Claims
- 1. A crosslinkable polymeric composition comprising:
- (a) a polymer selected from the group consisting of copolymers of ethylene and vinyl ethers of C.sub.2-6 aliphatic carboxylic acids, copolymers of ethylene and C.sub.1-6 alkyl acrylates, copolymers of ethylene and C.sub.1-6 alkyl methacrylates, or mixtures thereof;
- (b) 80 to 400 phr inorganic filler selected from the group consisting of hydrated aluminum oxide, hydrated magnesia, hydrated calcium silicate, and hydrated magnesium carbonate;
- (c) 0.5 to 8 phr of lower alkyl-, alkenyl-, alkynyl- or aryl-alkoxysilane having from 1 to 3 C.sub.1-6 alkoxy substituents;
- (d) 0.5 to 8 phr antioxidant; and
- (e) 0.25 to 8 phr low molecular weight polymeric processing additive comprised of aliphatic resins having an average molecular weight less than 2000 and containing ester functional groups.
- 2. The crosslinkable polymeric composition of claim 1 wherein the polymeric processing additive (e) is a mixture of hydrocarbon resin oligomers and ester-containing resin oligomers and wherein the predominant oligomers have molecular weights below 2000.
- 3. The crosslinkable polymeric composition of claim 2 wherein the polymer (a) is ethylene-vinyl acetate copolymer, ethylene-butyl acrylate copolymer, or mixtures thereof; and (d) is a thio compound, a hindered phenol, polymerized 1,2-dihydro-2,2,4-trimethyl quinoline, tris(3,5-di-t-butyl-4-hydroxy benzyl)isocyanurate or mixtures thereof.
- 4. The crosslinkable polymeric composition of claim 3 additionally containing from 1 to 8 phr of a chemical crosslinking agent.
- 5. The crosslinkable polymeric composition of claim 4 wherein the chemical crosslinking agent is an organic peroxide, the alkoxysilane (c) is a vinyl alkoxysilane, and the polymeric processing additive (e) has a specific gravity from 0.92 to 0.98 and softening point from 90.degree. C. to 110.degree. C.
- 6. The crosslinkable polymer composition of claim 5 additionally containing 0.25 to 5 phr of a second processing additive selected from the group consisting of a fatty acid, a calcium soap of a fatty acid, an aluminum soap of a fatty acid, a fatty acid amide, a mixture of a fatty acid and a fatty acid amide, a natural or synthetic wax and low molecular weight polyethylene.
- 7. The crosslinkable polymeric composition of claim 6 containing 80 to 200 phr (b), 0.75 to 4 phr (c), 1 to 6 phr (d), 0.25 to 5 phr (e) and 1.5 to 5 phr organic peroxide.
- 8. The crosslinkable polymeric composition of claim 7 wherein the polymer (a) is an ethylene-vinyl acetate copolymer having from 9% to 30% vinyl acetate polymerized and a melt index from 0.5 to 5.
- 9. The crosslinkable polymeric composition of claim 7 wherein the hydrated inorganic filler (b) is hydrated alumina.
- 10. The crosslinkable polymeric composition of claim 7 wherein the alkoxysilane (c) is vinyltrimethoxysilane.
- 11. The crosslinkable polymeric composition of claim 7 wherein the antioxidant (d) is a mixture of distearyl-3,3'-thiodipropionate and tetrakis(methylene (3,5-di-t-butyl-4-hydroxyhydrocinnamate)) methane.
- 12. The crosslinkable polymeric composition of claim 7 wherein the antioxidant (d) is a mixture of a bis alkyl sulfide and tetrakis(methylene (3,5-di-t-butyl-4-hydroxyhydrocinnamate)) methane.
- 13. The crosslinkable polymeric composition of claim 7 wherein the organic peroxide is dicumyl peroxide.
- 14. The crosslinkable polymeric composition of claim 7 wherein the organic peroxide is alpha, alpha'-bis(t-butylperoxy) diisopropylbenzene.
- 15. The crosslinkable polymeric composition of claim 7 wherein the second processing agent is a mixture of ethylene-bis-stearamide and lauric acid.
- 16. The crosslinkable polymeric composition of claim 7 wherein the polymeric processing additive (e) is a mixture of aliphatic hydrocarbon oligomers produced by the polymerization of a mixed olefin feed obtained from petroleum cracking with a minor amount of an olefin-vinyl ester copolymer.
- 17. The crosslinkable polymeric composition of claim 16 wherein the olefin-vinyl ester copolymer is an ethylene-vinyl acetate copolymer containing 12 to 32 percent vinyl acetate.
- 18. In a crosslinkable polymeric composition comprising a polymer selected from the group consisting of copolymers of ethylene and vinyl esters of C.sub.2-6 aliphatic carboxylic acids, copolymers of ethylene and C.sub.1-6 alkyl acrylates, copolymers of ethylene and C.sub.1-6 alkyl methacrylates, or mixtures thereof, 80 to 400 phr inorganic filler selected from the group consisting of hydrated aluminum oxide, hydrate magnesia, hydrated calcium silicate, or hydrated magnesium carbonate, 0.5 to 5 phr lower alkyl-, alkenyl-, alkynyl- or aryl-alkoxysilane having from 1 to 3 C.sub.1-6 alkoxy substituents and 0.5 to 8 phr antioxidant; the improvement which comprises admixing with said composition an amount of low molecular weight polymeric processing additive comprised of aliphatic resins having an average molecular weight less than 2000 and containing ester functionality to effectively increase the scorch resistance of the composition during processing and, after cure, to increase the heat stability of the composition.
- 19. The improvement according to claim 18 wherein the copolymer is an ethylene-vinyl acetate copolymer having from 9% to 30% vinyl acetate polymerized and a melt index from 0.5 to 5, the hydrated inorganic filler is hydrated alumina and 1 to 8 phr organic peroxide crosslinking agent is included in the composition.
- 20. The improvement according to claim 19 wherein the polymeric processing additive is a mixture of hydrocarbon resin oligomers and ester-containing resin oligomers wherein the predominant oligomers have molecular weights below 2000, said oligomer mixture having a specific gravity from 0.92 to 0.98 and softening point from 90.degree. C. to 100.degree. C.
- 21. The improvement according to claim 20 wherein the antioxidant is a mixture of tetrakis (methylene (3,5-di-t-butyl-4-hydroxyhydrocinnamate)) methane with distearyl-3,3'-thiodipropionate or a bis alkyl sulfide.
- 22. The improvement according to claim 21 wherein the alkoxysilane is vinyltrimethoxysilane.
- 23. The improvement according to claim 22 wherein the polymeric processing additive is present in conjunction with ethylene-bis-stearamide and lauric acid and the total processing additives comprise 1 to 6 phr.
- 24. The improvement according to claim 23 wherein the polymeric processing additive is a mixture of aliphatic hydrocarbon oligomers produced by the polymerization of a mixed olefin feed obtained from petroleum cracking with a minor amount of an olefin-vinyl ester copolymer.
- 25. The improvement according to claim 24 wherein the olefin-vinyl ester copolymer is an ethylene-vinyl acetate copolymer containing 12 to 32 percent vinyl acetate.
Parent Case Info
This is a continuation of application Ser. No. 07/562,762, filed Aug. 3, 1990 which is now abandoned.
US Referenced Citations (8)
Non-Patent Literature Citations (1)
Entry |
Product Specification "Polydis TRO60.RTM." Struktol Co. 201 E. Steels Corners Rd. Stow, Ohio 44224. |
Continuations (1)
|
Number |
Date |
Country |
Parent |
562762 |
Aug 1990 |
|