The present invention generally relates to electromagnetic interference (EMI) shielding, and more particularly (but not exclusively) to flame retardant fabric-over-foam EMI shields formed from environmentally friendly materials, such as halogen-free flame retardants.
The operation of electronic devices generates electromagnetic radiation within the electronic circuitry of the equipment. Such radiation results in electromagnetic interference (EMI), which can interfere with the operation of other electronic devices within a certain proximity. A common solution to ameliorate the effects of EMI has been the development of shields capable of absorbing and/or reflecting EMI energy. These shields are typically employed to localize EMI within its source, and to insulate other devices proximal to the EMI source.
According to one aspect of the present invention, an EMI shield generally includes a resilient core member and an electrically conductive layer. An adhesive bonds the electrically conductive layer to the resilient core member. The adhesive includes halogen-free flame retardant. In various embodiments, the electrically conductive layer can be provided with halogen-free flame retardant and/or a corrosion inhibitor.
In another aspect, the invention provides methods of making EMI shields. In one exemplary implementation, the method generally includes applying halogen-free flame retardant and/or a corrosion inhibitor to an electrically conductive layer, and bonding the electrically conductive layer to a resilient core member with an adhesive including halogen-free flame retardant.
Further aspects of the present invention will become apparent from the detailed description provided hereinafter. It should be understood that the detailed description and specific examples, while indicating various embodiments and methods of the invention, are for illustration purposes only and are not intended to limit the scope of the invention.
The invention will become more fully understood from the detailed description and the accompanying drawings, wherein:
The following description of the exemplary embodiments is merely exemplary in nature and is in no way intended to limit the invention, its application, or uses.
According to various aspects, the invention provides electromagnetic interference (EMI) shields, such as EMI gaskets. In one embodiment, an EMI shield generally includes a resilient core member and an electrically conductive layer. The electrically conductive layer is provided with (e.g., coated, impregnated, combinations thereof, etc.) halogen-free flame retardant. An adhesive bonds the electrically conductive layer to the core member. The adhesive is loaded with an effective amount of halogen-free flame retardant, which in combination with the halogen-free flame retardant provided to the electrically conductive layer, enables the shield to achieve a predetermined flame retardant rating (e.g., a UL 94 vertical flame rating of V0, etc.). The effective amount of halogen-free flame retardant in the adhesive, however, is less than a predetermined percentage below which the loaded adhesive provides at least a predetermined bond strength (e.g., at least about ten ounces per inch width as determined, for example, by a one hundred eighty degree peel test at twelve inches per minute, etc.). Accordingly, this particular embodiment of the EMI shield is halogen-free and environmentally friendly.
In another embodiment, an EMI shield generally includes a resilient core member and an electrically conductive layer. The electrically conductive layer is bonded to the core member with an adhesive. In this particular embodiment, the adhesive is loaded with an effective amount of halogen-free flame retardant such that the shield can achieve a predetermined flame retardant rating (e.g., a UL 94 vertical flame rating of V0, etc.) without flame retardant being provided to the electrically conductive layer. The effective amount of halogen-free flame retardant in the adhesive, however, is less than a predetermined percentage below which the loaded adhesive provides at least a predetermined bond strength (e.g., at least about ten ounces per inch width as determined, for example, by a one hundred eighty degree peel test at twelve inches per minute, etc.). Accordingly, this particular embodiment of the EMI shield is halogen-free and environmentally friendly.
In a further embodiment, an EMI shield generally includes a resilient core member and an electrically conductive layer. An adhesive, which includes halogen-free flame retardant, bonds the electrically conductive layer to the core member. In this particular embodiment, the electrically conductive layer is provided with (e.g., coated, impregnated, combinations thereof, etc.) a halogen-free corrosion inhibitor (e.g., benzotriazole, or other suitable corrosion inhibitor, for example, from the azole family and/or pyrole family, etc.). The corrosion inhibitor can also function as a flame retardant, which in combination with the flame retardant properties of the adhesive enables the shield to achieve a predetermined flame retardant rating (e.g., a UL 94 vertical flame rating of V0, etc.). The effective amount of halogen-free flame retardant in the adhesive, however, is less than a predetermined percentage below which the loaded adhesive provides at least a predetermined bond strength (e.g., at least about ten ounces per inch width as determined, for example, by a one hundred eighty degree peel test at twelve inches per minute, etc.). Accordingly, this particular embodiment of the EMI shield is halogen-free and environmentally friendly.
