Patent Application
20050202245
The present invention relates to planar flexible graphite articles, such as flexible graphite sheet, and to a system and method for continuously producing such articles. More particularly, the present invention relates to flexible graphite sheet material that exhibits enhanced isotropy with respect to thermal and electrical conductivity and fluid diffusion, as well as to a method for producing the sheet.
Graphites are made up of layer planes of hexagonal arrays or networks of carbon atoms. These layer planes of hexagonally arranged carbon atoms are substantially flat and are oriented or ordered so as to be substantially parallel and equidistant to one another. The substantially flat, parallel equidistant sheets or layers of carbon atoms, usually referred to as basal planes, are linked or bonded together and groups thereof are arranged in crystallites. Highly ordered graphites consist of crystallites of considerable size: the crystallites being highly aligned or oriented with respect to each other and having well ordered carbon layers. In other words, highly ordered graphites have a high degree of preferred crystallite orientation. It should be noted that graphites possess anisotropic structures and thus exhibit or possess many properties that are highly directional, e.g., thermal and electrical conductivity and fluid diffusion. Briefly, graphites may be characterized as laminated structures of carbon, that is, structures consisting of superposed layers or laminae of carbon atoms joined together by weak van der Waals forces. In considering the graphite structure, two axes or directions are usually noted, to wit, the “c” axis or direction and the “a” axes or directions. For simplicity, the “c” axis or direction may be considered as the direction perpendicular to the carbon layers. The “a” axes or directions may be considered as the directions parallel to the carbon layers or the directions perpendicular to the “c” direction. The natural graphites suitable for manufacturing flexible graphite possess a very high degree of orientation.
As noted above, the bonding forces holding the parallel layers of carbon atoms together are only weak van der Waals forces. Graphites, especially natural graphites, can be treated so that the spacing between the superposed carbon layers or laminae can be appreciably opened up so as to provide a marked expansion in the direction perpendicular to the layers, that is, in the “c” direction and thus form an expanded or intumesced graphite structure in which the laminar character of the carbon layers is substantially retained.
Natural graphite flake which has been expanded and more particularly expanded so as to have a final thickness or “c” direction dimension which is at least about 80 or more times the original “c” direction dimension can be formed without the use of a binder into cohesive or integrated sheets, e.g., webs, papers, strips, tapes, or the like. The formation of graphite particles which have been expanded to have a final thickness or “c” dimension which is at least 80 times the original “c” direction dimension into integrated sheets by compression, without the use of any binding material is possible. It is believed that this is due to the excellent mechanical interlocking, or cohesion that is achieved between the voluminously expanded graphite particles.
In addition to flexibility, the sheet material, as noted above, has also been found to possess a high degree of anisotropy with respect to thermal and electrical conductivity and fluid diffusion, comparable to the natural graphite starting material due to orientation of the expanded graphite particles substantially parallel to the opposed faces of the sheet resulting from very high compression, such as roll pressing. Sheet material thus produced has excellent flexibility, good strength and a very high degree of orientation.
Briefly, the process of producing flexible, binderless anisotropic graphite sheet material comprises compressing or compacting under a predetermined load and preferably in the absence of a binder, expanded graphite particles which have a “c” direction dimension which is at least 80 times that of the original particles so as to form a substantially flat, flexible, integrated graphite sheet. The expanded graphite particles are generally worm-like or vermiform in appearance, and once compressed, will maintain the compression set and alignment with the opposed major surfaces of the sheet. The density and thickness of the sheet material can be varied by controlling the degree of compression. The density of the sheet material can be within the range of from about 5 pounds per cubic foot to about 125 pounds per cubic foot. The flexible graphite sheet material exhibits an appreciable degree of anisotropy due to the alignment of graphite particles parallel to the major opposed, parallel surfaces of the sheet, with the degree of anisotropy increasing upon roll pressing of the sheet material to increased density. In roll pressed anisotropic sheet material, the thickness, i.e. the direction perpendicular to the opposed, parallel sheet surfaces comprises the “c” direction and the directions ranging along the length and width, i.e., along or parallel to the opposed, major surfaces comprises the “a” directions and the thermal, electrical and fluid diffusion properties of the sheet are very different, by orders of magnitude, for the “c” and “a” directions.
