Fire retardant jacket for tubing

Information

  • Patent Grant
  • 7367364
  • Patent Number
    7,367,364
  • Date Filed
    Friday, May 12, 2006
    18 years ago
  • Date Issued
    Tuesday, May 6, 2008
    16 years ago
Abstract
A tubing assembly including a conductive corrugated tubing including convolutions of peaks and valleys and a polymer jacket disposed along a length of said corrugated tubing, the polymer jacket including a fire retardant.
Description
BACKGROUND OF THE INVENTION

Corrugated tubing or metal hose provides an alternative to rigid piping systems as a conduit for transporting fluids such as natural gas. The corrugated tubing can be easily installed and is useful in many system applications. Corrugated tubing allows for simpler more cost-effective installation due to its uniquely flexible structure and relatively high strength. The same flexibility has inherent limitations. As the internal pressure of the working fluid inside the tubing is increased the corrugated tubing structure reacts to the pressure. The typical corrugated tubing structure begins to spread and expand along its length when the internal pressure overcomes the strength of the tubing material. The higher pressures of the working fluid cause the corrugations to expand. The corrugation expansion results in a distortion of the tubing out of its original shape and size.


In order to meet higher operating pressure ranges, conventional corrugated tubing may be sleeved with a wire braid. The braid is fixed at opposite ends of the corrugated tubing. The braid reinforces the corrugated tube structure thereby resisting the expansion of the corrugations when the internal pressure is increased. The braid is effective in the function of resisting the expansion of the corrugated tubing thereby increasing operational pressure capability. However, the braid covering the corrugated tubing outer diameter is subject to relative motion with the corrugated tubing that it covers. The tubing and the braid move relative to each other along the length of the corrugated tubing. In applications that plumb the corrugated tubing to mechanical equipment that create vibration translated to the tubing, the relative motion causes abrasion between the inside of the braid and the outer surface of the tubing. The abrasion between the tubing outer surface and the braid inner surface creates failure mechanisms that compromise the integrity of the corrugated tubing structure. The braid saws and rubs off the outer surface material of the corrugated tubing until the tubing pressure boundary fails and subsequently leaks the working fluid.


Another drawback to existing tubing is that the tubing is often contained within a jacket. Typically, the jacket is made from an insulative material. In the event that the piping is introduced to an electrical charge (e.g., from direct or indirect lightning), charge accumulates on the jacket and can burn through the jacket to the tubing resulting in a breach of the tubing.


SUMMARY OF THE INVENTION

An embodiment of the invention is a tubing assembly including conductive corrugated including convolutions of peaks and valleys and a polymer jacket disposed along a length of said corrugated tubing, the polymer jacket including a fire retardant.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is a side view, in partial cross-section, of a charge dissipating tubing assembly.





DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS


FIG. 1 is a side view, in partial cross-section, of a charge dissipating tubing assembly 10. The tubing assembly 10 includes tubing 12 and a conductive jacket 14. The tubing 12 may be annular, corrugated stainless steel tubing (CSST) for transporting fluids such as natural gas, liquids, etc. Alternatively, the tubing 12 may be helically wound tubing.


The jacket 14 is extruded over the tubing 12. The corrugated tubing 12 has an exterior surface and an interior surface. The interior surface is typically exposed to the working fluid. The corrugated tubing 12 comprises a structure that has varying diameters or convolutions that form peaks and valleys in alternating series along the length of the corrugated tubing 12. The exterior surface is used as the reference for the peak and valley as opposed to the interior surface. The peak consists of the convolution with the larger outside diameter and the valley consists of the convolution with the smaller outside diameter.


Conductive jacket 14 is disposed on the exterior surface of the corrugated tubing 12. The conductive jacket 14 may substantially fill the valleys and covers the peaks on the exterior surface. The conductive jacket 14 is disposed along the length of the corrugated tubing 12. The material makeup of the conductive jacket 14 has properties that resist forces that distort the material such as tension and shear forces. As a result, when the internal pressure of a working fluid increases and acts to spread apart the corrugated tubing 12 the conductive jacket 14 disposed in the valleys of exterior surface resists the forces that are created. The conductive jacket 14 inhibits the expansion or spreading of the corrugated tubing 12 such that the corrugated tubing 12 does not significantly distort either in the linear dimension or the diameter of the corrugated tubing 12. The conductive jacket 14 supports each convolution of the corrugated tubing 12. The material makeup of the conductive jacket 14 is also resilient and flexible. As the corrugated tubing 12 is bent and flexed along its length, the conductive jacket 14 bends and flexes with the corrugated tubing 12.