Other aspects of the invention methods of making and using EMI shields. Further aspects of the invention include adhesives loaded with halogen-free flame retardant. Additional aspects of the invention include electrically conductive materials (e.g., nylon ripstop (NRS) fabrics, mesh fabrics, taffeta fabrics, woven fabrics, non-woven fabrics, knitted fabrics, etc.) that are provided with (e.g., coated, impregnated, combinations thereof, etc.) halogen-free flame retardants and/or corrosion inhibitors. Further aspects include EMI shields in which the electrically conductive layer is not provided with flame retardant or a corrosion inhibitor.
A wide range of materials can be used for the resilient core member 22. In one embodiment, the resilient core member 22 is made of urethane foam having a polyester film scrim attached thereto. Alternatively, other materials can be used for the resilient core member, such as other resiliently compressible materials that are suitable for compression within an opening. Other materials and types can also be used for the scrim including fabrics. Yet other embodiments do not have a scrim attached to the resilient core member.
A wide range of materials can be used for the electrically conductive portion 26. Exemplary materials include conductive fillers within a layer, a metal layer, and/or a conductive non-metal layer. In some embodiments, the electrically conductive portion 26 comprises a metallized or plated fabric in which the metal is copper, nickel, silver, palladium aluminum, tin, alloys, and/or combinations thereof. For example, one particular embodiment includes a nickel copper nylon ripstop (NRS) fabric. In other embodiments, the electrically conductive portion 26 may comprise a layer of material that is impregnated with a metal material to thereby render the layer sufficiently electrically conductive for EMI shielding applications. The particular material(s) used for the electrically conductive portion 26 may vary, for example, depending on the desired electrical properties (e.g., surface resistivity, electrical conductivity, etc.), which, in turn, can depend, for example, on the particular application in which the EMI shield will be used.
In various embodiments, the adhesive layer 24 is an environmentally safe adhesive suitable for providing good bond strength between the electrically conductive portion 26 and the resilient core member 22. The adhesive layer 24 can include a wide range of suitable adhesives. In one embodiment, the adhesive layer 24 includes a solvent based polyester adhesive that is loaded with an effective amount of flame retardant to enable the EMI shield to achieve a predetermined flame rating while at the same time having good bond strength and retaining properties suitable (e.g., shielding effectiveness, bulk resistivity, etc.) for EMI shielding applications.
Flame ratings can be determined using the Underwriters Laboratories Standard No. 94, “Tests for Flammability of Plastic Materials for Parts in Devices and Appliances” (5th Edition, Oct. 29, 1996) or using an ASTM (American Society for Testing and Materials) flammability test. In one embodiment, the adhesive layer 24 includes an effective amount of flame retardant such that the EMI shield 20 has a UL 94 vertical flame rating of V0. In other embodiments, the adhesive layer may include less flame retardant (or lesser effective flame retardants) such that the EMI shield can only achieve a lower UL94 flame rating such as V1, V2, HB, or HF-1. The desired UL94 flame rating can depend, for example, on the particular application or installation for the EMI shield.
While the adhesive can include at least an effective amount of halogen-free flame retardant to achieve a predetermined flame rating, the adhesive can also include more than that effective amount. In various embodiments, the adhesive does not include more than a predetermined percentage by dry weight of the halogen-free flame retardant, below which percentage the adhesive provides at least a predetermined bond strength. As recognized by the inventor hereof, there is a delicate balance that should be maintained with the halogen-free flame retardant and the adhesive for some embodiments of the invention. If the adhesive contains too much halogen-free flame retardant, the bond strength can be compromised. But if the adhesive does not include enough halogen-free flame retardant, then the EMI shield may not be able to meet the desired UL94 flame rating (e.g., V0, V1, V2, HB, HF-1, etc.). Accordingly, in various embodiment, the adhesive includes at least an effective amount of halogen-free flame retardant for providing the shield with a predetermined UL flame rating, but less than a predetermined percentage below which the adhesive provides at least a predetermined bond strength.
In various embodiments, the halogen-free flame retardant is a phosphorous-based flame retardant. In one embodiment, the adhesive includes an amount of halogen-free flame retardant of at least about thirty percent (±five percent) but not more than about seventy percent by dry weight. In another embodiment, the adhesive includes an amount of halogen-free flame retardant of at least about fifty percent but not more than about sixty-three percent by dry weight. In yet another embodiment, the adhesive includes an amount of halogen-free flame retardant of about sixty-three percent by dry weight. In still another embodiment, the adhesive includes an amount of halogen-free flame retardant of about fifty-five percent by dry weight. In a further embodiment, the adhesive includes an amount of halogen-free flame retardant of about fifty percent by dry weight. In various embodiments, the adhesive is formed into a layer that may be laminated in production of the EMI shield.
