Patent Application
20180037998
The use of fire-retardant compositions to prevent and suppress flame intensity and rate of spread in wildland fires has been known since the 1950s. It should be understood that there are both short-term and long-term fire-retardants. Short-term retardants, also called suppressants or water enhancers, depend entirely on their contained water to cool the fire. Once their contained water evaporates, they are no longer effective. Water, itself can be considered a short-term retardant or suppressant. Bentonite clay and super absorbent polymers (SAP) are formulated examples of short-term retardants that are more effective than water because they are generally viscous and, consequently tend to remain where applied whereas liquid water runs off of the fuel onto the ground. Long-term fire-retardants, on the other hand, convert wildland vegetation from a substance that is flammable and, consequently, a fuel, to a substance that has been chemically modified or converted to a substance that does not ignite and provide fuel when heated to and beyond its ignition point by the advancing fire. Ammonium phosphate based long-term fire-retardants are the subject of this technology. They function by reacting with the fuel, converting it to a substance that does not release flammable gases when heated, but rather, decomposes to a graphic-like carbon via dehydration. This type of retardant is effective until it is removed from the vegetative fuel by either rain or some physical means. Many different types of long-term fire-retardants have been used, for example, sodium calcium borate, monoammonium and diammonium orthophosphate, diammonium sulfate, and aqueous solutions of ammonium polyphosphates that contains a mixture of ortho, pyro, and short chain polyphosphates. Ammonium phosphates are the long-term retardants specified by many agencies with responsibility for the prevention and management of wildland fire.
Fire-retardant application can be made from either aerial or ground vehicles, e.g., fixed-wing aircraft, rotatory wing aircraft (e.g., helicopters), and ground engines. Aerial attack is most commonly used when the fire is in areas not easily or quickly accessible from the ground. Typically, fire-retardants are supplied to the user as a dry or liquid concentrate which is subsequently mixed with water to form a solution containing a prescribed amount of fire-retardant concentrate per unit volume before or during loading the fire-retardant solution into the application vehicle. The prescription for the solution is determined by performance criteria when subjected to a standard fire test.
Fire-retardant solutions applied to fuels threatened by fire may accidently reach streams, rivers, lakes, ponds, and other waterways and wetland habitats. Consequently, it is desirable that fire-retardant solutions exhibit low aquatic toxicity. Since ammonia is toxic to many aquatic species, it is desirable that the fire-retardant solution contain a low ammonia content, consequently, there remains a need for fire-retardant solutions that contain reduced amounts of ammonia per unit volume.
Provided herein are fire-retardant concentrate compositions comprising a mixture of ammonium phosphates and a corrosion inhibitor system that comprises at least one biopolymer. In certain embodiments, the mixture of ammonium phosphates has a molar ratio of ammoniacal nitrogen to phosphorus (N/P molar ratio) in a range of from about 1.1 to about 1.9. In certain embodiments, the N/P molar ratio is from about 1.35 to about 1.65. In certain embodiments, the N/P molar ratio is from about 1.4 to about 1.6.
In certain embodiments of a fire-retardant concentrate composition disclosed herein, the amount of ammonium phosphate in the fire-retardant concentrate is from about 75% to about 97% by weight of the total concentrate composition. In certain embodiments, the ammonium phosphates comprise a mixture of at least two ammonium phosphates selected from the group consisting of ammonium orthophosphates, ammonium pyrophosphates, and ammonium polyphosphates having an average chain length of less than 20 phosphorus atoms. In certain embodiments, the fire-retardant concentrate composition comprises at least two ammonium orthophosphates or at least two ammonium pyrophosphates. In certain embodiments, the fire-retardant concentrate composition comprises at least one ammonium orthophosphate and at least one ammonium pyrophosphate.
In certain embodiments of a fire-retardant concentrate composition disclosed herein, the mixture of ammonium phosphates comprises monoammonium orthophosphate (MAP) and diammonium orthophosphate (DAP). In certain other embodiments, the mixture of ammonium phosphates consists essentially of monoammonium phosphate (MAP) and diammonium phosphate (DAP). In certain embodiments, the mixture of ammonium phosphates comprises: MAP containing from about 10% to about 12% ammoniacal nitrogen by weight and from about 40% to about 61% phosphorus pentoxide by weight; and DAP containing from about 16% to about 21% ammoniacal nitrogen by weight and from about 40% to about 54% phosphorus pentoxide by weight. In certain embodiments, the mixture of ammonium phosphates comprises: MAP containing about 11% to about 12% ammoniacal nitrogen by weight and about 55% to about 61% phosphorus pentoxide by weight; and DAP containing about 16% to about 21% ammoniacal nitrogen by weight and about 40% to about 54% phosphorus pentoxide by weight. In certain embodiments, the weight ratio of MAP to DAP is in the range of from about 5% to about 60% MAP to about 40% to about 95% DAP of the total ammonium phosphate in the concentrate. In certain embodiments, the weight ratio of MAP to DAP is in the range of from about 40% to about 60% MAP to about 40% to about 60% DAP of the total ammonium phosphate in the concentrate. In certain embodiments, the weight ratio of MAP to DAP is in the range of from about 50% to about 60% MAP and about 40% to about 50% DAP of the total ammonium phosphate in the concentrate.
