Patent Grant
8274014
The invention relates to relates to wire used in brazing and soldering. More particularly, the present invention is directed to a channeled wire having a flux solution deposited therein for use in joining two similar or dissimilar metals in industrial applications.
Brazing and soldering are two methods commonly used to join two similar or dissimilar metals together. These processes typically involve joining metal components together by disposing a brazing composition such as an aluminum or metal alloy adjacent to or between the faying surfaces, i.e., the surfaces to be joined. The brazing filler alloy and the faying surfaces are then heated to the brazing temperature, typically above the melting temperature of the braze alloy but below the melting temperature of the components to be joined. The brazing composition then melts, flows into the joint by capillary action and forms a fillet and seal that bonds the faying surfaces.
In most cases, these processes require a chemical flux in addition to the filler alloy. The flux prepares the base metals to accept the filler alloy which results in a strong bond. Fluxes are generally grouped under two categories: corrosive (must be removed) and non-corrosive (residues are left on the part).
Historically, the alloy and flux are applied as two separate steps. In recent years however, an increasing number of options have been developed that combine the filler alloys and fluxes in one complete form. These developments have taken place with brazing alloys that are aluminum based and silver based.
For instance, Omni Technologies Corporation (Epping, N.H.) developed a flux core wire, which is sold under the trademark SIL-CORE™. In order to accomplish this, Omni takes aluminum in the form of narrow sheet, deposits a quantity of powdered flux down the middle, and then form rolls the narrow sheet around the flux. This material is then put through draw dies to reduce the diameter and compact the flux inside. From this process, Omni offers several wire diameters as well as different flux compositions. In addition, the amount of flux can be changed as needed. This material is available on spools, large coils and custom fabricated shapes. The inventors of the present invention believe Omni uses a flux sold by Solvay Chemical Company under the name NOCOLOK®. NOCOLOK® brand is one of the most widely recognized non-corrosive aluminum fluxes. This product is described in U.S. Pat. No. 5,781,846, which is hereby incorporated by reference as if fully set forth herein. Omni claims the SIL-CORE™ product does not contain a binding agent.
The S.A. Day Corporation (Buffalo, N.Y.) produces an aluminum flux coated rod sold under name DAYROD. This rod includes an aluminum wire cut to 12 inch rods, and dipped in an aluminum flux bath. After dipping, the rods are hung to dry. Day does not use NOCOLOK® brand flux. Instead, Day uses a similar formulation which is mixed with a polymer-based binder system. This binder allows for the flux to remain ductile and not brittle. The flux coated rods can be bent or twisted and the flux will not fall off.
Day also produces a flux coated ring. Day purchases metallic rings from Bellman-Melcor, Inc. The rings are then loaded on a machine that “paints” a thin coating of flux on the outside edge of each ring. While the end product is acceptable, it is very slow to produce and consequently very expensive. Similar to the rods, the rings can be handled roughly and the flux remains intact.
Protechno-Richard (France) offers a product very similar to the Omni product.
Kin-Met (Korea) produces an extruded product. A powdered form of aluminum braze alloy is mixed with powdered flux. The combination is pressurized and extruded into final form.
Wolverine and Omni teamed up to create a flux coating for silver based materials. Made from a ductile binder system, this technology is sold under the name SILVACOTE™. SILVACOTE™ is a continuously coated, flux-coated brazing material.
The present invention is provided to solve the problems discussed above and other problems, and to provide advantages and aspects not provided by prior brazing wires of this type. A full discussion of the features and advantages of the present invention is deferred to the detailed description, which proceeds with reference to the accompanying drawings.
The present invention is directed to a wire for use in a brazing or soldering operation. The wire comprises an elongated body, a channel, and a flux solution. The elongated body is produced from a metallic material. The body has an outer surface. The channel is formed along at least a portion of the body. The channel has an opening. The flux solution is deposited within the channel and along the length of the body with a surface of the flux solution being exposed through the opening in the channel.
The metallic material may be an aluminum alloy, a silver alloy, a copper alloy, and/or a zinc alloy.
