Patent Grant
10494150
The present disclosure is directed to a flexible container for dispensing a flowable material and a process for producing the flexible container.
Known are flexible containers with a gusseted body section. These gusseted flexible containers are currently produced using flexible films which are folded to form gussets and heat sealed in a perimeter shape. The gusseted body section opens to form a flexible container with a square cross section or a rectangular cross section. The gussets are terminated at the bottom of the container to form a substantially flat base, providing stability when the container is partially or wholly filled. The gussets are also terminated at the top of the container to form an open neck for receiving a rigid fitment and closure.
Conventional procedures for fabricating gusseted flexible containers with a rigid fitment have shortcomings. One conventional approach only partially heat seals the flexible container—requiring the bottom of the container to remain unsealed or otherwise open. The rigid fitment is subsequently inserted through the open bottom of the container and into the neck. Once the fitment is placed into the neck, the heat seal process continues, with a heat seal formed to close the previously-open container bottom. This approach is inefficient as it interrupts the perimeter heat seal procedure and requires two steps to form the container.
Another conventional approach requires the rigid fitment to be manually installed, upside down, into the neck opening. The fitment is then rotated by hand inside of the flexible container and pushed into place, aligning the fitment with the neck opening to allow proper sealing between the flexible container film structure and the fitment. The fitment is subsequently clamp heat sealed to the neck. This approach is cumbersome, labor intensive and time consuming.
A need exists for a process of producing a gusseted flexible container which increases production efficiencies such as shortened production time, reduction of manual tasks via automation, and a streamlining of production steps.
A need further exists for a process of producing a gusseted flexible container with a fitment having improved impact strength.
A need further exists for a gusseted flexible container having a fitment with improved impact resistance and/or a thin-walled fitment.
The present disclosure provides a process for producing a flexible container and the resultant flexible container.
In an embodiment, a flexible container is provided. The flexible container includes four panels. The four panels form (i) a body portion; (ii) a neck portion, and a flare portion that extends from the neck portion; (iii) a tapered transition portion between the body portion and the neck portion; (iv) the neck portion having a reduced width, the flare portion having an expanded end. The width of the flare portion gradually increases from the neck portion to the expanded end.
The present disclosure provides another flexible container. In an embodiment a flexible container is provided and includes four panels. The four panels form (i) a body portion; (ii) a neck portion, and a flare portion that extends from the neck portion; (iii) a tapered transition portion between the body portion and the neck portion; (iv) the neck portion has a reduced width. The flexible container includes a fitment attached to the neck portion. The fitment is composed of a polymeric composition having an Izod impact resistance from greater than 50 J/m to 500 J/m.
The present disclosure provides another flexible container. In an embodiment, a flexible container is provided and includes four panels. The four panels form (i) a body portion, (ii) a neck portion, (iii) a tapered transition portion between the body portion and the neck portion, and (iv) the neck portion has a reduced width. The flexible container is void of a rigid fitment and includes a seal in the neck portion.
The present disclosure provides a process and a flexible container produced from the process. In an embodiment, the process includes (A) providing a flexible container with four panels. The four panels form (i) a body portion; (ii) a neck portion, and a flare portion that extends from the neck portion; (iii) a tapered transition portion between the body portion and the neck portion; and (iv) the neck portion has a reduced width, the flare portion has an expanded end; and the width of the flare portion gradually increases from the neck portion to the flare expanded end (i.e., the expanded end of the flare portion). The process includes (B) inserting a fitment into the flare portion from the expanded end.
1. Flexible Container
The process includes providing a flexible container 10. Flexible container 10 has a collapsed configuration (as shown in
The flexible container 10 is made from four panels. During the fabrication process, the panels are formed when one or more webs of film material are sealed together. While the webs may be separate pieces of film material, it will be appreciated that any number of the seams between the webs could be “pre-made,” as by folding one or more of the source webs to create the effect of a seam or seams. For example, if it were desired to fabricate the present flexible container from two webs instead of four, the bottom, left center, and right center webs could be a single folded web, instead of three separate webs. Similarly, one, two, or more webs may be used to produce each respective panel (i.e., a bag-in-a-bag configuration or a bladder configuration).
As shown in
When the container 10 is in the collapsed configuration, the flexible container is in a flattened, or in an otherwise evacuated state. The gusset panels 18, 20 fold inwardly (dotted gusset fold lines 60, 62 of
The four panels 18, 20, 22 and 24 can each be composed of a separate web of film material. The composition and structure for each web of film material can be the same or different. Alternatively, one web of film material may also be used to make all four panels and the top and bottom segments. In a further embodiment, two or more webs can be used to make each panel.
In an embodiment, four webs of film material are provided, one web of film for each respective panel 18, 20, 22, and 24. The process includes sealing edges of each film to the adjacent web of film to form peripheral seals 41 (
To form the top segment 28 and the bottom segment 26, the four webs of film converge together at the respective end and are sealed together. For instance, the top segment 28 can be defined by extensions of the panels sealed together at the tapered transition section III, the neck section IV, and the flare section V. The top end 44 includes four top panels 28a-28d (
The neck portion can extend from the transition portion. Alternatively, the neck portion can extend from one of the four panels of the body portion, or from a corner of the body portion.
In an embodiment, the neck 30 is positioned at a midpoint of the top segment 28. The neck 30 may (or may not) be sized smaller than a width of the body section III, such that the neck 30 can have an area that is less than a total area of the top segment 28. The location of the neck 30 can be anywhere on the top segment 28 of the container 10.
In an embodiment, the neck is formed from two or more panels. In a further embodiment, the neck 30 is formed from four panels.
Although
In an embodiment, the neck 30 is located in the top segment 28 and is centered between the legs 13 of the top handle 12.
The four panels of film that form the flexible container 10 extend from the body section II (forming body portion 47), to the tapered transition section III (forming tapered transition portion 48), to form a neck portion 30 (in the neck section IV) and a flare portion 50 (in the flare section V). The four panels of film also extend from the body section II to the bottom section I (forming bottom portion 49). When the flexible container 10 is in the collapsed configuration (
The expanded end 51 has a width G having a length that is greater than a width F of the neck portion 30, as shown in
When the flexible container 10 is in the expanded configuration (as shown in
As shown in
Each panel includes a respective bottom face.
