Flame retardant compositions

Abstract

Flame retardant compositions comprise linear alternating polymers of carbon monoxide and at least one ethylenically unsaturated hydrocarbon and a minor quantity, relative to the polymer of an alkaline earth metal hydroxide.

Description

FIELD OF THE INVENTION

Compositions comprising carbon monoxide/ethylenically unsaturated hydrocarbon polymers and certain alkaline earth metal hydroxides demonstrate flame retardancy and are non-toxic.

BACKGROUND OF THE INVENTION

The general class of polymers of carbon monoxide and one or more ethylenically unsaturated hydrocarbons has been known for some years. Brubaker, U.S. Pat. No. 2,495,286, produced such polymers of relatively low carbon monoxide content in the presence of free radical catalysts such as benzoyl peroxide. British Pat. No. 1,081,304 produced such polymers of higher carbon monoxide content in the presence of alkylphosphine complexes of palladium as catalyst. Nozaki extended the process to arylphosphine complexes of palladium. See, for example, U.S. Pat. No. 3,694,412.

More recently, the class of linear alternating polymers of carbon monoxide and unsaturated hydrocarbons, now known as polyketones, has become of greater interest, in part because of improved methods of production. Such methods are shown by European Patent Applications Nos. 181,014, 121,965, 222,454 and 257,663. The disclosed processes employ, inter alia, a compound of a Group VIII metal such as palladium, an anion of a non-hydrohalogenic acid having a pKa below 2 and a bidentate ligand of phosphorus. The resulting polymers are generally high molecular weight thermoplastic polymers having utility in the production of articles such as containers for food and drink and parts for the automotive industry or structural members for use in the construction industry.

With regard to any plastic material employed in a public application, some concern must be shown for the consequences of the material catching fire and burning. Many plastics, e.g., polyvinylchloride, produce highly toxic gases upon combustion. The use of polyketones has advantages in this regard since only atoms of carbon, hydrogen and oxygen are present in the polymer molecule. Nevertheless, it would be of advantage to provide for flame retardant compositions of polyketone polymers.

Others in the past have attempted to improve the flame retardancy of polyketone compositions. For example, U.S. Pat. No. 4,761,449 discloses compositions containing a carbon monoxide/ethylenically unsaturated hydrocarbon copolymer with an alkaline earth metal carbonate, such as calcium carbonate. While these compositions show improved flame retardancy they still have certain deficiencies. In particular, the compositions containing up to 25% calcium carbonate still have Limiting Oxygen Index (LOI) values of only 27-27.5. LOI values of 30 or greater are required for many commercial applications. In addition, the mechanical properties of the flame retardant compositions must remain high if the compositions are to have commercial significance. Therefore, it is important that the amount of flame retardant necessary to obtain commercial compositions be as small as possible.

SUMMARY OF THE INVENTION

This invention relates to flame-retardant compositions of linear alternating polymers of carbon monoxide and at least one ethylenically unsaturated hydrocarbon. More particularly, the invention relates to compositions of such polymers incorporating a flame-retardant quantity of an alkaline earth metal hydroxide. Compositions according to the present invention not only have high LOI values, but also may have V-O values according to UL-94 tests along with good mechanical values (i.e. high modulus and impact). Still further, these compositions are non-toxic, i.e. they do not release toxic fumes such as HCl or HF gases.

COPENDING PATENT APPLICATIONS

Copending U.S. patent application Ser. No. 332249, filed Mar. 31, 1989, titled "Flame Retardant Composition Containing Zinc Borate") discloses and claims a flame retardant composition comprising a polyketone polymer and zinc borate.

Copending U.S. patent application Ser. No. 332636, filed Mar. 31, 1989 (titled "Polyketone Flame Retardant Composition") discloses and claims a flame retardant composition with a polyketone polymer and various flame retardants, including antimony trioxide and decabromo diphenyloxide.