In certain embodiments of a fire-retardant concentrate composition disclosed herein, the biopolymer portion of the corrosion inhibitor system is in an amount of from about 2.0% to about 8.5% by weight of the total concentrate composition. In certain embodiments, the biopolymer is in an amount of from about 2.0% to about 3.0% by weight of the total concentrate composition. In certain embodiments, the corrosion inhibitor system further comprises anhydrous sodium molybdate, its dihydrate, or mixtures thereof. In certain embodiments, the amount of anhydrous sodium molybdate, its dihydrate, or mixtures thereof is in a range of about 0.01% to about 2.0% by weight of the total concentrate composition. In certain embodiments, the amount of anhydrous sodium molybdate, its dihydrate, or mixtures thereof is in a range of about 0.05% to about 0.3% by weight of the total concentrate composition. In certain embodiments, the amount of anhydrous sodium molybdate, its dihydrate, or mixtures thereof is in a range of from about 0.01% to about 2.0% by weight of the total concentrate composition and the biopolymer is in an amount of from about 2.5% to about 8.5% by weight of the total concentrate composition.
In certain embodiments of a fire-retardant concentrate composition disclosed herein, the biopolymer is selected from the group consisting of xanthan gum, rhamsan gum, welan gum, diutan gum, and mixtures thereof. In certain embodiments, the biopolymer is xanthan gum. In certain embodiments, the xanthan gum is in an amount of from about 2.0% to about 3.0% by weight of the total concentrate composition. In certain embodiments, the biopolymer is diutan gum. In certain embodiments, the diutan is in an amount of from about 2.0% to about 3.0% by weight of the total concentrate composition.
In certain embodiments of a fire-retardant concentrate composition disclosed herein, the fire-retardant concentrate composition further comprises a pigment or dye. In certain embodiments, the pigment or dye is a fluorescent pigment or dye. In certain embodiments, the pigment or dye is UV sensitive and/or formaldehyde-free. In certain embodiments, the fluorescent pigment or dye has a Lab color spacing of “L” in a range from about 34 to about 89, “a” in a range from about 18 to about 83 and “b” in a range from about −61 to about 56.
In certain embodiments of a fire-retardant concentrate composition disclosed herein, the composition comprises one or more additives selected from the group consisting of a flow conditioner, a surfactant, a foam controlling additive, a foam former, a biocide, and any combination thereof.
In certain embodiments of a fire-retardant concentrate composition disclosed herein, when the concentrate composition is mixed at a ratio of from about 0.9 to about 1.05, 1.1, 1.14, 1.2, or 1.3 pounds of the concentrate per 1.0 gallon of water, the resulting aqueous solution exhibits a magnesium alloy corrosion rate equal to or less than 4.0 milli-inches per year. In certain embodiments, when the concentrate composition is mixed at a ratio of from about 0.9 to about 1.05, 1.1, 1.14, 1.2, or 1.3 pounds of the concentrate per 1.0 gallon of water, the resulting aqueous solution exhibits a magnesium alloy corrosion rate equal to or less than 3.0 milli-inches per year. In certain embodiments, when the concentrate composition is mixed at a ratio of from about 0.9 to about 1.05, 1.1, 1.14, 1.2, or 1.3 pounds of the concentrate per 1.0 gallon of water, the resulting aqueous solution exhibits an aluminum corrosion rate equal to or less than 2.0 milli-inches per year. In certain embodiments, when the concentrate composition is mixed at a ratio of from about 0.9 to about 1.05, 1.1, 1.14, 1.2, or 1.3 pounds of the concentrate per 1.0 gallon of water, the resulting aqueous solution meets all of the required corrosion criteria of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments. In certain embodiments, when the concentrate composition is mixed at a ratio of from about 0.9 to about 1.05, 1.1, 1.14, 1.2, or 1.3 pounds of the concentrate per 1.0 gallon of water, the resulting aqueous solution meets all of the required stability criteria of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments. In certain embodiments, when the concentrate composition is mixed at a ratio of from about 0.9 to about 1.05, 1.1, 1.14, 1.2, or 1.3 pounds of the concentrate per 1.0 gallon of water, the resulting aqueous solution meets all of the required corrosion and stability criteria of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
Provided herein are fire-retardant solutions prepared by the method of mixing a fire-retardant concentrate composition disclosed herein with water. In certain embodiments, from about 0.9 pounds to about 1.05, 1.1, 1.14, 1.2, or 1.3 pounds of the fire-retardant concentrate composition is added per 1.0 gallon of water. In certain embodiments, from about 0.9 pounds to about 1.2 pounds of the fire-retardant concentrate composition is added per 1.0 gallon of water. In certain embodiments, the fire-retardant solution is a homogenous solution comprising the fire-retardant concentrate composition and water. In certain embodiments, the solution contains suspended water-insolubles. In certain embodiments, the fire-retardant solution exhibits a viscosity in the range of from about 150 cPs to about 1500 cPs.
In certain embodiments of a fire-retardant solution disclosed herein, the solution exhibits a magnesium alloy corrosion rate equal to or less than 4.0 milli-inches per year. In certain embodiments, the solution exhibits a magnesium alloy corrosion rate equal to or less than 3.0 milli-inches per year. In certain embodiments, the solution exhibits an aluminum corrosion rate equal to or less than 2.0 milli-inches per year. In certain embodiments, the solution meets all of the required corrosion criteria of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments. In certain embodiments, the solution meets all of the required stability criteria of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments. In certain embodiments, the solution meets all of the required corrosion and stability criteria of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
In certain embodiments of a fire-retardant solution disclosed herein, the solution exhibits an aquatic toxicity (LC50) in the range of from about 180 milligrams per liter to about 2700 milligrams per liter. In certain embodiments, the solution exhibits an aquatic toxicity (LC50) greater than 180 milligrams per liter.