This very considerable difference in properties, i.e., anisotropy, which is directionally dependent, can be disadvantageous in some applications. For example, in gasket applications where flexible graphite sheet is used as the gasket material and in use is held tightly between metal surfaces, the diffusion of fluid like gases or liquids occurs more readily parallel to and between the major surfaces of the flexible graphite sheet. It would, in most instances, provide for greater gasket performance, if the resistance to fluid flow parallel to the major surfaces of the graphite sheet (“a” direction) were increased, even at the expense of reduced resistance to fluid diffusion flow transverse to the major faces of the graphite sheet (“c” direction). With respect to electrical properties, the resistivity of anisotropic flexible graphite sheet is high in the direction transverse to the major surfaces (“c” direction) of the flexible graphite sheet, and very substantially less in the direction parallel to and between the major faces of the flexible graphite sheet (“a” direction). In applications such as seals or other components (such as fluid flow field plates or gas diffusion layers) of fuel cells, it would be of advantage if the electrical resistance transverse to the major surfaces of the flexible graphite sheet (“c” direction) were decreased, even at the expense of an increase in electrical resistivity in the direction parallel to the major faces of the flexible graphite sheet (“a” direction).
With respect to thermal properties, the thermal conductivity of a flexible graphite sheet in a direction parallel to the upper and lower surfaces of the flexible graphite sheet is relatively high, while it is relatively very low in the “c” direction transverse to the upper and lower surfaces. At times, and in certain applications, such as thermal interfaces, it may be desirable to increase the thermal conductivity of the sheet in the “c” direction.
In some applications, it is important to incorporate additives in the flexible graphite sheet in order to achieve corrosion resistance and to impregnate the flexible graphite sheet with resins and/or other material to increase the strength and water resistance of the flexible graphite sheet. Also, it is important at times to provide such additives in the course of processing the natural graphite into flexible graphite.
These foregoing situations are accommodated by the present invention.
In accordance with the present invention, a flexible graphite article in the form of a sheet having opposed, relatively planar, major surfaces is provided. The article is formed of particles of expanded (or exfoliated) graphite, an optically detectable portion of which, at magnifications of 100× or less, are substantially unaligned with the opposed planar major surfaces of the flexible graphite article. Preferably, at least a portion of the unaligned particles are transverse to the opposed major surfaces of the article. The flexible graphite article is characterized by having decreased electrical resistivity and increased thermal conductivity in a direction transverse to the opposed planar major surfaces of the flexible graphite sheet and increased resistance to fluid flow in a direction parallel to the opposed planar major faces of the flexible graphite sheet. The flexible graphite sheet, with or without additives and/or impregnants, can be mechanically altered, such as by embossing, die molding and cutting to form components for electrochemical fuel cells, gaskets and heat conducting and heat resistant articles.
The present invention also includes an apparatus, system and method for producing flexible graphite sheet articles, such as those having decreased electrical resistivity and increased thermal conductivity in a direction transverse to the opposed planar major surfaces of the flexible graphite sheet and increased resistance to fluid flow in a direction parallel to the opposed planar major faces of the flexible graphite sheet.
The inventive method comprises reacting raw graphite particles with a liquid intercalant solution to form intercalated graphite particles; exposing the intercalated graphite particles to a temperature of at least about 700° C. to expand the intercalated graphite particles to form a stream of exfoliated graphite particles; continuously compressing the stream of exfoliated graphite particles into a continuous coherent self-supporting mat of flexible graphite; continuously contacting the flexible graphite mat with liquid resin and impregnating the mat with liquid resin; and continuously calendering the flexible graphite mat to increase the density thereof to form a continuous flexible graphite sheet having a density of from about 5 to about 125 lbs/ft3 and a thickness of from about 1.0 to 0.003 inches.
The method also advantageously includes mechanically deforming a surface of the continuous flexible graphite sheet to provide a series of repeating patterns on a surface of the flexible graphite sheet or the removal of material from the flexible graphite sheet in a series of repeating patterns and vaporizing at least some of the solvent from the resin prior to mechanically deforming a surface of the continuous flexible graphite sheet.
As noted, the present invention also includes an apparatus for the continuous production of resin-impregnated flexible graphite sheet, comprising a reactor vessel for containing as reactants graphite particles in mixture with a liquid intercalant solution to form intercalated graphite particles; an expansion chamber in operative connection with the reactor vessel, the interior of the expansion chamber being at a temperature of at least about 700° C. (and preferably enclosing an open flame), such that passing intercalated graphite particles from the reactor vessel to the expansion chamber causes expansion of the intercalated graphite particles to form exfoliated graphite particles; a compression station positioned to receive exfoliated graphite particles for compressing such particles into a coherent self-supporting mat of flexible graphite; an impregnation chamber for contacting the flexible graphite mat with liquid resin and impregnating the mat with the liquid resin; a calender mill disposed to receive the flexible graphite mat for increasing the density of the mat to form a continuous flexible graphite sheet preferably having a density of from about 5 to about 125 lbs/ft3 and a thickness of no more than about 1.0 inches, more preferably about 1.0 to about 0.003 inches.