The front panel bottom face 26a includes a first line A defined by the inner edge 29a of the first peripheral tapered seal 40a and a second line B defined by the inner edge 29b of the second peripheral tapered seal 40b. The first line A intersects the second line B at an apex point 35a in the bottom seal area 33. The front panel bottom face 26a has a bottom distalmost inner seal point 37a (“BDISP 37a”). The BDISP 37a is located on the inner edge.
The apex point 35a is separated from the BDISP 37a by a distance S from 0 millimeter (mm) to less than 8.0 mm.
In an embodiment, the rear panel bottom face 26c includes an apex point similar to the apex point on the front panel bottom face. The rear panel bottom face 26c includes a first line C defined by the inner edge of the 29c first peripheral tapered seal 40c and a second line D defined by the inner edge 29d of the second peripheral tapered seal 40d. The first line C intersects the second line D at an apex point 35c in the bottom seal area 33. The rear panel bottom face 26c has a bottom distalmost inner seal point 37c (“BDISP 37c”). The BDISP 37c is located on the inner edge. The apex point 35c is separated from the BDISP 37c by a distance T from 0 millimeter (mm) to less than 8.0 mm.
It is understood the following description to the front panel bottom face applies equally to the rear panel bottom face, with reference numerals to the rear panel bottom face shown in adjacent closed parentheses.
In an embodiment, the BDISP 37a (37c) is located where the inner edges 29a (29c) and 29b (29d) intersect. The distance between the BDISP 37a (37c) and the apex point 35a (35c) is 0 mm.
In an embodiment, the inner seal edge diverges from the inner edges 29a, 29b (29c, 29d), to form an inner seal arc 39a (front panel) and inner seal arc 39c (rear panel) as shown in
In an embodiment, apex point 35a (35c) is separated from the BDISP 37a (37c) by the distance S (distance T) which is from greater than 0 mm to less than 6.0 mm.
In an embodiment, the distance from S (distance T) from the apex point 35a (35c) to the BDISP 37a (37c) is from greater than 0 mm, or 0.5 mm or 1.0 mm, or 2.0 mm to 4.0 mm or 5.0 mm or less than 5.5 mm.
In an embodiment, apex point 35a (apex point 35c) is separated from the BDISP 37a (BDISP 37c) by the distance S (distance T) which is from 3.0 mm, or 3.5 mm, or 3.9 mm, to 4.0 mm, or 4.5 mm, or 5.0 mm, or 5.2 mm, or 5.3 mm, or 5.5 mm.
In an embodiment, the distal inner seal arc 39a (39c) has a radius of curvature from 0 mm, or greater than 0 mm, or 1.0 mm to 19.0 mm, or 20.0 mm.
In an embodiment, each peripheral tapered seal 40a-40d (outside edge) and an extended line from respective peripheral seal 41 (outside edge) form an angle G as shown in
The bottom segment 26 includes a pair of gussets 54 and 56 formed thereat, which are essentially extensions of the bottom faces 26a-26d. The gussets 54 and 56 can facilitate the ability of the flexible container 10 to stand upright. These gussets 54 and 56 are formed from excess material from each bottom face 26a-26d that are joined together to form the gussets 54 and 56. The triangular portions of the gussets 54 and 56 comprise two adjacent bottom segment panels sealed together and extending into its respective gusset. For example, adjacent bottom faces 26a and 26d extend beyond the plane of their bottom surface along an intersecting edge and are sealed together to form one side of a first gusset 54. Similarly, adjacent bottom faces 26c and 26d extend beyond the plane of their bottom surface along an intersecting edge and are sealed together to form the other side of the first gusset 54. Likewise, a second gusset 56 is similarly formed from adjacent bottom faces 26a-26b and 26b-26c. The gussets 54 and 56 can contact a portion of the bottom segment 26, where the gusset portions gussets 54 and 56 can contact bottom faces 26b and 26d covering them, while bottom segment panels 26a and 26c remain exposed at the bottom end 46.
As shown in
The top handle 12 and the bottom handle 14 can comprise up to four plys of film sealed together for a four panel container 10. When more than four panels are used to make the container, the handles can include the same number of panels used to produce the container. Any portion of the handles 12, 14 where all four plys are not completely sealed together by the heat-sealing method, can be adhered together in any appropriate manner, such as by a tack seal to form a fully-sealed multilayer handle. Alternatively, the top handle can be made from as few as a single ply of film from one panel only or can be made from only two plies of film from two panels. The handles 12, 14 can have any suitable shape and generally will take the shape of the film end. For example, typically the web of film has a rectangular shape when unwound, such that its ends have a straight edge. Therefore, the handles 12, 14 would also have a rectangular shape.
Additionally, the bottom handle 14 can contain a handle opening 16 or cutout section therein sized to fit a user's hand, as can be seen in
Furthermore, a portion of the bottom handle 14 attached to the bottom segment 26 can contain a dead machine fold 42 or a score line that provides for the handle 14 to consistently fold in the same direction, as illustrated in
Additionally, as the flexible container 10 is evacuated and less product remains, the bottom handle 14 can continue to provide support to help the flexible container 10 to remain standing upright unsupported and without tipping over. Because the bottom handle 14 is sealed generally along its entire length extending between the pair of gusset panels 18 and 20, it can help to keep the gussets 54 and 56 (
As seen in
A portion of the top handle 12 can extend above the neck portion 30 and above the top segment 28 when the handle 12 is extended in a position perpendicular to the top segment 28 and, in particular, the entire upper handle portion 12a can be above the flare portion 50 and the top segment 28. The two pairs of legs 13 and 15 along with the upper handle portion 12a together make up the handle 12 surrounding a handle opening that allows a user to place their hand therethrough and grasp the upper handle portion 12a of the handle 12.
As with the bottom handle 14, the top handle 12 also can have a dead machine fold that permits folding in a first direction toward the front side panel 22 and restricts folding in a second direction toward the rear side panel 24. The machine fold can be located in each of the pair of legs 13, 15 at a location where the seal begins. The handle 12 can be adhered together, such as with a tack adhesive, for example. The machine fold in the handle 12 can allow for the handle 12 to be inclined to fold or bend consistently in the same first direction X as the bottom handle 14, rather than in the second direction Y. As shown in
In an embodiment, either top handle 12 or bottom handle 14 can be “a punch-out handle,” that is, a handle formed by a process the cuts out or “punches” film material from the flexile container, thereby removing film material from the flexible container. The punch-out handle does not have, or is otherwise void of, flap portion 36 (for top handle 12) and/or flap portion 38 (for bottom handle 14).
