Patent Application
20060029898
This application claims benefit of priority to Japanese Patent Application No. 2004-228649, filed on Aug. 4, 2004, PCT Application No. PCT/JP2005/001264, filed on Jan. 28, 2005, and PCT Application No. PCT/JP2005/002073, filed on Feb. 10, 2005.
The contents of those Applications are incorporated herein by reference in their entirety.
1. Field of the Invention
The present invention relates to: a firing furnace that is used for manufacturing a honeycomb structural body made of ceramics, a ceramic material and the like; a porous ceramic member manufacturing method using the same; and a porous ceramic member manufactured by the manufacturing method.
2. Discussion of the Background
There have been proposed various exhaust gas purifying honeycomb filters and catalyst supporting members which are used for purifying exhaust gases discharged from internal combustion engines of vehicles such as a bus, a truck and the like, construction machines and the like.
With respect to the exhaust gas purifying honeycomb filters and the like, there has been used a honeycomb structural body which is constituted by a non-oxide based ceramic porous body such as silicon carbide and has a superior heat resistance.
Conventionally, for example, JP-A 2001-48657 and JP-A 63-302291 have disclosed firing furnaces used for manufacturing non-oxide based ceramic members of this type.
The firing furnace to be used for manufacturing such non-oxide ceramic members is provided with a heater and the like in the furnace and a heat insulating layer mainly made of carbon.
In the case where a porous ceramic member made of silicon carbide is manufactured by using the above-mentioned firing furnace, since a formed body after a degreasing process is heated and fired at a high temperature of 1400° C. or more, gases including silicon carbide, silicon, SiO gases and the like are discharged into an ambient atmosphere inside the firing furnace, and these gases react with carbon members inside the firing furnace to be converted into silicon carbide and the like.
When the carbon members are converted into silicon carbide, there arises a difference in physical property such as thermal expansion coefficient between a surface layer of the heat insulating layer made of silicon carbide and an inner layer made of carbon. Thus, warping tends to occur in the heat insulating layer. Moreover, in combination with the conversion into silicon carbide and the like, reaction of carbon with oxygen remaining inside the furnace or with oxygen and the like generated from the formed body causes corrosion in the heat insulating layer.
When warping and corrosion occur in the heat insulating layer, the heat insulating performance is lowered, or separation or the like occurs in the heat insulating layer, making the firing furnace unable to function as a furnace; consequently, the heat insulating layer needs to be exchanged. However, changing the heat insulating layer requires high costs, resulting in a problem of high manufacturing costs.
Moreover, even if the heat insulating layer does not need to be changed, an efficient heating process is no longer available and firing costs increase when the heat insulating property of the firing furnace is deteriorated.
The contents of Japanese Patent Laid-Open Publication No. 2001-48657 and Japanese Patent Laid-Open Publication No. 1988-302291 are incorporated herein by reference in their entirety.
A first aspect of the present invention is related to a firing furnace comprising: a muffle formed so as to ensure a space for housing a formed body to be fired; a member that constitutes a heat generator and is placed on and/or around the muffle; and a heat insulating layer that contains the muffle and the heat generator inside thereof. Herein, a carbon-natured sheet is placed in the vicinity of corner portions of an inner face of the heat insulating layer.
In the firing furnace according to the first aspect of the present invention, the carbon-natured sheet may be placed on inner upper and lower faces of the heat insulating layer, may be placed on inner side faces of the heat insulating layer, or may be placed on entire inner faces of the heat insulating layer. Moreover, the carbon-natured sheet is desirably made of a graphite sheet, a carbon fiber composite (C/C composite) or a carbon cloth.
In the firing furnace according to the first aspect of the present invention, the carbon-natured sheet is desirably secured to an inner face of the heat insulating layer by using an adhesive (in particular, an inorganic adhesive) or a combining member. In the case where the carbon-natured sheet is secured to the inner face of the heat insulating layer by using the combining member, the combining member desirably has a density of at least about 2 pcs/m2 and at most about 100 pcs/m2 per unit area.
A second aspect of the present invention is related to a firing furnace comprising: a muffle formed so as to ensure a space for housing a formed body to be fired; a member that constitutes a heat generator and is placed on and/or around the muffle; and a heat insulating layer that contains the muffle and the heat generator inside thereof. Herein, the heat insulating layer is secured to a heat insulating layer attaching-enclosing member that is located on the periphery of the heat insulating layer by using a combining member.
In the firing furnace according to the second aspect of the present invention, the combining member desirably has a density of at least about 4 pcs/m2 and at most about 200 pcs/m2 per unit area.
A third aspect of the present invention is related to a firing furnace comprising: a muffle formed so as to ensure a space for housing a formed body to be fired; a member that constitutes a heat generator and is placed on and/or around the muffle; and a heat insulating layer that contains the muffle and the heat generator inside thereof. Herein, the heat insulating layer is divided into a plurality of heat insulating layers, while a reinforcing member that combines and reinforces the divided insulating layers arranged therein.
In the firing furnace according to the third aspect of the present invention, a carbon-natured sheet may be placed in the vicinity of corner portions of an inner face of the heat insulating layer, may be placed on inner upper and lower faces of the heat insulating layer, may be placed on inner side faces of the heat insulating layer, or may be placed on entire inner faces of the heat insulating layer. The reinforcing member is desirably made of a carbon fiber composite or graphite. Moreover, the carbon-natured sheet is desirably made of a graphite sheet, a carbon fiber composite (C/C composite) or a carbon cloth.
In the firing furnace according to any one of the first to third aspects of the present invention, the member that constitutes the heat generator is desirably a heater or a muffle.
A fourth aspect of the present invention is related to a porous ceramic member manufacturing method, upon firing a formed body to form a porous ceramic member, said method using a firing furnace that comprises: a muffle formed so as to ensure a space for housing the formed body to be fired; a member that constitutes a heat generator and is placed on and/or around the muffle; and a heat insulating layer that contains the muffle and the heat generator inside thereof. Herein, a carbon-natured sheet is placed in the vicinity of corner portions of an inner face of the heat insulating layer.
