First row transition metal amino borohydrides

Abstract

A transition metal amino borohydride material includes a first row transition metal in conjunction with an amine ligand and borohydride, in a condition of having been thermally treated to a temperature of at least 70° C. and up to but not including 800° C. An exemplary such material, Fe(DETA)(BH4)2 having been heat treated at 300° C., had good hydrogen storage characteristics.

Description

BACKGROUND

Hydrogen (H₂) is an attractive energy carrier, with a combustion product that is primarily if not entirely water, and possesses high gravimetric energy density. However, it suffers from an extremely low volumetric energy density. Storing hydrogen under high pressures or in the liquid state can increase volumetric density, but storing hydrogen at high pressures or as a liquid requires expensive, specialized tanks that are expensive, inconvenient, and otherwise disadvantageous, especially in mobile applications. A need exists for materials that simultaneously possess stability, reversibility, and high usable hydrogen density.

BRIEF SUMMARY

The materials described herein are first row transition metal borohydride complexes with amino ligands that have been added to promote stability and increase H₂ content. The amino ligands can be in the form of small molecules, or they can be oligomeric, or polymeric in nature. The amino ligands impart stability on the metal borohydride complexes at room temperature, with thermal dehydrogenation occurring around 100° C., and gravimetric hydrogen densities between 5%-7.5%

In one embodiment, a transition metal amino borohydride material comprises a first row transition metal in conjunction with an amine ligand and borohydride, in a condition of having been thermally treated to a temperature from between at least 70° C. and up to but not including 800° C.

In a further embodiment, a method of making a transition metal amino borohydride material includes reacting a salt of a transition metal with a borohydride in a solvent, then adding an amine ligand to the solvent with mixing, then collecting a solid reaction product and heating to a temperature from between at least 70° C. and up to but not including 800° C., thereby obtaining transition metal amino borohydride material.

Another embodiment is a method of storing hydrogen by providing a transition metal amino borohydride material comprising a first row transition metal in conjunction with an amine ligand and borohydride, in a condition of having been thermally treated to a temperature from between at least 70° C. and up to but not including 800° C.; and introducing hydrogen into the material under elevated pressure, thereby causing hydrogen to be reversibly stored in the material.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows amine ligands that have been used in preparing the first row transition metal borohydride complexes.

FIG. 2 shows Fourier transform infrared (FTIR) spectroscopy of prepared materials containing Fe and Cr.

FIG. 3A shows thermogravimetric analysis (TGA) with mass spectrometry showing the decomposition behavior of prepared materials and their evolved gases upon decomposition. FIG. 3B shows differential scanning calorimetry (DSC) traces for the Cr(BH₄)₂(DETA) complex at varying temperature ramp rates. FIG. 3C is a Kissinger plot shown constructed from the data in FIG. 3C.

FIGS. 4A and 4B are FTIR spectra for Fe and Cr complexes, respectively, heated to varying temperatures.

FIG. 5A shows X-ray powder diffraction patterns: the lower line is background, the second line from the bottom is as-synthesized Fe(DETA)(BH₄)₂, the third line from the bottom is the same heated to 350° C., and the top line is the same heated to 800° C. FIG. 5B shows thermal gravimetric analyses of Fe(DETA)(BH₄)₂ under vacuum. FIG. 5C is an FTIR spectra of a Fe(DETA)(BH₄)₂ sample as synthesized (bottom line), heated to 350° C. (middle line), and 800° C. (top). FIG. 5D is a nitrogen adsorption isotherms for Fe(DETA)(BH₄)₂ with no treatment (top line), the same heated to 350° C. (labeled 2), 800° C. (labeled 1).

FIGS. 6A-G show X-ray photoelectron spectra of Fe(DETA)(BH₄)₂ as synthesized (bottom line), heated to 350° C. (middle line), and 800° C. (top line).

FIG. 6A: survey spectra, FIG. 6B: Fe_2p spectra, FIG. 6C: B_1s spectra, FIG. 6D: N_1s spectra, FIG. 6E: O_1s spectra, FIG. 6F: Li_1s spectra, and FIG. 6G: Cl_2p spectra.

