Fire Retardant Formulations

Abstract

A fire-retardant formulation for styrene-containing polymers comprising tris(2,4,6-tribromophenoxy)-s-triazine (FR-245), antimony trioxide and polytetrafluoroethylene (PTFE), wherein the bromine concentration in said fire-retardant formulation is from about 9.0 to about 10.5 wt. %, said antimony trioxide concentration being lower than about 3.2 wt. %.

Description

FIELD OF THE INVENTION

The present invention relates to improved fire-retardant formulations. More specifically, the present invention relates to improved fire-retardant formulations for styrene polymers and more particularly for High Impact Polystyrene (HIPS) and Acrylonitrile-Butadiene-Styrene terpolymer (ABS).

BACKGROUND

Styrenic resins are widely used in many applications including those where fireproof materials are necessary. Such applications include for example TV cabinets, in which there is a need for the incorporation of fire-retardants (FR) in styrene-polymeric materials.

Traditional FRs for these applications include, enter alia, decabromodiphenyl oxide and more recently tris(2,4,6-tribromophenoxy)-s-triazine the latter known as FR-245. The advantages of FR-245 are good balance of properties, high level of mechanical properties, high processing heat stability, good light stability, high melt flow and no blooming. However, unlike formulations based on decabromodiphenyl oxide, the formulations based on FR-245 tend to induce long after glow time. This effect is enhanced when carbon black is added to the formulation. JP 11323064 discloses the incorporation of fire-retardant formulation comprising tris(2,4,6-tribromophenoxy)-s-triazine known as FR-245, tris(3-bromo-2,2(bromomethyl)propyl)phosphate known as FR-370, antimony trioxide (Sb₂O₃) and PTFE (polytetrafluoroethylene) in rubber reinforced polystyrene also known as HIPS, wherein the bromine content, the main component responsible for fire retardation, is between 9.5 and 11 wt. % and wherein antimony trioxide, serving as a synergist, is between 3.5 and 3.7 wt. %.

This formulation is claimed to successfully meet the requirement of UL-94 class V-0 according to the flammability tests, where five specimens are ignited, twice each, and the fulfillment of 5 requirements is necessary to pass a UL-94 V-0 standard, namely:

1. Maximum after flame time≦10 seconds (for each ignition).

2. Total after flame time of 10 ignitions less or equal to 50 seconds.

3. Maximum after flame+after glow time less or equal to 30 seconds.

4. None of the test specimens burns or glows up to the holding clamp.

5. No cotton ignition by dripping.

UL-94V is UL (Underwriter Laboratories) Standard for Safety for Tests for Parts in Devices and Appliances.

A fire-retardant formulation containing FR-245 with 11.5 wt. % Br, 0.08 wt. % PTFE and 3.5 wt. % antimony trioxide is also rated UL-94 V-0, but reducing the bromine content to 10.5 wt. % Br results in derating to UL-94 V-1 because of long afterglow time. JP 11323064 overcomes this problem by introducing FR-370 to the formulation, which effectively reduces that time, while keeping relatively low levels of bromine-based fire-retardant.

Although JP 11323064 states that incorporation of FR-370 in the formulation allows maintaining low levels of bromine, which enhances technical properties of articles incorporating it and leads to cost-effective FR formulations, the inventors of the present invention note that FR-370 is a very expensive material and its use in fire-retardant formulations offers a high-cost non-economical solution for reducing or eliminating the afterglow phenomenon and for achieving V-0 flammability test rating.

SUMMARY OF THE INVENTION

The applicants have surprisingly found that by lowering the concentration levels of antimony trioxide to certain ranges while maintaining low levels of bromine, a fire-retardant formulation that essentially meets the requirement UL-94 class V-0 standards is achieved without evoking the need for high-cost or other materials. In particular, it has also been found that even when incorporating additives to the formulation as carbon black pigment those concentration ranges of the respective components still allow to successfully pass the standard flammability tests.

It is therefore an object of the present invention to provide a fire-retardant formulation that essentially meets the requirement standard according to the flammability tests.

It is yet another object of the present invention to provide a pigmented fire-retardant formulation that essentially meets the requirement standard according to the flammability tests.

Still another object of the present invention is to provide a fire-retardant formulation with improved technical and mechanical properties.

Still another object of the present invention is to provide a fire-retardant formulation that is cost-effective.

Still anther object of the present invention is to provide a fire-retarded styrene-containing polymer for injection molding or extrusion essentially comprising said fire-retardant formulation.

Still another object of the present invention is to provide fire-retarded styrene-containing polymer that may be HIPS or ABS.