In the porous ceramic member manufacturing method according to the fourth aspect of the present invention, the carbon-natured sheet of the firing furnace may be placed on inner upper and lower faces of the heat insulating layer, may be placed on inner side faces of the heat insulating layer, or may be placed on entire inner faces of the heat insulating layer. Moreover, the carbon-natured sheet is desirably made of a graphite sheet, a carbon fiber composite (C/C composite) or a carbon cloth.
In the porous ceramic member manufacturing method according to the fourth aspect of the present invention, the carbon-natured sheet of the firing furnace is desirably secured to an inner face of the heat insulating layer by using an adhesive (in particular, an inorganic adhesive) or a combining member. In the case where the carbon-natured sheet is secured to the inner face of the heat insulating layer by using the combining member, the combining member desirably has a density of at least about 2 pcs/m2 and at most about 100 pcs/m2 per unit area.
A fifth aspect of the present invention is related to a porous ceramic member manufacturing method, upon firing a formed body to form a porous ceramic member, the method using a firing furnace that comprises: a muffle formed so as to ensure a space for housing a formed body to be fired; a member that constitutes a heat generator and is placed on and/or around the muffle; and a heat insulating layer that contains the muffle and the heat generator inside thereof. Herein, the heat insulating layer is secured to a heat insulating layer attaching-enclosing member that is located on the periphery of the heat insulating layer by using a combining member.
In the porous ceramic member manufacturing method according to the fifth aspect of the present invention, the combining member of the firing furnace desirably has a density of at least about 4 pcs/m2 and at most about 200 pcs/m2 per unit area.
A sixth aspect of the present invention is related to a porous ceramic member manufacturing method, upon firing a formed body to form a porous ceramic member, said method using a firing furnace that comprises: a muffle formed so as to ensure a space for housing the formed body to be fired; a member that constitutes a heat generator and is placed on and/or around the muffle and a heat insulating layer that contains the muffle and the heat generator inside thereof. Herein, the heat insulating layer is divided into a plurality of heat insulating layers, while a reinforcing member that combines and reinforces the divided insulating layers is arranged therein.
In the porous ceramic member manufacturing method according to the sixth aspect of the present invention, a carbon-natured sheet of the firing furnace may be placed at least in the vicinity of corner portions of an inner face of the heat insulating layer, may be placed on inner upper and lower faces of the heat insulating layer, may be placed on inner side faces of the heat insulating layer, or may be placed on entire inner faces of the heat insulating layer. The reinforcing member is desirably made of a carbon fiber composite or graphite. Moreover, the carbon-natured sheet is desirably made of a graphite sheet, a carbon fiber composite (C/C composite) or a carbon cloth.
In the porous ceramic member manufacturing method according to any one of the fourth to sixth aspects of the present invention, the member that constitutes the heat generator is a heater or a muffle.
A seventh aspect of the present invention is related to a porous ceramic member manufactured by firing a formed body, wherein the porous ceramic member is manufactured by, upon firing the formed body, using a firing furnace that comprises: a muffle formed so as to ensure a space for housing the formed body to be fired; a member that constitutes a heat generator and is placed on and/or around the muffle; and a heat insulating layer that contains the muffle and the heat generator inside thereof, in which a carbon-natured sheet is placed in the vicinity of corner portions of an inner face of the heat insulating layer.
An eighth aspect of the present invention is related to a porous ceramic member manufactured by firing a formed body, wherein the porous ceramic member is manufactured by, upon firing the formed body, using a firing furnace that comprises: a muffle formed so as to ensure a space for housing the formed body to be fired; a member that constitutes a heat generator and is placed on and/or around the muffle; and a heat insulating layer that contains the muffle and the heat generator inside thereof, in which the heat insulating layer is secured to a heat insulating layer attaching-enclosing member that is located on the periphery of the heat insulating layer by using a combining member.
A ninth aspect of the present invention is related to a porous ceramic member manufactured by firing a formed body, wherein the porous ceramic member is manufactured by, upon firing the formed body, using a firing furnace that comprises: a muffle formed so as to ensure a space for housing the formed body to be fired; a member that constitutes a heat generator and is placed on and/or around the muffle; and a heat insulating layer that contains the muffle and the heat generator inside thereof, in which the heat insulating layer is divided into a plurality of heat insulating layers while a reinforcing member that combines and reinforces the divided insulating layers is arranged therein.
According to the first aspect of the present invention, a firing furnace comprises: a muffle formed so as to ensure a space for housing a formed body to be fired; a member that constitutes a heat generator and is placed on and/or around the muffle; and a heat insulating layer that contains the muffle and the heat generator inside thereof. Herein, a carbon-natured sheet is placed in the vicinity of corner portions of an inner face of the heat insulating layer.
According to a second aspect of the present invention, a firing furnace comprises: a muffle formed so as to ensure a space for housing a formed body to be fired; a member that constitutes a heat generator and is placed on and/or around the muffle; and a heat insulating layer that contains the muffle and the heat generator inside thereof. Herein, the heat insulating layer is secured to a heat insulating layer attaching-enclosing member that is located on the periphery of the heat insulating layer by using a combining member.
The first aspect of the present invention does not have the limitation that the heat insulating layer is secured to the heat insulating layer attaching-enclosing member that is located on the periphery of the heat insulating layer by using the combining member. In contrast, the second aspect of the present invention does not have the limitation that the carbon-natured sheet is placed in the vicinity of the corner portions of the inner face of the heat insulating layer. Thus, the respective aspects of the present invention are different from each other in these points. However, the other members are formed in the same manner. Accordingly, the explanation will be given of both of the firing furnace according to the first aspect of the present invention and the firing furnace according to the second aspect of the present invention.
This firing furnace 10 comprises: a muffle 11 formed so as to ensure a space for housing a formed body to be fired; a heater 12 that constitutes a heat generator placed around the muffle 11; and a heat insulating layer 13 (13X, 13Y) that contains the muffle 11 and the heater 12 inside thereof. A furnace wall 14 made of metal is formed on the outermost side so as to be separated from the ambient atmosphere. The furnace wall 14 may be constituted by a cooling jacket. In other words, the furnace wall 14 may be formed by a metal member or the like, and also have a double structure, with water allowed to flow the inside thereof, so that the temperature of the furnace wall 14 is maintained within a predetermined range.