In certain embodiments of a fire-retardant solution disclosed herein, the solution has a pH not greater than about pH 8.0. In certain embodiments, the solution has a pH not greater than about pH 7.58. In certain embodiments, the solution has an acidic pH.
Provided herein are methods of producing a fire-retardant solution. In certain embodiments, the method comprises mixing from about 0.9 to about 1.05, 1.1, 1.14, 1.2, or 1.3 pounds of a fire-retardant concentrate composition disclosed herein per 1.0 gallons of water to produce a fire-retardant solution. In certain embodiments, the method comprises mixing from about 0.9 to about 1.2 pounds of a fire-retardant concentrate composition disclosed herein per 1.0 gallons of water. In certain embodiments, the fire-retardant solution produced is a fire-retardant solution disclosed herein.
Provided herein are methods of combatting a wildfire comprising applying a fire-retardant solution disclosed herein either directly onto flaming fuel or indirectly onto the fuel ahead of a potentially advancing fire front. In certain embodiments, the fire-retardant solution is applied from a ground platform, an aerial platform, or from both. In certain embodiments, the fire-retardant solution is applied from a rotary wing aircraft. In certain embodiments, the fire-retardant solution is applied from a device consisting of a helicopter bucket, an internal tank, or a tank directly attached to the exterior of the delivery platform.
It is to be noted that the term “a” or “an” entity refers to one or more of that entity; for example, “a plant,” is understood to represent one or more plants. As such, the terms “a” (or “an”), “one or more,” and “at least one” can be used interchangeably herein.
Furthermore, “and/or” where used herein is to be taken as specific disclosure of each of the two specified features or components with or without the other. Thus, the term and/or” as used in a phrase such as “A and/or B” herein is intended to include “A and B,” “A or B,” “A” (alone), and “B” (alone). Likewise, the term “and/or” as used in a phrase such as “A, B, and/or C” is intended to encompass each of the following embodiments: A, B, and C; A, B, or C; A or C; A or B; B or C; A and C; A and B; B and C; A (alone); B (alone); and C (alone).
Unless defined otherwise, technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure is related.
Numeric ranges are inclusive of the numbers defining the range.
The headings provided herein are solely for ease of reference and are not limitations of the various aspects or aspects of the disclosure, which can be had by reference to the specification as a whole. Accordingly, the terms defined immediately below are more fully defined by reference to the specification in its entirety.
As used herein, the terms “concentrate,” “retardant concentrate,” and “fire-retardant concentrate” can be used interchangeably to mean a concentrated product that is mixed with water to prepare a fire-retardant solution prior to application.
As used herein, the phrase “fire-retardant solution” includes suspensions of soluble and insoluble components.
As used herein, the phrase “corrosion inhibitor system” means a component or mixture of components that reduce the corrosion of fire-retardant concentrates and solutions. In certain embodiments, a corrosion inhibitor system reduces the corrosion of fire-retardant concentrates and solutions to within some or all of the requirements of paragraphs 3.7.1, 3.7.2, 4.7.1 and 4.7.2 in the U.S.D.A. Forest Service Specification 5100-304c, June 1, 2007 all Amendments.
As used herein, the term “free flowing” means that the substance will easily flow from or can be sucked from a container via a source of vacuum.
As used herein, the terms “powder, granular, or powder and granular form” means that the substance is composed of a distribution of particle sizes ranging from about 10 microns to about 900 microns.
As used herein, the “corrosion rate” of a fire-retardant concentrate or fire-retardant solution expressed in milli-inches per year (MPY) with respect to a metal is determined by the methods described in Section 4.7.1 and 4.7.2 of Forest Service Specification 5100-304c, June 1, 2007 and all Amendments.
As used herein, the qualifier “ammoniacal,” placed in front of nitrogen (i.e., “ammoniacal nitrogen”), when referring to the nitrogen to phosphorus molar ratio (N/P) specifies that the amount of nitrogen used to determine the N/P ratio is only that nitrogen present in the ammonium phosphate, and thus, if other nitrogen is present in the fire-retardant concentrate from other sources, this other nitrogen would not be considered when calculating the N/P ratio.
Long-term fire-retardant concentrate compositions described in this disclosure and solutions made therefrom are advantageous over prior compositions and solutions in terms of, for example, retardant concentrate effectiveness, solution stability, aquatic toxicity, visibility upon wildland fuels immediately after application, and the lack of long-term aesthetic impact. Certain embodiments of compositions disclosed herein can include, but are not limited to, monoammonium orthophosphate (MAP), diammonium orthophosphate (DAP), ammonium pyrophosphates, ammonium tripolyphosphates, ammonium tetrapolyphosphates, and other ammonium polyphosphates, alkaline earth substituted versions of all these examples, and mixtures thereof. In certain embodiments, the ammonium polyphosphates have an average chain length of less than 20 phosphorus atoms. The compositions also comprise a corrosion inhibitor system comprising at least one biopolymer. Representative examples of biopolymers include xanthan gum, rhamsan gum, welan gum, diutan gum, and mixtures thereof. Diutan gum is a water soluble biopolymer produced by fermentation for use in a variety of industrial applications. It is believed that such biopolymers impact both the rheological properties and the corrosion properties of the fire-retardant solutions. In certain embodiments, the corrosion is magnesium corrosion. Fire-retardant solutions made from fire-retardant concentrates can be transferred to application vehicles and applied either aerially or from the ground in the manner best suited to obtain and maintain control of a fire. Magnesium corrosion is a concern especially when helicopters are used for the application of the fire-retardant solution because magnesium is used to fabricate critical components in helicopters but not necessarily other types of delivery vehicles. In certain embodiments, fire retardant concentrates and solutions exhibit low levels of magnesium corrosion and their use is Federal and/or State qualified. Such solutions can be effective in preventing the spread of fire in wildland situations and from one structure to another.