The elongated body may have a substantially elliptical cross-sectional shape, a substantially rectangular shape cross-sectional shape, and or a substantially kidney-shaped cross-sectional shape.
The channel may have a substantially rectangular shape.
The flux solution may be a non-corrosive or corrosive flux solution.
The flux solution may include a polymer-base binder.
The opening may be about 0.030 inches.
The opening may be about 30% to 70% of a major axis of the wire.
The channel may be about 0.020 inches deep.
The channel may have a depth of about 10% to 50% of a major axis of the wire.
The elongated body may be formed into an annular ring having an inner wall and an opposing outer wall. The channel may form a portion of the inner wall. The flux solution within the channel may form a portion of the inner wall, and a top surface of the flux solution within the channel may be located below a straight line or imaginary plane spanning across the opening of the channel. The straight line may be located entirely along the inner wall of the ring.
The present invention is also directed to a wire for use in a brazing or soldering operation. The wire comprises an elongated body, a channel, and a flux solution. The elongated body is of a metallic material. The body has a length substantially greater than a width. The elongated body also has an outer surface. The channel is formed along a portion of the length of the body and has an opening. The flux solution is deposited within the channel and along the portion of the length of the body. The flux solution covers a portion of the outer surface. A portion of the flux solution is exposed through the opening in the channel.
The invention is further directed to a method of preparing a wire for use in a brazing or soldering operation. The method comprises the steps of providing an elongated wire, forming a channel along at least a portion of the length of the elongated wire, and depositing a flux solution into the channel. The elongated wire has a length substantially greater than a cross-sectional width and an outer exposed surface. The channel has an opening. The flux solution is deposited into the channel such that a portion of the flux solution is exposed in the opening.
The channel may span substantially the entire length of the elongated wire.
The opening may span substantially the length of the elongated wire.
The flux solution may comprise a metallic component and a polymeric-based component.
The polymeric-based component may be an acrylic polymer.
The metallic material may be an aluminum-based powder.
The invention is also directed to a further method of preparing a wire for use in a brazing or soldering operation. This method comprises the steps of: providing an elongated wire having a length substantially greater than a cross-sectional width and an outer exposed surface; forming a channel along at least a portion of the length of the elongated wire, the channel having an opening; depositing a flux solution through the opening into the channel wherein a portion of the outer surface of the elongated wire is covered by the flux solution and a portion of the flux solution is exposed in the opening; and curing the flux solution within the channel.
The method may comprise the further steps of: cutting the elongated wire to a predetermined length after the curing step; and forming an annular ring of the elongated wire. The forming the annular ring step may comprise the sub-step of creating an inner wall and an opposing outer wall, the inner wall including the channel containing the flux solution.
The depositing the flux solution step may also comprise the following sub-steps: providing a chamber including a volume of the flux solution; passing the elongated wire through an inlet in the chamber; removing the elongated wire from the chamber through an outlet in the chamber; and passing the wire through a die located adjacent the outlet; the die having a passageway therethrough wherein the shape of the passageway regulates the amount and location of the flux solution left on the elongated wire.
The curing step may include the step of: providing a source of power; and electrically connecting the elongated wire to the source of power.
Another aspect of the present invention is directed to a wire for use in a brazing or soldering operation. The wire comprises an elongated body of a metallic material, a channel formed along a length of the elongated body, the channel having an opening, and a flux solution within the channel, the flux solution comprising a flux material and binder material.
The binder material may be a polymer-base material. The polymer-base material may comprise a polymer selected from a group consisting of an acrylic polymer and a polymer produced from copolymerization of carbon dioxide. The polymer may be a poly alkylene carbonate.
The flux material may be aluminum-based or cesium-based.
The metallic material of the elongated body may be an aluminum alloy, or the metallic material may be a zinc/aluminum alloy comprising at least having at least 2 percent by weight aluminum.