This and other objects of the invention will become apparent as the description proceeds.

DETAILED DESCRIPTION OF THE INVENTION

The present invention provides a fire-retardant formulation that meets the requirement UL-94 V-0 standard according to the flammability tests and which is also cost-effective.

According to the present invention the formulation comprises FR-245, antimony trioxide, PTFE and optionally carbon black pigment, in which the acceptable concentrations of bromine range between about 9.0 and about 10.5 wt. % and those of antimony trioxide range between about 1.8 and about 3.2 wt. %.

Styrene rubber reinforced polymers containing fire-retardant formulations (FR-HIPS) are often required to possess a black or gray color. This is achieved by the incorporation of carbon black, a preferred pigment, to these formulations. However, a side-effect of carbon black when introduced in a fire-retardant formulation is long period of time afterglow effect, where the formulation comprises essentially the same components having the same concentrations as disclosed in JP 11323064, excluding the presence of FR-370.

In addition to the polystyrenic polymer, halogen based fire retardant, antimony oxide, PTFE and the carbon black there can be present in the formulation conventional additives in their conventional amounts. Examples of such additives are: fillers, pigments, dyes, impact modifiers, UV stabilizers, antioxidants, processing aids, nucleating agents, lubricants and the like.

The flame retarded formulations may be shaped into the final object by processes that are well known to the person skilled in the art; non limiting examples of such processes are: injection molding, extrusion, press molding, vacuum forming, etc.

EXAMPLES

The present invention will now be described in more detail with Examples and Reference Examples.

Tables 1-3 below summarize the materials used for the preparation of the test samples as well as the methods and conditions for their preparation. Flammability was tested according to UL94V.

TABLE 1
Materials
TRADE NAME        GENERAL INFO
HIPS              Styron 472 ex Dow Chemical
ABS               Magnum 3404 ex Dow Chemical
Antimony trioxide ACC-BS ex Antraco
FR-245 ex DSBG    Tris(2,4,6-tribromophenoxy)-s-
                  triazine
F-3020 ex DSBG    Endcapped brominated epoxy
                  oligomer (MW 2,000)
FR-1210 ex DSBG   Decabromodiphenyl oxide
Carbon Black      PSB 183 ex Hubron
                  manufacturing division limited
PTFE              Hostaflon 2071 ex Dynon-fine
                  powder (500μ)
*Antimony trioxide is added as 80% concentrate in polystyrene carrier.
*Carbon black is added as 35% concentrate in polystyrene carrier.

Compounding

All formulations were prepared under the same conditions.

The components are weighed on Sartorius semi-analytical scales with consequent manual mixing in plastic bags. All the components are introduced into an extruder via K-SFS 24 gravimetric feeding system ex. K-Tron.

Compounding is performed in a co-rotating twin-screw extruder ZE25 ex Berstorff with L/D=32. The compounding conditions are presented in Table 2. The extruded strands are pelletized in pelletizer 750/3 ex Accrapak Systems Limited.

The obtained pellets are dried in a circulating air oven ex Heraeus Instruments at 75° C. for 4 hours.

TABLE 2
Compounding conditions
	PARAMETER	UNITS	Set values
	Feeding zone temperature (T1)	° C.	no heating
	T2	° C.	160
	T3	° C.	230
	T4	° C.	230
	T5	° C.	230
	T6	° C.	230
	T7	° C.	200
	T8	° C.	230
	T9	° C.	230
	Temperature of melt	° C.	230
	Screw speed	RPM	300

Injection Molding

Test specimens were prepared by injection molding in an Allrounder 500 150 ex. Arburg, All test specimens were prepared under the same conditions. The injection molding conditions are presented in Table 3.

TABLE 3
Injection molding conditions
	PARAMETER	UNITS	Set values
	T1 (Feeding zone)	° C.	180
	T2	° C.	200
	T3	° C.	230
	T4	° C.	230
	T5 (nozzle)	° C.	230
	Mold temperature	° C.	40
	Injection pressure	bar	500
	Holding pressure	bar	250
	Back pressure	bar	20
	Injection time	sec	0.1
	Holding time	sec	10.0
	Cooling time	sec	5.0
	Mold closing force	kN	500
	Filling volume (portion)	ccm	21
	Injection speed	ccm/sec	10

Conditioning

Prior to UL-94 testing test specimens are conditioned at 70° C. for 168 hours and at 23° C. for 168 hours.

Compositions and flammability test results are presented in Table 4 for HIPS compositions and in Table 5 for ABS compositions.