Compositions, solutions, and suspensions described herein can contain less ammonia per unit volume of fire-retardant solution than previous long-term fire retardant solutions suitable for application from rotary-wing aircraft. The amount of fire-retardant concentrate required per unit volume/weight of solution can be lower than similar compositions, resulting in the need of less total chemical to gain control of a fire. In certain embodiments, fire-retardant solutions can be considerably more visible to firefighting personnel during firefighting activities which can aid in better placement of the fire-retardant solution and consequently can result in the use of considerably less fire-retardant solution to gain control of the incident. In certain embodiments, magnesium corrosion is reduced, which is advantageous because magnesium is a major material of construction of rotary wing aircraft.
The control of magnesium corrosion has generally been possible when using only basic diammonium phosphate containing fire retardant solutions. It has now been discovered, however, that the formulations described herein can meet the low USDA Forest Service magnesium corrosion requirements. In certain embodiments, a composition or solution meeting the low USDA Forest Service magnesium corrosion requirement is an acidic mixture of ammonium phosphates.
The present disclosure provides for fire-retardant concentrate compositions comprising a mixture of ammonium phosphates, for example, ammonium salts of ortho, pyro, tripoly, or tetrapoly phosphoric acid. In certain embodiments, the fire-retardant concentrate composition is a free flowing powder and/or granular material. In certain embodiments, the particle sizes range from any of about 10 microns to about 900 microns. In certain embodiments, the particle sizes range from any of about 10, 20, 30, 35, 37, 40, or 50 microns to about 900 microns. In certain embodiments, the particle sizes range from any of about 10, 20, 30, 35, 37, 40, or 50 microns to about 800 microns. In certain embodiments, the particle sizes range from any of about 10, 20, 30, 35, 37, 40, or 50 microns to about 700 microns. In certain embodiments, the particle sizes range from any of about 10, 20, 30, 35, 37, 40, or 50 microns to about 600 microns. In certain embodiments, the particle sizes range from any of about 10, 20, 30, 35, 37, 40, or 50 microns to about 500 microns. In certain embodiments, the particle sizes range from any of about 10, 20, 30, 35, 37, 40, or 50 microns to about 400 microns. In certain embodiments, the particle sizes range from any of about 10, 20, 30, 35, 37, 40, or 50 microns to about 300 microns. In certain embodiments, the particle sizes range from any of about 10, 20, 30, 35, 37, 40, or 50 microns to about 200 microns. In certain embodiments, the particle sizes range from about 37 to about 400 microns. In certain embodiments, the mixture of ammonium phosphates has a molar ratio of ammoniacal nitrogen to phosphorus (N/P ratio) in a range from about 1.1 to about 1.9. In certain embodiments, the mixture of ammonium phosphates has a molar ratio of ammoniacal nitrogen to phosphorus (N/P ratio) in a range from about 1.35 to about 1.65. In certain embodiments, the mixture of ammonium phosphates has a molar ratio of ammoniacal nitrogen to phosphorus (N/P ratio) in a range from about 1.4 to about 1.6. In certain embodiments, the mixture of ammonium phosphates has a molar ratio of ammoniacal nitrogen to phosphorus (N/P ratio) in a range from any of about 1.1, 1.2, 1.3, 1.35, 1.4, 1.5, 1.6, 1.7, or 1.8 to any of about 1.2, 1.3, 1.4, 1.5, 1.6, 1.65, 1.7, 1.8, or 1.9. The concentrate and its solutions generally contain less ammonia in comparison with previous products, and can result for example, in a lower aquatic toxicity.
The mixture of ammonium phosphates is generally the predominate component of the fire-retardant concentrate composition. In certain embodiments, the amount of the mixture of the ammonium phosphates is greater than about 60%, 65%, 70%, 75%, 80%, 85%, 90%, 95%, or 96% by weight of the total concentrate composition. In certain embodiments, the amount of the mixture of the ammonium phosphates is not more than about 90%, 95%, 96%, or 97% by weight of the total concentrate composition. In certain embodiments, the amount of the mixture of the ammonium phosphates is from about 75% to about 97% by weight of the total concentrate composition. In certain embodiments, the amount of the mixture of the ammonium phosphates is from about 80% to about 97% by weight of the total concentrate composition. In certain embodiments, the amount of the mixture of the ammonium phosphates is from about 90% to about 97% by weight of the total concentrate composition. In certain embodiments, the amount of the mixture of the ammonium phosphates is from about 95% to about 97% by weight of the total concentrate composition. In certain embodiments, the amount of the mixture of the ammonium phosphates is from any of about 60%, 65%, 70%, 75%, 80%, 85%, 90%, 95%, or 96% to any of about 65%, 70%, 75%, 80%, 85%, 90%, 95%, 96%, or 97% by weight of the total concentrate composition.