The adhesive may include any of a wide range of flame retardants, including environmentally friendly flame retardants that are substantially free or entirely free of halogens (e.g., bromines, chlorines, etc.). Particular examples of commercially available halogen-free phosphorous-based flame retardants are sold by Bostik, Inc. of Middleton, Mass. and Apex Chemical Company of Spartanburg, S.C. Other exemplary flame retardants that can be used include mineral oxides (e.g., magnesium hydroxide, antimony oxide, etc.), metal hydrates (e.g., aluminum trihydrate, etc.) boron compounds (e.g., boric acid, borax, etc.), melamines, and silicones.
The following non-limiting examples, flammability test results, tables (
For one particular series of tests, the test specimens included a commercially available Woodbridge four pound per cubic foot density urethane foam 0.125 inches thick by 0.5 inches wide. This foam was made in a layer thickness of 3.0 millimeters, which is suitable for a UL sample. The test specimens further included an electrically conductive metallized fabric material laminated to an adhesive layer. The adhesive layer included a polyester adhesive with about fifty-five percent by dry weight of a halogen-free phosphorous-based flame retardant. Specifically, the adhesive layer included 10-336 adhesive produced by Bostik, Inc. having a thickness of about 0.0025 inches. Aspects of the invention, however, are not limited to this particular type and kind of adhesive.
In this series of tests, the fabric was provided with urethane that did not include flame retardant (Non-FR urethane). The Non-FR urethane coating included about eighteen percent urethane solids such that the weight pick-up from the Non-FR urethane coating was about 0.15 ounces per square yard (opsy). Further, the fabric was laminated using a flat bed laminator set at two hundred sixty degrees Fahrenheit at approximately fifteen feet per minute (although other suitable means can also be employed). The fabric and adhesive layer may also be trimmed to any suitable size or shape.
The foam was joined together with the fabric and adhesive layer using a series of heated dies to form the shield in the desired shape. Samples of this shield embodiment having dimensions of approximately 3.0 millimeters thick by 12.5 millimeters wide by 125 millimeters long were then tested per the UL94 flame rating of V0. The exemplary flammability test results are set forth below in Table 1 for purposes of illustration only.
Total Afterflame 32
As shown in Table 1 above, this particular embodiment of the EMI shield included at least an effective amount of halogen-free flame retardant within the adhesive to provide the shield with a UL94 flame rating of V0.
For another series of tests, the test specimens included a commercially available Woodbridge four pound per cubic foot density urethane foam 0.125 inches thick by 0.5 inches wide. This foam was made in a layer thickness of 3.0 millimeters, which is suitable for a UL sample. The test specimens further included an electrically conductive metallized fabric material laminated to an adhesive layer. The adhesive layer included a polyester adhesive (e.g., 10-335 adhesive produced by Bostik, Inc., etc.) with about sixty-three percent by dry weight of a halogen-free phosphorous-based flame retardant.
In this series of tests, the fabric was not provided with a flame retardant. Further, the fabric was laminated using a flat bed laminator set at two hundred sixty degrees Fahrenheit at approximately fifteen feet per minute (although other suitable means can also be employed). The fabric and adhesive layer may also be trimmed to any suitable size or shape.
The foam was joined together with the fabric and adhesive layer using a series of heated dies to form the shield in the desired shape. Samples of this shield embodiment having dimensions of approximately 3.0 millimeters thick by 12.5 millimeters wide by 125 millimeters long were then tested per the UL94 flame rating of V0. The exemplary flammability test results are set forth below in Table 2 for purposes of illustration only.
Total Afterflame 46
As shown in Table 2, this particular embodiment of the EMI shield included at least an effective amount of halogen-free flame retardant within the adhesive to provide the shield with a UL94 flame rating of V1. These flammability results may be suitable for some applications as the desired flame rating can vary depending, for example, on the particular application in which the EMI shield will be used.
For another series of tests, the test specimens included a commercially available Woodbridge four pound per cubic foot density urethane foam 0.125 inches thick by 0.5 inches wide. This foam was made in a layer thickness of 3.0 millimeters, which is suitable for a UL sample. The test specimens further included an electrically conductive metallized fabric material that was again laminated to an adhesive layer. The adhesive layer included about sixty-three percent by dry weight of a halogen-free phosphorous-based flame retardant.