TABLE 4
HIPS compositions and flammability test results
		Reference	Reference	Reference	Reference	Reference	Reference	Reference	Reference	Reference
Components	Units	Example 1	example 2	example 3	example 4	example 5	example 6	example 7	example 8	example 9
HIPS Styron 472	%	82.5	81.5	84.4	84.5	83.4	79.2	78.2	81.5	81.6
FR-245	%						17.2	17.2	14.9	14.9
FR-1210	%	13.9	13.9	12.0	12.0	12.0
F-3020	%
Antimony trioxide	%	3.5	3.5	3.5	3.5	3.5	3.5	3.5	3.5	3.5
PTFE Hostaflon 2071	%	0.1	0.1	0.1		0.1	0.1	0.1	0.1
Carbon Black	%		1.0			1		1.0
Bromine calculated	%	11.5	11.5	10	10	10	11.5	11.5	10	10
Flammability UL-94V at 1.6 mm
Max flaming time	sec	2	1	2	4	1	2	1	2	3
Total flaming time	sec	10	9	10	17	10	11	7	12	11
Max after glow time	sec	12	0	0	0	11	20	36	31	0
Max after glow + after	sec	13	1	1	1	12	22	36	31	1
flame time
Specimens dripped	num	0	0	0	3	0	0	0	0	5
Cotton ignition	num	0	0	0	2	0	0	0	0	5
Sample burned up to	num	0	0	0	0	0	0	0	0	0
the holding clamps
Rating		V-0	V-0	V-0	V-2	V-0	V-0	V-1	V-1	V-2
		Reference	Reference	Reference	Reference	Reference	Reference
		example	example	example	example	example	example
Components	Units	10	11	12	13	14	15	Example 1	Example 2	Example 3
HIPS Styron 472	%	80.5	80.8	83.0	81.6	81.2	79.6	81.0	81.5	80.6
FR-245	%	14.9	14.9	14.9	14.9	14.9	10.4	14.9	14.9	10.4
FR-1210	%
F-3020	%						5.4			5.4
Antimony trioxide	%	3.5	3.2	1.0	2.5	2.5	3.5	3.0	2.5	2.5
PTFE Hostaflon 2071	%	0.1	0.1	0.1	0.02	0.4	0.1	0.1	0.1	0.1
Carbon Black	%	1	1.0	1.0	1.0	1.0	1.0	1.0	1.0	1.0
Bromine calculated	%	10	10	10	10	10	10	10	10	10
Flammability UL-94V at 1.6 mm
Max flaming time	sec	1	3	78	6	1	3	2	7	4
Total flaming time	sec	9	13	338	26	7	12	12	16	18
Max after glow time	sec	54	35	0	31	45	35	21	2	22
Max after glow + after	sec	55	37	78	33	46	38	22	2	24
flame time
Specimens dripped	num	0	0		3	0	0	0	0	0
Cotton ignition	num	0	0		3	0	0	0	0	0
Sample burned up to	num	0	0	4	0	0	0	0	0	0
the holding clamps
Rating		V-1	V-1	HB	V-2	V-1	V-1	V-0	V-0	V-0

Table 4 above summarizes several composition and flammability test results of prior art related fire-retardant formulations as well as of formulations relating to the present invention. From this table it is clearly seen that:

• • (a) Formulations (Reference Example-6) based on JP 11323064 pass successfully the V-0 flammability test, but introducing 1 wt. % carbon black pigment (Reference Example-7), results in derating to V-1 due to long afterglow time.
  • (b) In fire-retardant FR-1210 (decabromodiphenyl oxide) based formulations—Reference Examples 1-5—the first two formulations substantially having the same bromine, antimony trioxide and PTFE concentrations as in Reference Examples 6 and 7 pass V-0 tests, even when containing carbon black pigment (Reference Example 2). Reducing bromine content to 10 wt. % and then further elimination of PTFE from this formulation result in V-0 and V-2 rating, respectively (Reference Example 3 and Reference Example 4), the latter is due to burning drops ignited cotton effect. Addition of carbon black to Reference Example 3 does not derate the formulation and it passes V-0 tests (Reference Example 5). It should be noted that the antimony trioxide remains essentially unchanged in all those formulation variations.
  • (c) Reference Example 8, Reference Example 9, Reference Example 10 and Example 2 to Example 3 relate to FR-245 containing formulations having varying concentrations of the components Further reduction of FR-245 to 10 wt. % bromine while keeping the antimony trioxide concentration relatively high (Reference Example 8) results in derating to V-1. Omission of PTFE from this formulation (Reference Example 9) results in dripping with cotton ignition and V-2 rating. Further addition of carbon black to Reference Example 8 (Reference Example 10) results in long afterglow effect and a rating of V-1. However, reduction of antimony trioxide to 2.5 wt. % (Example 2) surprisingly improves flammability retardation and is rated V-0. Further reduction of antimony trioxide to 1 wt. % (Reference Example 12) results in total burning of the specimen up to the clamps and in a HB rating. The upper concentration limit of antimony trioxide is tested in Reference Example 11 vs. Example 1; at antimony trioxide concentration of 3.2 wt. % the formulation is rated V-1 because of long after glow time (Reference Example 11); at antimony trioxide concentration of 3.0 wt. % the formulation is rated V-0 (Example 1). The concentration limits of PTFE are tested in formulations Reference Example 13, 0.02 wt. %, and Reference Example 14, 0.4 wt. %. In the first an effect of burning drops ignited cotton leads to V-2 rating. The second is rated V-1 due to long afterglow time.

