Patent Grant
6933809
1. Field of the Invention
The present invention relates to a FBAR (Film Bulk Acoustic Resonator), and more particularly to a FBAR device comprising a lower electrode film with crystalline characteristics required to form an excellent piezoelectric film and improved electrode film characteristics, and a method for producing the same.
2. Description of the Related Art
In order to meet the rapid development of communication techniques, there has been required the development of signal processing and RF (Radio Frequency) component manufacturing techniques. Particularly, the RF component manufacturing techniques have been developed such that filter components are replaced with FBAR filters so as to meet miniaturization trends of mobile communication units and radio sets.
A FBAR device has a fundamental structure in which an electrode is formed on upper and lower surfaces of a piezoelectric layer on an air gap. When voltage is applied to the upper and lower electrodes, a part of electric energy is converted to mechanical energy such as an acoustic wave by resonance characteristics of the piezoelectric layer. Thereby, the FBAR device is operated as a filter.
Generally, a FBAR device is formed on a substrate. The substrate includes various isolation structures for protecting the substrate from acoustic waves generated from a piezoelectric layer of the FBAR device. For example, the substrate of the FBAR device may have a certain space formed at an area corresponding to a resonance generating position shown in
As shown in
Generally, the piezoelectric layer 24 is made of aluminum nitride, i.e., AlN, and the lower and upper electrode films 22 and 26 are made of molybdenum (Mo). Characteristics of the FBAR device are determined by the piezoelectric layer 24 and the lower and upper electrode films 22 and 26, and particularly resonance characteristics of the piezoelectric layer 24 is a leading factor for determining a Q value of the FBAR device.
In order to obtain excellent resonance characteristics of the FBAR device, the AlN layer of the piezoelectric layer 24 is grown so that it has a preference for (002) orientation. The crystalline characteristics of the piezoelectric layer 24 are much dependent on the crystalline characteristics of a lower electrode. That is, the resonance characteristics of the FBAR device depend on the crystalline structure of the Mo lower electrode film 26. Accordingly, in order to obtain a preference for (002) orientation of the AlN layer, the lower electrode film 22 requires a preference for (110) orientation during its growth.
Conventionally, in order to obtain the above crystalline characteristics of the Mo lower electrode film, a method for improving the conditions in a depositing step of the lower electrode film has been used. For example, the crystalline characteristics of the Mo lower electrode film are changed by raising the sputtering power or the temperature of the substrate in the depositing step or lowering the partial pressure of argon (Ar) in a Mo sputtering step for forming the lower electrode film. However, it is difficult to obtain sufficient crystalline characteristics of the Mo lower electrode film only by changing the conditions of the sputtering step, and the control of the change of the conditions complicates the process.
Further, the change of the conditions undesirably influences the Mo electric film, in the process for improving the crystalline characteristics of the Mo electrode film. For example, the raising of the sputtering power improves the crystalline characteristics of the Mo electrode film, but causes exfoliation of the Mo electrode film from the substrate due to stress generated in the sputtering step.
Moreover, the lower electrode film grown on the substrate in the conventional FBAR device cannot have excellent electrode characteristics.
a and 2b are photographs, each illustrating the surface state and the sectional structure of the Mo lower electrode film of the conventional FBAR device, taken by means of a SEM (Scanning Electron Microscope).
With reference to
Accordingly, there has been required a technique for forming a Mo lower electrode with excellent crystalline characteristics so that the resonance characteristics of the piezoelectric layer and the electrode film characteristics of the Mo lower electrode film are improved regardless of the Mo depositing conditions by sputtering.
Therefore, the present invention has been made in view of the above problems, and it is an object of the present invention to provide a FBAR device comprising a seed layer made of Au or Ti between a substrate structure and a lower electrode film so as to improve the crystalline characteristics and the electrode characteristics of the lower electrode film.
It is another object of the present invention to provide a method for producing a FBAR device, in which a seed layer made of Au or Ti is formed on a substrate structure before a lower electrode film is formed thereon so as to improve the crystalline characteristics and the electrode characteristics of the lower electrode film.
