Claims
- 1. A composition consisting essentially of
- (a) from about 5 percent to about 60 percent by weight of a mixture of at least two copolymers of ethylene, copolymer (A) and copolymer (B), each copolymer having at least one polar comonomer selected from the group consisting of vinyl esters of saturated carboxylic acids wherein the acid moiety has up to 4 carbon atoms, unsaturated mono- or dicarboxylic acids of 3 to 5 carbon atoms, the salts of said unsaturated acids, and esters of said unsaturated acids wherein the alcohol moiety has 1 to 8 carbon atoms, copolymer (A) having a polar comonomer content of from about 2 to about 30 percent by weight, an ethylene content of from about 70 to about 98 percent by weight and a melt index of from about 0.1 to about 20, and copolymer (B) having a polar conomoner content of from about 28 to about 70 percent by weight, an ethylene content of from about 30 to about 72 percent by weight and a melt index of from about 5 to about 1000, provided that the polar comonomer content of copolymer (B) is at least 12 percent by weight higher than the polar comonomer content of copolymer (A) and the weight ratio of copolymer (A) to copolymer (B) is from about 99/1 to about 55/45;
- (b) from about 40 percent to about 90 percent by weight of filler;
- (c) from 0 percent to about 15 percent by weight of at least one plasticizer selected from the group consisting of processing oils, polyesters, polyethers and polyether esters provided that, when the filler level is above about 75 percent by weight, there is at least about 1 percent by weight of plasticizer present, provided that when the filler level is at least 70 percent by weight said composition exhibits a tensile elongation at least 50% higher than a blend containing a single copolymer of ethylene having the same polar comonomer content and melt index as the mixture of at least two copolymers of ethylene has;
- (d) from 0 to about 27% by weight of elastomeric polymer; and
- (e) from 0 to about 48% by weight of olefin polymer selected from the group consisting of low density branched polyethylene, high density linear polyethylene, linear copolymers of ethylene and another olefin comonomer, polypropylene and copolymers of propylene and ethylene where the ethylene content is up to 20% by weight.
- 2. The composition of claim 1 wherein said elastomeric polymer and said olefin polymer are present in an amount of 0% by weight.
- 3. The composition of claim 2 wherein (a) said mixture of at least two copolymers of ethylene is present in an amount of from about 8 to about 30 percent by weight, (b) said filler is present in an amount of from about 50 to about 85 percent by weight, and (c) said plasticizer is present in an amount of from about 3 to about 10 percent by weight.
- 4. The composition of claim 3 wherein the ratio of copolymer (A) to copolymer (B) is from about 97/3 to about 60/40.
- 5. The composition of claim 4 wherein said filler is selected from the group consisting of calcium carbonate, barium sulfate, hydrated alumina clay, magnesium carbonate, calcium sulfate, silica flyash, cement dust, wood flour, ground rice hulls and mixtures thereof.
- 6. The composition of claim 5 wherein said filler is selected from the group consisting of calcium carbonate, barium sulfate, hydrated alumina, and mixtures thereof.
- 7. The composition of claim 6 wherein copolymer (A) has a polar comonomer content of from about 5 to about 23 percent by weight, an ethylene content of from about 72 to about 95 percent by weight and a melt index of from about 0.3 to about 10; and wherein copolymer (B) has a polar comonomer content of from about 30 to about 65 percent by weight, an ethylene content of from about 35 to about 70 percent by weight and a melt index of from about 10 to about 200, provided that the polar comonomer content of copolymer (B) is at least 15 percent by weight higher than the polar comonomer content of copolymer (A), and when the filler level is at least 70 percent by weight said composition exhibits a tensile elongation at least 100% higher than a blend containing a single copolymer of ethylene having the same polar comonomer content and melt index as the mixture of at least two copolymers of ethylene has.
- 8. The composition of claim 7 wherein said plasticizer is selected from the group consisting of processing oils.
- 9. The composition of claim 8 wherein said processing oil is selected from the group consisting of naphthenic and aromatic oils.
- 10. The composition of claim 9 wherein said plasticizer is a mixture of (.alpha.) processing oil; and (.beta.) polyester or polyether or polyether ester or any combination thereof; wherein said processing oil is present in an amount of from about 50 to about 95 percent by weight.
- 11. The composition of claim 10 wherein said processing oil is present in an amount of from about 50 to about 80 percent by weight.
- 12. The composition of claim 10 wherein said copolymers of ethylene are selected from the group consisting of ethylene/vinyl acetate, ethylene/acrylic acid and its ionomers, ethylene/methacrylic acid and its ionomers, ethylene/methyl acrylate, ethylene/ethyl acrylate, ethylene/isobutyl acrylate, ethylene/normal butyl acrylate, ethylene/isobutyl acrylate/methacrylic acid and its ionomers, ethylene/normal butyl acrylate/methacrylic acid and its ionomers, ethylene/isobutyl acrylate/acrylic acid and its ionomers, ethylene/normal butyl acrylate/acrylic acid and its ionomers, ethylene/methyl methacrylate, ethylene/vinyl acetate/methacrylic acid and its ionomers, ethylene/vinyl acetate/acrylic acid and its ionomers, ethylene/vinyl acetate/monoethyl maleate and ethylene/methyl acrylate/monoethyl maleate.
- 13. The composition of claim 12 wherein said copolymers of ethylene are selected from the group consisting of ethylene/vinyl acetate, ethylene/ethyl acrylate, ethylene/methyl acrylate, ethylene/isobutyl acrylate, and ethylene/methyl methacrylate.