DETAILED DESCRIPTION

Definitions

Before describing the present invention in detail, it is to be understood that the terminology used in the specification is for the purpose of describing particular embodiments, and is not necessarily intended to be limiting. Although many methods, structures and materials similar, modified, or equivalent to those described herein can be used in the practice of the present invention without undue experimentation, the preferred methods, structures and materials are described herein. In describing and claiming the present invention, the following terminology will be used in accordance with the definitions set out below.

As used herein, the singular forms “a”, “an,” and “the” do not preclude plural referents, unless the content clearly dictates otherwise.

As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items.

As used herein, the term “about” when used in conjunction with a stated numerical value or range denotes somewhat more or somewhat less than the stated value or range, to within a range of ±10% of that stated.

Overview

A new class of materials based on first row transition metal amino borohydride complexes is useful for hydrogen storage applications. The technique allows for high gravimetric and volumetric hydrogen density that can be released at relevant temperatures and pressures of technological interest. Identifying hydrogen storage materials that operate at relevant conditions and show reversibility is of importance due to the increasing need to use hydrogen as a fuel, particularly in mobility applications. This material represents a significant advance over currently known hydrogen storage technologies because it shows high hydrogen capacity that is reversible, while using low cost first row transition metals together with amino and borohydride ligands.

Metal borohydrides are made by dissolving a metal chloride in an appropriate solvent (for example, 1,2-dimethoxyethane, THF, etc.), then to that solvent adding an alkali metal borohydride complex (e.g., NaBH₄ and/or LiBH₄). The borohydride anions replace the chlorides on the metal, and in some cases reduce the metal center, resulting in a metal borohydride complex. The metal borohydride can then interact with the solvent molecules, stabilizing the metal borohydride. The preparation of transition metal amino borohydride complexes occurs by a similar method, but after the formation of the metal borohydride complex, a suitable amine ligand is added to react with the metal borohydride complex, replacing the stabilizing role of solvent molecules. The general preparation method is:M¹Cl₃+3M²BH₄→M¹(BH₄)₂+3M₂Cl+½B₂H₆+½H₂

(M¹=preferably Cr³⁺, V³⁺, or Fe³⁺, but possibly any of the first row transition metals,) (M²=Li or Na)M¹(BH₄)₂(DME/THF)+amine ligand→DME/THF+M¹(BH₄)₂(amine)

Examples of suitable amine ligands are shown in FIG. 1 and include diethylenetriamine (DETA) (101), tetramethylethylenediamine (TMEDA) (102), and/or pentamethyldiethylenetriamine (PMDETA) (103). A variety of other amine ligands could be used including those with longer chains and protonated and/or and permethylated varieties.

The process steps should be conducted under an inert atmosphere such as under nitrogen or argon gas.

EXAMPLES

Various complexes containing Cr, Fe, and V metal centers with varying amino ligands were prepared. Complexes containing the other first row transition metals, for example Ti, Co, Mn, Cu, Zn, are also envisioned.

FIG. 2 shows FT-IR spectra for synthesized Cr and Fe (BH₄)₂(DETA) complexes. These spectra were collected in a transmission geometry in a KBr pellet. The synthesized powders show characteristic absorbance at ≈2300 cm⁻¹, 3000 cm⁻¹, and 3200 cm⁻¹ corresponding to B—H, C—H, and N—H stretching modes, respectively. These absorbance bands are commensurate with those observed in corresponding precursors. However, it should be noted that the broad, free N—H band of the DETA at 800 cm⁻¹ is not observed in the synthesized complexes; implying that each amine moiety is ligated to the metal center, and minimal residual DETA precursor is present in the powders.