The entire floor portion of the muffle 11 is supported by a supporting member (not shown) so that a supporting base (cart) 8 on which a laminated body of jigs for firing 15 in which formed bodies 9 to be fired are placed is allowed to pass. Heaters 12 made of graphite or the like are placed on the upper and lower portions of the muffle 11. The heaters 12 are connected to an outside power supply (not shown) through terminals 18.
A heat insulating layer 13 (13X, 13Y) constituted by three layers, that is, carbon members 13a, 13b and ceramic fibers 13c that are successively laminated in this order from the inner side is further formed outside the heater 12. A carbon-natured sheet 16 is placed on inside end portions (in the vicinity of corner portions) of the upper and lower heat insulating layers 13X. The heat insulating layer 13 on which this carbon-natured sheet 16 has been placed is secured to a heat insulating layer attaching-enclosing member 19 placed on the periphery of the heat insulating layer 13 through bolts 17a and nuts 17b made of carbon, which serve as combining members.
In
The inner surface of the heat insulating layer 13 is covered with the carbon-natured sheet 16 because of the following reasons. In particular, in the case where a porous ceramic member made of silicon carbide is manufactured, since a carbon member 13a located on the inner side is mainly made of carbon fibers, an inside portion close to the formed body is converted into silicon carbide due to silicon carbide, silicon, SiO gas and the like generated upon firing. When carbon has been converted into silicon carbide, there arises a difference in physical property such as thermal expansion coefficient between the surface layer made of silicon carbide and the inner layer made of carbon of the carbon member 13a constituting the heat insulating layer 13, so that warping is caused in the heat insulating layer. Therefore, in order to prevent the occurrence of warping (reaction) in the heat insulating layer due to the above-mentioned reaction, the inner surface thereof is covered with the carbon-natured sheet 16.
As shown in
The carbon-natured sheet 16 may be bonded to the inner surface of the heat insulating layer 13 by using an adhesive or the like; however, as shown in
In the firing furnace having the above-mentioned structure, upon manufacturing porous ceramic members such as oxide ceramics, carbide ceramics other than silicon carbide, nitride ceramics and the like, it is also possible to prevent the warping of the heat insulating layer due to changes in physical properties such as thermal expansion coefficient and the like.
Here, in the firing furnace 10 shown in
This firing furnace 10 is a continuous firing furnace in which the jig for firing 15 is gradually heated to a high temperature during the passage through it, and after having reached the highest temperature, the temperature is gradually lowered. For this reason, normally, for example, the length is desirably set to 10 m or more. Therefore, the length in the depth (length direction) of the heat insulating layer 13 is made considerably longer in comparison with the dimension of the cross section shown in
As shown in
Here, the firing furnace may partially have an area having no heat insulating layer 13 in the length direction thereof. In this case, in the area having the heat insulating layer 13, the carbon sheet is placed on the inner face of the heat insulating layer in the mode as described above. However, in order to prevent SiO and the like generated from a formed body from scattering toward the furnace wall and the like, the carbon sheet may also be placed on the portion having no insulating layer 13 in the above-mentioned mode.
In the firing furnace 10 shown in
FIGS. 3 to 7 are cross-sectional views that schematically show states where carbon sheets are placed on heat insulating layers that form the respective firing furnaces, and portions other than the heat insulating layer and the peripheral portion thereof are not shown; however, as shown in the figures, the modes of the insulating layers and the shapes and the attaching modes of the carbon sheets are different from each other.
In heat insulating layers 63 (63X, 63Y) shown in
In
In heat insulating layers 13 (13X, 13Y) shown in
Since heat insulating layers 13 (13X, 13Y) shown in
Heat insulating layers 63 (63X, 63Y) shown in
Heat insulating layers 63 (63X, 63Y) shown in
As described above, upon placing a carbon sheet, since warping tends to occur in portions of those heat insulating layers that are not extended to the end portions among heat insulating layers, the occurrence of warping and the like in the heat insulating layers can be prevented by placing carbon sheets and/or fixing members at least in the vicinity of the corner portions of the heat insulating layers that are not extended to the end portions. In this case, in order to reduce corrosion in the heat insulating layers, greater area of the carbon sheet is more preferable, and, for example, the carbon sheets may be placed on the entire upper and lower inner faces, may be placed on the entire right and left inner faces of the heat insulating layers, or may be placed on the entire inner faces of the heat insulating layers.
The carbon-natured sheet refers to a sheet-shaped material mainly composed of carbon, and the sheet-shaped material is desirably made of a graphite sheet, a carbon fiber composite (C/C composite) or a carbon cloth.
The graphite sheet refers to a sheet mainly composed of graphite particles, and the density thereof is preferably at least about 0.1 g/cm3 and at most about 5 g/cm3. Moreover, the graphite sheet desirably has a thickness of at least about 0.05 mm and at most about 5 mm. In the case where a graphite sheet is placed in corner portions of the inner faces of heat insulating layers as shown in
The carbon fiber composite (C/C composite) refers to a composite of carbon particles and carbon fibers, and the bulk density thereof is preferably at least about 0.5 g/cm3 and at most about 5 g/cm3. Moreover, the thickness of the C/C composite is desirably at least about 0.5 mm and at most about 5 mm, and the width of a sheet of C/C composite is preferably at least about 5% and at most about 50% with respect to the width L (mm) of the heat insulating layers on the upper and lower sides, shown in
The carbon cloth refers to a cloth formed by paper-making process or weaving process using carbon fibers. In the case of the product formed by paper-making process, the carbon fibers are bonded with one another through an inorganic bonding material or the like and formed into a sheet shape. The carbon cloth preferably has a density of at least about 0.05 g/cm3 and at most about 5 g/cm3, and desirably has a thickness of at least about 0.1 mm and at most about 5 mm. The width of a carbon cloth is preferably at least about 5% and at most about 50% with respect to the width L (mm) of the heat insulating layers 13 on the upper and lower sides, shown in
In the case where combining members such as bolts, nuts and the like are used, the density of the combining members per unit area is desirably at least about 2 pcs/m2 and at most about 100 pcs/m2.