DESCRIPTION OF THE INVENTION

The polymers from which the compositions of the invention are produced are linear alternating polymers of carbon monoxide and at least one ethylenically unsaturated hydrocarbon. Suitable ethylenically unsaturated hydrocarbons have up to 20 carbon atoms inclusive, preferably up to 10 carbon atoms inclusive and are wholly aliphatic such as ethylene and other .alpha.-olefins including propylene, butene-1, octene-1 and dodecene-1 or are arylaliphatic containing an aryl substituent on an otherwise aliphatic molecule, particularly an aryl substituent on a carbon atom of the ethylenic unsaturation. Illustrative of this latter class of olefins are styrene, p-methylstyrene, m-methylstyrene and p-ethylstyrene. Preferred polyketone polymers are copolymers of carbon monoxide and ethylene or terpolymers of carbon monoxide, ethylene and a second aliphatic .alpha.-olefin of 3 or more carbon atoms, particularly propylene.

Of particular interest are those polymers of molecular weight from about 1,000 to about 200,000, particularly those of molecular weight from about 10,000 to about 50,000, and containing substantially equimolar quantities of carbon monoxide and ethylenically unsaturated hydrocarbon.

Such polymers are typically produced by contacting the carbon monoxide and the ethylenically unsaturated hydrocarbon(s) under polymerization conditions in the presence of a catalytic amount of a catalyst formed from a compound of the Group VIII metals palladium, cobalt or nickel, the anion of a non-hydrohalogenic acid of a pKa less than about 6, preferably less than about 2, and a bidentate ligand of phosphorus, sulfur, arsenic or antimony. Although the scope of the polymerization is extensive, for purposes of illustration a preferred Group VIII metal compound is palladium acetate, the anion is the anion of an acid selected from trifluoroacetic acid and para-toluenesulfonic acid and the bidentate ligand is selected from 1,3-bis(diphenylphosphino)propane and 1,3-bis[di(2-methoxyphenyl)phosphino]propane.

Polymerization is carried out at polymerization conditions, typically at elevated temperature and pressure, in the gaseous phase or in the liquid phase in the presence of an inert diluent, e.g., a lower alkanol such as methanol or ethanol. The reactants are contacted by conventional methods such as stirring or shaking and subsequent to reaction the polymer product is recovered as by decantation or filtration. The polymer product may contain metallic residues from the catalyst which are removed by contact with a solvent which is selective for the residues. Production of these polymers is illustrated, for example, by published European Patent Applications 181,014, 121,965, 222,454 and 257,663.

The physical properties of the polymer will be determined in part by the molecular weight and by whether the polymer is a copolymer or a terpolymer. Typical melting points are from about 175.degree. C. to about 300.degree. C., more typically from about 210.degree. C. to about 280.degree. C. The structure of the preferred polymers is that of a linear alternating polymer of carbon monoxide, ethylene and any second ethylenically unsaturated hydrocarbon. When terpolymers of carbon monoxide, ethylene and a second ethylenically unsaturated hydrocarbon, e.g., a hydrocarbon of at least 3 carbon atoms, are produced there will be at least two units incorporating moieties of ethylene per unit incorporating a moiety of the second unsaturated hydrocarbon, preferably from about 10 units to about 100 units incorporating moieties of ethylene per unit incorporating a moiety of the second unsaturated hydrocarbon. The polymer chain of the preferred class of polymers is illustrated by the formula

--CO(C.sub.2 H.sub.4 ].sub.x [CO--(B)].sub.y wherein B is the moiety obtained by polymerization of the second ethylenically unsaturated hydrocarbon through the ethylenic unsaturation. The --CO(C.sub.2 H.sub.4 -- units and the --CO(B-- units occur randomly throughout the polymer molecule and the ratio of y:x is no more than about 0.5. In the modification of the invention which employs copolymers of carbon monoxide and ethylene without the presence of a second ethylenically unsaturated hydrocarbon, the term y is zero and the ratio of y:x is also zero. When terpolymers are employed, i.e., y is greater than zero, ratios of y:x from about 0.01 to about 0.1 are preferred. The end groups or "caps" of the polymer chain will depend on the particular materials present during its production and whether and how the polymer has been purified. The precise nature of the end groups is of little significance with regard to the overall properties of the polymer so that the polymer is fairly represented by the polymer chain as depicted above.

The flame retardant compositions of the invention contain a flame retarding quantity of an alkaline earth metal hydroxide which will be a minor quantity, relative to the polymer. By alkaline earth metal hydroxide is meant a hydroxide of a metal of group IIA of the Periodic Table of Elements. While hydroxides of berylium, magnesium, calcium, strontium and barium are suitable, the preferred flame retarding hydroxide is magnesium hydroxide.