In an embodiment, a grip member can be attached to either the top handle 12 or the bottom handle 14. The grip member can be placed around top handle 12 and/or bottom handle 14. Grip member can also be molded into the flexible container. The grip member can be adhesively attached to any portion of the flexible container. The grip member provides additional comfort to the user when carrying, or otherwise using, the flexible container. The grip member provides additional reinforcement to the flexible container. In a further embodiment, the grip member can be removed from the flexible container 10 after use and be re-used with another flexible container.
When the container 10 is in a rest position, such as when it is standing upright on its bottom segment 26, as shown in
The material of construction of the flexible container 10 can comprise food-grade plastic. For instance, nylon, polypropylene, polyethylene such as high density polyethylene (HDPE) and/or low density polyethylene (LDPE) may be used as discussed later. The film of the plastic container 10 can have a thickness and barrier properties that is adequate to maintain product and package integrity during manufacturing, distribution, product shelf life and customer usage.
In an embodiment, the flexible multilayer film has a thickness from 100 micrometers, or 200 micrometers, or 250 micrometers to 300 micrometers, or 350 micrometers, or 400 micrometers. In an embodiment, the film material provides the appropriate atmosphere within the flexible container 10 to maintain the product shelf life of at least about 180 days. Such films can comprise an oxygen barrier film, such as a film having a low oxygen transmission rate (OTR) from greater than 0 to 0.4 cc/m2/atm/24 hrs at 23° C. and 80% relative humidity (RH). Additionally, the flexible multilayer film can also comprise a water vapor barrier film, such as a film having a low water vapor transmission rate (WVTR) from greater than 0 to 15 g/m2/24 hrs at 38° C. and 90% RH. Moreover, it may be desirable to use materials of construction having oil and/or chemical resistance particularly in the seal layer, but not limited to just the seal layer. The flexible multilayer film can be either printable or compatible to receive a pressure sensitive label or other type of label for displaying of indicia on the flexible container 10.
In an embodiment the film can also be made of non-food grade resins for producing containers for materials other than food.
In an embodiment, each panel is made from a flexible multilayer film having at least one, or at least two, or at least three layers. The flexible multilayer film is resilient, flexible, deformable, and pliable. The structure and composition of the flexible multilayer film for each panel may be the same or different. For example, each of the four panels can be made from a separate web, each web having a unique structure and/or unique composition, finish, or print. Alternatively, each of the four panels can be the same structure and the same composition.
In an embodiment, each panel 18, 20, 22, 24 is a flexible multilayer film having the same structure and the same composition.
The flexible multilayer film may be (i) a coextruded multilayer structure or (ii) a laminate, or (iii) a combination of (i) and (ii). In an embodiment, the flexible multilayer film has at least three layers: a seal layer, an outer layer, and a tie layer between. The tie layer adjoins the seal layer to the outer layer. The flexible multilayer film may include one or more optional inner layers disposed between the seal layer and the outer layer.
In an embodiment, the flexible multilayer film is a coextruded film having at least two, or three, or four, or five, or six, or seven to eight, or nine, or 10, or 11, or more layers. Some methods, for example, used to construct films are by cast co-extrusion or blown co-extrusion methods, adhesive lamination, extrusion lamination, thermal lamination, and coatings such as vapor deposition. Combinations of these methods are also possible. Film layers can comprise, in addition to the polymeric materials, additives such as stabilizers, slip additives, antiblocking additives, process aids, clarifiers, nucleators, pigments or colorants, fillers and reinforcing agents, and the like as commonly used in the packaging industry. It is particularly useful to choose additives and polymeric materials that have suitable organoleptic and or optical properties.
In another embodiment, the flexible multilayer film can comprise a bladder wherein two or more films that are adhered in such a manner as to allow some delamination of one or more plies to occur during a significant impact such that the inside film maintains integrity and continues to hold contents of the container.
Nonlimiting examples of suitable polymeric materials for the seal layer include olefin-based polymer (including any ethylene/C3-C10 α-olefin copolymers linear or branched), propylene-based polymer (including plastomer and elastomer, random propylene copolymer, propylene homopolymer, and propylene impact copolymer), ethylene-based polymer (including plastomer and elastomer, high density polyethylene (“HDPE”), low density polyethylene (“LDPE”), linear low density polyethylene (“LLDPE”), medium density polyethylene (“MDPE”), ethylene-acrylic acid or ethylene-methacrylic acid and their ionomers with zinc, sodium, lithium, potassium, magnesium salts, ethylene vinyl acetate copolymers and blends thereof.
Nonlimiting examples of suitable polymeric material for the outer layer include those used to make biaxially or monoaxially oriented films for lamination as well as coextruded films. Some nonlimiting polymeric material examples are biaxially oriented polyethylene terephthalate (OPET), monoaxially oriented nylon (MON), biaxially oriented nylon (BON), and biaxially oriented polypropylene (BOPP). Other polymeric materials useful in constructing film layers for structural benefit are polypropylenes (such as propylene homopolymer, random propylene copolymer, propylene impact copolymer, thermoplastic polypropylene (TPO) and the like, propylene-based plastomers (e.g., VERSIFY™ or VISTAMAX™)), polyamides (such as Nylon 6, Nylon 6,6, Nylon 6,66, Nylon 6,12, Nylon 12 etc.), polyethylene norbornene, cyclic olefin copolymers, polyacrylonitrile, polyesters, copolyesters (such as PETG), cellulose esters, polyethylene and copolymers of ethylene (e.g., LLDPE based on ethylene octene copolymer such as DOWLEX™, blends thereof, and multilayer combinations thereof.
Nonlimiting examples of suitable polymeric materials for tie layer include functionalized ethylene-based polymers such as ethylene-vinyl acetate (“EVA”), polymers with maleic anhydride-grafted to polyolefins such as any polyethylene, ethylene-copolymers, or polypropylene, and ethylene acrylate copolymers such an ethylene methyl acrylate (“EMA”), glycidyl containing ethylene copolymers, propylene and ethylene based olefin block copolymers INFUSE™ Olefin Block Copolymers available for the Dow Chemical Company and INTUNE™ (PP-based Olefin Block Copolymers available from The Dow Chemical Company, and blends thereof.