But unlike the above test specimens, the fabric was provided with a material (e.g., coating) that included halogen-free flame retardant and urethane such that the weight pick-up therefrom (from the material including the halogen-free flame retardant and urethane) was about 0.27 ounces per square yard (opsy). The halogen-free flame retardant was a water-based urethane dispersion (having about thirteen percent solids by weight) including about fifteen percent by weight of cyclic phosphonate esters with the remaining balance being de-ionized water. This phosphorous-based flame retardant liquid was then applied to the fabric by dipping the fabric into the flame retardant. The excess flame retardant was removed from the fabric (e.g., by squeezing the fabric with a pair of rubber nip rollers at about twenty pounds per square inch, etc.) and then drying the fabric in an oven when the oven temperature is at about three hundred twenty degrees Fahrenheit for twenty five minutes residence time in the oven. After drying, the flame retardant urethane coating included about fifty-four percent phosphorous-based flame retardant and about forty-six percent urethane.
In this particular embodiment, the fabric was laminated using a flat bed laminator set at about two hundred sixty degrees Fahrenheit at approximately fifteen feet per minute (although it may be laminated using other suitable means for achieving a desired adherence). The foam was joined together with the electrically conductive layer and the adhesive laminate using a series of heated dies to form the shield in the desired shape. Samples of this embodiment of a shield having dimensions of approximately 3.0 millimeters thick by 12.5 millimeters wide by 125 millimeters long were then tested per the UL94 flame rating of V0. The shield of this embodiment in which the fabric was provided with halogen-free flame retardant, in combination with an adhesive loaded with about sixty-three percent by dry weight of halogen-free flame retardant, met the UL94 flame rating as V0 as shown in Table 3 below.
Total Afterflame 28
For another series of tests, the test specimens included a commercially available Woodbridge four pound per cubic foot density urethane foam 0.125 inches thick by 0.5 inches wide. This foam was made in a layer thickness of 3.0 millimeters, which is suitable for a UL sample. The test specimens further included an electrically conductive metallized fabric material that was laminated to an adhesive layer. The adhesive layer included a polyester adhesive (e.g., 10-335 adhesive produced by Bostik, Inc., etc.) with about fifty percent by dry weight of a halogen-free phosphorous-based flame retardant.
The fabric was provided with a material (e.g., coating) that included halogen-free flame retardant and urethane such that the weight pick-up therefrom was about 0.27 ounces per square yard (opsy). In this particular embodiment, the halogen-free flame retardant was a water-based urethane dispersion (having about thirteen percent solids by weight) including about fifteen percent by weight of cyclic phosphonate esters with the remaining balance being de-ionized water. This phosphorous-based flame retardant liquid was applied to the metallized fabric layer by dipping the metallized fabric into the flame retardant. The excess flame retardant was removed from the metallized fabric (e.g., by squeezing the fabric with a pair of rubber nip rollers at twenty pounds per square inch, etc.) and then drying the metallized fabric in an oven when the oven temperature is at about three hundred twenty degrees Fahrenheit for twenty five minutes residence time in the oven. After drying, the flame retardant urethane coating included about fifty-four percent phosphorous-based flame retardant and about forty-six percent urethane.
In this particular embodiment, the fabric was laminated using a flat bed laminator set at about two hundred sixty degrees Fahrenheit at approximately fifteen feet per minute (although it may be laminated using other suitable means for achieving a desired adherence). The foam was joined together with the electrically conductive layer and the adhesive laminate using a series of heated dies to form the shield in the desired shape. Samples of this embodiment of a shield having dimensions of approximately 3.0 millimeters thick by 12.5 millimeters wide by 125 millimeters long were tested per the UL94 flame rating of V0. As shown in Table 4 below, the shield of this embodiment in which the fabric was provided with halogen-free flame retardant, in combination with an adhesive loaded with about fifty percent by dry weight of halogen-free flame retardant, met the UL94 flame ratings of V0.