In a preferred embodiment the magnesium hydroxide is surface treated to improve the ease of dispersion. Preferably, the magnesium hydroxide is surface treated with a fatty acid. Fatty acids are well known, and are broadly defined in Kirk-Othmer Encyclopedia of Chemical Technology, Interscience Publishers, 1965, Volume 8, pages 811-838. Fatty acids may be natural or synthetic, and are broadly termed aliphatic monocarboxylic acids. These acids have the general formula C.sub.n H.sub.2n+1 COOH where n is 6 to 24. A much preferred fatty acid is stearic acid. A relatively low level of stearic acid is required to treat the magnesium hydroxide, e.g. about 0.01 to about 5 percent by weight of the magnesium hydroxide is useful.

Such modified magnesium hydroxides are commercially available. For example, Zerogen.TM.35 flame retardant from Solem Industries is a low-toxicity halogen-free composition. It is our understanding that Zerogen 35 is magnesium hydroxide modified with stearic acid. Zerogen 35 has temperature stability (i.e. decomposition temperature) in excess of 630.degree. F., and is therefore much preferred with the presently claimed polyketone polymers which are typically processed (i.e. extruded) at temperatures of about 400.degree. to about 600.degree. F. It is preferred that the alkaline earth metal hydroxide utilized herein have a decompositon temperature above about 600.degree. F.

______________________________________Zerogen 35 has the following typical physical properties:______________________________________Specific Gravity, gm/cc 2.26Retain in 325 Mesh, % 0.01Average Particle Size (microns)* 1.1Surface Area (BET, m.sup.2 /gm) 12-15Free Moisture, 105.degree. C. (at 2 hrs.), % <1TGA, Weight Loss at 332.degree. C. (630.degree. F.), % 2Bulk Density (loose, gm/cc) 0.3Bulk Density (packed, gm/cc) 0.6Oil Absorption, cc/100 gm 56______________________________________ *Measured by Micromeretics Sedigraph 5000

The alkaline earth metal hydroxides are employed in an amount sufficient to render the resulting composition flame retardant. Compositions from about 2 to about 50 percent by weight, based on the total composition, of the alkaline earth metal hydroxide are preferred. More preferred are compositions having about 15 to about 40 percent by weight alkaline earth metal hydroxide, while compositions of 20 to about 30 percent by weight are most preferred.

In an alternative embodiment an alkaline earch metal carbonate is also incorporated in the composition to replace a portion of the alkaline earth metal hydroxide. One of the considerations in adding the carbonate is cost.

By alkaline earth metal carbonate is meant a carbonate salt of a metal of Group IIA of the Periodic Table of Elements. While carbonate salts of berylium, magnesium, calcium, strontium and barium are suitable, the preferred flame retarding carbonate salts are carbonates of magnesium and calcium, particularly calcium. If desired the CaCO.sub.3 may be surface treated to improve dispersion. Such surface treatments include treatment with stearic acid or salts of stearic acid.

The alkaline earth metal carbonate is typically provided in the form of a fine powder, for example, above about 0.04 .mu.m but below about 100 .mu.m. The alkaline earth metal carbonate is preferably employed as such, but in alternate modifications alkaline earth metal compounds may be utilized which serve to generate alkaline earth metal carbonates during processing or upon exposure of the resulting composition to heat at temperatures lower than those at which flame would result. An example of a material useful as an alkaline earth metal carbonate precursor is the corresponding alkaline earth metal bicarbonate.

The following relative amounts of polymer, alkaline earth metal hydroxide and alkaline earth metal carbonate are suitable (expressed in weight percent of the total composition):

______________________________________ More Preferred Preferred______________________________________Polyketone Poly- about 60 to about 85% about 60 to about 85%meralkaline earth about 5 to about 30% about 20 to about 30%metal hydroxidealkaline earth about 5 to about 20% about 5 to about 10%metal carbonate______________________________________ Note the percentages should add up to 100 percent in actual compositions.

The relative amount of alkaline earth metal hydroxide to alkaline earth metal carbonate should be 1:1 or greater, preferably the weight ratio should be at least 2:1, for example between 2:1 and 3:1.

The alkaline earth metal hydroxides may be employed with other materials such as ammonium thiosulfate, asbestos, alkali metal carbonates or bicarbonates, e.g., potassium bicarbonate or stannous or stanic oxide. The preferred compositions of the invention, however, are those wherein alkaline earth metal hydroxide is employed as substantially the sole material used to impart flame retardancy to the polyketone composition.

