Fire refractory ceramic moulded piece, use thereof and composition for production of moulded pieces

Abstract

The invention relates to a fired refractory ceramic molded piece with a spinel matrix based on (Mg)2+ (Al, Cr)23+O4, in which coarser particles based on chromium corundum and/or corundum and coarser particles based on ZrO2 are present.

Description

DESCRIPTION

[0001] The invention concerns a fired refractory ceramic molded piece, a possible use, as well as a composition for the production of said molded piece.

[0002] From Schulle “Refractory Materials”, 1st Edition, 1990 (ISBN 3-342-00306-5), pp. 288, 289, refractory materials based on chromium corundum, with a proportion of around 10% by weight CrO2 and about 90% by weight Al2O3 are known. Also mentioned there are refractory materials based on Cr2O3/ZrO2. At the same time, it is also noted that the use of materials of this type as refractory ceramics is little known.

[0003] In DE 197 27 917 C1 is described a composition of 5 to 35% by weight Cr2O3 with a grain size <0.1 mm, 1 to 10% by weight ZrO2 with a grain size between 0.5 and 4 mm, as well as 55 to 94% by weight Al2O3 with a grain size between 0.2 and 4.0 mm for the manufacture of fired refractory ceramic molded pieces that can be used in slag-carrying furnaces with great thermal shock resistance and high operating temperatures, for example in rotary furnaces for burning garbage. Good structural elasticity and good corrosion-resistance are reported of these bricks.

[0004] However, in incinerator plants for special waste there is always a high degree of corrosion of the matrix of the refractory material. This is true particularly for strongly alkaline slags, or for slags with a high iron oxide content, or with slags whose C/S ratio (basicity) is variable during the respective process. Here, even bricks burned from a composition in accordance with DE 197 27 917 C1 may reach their limits, in other words, exhibit unsatisfactory wear characteristics.

[0005] The objective of the invention is to offer molded pieces that, in contrast to products according to DE 197 27 917 C1 exhibit better corrosion resistance, especially improved corrosion resistance with respect to slag with variable/changing basicity.

[0006] Application areas for such pieces may be: linings in waste incinerator plants and other furnaces/melting equipment, or in gasification plants, in which aggressive melts and/or slags are encountered.

[0007] The basic idea of the invention is, in particular, to fashion the matrix of the molded piece to be more stable (more resistant) in the face of an aggressive slag.

[0008] A fired refractory ceramic molded piece according to the invention is distinguished in its most general embodiment by a spinel mixture matrix, in which relatively coarse grains based on corundum and/or chromium corundum, as well as ZrO2 are present. The desired product properties are achieved, for example, by the simultaneous presence of chromium corundum and zirconium corundum, or by the simultaneous presence of corundum and zirconium mullite.

[0009] The spinel mixture matrix can be produced from appropriate composition components such as Cr2O3, MgO, or Al2O3 as individual components and/or in the form of pre-synthesized spinels, in particular MA-spinels (MgO—Al2O3) or MCA-spinels, in particular (MgO—Cr2O3—Al2O3), or by other means.

[0010] The chromium corundum grains have their origin in the composition in the oxides of chromium and aluminum, and are created during the firing process. They may also be introduced, at least partially, as previously reacted components.

[0011] The ZrO2-containing grains may be derived from baddeleyite-containing material (raw material), or, for example, from sinter-zirconium mullite, melt zirconium mullite, sinter zirconium corundum, melt zirconium corundum, or from a ZAC material (pre-reacted material of SiO2, ZrO2 and Al2O3), separately or in a mixture.

[0012] A composition component based on an MA-spinel [(MgO, Al2O3)]-spinel, in a fraction of <0.5 or <0.3 or <0.1 mm may be used. This spinel, which preferably is not stoichiometiric, say, for example, with an excess of MgO, reacts with the chromium oxide of the composition to form a mixed spinel in the form of (Mg)2+ (Al, Cr)23+O4 and forms essential positions of the base material of the matrix of the fired product. This mixed spinel exhibits an outstanding resistance relative to the named critical slags.

[0013] Aluminum oxide, especially as a component in the grain-size range of 0.5-10 mm, can react with (fine-particled) chromium oxide, and leads to the already mentioned chromium corundum grains, which are distributed within the matrix the same as the said ZrO2-containing grains.

[0014] It is self-evident that, depending on the degree of contamination of the raw materials, additional ingredients may be present in the composition components, and thus become secondary constituents of the molded piece.

