Flat battery

TECHNICAL FIELD

The present invention relates to a flat battery used for D.C. power sources of thin devices such as watches, pocket calculators, and memory cards, as well as for memory backup power sources. More specifically the present invention pertains to an ultra-thin battery of especially not greater than 1 mm in thickness, wherein a power generation element is sealed with a case, a sealing plate, and a gasket.

BACKGROUND ART

Organic electrolytic solution-containing flat batteries (hereinafter simply referred to as ‘flat batteries’), where a power generation element obtained by combining an alkaline metal or the alloy thereof with an organic electrolytic solution is placed in a flat battery case (hereinafter simply referred to as ‘case’), have high reliability and high potential for size and weight reduction, so that the use of the flat batteries have been increasing as main power sources of various electronic devices and memory backup power sources.

With an increase in demand for card-type thin electronic devices, thinner batteries are required as their main power sources and backup power sources. Typical applications of the card-type electronic devices include ID cards and prepaid cards. Electronic settlement with the IC card will be common in near future, and the market of thin batteries will be expected to expand significantly.

Since the thickness of the typical credit cards is about 1 mm, it is accordingly required that the thickness of the batteries used for the thin devices is not greater than 1 mm.

The following problems, however, arise by simply reducing the thickness of the prior art flat battery to 1 mm or less in order to fulfill the requirement discussed above. In

FIG. 13

, a sectional view schematically illustrating the structure of a prior art coin type battery is shown. The prior art coin type battery having the thickness of greater than 1 mm as illustrated in

FIG. 13

includes a power generation element that is sealed with a case

21

and a sealing plate

22

having a U-shaped curved periphery

22

a

via a gasket

23

.

In the process of manufacturing the battery of approximately 1 mm in thickness, however, there is difficulty in press working to form-the U-shaped curved periphery

22

a.

Even if press working is allowed, the size is not stabilized and the resulting battery has poor leakage resistance.

Then, as shown in

FIG. 14

, other flat batteries have been proposed (for example, the U.S. Pat. No. 5,486,431), where by using a sealing plate (hat-shaped sealing plate)

12

including a flat central section projected outward of a case and a flat peripheral section extending substantially parallel to the flat central section, a case

11

is fitted to the periphery of the sealing plate

12

in a case

11

via a gasket

13

.

FIG. 14

is a sectional view schematically illustrating the structure of this another prior art flat battery.

In the flat battery having the structure of

FIG. 14

, a power generation element, the gasket

13

, and the sealing plate

12

are placed on the case

11

having a top-open circumferential wall, and the opening end of the circumferential wall is curved (bent) inward for sealing. This structure does not require formation of the U-shaped curved periphery

22

a

on the periphery of the sealing plate

22

as in the case of the coin type battery shown in

FIG. 13

to allow press working and relatively facilitate manufacture of the battery.

The gasket

13

is simply in the state of being interposed between the case

11

and the upper face and the lower face of the flat periphery section of the sealing plate

12

and the drawbacks of this structure are accordingly that the force applied to the gasket

13

is insufficient and that the resulting battery has poor leakage resistance. This is because, in the coin type battery shown in

FIG. 13

, the curved periphery

22

a

of the sealing plate

22

partly presses the gasket

23

to enhance the leakage resistance when sealing but, in the flat battery shown in

FIG. 14

, it is difficult to form a curved portion on the sealing plate

12

to partly press the gasket

13

.

Further, the case and the sealing plate should be thinned to reduce the thickness of the resulting battery. There is a problem that decreasing the thickness of the case, however, undesirably lowers the strength of the opening end of the case bent inward. This results in lowering the leakage resistance and durability of the battery.

In order to overcome the drawbacks discussed above, the object of the present invention is to improve the shape of the sealing plate and/or the case and thereby to provide a flat battery having excellent leakage resistance and durability and good mass productivity while being as thick as not greater than 1 mm.

DISCLOSURE OF THE INVENTION

For solving the above-mentioned problem in a flat battery constituted by sealing a power generation element with: a case that works as one electrode terminal; a sealing plate that works as the other electrode terminal and has a flat central section projected outward and a flat peripheral section extending substantially parallel to the flat central section; a gasket in the form of film that insulates the case from the sealing plate, the present invention is characterized in that an outer circumferential part of the peripheral section in the sealing plate is bent and/or that the case has a turned edge which fit the peripheral section of the sealing plate fitted via the gasket and said turned edged partly presses the gasket.

In the embodiment wherein the outer circumferential part of the peripheral section of the sealing plate is bent, it is preferable that the outer circumferential part is located in the case and the height of the outer circumferential part is not greater than 95% of thickness of the gasket.

It is also preferable that the bending angle of the outer circumferential part is in a range of 5 to 45 degrees relative to a direction parallel to a bottom face of the case (that is, relative to a horizontal plane).

In the embodiment wherein the case has the turned edge which fit the peripheral section of the sealing plate via the gasket and the turned edge partly presses the gasket, it is preferable that the turned edge has a circular recess partly pressing the gasket.

It is also preferable that the turned edge further has an outer circumferential end bent toward the gasket to partly press the gasket.

It is further preferable that the turned edge is inclined to the bottom face of the case to partly press the gasket. In this case, the angle of the inclination is preferably in a range of 5 to 20 degrees.

In the present invention, it is preferable that the gasket is composed of polyphenylene sulfide, and the partly pressed part of the gasket is pressed at a rate of 10 to 50% of original thickness of the gasket in the non-pressed state.

It is also preferable that the gasket is composed of polypropylene, and the partly pressed part of the gasket is pressed at a rate of 30 to 80% of original thickness of the gasket in the non-pressed state.

It is also preferable that the gasket is composed of polyethylene terephthalate, and the partly pressed part of the gasket is pressed at a rate of 10 to 70% of original thickness of the gasket in the non-pressed state.

It is also preferable that the gasket is composed of polyethylene naphthalate, and the partly pressed part of the gasket is pressed at a rate of 10 to 70% of original thickness of the gasket in the non-pressed state.

It is preferable that the flat battery of the present invention includes the sealing plate of not greater than 0.2 mm in thickness and has a thickness of not greater than 1.0 mm.

The present invention is also directed to a method of manufacturing a flat battery wherein a gasket of a substantially L-shaped cross section and a sealing plate that has a flat central section projected outward and a flat peripheral section extending substantially parallel to the flat central section are placed inside a top-open battery case, and a periphery of the case and the peripheral section of the sealing plate are fastened to each other via the gasket, the method comprising the steps of: curving an open end of the case inward to make the periphery of the case U-shaped and thereby form a turned edge; and recessing at least a portion of the turned edge or bending an outer circumferential part of the peripheral section toward the gasket, so as to form a part at which the sealing plate partly presses the gasket.

The present invention also provides a method of manufacturing a flat battery wherein a gasket of a substantially L-shaped cross section and a sealing plate that has a flat central section projected outward and a flat peripheral section extending substantially parallel to the flat central section are placed inside a top-open battery case, and a periphery of the case and the peripheral section of the sealing plate are fastened to each other via the gasket, the method comprising the steps of: curving an open end of the case inward to make the periphery of the case U-shaped and thereby form a turned edge that is substantially parallel to a bottom face of the case; and inclining the turned edge to the bottom face of the case, so as to partly press the gasket.