The flame retardant compositions are produced by mixing the alkaline earth metal hydroxide throughout the polyketone polymer. The method of forming the composition is not critical so long as the method results in a uniform mixture of alkaline earth metal hydroxide throughout at least the outer layer of the polyketone polymer. In a preparation of a composition useful in the form in which it is produced, only the outermost portion of the composition need be provided with alkaline earth metal hydroxide. However, in most applications, a flame retardant composition is produced which is then processed further and in such applications the production of a substantially uniform mixture of polyketone polymer and alkaline earth metal hydroxide is preferred. In one modification, the compositions are produced by dry blending the components in particulate form and converting to a substantially uniform composition by application of heat and pressure. Alternatively, the compositions are produced by heating the polyketone polymer until molten and the alkaline earth metal hydroxide thereof is mixed throughout the polymer by use of a high-shear mixer or extruder.

The polymer composition, in addition to polymer and alkaline earth metal hydroxide, may incorporate other conventional additives which do not detract from the flame retardant character of the composition. Examples of such additives are plasticizers, mold release agents and antioxidants which are added by blending or other conventional methods together with or separately from the alkaline earth metal hydroxide.

The flame retardant compositions are processed by injection molding, pressure forming or other conventional fabrication methods. They are characterized by the same combination of good impact, stiffness and heat resistant properties found in the neat polymer, and in addition have excellent flame retardancy. The compositions of this invention are useful in a variety of applications, particularly where exposure to elevated temperature is likely to be encountered. The compositions are useful in the production of parts for the automotive industry, electronics industry and electrical industry. The compositions are particularly useful for those automotive parts located within the engine compartment where high temperatures are encountered or those parts which encounter heat as during the baking of painted surfaces, e.g. wire coatings, connectors, etc.

The compositions of the invention are further illustrated by the following Comparative Examples and Illustrative Embodiments which should not be construed as limiting the invention.

ILLUSTRATIVE EMBODIMENT I

A first terpolymer (Polymer 1) of carbon monoxide, ethylene and propylene was prepared in the presence of a catalyst formed from palladium acetate, trifluoroacetic acid and 1,3-bis(diphenylphosphino)propane. The polymer had a melting point of 219.degree. C. and a limiting viscosity number (LVN) of 1.60 measured at 60.degree. C. in m-cresol. A second terpolymer (Polymer 2) of carbon monoxide, ethylene and propylene was prepared in the presence of a catalyst formed from palladium acetate, trifluoracetic acid and 1,3-bis[di(2-methoxyphenyl)phosphino]propane. The second terpolymer had a melting point of 221.degree. C. and a LVN of 1.83 measured at 60.degree. C. in m-cresol.

COMPARATIVE EXAMPLE I

Polymer 1 of Illustrative Embodiment I was blended with different weight percents of calcium carbonate by use of a twin-screw extruder to extruder to produce nibs. Polymer 2 was also extruded to produce nibs for comparison purposes as a control without the addition of calcium carbonate. The nibs were injection molded into test bars of approximately 4.75 in. by 0.5 in. by 0.125 in. dimensions. The test bars were then sliced lengthwise into 3 equal strips and the edges were smoothed off. These strips were tested for flame retardancy.

Standard test method ASTM D2863-77 was used to evaluate the burning behavior of the different blend compositions. This test measures the minimum concentration of oxygen in an oxygen-nitrogen atmosphere that is necessary to initiate and support a flame for 180 seconds on a test strip. The result of the test is expressed as the percentage of oxygen in the oxygen-nitrogen atmosphere and is called the Limiting Oxygen Index (LOI) of the composition.

The LOI values determined for three different blends of the terpolymer of Illustrative Embodiment I and calcium carbonate are given in Table I together with the LOI of the terpolymer without added calcium carbonate used as a control sample. One can see from the LOI values in Table A that a greater percentage of oxygen was required in an oxygen-nitrogen atmosphere to initiate and support a flame on the samples containing calcium carbonate in comparison to the control sample without calcium carbonate. The flame retardancy of the blend compositions is improved for the samples containing calcium carbonate, however the LOI values are still too low for most commercial applications.