In accordance with one aspect of the present invention, the above and other objects can be accomplished by the provision of a FBAR device comprising: a substrate structure provided with an upper surface; a seed layer formed on the upper surface of the substrate structure and made of one selected from gold (Au) and titanium (Ti); and one or more acoustic resonant portions, each including a lower electrode film formed on the seed layer and made of molybdenum (Mo), a piezoelectric layer formed on the lower electrode film and made of aluminum nitride (AlN), and an upper electrode film formed on the piezoelectric layer.
Preferably, the FBAR device may further comprise a layer made of tantalum (Ta) and formed between the seed layer and the substrate structure, in case that the seed layer is made of Au. Further, the upper electrode film may be made of Mo.
The present invention may be applied to various structures of the FBAR device.
In a further embodiment, the substrate structure may be a substrate provided with air gaps formed on its upper surface. Here, the acoustic resonant portions are plural in number and the air gaps are formed on the substrate at positions corresponding to each of the acoustic resonant portions.
In another embodiment, the substrate structure may include a substrate provided with a flat upper surface, and a membrane layer provided with an air gap formed on the upper surface of the substrate.
In another embodiment, the substrate structure may include a substrate provided with a flat upper surface, a membrane support layer formed on the upper surface of the substrate so that an air gap is surrounded by the membrane support layer, and a membrane layer formed on the upper surface of the membrane support layer so that the air gap is covered by the membrane layer.
Preferably, the membrane layer may be made of a silicon nitride or a silicon oxide. Here, the seed layer made of Au or Ti is formed on the membrane layer.
In accordance with another aspect of the present invention, there is provided a method for producing a FBAR device comprising the steps of: (a) preparing a substrate structure provided with an upper surface; (b) forming a seed layer made of one selected from gold (Au) and titanium (Ti) on the upper surface of the substrate structure; and (c) forming one or more acoustic resonant portions by sequentially stacking a lower electrode film formed on the seed layer and made of molybdenum (Mo), a piezoelectric layer formed on the lower electrode film and made of aluminum nitride (AlN), and an upper electrode film formed on the piezoelectric layer.
The above and other objects, features and other advantages of the present invention will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawings, in which:
a and 2b are photographs, each illustrating the surface state and the sectional structure of a Mo lower electrode film of the conventional FBAR device, taken by means of a SEM (Scanning Electron Microscope);
a to 5c are cross-sectional views of FBAR devices in accordance with other embodiments of the present invention;
a to 8d are photographs, each illustrating the surface state and the sectional structure of a Mo lower electrode film of the FBAR device of the present invention, taken by means of a SEM.
Now, preferred embodiments of the present invention will be described in detail with reference to the annexed drawings.
With reference to
The present invention provides a method for improving the crystalline characteristics of the lower electrode film 42 made of Mo. Before the Mo lower electrode film 42 is deposited, a seed layer 39 made of Au or Ti is formed on the silicon substrate 31, thus allowing the Mo lower electrode film 42 grown in the seed layer 39 to have a preference for (110) orientation. When the lower electrode film 42 has the preference for (110) orientation, the piezoelectric layer 44 formed on the lower electrode film 42 can have a preference for (002) orientation. Accordingly, it is possible to improve the piezoelectric characteristics of the piezoelectric layer 44 and further to improve the resonance characteristics of the FBAR device. The lower electrode film 42 formed on the seed layer 39 is higher in density and smoother at its surface than the conventional lower electrode film, thus having improved electrical and mechanical electrode film characteristics. The thickness of the seed layer 39 employed by the present invention may be formed in the range several tens of Řseveral thousands of Å.
In case that the seed layer 39 is made of Au, in order to prevent the seed layer 39 from being diffused into the silicon substrate 31, it is preferable to form a tantalum (Ta) layer (not shown) on the silicon substrate 31 before the seed layer 39 is deposited thereon.
In a method for producing the FBAR device shown in
After the seed layer 39 made of Au or Ti is formed on the upper surface of the substrate 31, the Mo lower electrode film 42, the AlN piezoelectric layer 44 and the upper electrode film 46 are sequentially deposited to form the acoustic resonant portion 40. Finally, via holes are formed through the substrate 31 so that the sacrificial layer is removed by wet-etching using the via holes so as to form the air gap 35. Thereby, the FBAR device in accordance with this embodiment of the present invention is produced.
In the present invention, the lower electrode film 42 with the preference for (110) orientation is grown by forming the seed layer 39 made of Au or Ti before the deposition of the lower electrode film 42 made of Mo. As a result, the FBAR device of the present invention improves the piezoelectric characteristics of the piezoelectric layer 44 formed on the lower electrode film 42 as well as the electrode film characteristics of the lower electrode film 42.