In this case, it is preferable that angle of the inclination of the turned edge is in a range of 5 to 20 degrees relative to a direction parallel to the bottom face of the case.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1

is a sectional view schematically illustrating the structure of a flat battery according to Embodiment 1 of the present invention.

FIG. 2

is a sectional view schematically illustrating the structure of a sealing plate in Embodiment 1 of the present invention.

FIG. 3

is a sectional view schematically illustrating the structure of a flat battery according to a second embodiment of the present invention.

FIG. 4

is a sectional view schematically illustrating the structure of a mold used for manufacturing the flat battery in the second embodiment of the present invention.

FIG. 5

is a sectional view schematically illustrating the structure of another mold used for manufacturing the flat battery in the second embodiment of the present invention.

FIG. 6

is a sectional view schematically illustrating the structure of still another mold used for manufacturing the flat battery in the second embodiment of the present invention.

FIG. 7

is a sectional view schematically illustrating a structure of a sealing portion of the flat battery in the second embodiment of the present invention.

FIG. 8

is a sectional view schematically illustrating a structure of another sealing portion of the flat battery in the second embodiment of the present invention.

FIG. 9

is a sectional view schematically illustrating a structure of still another sealing portion of the flat battery in the second embodiment of the present invention.

FIG. 10

is a sectional view schematically illustrating the structure of another flat battery according to the second embodiment of the present invention.

FIG. 11

is a sectional view schematically illustrating the structure of a mold used for manufacturing the another flat battery in the second embodiment of the present invention.

FIG. 12

is a sectional view schematically illustrating a structure of still another sealing portion of the another flat battery in the second embodiment of the present invention.

FIG. 13

is a sectional view schematically illustrating the structure of a prior art coin type battery.

FIG. 14

is a sectional view schematically illustrating the structure of another prior art flat battery.

BEST MODES FOR CARRYING OUT THE INVENTION

As described previously, in a flat battery constituted by sealing a power generation element with: a case that works as one electrode terminal; a sealing plate that works as the other electrode terminal and has a flat central section projected outward and a flat peripheral section extending substantially parallel to the flat central section; and a gasket that insulates the case from the sealing plate, the characteristic of the present invention is that an outer circumferential part of the peripheral section of the sealing plate is bent and/or that the case has a turned edge provided which fit the peripheral section of the sealing plate via the gasket and the turned edge partly presses the gasket.

The following describes one mode that the outer circumferential part of the peripheral section of the sealing plate is bent, as Embodiment 1 of the present invention, and another mode that the case has the turned edge provided which fit the peripheral section of the sealing plate via the gasket and the turned edge partly presses the gasket, as a second embodiment of the present invention. The flat battery of the present invention may have both the characteristics of Embodiment 1 and the second embodiment.

I. Embodiment 1

A flat battery according to Embodiment 1 of the present invention is discussed below with referring to FIG.

1

.

The flat battery of the present invention has a power generation element that is sealed with a case

2

working as one electrode terminal, a sealing plate

1

working as the other electrode terminal, and a gasket

3

insulating the case

2

from the sealing plate

1

.

As clearly understood from the vertical sectional view shown in

FIG. 2

, the flat battery wherein the sealing plate

1

includes a convex section

7

having the primary face thereof protruded outward and a flat peripheral section

8

extending substantially parallel to the primary face, it is characterized that an outer circumferential part

9

of the flat peripheral section

8

is bent. Namely the main characteristic of this embodiment is the shape of the sealing plate

1

.

By employing the above-mentioned structure of the sealing plate in the present invention, when the open end of the case

2

is curved inward and clamped, the outer circumferential part

9

of the sealing plate

1

bites the gasket

3

and the case

2

then presses the outer circumferential part

9

via the gasket

3

, so that the force works to reduce the bending angle. In other words, the force applied to the outer circumferential part

9

of the sealing plate

1

works to return the outer circumferential part

9

to the original angle before bending.

Therefore, there can be obtained effects that the sealing properties between the sealing plate

1

, the case

2

, and the gasket

3

is enhanced and the leakage resistance and the durability of the resulting battery are also improved.

It is preferable that the outer circumferential part

9

is bent upward in a range of 5 to 45 degrees relative to the horizontal plane. The bending angle of less than 5 degrees does not enable the outer circumferential part

9

to sufficiently bite the gasket

3

in the process of curving of the case

2

and the force pressing the gasket

3

is weakened, and when the bending angle is greater than 45 degrees, on the other hand, there is a possibility that the outer circumferential part

9

pierces the gasket

2

to cause a short circuit in the process of curving of the case

2

.

It is also preferable that the height of the bent outer circumferential part

9

is not greater than 95% of the thickness of the gasket

3

. Otherwise there is a possibility that the outer circumferential part

9

pierces the gasket

2

to cause a short circuit in the process of curving and clamping the open end of the case

2

.

In order to minimize the total thickness of the resulting battery, it is preferable that the thickness of the sealing plate

1

is not greater than 0.2 mm. The total thickness of the resulting flat battery is preferably not greater than 1.0 mm.

Then, the respective constituents of the flat battery of the present invention may be composed of any conventionally used materials. The flat battery may be manufactured according to any of the prior art methods.

As the material used for the case

2

working as one electrode terminal and the sealing plate

1

working as the other electrode terminal, there is a stainless steel or the like, for example. It is preferable that these are composed of an identical material and preferably composed of a stainless steel having excellent corrosion resistance.

As the material used for the gasket

3

, which insulates the case

2

from the sealing plate

1

, there are polyethylene, polypropylene, polyphenylene sulfide, polyethylene terephthalate and the like, for example. Especially preferable is polyphenylene sulfide, which has a sufficient breaking strength and is not damaged in the process of curving of the case

2

.

A separator

4

may be composed of a non-woven fabric of polypropylene or cellulose or a film of porous polypropylene or polyethylene, and any of conventionally used materials may be used for a positive electrode and a negative electrode.

As the material of the positive electrode, for example, manganese dioxide, graphite fluoride, sulfinyl chloride, sulfur dioxide, or silver chromate can be employed.

The negative electrode, the positive electrode, and an electrolytic solution may be modified within the scope that does not damage the effects of the present invention. For example, a chargeable secondary battery may be obtained by applying metal lithium, a lithium alloy that allows absorption and desorption of lithium, carbon, a metal oxide, or polyacene for the negative electrode, an organic electrolytic solution for the electrolytic solution, and a material combined with lithium ion to form an intercalation compound (for example, a metal oxide such as divanadium pentaoxide, diniobium pentaoxide, or manganese dioxide, a composite oxide of lithium and a metal oxide, a sulfide such as titanium disulfide or molybdenum disulfide, and a conductive polymer such as polyaniline or polyacene) for the positive electrode.

The present invention also naturally provides a method of manufacturing the flat battery according to Embodiment 1. The manufacturing method is similar to the prior art method, except the step of previously forming an outer circumferential part of the sealing plate.

Embodiment 1 of the present invention is discussed in detail below with some examples, although the invention is not restricted to such examples in any sense.