TABLE I______________________________________Sample % Weight Calcium Carbonate LOI*______________________________________Control none 18.5-191 5 23-23.52 10 25.5-263 25 27-27.5______________________________________ *LOI values are expressed as a range obtained for three duplicate test samples.

ILLUSTRATIVE EMBODIMENT II

A linear alternating terpolymer of carbon monoxide, ethylene and propylene was prepared, hereinafter referred to as Polymer 87-011. Polymer 87-011 was prepared in the presence of a catalyst formed from palladium acetate, the anion of trifluoroacetic acid, and 1,3-bis(diphenylphosphino)propane. Polymer 87-011 had a melting point of 218.degree. C. and an LVN of 1.14.

In Illustrative Embodiment II, four fillers (talc, mica, surface treated mica and calcium carbonate) and three flame retardants (Kisuma 5BG magnesium hydroxide, Zerogen 35 surface treated magnesium hydroxide and zinc borate) were dry blended with Polymer 87-011 at amounts of 20 and 40% by weight of the filler/flame retardant on a 15 mm Baker Perkins twin-screw extruder. This equipment had no devolatilization capabilities. Extrusion conditions were:

Atmosphere: air RPM: 300 Feed Rate and Torque: adjusted maximize mixing Temperatures: 425.degree. F., 454.degree. F., 486.degree., 456.degree. F. Feed - - - Die All of the extrudates were foamy except for those from the calcium carbonate blends. Some foaming was expected due to the inability to devolatilize. The extrudates were then pelletized, dried at 50.degree. C. for 16 hours, and compression molded into 5".times.0.5".times.0.125" test schemes for the LOI test.

The LOI results are listed in Table II. As seen in Table II, the compositions containing Kisuma 5BG (a magnesium hydroxide) and Zerogen 35 (a stearic acid treated magnesium hydroxide) are much preferred.

TABLE II______________________________________PRELIMINARY SCREENING OF FLAMERETARDANTS FOR POLYKETONEBASE POLYMER:Polymer 87-011 LVN = 1.14 LEVELFILLER (wt. % based on total blend) LOI______________________________________Talc 20% 22.5Talc 40% 26.5Kisuma 5BG (MgOH) 20% 32.5Kisuma 5BG (MgOH) 40% 41.0Zinc Borate 20% 27.5Zinc Borate 40% 30.5Zerogen 35 (modified 20% 30.5MgOH)Zerogen 35 (modified 40% 39.5MgOH)Mica 20% 24.5Mica 40% 23.5Surfaced treated Mica 20% 21.5Surfaced treated Mica 40% 29.5Calcium Carbonate 20% 22.5Calcium Carbonate 40% 29.5______________________________________

ILLUSTRATIVE EMBODIMENT III

In Illustrative Embodiment III, the polyketone employed was a blend of two specific linear alternating polymers. This blend comprised 33% of the novel polyketone polymer 088-005 and 67% of the novel polyketone polymer 088-006. Polymer 088-005 was a linear alternating terpolymer of carbon monoxide, ethylene and 7 wt% propylene prepared by employing a catalyst composition formed from palladium acetate, the anion of trifluroacetic acid and 1,3-bis[di(methoxy-phenyl)phosphino]propane. Polymer 088-005 had a melting point of 220.degree. C. and a limiting viscosity number (LVN) measured in 60.degree. C. meta-cresol of 1.79. Polymer 088-006 was a linear alternating polymer prepared in a manner identical to to the 088-005 polymer. The 088-006 polymer had a melting point of 223.degree. C. and an LVN of 1.62. The neat polymer blend was formed by drying mixing pellets of the two polymers 088-005 with 088-006 in a conventional manner. The blended mixture was then melt blended in a 30 mm co-rotating twin screw extruder having seven zones and total L/D of 27/1. The melt temperature at the die exit was 260.degree. C. and the temperatures along the barrel were maintained at about 466.degree. F.

Based on the results from Illustrative Embodiment II, three flame retardants were chosen, in conjunction with calcium carbonate, to scale up to larger batch size. About 15 pounds of each of the blends listed in Table III were compounded on a 30 mm ZSK twin-screw extruder.

