Claims
- 1. A method of laminating a polyolefin plastic film to a surface of a foamed plastic material comprising the steps of applying an initially wet coating of a heat-sensitive plastic resin adhesive on a surface of substantially unoriented polyolefin film and drying said coating, and thereafter heating said dried adhesive to a temperature above its softening point but below the softening points of said film and said foamed plastic material while holding said coated film surface and said foamed plastic material surface against each other, and thereafter cooling the laminated material to a temperature below said softening point of the adhesive.
- 2. A method according to claim 1 wherein said cooling is effected by pressing and holding said laminated material against a relatively cold surface.
- 3. A method according to claim 2 wherein said pressing for cooling said laminated material is effected by fluid pressure.
- 4. A method according to claim 1 wherein said foamed plastic material is heated to said temperature above the softening point of said adhesive before said coated film surface and said foamed plastic material surface are placed in contact with each other.
- 5. A method according to claim 4 wherein said film is placed against said foamed plastic material using a relatively cold pressing means.
- 6. A method according to claim 5 wherein said coated surface of the film is preheated to a temperature of from substantially 100.degree. F. to substantially 180.degree. F. by a stream of heated air directed against said film surface prior to said placing of said film and said foamed plastic material against each other.
- 7. A method according to claim 5 wherein said foamed plastic material is polystyrene, and said polystyrene foam is heated to a temperature within the range of from about 250.degree. F. to about 275.degree. F., and the temperature of said pressing means for placing said film against said foamed plastic material is below 150.degree. F.
- 8. A method according to claim 7 wherein said polyolefin film is polypropylene.
- 9. A method according to claim 7 wherein said polyolefin is polyethylene, and said polystyrene foam is heated to substantially 250.degree. F.
- 10. A method according to claim 7 wherein said pressing means is a relatively cold roller.
- 11. A method according to claim 10 wherein said cooling of the laminated material is effected by using fluid pressure to press said laminated material against a relatively cold surface.
- 12. A method according to claim 11 wherein said relatively cold surface is a receptacle mold.
- 13. A method according to claim 7 wherein said plastic resin adhesive is a solvent solution of a polyamide resin.
- 14. A method according to claim 7 wherein said plastic resin adhesive is a vinylic polymer.
- 15. A method according to claim 14 wherein said vinylic polymer is a polymer based on vinyl acetate.
- 16. A method according to claim 15 wherein said vinylic polymer is a copolymer of ethylene and vinyl acetate.
- 17. A method according to claim 16 wherein said copolymer is a polyvinyl acetate maleate copolymer emulsion.
- 18. A method according to claim 16 wherein said polyolefin film and said ethylene-vinyl acetate are coextruded to form said coated film.
- 19. A method according to claim 15 wherein said vinylic polymer is a blend of polyvinyl acetate and a polyvinyl acetate acrylic copolymer.
- 20. A process for manufacturing receptacles from a sheet of cellular polystyrene foam material coated with a film of polyolefin material secured to the foam by a plastic resin adhesive comprising the steps of applying said adhesive to one side of a substantially unoriented polyolefin film and allowing the adhesive to dry, heating both said foam and the adhesive coated film to a temperature of substantially 260.degree. F. while pressing the adhesive coated side of said film against said foam to form a laminate, and vacuum-forming said laminate into the form of a receptacle by drawing said laminate into a cold mold while said foam and said film are heated.
- 21. The process of claim 20 wherein said polyolefin is polypropylene.
- 22. The process of claim 20 which further comprises similarly applying adhesive coated film to both sides of said foam material prior to said forming step.
Parent Case Info
This is a division of application Ser. No. 482,321, filed June 24, 1974 now U.S. Pat. No. 4,008,347.
US Referenced Citations (8)
Divisions (1)
|
Number |
Date |
Country |
Parent |
482321 |
Jun 1974 |
|