EXAMPLES 1 TO 5

FIG. 1

is a vertical sectional view illustrating the structure of flat batteries (manganese dioxide/lithium batteries) of these Examples. In

FIG. 1

,

1

is a sealing plate composed of stainless steel and having a bent outer circumferential part around a flat peripheral section,

2

is a case also working as a positive electrode terminal. Also,

3

is ring gasket composed of polyphenylene sulfide and

4

is a separator composed of a polypropylene non-woven fabric and

5

is a positive electrode obtained by kneading a powder mixture of manganese dioxide, graphite and a binding agent (fluororesin) with water, granulating, then drying, and compression molding to a fixed dimension. And,

6

is a negative electrode including metal lithium as the active material thereof.

In first, the positive electrode

5

, the separator

4

, and the negative electrode

6

were placed in the case

2

and an organic electrolytic solution (obtained by dissolving lithium perchlorate at a concentration of 1 mol/liter in an equal-volume solvent mixture of propylene carbonate and 1,2-dimethoxyethane) was charged into the case

2

. The opening of the case

2

was caulked via the gasket

3

, which was an insulator against both the case

2

and the sealing plate

1

to give the flat batteries having the structure discussed above.

The thicknesses of the case and the sealing plate were set to 0.1 mm and the thickness of the gasket (‘a’ in

FIG. 1

) was set to 0.25 mm and flat-type manganese dioxide-lithium batteries having the diameter of 20.0 mm and the thickness of 1.0 mm were manufactured. The length of the peripheral section of the sealing plate

1

was set to 0.80 mm, and the length of the outer circumferential part (‘c’ in

FIG. 2

) was set to 0.40 mm. The bending height (‘b’ in

FIG. 2

) and the bending angle of the outer circumferential part are shown in Table 1.

Evaluation

Rate of leakage

A hundred batteries of each Example were manufactured and subjected to a thermal impact cycle test for evaluation of leakage, which repeated a cycle that kept the battery at a temperature of −10° C. for one hour and then at a temperature of 60° C. for one hour. The confirmation of leakage was carried out by the manner of taking batteries after 120 cycles and 240 cycles and visually observing the surface of each battery. The rate of occurrence of leakage was determined by an equation of:

(Number of batteries with leakage)/(Total number of batteries (100))×100(%).

Results are shown in Table 1.

Rate of occurrence of short circuit

After assembly of the batteries, the voltage of each battery was measured to confirm the occurrence of short circuit. The rate of occurrence of short circuit was determined by an equation of:

(Number of batteries short-circuiting)/(Total number of batteries (100))×100(%).

Results are shown in Table 1.

COMPARATIVE EXAMPLE 1

A flat battery having the prior art structure was produced for the purpose of comparison in the same manner as Example 1, except that the peripheral section of the sealing plate was not bent to form the outer circumferential part. This battery was evaluated in the same manner as Example 1. Results of evaluation are shown in Table 1.

TABLE 1

(Gasket

Rate of

Rate of

thickness/

leakage

occurrence

Bending

Bending

Bending

(%)

of short

Height

Angle

height) ×

120

240

circuit

(mm)

(°)

100 (%)

cycle

cycle

(%)

Ex.

1

0.34

40

136

0

0

9

2

0.23

30

92

0

0

0

3

0.15

20

60

0

0

0

4

0.07

10

28

0

0

0

5

0.03

5

12

3

0

0

Com.

0

0

0

15

0

0

Ex. 1

EXAMPLES 6 TO 11

Flat batteries in accordance with the present invention were produced in the same manner as Example 1, except that the length of the outer circumferential part of the sealing plate was set to 0.20 mm and that the bending height and the bending angle were set as shown in Table 2. these batteries were evaluated in the same manner as Example 1. Results of evaluation are shown in Table 2.

TABLE 2

(Gasket

Rate of

Rate of

thickness/

leakage

occurrence

Bending

Bending

Bending

(%)

of short

Height

Angle

height) ×

120

240

circuit

(mm)

(°)

100 (%)

cycle

cycle

(%)

Ex.

6

0.24

50

96

0

0

1

7

0.17

40

68

0

0

0

8

0.12

30

48

0

3

0

9

0.07

20

28

0

7

0

10

0.04

10

16

0

17

0

11

0.02

5

8

5

44

0

EXAMPLES 12 TO 15

Flat batteries in accordance with the present invention were produced in the same manner as Example 1, except that the thickness of the resulting battery was set to 0.5 mm, that the thickness of the gasket was set to 0.10 mm, and that the bending height and the bending angle were set as shown in Table 3. These batteries were evaluated in the same manner as Example 1. Results of evaluation are shown in Table 3.

COMPARATIVE EXAMPLE 2

A flat battery having the prior art structure was produced for the purpose of comparison in the same manner as example 12, except that the peripheral section of the sealing plate was not bent to form the outer circumferential part. This battery was evaluated in the same manner as Example 1. Results of evaluation are shown in table 3.

TABLE 3

(Gasket

Rate of

Rate of

thickness/

leakage

occurrence

Bending

Bending

Bending

(%)

of short

Height

Angle

height) ×

120

240

circuit

(mm)

(°)

100 (%)

cycle

cycle

(%)

Ex.

12

0.15

30

150

0

0

13

13

0.11

15

110

0

0

2

14

0.07

10

70

0

5

0

15

0.03

5

30

2

14

0

Com.

0

0

0

17

55

0

Ex. 2

EXAMPLES 16 TO 21

Flat batteries in accordance with the present invention were produced in the same manner as Example 12, except that the length of the outer circumferential part of the sealing plate was set to 0.20 mm and that the bending height and the bending angle were set as shown in Table 4. these batteries were evaluated in the same manner as Example 1. Results of evaluation are shown in Table 4.

TABLE 4

(Gasket

Rate of

Rate of

thickness/

leakage

occurrence

Bending

Bending

Bending

(%)

of short

Height

Angle

height) ×

120

240

circuit

(mm)

(°)

100 (%)

cycle

cycle

(%)

Ex.

16

0.12

30

120

0

0

7

17

0.09

25

90

0

0

0

18

0.07

20

70

0

0

0

19

0.05

15

50

0

0

0

20

0.04

10

40

0

7

0

21

0.02

5

20

6

21

0

EXAMPLES 22 TO 26

Flat batteries in accordance with the present invention were produced in the same manner as Example 12, except that the bending height of the outer circumferential part of the sealing plate was fixed constant to 0.07 mm and that the length of the outer circumferential part and the bending angle were set as shown in Table 5. These batteries were evaluated in the same manner as Example 1. Results of evaluation are shown in Table 5.

TABLE 5

Length

of outer

(Gasket

Rate of

Rate of

circum-

thickness/

leakage

occurrence

ferential

Bending

Bending

(%)

of short

part

Angle

height) ×

120

240

circuit

(mm)

(°)

100 (%)

cycle

cycle

(%)

Ex.

22

0.60

7

70

5

15

0

23

0.40

10

70

0

5

0

24

0.30

13

70

0

0

0

25

0.20

20

70

0

0

0

26

0.10

35

70

0

0

0

The results of Tables 1 to 5 give the following conclusions:

In the flat batteries in accordance with the present invention where the value of the (thickness of the gasket/the bending height)×100(%) is not greater than 95, no short circuit occurs after sealing of the battery.

Since the batteries that are free from leakage after 120 cycles in the thermal impact test for evaluation of leakage may be used for 3 to 5 years in the normal working state and the batteries that are free from leakage after 240 cycles may be used for 5 to 10 years in the normal working state, the flat batteries in accordance with the present invention accordingly have long life.

