Flexible, high purity expanded graphite sheet, method of producing same, and carbon crucible lining using said sheet

Abstract

The invention provides a flexible, highly pure expanded graphite sheet characterized by having an impurity content of 10 ppm or less and such a degree of flexibility that a sample thereof, 10×100 mm in size can withstand at least 10 times of bending in flexibility test comprising repeatedly bending the sample, with a 50-g weight suspended from one end thereof, by means of bending bodies with a diameter of 6 mm.

Description

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a flexible, high-purity expanded graphite sheet, and to a method of producing the same.

[0003] 2. Description of the Prior Art

[0004] Expanded graphite sheets are generally produced by treating natural graphite, pyrolytic graphite, kish graphite or the like with a mixed solution containing sac acid and nitric acid, for instance, then washing the same with water, drying the same, treating the same for expansion in an expansion oven at about 1,000° C., and forming the same into sheets using a rolling machine, for instance. Expanded graphite sheets are excellent in heat resistance and in gas and liquid impermeability and therefore are used as packing materials, valve sheets, gaskets, and fuel cell separators, among others.

[0005] Japanese Patent No. 2,620,606 discloses that highly pure expanded graphite sheets having an impurity content of not more than 15 ppm can be obtained by treating such expanded graphite sheets for increased purity in a halogen gas atmosphere at 2,000° C. or above. Such sheets are used in the process of semiconductor production.

[0006] Hereinafter, a detailed description is given of a high-purity expanded graphite sheet for use in semiconductor production, which is taken as an example. Such a high purity expanded graphite sheet is also used in the Czochralski (hereinafter referred to as “CZ” for short) process, which is a representative single crystal pig technique. A sectional view of the main parts of a CZ apparatus is shown in FIG. 1. The CZ apparatus comprises such parts as a carbon crucible 5 supporting a quarts crucible 1, a heater 2, an upper ring 6, and an inner shield 7, among others. In the CZ apparatus, polycrystalline silicon placed m the quartz crucible 1 is heated to a high temperature to give a silicon melt 3, and the tip of a seed crystal held by a seed chuck is brought into contact with the raw material melt 3 and then pulled up while maintaining the contact to thereby pull up a silicon single crystal 4.

[0007] As shown in FIG. 1, the carbon crucible 5 made of graphite or a carbon fiber-reinforced carbon composite material (such crucible is hereinafter referred to as ‘carbon crucible’) is in direct contact with the quartz crucible 1 and, therefore, the surface of the carbon crucible 5 is gradually converted to silicon carbide (hereinafter referred to as “SiC”) as a result of the reaction between the quartz crucible 1 and carbon crucible 5 and/or the reaction between vaporized silicon and the graphite crucible. The difference in coefficient of thermal expansion between carbon and SiC is conducive to cracking of the carbon crucible, for instance. Furthermore, the quartz crucible 1 becomes firmly sticking to the carbon crucible 5, making it difficult to take out the quart crucible 1.

[0008] Japanese Patent No. 2,528,285 discloses, as a means for solving such problems, the use of a high-purity expanded graphite sheet as a liner intervening between the quartz crucible 1 and carbon crucible 5.

[0009] When an expanded graphite sheet is treated for improving the purity thereof, the flexibility of the expanded graphite sheet is generally impaired, so that it can no loner be used as a member which is required to have flexibility; Therefore, Japanese Patent No. 2,620,606 discloses a method of restoring flexibility which comprises compression molding. However, the method has other problems; the purity of the high-purity expanded graphite sheet is decreased upon compression molding and, when a complicated shape is given to the high-purity expanded graphite sheet insufficient in flexibility restoration by working with a cutter, for instance, the peripheral parts of the sheet are subject to cracking and/or chipping.

[0010] When the whole inside surface of the carbon crucible is covered with an expanded graphite sheet, the efficiency of heating of the quartz crucible 1 decreases. Therefore, in recent years, various complicated liner shapes have been proposed so that the quartz crucible heating efficiency may be improved. Basically, each single crystal production operation consumes one intervening liner and, therefore, it is important to provide a method of producing high-purity expanded graphite sheets which is excellent in mass productivity.

[0011] Accordingly, it is an object of the present invention to provide a high-purity expanded graphite sheet having flexibility and a method of producing the same. Another object of the invention is to provide a method of manufacturing expanded graphite sheets which is suited for mass production as well.