(d) The employment of both FR-245 and F-3020 (MBEO endcapped brominated epoxy resin) as the bromine fire-retardants, the first contributing about 7 wt. % and the second about 3 wt. % of the bromine content, leads to long afterglow time (Reference Example 15) when incorporating 3.5 wt. % antimony trioxide, i.e. V-1 rating, and to successful results (Example 3) when lowering antimony trioxide concentration to 2.5 wt. %, i.e. V-0. These two results are similar to the ones achieved for formulations containing only FR-245, i.e. Reference Example 10 and Example 2, and further stress the optimal relation between bromine fire-retardant and antimony trioxide synergist contents.

	TABLE 5
			Reference
	Components	Units	example 16	Example 4
ABS compositions and results of flammability results
	ABS Magnum 3404	%	80.0	81.0
	FR-245	%	14.9	14.9
	Antimony trioxide	%	4.0	3.0
	PTFE Hostaflon 2071	%	0.1	0.1
	Carbon Black	%	1.0	1.0
	Bromine calculated	%	10	10
Flammability UL-94V at 1.6 mm
	Max flaming time	Sec	5	7
	Total flaming time	Sec	16	29
	Max after glow time	Sec	36	21
	Max after glow + after	Sec	38	23
	flame time
	Specimens dripped	Num	0	0
	Cotton ignition	Num	0	0
	Sample burned up to the	Num	0	0
	holding clamps
	Rating		V-1	V-0

Table 5 demonstrates that the same effects, which are observed in HIPS formulations, are also applied in ABS based formulations.

HIPS and ABS containing fire-retardant formulations containing FR-245 or a combination of FR-245 and BEO's at low bromine content and with the incorporation of carbon black do not pass UL-94 V-0 because of long after glow time. It is surprisingly found that at low antimony trioxide concentrations it is possible to pass UL-94 V-0 and get economic cost-effective formulations with good mechanical, thermal and processing properties.

While examples of the invention have been described for purposes of illustration, it will be apparent that many modifications, variations and adaptations can be carried out by persons skilled in the art, without exceeding the scope of the claims.

Claims

1. A fire-retardant formulation for styrene-containing polymers comprising tris(2,4,6-tribromophenoxy)-s-triazine (FR-245), antimony trioxide and polytetrafluoroethylene (PTFE), wherein the bromine concentration in said fire-retardant formulation is from about 9.0 to about 10.5 wt. %, said antimony trioxide concentration being lower than about 3.2 wt. %.

2. A formulation according to claim 1, wherein the antimony trioxide concentration is from about 1.8 to about 3.2 wt. % and the PTFE concentration is from about 0.03 to about 0.2 wt. %.

3. The fire-retardant formulation of any one of claims 1 or 2, wherein the bromine concentration is about 10 wt. %, the antimony trioxide concentration is about 3.0 wt. %, and the PTFE concentration is about 0.1 wt. %.

4. The fire-retardant formulation of any one of claims 1 or 2, wherein the bromine concentration is about 10 wt. %, the antimony trioxide concentration is about 2.5 wt. %, and the PTFE concentration is about 0.1 wt. %.

5. A fire-retardant formulation according to claim 1, further comprising carbon black, wherein the bromine concentration in said fire-retardant formulation is from about 9.0 to about 10.5 wt. %, said antimony trioxide concentration being lower than about 3.2 wt. %.

6. The fire-retardant formulation of claim 5, wherein the carbon black concentration is from about 0.3 to about 2 wt. %.

7. The fire-retardant formulation of any one of claims 5 or 6, wherein the bromine concentration is about 10 wt. %, the antimony trioxide concentration is about 3.0 wt. %, the PTFE concentration is about 0.1 wt. % and the carbon black concentration is about 1.0 wt. %.

