Flame-retardant molded component

Abstract

Flame-retardant polyester monofilaments formed by extrusion from a mixture consisting essentially of 5 to 20 weight percent melamine cyanurate and 3 to 10 weight percent organopolyphosphonate with the balance being either poly(ethylene terephthalate) or poly(ethylene naphthalate).

Description

FIELD OF THE INVENTION

This invention is concerned with a flame-retardant molded component. The invention is particularly applicable to monofilaments for formation into braided sleeves used to protect electrical wires or pipes.

BACKGROUND OF THE INVENTION

It is well-known to form molded components from polymers such as nylon 6. For example, braided sleeves used for protecting wires or pipe from abrasion damage, for example, in an engine compartment of a vehicle, are often formed from monofilaments of nylon 6. The monofilaments have a diameter of about 0.25 mm to about 3.25 mm.

It is also well-known to provide polyamides, e.g., nylon 6 or nylon 66, or other polymers with flame-retardancy properties by filling them with flame-retardant materials. Typical applications include molded containers for electrical equipment and coatings for electrical wires. Melamine cyanurate is a known flame-retardant filler for use in polyamides for such applications. In the event of fire, the melamine cyanurate decomposes giving off flame-retardant gases. However, as the proportion of melamine cyanurate increases, the flexibility and surface quality of the material decreases making the material prone to cracking. For this reason, providing sufficient melamine cyanurate for the required flame-retardancy renders the material unsuitable for many uses, for example, for forming into the above-mentioned monofilaments. For this reason, the protective sleeves referred to above are not formed from flame-retardant monofilaments despite the obvious fire risks present in engine compartments.

Polyphosphonates are known as flame-retardant fillers in some polymeric matrices. However, they are not effective enough when used alone to enable a molded component to pass flame-retardancy tests.

SUMMARY AND OBJECTS OF THE INVENTION

It is an object of the present invention to provide a flame-retardant molded component which combines good flame-retardancy properties with good flexibility and good surface quality.

DETAILED DESCRIPTION OF THE INVENTION

The invention provides a flame-retardant molded component comprising a matrix-forming polymer material, characterized in that the component also comprises 5 to 20 weight percent of melamine cyanurate and 3 to 10 weight percent of a polyphosphonate.

In a component according to the invention, it is found that the presence of both melamine cyanurate and a polyphosphonate enables a greater proportion of melamine cyanurate to be included before the flexibility and surface quality become unacceptable. Furthermore, since the polyphosphonate itself has flame-retardancy properties, the quantity of melamine cyanurate required is reduced. The polyphosphonate also acts as a plasticizer improving the mechanical properties of the component and assisting the dispersion of the melamine cyanurate. In particular, it is found that the component can be molded in the form of a successful flame-retardant monofilament.

Preferably, the quantity of polyphosphonate is 3 to 10 weight percent.

The matrix of a component according to the invention is preferably formed from nylon 6, but nylon 12 or 66 are also possible. Also possible are poly(ethylene terephthalate) and poly(ethylene naphthalate).

The polyphosphonate is preferably an organopolyphosphate called Amguard P45 and obtainable from Albright & Wilson.

There now follows a detailed description of an example which is illustrative of the invention.

In the example, 85 weight percent of nylon 6 was compounded with 10 weight percent of melamine cyanurate in the form of particles averaging 10 microns in diameter and with 5 weight percent of Amguard P45. The mixture was extruded as a monofilament having a diameter of 3.25 mm. This monofilament was braided into a protective sleeve in a conventional manner.

The sleeve achieved the UL1441 VW-1 requirements for electrical sleeving and passed the UL94 Vo standard for flame retardancy at 0.8 mm thickness. The monofilaments had good flexibility and surface quality.

Claims

1. A flame-retardant polyester monofilament formed by a process comprising the steps of compounding a mixture consisting essentially of 5 to 20 weight percent melamine cyanurate and 3 to 10 weight percent of an organopolyphosphonate, with the balance being a polymer selected from the group consisting of poly(ethylene terephthalate) and poly(ethylene naphthalate), and extruding as a monofilament said compounded mixture.

2. The flame-retardant polyester monofilament of claim 1, comprising from 5 to 15 weight percent of melamine cyanurate.

3. The flame-retardant polyester monofilament of claim 2, comprising 10 weight percent of melamine cyanurate and 5 weight percent of organopolyphosphonate.