Another aspect of the invention is directed to a wire for use in a brazing or soldering operation. The wire comprises an elongated body, a first channel, a second channel, a first volume of a first flux solution, and a second volume of a second flux solution. The elongated body is produced from a metallic material. The first channel has a first opening formed along a length of the elongated body. The second channel has a second opening formed along a length of the elongated body. The first volume of a first flux solution is located within the first channel and along at least a portion of the length of the elongated body. The second volume of a second flux solution is located within the second channel and along at least a portion of the length of the elongated body.
This aspect of the invention may include several other design chracteristics, alone or in any combination. For instance, the first volume of the first flux solution and the second volume of the second flux solution of the wire of this aspect of the invention may not be equal. Also, the top surface of the first volume of the first flux solution may be located below an imaginary plane spanning across uppermost points forming the first opening in the first channel. Each channel may comprise a pair of sidewalls separated by a base, each sidewall extending radially outwardly from the base and forming an angle with the base greater than 90 degrees. The first flux solution and the second flux solution may have different chemistries. The openings in the first and second channels may be parallel or transverse to a central axis of the wire. The wire may form a ring and the first channel is located along a radially inner wall and the second channel is located along a radially outer wall. The first and second flux solutions may comprise a flux material and binder material. The metallic material of the elongated body may be an aluminum alloy. A surface of the first flux solution may be exposed through the opening in the first channel. A surface of the second flux solution may be exposed through the opening in the second channel. The opening in the first channel may be 30% to 70% of the length of a major axis of the wire. The second channel may be 30% to 70% of the length of a major axis of the wire. The first and second channels may be transverse to a central axis of the wire.
Other features and advantages of the invention will be apparent from the following specification taken in conjunction with the following drawings.
To understand the present invention, it will now be described by way of example, with reference to the accompanying drawings in which:
While this invention is susceptible of embodiments in many different forms, there is shown in the drawings and will herein be described in detail preferred embodiments of the invention with the understanding that the present disclosure is to be considered as an exemplification of the principles of the invention and is not intended to limit the broad aspect of the invention to the embodiments illustrated.
The present invention is directed to a brazing/soldering wire for use in multiple metal combinations including aluminum applications. The end use for these materials is typically industrial applications, such as automobiles and automobile component manufacturing as well as other heat transfer applications including air conditioning and refrigeration manufacture. Of course, other applications can be had as well. The brazing/soldering wire of the present invention may be used on many different materials including aluminum alloys, zinc alloys, copper alloys and silver alloys, etc. The wire itself can be produced from an aluminum alloy, a silver alloy, a copper alloy, and/or a zinc alloy.
The Wire
The present invention includes a solid wire 10 rather than a narrow sheet or strip that is preferably very robust and will not move when assembled onto component parts. This is important because in air conditioning applications, braze wire is commonly supplied in ring-form. The rings are friction fit or snuggly placed around tubes. Because current ring shaped braze wires often lose their grip on component parts, causing the rings to shift or fall off altogether, rings formed from the wire 10 of the present invention are specifically constructed so as to be less likely to plastically deform by the friction fit about the component parts. As a result, they are less likely to shift or fall off prior to the brazing or soldering process. This important aspect of the present invention is described in more detail below.
Referring to
The channel 14 typically has a substantially rectangular or conic section shape having an opening A1 parallel to a central axis 19 of the wire 10 of about 0.030 inches (0.76 mm) and a depth B1 of about 0.020 inches (0.51 mm). Preferably, the opening A1 is about 30% to 70% of the starting diameter of the wire or a major axis of the reformed wire, and the channel 14 has a depth B1, about 10% to 50% of the starting diameter of the wire or a major axis of the reformed wire. Again, it would be appreciated by one of ordinary skill in the art that dimensions of the channel 14 may vary greatly based on customer requirements.
The channel 14 is at least partially filled with a volume of flux solution 22. The volume of flux solution 22 per length of the wire 10 is determined by the end use for the wire. However, it is preferable for the entire volume of flux solution 22 to be positioned within the channel 14 and for the flux solution to be exposed through the opening in the channel 14. Thus, the remaining portions of the outer surface 18 of the wire are free of flux solution 22. A top surface of the flux solution 22 is preferably located below an imaginary line or plane 24 spanning the uppermost surface of the opening A1 of the channel 14. (See
The flux solution 22 preferably comprises a polymer-based binder combined with a flux material. Because the flux solution 22 includes a polymer-based binder, the wire 10 may be manipulated into virtually any shape without disturbing the flux solution 22. Thus, the wire 10 of the present invention may be provided on spools, coils, straight rods and most importantly made to order custom performs, such as rings and the like. The wire 10 may further be supplied in unlimited wire sizes with different flux formulations as well as different alloy/flux ratios.