In the case where the density of the combining members per unit area is at least about 2 pcs/m2 and at most about 100 pcs/m2, the surface of the heat insulating layers can be firmly covered with the carbon-natured sheet. Thus, silicon and the like do not enter the insulating layers through gaps to cause a reaction. Further, the number of the combining members is small and the cost can be reduced.
The lower limit value of the density of the combining members per unit area is desirably set to about 4 pcs/m2, and the upper limit value thereof is desirably set to about 40 pcs/m2.
Although the firing furnace 10 shown in
The ambient atmosphere of the firing furnace 10 is desirably prepared as an inert gas atmosphere, and more desirably prepared as an ambient atmosphere such as an argon gas atmosphere, a nitrogen gas and the like.
Normally, as shown in
The firing furnace 10 has a structure that heaters 12 are arranged above and below the muffle 11 with a predetermined gap, and the jig for firing 15 is gradually heated to a high temperature by the heaters 12 during the passage through it, and after having reached the highest temperature, the temperature is gradually lowered. Thus, the supporting base 8 on which the laminated body of the jigs for firing 15 is placed is continuously transported from an inlet into the firing furnace 10, and after having been subjected to the sintering process, the jigs for firing 15 the temperature of which is lowered are transported from an outlet to manufacture a porous ceramic member.
In the firing furnace 10 shown in
The combining members desirably have a density of at least about 4 pcs/m2 and at most about 200 pcs/m2 per unit area.
In the case where the density of the combining members per unit area is at least about 4 pcs/m2 and at most about 200 pcs/m2, the heat insulating layer 13 can be firmly secured; thus, warping, damages and the like hardly occur. Further, the number of combining members is small and the cost can be reduced.
The lower limit value of the density of the combining members per unit area is more desirably set to about 8 pcs/m2, and the upper limit value thereof is more desirably set to about 80 pcs/m2.
In the conventional firing furnace, a portion at which warping tends to occur due to a conversion of carbon members into silicon carbide is mainly located at a corner portion of the heat insulating layer. In the firing furnace of the first aspect of the present invention, since a carbon-natured sheet is placed in the vicinity of corner portions of an inner face of the heat insulating layer, the corner portion of the heat insulating layer is protected and made less susceptible to a reaction and free from occurrence of warping and corrosion; thus, it becomes possible to eliminate the necessity of exchanging members forming the heat insulating layer for a long period and, consequently, to provide a firing furnace which is excellent in durability and heat efficiency.
According to the firing furnace of the second aspect of the present invention, since the heat insulating layer is secured to a heat insulating layer attaching-enclosing member that is located on the periphery of the heat insulating layer by using a combining member, no warping occurs in the heat insulating layer and it becomes possible to provide a firing furnace which is excellent in durability.
According to the third aspect of the present invention, a firing furnace comprises a muffle formed so as to ensure a space for housing a formed body to be fired, a member that constitutes a heat generator and is placed on and/or around the muffle, and a heat insulating layer that contains the muffle and the heat generator inside thereof. Herein, the heat insulating layer is divided into a plurality of heat insulating layers, and a reinforcing member used for combining and reinforcing the heat insulating layers with each other is arranged.
In the firing furnace according to the first aspect of the present invention shown in
Although not particularly limited, examples of the material of the reinforcing member 21 include a carbon fiber composite (C/C composite), graphite and the like. Moreover, the shape of the reinforcing member 21 may have a right angled-U figure-shape in its cross section, an L-shape in its cross section, or a plate shape. In the case where the reinforcing member 21 having the L-shape in its cross section or the plate shape is used, it needs to be fixedly secured by using combining members.
In the case where the reinforcing member 21 is used, a carbon-natured sheet is desirably placed at least in the vicinity of corner portions on the inner face of the heat insulating layer. In particular, upon manufacturing a porous ceramic material made of silicon carbide, this structure makes it possible to prevent the carbon member 13a and the like from being converted into silicon carbide through reactions.
The carbon-natured sheet may be bonded to the inner surface of the heat insulating layer 13 by using an adhesive or the like, or may be fastened to the insulating layer 13 by using the bolts 17a and the nuts 17b serving as combining members (or may be fixedly secured to a heat insulating layer attaching-enclosing member).
In the third aspect of the present invention, in the case where only the reinforcing member is placed, the density of the reinforcing member per unit area of the heat insulating member is desirably at least about 3 pcs/m2 and at most about 15 pcs/m2.
The area of the heat insulating layer refers to an area of a main face of the heat insulating layer, and the reinforcing member is placed in a manner so as to cover at least a part of the main face of the heat insulating layer. In this structure, the dimension of the reinforcing member that covers a part of the main face of the heat insulating layer is set in the range of about 50 to 100 mm in length as well as in the range of about 200 to 400 mm in width, and these reinforcing members are placed at the above-mentioned density.
In the case where the density of the reinforcing member per unit area in the heat insulating layer is at least about 3 pcs/m2 and at most about 15 pcs/m2, the heat insulating layer can be firmly secured; thus, warping and the like hardly occur. Further, the number of reinforcing members is small and the cost can be reduced.
The upper limit value of the density of the reinforcing member per unit area in the heat insulating layer is more desirably set to about 8 pcs/m2. Here, the dimension of the reinforcing member to cover a part of the main face of the heat insulating layer is set in the same manner as the above-mentioned case.
In the third aspect of the present invention, when the reinforcing members are placed on the attached carbon-natured sheet so as to fixedly secure the carbon-natured sheet by the reinforcing member, the density of the reinforcing member per unit area in the heat insulating layer is desirably at least about 2 pcs/m2 and at most about 15 pcs/m2.
In the case where the density of the reinforcing member per unit area in the heat insulating layer is at least about 2 pcs/m2 and at most about 15 pcs/m2, the heat insulating layer can be firmly secured. Thus, warping and the like hardly occur. Further, the number of reinforcing members is small and the cost can be reduced.
The upper limit value of the density of the reinforcing member per unit area in the heat insulating layer is more desirably set to about 8 pcs/m2.