The thickness of the conductive jacket 14 can be varied to enhance resistance to tube expansion or to provide more or less flexibility to the corrugated tubing 12. A variety of pressure ratings can be met by changing the thickness of the conductive jacket 14. A direct relationship exists between the thickness of the conductive jacket 14 and the pressure rating of the corrugated tubing 12. Applying a conductive jacket 14 to the corrugated tubing 12 increases the pressure rating of the corrugated tubing 12 above the pressure rating of the corrugated tubing 12 without a conductive jacket 14. The conductive jacket 14 also increases the number of flex cycles required to create metal fatigue failure in the corrugated tubing 12 and attenuates vibration to reduce failure of corrugated tubing 12 due to vibration fatigue.


The conductive jacket 14 can be extruded into the corrugations of corrugated tubing 12. The use of other manufacturing processes can be employed to dispose the conductive jacket 14 onto the exterior surface of the corrugated tubing 12. In one embodiment, the conductive jacket 14 is driven into the valleys to substantially fill valleys and covers peaks. As the conductive jacket 14 is extruded it is substantially molten and flows down into the corrugations of the corrugated tubing 12. The molten conductive jacket 14 cools on the corrugated tubing 12. The molten material substantially fills the valleys and covers the peaks. In an alternate embodiment, a polymer conductive jacket 14 is extruded down into the corrugations and then cured (e.g., through heat).


The conductive jacket 14 may be applied so that the conductive jacket 14 bonds to substantially the entire exterior surface of the corrugated tubing. The optional bonding of the conductive jacket 14 to the exterior surface can be mechanical bonding or chemical bonding such that conductive jacket 14 substantially adheres to the exterior surface of the corrugated tubing 12. Also, by being located in the valleys, the conductive jacket 14 mechanically blocks the deformation of the corrugated tubing 12 as a result of the material properties of the conductive jacket 14. With the conductive jacket 14 applied such that there is an adhesion between the conductive jacket 14 and the surface of the corrugated tubing 12, there is no relative motion between the conductive jacket 14 and the surface of the corrugated tubing 12. Having eliminated the relative motion between the conductive jacket 14 and the exterior surface, the abrasive wear mechanism is substantially eliminated while still providing pressure reinforcement.


In an alternate embodiment, the conductive jacket 14 is extruded over the corrugated tubing 12, but not driven into the valleys of the corrugated tubing. The conductive jacket 14 covers the peaks of the corrugated tubing 12 but is not driven into the valleys.


Conductive jacket 14 may be made from a conductive, thermoplastic polymer such as a thermoplastic polyether-based polyurethane compound. Other conductive thermoplastics may be used for jacket 14, and the invention is not limited to polyurethane. The polymer preferably has the following properties.











TABLE A





Property
Method
Value







Tensile Strength
ASTM D638
about 4000 psi Minimum


Elongation
ASTM D638
about 300% Minimum


Flexural Modulus
ASTM D790
about 25,000 psi Minimum


Volume Resistivity
ASTM D257
about 7 × 10{circumflex over ( )}4 ohm-cm Maximum









In an alternate embodiment, the conductive jacket is made from a thermoplastic, polyethylene having characteristics identified in Table A. The polyethylene jacket may bond to the corrugated tubing 12 as described above.


At one or both ends of the tubing assembly are fittings 16. The fittings 16 may be existing CSST fittings such as those disclosed in U.S. Pat. Nos. 5,799,989, 6,079,749, 6,276,728, the entire contents of these patents being incorporated herein by reference. Preferably the end fittings are made from metals (e.g., brass).


Since the jacket 14 is made from a conductive thermoplastic, charge accumulated on jacket 14 (e.g., due to direct or indirect lightning strike) is conducted through the jacket 14 to the tubing 12 and then to the end fittings 16 and through components connected to fittings 16. Thus, the tubing 12 is not damaged by a build up of charge on a non-conductive jacket.


The tubing assembly may be used in a number of applications including residential or commercial, interior or exterior, and aboveground or underground installations where there is a likelihood for lightning strikes (direct or indirect) or other causes of electrical charge accumulation.


In alternate embodiments, one or more fire retardants may be incorporated into the polymer jacket 14, in addition to the conductive materials. The fire retardant may allow the tubing assembly to meet or exceed various standards. For example, embodiments of the invention include fire retardants in an amount sufficient for the tubing assembly to pass UL723/ASTM E84 testing for <50 smoke density and <25 flame spread and rated for 1, 2, and 4 hour UL Through Penetration Firestop System Classifications without jacket removal.


Table B below illustrates exemplary fire retardant types that may be incorporated into polymer jacket 14 and percentages of the fire retardant by weight.