Referring to
Further to the structure of the inner wall of the ring 30, the imaginary straight line or plane 24, of which the top surface of the flux solution 22 is preferably below, is located entirely along the inner wall 32 of the ring 30. Thus, the opening A1 of the channel 14 is also located entirely along the inner wall 32 of the ring 30. In other words, the flux solution 22 forms a portion of the inner wall 32. More particularly, the top surface of the flux solution 22 forms at least a portion of the inner wall 32.
Referring to
Now referring specifically to
Each channel 14a,14b forms a separate discontinuity 20a, 20b in the outer surface 18 and has a base 40 joining a pair of opposing sidewalls 44a,44b. The discontinuities 20a,20b alter the outer surface 18 and, thus the shape of the wire 10. It would be appreciated by one of ordinary skill in the art that dimensions of the wire 10 may vary greatly based on customer requirements. Furthermore, the channels 14a,14b may have disparate volumes or may have equal volumes depending on end use requirements, and/or the volume of flux required. In other words, the ratio of the flux to the wire volume may be varied from channel to channel. Moreover, the chemistry of the flux in one channel may be varied comparatively to the chemistry of the flux in a second channel.
The base 40 is generally planar as illustrated but may be curved or bowed, either convexly or concavely or some combination thereof. The sidewalls 44a,44b angle radially outwardly from the base 40 such that the sidewalls 44a,44b form angles αa,αb,αc,αd with the base 40. The angles αa,αb,αc,αd may be less than, equal to, or greater than 90 degrees. Preferably, the angles αa,αb,αc,αd are greater than 90 degrees; more preferably, the angles αa,αb,αc,αd are between 90 and 150 degrees; and most preferably, the angles αa,αb,αc,αd are between 90 and 120 degrees; the angles αa,αb,αc,αd may be any range or combination of ranges therein, collectively (all equal) or individually (disparate values or some combination of equal and unequal values).
The channels 14a14b are at least partially filled with separate volumes of flux solution 22a,22b. The volume of flux solution 22a,22b per length of the wire 10 is determined by the end use for the wire 10. However, it is preferable for the entire volume of flux solution 22a,22b to be positioned within the channels 14a,14b and for the flux solution to be exposed through the opening in the channel 14. Thus, the remaining portions of the outer surface 18 of the wire 10 are free of flux solution 22. A top surface of the flux solution 22a,22b may be located above, below, or co-planar with the an imaginary line or plane spanning the uppermost surface of the opening A1,A2 of each channel 14a,14b. Of course, the separate top surfaces of the flux solution 22a,22b in the first and second channels 14a,14b respectively, may have different heights as shown in
There are several advantages of the wires of the present invention. For example, the raw material is cheaper and the process speed is significantly faster than any other product combining wire and flux. As compared to the Omni product, the wires 10 of the present invention include a flux solution which is exposed along a length of the wire 10. The flux solution 22 is not encased. As a result, this allows the flux within the flux solution 22 to melt and release from the wire prior to the alloy of the wire melting.
The Flux Solution
The flux solution 22 is preferably prepared in the following manner. A granulated or beaded polymer is first dissolved in a solvent to form a liquefied suspension. The polymeric material may be derived from an acrylic polymer, such as a proprietary acrylic polymer manufactured by S.A. Day Mfg. Co. The polymeric material, however, is preferably derived from a carbon dioxide rather than a petroleum; it is enzyme degradable; and it is biocompatible where thermal decomposition yields a carbonate which vaporizes for complete removal, leaving minimal ash residue. The products of combustion are non-toxic (primarily carbon dioxide and water). Accordingly, the polymer is generally a thermoplastic, preferably a copolymer, more preferably a poly alkylene carbonate produced through the copolymerization of CO2 with one or more epoxides.