According to the firing furnace of the third aspect of the present invention, since a reinforcing member for combining and reinforcing the heat insulating layers with each other is arranged, the heat insulating layers are secured to each other; therefore, no warping occurs in the heat insulating layer, and flaking off of the insulating layer due to corrosion and the like hardly occurs. It becomes possible to eliminate the necessity of exchanging members constituting the heat insulating layer for a long time and, consequently, to provide a firing furnace which is excellent in durability and heat efficiency.
The foregoing explanation has discussed the firing furnace having a heat generator with a heating system which applies a current to a heater (heat generating body) to generate heat. However, the firing furnaces of the first to third aspects of the present invention may adopt an induction heating system.
This firing furnace 30 comprises a muffle 32 that is formed to ensure a space used for housing a formed body to be fired and serves as a heat generating body, a heat insulating layer 33 placed outside the muffle 32 and a coil 31 with a wire wound around a plurality of times, which is placed outside the heat insulating layer 33. Here, the heat insulating layer 33 may be placed outside the coil 31.
A carbon-natured sheet 16 is placed on inside end portions (in the vicinity of corner portions) of upper and lower heat insulating layers 33, and fixedly secured on the surface of the heat insulating layer 33 by using bolts 17a and nuts 17b that are made of carbon and serve as combining members. Moreover, the heat insulating layer 33 and the carbon-natured sheet 16 are attached to a heat insulating layer attaching-enclosing member 34 through the combining members and secured thereon.
As shown in
The entire floor portion of the muffle 32 is supported by a supporting member (not shown), so that a laminated body of jigs for firing 36 in which formed bodies to be fired are placed is allowed to pass.
This firing furnace 30 has an induction heating system, and an alternating current is applied to the coil 31 so that an eddy current is generated in the muffle (heat generating body) 32 placed inside thereof; thus, the muffle (heat generating body) 32 has a temperature rise to serve as a heater.
Moreover, when an object to be heated is made of an electrically conductive material, an electric current is generated therein so that the object to be heated is allowed to generate heat.
In this firing furnace 30, the muffle (heat generating body) 32 made of carbon (graphite) is placed inside the coil 31 so that, when an alternating current is applied to the coil 31, an eddy current is generated therein to allow the muffle (heat generating body) 32 to generate heat and to heat the object to be heated such as the formed body 9 or the like.
The ambient atmosphere of the firing furnace 30 is desirably prepared as an inert gas atmosphere, such as an argon gas atmosphere, a nitrogen gas atmosphere and the like.
Normally, as shown in
The firing furnace 30 is provided with a muffle (heat generating body) 32 that generates heat upon application of a current to the coil 31 so that the jig for firing 15 is gradually heated to a high temperature during the passage through it, and after having reached the highest temperature, the temperature is gradually lowered; thus, the supporting base 35 on which the laminated body of the jigs for firing 15 is placed is continuously transported into the firing furnace 30 from an inlet, and the jigs for firing 15 the temperature of which is lowered are transported from an outlet to manufacture a porous ceramic member.
In the induction heating system, since the muffle (heat generating body) 32 can be placed in the vicinity of the object to be heated, it becomes possible to heat the object more efficiently.
In the firing furnace 30 shown in
Therefore, in the case where the four corner portions of the heat insulating layers 33 are constituted by heat insulating layers 33X that are placed on the upper and lower sides, the heat insulating layers 33Y placed on the right and left sides are more likely to generate warping. Accordingly, portions close to the corner portions of the heat insulating layers 33X placed on the right and left sides are desirably secured by using a combining member.
Also in the heat insulating layers 33 shown in
Ceramic materials to be manufactured by using the firing furnaces according to the first to third aspects of the present invention are not particularly limited, and various ceramic products may be listed. One of those is a porous ceramic member to be used as a filter or a catalyst supporting member. With respect to the material for the porous ceramic member, examples thereof include oxide ceramics such as cordierite, alumina, silica, mullite, and aluminum titanate, carbide ceramics such as silicon carbide, zirconium carbide, titanium carbide, tantalum carbide, and tungsten carbide, nitride ceramics such as aluminum nitride, silicon nitride, boron nitride, and titanium nitride, a composite of silicon carbide and silicon, and the like. Among these, non-oxide ceramics, such as carbide ceramics and nitride ceramics, which have high heat resistance, superior mechanical properties and a high thermal conductivity, are desirably used, and among the non-oxide ceramics, silicon carbide is more preferably used.
With respect to the application of the porous ceramic member, as described earlier, for example, a ceramic filter, a catalyst supporting member and the like used for purifying exhaust gases discharged from an internal combustion engine such as a diesel engine are listed.
Here, the porous ceramic member to be used as the ceramic filter, the catalyst supporting member and the like is referred to as a honeycomb structural body.
In the following, explanation will be given of a honeycomb structural body to be manufactured by using the above-mentioned firing furnace and a manufacturing method thereof including the firing processes thereof.
The honeycomb structural body has a structure that a plurality of pillar-shaped porous ceramic members each having a large number of throughholes placed in parallel with one another in the length direction with a partition wall interposed therebetween are bound to one another through a sealing material layer.
The honeycomb structural body 40 has a structure that a plurality of porous ceramic members 50 made of silicon carbide are bound to one another through a sealing material layer 43 to form a ceramic block 45, and a sealing material layer 44 is formed on the circumference of this ceramic block 45. Here, the porous ceramic member 50 has a structure that a large number of through holes 51 are placed in parallel with one another in the length direction so that a partition wall 53 separating the through holes 51 is allowed to function as a particle collecting filter.
In other words, as shown in
Since the honeycomb structural body 40 of this type has superior heat resistance and provides easy regenerating processes and the like, it has been applied to various large-size vehicles and vehicles with diesel engines.
The sealing material layer 43, which is placed between the porous ceramic members 50, and serves as an adhesive layer used for bonding the porous ceramic members 50 to each other, is also allowed to serve as a filter. With respect to the material for the sealing material layer 43, although not particularly limited, approximately the same material as the porous ceramic member 50 is desirably used.