FIG. 3A shows the TGA traces for the synthesized Cr, V, and Fe complexes with evolved gas analysis using a mass spectrometer attachment. The Cr complex showed a mass loss of 7.25%, with an onset temperature of 91.3° C. The evolved gas analysis showed only signal for H₂ (m/z=2) during this decomposition event. A 7.25% mass loss equates to a loss of 13 hydrogen atom equivalents per Cr complex molecule, which is the predicted number of H atoms on the B and N atoms per complex molecule.

The V amino borohydride complex lost 18.9% mass at 92.1° C., evolving H₂, B₂H₆ and NH₃ gases. This high degree of mass loss coupled with detection of NH₃ and B₂H₆ shows the V complex to have poor hydrogen release properties for a hydrogen storage material. Also, analysis of a product heated to 400° C. displayed a significant amount of residual B—H stretching modes in FT-IR, implying that very high temperatures are necessary to achieve complete dehydrogenation.

The Fe amino borohydride complex displayed bimodal decomposition behavior. At 94.8° C., a mass loss of 3.95% was recorded. The evolved gases were H₂ with a small signal for B₂H₆. Heating further to 196.8° C., resulted in a second mass loss event of 29.5% and release of B₂H₆ and NH₃ gases. The mass loss at 94.8° C., equates to the release of 7.5H atoms per Fe complex molecule.

In order to assess the thermodynamic and kinetic aspects of decomposition, differential scanning calorimetry was used. FIG. 3B shows the calorimetry results during decomposition for Cr(BH₄)₂(DETA) at various heating rates. On average the decomposition process released 24 J/g, with peak heat release values between 103.0° C. and 112.9° C. for 2.5 and 10° C./min heating rates, respectively. Kissinger plots were constructed (FIG. 3C) using the observed peak temperature values and yielded an activation energy for decomposition of 162 kJ/mol. The activation energy calculated from simultaneous TGA measurements was calculated to be 281 kJ/mol. This discrepancy could be due to slowed detector response due to heat diffusion during the DSC collection. The Fe and V complexes were not analyzed using Kissinger analysis since their decomposition process was slower and occurred over a broad temperature range.

To further explore the decomposition behavior of metal amino borohydride complexes, intermediate decomposition products were analyzed using FTIR spectroscopy (FIGS. 4A and 4B). The Fe complex showed a decrease in B—H stretching mode signal when heated to 120° C. Heating to 400° C. results in a loss in B—H and C—H stretching modes and the emergence vibrational modes characteristic for boron nitride materials. N—H stretching modes were present for each Fe sample tested, but with diminished signal at higher temperatures. Upon heating the Cr(BH₄)₂(DETA) complex, a simultaneous loss in B—H and N—H absorbance is observed. At 120° C. this loss results in signal for a B—N stretching mode at ≈1400 cm⁻¹. At 250° C., minimal B—H and N—H absorbance is observed, with a significant decrease in C—H stretching signal. By 400° C. only signal for B—N vibrational modes are detected.

Thermalized Material

In a further example, amorphous Fe—N—B material was prepared by including a heat-treatment (thermalization) process and was found to exhibit good hydrogen storage ability. Synthetic procedures were conducted under inert conditions; that is, in a glovebox under an atmosphere of N₂. The material was prepared by first dissolving 5 g (31 mmol) of FeCl₃ in 500 mL dimethoxyethane (DME) producing a solution golden brown in color. This was added slowly to 2 g (93 mmol) LiBH₄ (also dissolved in DME) with vigorous stirring. The solution became lighter in color with a yellowish hue. This solution was allowed to stir at room temperature for one hour (or until the evolution of gas was observed to stop). Then around 4.5 g (4.3 mmol) of diethylenetriamine (DETA) was added dropwise to the solution and the resulting suspension was allowed to stir at room temperature for one hour. A dark red precipitate was observed to form initially upon addition of the DETA; this red precipitate, however, was observed to become yellowish (or tan in color when dry) over the course of the hour upon homogenization of the suspension with vigorous stirring. After the hour of stirring, the suspension was then filtered through a medium glass frit and the resultant tan colored powder was collected and dried by evacuation at room temperature under dynamic vacuum. A total of 5 g of product was recovered from filtration and evacuation. This product was then thermalized in a quartz vessel by heating to 350° C. and 800° C. over a sand bath or furnace, respectively, under dynamic vacuum.

