Patent Application
20160107427
The present invention relates to improved films for printed hydrographics, and to methods of making and using the same.
The market for printed hydrographics, also commonly referred to as immersion printing or water transfer printing, is growing rapidly due to the ease with which three-dimensional articles can be decorated and transformed simply by floating a printed hydrographic in a water-filled container, allowing the water-soluble film on the printed hydrographics to liquefy, applying an activator, and then lowering the article into the water through the floating ink layer. The ink wraps around the article and adheres itself thereto providing the article with the image from the printed hydrographic design.
Printed hydrographics are typically formed by printing the desired graphic design on a very thin film of water-soluble polymer, commonly polyvinyl alcohol (PVA).
Such water-soluble polymer films are very sensitive to heat, moisture and mechanical stresses that may occur during printing processes, and are thus limited to use with certain types of printing processes and are subjected to slower line speeds to avoid stress on the film. PVA is currently printed at line speeds of only up to about 100 feet/minute .
U.S. Pat. No. 6,953,511 is directed to a method of high definition printing for dip transfer of hydrographic designs onto three dimensional articles using thin polyvinyl alcohol films which are not suitable for digital printing or high speed printing such as gravure printing.
There remains a need in the art for improved substrates for printing of hydrographic designs.
Without limiting the scope of the invention a brief summary of some of the claimed embodiments of the invention is set forth below. Additional details of the summarized embodiments of the invention and/or additional embodiments of the invention may be found in the Detailed Description of the Invention below.
In one aspect, the present invention relates to a multilayer film comprising a printed hydrographic design, the multilayer film comprising a support liner, a film fixedly attached to the support liner and a hydrograph design printed thereon, the hydrographic design comprising a solvent based ink.
In another aspect, the present invention relates to a method of making a printed hydrographic design, the method comprising providing a substrate, the substrate comprising at least one support liner and at least one water-soluble film fixedly attached thereto and printing a hydrographic design on the at least one film with a solvent-based ink.
In another aspect, the present invention relates to an inline integrated method of providing an article with a hydrographic design, the method comprising providing a substrate, the substrate comprising a support liner and a water-soluble polymer film, printing a hydrograph design on the water-soluble polymer film, removing the support liner from the water-soluble film, depositing the substrate comprising the hydrographic design in a dipping tank, applying an activator, providing an article and dipping the article into the dipping tank whereby the hydrographic design is transferred onto the article.
These and other aspects, embodiments and advantages of the present disclosure will become immediately apparent to those of ordinary skill in the art upon review of the Detailed Description and Claims to follow.
While embodiments of the present disclosure may take many forms, there are described in detail herein specific embodiments of the present disclosure. This description is an exemplification of the principles of the present disclosure and is not intended to limit the disclosure to the particular embodiments illustrated.
As used herein, the term “hydrographic design” or “hydrographics” shall refer to a process by which a printed design is transferred onto an article, particularly those that are three-dimensional, by dipping the article in a water-filled tank, referred to as immersion printing, water transfer printing, water transfer imaging or cubic printing.
This process is useful on all types of substrates including, but not limited to metal, polymer, glass, wood, ceramic, etc.
Turning now to the figures,
Suitably, the water-soluble polymer film has a thickness of about 30 microns to about 50 microns and more suitably about 35 microns to about 40 microns.
In some embodiments, the water-soluble polymer film has a thickness of about 38 microns to about 40 microns.
The support liner may be formed from a number of suitable materials including, but not limited to paper or a paper product, non-woven fabrics, or a polymer film, suitably paper or paper product, polyester, polypropylene, polyethylene, or copolymers of terpolymers thereof.
If an adhesive is employed on the support liner, suitably the support liner includes one side to which the adhesive will not adhere. The support liner suitably has a thickness of about 2 mils to about 10 mils, and more suitably about 4 mils to about 10 mils.
In some embodiments, a 40 lb/1000 ft2 paper liner is employed.
The water-soluble polymer film is suitably formed from polyvinyl alcohol (PVA), although other water-soluble polymers can be employed including, but not limited to hydroxyethyl cellulose, ethylcellulose polymers, polyacrylamides, polyethyleneimines, polymethacrylates, polyethylene oxide, polyethylene glycol, polyvinylpyrrolidone, poly(N-isopropylacrylamide), poly(2-oxaazoline), polyelectrolytes, and copolymers thereof, etc.
These lists are intended for illustrative purposes only, and not as a limitation on the scope of the present invention. Other suitable support liner materials and water-soluble polymer films could be substituted herein without departing from the scope of the present invention.
The water-soluble polymer film 12 can be fixedly secured to the support liner 14 using any method known in the art including, but not limited to, chemical bonding, adhesive bonding, mechanical bonding such as through the use of heat and pressure, electrostatic attraction, etc.
The adhesive may include any suitable adhesive known in the art including thermoplastic adhesives, thermoset adhesives, water-based adhesives, etc. Thermoset adhesives include one and two-part adhesives and may include radiation curing adhesives, for example.
Suitably, the adhesive is a pressure sensitive adhesive and is disposed on a surface of the liner, the liner having one surface to which the adhesive does not adhere, similar to that of a roll of tape.
The water-soluble polymer film can be laminated to the support liner using any method known in the art.