The sealing material layer 44, formed on the periphery of the ceramic block 45, is used for preventing leak of exhaust gases from the peripheral portion of the ceramic block 45, when the honeycomb structural body 40 is placed in an exhaust passage of an internal combustion engine. With respect to the material for the sealing material layer 44, although not particularly limited, approximately the same material as the porous ceramic member 50 is desirably used.
Here, with respect to the porous ceramic member 50, the end portions of the through holes need not necessarily be sealed, and when not sealed, the honeycomb structural body can be used as a catalyst supporting member on which, for example, a catalyst for converting exhaust gasses is supported.
The porous ceramic member shown in
The average pore diameter of the porous ceramic 50 is desirably set in the range of about 5 to 100 μm. The average pore diameter of less than about 5 μm tends to cause particulates to easily clog the pores. In contrast, the average pore diameter exceeding about 100 μm tends to cause particulates to pass through the pores; thus, the particulates cannot be collected, making the porous ceramic unable to function as a filter.
Although not particularly limited, the porosity of the porous ceramic member 50 is desirably set to about 40% to 80%. When the porosity is less than about 40%, particulates tend to cause clogging. In contrast, the porosity exceeding about 80% causes degradation in the strength of the pillar-shaped body; thus, it might be easily broken.
With respect to the particle diameter of ceramic particles to be used upon manufacturing the porous ceramic members 50, although not particularly limited, those which are less likely to shrink in the succeeding firing process are desirably used, and for example, those particles, prepared by combining 100 parts by weight of ceramic powders having an average particle diameter of about 0.3 to 50 μm with about 5 to 65 parts by weight of ceramic powders having an average particle diameter of about 0.1 to 1.0 μm, are desirably used. By mixing ceramic powders having the above-mentioned respective particle sizes at the above-mentioned blending ratio, it becomes possible to manufacture a pillar-shaped body made of porous ceramics.
Moreover, the shape of the honeycomb structural body 40 is not limited to the cylindrical shape shown in
Here, the honeycomb structural body 40 can be used as a catalyst supporting member, and in this case, a catalyst (catalyst for converting exhaust gasses) used for converting exhaust gases is supported on the honeycomb structural body.
By using the honeycomb structural body as a catalyst supporting member, toxic components in exhaust gases such as HC, CO, NOx and the like and HC and the like derived from organic components slightly contained in the honeycomb structural body can be surely converted.
The catalyst for converting exhaust gases is not particularly limited, and examples thereof include noble metals such as platinum, palladium, and rhodium. Each of these noble metals may be used alone, or two or more kinds of these may be used in combination.
In the following, explanation will be given of a method for manufacturing the honeycomb structural body.
Herein, explanation will be given of a manufacturing method of a honeycomb structural body that uses the porous ceramic member 50 made of silicon carbide as its constituent member; however, the material for the porous ceramic member is not particularly limited.
More specifically, a ceramic laminated body to form a ceramic block 45 is formed (see
The ceramic laminated body has a pillar structure in which a plurality of pillar-shaped porous ceramic members 50 are bound to one another through a sealing material layer 43.
In order to manufacture the porous ceramic member 50 made of silicon carbide, a mixed composition, prepared by adding a binder and a dispersant solution to silicon carbide powder, is first mixed by an attritor or the like and sufficiently kneaded by a kneader or the like, and then extrusion-formed so that a pillar-shaped formed body having approximately the same shape as the porous ceramic member 50 shown in
With respect to the particle diameter of the silicon carbide powder, although not particularly limited, that which is less likely to shrink in the succeeding firing process is preferable, and for example, silicon carbide powders, prepared by combining 100 parts by weight of powders having an average particle diameter of about 0.3 to 50 μm with about 5 to 65 parts by weight of powders having an average particle diameter of about 0.1 to 1.0 μm, are desirably used.
The above-mentioned binder is not particularly limited, and examples thereof include methylcellulose, carboxymethyl cellulose, hydroxyethyl cellulose, polyethylene glycol, phenolic resin, epoxy resin and the like.
In general, the blending amount of the above-mentioned binder is preferably set to about 1 to 10 parts by weight with respect to 100 parts by weight of the silicon carbide powder.
The dispersant solution is not particularly limited, and examples thereof include an organic solvent such as benzene, alcohol such as methanol, water and the like.
An appropriate amount of the above-mentioned dispersant solution is mixed therein so that the viscosity of the mixed composition is set within a fixed range.
Next, the silicon carbide formed body is dried and, if necessary, a mouth-sealing process is carried out so that predetermined through holes are filled with plugs, and the resulting formed body is again subjected to a drying process.
Next, the resulting silicon carbide formed body is heated at about 400° C. to 650° C. in an oxygen-containing atmosphere so as to be degreased, and heated at about 1400° C. to 2200° C. in an inert gas atmosphere such as nitrogen or argon to be fired so that the ceramics powder is sintered to manufacture a porous ceramic member 50 made of silicon carbide.
Upon carrying out the firing process, any one of the firing furnaces according to the first to third aspects of the present invention is used.
In other words, any one of the following furnaces is used: the firing furnace according to the first aspect of the present invention that comprises a muffle formed so as to ensure a space for housing a formed body to be fired, a member that constitutes a heat generator and is placed on and/or around the muffle, and a heat insulating layer that contains the muffle and the heat generator inside thereof, in which a carbon-natured sheet placed in the vicinity of corner portions of an inner face of the heat insulating layer; the firing furnace according to the second aspect of the present invention that comprises a muffle formed so as to ensure a space for housing a formed body to be fired, a member that constitutes a heat generator and is placed on and/or around the muffle, and a heat insulating layer that contains the muffle and the heat generator inside thereof, in which the heat insulating layer being secured to a heat insulating layer attaching-enclosing member that is located on the periphery of the heat insulating layer by using a combining member; and the firing furnace according to the third aspect of the present invention that comprises a muffle formed so as to ensure a space for housing a formed body to be fired, a member that constitutes a heat generator and is placed on and/or around the muffle, and a heat insulating layer that contains the muffle and the heat generator inside thereof, in which the heat insulating layer divided into a plurality of heat insulating layers while a reinforcing member that combines and reinforces the divided insulating layers is arranged therein.