The flexible multilayer film may include additional layers which may contribute to the structural integrity or provide specific properties. The additional layers may be added by direct means or by using appropriate tie layers to the adjacent polymer layers. Polymers which may provide additional mechanical performance such as stiffness or opacity, as well polymers which may offer gas barrier properties or chemical resistance can be added to the structure.
Nonlimiting examples of suitable material for the optional barrier layer include copolymers of vinylidene chloride and methyl acrylate, methyl methacrylate or vinyl chloride (e.g., SARAN resins available from The Dow Chemical Company); vinylethylene vinyl alcohol (EVOH), metal foil (such as aluminum foil). Alternatively, modified polymeric films such as vapor deposited aluminum or silicon oxide on such films as BON, OPET, or OPP, can be used to obtain barrier properties when used in laminate multilayer film.
In an embodiment, the flexible multilayer film includes a seal layer selected from LLDPE (sold under the trade name DOWLEX™ (The Dow Chemical Company)), single-site LLDPE substantially linear, or linear ethylene alpha-olefin copolymers, including polymers sold under the trade name AFFINITY™ or ELITE™ (The Dow Chemical Company) for example, propylene-based plastomers or elastomers such as VERSIFY™ (The Dow Chemical Company), and blends thereof. An optional tie layer is selected from either ethylene-based olefin block copolymer PE-OBC (sold as INFUSE™) or propylene-based olefin block copolymer PP-OBC (sold as INTUNE™). The outer layer includes greater than 50 wt % of resin(s) having a melting point, Tm, that is from 25° C., to 30° C., or 40° C. or higher than the melting point of the polymer in the seal layer wherein the outer layer polymer is selected from resins such as VERSIFY or VISTAMAX, ELITE™, HDPE or a propylene-based polymer such as propylene homopolymer, propylene impact copolymer or TPO.
In an embodiment, the flexible multilayer film is co-extruded.
In an embodiment, flexible multilayer film includes a seal layer selected from LLDPE (sold under the trade name DOWLEX™ (The Dow Chemical Company)), single-site LLDPE (substantially linear, or linear, olefin polymers, including polymers sold under the trade name AFFINITY™ or ELITE™ (The Dow Chemical Company) for example, propylene-based plastomers or elastomers such as VERSIFY™ (The Dow Chemical Company), and blends thereof. The flexible multilayer film also includes an outer layer that is a polyamide.
In an embodiment, the flexible multilayer film is a coextruded film and includes:
(i) a seal layer composed of an olefin-based polymer having a first melt temperature less than 105° C., (Tm1); and
(ii) an outer layer composed of a polymeric material having a second melt temperature, (Tm2),
wherein Tm2−Tm1>40° C.
The term “Tm2−Tm1” is the difference between the melt temperature of the polymer in the outer layer and the melt temperature of the polymer in the seal layer, and is also referred to as “ΔTm.” In an embodiment, the ΔTm is from 41° C., or 50° C., or 75° C., or 100° C., to 125° C., or 150° C., or 175° C., or 200° C.
In an embodiment, the flexible multilayer film is a coextruded film, the seal layer is composed of an ethylene-based polymer, such as a linear or a substantially linear polymer, or a single-site catalyzed linear or substantially linear polymer of ethylene and an alpha-olefin monomer such as 1-butene, 1-hexene or 1-octene, having a Tm from 55° C. to 115° C. and a density from 0.865 to 0.925 g/cm3, or from 0.875 to 0.910 g/cm3, or from 0.888 to 0.900 g/cm3 and the outer layer is composed of a polyamide having a Tm from 170° C. to 270° C.
In an embodiment, the flexible multilayer film is a coextruded film having at least five layers, the coextruded film having a seal layer composed of an ethylene-based polymer, such as a linear or substantially linear polymer, or a single-site catalyzed linear or substantially linear polymer of ethylene and an alpha-olefin comonomer such as 1-butene, 1-hexene or 1-octene, the ethylene-based polymer having a Tm from 55° C. to 115° C. and density from 0.865 to 0.925 g/cm3, or from 0.875 to 0.910 g/cm3, or from 0.888 to 0.900 g/cm3 and an outermost layer composed of a polyamide having a Tm from 170° C. to 270° C.
In an embodiment, the flexible multilayer film is a coextruded film having at least seven layers. The seal layer is composed of an ethylene-based polymer, such as a linear or substantially linear polymer, or a single-site catalyzed linear or substantially linear polymer of ethylene and an alpha-olefin comonomer such as 1-butene, 1-hexene or 1-octene, the ethylene-based polymer having a Tm from 55° C. to 115° C. and density from 0.865 to 0.925 g/cm3, or from 0.875 to 0.910 g/cm3, or from 0.888 to 0.900 g/cm3. The outer layer is a polyamide having a Tm from 170° C. to 270° C.
In an embodiment, the flexible multilayer film includes a seal layer composed of an ethylene-based polymer, or a linear or substantially linear polymer, or a single-site catalyzed linear or substantially linear polymer of ethylene and an alpha-olefin monomer such as 1-butene, 1-hexene or 1-octene, having a heat seal initiation temperature (HSIT) from 65° C. to less than 125° C. Applicant discovered that the seal layer with an ethylene-based polymer with a HSIT from 65° C. to less than 125° C. advantageously enables the formation of secure seals and secure sealed edges around the complex perimeter of the flexible container. The ethylene-based polymer with HSIT from 65° C. to less than 125° C. is a robust sealant which also allows for better sealing to the rigid fitment which is prone to failure. The ethylene-based polymer with HSIT from 65° C. to 125° C. enables lower heat sealing pressure/temperature during container fabrication. Lower heat seal pressure/temperature results in lower stress at the fold points of the gusset, and lower stress at the union of the films in the top segment and in the bottom segment. This improves film integrity by reducing wrinkling during the container fabrication. Reducing stresses at the folds and seams improves the finished container mechanical performance. The low HSIT ethylene-based polymer seals at a temperature below what would cause the outer layer to be compromised.