A mixture of ammonium phosphates comprises at least two ammonium phosphates. In certain embodiments, the mixture comprises at least two, at least three, or at least four ammonium phosphates. Representative ammonium phosphates include ammonium orthophosphates, ammonium pyrophosphates, ammonium tripolyphosphates, ammonium tetrapolyphosphates, and other ammonium polyphosphates having an average chain length less than 20 (e.g., less than 20, 19, 18, 17, 16, 15, 14, 13, 12, 11, 10, 9, 8, 7, 6, or 5). In certain embodiments, the mixture of ammonium phosphates comprises, consists essentially of, or consists of monoammonium orthophosphate (MAP) and diammonium orthophosphate (DAP). In certain embodiments, the MAP contains from about 10% or 11% to about 12% ammonia by weight and from about 40% or 55% to about 61% phosphorus pentoxide by weight. In certain embodiments, the DAP contains from about 16% to about 21% ammonia by weight and from about 40% to about 54% phosphorus pentoxide by weight. Further, in certain embodiments, the weight ratio of MAP to DAP is in the range of from about 5% to about 60% MAP to about 40% to about 95% DAP of the total ammonium phosphate in the concentrate. In certain embodiments, the weight ratio of MAP to DAP is in the range of from about 40% to about 60% MAP to about 40% to about 60% DAP of the total ammonium phosphate in the concentrate. In certain embodiments, the weight ratio of MAP to DAP is in the range of from about 50% to about 60% MAP to about 40% to about 50% DAP of the total ammonium phosphate in the concentrate.
The fire-retardant concentrate compositions of the present disclosure also comprise a corrosion inhibitor system comprising at least one biopolymer. It has been discovered that biopolymer containing solutions exhibit reduced corrosion, and in particular, reduced magnesium corrosion. Thus, the compositions are well-suited for application from, for example, tanks mounted within or externally attached to the heli-tanker (a tanked rotary wing aircraft). In certain embodiments, the biopolymer portion of the corrosion inhibitor system is in an amount of from about 2.0% or 2.5% to about 8.5% by weight of the total concentrate composition. In certain embodiments, the biopolymer portion of the corrosion inhibitor system is in an amount of from about 2.0% to about 3.0% by weight of the total concentrate composition. In certain embodiments, the biopolymer portion of the corrosion inhibitor system is in an amount of from any of about 0.5%, 1.0%, 2.0%, 2.5%, 3.0%, 4.0% or 5.0% to any of about 1.0%, 2.0%, 2.5%, 3.0%, 4.0%, 5.0%, or 8.5% by weight of the total concentrate composition. Representative examples of biopolymers include xanthan gum, rhamsan gum, welan gum, diutan gum, and mixtures thereof. In certain embodiments, the biopolymer is xanthan gum in an amount disclosed herein for a biopolymer. In certain embodiments, the amount of xanthan gum is from about 2.0% to about 3.0% by weight of the total concentrate composition.
In addition to a biopolymer, the corrosion inhibitor system can comprise additional components. In certain embodiments, the corrosion inhibitor system further comprises anhydrous sodium molybdate, its dihydrate, or mixtures thereof. In certain embodiments, the amount of anhydrous sodium molybdate, its dihydrate, and mixtures thereof is from about 0.01% to about 2.0% by weight of the total concentrate concentration. In certain embodiments, the amount of anhydrous sodium molybdate, its dihydrate, mixtures thereof is from about 0.05% to about 0.3% by weight of the total concentrate concentration. In certain embodiments, the amount of anhydrous sodium molybdate, its dihydrate, and mixtures thereof is from any of about 0.01%, 0.05%, 0.1%, 0.2%, 0.3%, 0.4%, or 0.5% to any of about 0.05%, 0.1%, 0.2%, 0.3%, 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1.0%, 2.0% or 3.0% by weight of the total concentrate composition.
In certain embodiments, the corrosion inhibitor system can optionally comprise one or more components such as sodium silicofluoride (SSF), sodium thiosulfate (STS), and dimercaptothiadiazole (DMTD). However, in certain embodiments, these corrosion inhibitor components are not required. In certain embodiments, the corrosion inhibitor system does not contain one or more of sodium silicofluoride (SSF), sodium thiosulfate (STS), and dimercaptothiadiazole (DMTD). Likewise, in certain embodiments, a solution produced from a fire-retardant concentrate composition described herein may or may not contain one or more of sodium silicofluoride (SSF), sodium thiosulfate (STS), and dimercaptothiadiazole (DMTD).
In certain embodiments, the fire-retardant concentrate composition comprises additional components, for example, benzotriazole, tolyltriazole, sodium benzoate, mercaptobenzothiazole, or combinations thereof. In certain embodiments, the fire-retardant concentrate composition comprises a pigment or dye. In certain embodiments, the pigment or dye is a fluorescent pigment or dye. In certain embodiments, the pigment or dye is UV sensitive. In certain embodiments, the pigment or dye is formaldehyde-free. In certain embodiments, a fluorescent pigment or dye has a Lab color spacing of “L” in a range from about 34 to about 89, “a” in a range from about 18 to about 83 and “b” in a range from about −61 to about 56. The LAB color space model was developed by the International Commission of Illumination (CIE) and is one convention of describing colors. The model has a 3 axis system. The L* represents the lightness and is on the vertical axis. The “0” on bottom of the vertical axis indicates the absence of light. The maximum lightness is on the top “100”. The a* is on the horizontal axis indicating red (−a) to green (a+). The b* is on the horizontal axis indicating blue (−b) to yellow (+b). The center of the axis is neutral.
www.colourphil.co.uk/lab_lch_colour_space.shtml
Additional components can include one or more selected from the group consisting of an iron containing pigment, a titanium containing pigment, a fugitive pigment or dye, a flow conditioner (e.g., tricalcium phosphate or micronized silica), a surfactant, a foam controlling additive (e.g., PLURONIC® L-101), foam formers, biocides, and any combination thereof.
