Fire resistant windows

Abstract

An optically transparent aqueous intumescent gel for use with transparent laminates comprising about 5 to 30% by weight acrylamide, about 0 to 4% by weight of a crosslinking agent, about 5 to 28% by weight of an ammonium or alkali metal salt of an alkanoic acid having 1 to 4 carbon atoms, about 0.05 to 10% by weight of a polymerization catalyst, and water, and a laminate with the gel.

Description

Claims

1. A fire resistant and impact resistant transparent laminate comprising at least two spaced parallel sheets of transparent material selected from the group consisting of group and polymeric material, at least one optically transparent resinous inner layer between said parallel sheets, and a layer of the optically transparent gel on at least one side of said inner layer, said gel comprising about 5 to 30% by weight acrylamide, about 0 to 4% by weight of a crosslinking agent, about 5 to 28% by weight of an ammonium or alkali metal salt of an alkanoic acid having 1 to 4 carbon atoms, about 0.05 to 10% by weight of a polymerization catalyst, and water.

2. The laminated claim 1, wherein said resinous layer is an ionomer.

3. The laminate of claim 1, wherein said spaced sheets comprises glass.

4. The laminate of claim 1, comprising two spaced glass layers, a siloxane coated ionomer layer between said spaced glass layers and said gel being adhered to said coated ionomer.

5. The laminate of claim 1 wherein said crosslinking agent in said gel is about 5 to 30% by weight acrylamide, about 0 to 4% by weight of a crosslinking agent, about 5 to 28% by weight of an ammonium or alkali metal salt of an alkanoic acid having 1 to 4 carbon atoms, about 0.05 to 10% by weight of a polymerization catalyst, N,N'-methylene bisacrylamide and water.

6. The laminate of claim 1 wherein said alkali metal salt of an alkanoic acid in said gel is sodium formate.

7. The laminate of claim 1 wherein said alkali metal salt of an alkanoic acid in said gel is sodium acetate.

8. The laminate of claim 1 wherein said catalyst in said gel is ammonium persulphate.

9. The laminate of claim 1 including N,N,N',N-tetramethylethylenediamine in said gel.

10. The laminate of claim 1 including a melting point depressant in said gel selected from the group consisting of sodium bicarbonate, sodium silicate, sodium chloride and ethylene glycol.

11. The laminate of claim 1 wherein said outer sheets are glass.

12. The laminate of claim 1 wherein at least one outer sheet is polycarbonate.

13. The laminate of claim 1 wherein the surfaces adjacent said gel are primed to obtain better adhesion of said gel.