In an embodiment, the flexible multilayer film is a coextruded five layer film, or a coextruded seven layer film having at least two layers containing an ethylene-based polymer. The ethylene-based polymer may be the same or different in each layer.
In an embodiment, the flexible multilayer film is a coextruded five layer, or a coextruded seven layer film having at least two layers containing a polyamide polymer.
In an embodiment, the flexible multilayer film is a seven-layer coextruded film with a seal layer composed of an ethylene-based polymer, or a linear or substantially linear polymer, or a single-site catalyzed linear or substantially linear polymer of ethylene and an alpha-olefin monomer such as 1-butene, 1-hexene or 1-octene, having a Tm from 90° C. to 104° C. The outer layer is a polyamide having a Tm from 170° C. to 270° C. The film has a ΔTm from 40° C. to 200° C. The film has an inner layer (first inner layer) composed of a second ethylene-based polymer, different than the ethylene-based polymer in the seal layer. The film has an inner layer (second inner layer) composed of a polyamide the same or different to the polyamide in the outer layer. The seven layer film has a thickness from 100 micrometers to 250 micrometers.
In
In an embodiment, the apex point 35a is located above the overseal 64. The apex point 35a is separated from, and does not contact the overseal 64. The BDISP 37a is located above the overseal 64. The BDISP 37a is separated from and does not contact the overseal 64.
In an embodiment, the apex point 35a is located between the BDISP 37a and the overseal 64, wherein the overseal 64 does not contact the apex point 35a and the overseal 64 does not contact the BDISP 37a.
The distance between the apex point 35a to the top edge of the overseal 64 is defined as distance W shown in
When more than four webs are used to produce the container, the portion 68 of the overseal 64 may be a 4-ply, or a 6-ply, or an 8-ply portion.
In an embodiment, the flexible container 10 has a vertical drop test pass rate from 90%, or 95% to 100%. The vertical drop test is conducted as follows. The container is filled with tap water to its nominal capacity, conditioned at 25° C. for at least 3 hours, held in upright position from its upper handle at 1.5 m height (from the base or side of the container to the ground), and released to a free fall drop onto a concrete slab floor. If any leak is detected immediately after the drop, the test is recorded as a failure. A minimum of twenty flexible containers are tested. A percentage for pass/fail containers is then calculated.
In an embodiment, the flexible container 10 has a side drop pass rate from 90%, or 95% to 100%. This side drop test is conducted as follows. The container is filled with tap water to its nominal capacity, conditioned at 25° C. for at least 3 hours, held in upright position from its upper handle. The flexible container is released on its side from a 1.5 m height to a free fall drop onto a concrete slab floor. If any leak is detected immediately after the drop, the test is recorded as failure. A minimum of twenty flexible containers are tested. A percentage for pass/fail containers is then calculated.
In an embodiment, the flexible container 10 passes the stand-up test where the package is filled with water at ambient temperature and placed on a flat surface for seven days and it should remain in the same position, with unaltered shape or position.
In an embodiment, the flexible container 10 has a volume from 0.050 liters (L), or 0.1 L, or 0.15 L, or 0.2 L, or 0.25 liters (L), or 0.5 L, or 0.75 L, or 1.0 L, or 1.5 L, or 2.5 L, or 3 L, or 3.5 L, or 4.0 L, or 4.5 L, or 5.0 L to 6.0 L, or 7.0 L, or 8.0 L, or 9.0 L, or 10.0 L, or 20 L, or 30 L.
The flexible container 10 can be used to store any number of flowable substances therein. In particular, a flowable food product can be stored within the flexible container 10. In one aspect, flowable food products such as salad dressings, sauces, dairy products, mayonnaise, mustard, ketchup, other condiments, beverages such as water, juice, milk, or syrup, carbonated beverages, beer, wine, animal feed, pet feed, and the like can be stored inside of the flexible container 10.
The flexible container 10 is suitable for storage of other flowable substances including, but not limited to, oil, paint, grease, chemicals, suspensions of solids in liquid, and solid particulate matter (powders, grains, granular solids).
The flexible container 10 is suitable for storage of flowable substances with higher viscosity and requiring application of a squeezing force to the container in order to discharge. Nonlimiting examples of such squeezable and flowable substances include grease, butter, margarine, soap, shampoo, animal feed, sauces, and baby food.
2. Fitment
The present process includes inserting a fitment into the flare portion 50 from the expanded end 51. As shown in
In an embodiment, the outer surface of the base 72 has surface texture. The surface texture can include embossment 73, and a plurality of radial ridges to promote sealing to the inner surface of the neck portion 30 as will be discussed below.
In an embodiment, the fitment 70 excludes fitments with oval, wing-shaped, eye-shaped, or canoe-shaped bases.
Although
In an embodiment, the closure 74 is watertight. In a further embodiment, the closure 74 provides a hermetic seal to the container 10.
In an embodiment, the fitment 70 can be made of a rigid construction and can be formed of any appropriate plastic, such as high density polyethylene (HDPE), low density polyethylene (LDPE), polypropylene (PP), and combinations thereof. The location of the neck portion 30 can be anywhere on the top segment 28 of the container 10. In an embodiment the neck portion 30 is located at the center or midpoint of the top segment 28.
In an embodiment, the fitment is made by co-injection of a two-component structure A/B wherein A is an inside material having a melting point, Tm, greater than the Tm of an outside material B (seal side). In another embodiment, the materials A and B are different types of materials, where an optional tie layer C adheres material A to material B. In a further embodiment, the outside material B has a low coefficient of friction (COF) to facilitate fitment insertion into the neck portion 30.
In an embodiment, the fitment 70 includes a polymeric composition having an Izod impact resistance from greater than 50 Joules (J)/meter (m), or 100 J/m, or 150 J/m, or 200 J/m, or 250 J/m to 300 J/m, or 350 J/m, or 400 J/m, or 450 J/m, or 500 J/m. Izod impact resistance is measured in accordance with ASTM D 256. In a further embodiment, the fitment includes a polyolefin having an Izod impact resistance from greater than 50 J/m, or 100 J/m, or 150 J/m, or 200 J/m, or 250 J/m to 300 J/m, or 350 J/m, or 400 J/m, or 450 J/m, or 500 J/m.
