crystallize in a cubic Pm3m structure.
Seebeck coefficient measurements can be performed by heating one end of the sample and establishing a thermal gradient along the length of the sample. The Seebeck voltage is measured with a Keithley 181 nanovoltmeter manufactured by Keithley Instruments, Inc. of Cleveland, Ohio 44139, at both ends, and is compared to the temperature differential at the point of measurement. The resistivity and thermal conductivity can be determined by using a PPMS system manufactured by Quantum Design of San Diego, Calif. following manufacturer's procedure. Thermoelectric materials such as n-type YbAl3-x Mnx (0<x<1) can be used to manufacture thermoelectric refrigerators, heaters or generators in conjunction with p-type materials such as Bi—Sb alloys or Bi2Te3 based alloys In a thermoelectric refrigerator, the thermoelectric material is typically mounted between two plates of materials such as ceramics. One plate is located at the region to be cooled. The other plate is located where the heat is to be rejected. Current of the appropriate polarity is passed through the thermoelectric material, cooling the desired location. If the polarity of the current is reversed, the previously cooled plate will be heated and the plate rejecting the heat will be cooled. To use thermoelectric devices as generators, the thermoelectric material is again mounted between two plates. One plate is exposed to a high temperature source while the second plate is maintained at a lower temperature. Electrical power can be obtained from electrical connections across the sides of the thermoelectric material in the temperature gradient.
The compositions YbAl3-x Mnx of Examples 1-5 wherein were made using the following procedure. For each Example, appropriate amounts of the starting metals Yb, Al and Mn were weighed according to the stoichiometric ratios and mixed thoroughly in an agate mortar inside a dry box. The gram amounts for a 4 gram sample size of the starting materials used are given in Table 1.
In each Example, the mixed powder was pressed into a disk and fired at 800° C. for 12 hours in a vacuum furnace and cooled in vacuum to room temperature. The calcined powder was reground and pressed to 12.7 mm diameter/1-2 mm thick disks for thermal conductivity, 3 mm×3 mm bars for mounting into the PPMS for resistivity and Seebeck coefficient measurements.
X-ray powder diffraction patterns were recorded and the data showed all samples crystallized in a cubic Pm3m structure. The measured electrical and thermal properties are listed in Table 2.
The disk samples were cut and sanded to produce smooth surface. The measurement lead were attached to the sample using silver epoxy. Thermal conductivity and resistivity measurements done at room temperature in the PPMS. From Table 2, one can see a steady drop in thermal conductivity from 12 to 3 W/mK, a slight increase in resistivity from 100 to 220 μOhm-cm but nearly constant value of the Seebeck coefficient.
The figures of merit (ZT) for the undoped and Mn doped samples are shown in Table 3. The addition of 4% manganese (YbAl2.96 Mn.04) increases the ZT by a factor of three over the undoped sample (YbAl3), from 0.18 to 0.60.