Especially when the bending angle of the outer circumferential part of the sealing plate is not less than 10 degrees, the batteries tend to be free from leakage after 120 cycles, and the batteries having the greater bending angle with the same length of the outer circumferential part tend to have better leakage resistance.

II. Second Embodiment

The second embodiment of the present invention is characterized in that the case has the turned edge which fit the peripheral section of the sealing plate via the gasket and the turned edge partly presses the gasket.

AS the concrete applications of the second embodiment, there are a Embodiment 2-1 that the turned edge has a circular recess for partly pressing the gasket and another Embodiment 2-2 that the turned edge is inclined to the bottom face of the case to partly press the gasket.

(1) Embodiment 2-1

The flat battery of the Embodiment 2-1 in accordance with the present invention is constituted by sealing a power generation element with: a battery case that works as one electrode terminal; a sealing plate that works as the other electrode terminal and has a flat central section projected outward and a flat peripheral section extending substantially parallel to the flat central section; and a gasket that insulates the case from the sealing plate, and characterized in that the case has a turned edge which fit the peripheral section of the sealing plate via the gasket and has a circular recess for partly pressing the gasket therein.

This means that the case with the circular recess naturally has a circular convex at the side opposite to the circular recess and this circular convex partly presses the gasket.

In this case, the turned edge may have an outer circumferential end bent toward the gasket and the bent outer circumferential end may partly press the gasket.

In the flat battery of the Embodiment 2-1 in accordance with the present invention, the degree of pressing the partly pressed part of the gasket relative to the thickness of the gasket in the non-pressed state, that is, the pressing rate of the partly pressed part of the gasket, may be varied depending upon the material of the gasket.

For example, when the gasket is composed of polyphenylene sulfide, the preferable pressing rate ranges from 10% to 50%. When the gasket is composed of polypropylene, the preferable pressing rate ranges from 30% to 80%. When the gasket is composed of polyethylene terephthalate, the preferable pressing rate ranges from 10% to 70%. When the gasket is composed of polyethylene naphthalate, the preferable pressing rate ranges from 10% to 70%.

When the local pressing rate of any of these gaskets is less than the corresponding lower limit, the leakage resistance may not be improved due to the insufficient pressing rate, and when the local pressing rate exceeds the upper limit, destructions such as cracks and breaks may occur in the gasket due to the excessive pressing rate to cause insufficient insulation of the battery case from the sealing plate and to cause a short circuit in the battery.

The other constituents are identical with those of Embodiment 1 discussed above.

On the other hand, the present invention also provides a method of manufacturing the flat battery in accordance with the Embodiment 2-1. More specifically the present invention is directed to a method of manufacturing a flat battery, wherein a gasket of a substantially L-shaped cross section and a sealing plate that has a flat central section projected outward and a flat peripheral section extending substantially parallel to the flat central section are placed inside a top-open battery case, and a periphery of the case and the peripheral section of the sealing plate are fastened to each other via the gasket, the method comprising the steps of: curving an open end of the case inward to make the periphery of the case U-shaped and thereby form a turned edge; and recessing at least a portion of the turned edge or bending an outer circumferential part of the peripheral section toward the gasket, so as to form a part at which the sealing plate partly presses the gasket.

The Embodiment 2-1 in accordance with the present invention is discussed below in detail with referring to drawings, although the present invention is not restrictive in any sense.

FIG. 3

is a sectional view schematically illustrating a flat battery according to the Embodiment 2-1 of the present invention. In

FIG. 3

, a case

2

working as a positive electrode terminal was composed of stainless steel having good corrosion resistance. A sealing agent mainly composed of asphalt was applied on the inner surface of the case

2

to form a coating film, although it is not illustrated. A sealing plate

1

formed to a hat shape was also made of stainless steel, like the case

2

. The sealing plate

1

had a flat central section

1

a

protruded outward and a flat peripheral section

1

b

extending substantially parallel to the central section

1

a.

A gasket

3

composed of polyphenylene sulfide and having a substantially L-shaped cross section was placed on the inner surface of the top-open case

2

. In the process of bending the gasket

3

inward with the open end of the case

2

, the peripheral section

1

b

of the sealing plate

1

was interposed between the bent gasket

3

to attain insulation of the case

2

from the sealing plate

1

and sealing of the case. At this time, a turned edge

2

a

was formed on the case

2

. Further, a circular recess

2

b

was formed on the turned edge

2

a

in the course of caulking.

A positive electrode

5

was provided by mixing manganese dioxide, carbon as an electrically conductive agent, and fluororesin powder as a binding agent, press molding them to pellets of 15 mm in diameter and 0.3 mm in thickness, and drying the pellets at 200° C. for 12 hours.

A negative electrode

6

of a circular shape was punched out of a metal lithium in the form of hoop and bonded to the inner surface of the convex of the sealing plate

1

with pressure. A separator

4

was composed of a polypropylene non-woven fabric and an electrolytic solution was obtained by dissolving lithium perchlorate at a concentration of 1 mol/liter in an equal-volume solvent mixture of propylene carbonate and 1,2-dimethoxyethane.

The flat battery shown in

FIG. 3

was manufactured according to the following procedure. In first, the gasket

3

of the substantially L-shaped cross section and the sealing plate

1

having the central section

1

a

protruded outward and the flat peripheral section

1

b

were placed in the top-open case

2

. At this time, the power generation element having the positive electrode

5

and the negative electrode

6

disposed opposite to each other via the separator

4

was contained in a space defined by the central section

1

a

of the sealing plate

1

and the case

2

. The open end of the case

2

in the state of having the respective constituents contained therein was deformed inward to be U shape along the outer circumference end of the sealing plate via the gasket. Thus, the turned edge fitting the peripheral section of the sealing plate was formed in the case

2

to give the flat battery having a similar cross section to that of the prior art flat battery shown in FIG.

14

. At this time, a mold having the cross section shown in

FIG. 4

was used to curve the open end of the case

2

inward and attain caulking.

FIG. 4

is a sectional view schematically illustrating the structure of the mold used for manufacturing the flat battery according to the Embodiment 2-1 in accordance with the present invention.

Then, for the flat battery having the turned edged

2

a

formed, the turned edge

2

a

of the flat battery was pressed again and attained second caulking to form a portion partly pressing the gasket. This gave a circular recess in part of the turned edge

2

a

and/or an outer circumferential end of the turned edge bent toward the gasket. At the circular recess and/or the bent outer circumferential end, the sealing plate

1

partly pressed the gasket.

The molds used for such second caulking had cross sections shown in

FIGS. 5 and 6

. The mold shown in

FIG. 5

was used to bend the outer circumferential end toward the gasket. The mold shown in

FIG. 6

was used to form the circular recess. The structures of the caulked portions of the flat batteries by using these molds were shown in

FIGS. 7 through 9

show. It is noted that, in the flat battery of

FIG. 3

, a circular recess

2

b

was formed on the turned edge

2

a

of the case

2

.

Flat batteries were produced with the molds shown in

FIGS. 4

to

6

as Examples according to the Embodiment 2-1 in accordance with the present invention, and the properties of the flat batteries were evaluated.

EXAMPLES 27 TO 31 AND COMPARATIVE EXAMPLES 3 TO 5

The power generation element including the positive electrode

5

, the negative electrode

6

, and the separator

4

as shown in FIG.