In an embodiment, the fitment 70 includes a polymeric composition containing a polyolefin with a melt temperature (Tm) greater than or equal to the melt temperature of the polyolefin present in the seal layer of the multilayer film used to make the panels. When clamp heat sealing is utilized to form the seal between the base 72 and the neck portion 30, a nonlimiting example includes a fitment 70 composed of a HDPE having a Tm of 125° C. and the seal layer for the container 10 contains an LDPE with a Tm of 105° C. Another nonlimiting example is a fitment 70 composed of LLDPE with Tm of 120° C., and the container 10 has a seal layer containing an ethylene/α-olefin copolymer (AFFINITY™ PL 1140G) with a Tm 96° C.
In an embodiment, the process includes supporting the fitment 70 on a mandrel 80, and subsequently inserting the fitment 70 first into the expanded end 51, then into the flare portion 50, and then into the neck portion 30. A plurality of fitments may be fed sequentially to the mandrel 80 by an automated feed system as shown in
In an embodiment, the mandrel 80 is a component of an automated system, the mandrel a component of a movable arm as shown in
Although
In an embodiment, the process includes adjoining the fitment 70 to the neck portion 30. As shown in
With the base 72 located in the neck portion 30, an embodiment of the process includes heat sealing the base 72 of the fitment 70 to the neck portion 30. The heat sealing procedure utilizes opposing heat seal clamps 90, 92 as shown in
In an embodiment, the process includes ultrasonic sealing the base 72 of the fitment 70 to the neck portion 30. Ultrasonic sealing entails directing ultrasonic vibration to the interface between the base 72 and the neck portion 30 while pressure is applied. The ultrasonic energy melts a portion of the interface to create a seal between the base 72 and the neck portion 30. In an embodiment, the process includes ultrasonically sealing a base 72 composed of ethylene/α-olefin copolymer such as ELITE™ (4.0 MI and 122° C. Tm) to a neck portion 30 having seal layer composed of ethylene/α-olefin copolymer ELITE™ 5400G (1.0 MI, 122° C. Tm) and/or ethylene/α-olefin copolymer AFFINITY™ PL 1880G (1.0 MI, 99° C. Tm).
Since ultrasonic sealing heats only the seal layer, the Tm of the seal layer can be from 10° C. to 5° C. less than the Tm of the fitment. In an embodiment, the process includes ultrasonically sealing a fitment 70 composed of an ethylene/α-olefin copolymer (such as AFFINTIY™ PL 1880G) having a Tm of 99° C. to a neck portion 30 having a seal layer composed of an LDPE with a Tm of 105° C.
In an embodiment, the process includes rotating the flexible container 90° or from 80° to 100°, with respect to the heat seal clamps and repeating the heat sealing procedure described above.
In an embodiment, the process includes forming a watertight seal between the base 72 and the neck portion 30.
In an embodiment, the process includes forming a watertight and airtight seal between the base 72 and the neck portion 30.
As shown in
In an embodiment, the process includes removing the excess flare portion 96 from the flexible container 10.
In an embodiment, the process includes inserting the fitment through the flare portion. The mandrel enters the neck portion such that the fitment base enters the container interior. The mandrel may extend to such a length that the entire fitment (base and top) may be inserted, or otherwise enter, the container interior. The process includes contacting the score device with the neck portion and supporting the neck portion with the mandrel during the contacting. The process includes rotating the neck portion (or rotating the score device) to cut excess flare portion from the neck portion. In this way, the mandrel supports the neck during scoring, thereby avoiding cuts to the fitment. The process includes removing the excess flare portion from the neck portion. Once the excess flare portion is removed, the process includes retracting, with the mandrel, the fitment into the neck portion and sealing the fitment base to the neck portion.
In an embodiment, a flowable substance can be added to the flexible container 10 either before or after the fitment 70 is inserted into the flare portion 50. The flowable substance can be any flowable substance (particulate or liquid) as previously disclosed above. In one embodiment, the process includes inserting a flowable substance through the fitment 70 that is previously adjoined to the neck portion 30.
In another embodiment, the process includes adding a flowable substance to the flexible container interior before the fitment 70 is inserted into the expanded end 51. The process includes adding the flowable substance through the expanded end 51, through the flare portion 50, through the neck portion 30, and into the container interior. After flowable substance is added to the container interior, the fitment 70 can be inserted into the expanded end 51, into the flare portion 50, and adjoined to the neck portion 30 as previously discussed above.
In an embodiment, a carry member is attached to the fitment. The carry member can be attached to fit around a portion of, or all, the outer circumference of the fitment by way of one, some, or all of the following: friction fit, compression fit, and snap-on fit. The carry member is advantageous when the flexible container does not include handles. The carry member can also be used to dispense the contents from the flexible container.
3. Sealed Container No Fitment
The present disclosure provides another process. In an embodiment, the process includes (A) providing a flexible container with four panels. The four panels form (i) a body portion, (ii) a neck portion, (iii) a tapered transition portion between the body portion and the neck portion, and (iv) the neck portion has a reduced width. The process includes (B) adding, through the neck, a flowable substance into the container interior; and (C) sealing the neck portion.
The flexible container can be any flexible container as described above. However, in this embodiment, the flexible container lacks a fitment (i.e., lacks fitment 70) and the flare portion is optional.
In an embodiment, the flexible container does not include, or is otherwise void of, a flare portion as shown in
In an embodiment, the neck seal 150 is a heat seal.
The neck seal 150 may include notches 152 (or cut-outs), and/or a perforation 154 to promote actuation of, or opening, the neck seal 150. Actuation of the neck seal 150 may be performed by hand (tear seal) or by way of scissors, blade or other sharp object.
In an embodiment, the flexible container 10 includes the flare portion 50 as shown in
The flare seal 160 can include notches 162 and/or a perforation 164 to promote actuation of the flange seal as disclosed above with respect to the neck seal.
The flexible container with the neck seal or the flare seal can be a single use container or a re-sealable container. In an embodiment, the flexible container is a single use container and the process includes adding a flowable substance through either the neck portion 30 (or through the flare portion 50) and into the container interior. With the flowable substance in the container interior, the process includes forming a notched seal (also known as a tear seal) in either the neck portion 30 (notches 152,
In an embodiment, either the neck seal 150 or the flare seal 160 can be a re-sealable seal. The process includes adding a flowable substance through the neck 30 (or through the expanded end 51, through the flare portion 50, through the neck portion 30), and into the container interior. With the flowable substance in the container interior, the process includes forming a re-sealable seal in either the neck portion 30 or in the flare portion 50.