In the firing process, the heating processes are carried out at the above-mentioned temperatures; thus, SiO, Si and SiC contained in the silicon carbide formed body are evaporated to cause a warping in the heat insulating layer. However, in the first to third aspects of the present invention, since the portion in the heat insulating layer at which the warping occurs is covered with a carbon-natured sheet or since the portion is firmly secured so as to prevent the warping, no warping occurs in the heat insulating layer. Thus, the same firing furnace can be used for a long time, thereby making it possible to manufacture a porous ceramic member under the same conditions with high reproducibility. Moreover, each of the firing furnaces of the first to third aspects of the present invention may be prepared as a continuous furnace, and a porous ceramic member 50 can be continuously manufactured.
Thereafter, a plurality of porous ceramic members 50, thus manufactured, are bound to one another through a sealing material layer 43, and after this has been machined into a predetermined shape, a sealing material layer 34 is formed on the periphery thereof; thus, manufacturing processes of the honeycomb structural body are completed.
According to the porous ceramic member manufacturing methods of the fourth to sixth aspects of the present invention, the firing furnace according to any one of the first to third aspects of the present invention is used upon firing a formed body to form the porous ceramic member. Thus, it is possible to carry out the firing process under a stable condition, and to manufacture porous ceramic members having superior properties under the same condition with high reproducibility, while preventing impurities derived from warping and corrosion in the heat insulating layer from contaminating the product.
According to the seventh to ninth aspects of the present invention, since the firing furnace according to any one of the first to third aspects of the present invention is used upon firing a formed body to form the porous ceramic member, the porous ceramic member can be free from contamination with impurities derived from warping and corrosion in the heat insulating layer, can be manufactured with a high reproducibility, and has excellent properties.
In the following, explanation will be given of specific examples; however, the present invention is not intended to be limited only by these examples.
(1) Powders of α-type silicon carbide having an average particle diameter of 10 μm (60% by weight) and powders of α-type silicon carbide having an average particle diameter of 0.5 μm (40% by weight) were wet-mixed, and to 100 parts by weight of the resulting mixture were added and kneaded 5 parts by weight of an organic binder (methyl cellulose) and 10 parts by weight of water to obtain a mixed composition. Next, after a slight amount of a plasticizer and a lubricant had been added and kneaded therein, the resulting mixture was extrusion-formed to form a raw formed product.
Next, after the above-mentioned raw formed product had been dried by using a microwave drier or the like to form a ceramic dried body, predetermined through holes were filled with a paste having the same composition as the raw formed product. After having been again dried by using a drier, the resulting product was degreased at 400° C., and fired at 2200° C. in a normal-pressure argon atmosphere for 3 hours to manufacture a porous ceramic member having a shape as shown in
When the firing process was carried out, a firing furnace in which carbon-natured sheets (FGL-253C (cloth), made by Nippon Carbon Co., Ltd., density: 0.16 g/cm3) were placed on end portions of an inner face of upper and lower heat insulating layers as shown in
Thereafter, the method, described in “DESCRIPTION OF THE EMBODIMENTS”, was used to manufacture a honeycomb structural body 40 in which a plurality of porous ceramic members 50 made of silicon carbide, shown in
Moreover, the above-mentioned firing furnace was used to continuously carry out the manufacturing processes of the porous ceramic members for 1000 hours, and the heat insulating layers constituting the firing furnace were observed for any warping; however, no warping was found in the heat insulating layers.
The honeycomb structural body in which the porous ceramic members thus manufactured were used was able to sufficiently satisfy properties as a filter, and the honeycomb structural body, which was manufactured by using porous ceramic members that were continuously manufactured, had no change in characteristics as the honeycomb structural body.
The same processes as Example 1 were carried out except that DON-3000 (graphite foil, made by Donack Co., Ltd., density: 0.15 g/cm3) was used as the carbon-natured sheets to be placed on end portions of the inner face of upper and lower heat insulating layers that constitute the firing furnace to manufacture porous ceramic members, and the resulting porous ceramic members were used to manufacture a honeycomb structural body. In this case, the processes used for manufacturing the porous ceramic members were continuously repeated for 1000 hours in the same manner as Example 1, and the heat insulating layers constituting the firing furnace were observed for any warping.
As a result, no warping was observed in the same manner as Example 1.
The honeycomb structural body in which the porous ceramic members thus manufactured were used was able to sufficiently satisfy properties as a filter, and the honeycomb structural body, which was manufactured by using porous ceramic members that were continuously manufactured, had no change in characteristics as the honeycomb structural body.
The same processes as Example 1 were carried out except that no carbon-natured sheets were placed on end portions of the inner face of upper and lower heat insulating layers that constitute the firing furnace, with the heat insulating layers 13 being secured to a heat insulating layer attaching-enclosing member 19 with bolts 17a and nuts 17b serving as combining members, to manufacture porous ceramic members and a honeycomb structural body formed thereby.
In this case, the process used for manufacturing the porous ceramic members were continuously carried out for 1000 hours in the same manner as Example 1, and after a lapse of 700 hours as well as after a lapse of 1000 hours, the heat insulating layers forming the firing furnace were observed for any warping. As a result, no warping was observed in the heat insulating layers in any of the lapses of time.
The honeycomb structural body in which the porous ceramic members thus manufactured were used was able to sufficiently satisfy properties as a filter, and the honeycomb structural body, which was manufactured by using porous ceramic members that were continuously manufactured, had no change in characteristics as the honeycomb structural body.
Incidentally, the density per unit area of the combining members was 4 pcs/m2.
The same processes as Example 1 were carried out except that no carbon-natured sheets were placed on end portions of the inner face of upper and lower heat insulating layers that constitute the firing furnace, with the heat insulating layers 13 being secured to a heat insulating layer attaching-enclosing member 19 with bolts 17a and nuts 17b serving as combining members, to manufacture porous ceramic members and a honeycomb structural body formed thereby.
In this case, the process used for manufacturing the porous ceramic members were continuously carried out for 1000 hours in the same manner as Example 1, and after a lapse of 700 hours as well as after a lapse of 1000 hours, the heat insulating layers forming the firing furnace were observed for any warping. As a result, no warping was observed in the heat insulating layers in any of the lapses of time.