3

and the sealing plate

1

were placed in the top-open case

2

. The gasket

3

used here was composed of polyphenylene sulfide and had the substantially L-shaped cross section.

After sealing with the mold shown in

FIG. 4

, the second caulking was performed with the second mold shown in FIG.

5

. The second caulking bent the outer circumferential end of the case

2

toward the gasket to form a bent outer circumferential end

2

c.

As clearly seen in the sectional view of

FIG. 7

, the bent outer circumferential end

2

c

partly pressed the gasket in the caulked portion.

The pressing rate of the partly pressed part of the gasket was calculated by measuring the thickness of the gasket in the pressed state from photographs of the cross sections of the respective batteries manufactured, measuring the thickness of the gasket in the non-pressed state, and using an equation of:

(Pressing rate of gasket) (%)=((Gasket thickness in non-pressed state)−(Gasket thickness in pressed state))/(Gasket thickness in non-pressed state)×100.

The pressure applied to the mold was regulated in the second caulking process to vary the degree of bending the outer circumferential end toward the gasket and thereby adjust the pressing rate. A flat battery manufactured with the pressing rate of the pressed part of the gasket (hereinafter simply referred to as the ‘pressing rate ’) set to 10% was named Battery A.

In the same manner, a flat battery manufactured by using the mold shown in

FIG. 5

for the second caulking and having the pressing rate of the gasket set to 30% and the same structure as that of the battery A was named Battery B.

Further, a flat battery manufactured by using the mold shown in

FIG. 5

for the second caulking and having the pressing rate of the gasket set to 50% and the same structure as those of the Batteries A and B was named Battery C.

A battery having the circular recess

2

b

formed on part of the turned edge

2

a

of the case

2

was manufactured with the mold shown in FIG.

6

. As clearly seen in the sectional view of

FIG. 8

, the caulked portion of the obtained battery has the structure wherein the recess pressed the gasket. A flat battery manufactured having the pressing rate of the gasket set to 30% and otherwise a similar structure to that of the battery A was named Battery D.

After the second caulking with the mold shown in

FIG. 6

, still another caulking was performed with the mold shown in FIG.

5

. The caulked portion of the resulting battery had the outer circumferential end

2

c

of the case

2

bent toward the gasket and the circular recess

2

b

formed on part of the turned edge

2

a

as shown in

FIG. 9. A

flat battery manufactured having the pressing rate of the gasket set to 30% at both the contact of the outer circumferential end with the gasket and at the circular recess and otherwise a similar structure to that of the battery A was named Battery E.

On the other hand, a flat battery manufactured as a comparative example had a similar structure to that of the battery A, except that the second caulking was not performed and only the turned edge

2

a

was formed. The cross section of the battery of the comparative example was the same as that of the prior art flat battery shown in FIG.

14

. The gasket did not have any specifically pressed part, but was pressed at the rate of 10% against the thickness in the non-pressing state. Obtained here was named Battery F.

Another flat battery was manufactured by bending the outer circumferential end of the battery case toward the gasket at a pressing rate of 5%, and otherwise had a similar structure to that of the battery A. Obtained here was named Battery G. Still another flat battery was manufactured at a pressing rate of 55%, and otherwise had a similar structure to that of the battery A. Obtained here was named Battery H.

All Batteries A through H obtained, which were the flat batteries, had the diameter of 20 mm and the thickness of 0.5 mm. Table 6 shows the pressing rate, the shape of the second mold used, and the structure of the caulked portion with regard to the respective batteries.

TABLE 6

Example

Com. Ex.

(Battery)

(Battery)

A

B

C

D

E

F

G

H

Material

Polyphenylene sulfide

Polyphenylene

of gasket

sulfide

Pressing

10

30

50

30

30

None

5

55

rate (%)

Shape of

FIG. 5

FIG. 6

FIGS. 5

Not

FIG. 5

second

and 6

used

mold

Cross

FIG. 7

FIG. 8

FIG. 9

FIG. 14

FIG. 8

section of

caulked

portion

A thousand of each of the batteries A through H were manufactured and subjected to evaluation of properties and for the occurrence of leakage. Evaluated properties were the open circuit voltage immediately after assembly of the batteries, the internal resistance under the condition of the alternating current of 1 kHz, and the rate of occurrence of internal short circuit. The open circuit voltage immediately after assembly of the batteries and the internal resistance under the condition of the alternating current of 1 kHz were based on the measurement of 100 batteries each. The rate of occurrence of internal short circuit was obtained by checking all the batteries manufactured.

The batteries were kept at the environmental temperature of 60° C. and the environmental humidity of 90%, that is, under the high hot and humid condition and the state of leakage was visually observed after 20 days.

The batteries were also subjected to a thermal impact test for evaluation of leakage, which repeated a 4 hour cycle that kept the battery at a temperature of −10° C. for 1 hour, heated the battery to 60° C. over 1 hour, kept the battery at the temperature of 60° C. for 1 hour, and cooled down the battery to −10° C. over 1 hour. The state of leakage was visually observed after 100 cycles. Results of evaluation are shown in Table 7.

TABLE 7

Example (Battery)

Com. Ex. (Battery)

A

B

C

D

E

F

G

H

Open circuit

Mean (V)

3.302

3.310

3.312

3.313

3.316

3.320

3.320

3.318

voltage

Standard deviation

0.001

0.001

0.002

0.002

0.001

0.001

0.001

0.001

Internal

Mean (V)

12.3

12.5

12.1

11.8

11.6

12.3

12.4

11.7

resistance

Standard deviation

1.0

0.9

1.3

1.2

1.0

1.0

1.0

0.8

Thermal impact

State of leakage

No

No

No

No

No

3

2

No

test

leak

leak

leak

leak

leak

leaked

leaked

leak

Storage in

State of leakage

No

No

No

No

No

5

3

No

hot, humid

leak

leak

leak

leak

leak

leaked

leaked

leak

condition

Internal short

Occurrence rate (%)

0

0

0

0

0

0

0

12

circuit

Results of Table 7 show that all the batteries of Examples 27 to 31 and Comparative Examples 3 to 5 have the stable voltage and internal resistance with little variation and no significant difference of such properties was observed according to the presence of the specifically pressed part of the gasket or its degree of pressing.

The occurrence of leakage was, however, observed in both the evaluation tests of leakage with regard to Battery G having the low pressing rate and Battery F having no specifically pressed part, which may be ascribed to the insufficient pressing rate of the gasket. With regard to Battery H having the high pressing rate, on the other hand, the internal short circuit occurred after assembly of the battery, which was ascribed to the excessive pressing rate of the gasket, which resulted in cracking and breaking the gasket to bring the sealing plate into contact with the inner side face of the case.

EXAMPLES 32 TO 34

Flat batteries were manufactured with the molds of

FIGS. 4 through 6

in the same manner as Example 27, except that materials other than polyphenylene sulfide were used for the gasket and the properties of these batteries were evaluated.

The same power generation element and casing as those of Example 27 were used and the power generation element including the positive electrode

5

, the negative electrode

6

, and the separator

4

as shown in FIG.

3

and the sealing plate

1

were placed in the top-open case

2

. The gasket

3

used here was composed of polypropylene and had the substantially L-shaped cross section.