The addition of DETA to a DME solution of Fe(BH₄)₂ resulted in a pale yellowish tan amorphous solid product as evidenced by powder X-ray diffraction (PXRD) which is relatively featureless up to 800° C. (FIG. 5A). After heating to 800° C. the PXRD pattern displays signals located at 2Θ of 43.6°, 44.4°, 50.8°, 64.8°, and 82.2°. These neither match the background signal, nor the Pnma, P63mc, Ama2, and Fm3m known crystallographic forms of LiBH₄. Thermogravimetric analysis of Fe(DETA)(BH₄)₂ under vacuum displays an approximately 60% loss of mass between 150° C. and 300° C. (FIG. 5B) which is in good agreement with a previous reported result which was attributed to the evolution of H₂, B₂H₆, and NH₃. Upon evacuation, the FTIR spectra of the Fe(DETA)(BH₄)₂ displays (FIG. 5C) characteristic signals between 1500 cm⁻¹ and 1650 cm⁻¹ as well as between 2000 cm⁻¹ and 2500 cm⁻¹ corresponding to B—H bending and stretching modes, respectively. Signals corresponding to C—H and N—H stretching modes are also present between 2700 cm⁻¹-3000 cm⁻¹ and 3000 cm⁻¹-3400 cm⁻¹. Upon heating the material to 350° C. for 8 hours these features are no longer present in the FTIR spectra. When heated to 800° C. a weak signal is observed at 1390 cm⁻¹ that may be due to the formation of B—N bonds.

X-ray photoelectron spectra of the un-treated material display relatively strong signals at 709.6 eV and 723.1 eV and much weaker signals at 714.1 eV and 727.6 eV corresponding to Fe 2p_3/2 (low energy) and 2p_1/2 (high energy) electrons, respectively. The 2p_3/2 signals are distinct from those observed for FeCl₃ which appears at 711.5 eV and closer to those observed for FeCl₂ at 710.8 eV potentially confirming the oxidation state of the Fe as in the ferrous form. The position of the Fe 2p signals displayed no significant shifts upon heating the material to 350° C. and 800° C. indicating no change in the oxidation state of the Fe with heat treatment. The Fe 2p_3/2 signal observed at 714.1 eV resembles that observed for ferric FeF₃ at 714.4 eV suggesting the potential presence of a second ferric iron species. The B 1s spectra of the untreated sample displays multiple signals at 187.8 eV, 189.5 eV, and 191.7 eV; upon heating to 350° C. a single band is observed at 191.3 eV and 189.8 eV upon heating to 800° C. The N 1s signal of the untreated and treated material shows two overlapping bands upon analysis—a relatively strong band centered at 399.4 eV and another weaker signal at 401.1 eV for the untreated sample. The later band displays a shift to 398.4 eV upon heating to 350° C. and 397.8 eV when heated to 800° C. The photoelectron spectra of the untreated and heated materials also display bands corresponding to O 1s, Li 1s, Cl 2p atoms. No significant changes in the band position are observed for the Li 1s signal at 55.2 eV upon heating the material to 800° C. Similarly, the position of the O 1s band is centered at around 531.5 eV up to 350° C.; at 800° C. a second band centered at 536.3 eV is observed in addition to the primary band at 531.5 eV. The Cl 2p_3/2 is observed to shift from 197.3 eV (for the untreated sample) to 198.0 eV when heated to 350° C. and 198.8 eV when heated to 800° C.

Brunauer-Emmett-Teller (BET) analysis of the Fe(DETA)(BH₄)₂ compound indicates a surface area of approximately 12 m²/g which decreases significantly to approximately 2 m²/g upon heating to 350° C. with little additional change upon heating to 800° C. (Table 1). Despite the low surface area obtained by BET analysis, the material demonstrates a gravimetric capacity for H₂ sorption of approximately 1% by wt at 70 atm and −150° C. which is comparable to H₂ sorption by the high surface area (555 m²/g) porous metal-organic framework UiO-66 (Table 1).