In order to obtain the improved crystalline characteristics, five Mo lower electrode films with different structures are formed under the same depositing conditions using an Emerald sputter, in which sputtering power is 3 kw, the partial pressure of used argon is 2×10−2 torr, and the temperature of the substrate is 250° C. That is, in the first comparative example (a), the Mo lower electrode film is deposited directly on the silicon substrate in accordance with the conventional manner. In the second and third comparative examples (b and c), the seed layers individually made of Ta and Cr, which are conventional materials, are formed on the silicon substrate, and then each of Mo lower electrode films is deposited thereon.
Further, in first and second test examples (d and e) of the present invention, the seed layer individually made of Ti and Au are formed on the silicon substrate, and then each of Mo lower electrode films is deposited thereon. In the second test example, a Ta layer is first formed on the substrate in order to prevent the Au material from being diffused into the substrate.
The crystalline characteristics of the Mo lower electrode films obtained by each comparative and test examples were analyzed using an XRD (X-ray diffraction) technique. Each XRD σ values of the resulting Mo lower electrode films were calculated by the equation (σ=FWHM (Full Width at Half Maximum)×0.425). The above-calculated XRD σ values correspond to refraction angles (θ=20°), and denote preferences to (110) orientation of Mo. The results of the XRD analysis and the obtained XRD σ values are shown by the graphs in FIG. 4.
With reference to the graphs in
On the other hand, since the XRD σ values in the first and second test examples of the present invention are very low, i.e., 0.81° and 0.53°, the Mo lower electrode films obtained by the first and second test examples have excellent preferences to (110) orientation.
As described above, in case that the seed layer is not formed or the seed layer made of Cr or Ta is formed, the Mo lower electrode film deposited on the seed layer does not have the preference or has poor preference for (110) orientation. On the other hand, in case that the seed layer made of Au or Ti in accordance with the present invention is formed, the Mo lower electrode film deposited on the seed layer has excellent preference for (110) orientation.
The present invention may be advantageously applied to other structures of the FBAR device.
With reference to
In this embodiment, the same as the previous embodiment shown in
In a method for producing the FBAR device shown in
b is a cross-sectional view a FBAR device in accordance with another embodiment of the present invention.
With reference to
As described above, this embodiment uses the substrate structure with a different-type air gap in order to prevent the influence of acoustic waves on the substrate. In this embodiment, before the Mo lower electrode film 92 is deposited, the seed layer 89 made of Au or Ti is formed on the membrane layer 83, thus allowing the Mo lower electrode film 82 grown on the seed layer 89 to have the preference for (110) orientation.
In a method for producing the FBAR device shown in
Further, the present invention may be applied to another FBAR device shown in
With reference to
As described above, the present invention is applied to various structures of the FBAR device. Therefore, the present invention provides the FBAR device in which the crystalline characteristics of the Mo lower electrode film are improved, thus allowing the FBAR device to have excellent piezoelectric characteristics of the piezoelectric layer and excellent electrode film characteristics of the Mo lower electrode film. In the FBAR devices shown in
The seed layer in accordance with the present invention is little affected by the depositing conditions. Particularly, the Mo lower electrode film with excellent crystalline characteristics is grown on the seed layer regardless of the variation of the partial pressure of argon required to control internal stress in the deposition of the Mo lower electrode film.
In order to confirm the above fact, in the present invention, the membrane layer made of a silicon nitride (SixN1−x) is formed on the silicon substrate, and the seed layer made of Ti is formed on the membrane layer. Then, after the Mo lower electrode film is deposited on the seed layer, the crystalline characteristics of the lower electrode film are observed.
In this test, four Mo lower electrode films with different partial pressures of argon, i.e., 2×10−3, 5×10−3, 5×10−2, and 2×10−2 torr in accordance with four test examples (a, b, c, and d) are formed using an Emerald sputter under the same depositing conditions in which the sputtering power is 3 kw, the partial pressure of argon is 2×10−2 torr, and the temperature of the substrate is 250°.