Like Battery A of Example 27, after sealing with the mold shown in

FIG. 4

, the caulking was performed with the mold shown in FIG.

5

. At this time, the pressing rate of the gasket was set to 60%. Obtained here was called Battery I.

Battery J was manufactured with a gasket of polyethylene terephthalate and at the pressing rate of the gasket set to 60%, and otherwise had the same structure as that of Battery A.

Battery K was manufactured with a gasket of polyethylene naphthalate and at the pressing rate of the gasket set to 60%, and otherwise had the same structure as that of the battery A.

All Batteries I through K obtained, which were flat batteries, had the diameter of 20 mm and the thickness of 0.5 mm. Table 8 shows the material of the gasket, the pressing rate, the shape of the second mold used, and the structure of the caulked portion with regard to the respective batteries.

TABLE 8

Example

Battery I

Battery J

Battery K

Material of

Polypropylene

Polyethylene

Polyethylene

gasket

terephthalate

naphthalate

Pressing rate

60

(%)

Shape of

FIG. 5

second mold

Cross section

FIG. 7

of caulked

portion

Then, a thousand of each of the batteries were manufactured and subjected to evaluation of properties and for the occurrence of leakage in the same manner as Example 27. Results of evaluation are shown in Table 9.

TABLE 9

Example (Battery)

I

J

K

Open circuit

Mean (V)

3.321

3.320

3.319

voltage

Standard deviation

0.0015

0.0013

0.002

Internal

Mean(V)

12.4

12.3

11.9

resistance

Standard deviation

1.0

1.0

1.1

Thermal impact

No

2

No

test

State of leakage

leak

leaked

leak

Storage in

hot, humid

State of leakage

No

3

No

leak

leaked

leak

condition

Internal short

Occurrence rate (%)

0

0

0

circuit

As apparent from results of Table 9, all Batteries I to K have the stable voltage and internal resistance with little variation and no significant difference of such properties was observed according to the presence of the specifically pressed part of the gasket or the degree of pressing. No leakage was observed in either of the leakage evaluation tests. As in the case of Example 27, these results prove that formation of the recess on part of the turned edge and/or formation of the bent outer circumferential end to partly press the gasket give the flat batteries that are substantially free from the occurrence of leakage or internal short circuit, without deteriorating the properties of the batteries.

Under the condition of the insufficient pressing rate of the gasket, the occurrence of leakage was observed with regard to the batteries having the gaskets composed of the materials in Examples 32 to 34. The respective materials of the gasket had the intrinsic minimum limits of the pressing rate of the gasket.

In order to obtain the batteries of high reliability, the pressing rate of the gasket by the recess formed along the whole circumference of the turned edge should be not less than the minimum limit specified for each material of the gasket.

Further, in the case of the excessive pressing rate of the gasket, there is observed a short circuit between the sealing plate and the inner side face of the case due to the destruction of the gasket. Such failures are generally checked by the inspection in the manufacturing process and may not be found in the market, but in order to enhance the reliability of the batteries, the local pressing rate of the gasket by the recess formed along the whole circumference of the turned edge should be not greater than the maximum limit specified for each material of the gasket.

In the above examples, the recess was formed by caulking the turned edge of the case. Another applicable procedure may form a recess in the case and then carry out caulking.

(2) Embodiment 2-2

The flat battery of Embodiment 2-2 in accordance with the present invention is constituted by sealing a power generation element with: a battery case that works as one electrode terminal; a sealing plate that works as the other electrode terminal and has a flat central section projected outward and a flat peripheral section extending substantially parallel to the flat central section; and a gasket that insulates the case from the sealing plate, characterized in that the turned edge is inclined to the bottom face of the case to partly press the gasket.

In the flat battery of Embodiment 2-2, the degree of pressing a part of the gasket relative to the thickness of the gasket in the non-pressed state, that is, the pressing rate of the pressed part of the gasket, depends upon the material of the gasket.

As in Embodiment 2-1 discussed above, for example, when the gasket is composed of polyphenylene sulfide, the preferable pressing rate ranges from 10% to 50%. When the gasket is composed of polypropylene, the preferable pressing rate ranges from 30% to 80%. When the gasket is composed of polyethylene terephthalate, the preferable pressing rate ranges from 10% to 70%, and when the gasket is composed of polyethylene naphthalate, the preferable pressing rate ranges from 10% to 70%.

The flat battery of Embodiment 2-2 is obtained by otherwise using the same constituents as those of Embodiment 1 and Embodiment 2-1.

Therefore, the present invention also relates to a method of manufacturing the flat battery according to Embodiment 2-2. More specifically the present invention is directed to a method of manufacturing a flat battery, wherein a gasket of a substantially L-shaped cross section and a sealing plate that has a flat central section projected outward and a flat peripheral section extending substantially parallel to the flat central section are placed inside a top-open battery case, and a periphery of the case and the peripheral section of the sealing plate are fastened to each other via the gasket, the method comprising the steps of: curving an open end of the case inward to make the periphery of the case U-shaped and thereby form a turned edge that is substantially parallel to a bottom face of the case; and inclining the turned edge to the bottom face of the case, so as to partly press the gasket.

In this case, it is preferable that angle of the inclination of the turned edge is in a range of 5 to 20 degrees relative to a direction parallel to the bottom face of the case.

The Embodiment 2-2 in accordance with the present invention is discussed below in detail with referring to drawings, although the discussion is not restrictive in any sense.

FIG. 10

is a sectional view schematically illustrating a flat battery according to Embodiment 2-2 of the present invention. In

FIG. 10

, a case

2

working as a positive electrode terminal was composed of stainless steel having good corrosion resistance. A sealing agent mainly composed of asphalt was applied on the inner surface of the case

2

to form a coat, although it is not illustrated. A sealing plate

1

formed to a hat shape was also made of stainless steel like the case

2

and worked as a negative electrode terminal. The sealing plate

1

had a flat central section

1

a

protruded outward and a flat peripheral section

1

b

extending substantially parallel to the central section

1

a.

A gasket

3

composed of polyphenylene sulfide and having a substantially L-shaped cross section was placed on the inner surface of the top-open case

2

. In the process of bending the open end of the case

2

inward, the peripheral section

1

b

of the sealing plate

1

was interposed between the bent gasket

3

to attain insulation of the case

2

from the sealing plate

1

and sealing of the case. At this time, a turned edge

2

a

was formed on the case

2

. Further, in the course of caulking, the end of the turned edge

2

a

was inclined to the gasket

3

, so as to form a specific part that pressed the gasket

3

.

A positive electrode

5

was provided by mixing manganese dioxide, carbon as an electrically conductive agent, and fluororesin powder as a binding agent, press forming the mixture to pellets of 15 mm in diameter and 0.3 mm in thickness, and drying the pellets at 200° C. for 12 hours. A negative electrode

6

of a circular shape was punched out of a metal lithium in the form of hoop and bonded to the inner surface of the convex of the sealing plate

1

with pressure.

A separator

4

was composed of a polypropylene non-woven fabric. An electrolytic solution was obtained by dissolving lithium perchlorate at a concentration of 1 mol/liter in an equal-volume solvent mixture of propylene carbonate and 1,2-dimethoxyethane.

The battery shown in

FIG. 10

was manufactured according to the following procedure.