Total Afterflame 27
In the latter two tests described above, the fabric was provided with halogen-free flame retardant urethane such that the weight pick-up therefrom was about 0.27 ounces per square yard (opsy). In other embodiments, however, the electrically conductive fabric (e.g., nylon ripstop (NRS) fabrics, mesh fabrics, taffeta fabrics, woven fabrics, non-woven fabrics, knitted fabrics, etc.) can be provided with (e.g., coated, impregnated, combinations thereof, etc.) a different amount of halogen-free flame retardant. Various embodiments include an electrically conductive fabric provided with halogen-free flame retardant urethane (e.g., coating, etc.) such that the weight pick-up therefrom is between about 0.16 opsy and about 0.33 opsy (e.g., about 0.16 opsy, about 0.20 opsy, about 0.26 opsy, about 0.27 opsy, about 0.33 opsy, etc.).
In various embodiments, an electrically conductive fabric includes a halogen-free flame retardant urethane coating having a thickness of about one micron or less. In such embodiments, the thickness of the halogen-free flame retardant urethane coating can vary across the surface of the fabric. Alternatively, the thickness of the halogen-free flame retardant urethane coating can be substantially uniform across the surface of the fabric. To help maintain electrical conductivity, the fabric in various embodiments is not entirely permeated or encapsulated with flame retardant urethane.
In some embodiments, the electrically conductive fabric may be provided with a halogen-free corrosion inhibitor (e.g., benzotriazole, or other suitable corrosion inhibitor, for example, selected from the azole family and/or pyrole family, etc.). Depending on the particular corrosion inhibitor used, the corrosion inhibitor may function as a halogen-free flame retardant. In such embodiments, the corrosion inhibitor may thus be referred to herein as a halogen-free flame retardant. In yet other embodiments, the electrically conductive fabric is provided (e.g., coated, etc.) with both a corrosion inhibitor and flame retardant.
In still other embodiments, the electrically conductive fabric is provided (e.g., coated, etc.) with a material that does not including any halogen-free flame retardant. For example, in the test first described above, the electrically conductive layer was provided with a Non-FR urethane coating having about eighteen percent urethane solids such that the weight pick-up from the Non-FR urethane coating was about 0.15 opsy. Yet other embodiments include an electrically conductive fabric provided with Non-FR urethane (e.g., coating, etc.) having about ten percent to about eighteen percent urethane solids such that the weight pick-up on the fabric is between about 0.05 opsy and about 0.35 opsy (e.g., about 0.05 opsy, about 0.15 opsy, about 0.35 opsy, etc.).
By way of example,
While the halogen-free flame retardant provided to the fabrics in
In some embodiments, the halogen-free flame retardant urethane provided (e.g., applied, coated, impregnated, combinations thereof, etc.) to the electrically conductive portion is formed, for example, by combining together while substantially continuously, vigorously mixing in the following exemplary ratio and order about thirty-five percent by weight of Soluol 1024 water-based urethane dispersion (having about thirty-seven percent solids) including about fifty percent by weight of de-ionized water and about fifteen percent by weight of phosphorous-based flame retardant. The resulting flame retardant urethane includes about twenty-nine percent solids and has a viscosity of about twenty centipoise per second (cps). Accordingly, and after drying in this particular embodiment, the halogen-free flame retardant urethane provided to the electrically conductive portion includes about forty-six percent by dry weight of urethane and about fifty-four percent by dry weight of flame retardant. In another embodiment, however, the electrically conductive portion is provided (e.g., applied, coated, impregnated, combinations thereof, etc.) with a halogen-free flame retardant urethane that includes about fifty-two percent by dry weight of halogen-free flame retardant and about of about forty-eight by dry weight of urethane. Exemplary phosphorous-based flame retardants that can be used include cyclic phosphonate ester blends available from Sovereign Specialty Chemicals, Inc. of Chicago, Ill. and/or from AKSO Nobel Phosphorous Chemicals, Inc. of Dobbs Ferry, N.Y. Alternatively, other suitable flame retardants can be used including mineral oxides (e.g., magnesium hydroxide, antimony oxide, etc.), metal hydrates (e.g., aluminum trihydrate, etc.) boron compounds (e.g., boric acid, borax, etc.), melamines, silicones, among others.
In various embodiments, the resilient core member (e.g., urethane foam, etc.) is also provided with flame retardant. For example, various embodiments include a resilient core member provided (e.g., impregnated with, etc.) with an antimony flame retardant such that the resilient core member is able to achieve a UL rating of HF1.
Accordingly, various EMI shields of the present invention include a core member, an electrically conductive portion, and an adhesive bonding the electrically conductive portion to the core member, wherein the core member, the electrically conductive portion, and the adhesive are each provided with (e.g., coated, impregnated, combination thereof, etc.) a flame retardant. In these embodiments, the flame retardant applied to the electrically conductive portion can be a corrosion inhibitor, such as benzotriazole or other suitable corrosion inhibitor, for example, selected from the azole family and/or pyrole family, etc.