Once the polymer is dissolved in the solvent, a flux is then added in powder form. Any suitable flux, corrosive and non-corrosive, can be used depending on the desired end use. The resulting solution is a thick, homogeneous mixture having a paste-like consistency similar to caulk.
The Method of Manufacture
As illustrated in
As the wire 10 exits the rolling operation, the flux solution 22 (or flux solutions 22a,22b) is added to the channel 14. This is accomplished by inserting the flux solution 22 within a dispensing cartridge 108. An external source of pressure, shown schematically at reference number 112, forces the solution 22 from the cartridge 108 to a holding chamber or die chamber 116 wherein a bath of the solution 22 is generated within the chamber 116. The amount of flux solution 22 forced from the cartridge 108 to the chamber 116 is controlled by a metering device.
The reformed wire 10 enters the chamber 116 through an opening at one end of the chamber 116 so that the solution 22 coats the entire surface of the wire 10. The solution 22 also enters the channel 14 through the opening A1 and fills, or partially fills, the channel 14 on the wire's outer surface 18. The coated wire 10 then exits the chamber 116 through a rubber wiper or die 120 which includes a shaped opening or passageway 124. Excess solution 22 is wiped or cleaned as the wire 10 exits the chamber, leaving only the desired amount of flux solution 22 on the wire 10, preferably only within the channel 14. In other words, the die controls the amount of solution left within the channel 14, distributes the solution 22 evenly within the channel, and ensures no excess solution 22 remains on the wire 10.
Once the channel 14 is filled with the desired volume of solution 22, the solution is dried or cured to form a solid within the channel 14. Any number of methods may be used, including ultra-violet, infra-red, heated fluid pressure, etc. In this embodiment, electrodes 128a,128b are electrically connected to the coated wire 10 wherein an electric current from a source of power 132 heats the wire 10 to the desired temperature, generally between 100° F. to 250° F. (38° C. to 121° C.), preferably between 125° F. to 175° F. (52° C. to 79° C.), most preferably 150° F. (66° C.), or any range or combination of ranges therein.
Once the solution is sufficiently dried, the wire 10 is spooled for delivery or further process.
Method of Use
An example of the present invention is illustrated in
In a second example, the ring 30 described in conjunction with the previous example is an aluminum soft temper alloy such 4047 aluminum. The first and second tubular parts 200,204 are produced from aluminum or an aluminum alloy. The flux solution 22 is produced by dissolving QPAC® polymer beads manufactured by Empower Materials Inc. in a methyl ethyl ketone (MEK) solvent. The flux is a non-corrosive aluminum flux such as the aluminum potassium fluoride NOCOLOK® having a melting temperature of about 1049° F. to 1062° F. (565° C. to 572° C.) or flux B sold by S.A. Day Mfg. Co. containing potassium tetrafluoroaluminate and cesium tetrafluoroaluminate having a melting temperature of about 1055° F. (560° C.).
The MEK solvent is particularly useful. MEK solvent is highly evaporative so a low heat will cure the solution 22. Thus, the flux of this example can be liquefied and released from the flux solution 22 within the desired range of between 100° F. (38° C.) and 250° F. (121° C.), most preferably about 150° F. (66° C.), or any range or combination of ranges therein. These ranges will sufficiently evaporate the solvent without causing the remaining flux/polymer mix 22 to become brittle.
In a third example, the tubular parts 200,204 are of aluminum or an aluminum alloy having a melting temperature of about 1150° F. to 1200° F. (620° C. to 650° C.). The wire is produced from a zinc/aluminum alloy having a melting temperature of about 850° F. to 950° F. (454° C. to 510° C.), such as an alloy comprising at least about 2% aluminum, preferably about 65% to 85% zinc and 15% to 35% aluminum, and most preferably 78% zinc and 22% aluminum and having a melting temperature of about 900° F. (482° C.), or any range or combination of ranges therein. The channel 14 is filled with a polymer/flux blend 22 which activates at about 788° F. to 900° F. (420° C. to 482° C.), preferably a polymer as described above with a cesium-based flux in the amount of about 56% to 66% cesium, 27% to 32.2% fluorine, and 8.6% to 11.4% aluminum or about 6.4% silicon, or any range or combination of ranges therein. Most preferably, the flux solution 22 includes a cesium-based flux which has an activation temperature of about 865° F. (463° C.), such as those produced by Chemetall GmbH of Frankfurt, Germany.