[0015] The aforementioned coarse grains in the fired product may attain an average diameter (d0.50) between 0.5 to 10 mm.

[0016] The chromium oxide concentration within the chromium corundum grains can fluctuate, depending on the firing temperature and furnace atmosphere, as well as on the proportions of chromium oxide or corundum (Al2O3), while the firing process can be managed in a way such that within the chromium corundum grains there remains at least one zone, especially a core zone, that is free of chromium oxide.

[0017] Correspondingly, the firing process can be controlled so that the chromium grains have their highest chromium oxide concentration within the region close to their surface.

[0018] FIGS. 1 to 4 show microscopic photographs on the indicated scale of ground surfaces of a fired product. In them, the numbers signify: 1. Chromium corundum grains; 2. Zirconium corundum grains; 3. Mixed spinel matrix; 4. Pores. The coarse grains based on chromium corundum and zirconium corundum are distinctly visible in the fine-grained spinel matrix.

[0019] The matrix component, i.e. the proportion consisting essentially of the named mixed spinel, may constitute between 10 and 70% by weight of the total mass, and usually between 15 and 50% by weight.

[0020] By virtue of its outstanding stability, particularly vis-à-vis aggressive slags, such as alkali-containing slags, or slags with a high iron oxide content, the fired refractory ceramic molded piece is suitable for the lining of a furnace for burning refuse, for example for the incineration of special refuse, where slags of this type occur.

[0021] The composition (batch) for producing the previously named molded piece encompasses, in its most generalized implementing form, the following components (which, alone, or with additional components, add up to 100% by weight):

[0022] 2 to 35% by weight chromium oxide <0.5 mm,

[0023] 1 to 15% by weight zirconium dioxide >0.2 mm,

[0024] 1 to 12% by weight magnesium oxide <0.5 mm,

[0025] 38 to 96% by weight aluminum oxide <10 mm.

[0026] The components being added to the composition may be pure oxides or materials that introduce the named oxides into the composition in the stated proportions.

[0027] A particularly conspicuous aspect of this composition process lies in the fact that the composition, using exclusively a temporary binding agent, e.g. sulfite waste liquor, can be manufactured into molded pieces, firing them subsequently, at which time the sulfite waste liquor is to almost entirely burned off.

[0028] By dint of the invention, that is, the use of, e.g. phosphate-containing binding agents can be avoided, which represents an additional substantial advantage vis-à-vis the state of the art.

[0029] Contrariwise, the composition according to DE 197 27 917 C1 cannot be processed with an exclusively temporary binding agent such as sulfite waste liquor. With the known composition, it is impossible with a temporary binding agent to achieve an adequate degree of firmness in the pre-firing state.

[0030] The composition may be varied within the scope of the following provisions:

[0031] The grain-size fraction of the Al2O3 component may be <6 mm or <4 mm,

[0032] The grain-size fraction of the ZrO2-containing component can be between 1 and 4 mm,

[0033] The grain-size fractions of Cr2O3 and MgO may be <0.2 mm, <0.1 mm, or also >0.05 mm,

[0034] Al2O3, Cr2O3 and/or MgO may be introduced, first of all, at least partially as spinel, particularly MA- or MCA spinel, at 5 to 25% by weight, for example,

[0035] Where MgO is present at least partially as spinel, the Al2O3 or Cr2O3 component needs to be reduced proportionally,

[0036] The content of Cr2O3 may be set at 5 to 25% by weight,

[0037] The ZrO2 content in the composition may be 1 to 6% by weight,

[0038] The Al2O3 component in the composition may be between 64 and 87% by weight of the total composition, and a portion may be present in a fine fraction (<0.1 mm),

[0039] The SiO2 content should be limited to <3.0% by weight or, better: <0.1% by weight.

[0040] In this connection, it is recommended that a ZrO2-containing component be used which, if possible, is free of SiO2 content,

[0041] The Fe2O3 content may be <0.5% by weight,

[0042] The MgO content in the composition may amount 3 to 8% by weight,

[0043] The Al2O3 content may be added at least in part as chromium corundum,

[0044] The MA-spinel can, by way of example, consist of the following components (all data are in % by weight):

MgO:   31-35
Al2O3: 64-67
CaO:   0.3-0.6
Fe2O3: 0.1-0.3

[0045] Besides other components such as Na2O, SiO2, whose respective proportion amounts to <0.2% by weight.