The honeycomb structural body in which the porous ceramic members thus manufactured were used was able to sufficiently satisfy properties as a filter, and the honeycomb structural body, which was manufactured by using porous ceramic members that were continuously manufactured, had no change in characteristics as the honeycomb structural body.
Incidentally, the density per unit area of the combining member was 100 pcs/m2.
The same processes as Example 1 were carried out except that a reinforcing member 21 made of a carbon fiber composite material (C/C composite) (K-200, made by Kureha Chemical Industry Co., Ltd., density: 1.75 g/ml) was attached to a joint portion of heat insulating layers that constitute a firing furnace, as shown in
As a result, no warping was found in any portion of the heat insulating layers.
The honeycomb structural body in which the porous ceramic members thus manufactured were used was able to sufficiently satisfy properties as a filter, and the honeycomb structural body, which was manufactured by using porous ceramic members that were continuously manufactured, had no change in characteristics as the honeycomb structural body.
The same processes as Example 1 were carried out except that, upon firing, carbon-natured sheets 160 (FGL-253C (cloth), made by Nippon Carbon Co., Ltd.; density: 0.16 g/cm3) were placed in the vicinity of end portions of an inner face of heat insulating layers 63Y on the right and left side faces as shown in
As a result, no warping was found in the heat insulating layers 63.
The honeycomb structural body in which the porous ceramic members thus manufactured were used was able to sufficiently satisfy properties as a filter, and the honeycomb structural body, which was manufactured by using porous ceramic members that were continuously manufactured, had no change in characteristics as the honeycomb structural body.
Incidentally, the density per unit area of the combining member was 4 pcs/m2.
The same processes as Example 1 were carried out except that, upon firing, approximately L-shaped carbon-natured sheets 161 (FGL-253C (cloth), made by Nippon Carbon Co., Ltd.; density: 0.16 g/cm3) were placed at four corners of an inner face of a heat insulating layer 13 as shown in
As a result, no warping was found in the heat insulating layers 13.
The honeycomb structural body in which the porous ceramic members thus manufactured were used was able to sufficiently satisfy properties as a filter, and the honeycomb structural body, which was manufactured by using porous ceramic members that were continuously manufactured, had no change in characteristics as the honeycomb structural body.
Incidentally, the density per unit area of the combining member was 4 pcs/m2.
The same processes as Example 1 were carried out except that, upon firing, carbon-natured sheets 162 (FGL-253C (cloth), made by Nippon Carbon Co., Ltd.; density: 0.16 g/cm3) were placed over the entire inner faces of upper and lower heat insulating layers 13, as shown in
As a result, no warping was found in the heat insulating layers 13.
The honeycomb structural body in which the porous ceramic members thus manufactured were used was able to sufficiently satisfy properties as a filter, and the honeycomb structural body, which was manufactured by using porous ceramic members that were continuously manufactured, had no change in characteristics as the honeycomb structural body.
Incidentally, the density per unit area of the combining member was 4 pcs/m2.
The same processes as Example 1 were carried out except that, upon firing, carbon-natured sheets 163 (FGL-253C (cloth), made by Nippon Carbon Co., Ltd., density: 0.16 g/cm3) were placed over the entire inner faces of insulating layers 63Y on right and left side faces, as shown in
As a result, no warping was found in the heat insulating layers 63Y.
The honeycomb structural body in which the porous ceramic members thus manufactured were used was able to sufficiently satisfy properties as a filter, and the honeycomb structural body, which was manufactured by using porous ceramic members that were continuously manufactured, had no change in characteristics as the honeycomb structural body.
Incidentally, the density per unit area of the combining members was 4 pcs/m2.
The same processes as Example 1 were carried out except that, upon firing, carbon-natured sheets 164 (FGL-253C (cloth), made by Nippon Carbon Co., Ltd.; density: 0.16 g/cm3) were placed over the entire inner faces of the heat insulating layer 13, as shown in
As a result, no warping was found in the heat insulating layer 13.
The honeycomb structural body in which the porous ceramic members thus manufactured were used was able to sufficiently satisfy properties as a filter, and the honeycomb structural body, which was manufactured by using porous ceramic members that were continuously manufactured, had no change in characteristics as the honeycomb structural body.
Incidentally, the density per unit area of the combining member was 4 pcs/m2.
The same processes as Example 1 were carried out except that no carbon-natured sheets were placed on end portions of the inner face of upper and lower heat insulating layers that constitute the firing furnace, with the heat insulating layers 13 being secured to a heat insulating layer attaching-enclosing member 19 with bolts 17a and nuts 17b serving as combining members, to manufacture porous ceramic members and a honeycomb structural body formed thereby.
In this case, the process used for manufacturing the porous ceramic members were continuously carried out for 1000 hours in the same manner as Example 1, and after a lapse of 700 hours as well as after a lapse of 1000 hours, the heat insulating layers forming the firing furnace were observed for any warping. As a result, no warping was observed in the heat insulating layers after the lapse of 700 hours; however, a warping was observed in the heat insulating layers after the lapse of 1000 hours.
The honeycomb structural body in which the porous ceramic members thus manufactured were used was able to sufficiently satisfy properties as a filter, and the honeycomb structural body, which was manufactured by using porous ceramic members that were continuously manufactured, had no change in characteristics as the honeycomb structural body.
Incidentally, the density per unit area of the combining member was 2 pcs/m2.
The same processes as Example 1 were carried out except that a conventional firing furnace in which no carbon-natured sheets were placed on end portions of an inner face of upper and lower heat insulating layers was used to manufacture porous ceramic members, and a honeycomb structural body was manufactured by using the resulting porous ceramic members.
As a result, after the lapse of 700 hours, a warping occurred, and when the manufacturing processes were continuously carried out, flaking off of the insulating layer occurred after the lapse of 2000 hours.
As clearly indicated by the above-mentioned Examples, the present invention is desirably applied to a manufacturing method of a honeycomb structural body made of non-oxide based ceramics.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2004-228649 | Aug 2004 | JP | national |
| PCT/JP05/01264 | Jan 2005 | WO | international |
| PCT/JP05/02073 | Feb 2005 | WO | international |