In first, the gasket

3

of the substantially L-shaped cross section and the sealing plate

1

having the central section

1

a

protruded outward and the flat peripheral section

1

b

were placed in the top-open case

2

. At this time, the power generation element having the positive electrode

5

and the negative electrode

6

opposed to each other via the separator

4

was contained in a space defined by the central section

1

a

of the sealing plate

1

and the case

2

. The open end of the case

2

in the state of having the respective constituents contained therein was deformed inward and turned along the outer circumference end of the sealing plate via the gasket

3

. Namely, the outer circumference end of the case

2

was to be in the U shape. Thereby, the turned edge

2

a

fitting the peripheral section of the sealing plate fitted therein was accordingly formed in the case

2

to give the flat battery having a similar cross section to that of the prior art flat battery shown in FIG.

14

. At this time, a mold having the cross section shown in

FIG. 4

was used to deform the open end of the case

2

inward and attain caulking.

For the flat battery with the turned edge

2

a

formed, the turned edge

2

a

of the flat battery was pressed again to attain second caulking to form a portion partly pressing the gasket. Thereby, the end of the turned edge

2

a

was then further bent toward the gasket, so that the gasket

3

was partly pressed by the peripheral section

1

b

of the sealing plate

1

and the turned edge

2

a

of the case

2

.

The mold used for the second caulking had a cross section shown in FIG.

11

. It is preferable that the caulking section of the mold shown in

FIG. 11

has the angle of inclination in a range of 5 to 20 degrees relative to the horizontal plane. A sectional view schematically illustrating the caulked portion of the flat battery with this mold is shown in FIG.

12

.

Flat batteries were produced with the molds shown in

FIGS. 4 and 11

as Examples of Embodiment 2-2 in accordance with the present invention, and the properties of the flat batteries were evaluated.

EXAMPLES 35 TO 38 AND COMPARATIVE EXAMPLE 6 TO 10

The power generation element including the positive electrode

5

, the negative electrode

6

, and the separator

4

as shown in FIG.

10

and the sealing plate

1

were placed in the top-open case

2

. The gasket

3

used here was composed of polyphenylene sulfide and had the substantially L-shaped cross section.

After caulking and sealing with the mold shown in

FIG. 4

, the second caulking was performed with the second mold shown in FIG.

11

. The second mold had the angle of inclination set to 5 degrees relative to the horizontal plane. The second caulking further bent the turned edge

2

a

of the case

2

toward the gasket

3

to form an inclination. As clearly seen in the sectional view of

FIG. 12

, the inclined turned edge

2

a

partly pressed the gasket in the caulked portion.

The pressing rate of the gasket in the partly pressed part was calculated by measuring the thickness of the gasket from photographs of the cross sections of the respective batteries manufactured, measuring the thickness of the gasket in the non-pressed state, and using an equation of:

(Pressing rate of gasket) (%)=((Gasket thickness in non-pressed state)−(Gasket thickness in pressed state))/(Gasket thickness in non-pressed state)×100.

The pressure applied to the mold was regulated in the second caulking process to vary the angle of inclination of the turned edge

2

a

to the gasket

3

and thereby adjust the pressing rate. A flat battery manufactured here having the pressing rate of the partly pressed part of the gasket

3

set to 10% was named Battery L.

In the same manner, one manufactured with the mold shown in

FIG. 11

for the second caulking, and otherwise having the same structure as that of the battery A with the pressing rate of the gasket set to 30% was named Battery M.

Further, one manufactured with the mold shown in

FIG. 11

for the second caulking, and otherwise having the same structure as that of the battery A with the pressing rate of the gasket set to 50% was named Battery N.

One manufactured with the mold of

FIG. 11

for second caulking, which had the angle of inclination set to 20 degrees relative to the horizontal plane, and otherwise having the same structure as that of the battery A with the pressing rate of the gasket set to 30% was named Battery O.

On the other hand, a battery was manufactured as a comparative example, which had a similar structure to that of the battery A, except that the second caulking was not performed and only the turned edge

2

a

was formed. The cross section of the battery manufactured here was the same as that of the prior art flat battery shown in FIG.

14

. At this time, the gasket did not have any specifically pressed part, but was pressed at the rate of 10% against the thickness in the non-pressed state. Obtained here was named Battery P.

Battery Q was manufactured with the mold of

FIG. 11

for second caulking, which had the angle of inclination set equal to 5 degrees relative to the horizontal plane, and otherwise had a similar structure to that of the battery A with the pressing rate of the gasket set to 5%. Still another Battery R was manufactured with the mold of

FIG. 11

for second caulking, which had the angle of inclination set equal to 5 degrees relative to the horizontal plane, and otherwise had a similar structure to that of the battery A with the pressing rate of the gasket set to 55%.

As a further comparative example, another Battery S was manufactured with the mold of

FIG. 11

for second caulking, which had the angle of inclination set equal to 3 degrees relative to the horizontal plane, and otherwise had a similar structure to that of the battery A. Still another Battery T was manufactured with the mold of

FIG. 11

for second caulking, which had the angle of inclination set equal to 30 degrees relative to the horizontal plane, and otherwise had a similar structure to that of the battery A.

All the flat batteries L through T thus obtained had the diameter of 20 mm and the thickness of 0.5 mm. Table 10 shows the pressing rate, the angle of inclination of the mold shown in

FIG. 11

, and the structure of the caulked portion with regard to the respective batteries.

TABLE 10

Example

(Battery)

Com. Ex. (Battery)

L

M

N

O

P

Q

R

S

T

Material of

Polyphenylenesulfide

gasket

Pressing rate

10

30

50

30

None

5

55

—

—

(%)

Angle of

5

20

Not

5

3

30

inclination

conducted

of second

mold

Cross section

FIG. 12

FIG. 14

FIG. 12

FIG. 14

FIG. 12

of caulked

portion

Then, a thousand of each of the batteries were manufactured and subjected to evaluation of battery properties and for the occurrence of leakage. Evaluated properties were the open circuit voltage immediately after assembly of the batteries, the internal resistance under the condition of the alternating current of 1 kHz, and the rate of occurrence of internal short circuit. The open circuit voltage immediately after assembly of the batteries and the internal resistance under the condition of the alternating current of 1 kHz were based on the measurement of 100 batteries each and the rate of occurrence of internal short circuit was the results of checking all the batteries manufactured.

The batteries were kept at the environmental temperature of 60° C. and the environmental humidity of 90%, that is, under the hot, humid condition, and the state of leakage was visually observed after 20 days. The batteries were also subjected to a thermal shock test for evaluation of leakage, which repeated a 4-hour cycle that kept the battery at a temperature of −10° C. for 1 hour, heated the battery to 60° C. over 1 hour, kept the battery at the temperature of 60° C. for 1 hour, and cooled down the battery to −10° C. over 1 hour. The state of leakage was visually checked after 100 cycles. Results of evaluation are shown in Table 11.