8. The fire-retardant formulation of any one of claims 5 or 6, wherein the bromine concentration is about 10 wt. %, the antimony trioxide concentration is about 2.5 wt. %, the PTFE concentration is about 0.1 wt. % and the carbon black concentration is about 1.0 wt. %.

9. The fire-retardant formulation according to any one of claims 1 to 8, further comprising brominated epoxy resin (BEO) or endcapped brominated epoxy resin (MBEO).

10. The fire-retardant formulation of claim 9, wherein said bromine of said BEO or MBEO is at least 3 wt. %.

11. Fire-retarded styrene-containing polymer comprising fire-retardant formulation for injection-molding or extrusion, wherein said fire-retardant formulation comprises tris(2,4,6-tribromophenoxy)-s-triazine (FR-245), antimony trioxide and polytetrafluoroethylene (PTFE) and optionally carbon black, wherein the bromine concentration in said fire-retardant formulation is from about 9.0 to about 10.5 wt. % and the antimony trioxide concentration lower than about 3.2 wt. %.

12. The polymer of claim 11, wherein the antimony trioxide concentration is from about 1.8 to about 3.2 wt. % and the PTFE concentration is from about 0.03 to about 0.2 wt. %.

13. The fire-retarded styrene-containing polymer of claim 12, wherein the fire-retardant formulation further comprises brominated epoxy resin (BEO).

14. The fire-retarded styrene-containing polymer of claim 13, wherein the bromine concentration of said BEO is about 3 wt. %.

15. A fire-retarded styrene-containing polymer according to any one of claims 11 to 14, wherein the carbon black concentration is from about 0.3 to about 2 wt. %.

16. A fire-retarded styrene-containing polymer according to claim 11, said polymer comprising a fire-retardant formulation for injection-molding or extrusion, said formulation comprising bromine in a concentration of about 10 wt. % essentially comprised in tris(2,4,6-tribromophenoxy)-s-triazine (FR-245), antimony trioxide in a concentration of about 3.0 wt. %, PTFE in a concentration of about 0.1 wt. % and carbon black in a concentration of about 1.0 wt. %.

17. A fire-retarded styrene-containing polymer according to claim 11, said polymer comprising a fire-retardant formulation for injection-molding or extrusion, said formulation comprising bromine in concentration of about 10 wt. % essentially comprised in tris(2,4,6-tribromophenoxy)-s-triazine (FR-245), antimony trioxide in a concentration of about 2.5 wt. %, PTFE in a concentration of about 0.1 wt. % and carbon black in a concentration of about 1.0 wt. %.

18. A fire-retarded styrene-containing polymer according to claim 11, said polymer comprising a fire-retardant formulation for injection-molding or extrusion, said formulation comprising bromine in a concentration of about 10 wt. % essentially comprised in tris(2,4,6-tribromophenoxy)-s-triazine (FR-245) and BEO, antimony trioxide in a concentration of about 2.5 wt. %, PTFE in a concentration of about 0.1 wt. % and carbon black in a concentration of about 1.0 wt. %.

19. A fire-retarded styrene-containing polymer according to any one of claims 11 to 18, wherein said polymer is high-impact polystyrene (HIPS).

20. A fire-retarded styrene-containing polymer according to any one of claims 11 to 18, wherein said polymer is acrylonitrile-butadiene-styrene polymer (ABS).

21. A method for upgrading fire-retardation in styrene-containing polymer, said polymer comprising a fire-retardant formulation, said fire-retardant formulation comprising tris(2,4,6-tribromophenoxy)-s-triazine (FR-245), antimony trioxide and polytetrafluoroethylene (PTFE) and optionally carbon black and brominated epoxy resin (BEO) or endcapped brominated epoxy resin (MBEO), wherein said upgrading comprises decreasing said antimony trioxide concentration in said fire-retardant formulation, to a level equal to or below 3.2 wt %.

22. A method according to claim 21, wherein the bromine concentration in the fire-retardant formulation is from about 9.0 to about 10.5 wt. %, the antimony trioxide concentration is from about 1.8 to about 3.2 wt. % and the PTFE concentration is from about 0.03 to 0.2 wt. %.

23. The method according to claim 21 or 22, wherein the bromine concentration from the BEO or MBEO is about 3 wt. %.

24. The method according to any one of claims 21 to 23, wherein the styrene-containing polymer is HIPS.

25. The method according to any one of claims 21 to 23, wherein the styrene-containing polymer is ABS.

26. A flame-retardant formulation for styrene-containing polymer, substantially as described and exemplified.

27. A flame-retarded styrene-containing polymer, substantially as described and exemplified.