[0046] The composition, including its temporary binding agent, is prepared in the usual manner, and fabricated into molded pieces, principally by pressing. It is subsequently fired at temperatures between 1,200 and 1700° C.

[0047] Starting with a composition of:

[0048] 8% by weight chromium oxide <0.1 mm

[0049] 5% by weight zirconium corundum 0.5 to 4 mm

[0050] 15% by weight non-stoichiometric MA-spinel (of previously mentioned type) <0.1 mm

[0051] Remainder corundum <4 mm,

[0052] and adding 3% by weight sulfite waste liquor (relative to the total of components), bricks were pressed at 100 MPa pressure, and fired at 1,550° C. The bricks exhibited the following characteristic values:

	Rough density (per DIN EN 993-1):	3.35	g/cm3
	Open porosity (per DIN EN 993-1):	15.1%
	Cold compression strength (per DIN 51607):	170	N/mm2
	Softening under pressure (per DIN 51053 T1):	T0 > 1,700° C.
	Thermal shock resistance (per DIN EN 993,	>30	cycles.
	Part 11, relative to water):

[0053] These values fall within the range of bricks according to DE 197 27 917 C1. However, the bricks according to the invention prove to be distinctly superior in their corrosion resistance, particularly vis-à-vis the cited critical slags. Their resistance in a laboratory test (slagging test in an induction crucible furnace) was 30% higher.

Claims

1. Fired refractory ceramic molded piece with a spinel matrix based on (Mg)2+ (Al, Cr)23+O4, in which coarser particles based on chromium corundum and/or corundum and coarser particles based on ZrO2 are present.

2. Molded piece according to claim 1, in which the coarser particles vis-à-vis the particles of the spinel matrix consist of the components chromium corundum and zirconium corundum.

3. Molded piece according to claim 1, in which the corundum and/or chromium corundum grains have an average diameter (d0.50) of 0.5 to 10 mm.

4. Molded piece according to claim 1, in which the ZrO2-containing grains have an average diameter (d.50) of 0.5 to 10 mm.

5. Molded piece according to claim 1, in which the spinel matrix constitutes 10 to 70% by weight of the total mass.

6. Use of the molded piece in accordance with one of the claims 1 to 5 for lining a furnace for burning refuse, particularly special type refuse.

7. Composition (batch) for the manufacture of a molded piece according to one of the claims 1 to 5, with 7.1 2 to 35% by weight Cr2O3 in a grain size fraction <0.5 mm, 7.2 1 to 15% by weight ZrO2, in a grain-size fraction >or equal to 0.2 mm, 7.3 1 to 12% by weight MgO in a grain-size fraction of <0.5 mm, 7.4 38 to 96% by weight Al2O3 in a grain-size fraction of <10 mm.

8. Composition in accordance with claim 7, in which at least a part of the components MgO, Al2O3, or Cr2O3 is present as a spinel.

9. Composition according to claim 8, in which at least a part of the components is present as MA- or MCA-spinel.

10. Composition according to claim 7, in which the Cr2O3 content is 5 to 25% by weight.

11. Composition according to claim 7, in which the ZrO2-content is between 1 and 6% by weight.

12. Composition according to claim 11, in which the Al2O3-content is between 64 and 87% by weight.

13. Composition according to claim 7, with an Fe2O3-content <0.5% by weight.

14. Composition according to claim 7, in which the ZrO2 content is fashioned by a baddelyite-containing raw material.

15. Composition according to claim 7, in which the ZrO2 content is made up by a sinter-zirconium mullite, melt-zirconium mullite, sinter zirconium corundum, melt zirconium corundum or a ZAC material, separately or as a mixture.

16. Composition according to claim 7, in which the ZrO2 content is present in a grain size of between 1 and 4 mm.

17. Composition according to claim 7, with an MA-spinel content of between 5 and 25% by weight.

18. Composition according to claim 7, in which at least one of the Cr2O3- and MgO containing components is present in a grain size of <0.2 mm.

19. Composition according to claim 7, in which at least one of the Cr2O3 and MgO-containing components is present in a grain-size fraction of <0.1 mm.

20. Composition according to claim 7, in which up to 30% by weight is present as Al2O3 in a grain-size fraction of <0.1 mm.

21. Composition according to claim 7, in which Al2O3 is present in a grain-size fraction of >0.2 mm.