TABLE B







Fire Retardants
% by weight









Nitrogen/Phosphorus
about 40-about 60



Brominated
about 10-about 20



Chlorinated
about 30-about 50



Magnesium Hydroxide
about 40-about 60



Aluminum Trihydrate
about 40-about 60










Embodiments of the invention including the fire retardant result in a polymer jacket having the physical properties in Table C below.









TABLE C





Mechanical Properties


















Tensile strength
about 1500 PSI minimum



Elongation
about 200% minimum



Flexural Modulus
about 50,000 PSI minimum










While preferred embodiments have been shown and described, various modifications and substitutions may be made thereto without departing from the spirit and scope of the invention. Accordingly, it is to be understood that the present invention has been described by way of illustration and not limitation.

Claims
  • 1. A tubing assembly comprising: conductive, metal corrugated tubing including convolutions of peaks and valleys;a conductive polymer jacket disposed along a length of said corrugated tubing, said conductive polymer jacket forming a conductive path from the jacket to the corrugated tubing;the conductive polymer jacket has a volume resistively sufficient conduct charge from an outer surface of the polymer jacket through the conductive polymer jacket to the conductive, metal corrugated tubing;the conductive polymer jacket including a fire retardant;wherein the polymer jacket has a minimum tensile strength of about 1500 psi, a minimum elongation of about 200%, and a minimum flexural modulus of about 50,000.
  • 2. The tubing assembly of claim 1 wherein: said fire retardant is present in an amount sufficient for the tubing assembly to pass UL723/ASTM E84 testing for >50 smoke density and >25 flame spread and rated for 1, 2, and 4 hour UL Through Penetration Firestop System Classifications.
  • 3. The tubing assembly of claim 1 wherein: said fire retardant is nitrogen/phosphorus type present in the polymer jacket in about 40% to about 60% by weight.
  • 4. The tubing assembly of claim 1 wherein: said fire retardant is brominated type present in the polymer jacket in about 10% to about 20% by weight.
  • 5. The tubing assembly of claim 1 wherein: said fire retardant is chlorinated type present in the polymer jacket in about 30% to about 50% by weight.
  • 6. The tubing assembly of claim 1 wherein: said fire retardant is magnesium hydroxide type present in the polymer jacket in about 40% to about 60% by weight.
  • 7. The tubing assembly of claim 1 wherein: said fire retardant is aluminum trihydrate type present in the polymer jacket in about 40% to about 60% by weight.
  • 8. The tubing assembly of claim 1 wherein: said corrugated tubing is annular.
  • 9. The tubing assembly of claim 1 wherein: said corrugated tubing is helical.
  • 10. The tubing assembly of claim 1 further comprising: a fitting coupled to said corrugated tubing at an end thereof.
  • 11. A tubing assembly comprising: conductive, metal corrugated tubing for transporting fluids under pressure, the tubing including convolutions of peaks and valleys;a conductive polymer jacket disposed along a length of said corrugated tubing, the conductive polymer jacket forming a conductive path from the jacket to the corrugated tubing;wherein the polymer jacket has a minimum tensile strength of about 4000 psi, a minimum elongation of about 300%, a minimum flexural modulus of about 25,000 psi and a maximum volume resistivity of about 7×10^4 ohm-cm.
CROSS REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of U.S. patent application Ser. No. 10/820,531, filed Apr. 7, 2004, now U.S. Pat. No. 7,044,167 the entire contents of which are incorporated herein by reference, which claims the benefit of U.S. provisional patent application Ser. No. 60/461,085, filed Apr. 8, 2003, then entire contents of which are incorporated herein by reference.

US Referenced Citations (13)
Number Name Date Kind
3311133 Kinander Mar 1967 A
4147185 Hines Apr 1979 A
4326561 Kutnyak Apr 1982 A
4334121 Kutnyak Jun 1982 A
4800351 Rampalli et al. Jan 1989 A
5011880 Cornibert et al. Apr 1991 A
5284184 Noone et al. Feb 1994 A
5474602 Brown et al. Dec 1995 A
6404971 Mehl Jun 2002 B2
6584959 Stieler Jul 2003 B2
7044167 Rivest May 2006 B2
20020117226 Malcarne, Jr. Aug 2002 A1
20040190841 Anderson et al. Sep 2004 A1
Related Publications (1)
Number Date Country
20060254662 A1 Nov 2006 US
Provisional Applications (1)
Number Date Country
60461085 Apr 2003 US
Continuation in Parts (1)
Number Date Country
Parent 10820531 Apr 2004 US
Child 11382960 US