In certain embodiments, a fire-retardant composition is mixed with water to form an aqueous fire-retardant solution, such as in any ratio as described for fire-retardant solutions herein (the “prescribed ratio”). When reference is made to the corrosion rate of a metal, such as a magnesium alloy, aluminum, etc., the metal composition referred to is that tested in accordance with U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
In certain embodiments, the prescribed ratio of a fire-retardant is predetermined based on the performance of its fire-retardant solutions when tested in accordance with U.S.D.A. Forest Service Specification 5100-304c, ¶ 3.5.2 or 4.5. In certain embodiments, when a fire-retardant composition is mixed with water at the prescribed ratio, the resulting aqueous solution exhibits a magnesium alloy corrosion rate equal to or less than 4.0 milli-inches per year (mpy). In certain embodiments, when a fire-retardant composition is mixed with water at the prescribed ratio, the resulting aqueous solution exhibits a magnesium alloy corrosion rate equal to or less than 3.0 milli-inches per year. In certain embodiments, when a fire-retardant composition is mixed with water at the prescribed ratio, the resulting aqueous solution exhibits a magnesium alloy corrosion rate equal to or less than 2.0 milli-inches per year. In certain embodiments, when a fire-retardant composition is mixed with water at the prescribed ratio, the resulting aqueous solution exhibits a magnesium alloy corrosion rate equal to or less than 1.0 milli-inches per year. In certain embodiments, when a fire-retardant composition is mixed with water at the prescribed ratio, the resulting aqueous solution exhibits an aluminum corrosion rate equal to or less than 2.0 milli-inches. In certain embodiments, when a fire-retardant composition is mixed with water at the prescribed ratio, the resulting aqueous solution exhibits a mild steel corrosion rate equal to or less than 5.0 milli-inches per year. In certain embodiments, when a fire-retardant composition is mixed with water at the prescribed ratio, the resulting aqueous solution exhibits a brass corrosion rate equal to or less than 5.0 milli-inches per year. In certain embodiments, when a fire-retardant composition is mixed with water at the prescribed ratio, the resulting aqueous solution exhibits two or more of the above described corrosion rates for magnesium, aluminum, mild steel and/or brass.
In certain embodiments, when a fire-retardant composition is mixed with water at the prescribed ratio, the resulting aqueous solution meets one or more of the required criteria of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
In certain embodiments, when a fire-retardant composition is mixed with water at the prescribed ratio, the resulting aqueous solution meets one or more of the required criteria for corrosion and/or stability of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
In certain embodiments, when a fire-retardant composition is mixed with water at the prescribed ratio, the resulting aqueous solution meets all of the required criteria for corrosion of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
In certain embodiments, when a fire-retardant composition is mixed with water at the prescribed ratio, the resulting aqueous solution meets all of the required criteria for stability of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
In certain embodiments, when a fire-retardant composition is mixed with water at the prescribed ratio, the resulting aqueous solution meets all of the required criteria for corrosion and stability of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
In certain embodiments, when a fire-retardant composition is mixed with water at the prescribed ratio, the resulting aqueous solution meets all of the required criteria of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
Provided for herein are fire-retardant solutions prepared by mixing a fire-retardant concentrate composition, as described anywhere herein, with water to form an aqueous solution. In certain embodiments, a homogenous solution is formed. In certain embodiments, the water contains low levels of bacterial contamination that can impact viscosity and/or stability by consuming biopolymers. Thus, in certain embodiments, the water contains a biocide to prevent bacterial contamination. In certain embodiments, the solution comprises insoluble components. In certain embodiments, the ratio of concentrate to water is from about 0.9 pounds to about 1.14 pounds of concentrate per 1.0 gallon of water. In certain embodiments, the ratio of concentrate to water is from about 0.9 pounds to about 1.1 pounds of concentrate per 1.0 gallon of water. In certain embodiments, the ratio of concentrate to water is from any of about 0.5, 0.6, 0.7, 0.8, 0.9, or 1.0 pounds to any of about 0.9, 1.0, 1.1, 1.14, 1.2, 1.3, 1.4, or 1.5 pounds of concentrate per 1.0 gallon of water. In certain embodiments, the ratio of concentrate to water is from any of about 0.05, 0.06, 0.07, 0.08, 0.09, 0.10, 1.11, or 0.12 kilograms to any of about 0.10, 0.11, 0.12, 0.13, 0.14, 0.15, 0.16, 0.17, 0.18, 0.19, or 2.0 kilograms of concentrate per 1.0 liter of water.
These dilution levels result in a fire-retardant solution having a lower density in comparison to state of the art fire-retardant solutions with equivalent performance characteristics, which in turn, can either reduce the weight of a fully loaded aircraft or increase the volume that an aircraft is capable of carrying. This factor can reduce the hazards associated with aerial firefighting. Further, the mix or dilution rate of the concentrate can be predetermined by evaluation of its performance in retarding the rate of flame spread and fuel consumption.