In an embodiment, either the neck seal 150 or the flare seal 160 includes a microcapillary strip. With actuation of seal 150/160, the microcapillary strip provides controlled spray delivery of the container contents.
In an embodiment, either the neck seal 150 or the flare seal 160 may include a closure. The closure covers the exposed opening of the neck seal or flare seal after the seal has been actuated. Nonlimiting examples of suitable closures include a Ziploc-type closure, hook and loop material (i.e., Velcro), an adhesive strip (such as packaging tape, for example), and flexible material hingedly attached to the flexible pouch for placement over the opened seal.
The present process may comprise two or more embodiments disclosed herein.
The numerical ranges disclosed herein include all values from, and including, the lower value and the upper value. For ranges containing explicit values (e.g., 1 or 2, or 3 to 5, or 6, or 7) any subrange between any two explicit values is included (e.g., 1 to 2; 2 to 6; 5 to 7; 3 to 7; 5 to 6; etc.).
Unless stated to the contrary, implicit from the context, or customary in the art, all parts and percents are based on weight, and all test methods are current as of the filing date of this disclosure.
The term “composition,” as used herein, refers to a mixture of materials which comprise the composition, as well as reaction products and decomposition products formed from the materials of the composition.
The terms “comprising,” “including,” “having,” and their derivatives, are not intended to exclude the presence of any additional component, step or procedure, whether or not the same is specifically disclosed. In order to avoid any doubt, all compositions claimed through use of the term “comprising” may include any additional additive, adjuvant, or compound, whether polymeric or otherwise, unless stated to the contrary. In contrast, the term, “consisting essentially of” excludes from the scope of any succeeding recitation any other component, step or procedure, excepting those that are not essential to operability. The term “consisting of” excludes any component, step or procedure not specifically delineated or listed.
Dart drop test is measured in accordance with ASTM D 1709 with results reported in grams, g.
Density is measured in accordance with ASTM D 792 with results reported as grams per cubic centimeter, or g/cm3.
Elmendorf tear, machine direction, MD, cross direction CD, is measured in accordance with ASTM D 1922, with results reported in grams, g.
An “ethylene-based polymer,” as used herein is a polymer that contains more than 50 mole percent polymerized ethylene monomer (based on the total amount of polymerizable monomers) and, optionally, may contain at least one comonomer.
Flexural modulus (2%) is measured in accordance with ASTM D 790 with results reported in megaPascals, MPa.
The term “heat seal initiation temperature,” is minimum sealing temperature required to form a seal of significant strength, in this case, 2 lb/in (8.8N/25.4 mm). The seal is performed in a Topwave HT tester with 0.5 seconds dwell time at 2.7 bar (40 psi) seal bar pressure. The sealed specimen is tested in an Instron Tensiomer at 10 in/min (4.2 mm/sec or 250 mm/min).
Izod impact resistance is measured at 25° C. and in accordance with ASTM D 256 with results reported in Joules per meter, J/m.
Melt flow rate (MFR) is measured in accordance with ASTM D 1238, Condition 280° C./2.16 kg (g/10 minutes).
Melt index (MI) is measured in accordance with ASTM D 1238, Condition 190° C./2.16 kg (g/10 minutes).
Secant modulus (2%), MD and CD, is measured in accordance with ASTM D 882 with results reported as megaPascals, or MPa.
Strain at tensile strength, MD and CD, is measured in accordance with ASTM D 882 with results reported as percent, %.
Tensile elongation to break is measured in accordance with ASTM D 638 with results reported in percent, %.
Tensile strength, MD and CD, is measured in accordance with ASTM D 882 with results reported as megaPascals, or MPa.
Tensile strength to yield is measured in accordance with ASTM D 638 results reported in megaPascals, MPa.
Tm or “melting point” as used herein (also referred to as a melting peak in reference to the shape of the plotted DSC curve) is typically measured by the DSC (Differential Scanning calorimetry) technique for measuring the melting points or peaks of polyolefins as described in U.S. Pat. No. 5,783,638. It should be noted that many blends comprising two or more polyolefins will have more than one melting point or peak, many individual polyolefins will comprise only one melting point or peak.
An “olefin-based polymer,” as used herein is a polymer that contains more than 50 mole percent polymerized olefin monomer (based on total amount of polymerizable monomers), and optionally, may contain at least one comonomer. Nonlimiting examples of olefin-based polymer include ethylene-based polymer and propylene-based polymer.
A “polymer” is a compound prepared by polymerizing monomers, whether of the same or a different type, that in polymerized form provide the multiple and/or repeating “units” or “mer units” that make up a polymer. The generic term polymer thus embraces the term homopolymer, usually employed to refer to polymers prepared from only one type of monomer, and the term copolymer, usually employed to refer to polymers prepared from at least two types of monomers. It also embraces all forms of copolymer, e.g., random, block, etc. The terms “ethylene/α-olefin polymer” and “propylene/α-olefin polymer” are indicative of copolymer as described above prepared from polymerizing ethylene or propylene respectively and one or more additional, polymerizable α-olefin monomer. It is noted that although a polymer is often referred to as being “made of” one or more specified monomers, “based on” a specified monomer or monomer type, “containing” a specified monomer content, or the like, in this context the term “monomer” is understood to be referring to the polymerized remnant of the specified monomer and not to the unpolymerized species. In general, polymers herein are referred to has being based on “units” that are the polymerized form of a corresponding monomer.
A “propylene-based polymer” is a polymer that contains more than 50 mole percent polymerized propylene monomer (based on the total amount of polymerizable monomers) and, optionally, may contain at least one comonomer.
Some embodiments of the present disclosure will now be described in detail in the following Examples.
1. Materials
Four panel flexible containers having a neck and a body as shown in
The flexible containers are fabricated under the heat seal conditions provided in Table 3 below using fabrication equipment by KRW Machinery Inc. (Weaverville, N.C.). All seals in the flexible containers are made with one strike.