The goal of this compounding was to incorporate the chosen flame retardants into the polyketone polymer utilizing two stage feed with vacuum devolatilization. The initial screw design was similar to successful screws used when compounding the polyketone with other polymers. This screw was intended to provide good melting and mixing prior to the second stage. This screw ran the neat polymer well; however, severe temperature rises occurred with the downstream addition of the Kisuma 5BG. Possible causes for this were thought to be:

1. First stage too intense. Melt temperature at the point of flame retardant addition triggered foaming of retardant.

2. Insufficient mixing of flame retardant and polymer in second stage.

A single feed, gentle mixing screw was assembled to eliminate the severe temperature rise. The Kisuma 5BG blends continued to foam, so no further compounding with this flame retardant was done. The Zerogen 35 and the Firebrake ZB blends compounded satisfactorily.

The blends were pelletized, dried at 160.degree. F. for 16 hours, and injection molded into test specimens. Room temperature Notched Izod, Flex Modulus, LOI and UL94 tests were run.

The UL94 test is a vertical burn test. A test specimen is hung in a test chamber vertically and a flame held in contact with it for 10 seconds then removed. The time that it takes for the specimen to stop burning is recorded. This is repeated four times with fresh specimens. These times are totaled and if the total is less than 50 seconds then the sample is given a rating of V-0, greater than 50 but less than 250 seconds with no flaming drip is V-1 and greater than 50 but less than 250 seconds with a flaming drip is rated V-2. If the sample burns longer than 250 seconds it is considered a failure.

All test results are listed in Table III.

TABLE III______________________________________PHYSICAL PROPERTIES OF FLAME RETARDED POLY-KETONE POLYMER NOTCHED FLEXCOMPOSITION IZOD MOD. UL94 LOI______________________________________ ft.-lb/in psiPolymer Blend 3.00 260,000 -- 17.588-005,006Polymer Blend88-005,006/Zerogen/CaCO.sub.380/10/10* 1.48 335,000 V-1 29.570/20/10 1.61 390,000 V-0 30.560/30/10 1.17 430,000 V-0 34.575/20/5 1.56 340,000 V-0 30.580/20/0 1.75 340,000 V-0 30.570/30/0 1.83 310,000 V-0 31.560/40/0 1.66 405,000 V-0 35.5Polymer Blend88-005,006/Zinc Borate/CaCO380/10/10 0.94 325,000 -- 24.570/20/10 0.75 410,000 -- 27.560/30/10 0.52 480,000 -- 30.575/20/5 0.75 370,000 -- 29.5______________________________________ Note: All samples had 0.3% Ethanox 330 added based on Polyketone content. All samples were compounded in a 30 mm ZSK Twin Screw Extruder and injection molded. *The amounts listed are weight percent based on total composition.

A number of conclusions can be reached from the data in Table III:

1. With the high processing temperatures required with the high melting polyketone polymer, choice of flame retardant is crucial. Zerogen 35 is a good choice because of its temperature stability in excess of 630.degree. F. Kisuma 5BG apparently does not have as high temperature stability.

2. Screw design is very important. It must provide good mixing without overheating the polymer.

3. The substitution of calcium carbonate for some of the Zerogen 35 does not greatly affect the UL94 rating or the physical properties. The use of calcium carbonate may allow a lower cost without greatly affecting its properties.

COMPARATIVE EXAMPLE II

Comparative Example II is presented to show that Zerogen 35 is is typically employed at very high levels in order to achieve an acceptable V-0 rating when used with other polymers, such as polypropylene.

In Comparative Example II, a blend of 40% weight Himont 6523 polypropylene homopolymer and 60% weight Zerogen 35 was prepared. Compounds were produced using a 30 mm ZSK twin screw extruder and were screened through a 20/40 screen pack. Melt temperature was 460.degree. F. at 300 rpm. Test speciments were injection molded on a 50-ton Newbury injection press at a melt temperature of 440.degree. F. All test specimens were conditioned for 40 hours at room temperature.

______________________________________TEST DATA______________________________________Flame Rating UL94.sup.1 V-0 Flexural.sup.3 Strength 5400Tensile.sup.2 Modulus Izod Impact(.times. 10.sup.3 PSI) 333 (Notched, ft-lb/in) 1.5Tensile.sup.2 @ Yield 2600 Drop Weigh Impact 117 (in-lbs)Tensile.sup.2 @ Break 1800 Melt Flow 4.0 (Cond. L)Elongation @ Break 12 Density 1.336 (gm/cc)Flexural.sup.3 Modulus 418______________________________________ .sup.1 UL94 Test procedure run using a 1/8" thick sample. .sup.2 Cross head speed 0.2 inches/minute. .sup.3 Cross head speed 0.5 inches/minute.