- 14. The composition of claim 12 wherein (a) said mixture of at least two copolymers of ethylene is present in an amount of from about 11 to about 25 percent by weight, (b) when said filler is calcium carbonate or hydrated alumina the amount of filler is from about 65 to about 80 percent by weight, and when said filler is barium sulfate the amount of filler is from about 70 to about 85 percent by weight, and (c) said plasticizer is present in an amount of from about 4 to about 8 percent by weight.
- 15. The composition of claim 14 wherein copolymer (A) has a polar comonomer content of from about 10 to about 25 percent by weight, an ethylene content of from about 75 to about 90 percent by weight and a melt index of from about 0.5 to about 2 and wherein copolymer (B) has a polar comonomer content of from about 33 to about 60 percent by weight, an ethylene content of from about 40 to about 67 percent by weight and a melt index of from about 15 to about 100, and wherein the ratio of copolymer (A) to copolymer (B) is from about 95/5 to about 65/35, provided that the polar comonomer content of copolymer (B) is at least 18 percent by weight higher than the polar comonomer content of copolymer (A), and when the filler level is at least 70 percent by weight said composition exhibits a tensile elongation at least 150% higher than a blend containing a single copolymer of ethylene having the same polar comonomer content and melt index as the mixture of at least two copolymers of ethylene has.
- 16. The composition of claim 15 wherein the ratio of copolymer (A) to copolymer (B) is from about 85/15 to about 65/35.
- 17. The composition of claim 15 wherein said copolymers of ethylene are ethylene/vinyl acetate copolymers.
- 18. The composition of claim 7 wherein said plasticizer is selected from the group consisting of polyesters.
- 19. The composition of claim 18 wherein said polyester is a liquid condensation product of (.alpha.) a dibasic acid selected from the group consisting of saturated aliphatic dibasic acids and aromatic dibasic acids and (.beta.) a polyol selected from the group consisting of aliphatic polyols and polyoxyalkylenepolyols.
- 20. The composition of claim 19 wherein greater than 50 percent by weight of the acid component of said polyester is selected from dibasic acids and the polyol component is selected from aliphatic glycols.
- 21. The composition of claim 7 wherein said polyether is selected from polyols based on random and block copolymers of ethylene oxides or propylene oxides.
- 22. The composition of claim 7 wherein said polyether ester is selected from esters of polyols based on polymers or copolymers of ethylene oxides or propylene oxides.
- 23. The composition of claims 1, 3, 7, 14, 17, 21 or 22 in the form of a sound-deadening sheet.
- 24. A carpet having a backside coating consisting essentially of the composition of claims 1, 3, 7, 14, 17, 21 or 22.
- 25. An automotive carpet having a backside coating consisting essentially of the composition of claims 1, 5, 7, 14, 17 21 or 22.
- 26. The composition of claims 4, 8, 13, 17, 19, 21 or 22 containing at least one modifier selected from the following groups
- (d) from 0 to about 27% by weight of unvulcanized elastomeric polymer; and
- (e) from 0 to about 48% by weight of olefin polymer selected from the group consisting of low density branched polyethylene, high density linear polyethylene, linear copolymers of ethylene and another olefin comonomer, polypropylene and copolymers of propylene and ethylene where the ethylene content is up to 10% by weight.
- 27. The composition of claims 4, 8, 13, 17, 19, 21 or 22 containing at least one modifier selected from the following groups
- (d) unvulcanized elastomeric polymer selected from the group consisting of styrene-butadiene rubber, polyisobutylene, ethylene/propylene rubber, and terpolymers of ethylene, propylene and a diene monomer; and
- (e) olefin polymer selected from the group consisting of high density linear polyethylene, linear copolymers of ethylene and another olefin comonomer and copolymers of propylene and ethylene where the ethylene content is up to 20% by weight provided that when present at all component (d) is present in an amount of from about 1 to about 17% by weight and component (e) is present in an amount of from about 1 to about 22% by weight.
- 28. The composition of claims 4, 8, 13, 17, 19, 21 or 22, containing at least one modifier selected from the following groups
- (d) unvulcanized elastomeric polymer selected from the group consisting of ethylene/propylene and terpolymers of ethylene, propylene and a diene monomer, wherein the ethylene content is from above 20 to about 80% by weight and the diene content is from 0 to about 5% by weight, said dienes being selected from the group consisting of methylene norbornene, ethylidene norbornene, dicyclopentadiene and 1,4-hexadiene; and
- (e) olefin polymer selected from the group consisting of high density linear polyethylene, linear copolymers of ethylene and another olefin comonomer and copolymers of propylene and ethylene where the ethylene content is up to 20% by weight provided that when present at all component (d) is present in an amount of from about 2% to about 12% by weight and component (e) is present in an amount of from about 2 to about 15% by weight.
Parent Case Info
This application is a continuation-in-part of my copending application Ser. No. 251,989 filed Apr. 6, 1981, now abandon which application is a continuation-in-part of Ser. No. 176,782 filed Aug. 11, 1980, now abandon.
US Referenced Citations (15)
Foreign Referenced Citations (4)
Number |
Date |
Country |
2319431 |
Oct 1973 |
DEX |
940713 |
Oct 1963 |
GBX |
2011803 |
Jul 1979 |
GBX |
2016500 A |
Sep 1979 |
GBX |
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
251989 |
Apr 1981 |
|
Parent |
176782 |
Aug 1980 |
|