While the specific embodiments have been illustrated and described, numerous modifications are possible without significantly departing from the spirit of the invention, and the scope of protection is only limited by the scope of the accompanying Claims.
This Application is a continuation-in-part of application Ser. No. 11/753,045, filed on May 24, 2007 which claimed the benefit of Provisional Patent Application Ser. No. 60/808,416 filed on May 25, 2006.
| Number | Name | Date | Kind |
|---|---|---|---|
| 400869 | Norton et al. | Apr 1889 | A |
| 607504 | Crowther | Jul 1898 | A |
| 1629748 | Stoody | May 1927 | A |
| 1968618 | Padgett et al. | Feb 1932 | A |
| 2005189 | Herr | Jun 1935 | A |
| 2055276 | Brownsdon et al. | Sep 1936 | A |
| 2499641 | Goody | Mar 1950 | A |
| 2565477 | Crowell et al. | Aug 1951 | A |
| 2927043 | Stetson | Mar 1960 | A |
| 2958941 | Goerg | Nov 1960 | A |
| 3033713 | Bielenberg et al. | May 1962 | A |
| 3077131 | McShane | Feb 1963 | A |
| 3162551 | Short | Dec 1964 | A |
| 3198560 | Collins | Aug 1965 | A |
| 3239125 | Sherlock | Mar 1966 | A |
| 3290772 | Crouch | Dec 1966 | A |
| 3542998 | Huff | Nov 1970 | A |
| 3610663 | Lago | Oct 1971 | A |
| 3619429 | Torigai et al. | Nov 1971 | A |
| 3620830 | Kramer | Nov 1971 | A |
| 3620869 | Stump et al. | Nov 1971 | A |
| 3639721 | Hubbel | Feb 1972 | A |
| 3642998 | Jennings | Feb 1972 | A |
| 3695795 | Jossick | Oct 1972 | A |
| 3703254 | Maierson et al. | Nov 1972 | A |
| 3745644 | Moyer et al. | Jul 1973 | A |
| 3935414 | Ballass et al. | Jan 1976 | A |
| 3967036 | Sadowski | Jun 1976 | A |
| 3980859 | Leonard | Sep 1976 | A |
| 4041274 | Sadowski | Aug 1977 | A |
| 4121750 | Schoer et al. | Oct 1978 | A |
| 4301211 | Sloboda | Nov 1981 | A |
| 4379811 | Puschner et al. | Apr 1983 | A |
| 4396822 | Kishida et al. | Aug 1983 | A |
| 4447472 | Minnick et al. | May 1984 | A |
| 4493738 | Collier et al. | Jan 1985 | A |
| 4497849 | Hughes et al. | Feb 1985 | A |
| 4571352 | Aoki | Feb 1986 | A |
| 4587097 | Rabinkin et al. | May 1986 | A |
| 4624860 | Alber et al. | Nov 1986 | A |
| 4762674 | Cheng et al. | Aug 1988 | A |
| 4785029 | Honma et al. | Nov 1988 | A |
| 4785092 | Nanba et al. | Nov 1988 | A |
| 4800131 | Marshall et al. | Jan 1989 | A |
| 4831701 | Yutaka | May 1989 | A |
| 4901909 | George | Feb 1990 | A |
| 5098010 | Carmichael et al. | Mar 1992 | A |
| 5175411 | Barber | Dec 1992 | A |
| 5184767 | Estes | Feb 1993 | A |
| 5280971 | Tokutake et al. | Jan 1994 | A |
| 5316206 | Syslak et al. | May 1994 | A |
| 5360158 | Conn et al. | Nov 1994 | A |
| 5418072 | Baldantoni et al. | May 1995 | A |