The inventive apparatus also preferably includes a device for mechanically deforming a surface of the continuous flexible graphite sheet to provide a series of repeating patterns on a surface of the flexible graphite sheet or the removal of material from the flexible graphite sheet in a series of repeating patterns. It further advantageously has an oven for receiving the mat from the device for mechanically deforming a surface of the continuous flexible graphite sheet, to cure the resin with which the continuous flexible graphite sheet is impregnated.
In a particular embodiment of the invention, a system for the continuous production of surface patterned, resin-impregnated flexible graphite sheet is presented. The system includes:
FIGS. 2, 2(A) show planar bodies of flexible graphite having portions of un-aligned graphite particles;
FIGS. 5(A) and 5(B) show different types of the flexible graphite articles noted above; and
FIGS. 5(C) and 5(D) show conventional mechanisms for producing different types of flexible graphite articles noted above.
Graphite is a crystalline form of carbon comprising atoms covalently bonded in flat layered planes with weaker bonds between the planes. By treating particles of graphite, such as natural graphite flake, with an intercalant of, e.g., a solution of sulfuric and nitric acid, the crystal structure of the graphite reacts to form a compound of graphite and the intercalant. The treated particles of graphite are often referred to as “particles of intercalated graphite.” Upon exposure to high temperature, the particles of intercalated graphite expand in dimension as much as about 80 or more times its original volume in an accordion-like fashion in the “c” direction, i.e., in the direction perpendicular to the crystalline planes of the graphite. The exfoliated graphite particles are vermiform in appearance, and are therefore commonly referred to as worms. The worms may be compressed together into flexible sheets that, unlike the original graphite flakes, can be formed and cut into various shapes.
A common method for manufacturing graphite sheet or foil is described by Shane et al. in U.S. Pat. No. 3,404,061, the disclosure of which is incorporated herein by reference. In the typical practice of the Shane et al. method, natural graphite flakes are intercalated by dispersing the flakes in a solution containing an oxidizing agent of, for instance, a mixture of nitric and sulfuric acid. The intercalation solution contains oxidizing and other intercalating agents known in the art. Examples include those containing oxidizing agents and oxidizing mixtures, such as solutions containing nitric acid, potassium chlorate, chromic acid, potassium permanganate, potassium chromate, potassium dichromate, perchloric acid, and the like, or mixtures, such as for example, concentrated nitric acid and chlorate, chromic acid and phosphoric acid, sulfuric acid and nitric acid, or mixtures of a strong organic acid, e.g. trifluoroacetic acid, and a strong oxidizing agent soluble in the organic acid.
In a preferred embodiment, the intercalating agent is a solution of a mixture of sulfuric acid, or sulfuric acid and phosphoric acid, and an oxidizing agent like nitric acid, perchloric acid, chromic acid, potassium permanganate, hydrogen peroxide, iodic or periodic acids, or the like. Although less preferred, the intercalation solutions may contain metal halides such as ferric chloride, and ferric chloride mixed with sulfuric acid, or a halide, such as bromine as a solution of bromine and sulfuric acid or bromine in an organic solvent.
After the flakes are intercalated, any excess solution is drained from the flakes and the flakes are water-washed. The quantity of intercalation solution retained on the flakes after draining may range from 20 to 150 parts of solution by weight per 100 parts by weight of graphite flakes (pph) and more typically about 50 to 120 pph. Alternatively, the quantity of the intercalation solution may be limited to between 10 to 50 parts of solution per hundred parts of graphite by weight (pph) which permits the washing step to be eliminated as taught and described in U.S. Pat. No. 4,895,713, the disclosure of which is also herein incorporated by reference.
Referring now to
The dispersed expanded particles 5, with optional additive 4, are collected and confined in the large open-topped vessel as a layer 8 of pre-determined depth “d” and are to a large extent omnidirectionally oriented, with some horizontally aligned, as shown at 50 in
The use of continuous converging opposing belts, as shown at 457, 458 in
The article of
The articles of FIGS. 2, 2(A) and the material shown in the photograph (100×) of
With reference to
The graphite flakes in reactor vessel 404 are subjected to interlayer attack by the acid mixture intercalant, as described in U.S. Pat. No. 3,404,061 to Shane et al. The resulting intercalated graphite particles are soggy and acid coated and are conducted (such as via conduit 412) to a wash tank 414 where the particles are washed, advantageously with water which enters and exits wash tank 414 at 416, 418. The washed intercalated graphite flakes are then passed to drying chamber 422 such as through conduit 420. Additives such as buffers, antioxidants, pollution reducing chemicals can be added from vessel 419 to the flow of intercalated graphite flake for the purpose of modifying the surface chemistry of the exfoliate during expansion and use and modifying the gaseous emissions which cause the expansion.