Crystalline characteristics of the resulting four Mo lower electrode films were analyzed using an XRD (X-ray diffraction) technique, and the analyzed results are shown in graphs of FIG. 6. XRD σ values of the resulting four Mo lower electrode films are very small, in the range of 0.58°˜0.64°, and denote excellent preferences to (110) orientation. Further, the variation of XRD σ values according to the variation of the partial pressure of argon is only about 0.6°. Thus, it is appreciated that the variation of the XRD σ value is little influenced by the variation of the partial pressure of argon.
In order to more specifically analyze the effects of the variation of the argon partial pressure in the deposition of the Mo lower electrode film and the material of the seed layer on the crystallization of the Mo lower electrode film, another test is additionally carried out, as follows.
First, in the first and second test examples (a and b), the seed layer made of Ti is formed on the silicon substrate and the silicon nitride layer, and then the Mo lower electrode film is formed on the seed layer. In the first and second comparative test examples (c and d), the Mo lower electrode film is formed directly on the silicon substrate and silicon nitride layer without the formation of the seed layer. In each of the above test and comparative examples (a, b, c, and d), different partial pressures of argon in a sputtering step for forming the Mo lower electrode film, i.e., 2×10−3, 5×10−3, 5×10−2, and 2×10−2 torr, are applied, thus producing 4 samples from each examples, i.e., total 16 samples. Then, the obtained samples were analyzed using an XRD (X-ray diffraction) technique, and XRD σ values denoting the preference for (110) orientation of the samples were calculated. Using the calculated XRD σ values, graphs, which represent the relationship between the variation of the partial pressure of argon and the variation of the XRD σ value, are obtained in FIG. 7.
The Mo lower electrode films obtained by the first and second test examples have very small XRD σ values in the range of 0.53°˜0.57° and in the range of 0.58°˜0.64°, and very small variation of the XRD σ value according to the variation of the partial pressure of argon, i.e., 0.04° and 0.06°. On the other hand, the Mo lower electrode films obtained by the first and second comparative examples have large XRD σ values in the range of 1.59°˜1.95° and in the range of 2.31˜2.47°, and large variation of the XRD σ value according to the variation of the partial pressure of argon, i.e., 0.36° and 0.16°.
As the result of the above test, the conventional Mo lower electrode film has a poor preference for (110) orientation, and the orientation is very sensitive to the variation of the partial pressure of argon. On the other hand, the Mo lower electrode film formed on the Ti seed layer in accordance with the present invention has an excellent preference for (110) orientation, and the orientation is little influenced by the variation of the partial pressure of the argon. Accordingly, the FBAR device of the present invention has a comparatively wide allowable range of the partial pressure of argon applied in the sputtering step, in order to obtain proper internal stress of the Mo lower electrode film required to support the air gap.
As shown in
The Mo lower electrode film of the FBAR device of the present invention has a very small grain size, a smooth surface state, and a high-density structure.
a to 8d are photographs, taken by a SEM, of the Mo lower electrode films of the FBAR device of the present invention.
Here,
With reference to
Further, as shown in
The substrate structure of the FBAR device of the present invention is a substrate provided with a structure for reducing the effect of the substrate on acoustic waves, such as the air gap. It will be appreciated to the persons skilled in the art that a substrate structure using Bragg reflection may be employed by the FBAR device of the present invention instead of the above-described substrate structure provided with the air gap. That is, the substrate structure has a structure of a reflective layer in which two or more layers with different impedances are alternately stacked.
As apparent from the above description, the present invention provides a FBAR device, in which a Mo lower electrode film is formed on a seed layer made of Au or Ti, thus improving the electrode film characteristics (resistivity) and having the smooth surface state and high-density structure. Further, the FBAR device of the present invention has an excellent preference for (110) orientation, thus allowing an AIN piezoelectric layer formed on the lower electrode film to have (002) orientation with excellent piezoelectric characteristics. Accordingly, it is possible to improve the resonance characteristics of the FBAR device. Although the preferred embodiments of the present invention have been disclosed for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2003-0021705 | Apr 2003 | KR | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20040021191 | Bradley | Feb 2004 | A1 |
| 20040021400 | Bradley et al. | Feb 2004 | A1 |
| 20040142497 | Bradley | Jul 2004 | A1 |
| 20040172798 | Ruby et al. | Sep 2004 | A1 |
| 20040227590 | Larson, III et al. | Nov 2004 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20050035828 A1 | Feb 2005 | US |