In certain embodiments, a fire-retardant solution exhibits a magnesium alloy corrosion rate equal to or less than 4.0 milli-inches per year (mpy). In certain embodiments, a fire-retardant solution exhibits a magnesium alloy corrosion rate equal to or less than 3.0 milli-inches per year. In other embodiments, a fire-retardant solution exhibits a magnesium alloy corrosion rate equal to or less than 2.0 milli-inches per year. In certain embodiments, a fire-retardant solution exhibits an aluminum corrosion rate equal to or less than 2.0 milli-inches or less than 1.0 milli-inches per year. In certain embodiments, a fire-retardant solution exhibits a mild steel corrosion rate equal to or less than 5.0 milli-inches per year. In certain embodiments, a fire-retardant solution exhibits a brass corrosion rate equal to or less than 5.0 milli-inches per year. In certain embodiments, a fire-retardant solution exhibits two or more of the above described corrosion rates for magnesium, aluminum, mild steel and/or brass.
In certain embodiments, a fire-retardant solution meets one or more of the required criteria for of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
In certain embodiments, a fire-retardant solution meets one or more of the required criteria for corrosion and/or stability of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
In certain embodiments, a fire-retardant solution meets all of the required criteria for corrosion of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
In certain embodiments, a fire-retardant solution meets all of the required criteria for stability of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
In certain embodiments, a fire-retardant solution meets all of the required criteria for corrosion and stability of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
In certain embodiments, a fire-retardant solution meets all of the required criteria of U.S. Department of Agriculture, Forest Service, Specification Number 5100-304c, Long Term Retardant, Wildland Firefighting, June 2007, including all amendments.
In certain embodiments, the fire-retardant solution exhibits a viscosity in the range of from about 150 cPs to about 1500 cPs when measured in accordance with paragraph 4.6.3.1. of Specification 5100-304c.
The disclosed solutions also exhibit low aquatic toxicity. For example, in certain embodiments, a solution exhibits an aquatic toxicity (LC50) in the range of from about 180 milligrams per liter to about 2700 milligrams per liter. In certain embodiments, a solution exhibits an aquatic toxicity (LC50) greater than about 180, 200, 500, 1000, 2000, or 2500 milligrams per liter. In certain embodiments, a solution exhibits an aquatic toxicity (LC50) in the range of from any of about 180, 200, 500, 1000, 2000, or 2500 milligrams per liter to any of about 200, 500, 1000, 2000, 2500, or 2700 milligrams per liter.
In certain embodiments, a fire-retardant solution has a pH in the range of from about pH 4.0 or 5.0 to about pH 8.0. In certain embodiments, a fire-retardant solution has a pH in the range of from about pH 6.0 about pH 8.0. In certain embodiments, a fire-retardant solution has a pH in the range of from about pH 6.0 or 6.10 to about pH 7.80. In certain embodiments, a fire-retardant solution has a pH in the range of from about pH 6.0 or 6.10 to about pH 7.70. In certain embodiments, a fire-retardant solution has a pH in the range of from about pH 6.0 or 6.10 to about pH 7.60. In certain embodiments, a fire-retardant solution has a pH in the range of from about pH 6.0, 6.10 or 6.20 to about pH 7.60. In certain embodiments, a fire-retardant solution has a pH in the range of from about pH 6.20 to about pH 7.58. In certain embodiments, a fire-retardant solution has an acidic pH.
In certain embodiments, visibility of the applied solution is improved, allowing firefighting forces to draw an effective chemical fire barrier using less total solution.
Disclosed herein are methods of making a fire-retardant solution by mixing a fire-retardant concentrate composition described anywhere herein with water. In certain embodiments, a fire-retardant concentrate is added to water and mixed until a solution is obtained. In certain embodiments, the solution is a homogeneous solution. It is understood that the solution can include the suspension of water-insoluble components as well as water-soluble components. These are suspended in the solution dependent on the viscosity of the solution. In certain embodiments, free flowing powder and/or granules are sucked from a fluidized container into a water stream via use of an eductor mixer.
In certain embodiments, the ratio of concentrate to water is from about 0.9 pounds to about 1.14 pounds of concentrate per 1.0 gallon of water. In certain embodiments, the ratio of concentrate to water is from about 0.9 pounds to about 1.1 pounds of concentrate per 1.0 gallon of water. In certain embodiments, the ratio of concentrate to water is from any of about 0.5, 0.6, 0.7, 0.8, 0.9, or 1.0 pounds to any of about 0.9, 1.0, 1.1, 1.14, 1.2, or 1.3 pounds of concentrate per 1.0 gallon of water.
Disclosed herein are methods of combatting a wildfire by applying a fire-retardant solution described anywhere herein for the purpose of suppressing, containing, controlling, or extinguishing, etc., a wildfire. In certain embodiments, the fire-retardant solution is applied directly onto a flaming fuel. In other embodiments, the fire-retardant solution is applied indirectly, e.g., in front of or parallel to the moving fire front. The distance between the advancing fire and the retardant fire-break depends on the rate that the solution can be applied, the rate of spread of the moving fire front, and the presence or absence of a natural fuel break identified by changes in the geometry of the ground being threatened. In certain embodiments, the fire-retardant solution is applied from a ground platform such as a fire-engine. In certain embodiments, the fire-retardant solution is applied from an aerial platform such as a fixed-wing aircraft or a rotary-wing aircraft. In certain embodiments, the fire-retardant solution is applied from a rotary-wing aircraft such as a helicopter. In certain embodiments, the fire-retardant solution is applied from a helicopter bucket which is slung below the helicopter and in other embodiments the fire-retardant solution is contained within tanks mounted in or attached externally to the helicopter. In other embodiments, the fire retardant solution is applied from a mix of all of those listed vehicles or platforms. Obviously, the safety of the solution relative to aircraft corrosion and fouling of critical components must be greater when the solution is within or in contact with the aircraft.