The intercalated graphite flake is dried in dryer 422, preferably at temperatures of about 75 to about 150° C., generally avoiding any intumescence or expansion of the intercalated graphite flakes. After drying, the intercalated graphite flakes are fed as a stream into flame 300, by, for instance, being continually fed to collecting vessel 424 by way of conduit 426 and then fed as a stream into flame 300 in expansion vessel 428 as indicated at 2. Additives such as ceramic fiber particles formed of macerated quartz glass fibers, carbon and graphite fibers, zirconia, boron nitride, silicon carbide and magnesia fibers, naturally occurring mineral fibers such as calcium metasilicate fibers, calcium aluminum silicate fibers, aluminum oxide fibers and the like can be added from vessel 429 to the stream of intercalated graphite particles propelled by entrainment in a non-reactive gas introduced at 427.
The intercalated graphite particles 2, upon passage through flame 300 in expansion chamber 301, expand more than 80 times in the “c” direction and assume a “worm-like” expanded form; the additives introduced from 429 and blended with the stream of intercalated graphite particles are essentially unaffected by passage through the flame 300. The expanded graphite particles may pass through a gravity separator 430, in which heavy ash natural mineral particles are separated from the expanded graphite particles, and then into a wide topped hopper 432. Separator 430 can be by-passed when not needed.
The expanded, i.e., exfoliated graphite particles fall freely in hopper 432 together with any additives, and are randomly dispersed and passed into compression station 436, such as through trough 434. Compression station 436 comprises opposed, converging, moving porous belts 457, 458 spaced apart to receive the exfoliated, expanded graphite particles 50, 500, 5000. Due to the decreasing space between opposed moving belts 457, 458, the exfoliated expanded graphite particles are compressed into a mat of flexible graphite, indicated at 448 having thickness of, e.g., from about 1.0 to 0.003, especially from about 1.0 to 0.1 inches, and a density of from about 5 to 125 lbs./ft3. Gas scrubber 449 may be used to remove and clean gases emanating from the expansion chamber 301 and hopper 432.
The mat 448 is passed through vessel 450 and is impregnated with liquid resin from spray nozzles 438, the resin advantageously being “pulled through the mat” by means of vacuum chamber 439 and the resin is thereafter preferably dried in dryer 460 reducing the tack of the resin and the resin impregnated mat 443 is thereafter densified into roll pressed flexible graphite sheet 447 in calender mill 470. Gases and fumes from vessel 450 and dryer 460 are preferably collected and cleaned in scrubber 465.
The calendered flexible graphite sheet 447 is passed through surface shaping unit 480 and is mechanically deformed at its surface by embossing die stamping or the like, and thereafter heated in oven 490 to cure the resin, to continuously provide a flexible graphite sheet 444 of repeated surface altered patterns such as the grooved patterns 600 shown in
Depending on the nature of the resin system employed, and especially the solvent type and level employed, a vaporization drying step may be included prior to the surface shaping (such as embossing) step. In this drying step, the resin impregnated flexible graphite sheet is exposed to heat to vaporize and thereby remove some or all of the solvent, without effecting cure of the resin system. In this way, blistering during the curing step, which can be caused by vaopization of solvent trapped within the sheet by the densification of the sheet during surface shaping, is avoided. The degree and time of heating will vary with the nature and amount of solvent, and is preferably at a temperature of at least about 90° C. and more preferably from about 90° C. to about 125° C. for about 3 to about 20 minutes for this purpose.
The above description is intended to enable the person skilled in the art to practice the invention. It is not intended to detail all of the possible variations and modifications which will become apparent to the skilled worker upon reading the description. It is intended, however, that all such modifications and variations be included within the scope of the invention which is defined by the following claims. The claims are intended to cover the indicated elements and steps in any arrangement or sequence which is effective to meet the objectives intended for the invention, unless the context specifically indicates the contrary.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09548118 | Apr 2000 | US |
| Child | 09906281 | Jul 2001 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09906281 | Jul 2001 | US |
| Child | 11001698 | Dec 2004 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09287899 | Apr 1999 | US |
| Child | 09548118 | Apr 2000 | US |