The adhesively coated support liner 24 and the water-soluble polymer film may be adhered to together through the use of pressure, or heat and pressure, for example.
Alternatively, the web laminator 20 may be integrated in-line with a printing station wherein a hydrographic design is printed onto the water-soluble polymer film side of the multilayer substrate.
Any suitable transferable ink, meaning one that will transfer from the water soluble film onto the article may be employed herein. Solvent-based inks have been found to be preferable in transferring superior graphics onto an article, the invention is not limited as such. For example, water-based inks may also be employed herein.
The hydrographic design may be printed onto the film using any printing method known in the art. The present invention, wherein the multilayer substrate includes a support liner and water-soluble polymer film, the film having a thickness of about 30 microns or more, improves the mechanical strength, heat sensitivity and reduces the stress that may otherwise be put on a water-soluble polymer film such as those employed in hydrographic printing. This allows a significant advantage over previous hydrographic films in that printing methods not previously useful for hydrographic printing, such as digital printing, can be employed with the multilayer substrate disclosed herein.
The support liner and thickness also eliminate issues with stretching and or tearing of the thin water-soluble film which prevents the use of such films on high speed printing lines.
Furthermore, the increased strength and robustness of the hydrographically printed multilayer film can be bulk manufactured in rolls of about 12 inches up to about 120 inches wide, suitably about 12 inches to about 60 inches wide.
The multilayer substrate according to the invention finds particular utility for digital printing wherein a digital-based image is directly printed onto the water-soluble polymer film layer of the multilayer substrate using high-volume laser or inkjet printers. The increased rigidity provided by the support liner and the increased thickness allows for carrying of the water-soluble polymer film through the digital process including the optical registration and for stabilization during printing.
The multilayer substrate is also particularly suited for high speed/high volume gravure printing processes.
Other methods of printing the hydrographic design onto the water-soluble polymer film include, but are not limited to gravure, flexo, screen printing, three-dimensional printing and offset printing.
Furthermore, the line speeds of the printing process, such as for gravure printing, can be significantly increased from 100 feet/minute up to about 1500 feet/minute.
Gravure printing is typically between about 800 feet/minute to about 1500 feet/minute. However, line speeds in general may be about 250 feet/minute to about 1500 feet/minute, about 500 feet/minute to about 1000 feet/minute, and about 800 feet/minute to 1000 feet/minute.
The web laminator and the printing station may be further integrated in-line with a dipping tank. The laminated roll, which suitably includes a large plurality of hydrographic designs, may be cut in-line using, for example, die cutting. An individual hydrographic design can then be fed to a dipping station wherein it is deposited in a water bath, an activator is applied to the water-soluble film, the water-soluble film is allowed to liquefy, and an article is then deposited therein, wherein the ink wraps around the article transferring the graphic design thereon.
Digital printing allows for “on demand” printing as desired. One advantage of digital printing is that large rolls of printed hydrographic designs do not have to be stored for periods of time.
A solvent based or cosolvent based primer layer may be provided on the water soluble or water dispersible film prior to printing to facilitate adhesion of the ink to the film. Primers can also be applied between the layers of ink. These primers may be optionally added to assist in holding an image together as it goes into the dipping tank and is applied to the article. Examples of useful solvents include, but are not limited to alcohols and acetates. For example a cosolvent blend of 50% alcohol such as isopropyl alcohol and a 50% blend of an acetate such as n-propropyl acetate may be employed in the primer solution. Water-based primers may also be suitable for use herein.
Chemical activators for hydrographic designs are well known in the art.
The activator can be applied right before depositing the water-soluble film into the dipping tank, or at the time that the water-soluble film is deposited in the dipping tank.
This technique is particularly suitable for three-dimensional articles.
The present invention is suitable for decorating a vast number of articles formed from a variety of substrates including, but not limited to, automotive accessories for trucks, cars, ATVs, snowmobiles, go karts, golf carts, motorcycles and boats, including wheels, fenders and bumpers, hoods, side panels, dashboards, steering wheels, etc., helmets, hunting equipment such as guns and bows, musical instruments such as guitar bodies, kitchen wares, hair appliances, sporting goods such as bowling balls, wheel chairs, knives, medical enclosures, furniture, office products, prosthetics, etc.
All published documents, including all US patent documents and US patent publications, mentioned anywhere in this application are hereby expressly incorporated herein by reference in their entirety. Any copending patent applications, mentioned anywhere in this application are also hereby expressly incorporated herein by reference in their entirety. Citation or discussion of a reference herein shall not be construed as an admission that such is prior art. [0050] The description provided herein is not to be limited in scope by the specific embodiments described which are intended as single illustrations of individual aspects of certain embodiments. The methods, compositions and devices described herein can comprise any feature described herein either alone or in combination with any other feature(s) described herein. Indeed, various modifications, in addition to those shown and described herein, will become apparent to those skilled in the art from the foregoing description and accompanying drawings using no more than routine experimentation. Such modifications and equivalents are intended to fall within the scope of the appended claims.
This application claims priority under 35 U.S.C. §119 to U.S. Provisional Application Ser. No. 62/066,470, filed Oct. 21, 2014, the entirety of which is incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 62066470 | Oct 2014 | US |