	TABLE 1
		BET surface
		area	% H2 mass uptake
	Material	(m2 g−1)	(70 atm, 123K)
	Fe(DETA)(BH4)2	11.6 ± 0.1	0.74% wt
	FeNB that had been	1.39 ± 0.10	0.99% wt
	heated to 350° C.
	FeNB that had been	1.58 ± 0.05	0.31% wt
	heated to 800° C.
	UiO-66	556 ± 16	1.02% wt
		(823†)	(2.6% wt at 77K,
			26 atm†)

It is expected that the favorable impact of thermal treatment below 800° C. will extend to other first row transition metal amino borohydride complexes including those with other transition metals and those incorporating other ligands. Such materials might be thermally treated for a period of time ranging from one hour up to several days, at a temperature ranging from 70° C. and up to but not including 800° C.

Further Envisioned Embodiments

Also contemplated are devices for hydrogen storage and method for using such devices. The devices can include a transition metal amino borohydride complex enclosed in a suitable vessel (e.g., one capable of withstanding the associated pressures) with at least one port for inlet and outlet of hydrogen gas. A device optionally further includes heating and/or cooling mechanisms. A method of using the device can include loading hydrogen into it and causing the hydrogen to be released from it simply by regulating the temperature and pressure of hydrogen within the said vessel. It would be relatively facile to design such a vessel/system to take on any size and/or shape, as the associated temperatures of <200° C., and pressures <100 bar (optionally plus a safety factor of 50% or greater) are easily containable using available technology.

Suitable hydrogen-storage devices designed for use with metal hydrides are known in the art, for example as described in U.S. Pat. Nos. 8,597,410 and 6,651,701, each incorporated herein by reference for the disclosure of such devices and methods of their use. They could be adopted for use with the transition metal amino borohydride complexes described herein.

Advantages

The technique described herein allows for high gravimetric and volumetric hydrogen densities, as well as efficient hydrogen release and uptake at moderate temperature and hydrogen pressure. Additional desired properties include the use of inexpensive starting materials and hydrogen recyclability. The material described in this disclosure uses earth abundant first row transition metals, boron and nitrogen, indicating that they will be more affordable to produce than competing materials such as metal-organic frameworks.

CONCLUDING REMARKS

Although the present invention has been described in connection with preferred embodiments thereof, it will be appreciated by those skilled in the art that additions, deletions, modifications, and substitutions not specifically described may be made without departing from the spirit and scope of the invention. Terminology used herein should not be construed as being “means-plus-function” language unless the term “means” is expressly used in association therewith.

Claims

1. A transition metal amino borohydride material comprising: a first row transition metal in conjunction with a polymeric amine ligand having at least three amine groups and borohydride, in a condition of having been thermally treated to a temperature of 70° C. or greater and less than 800° C.

2. The material of claim 1, wherein said material is amorphous.

3. The material of claim 1, wherein said first row transition metal is selected from the group consisting of Cr3+, V3+, and Fe3+.

4. The material of claim 1, wherein said amine ligand is diethylenetriamine.

5. The material of claim 1, wherein said a first row transition metal in conjunction with an amine ligand and borohydride is Fe(DETA)(BH4)2.

6. The material of claim 1, wherein said thermal treatment has been made at a temperature of 350° C. or greater.

7. A transition metal amino borohydride material comprising: chromium in conjunction with a polymeric amine ligand having at least three amine groups and borohydride, in a condition of having been thermally treated to a temperature of 70° C. or greater and less than 800° C.

8. A transition metal amino borohydride material comprising: a first row transition metal in conjunction with a diethylenetriamine ligand and borohydride, in a condition of having been thermally treated to a temperature of 70° C. or greater and less than 800° C., wherein the material is polymeric.

9. The material of claim 8, wherein the metal is chromium.