These test data reveal a significant drop in physical properties (e.g. elongation at break drops from over 300% for unfilled PP to 12% for filled PP) when as much as 60% w Zerogen 35 is needed to achieve a V-0 rating.

The results in Comparative Example II are compared with the results in Illustrative Embodiment III where only 20% w Zerogen 35 was needed to achieve a V-0 rating when used with the polyketone polymer of the present invention.

Claims

1. A flame retardant polymer composition comprising a linear alternating polymer of carbon monoxide and at least one ethylenically unsaturated hydrocarbon and a flame retarding quantity of an alkaline earth metal hydroxide.

2. The composition of claim 1 wherein said alkaline earth metal is magnesium hydroxide.

3. The composition of claim 1 wherein said polymer is a linear alternating polymer of the general formula ##STR1## wherein B is the moiety of an ethylenically unsaturated .alpha.-olefin of at least 3 carbon atoms polymerized through the ethylenic unsaturation and the ratio of y:x is no more than about 0.5.

4. The composition of claim 3 wherein said ethylenically unsaturated .alpha.-olefin is propylene.

5. The composition of claim 2 wherein said quantity of magnesium hydroxide is about 2 to about 50 percent by weight, based on the total composition.

6. The composition of claim 5 wherein said quantity of magnesium hydroxide is about 15 to about 40 percent by weight, based on the total composition.

7. The composition of claim 6 wherein said quantity of magnesium hydroxide is about 20 to about 30 percent by weight, based on the total composition.

8. The composition of claim 2 wherein said magnesium hydroxide is surface treated with a fatty acid.

9. The composition of claim 8 wherein said fatty acid is an aliphatic monocarboxylic acid.

10. The composition of claim 8 wherein said fatty acid has the formula C.sub.n H.sub.2n+1 COOH where n is 6 to 24.

11. The composition of claim 8 wherein said fatty acid is stearic acid.

12. The composition of claim 3 wherein the .alpha.-olefin is propylene and the ratio of y:x is from about 0.01 to about 0.2.

13. The composition of claim 3 wherein y is zero.

14. As an article of manufacture, a fabricated article comprising the composition of claim 1.

15. A flame retardant composition comprising:

(a) about 50 to about 85 percent by weight of a linear alternating polymer of carbon monoxide and at least one ethylenically unsaturated hydrocarbon;

(b) about 5 to about 30 percent by weight of an alkaline earth metal hydroxide; and

(c) about 5 to about 20 percent by weight of an alkaline earth metal carbonate, wherein the weight ratio of said alkaline earth metal hydroxide to said alkaline earth metal carbonate is 1:1 or greater.

16. The composition of claim 15 wherein said alkaline earth metal is magnesium hydroxide.

17. The composition of claim 15 wherein said polymer is a linear alternating polymer of the general formula ##STR2## wherein B is the moiety of an ethylenically unsaturated .alpha.-olefin of at least 3 carbon atoms polymerized through the ethylenic unsaturation and the ratio of y:x is no more than about 0.5.

18. The composition of claim 16 wherein said alkaline earth metal is calcium carbonate.

19. The composition of claim 18 wherein the amount of said linear alternating polymer is about 60 to about 85 percent by weight, the amount of said magnesium hydroxide is about 20 to about 30 percent of weight and the amount of said calcium carbonate is about 5 to about 10 percent by weight.

20. The composition of claim 18 wherein said magnesium hydroxide is surface treated with a fatty acid.

21. The composition of claim 20 wherein said fatty acid is an aliphatic monocarboxylic acid.

22. The composition of claim 21 wherein said fatty acid is stearic acid.

23. The composition of claim 1 wherein said alkaline earth metal hydroxide has a decomposition temperature higher than the melting point of said linear alternating polymer.

24. The composition of claim 23 wherein said alkaline earth metal hydroxide has a decomposition temperature above 600.degree. F.

25. The composition of claim 18 wherein said calcium carbonate is surface treated.

26. The composition of claim 25 wherein said calcium carbonate is surface treated with stearic acid.