The flexible containers have the container geometry as described herein. In particular, each flexible container tested has the bottom geometry as shown in
Table 4 provides nonlimiting examples of materials suitable to produce a fitment that can be used in the present process. In an embodiment, the fitment is composed of a material having an Izod impact resistance from greater than 50 J/m to 500 J/m and shown in Table 4 below.
40+
5+
+MFR
A 3.875 L container blank made at the above conditions of film ISO X7-7135C-1TC and sealed as in Table 3 having no flare portion (fully formed container but has not had fitment yet attached) such that the neck is uniform in diameter. An HDPE fitment (70) of design shown in
A 3.875 L container blank made at the above conditions of film ISO X7-7135C-1TC and sealed as in Table 3 but having a flare portion such that top opening is a greater diameter than the neck diameter. An HDPE fitment 70 of design shown in
A 3.875 L container blank made at the above conditions of film ISO X7-7135C-1TC and sealed as in Table 3 but having a flare portion such that top opening is a greater diameter than the neck diameter. An HDPE fitment 70 of design shown in
A 3.875 L container blank made at the above conditions of film listed in Table 1 above has no fitment but having a flare portion such that top opening is a greater diameter than the neck diameter. An HDPE fitment 70 of design shown in
Table 5 shows the production steps from fitment insertion to heat sealing. These steps constitute the total time to build a flexible container with fitment, i.e., the “Total Build Time.” Total Build Time is reported in seconds. The values in Table 5 are an average of 10 production runs under the stated parameters for each sample.
Examples 1-3 each have a Total Build Time that is less than the Total Build Time for Comparative Sample 1. Table 5 shows that provision of the flare portion reduces production time (i.e., reduces Total Build Time) and improves production efficiency.
Containers are made as in the process described in Example 1 but using an alternate 38 mm fitment material having 1.6 mm wall thickness. The examples in Table 6 show a fitment consisting of different materials can be successfully installed. In an embodiment, the fitments have Izod impact strengths by ASTM D256 from greater than 50 J/m to 500 J/m. Table 6 also shows seals that have both strength and hermeticity can be achieved as shown by successful burst and hang tests, respectively.
Burst Test Procedure
Process:
Gravity Hang Test Procedure
Process:
Wall thickness is thickness (in mm) of the fitment base.
For example, the stiffness factor of HDPE 8262B at 1 mm wall thickness (1.1), is equivalent to the stiffness factor (1.1) of LLDPE Dowlex 2535 or LDPE 9931 at a wall thickness of 1.5 mm. For a lower modulus material such as ENGAGE 8401, a wall thickness of 3.3 mm would be required to obtain a stiffness factor of 1.1.
Applicant discovered that utilization of the present process (mandrel support of fitment and subsequent fitment insertion into neck portion via expanded end and flare portion) advantageously enables “thin-walling,” or the reduction of the wall thickness for the fitment base, permitting the use of thinner walled fitments as well as the opportunity to use different materials for the fitments.
For example, the wall thickness of the fitment base used in conventional four-sided flexible containers is about 2.0 mm. The present process advantageously enables “thin-walling,” or the reduction of the wall thickness for the base of the fitment. Applicant unexpectedly found that the present process enables the production of a four-panel flexible container with a fitment having a base wall thickness from 0.15 mm, or 0.2 mm, or 0.3 mm, or 0.5 mm, or 0.7 mm, or 0.9 mm, or 1.0 mm to 1.1 mm, or 1.3 mm, or 1.5 mm, or 1.7 mm, or 1.9 mm.
It is specifically intended that the present disclosure not be limited to the embodiments and illustrations contained herein, but include modified forms of those embodiments including portions of the embodiments and combinations of elements of different embodiments as come with the scope of the following claims.
| Number | Name | Date | Kind |
|---|---|---|---|
| 1433303 | Sampson | Oct 1922 | A |
| 3003681 | Rene | Oct 1961 | A |
| 3112047 | Weinreich et al. | Nov 1963 | A |
| 3434652 | Shore | Mar 1969 | A |
| 3810503 | Lewis, Jr. | May 1974 | A |
| 5761884 | Tobolka | Jun 1998 | A |
| 5783638 | Lai et al. | Jul 1998 | A |
| 5823383 | Hins | Oct 1998 | A |
| 5855544 | Buchanan | Jan 1999 | A |
| 5918984 | LaFleur | Jul 1999 | A |
| 6126315 | Ichikawa et al. | Oct 2000 | A |
| 6511568 | Eckstein | Jan 2003 | B1 |
| 6832852 | Wilkes | Dec 2004 | B2 |
| 7005150 | Kuge | Feb 2006 | B2 |
| 7147597 | Wilkes | Dec 2006 | B2 |
| 8231029 | Peer et al. | Jul 2012 | B2 |
| 8348509 | Wilkes et al. | Jan 2013 | B2 |
| 8360275 | Last | Jan 2013 | B2 |
| 8840305 | Wilkes et al. | Sep 2014 | B2 |
| 9624005 | Pereira | Apr 2017 | B2 |
| 9908668 | Wilkes | Mar 2018 | B2 |
| 20030077010 | Schulz | Apr 2003 | A1 |
| 20040136620 | Wilson | Jul 2004 | A1 |
| 20040144811 | Pennaneac'H | Jul 2004 | A1 |
| 20050031230 | Ernst | Feb 2005 | A1 |
| 20110286688 | Gum | Nov 2011 | A1 |
| 20150104120 | Huckriede | Apr 2015 | A1 |
| 20160016679 | Pereira | Jan 2016 | A1 |
| Number | Date | Country |
|---|---|---|
| 1088508 | Jun 1994 | CN |
| 3925871 | Feb 1991 | DE |
| 1182144 | Feb 2002 | EP |
| 1463579 | Feb 1977 | GB |
| 2004168341 | Jun 2004 | JP |
| 2006056523 | Mar 2006 | JP |
| 2011001125 | Jan 2011 | JP |
| 2005108228 | Nov 2005 | WO |
| Entry |
|---|
| Machine translation of the description of JP 2004168341 A. |
| Machine translation of the description of JP 2006056523 A. |
| Number | Date | Country | |
|---|---|---|---|
| 20170190493 A1 | Jul 2017 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62025273 | Jul 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14800264 | Jul 2015 | US |
| Child | 15465848 | US |