| 5575933 | Ni | Nov 1996 | A |
| 5749971 | Ni | May 1998 | A |
| 5759707 | Belt et al. | Jun 1998 | A |
| 5781846 | Jossick | Jul 1998 | A |
| 5791005 | Grabowski et al. | Aug 1998 | A |
| 5806752 | Van Evans et al. | Sep 1998 | A |
| 5820939 | Popoola et al. | Oct 1998 | A |
| 5903814 | Miura et al. | May 1999 | A |
| 6093761 | Schofalvi | Jul 2000 | A |
| 6204316 | Schofalvi | Mar 2001 | B1 |
| 6244397 | Kars | Jun 2001 | B1 |
| 6248860 | Sant'Angelo et al. | Jun 2001 | B1 |
| 6264062 | Lack et al. | Jul 2001 | B1 |
| 6277210 | Schuster | Aug 2001 | B1 |
| 6317913 | Kilmer et al. | Nov 2001 | B1 |
| 6344237 | Kilmer et al. | Feb 2002 | B1 |
| 6376585 | Schofalvi et al. | Apr 2002 | B1 |
| 6395223 | Schuster et al. | May 2002 | B1 |
| 6409074 | Katoh et al. | Jun 2002 | B1 |
| 6417489 | Blankenship et al. | Jul 2002 | B1 |
| 6426483 | Blankenship et al. | Jul 2002 | B1 |
| 6432221 | Seseke-Koyro et al. | Aug 2002 | B1 |
| 6497770 | Watsuji et al. | Dec 2002 | B2 |
| 6608286 | Jiang | Aug 2003 | B2 |
| 6680359 | Schoenheider | Jan 2004 | B2 |
| 6713593 | Ree et al. | Mar 2004 | B2 |
| 6733598 | Swidersky et al. | May 2004 | B2 |
| 6830632 | Fuerstenau et al. | Dec 2004 | B1 |
| 6846862 | Schofalvi et al. | Jan 2005 | B2 |
| 6864346 | Schoenheider | Mar 2005 | B2 |
| 6881278 | Amita et al. | Apr 2005 | B2 |
| 6960260 | Goto | Nov 2005 | B2 |
| 7267187 | Kembaiyan | Sep 2007 | B2 |
| 7337941 | Scott et al. | Mar 2008 | B2 |
| 7442877 | Kamata et al. | Oct 2008 | B2 |
| 20020020468 | Schuster et al. | Feb 2002 | A1 |
| 20030203137 | Teshima et al. | Oct 2003 | A1 |
| 20040171721 | Esemplare | Sep 2004 | A1 |
| 20050089440 | Kembaiyan | Apr 2005 | A1 |
| 20070093574 | Esemplare | Apr 2007 | A1 |
| 20070251602 | Gagnon, Jr. et al. | Nov 2007 | A1 |
| 20090101238 | Jossick et al. | Apr 2009 | A1 |
| Number | Date | Country |
|---|---|---|
| 1303605 | Jun 1992 | CA |
| 7612546 | Nov 1977 | FR |
| 1180735 | Feb 1970 | GB |
| 1481140 | Jul 1977 | GB |
| 63040697 | Feb 1988 | JP |
| 63303694 | Dec 1988 | JP |
| 01066093 | Mar 1989 | JP |
| 9900444 | Jan 1999 | WO |
| 0039172 | Jul 2000 | WO |
| 0052228 | Sep 2000 | WO |
| 0064626 | Nov 2000 | WO |
| 0200569 | Jan 2002 | WO |
| 0231023 | Apr 2002 | WO |
| 03068447 | Aug 2003 | WO |
| 03089176 | Oct 2003 | WO |
| 2004061871 | Jul 2004 | WO |
| 2004094328 | Nov 2004 | WO |
| WO-2007058969 | May 2007 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20090014093 A1 | Jan 2009 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60808416 | May 2006 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11753045 | May 2007 | US |
| Child | 12176126 | US |