TABLE 11

Example (Battery)

Com. Ex. (Battery)

L

M

N

O

P

Q

R

S

T

Open circuit

Mean (V)

3.320

3.321

3.335

3.315

3.322

3.333

3.316

3.330

3.320

voltage

Standard deviation

0.001

0.002

0.001

0.002

0.001

0.001

0.002

0.002

0.002

Internal

Mean (V)

12.3

11.8

12.5

11.9

12.4

11.1

12.7

11.8

12.0

resistance

Standard deviation

0.9

0.8

0.8

0.9

1.0

0.9

0.8

1.0

1.0

Thermal impact test

No

No

No

No

3

2

No

3

No

leak

leak

leak

leak

leaked

leaked

leak

leaked

leak

Storage in hot, humid condition

No

No

No

No

2

1

No

3

No

leak

leak

leak

leak

leaked

leaked

leak

leaked

leak

Internal short circuit

0

0

0

0

0

0

7.5

0

8.3

Occurrence rate (%)

From Table 11, all the Batteries L to T have the stable voltage and internal resistance with little variation and no significant difference of such battery properties was observed according to the presence of the pressed part of the gasket or the degree of pressing. The occurrence of leakage was, however, observed in both the evaluation tests of leakage with regard to the battery Q having the low pressing rate and the battery P having no specifically pressed part, which may be ascribed to the insufficient pressing rate of the gasket.

With regard to the battery R having the high pressing rate, on the other hand, there was observed that the internal short circuit occurred after assembly of the battery. As a result of investigation, this was ascribed to the excessive pressing rate of the gasket, which resulted in cracking and breaking the gasket to bring the sealing plate into contact with the inner side face of the case.

In the case of Battery S manufactured with the second caulking mold having the small angle of inclination, regulation of the pressure did not sufficiently raise the pressing rate of the gasket and the occurrence of leakage was observed in both the evaluation tests, which may be ascribed to the insufficient pressing rate of the gasket. In the case of the battery T manufactured with the second caulking mold having the large angle of inclination, on the other hand, regulation of the pressure did not sufficiently lower the pressing rate of the gasket. The internal short circuit occurred after assembly of the battery. As a result of investigation, this was ascribed to the excessive pressing rate of the gasket, which resulted in cracking and breaking the gasket to bring the sealing plate into contact with the inner side face of the case.

EXAMPLES 39 TO 41

Flat batteries were manufactured with the molds of

FIGS. 4 and 11

in the same manner as Example 35, except that materials other than polyphenylene sulfide were used for the gasket and the properties of these batteries were evaluated. The mold shown in

FIG. 11

had the angle of inclination set to 5 degrees.

The same power generation element and casing as those of Example 35 were used and the power generation element including the positive electrode

5

, the negative electrode

6

, and the separator

4

as shown in FIG.

10

and the sealing plate

1

were placed in the top-open case

2

. The gasket

3

used here was composed of polypropylene and had the substantially L-shaped cross section. Like the battery L of Example 35, after sealing with the mold shown in

FIG. 4

, the caulking was performed with the second mold shown in FIG.

11

. The pressing rate of the gasket was set to 60%. Obtained here was named Battery U.

Battery V was manufactured with a gasket of polyethylene terephthalate and at the pressing rate of the gasket set equal to 60%, and otherwise had the same structure as that of the battery L. Battery W was manufactured with a gasket of polyethylene naphthalate and at the pressing rate of the gasket set equal to 60%, and otherwise had the same structure as that of the battery L.

All Batteries U through W obtained, which were the flat batteries, had the diameter of 20 mm and the thickness of 0.5 mm. The material of the gasket, the pressing rate, the angle of inclination of the second mold shown in

FIG. 11

, and the structure of the caulked portion with regard to the respective batteries were shown in FIG.

12

.

TABLE 12

Example

Battery U

Battery V

Battery W

Material of

Polypropylene

Polyethylene

Polyethylene

gasket

terephthalate

naphthalate

Pressing rate

60

60

60

(%)

Angle of

FIG. 5

inclination of

second mold

Cross section

FIG. 12

of caulked

portion

A thousand of each of the batteries were manufactured and subjected to evaluation of properties and for the occurrence of leakage in the same manner as Example 35 by applying the same manner as in Example 35. Results of evaluation are shown in Table 13.

TABLE 13

Example (Battery)

U

V

W

Open circuit

Mean (V)

3.322

3.319

3.330

voltage

Standard deviation

0.002

0.002

0.001

Internal

Mean (V)

11.8

11.9

12.0

resistance

Standard deviation

0.9

0.8

0.8

Thermal impact test

No

No

No

leak

leak

leak

Storage in hot, humid condition

No

No

No

leak

leak

leak

Internal short circuit

0

0

0

Occurrence rate (%)

As apparent from Table 13, all Batteries U to W have the stable voltage and internal resistance with little variation and no significant difference of such properties was observed according to the material of the gasket. No leakage was observed in either of the leakage evaluation tests. As in the case of Example 35, these results prove that inclination of the turned edge of the case forms a specific part at the end of the case to partly press the gasket and accordingly gives the flat batteries that are substantially free from the occurrence of leakage or internal short circuit, without deteriorating the properties of the batteries.

Under the condition of the insufficient pressing rate of the gasket, the occurrence of leakage was observed with regard to the batteries having the gaskets composed of the above materials and the respective materials of the gasket had the intrinsic minimum limits of the pressing rate of the gasket. In order to obtain the batteries of high reliability, the pressing rate of the gasket by the inclination along the whole circumference of the turned edge of the case should be not less than the minimum limit specified for each material of the gasket.

The excessive pressing rate of the gasket damaged the gasket and caused a short circuit between the sealing plate and the inner side face of the case. Such failures are generally checked by the inspection in the manufacturing process and may not be found in the market. In order to enhance the reliability of the batteries, however, the pressing rate of the gasket by the inclination along the whole circumference of the turned edge of the case should be not greater than the maximum limit specified for each material of the gasket.

In Embodiment 2-2, use of the mold with the inclination shown in

FIG. 11

for the first caulking caused distortion of the battery, which may be ascribed to the excessive bending stress in the bending work. Such caulking at the lowered pressing speed prevents the distortion, but significantly damages the mass productivity. Division of the caulking process into two stages as discussed in the above embodiment gives the batteries of stable shape at the high mass productivity.

Industrial Applicability

The flat battery of the present invention has the peripheral section of the sealing plate and/or the turned edge of the case, which are formed to specific shapes. This arrangement ensures the secure caulking of the sealing plate, the gasket, and the case at the end of the case, thus giving the flat battery that is as thin as of not greater than 1 mm and has excellent leakage resistance and mass productivity.

Number	Date	Country
10-351629	Dec 1998	JP
11-016767	Jan 1999	JP
11-335936	Nov 1999	JP

Number	Name	Date	Kind
4659636	Suzuki et al.	Apr 1987	A
5486431	Tuttle et al.	Jan 1996	A
5707756	Inoue et al.	Jan 1998	A

Number	Date	Country
54-137731	Sep 1979	JP
55-068269	May 1980	JP
58-018364	Feb 1981	JP
57-173266	Nov 1982	JP
58-074764	May 1983	JP
58-179750	Dec 1983	JP
62-137557	Aug 1987	JP
05-013059	Jan 1993	JP
05-198292	Aug 1993	JP
08-339785	Dec 1996	JP
09-055227	Feb 1997	JP

	Number	Date	Country
Parent	PCT/JP99/06893	Dec 1999	US
Child	09/875217		US

Flat battery

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Term Extension

Abstract

Description

Claims

Priority Claims (3)

CROSS-REFERENCE TO RELATED APPLICATION

US Referenced Citations (3)

Foreign Referenced Citations (11)

Continuation in Parts (1)