In various embodiments, an EMI shield generally includes a resilient core member and an electrically conductive layer. In these particular embodiments, the electrically conductive layer is bonded to the core member with an adhesive layer having a thickness of about 0.0025. The adhesive layer is formed from 10-336 adhesive sold by Bostik, Inc. The inventor hereof has recognized that with this particular adhesive, the EMI shield can achieve a UL94 flame rating of V0 without any flame retardant being provided to the electrically conductive layer. For example, the electrically conductive layer in one embodiment includes a Non-FR urethane coating having about eighteen percent urethane solids such that the weight pick-up from the Non-FR urethane coating was about 0.15 opsy. Yet other embodiments include an electrically conductive layer provided with Non-FR urethane (e.g., coating, etc.) having about ten percent to about eighteen percent urethane solids such that the weight pick-up on the fabric is between about 0.05 opsy and about 0.35 opsy (e.g., about 0.05 opsy, about 0.15 opsy, about 0.35 opsy, etc.).
In further embodiments, an EMI shield generally includes a resilient core member and an electrically conductive layer. An adhesive, which include halogen-free flame retardant, bonds the electrically conductive layer to the core member. In these particular embodiments, the electrically conductive layer is provided with (e.g., coated, impregnated, combinations thereof, etc.) a halogen-free corrosion inhibitor (e.g., benzotriazole, or other suitable corrosion inhibitor, for example, selected from the azole family and/or pyrole family, etc.). Depending on the particular corrosion inhibitor used, the corrosion inhibitor may function as a halogen-free flame retardant, in which case, the corrosion inhibitor may thus be referred to herein as a halogen-free flame retardant. This corrosion inhibitor can be added to a urethane coating, which is applied to the electrically conductive layer. The inventor hereof has recognized that when halogen-free EMI shields are exposed to high temperature and humidity (e.g., sixty degrees Celsius or higher temperatures, ninety percent relative humidity or higher) for several days, a small amount of corrosion may form when the EMI shields are in contact with certain metals. Adding a corrosion inhibitor to the EMI shield can greatly improve the corrosion resistance of the halogen-free EMI shield in a high temperature and high humidity environment. In various embodiments, the electrically conductive layer of the EMI shield is provided with (e.g., coated, impregnated, combinations thereof, etc.) urethane that includes a corrosion inhibitor additive to thereby help protect the EMI shield from corrosion in high temperature and humidity applications. In one embodiment of a halogen-free EMI shield, the electrically conductive layer is provided or coated with liquid urethane having an amount of Benzotriazole corrosion inhibitor of at least about two percent by liquid weight. In another embodiment of a halogen-free EMI shield, the electrically conductive layer is provided or coated with liquid urethane having an amount of Benzotriazole corrosion inhibitor of at least about one percent by liquid weight. In a further embodiment of a halogen-free EMI shield, the electrically conductive layer is provided or coated with a dry urethane film having an amount of Benzotriazole corrosion inhibitor of at least about four percent by dry weight. Alternatively, other suitable corrosion inhibitors and/or in other amounts can be used depending on the particular application in which the EMI shield will be used.
Accordingly, various embodiments of the present invention include fabric-over-foam EMI shields that are formed from environmentally friendly retardants (e.g., halogen-free flame retardants, etc.) and still are able achieve a UL flame rating of V0 while also having a bond strength of at least ten ounces per inch width (e.g., as determined by standard testing, for example, such as a one hundred eighty degree peel at twelve inches per minute, etc.) to a foam and a scrim attached to the foam and retaining properties suitable (e.g., shielding effectiveness, bulk resistivity, etc.) for EMI shielding applications.
The teachings of the present invention can be applied in a wide range of applications. Accordingly, the specific references to electromagnetic interference shielding applications should not be construed as limiting the scope of the present invention to use in only electromagnetic interference shielding applications.
The description of the invention is merely exemplary in nature and, thus, variations that do not depart from the gist of the invention are intended to be within the scope of the invention. Such variations are not to be regarded as a departure from the spirit and scope of the invention.
This application claims priority to U.S. Provisional Application 60/651,252, filed Feb. 9, 2005, the entire disclosure of which is incorporated herein by reference.
Number | Date | Country | |
---|---|---|---|
60651252 | Feb 2005 | US |