For Tables 1A-1D:
** Magnesium corrosion is nearing the U.S. Forest Service corrosion maximum requirement.
† Corrosion values failed U.S. Forest Service corrosion requirements.
RT/T refers to room temperature (70° F./21° C.) storage and T indicates total submersion of the coupon in the solution and P indicates that the coupon was partially immersed.
RT/P refers to room temperature(70° F./21° C.) storage and P indicates 50% (partial) immersion of the coupon in the solution.
ET/T refers to elevated temperature (120° F./49° C.) storage and T indicates total submersion of the coupon in the solution.
ET/P refers to elevated temperature (120° F./49° C.) storage and P indicates 50% (partial) immersion of the coupon in the solution.
Based on the data presented in Tables 1A to 1D, a combination of xanthan gum and sodium molybdate provided a superior corrosion inhibitor system for MAP:DAP based fire-retardant formulations. In addition, xanthan gum thickens the retardant solution to a predetermined desirable level. The substitution of MAP for a portion of the DAP allows the preparation of fire-retardant solutions containing less total retardant concentrate and containing less ammonia per unit weight. Formulations containing the greatest amount of MAP with the ability to pass Forest Service requirements were considered the most advantageous. Certain xanthan gum thickened solutions were stable as determined by Forest Service testing when stored for one year.
For Tables 2A-2B:
† Corrosion values failed U.S. Forest Service corrosion requirements.
RT/T refers to room temperature (70° F./21° C.) storage and T indicates total submersion of the coupon in the solution.
RT/P refers to room temperature(70° F./21° C.) storage and P indicates 50% (partial) immersion of the coupon in the solution.
ET/T refers to elevated temperature (120° F./49° C.) storage and T indicates total submersion of the coupon in the solution.
ET/P refers to elevated temperature (120° F./49° C.) storage and P indicates 50% (partial) immersion of the coupon in the solution.
Based on the data presented in Tables 2A and 2B, solutions with sodium molybdate passed aluminum corrosion requirements. The maximum MAP concentration at which the magnesium corrosion requirement was met was between 45% and 50%, when the formulation was thickened with the amount of xanthan gum shown.
N/P Molar Ratio=1.1
Mix Ratio—1.03 pounds per gallon of water.
For Tables 3A to 3F:
* Heavy rusting above the surface.
† Corrosion values failed U.S. Forest Service corrosion requirements.
RT/T refers to room temperature (70° F./21° C.) storage and T indicates total submersion of the coupon in the solution.
RT/P refers to room temperature (70° F./21° C.) storage and P indicates 50% (partial) immersion of the coupon in the solution.
ET/T refers to elevated temperature (120° F./49° C.) storage and T indicates total submersion of the coupon in the solution.
ET/P refers to elevated temperature (120° F./49° C.) storage and P indicates 50% (partial) immersion of the coupon in the solution.
Mix Ratio—1.03 pounds per gallon of water.
For Tables 4A to 4E:
† Corrosion values failed U.S. Forest Service corrosion requirements.
RT/T refers to room temperature (70° F./21° C.) storage and T indicates total submersion of the coupon in the solution.
RT/P refers to room temperature (70° F./21° C.) storage and P indicates 50% (partial) immersion of the coupon in the solution.
ET/T refers to elevated temperature (120° F./49° C.) storage and T indicates total submersion of the coupon in the solution.
ET/P refers to elevated temperature (120° F./49° C.) storage and P indicates 50% (partial) immersion of the coupon in the solution.
† Corrosion values failed U.S. Forest Service corrosion requirements.
* This is a preferred fugitive. Other alternative such as pigment red 106 has the same function but not limited to these.
** This is a preferred fugitive. Other alternative such as Magenta PB PI-44/AST-A and Magenta PB PI-46/AST-A has the same function but not limited to these.
RT/T refers to room temperature (70° F./21° C.) storage and T indicates total submersion of the coupon in the solution.
RT/P refers to room temperature (70° F./21° C.) storage and P indicates 50% (partial) immersion of the coupon in the solution.
ET/T refers to elevated temperature (120° F./49° C.) storage and T indicates total submersion of the coupon in the solution.
ET/P refers to elevated temperature (120° F./49° C.) storage and P indicates 50% (partial) immersion of the coupon in the solution.
Based on the data presented in Tables 5A and 5B:
The breadth and scope of the present disclosure should not be limited by any of the above-described exemplary embodiments, but should be defined only in accordance with the following claims and their equivalents.
1All uniform corrosion rates shall be determined by 90-day weight loss tests. All uniform corrosion rates are the maximum allowable average of all replicates.
2Magnesium uniform corrosion tests shall be performed for performance information. Intergranular corrosion tests are not required on aluminum or magnesium.
3Intergranular corrosion tests shall be performed on aluminum and magnesium coupons; no intergranular corrosion is allowed.
4Intergranular corrosion tests shall be performed on aluminum coupons; no intergranular corrosion is allowed. Magnesium uniform corrosion tests shall be performed for performance information. Intergranular corrosion tests are not required on magnesium.
This application is a non-provisional U.S. Patent Application that claims the benefit of U.S. Provisional Patent Application No. 62/372,012, filed Aug. 8, 2016, the entirety of which is hereby incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| 62372012 | Aug 2016 | US |