SUMMARY OF THE INVENTION

[0012] The present inventors made intensive investigations in an attempt to accomplish the above objects and, as a result, found that when an expanded graphite sheet whose bulk density is within a certain specific range is treated for attaining high purity, a high-purity expanded graphite sheet can be obtained without deterioration in flexibility even after the treatment for attaining high purity. This and other findings have now led to completion of the present invention. Thus, in a first, aspect (claim 1), the invention provides a flexible, high-purity expanded graphite sheet characterized in that it has an impurity content not exceeding 10 ppm and has such a degree of flexibility that a sample thereof can withstand at least 10 times of bending on a testing apparatus such as shown in FIG. 4. In a second aspect (claim 2), the invention provides a flexible, high-purity expanded graphite sheet which has the above characteristics and is further characterized by its bulk density being 0.5 to 1.3 g/cm. In a third aspect (claim 3), the invention provides a flexible, high-purity expanded graphite sheet as defined in claim 1 or 2 which is further characterized by its thickness being 0.2 to 1.0 mm.

[0013] For obtaining the flexible, high-purity expanded graphite sheet according to claim 1, it is necessary to use scaly graphite, kish graphite, pyrolytic graphite or the like as a filler, subject this to oxidation treatment by immersing the same in a mixed acid supplemented with concentrated sulfuric acid, concentrated nitric acid, etc., wash the immersed filler with water and, after drying, treat the same for expansion by heating to give expanded graphite, and adjust the bulk density thereof to about 0.7 to 1.3 g/cm3 by compression molding using a press or rolling machine. Expanded graphite sheets having a bulk density lower than 0.7 g/cm3 cannot acquire, even after purification treatment, such a degree of flexibility as to withstand at least 10 times of bending, hence are unfavorable. Expanded graphite sheets having a bulk density exceeding 1.3 g/cm3 are also undesirable, since the impurity content therein cannot be reduced to 10 ppm or below even by purification treatment. In a preferred embodiment of the invention, expanded graphite sheets with a bulk deity adjusted to 0.8 to 1.3 g/cm3, more preferably to 0.9 to 1.3 g/cm3, are subjected to treatment for attaining high purity. The method of purification treatment itself may be any of those known in the art. For example, flexible, high-purity expanded graphite sheets having an impurity content of not more than 10 ppm and a degree of flexibility as to withstand at least 10 times of bending can be obtained by heating expanded graphite sheets at 2,000° C. or above in a halogen gas atmosphere to thereby convert metals in the sheets to metal halide compounds showing a high vapor pressure and allow them to vaporize. The bulk density and sheet thickness of expanded graphite sheets after purification treatment show little changes and remain almost equal to those before treatment. A flexibility measuring apparatus is schematically shown in FIG. 3. A 50-g weight 22 is attached to one end of a 10 mm×100 mm sample 21 of a high-purity expanded graphite sheet and subjected to repeated bending by means of bending bodies 24 with a diameter of 6 mm. The number of times of bending until breakage is counted and recorded as the flexibility in the longitudinal direction.

[0014] In a fourth aspect (claim 4), the invention provides a method of producing flexible, high-purity expanded graphite sheets which comprises forming an expanded graphite sheet having a bulk density of 0.7 to 1.3 g/cm3 into a desired shape and then subjecting the shaped sheet to purification treatment. Expanded graphite sheets hang a bulk density less than 0.7 g/cm3 are undesirable since any purification treatment cannot improve their flexibility to a level of at least 10 times, as mentioned above. Expanded graphite sheets having a bulk density exceeding 1.3 g/cm3 are also unfavorable since their impurity content cannot be reduced to 10 ppm or less by purification treatment. Preferably, the expanded graphite sheet to be treated for purification has a thickness of 0-2 to 1.0 mm. When the expanded graphite sheet before purification treatment is less than 0.2 mm in thickness, the sheet after purification treatment tends to show marked decreases in flexibility and strength, hence are susceptible to cracking, for instance. When the expanded graphite sheet is thicker than 1.0 mm, the impurity content cannot be reduced to a satisfactory extent by purification treatment. More preferably, the expanded graphite sheet to be subjected to purification treatment has a thickness of 0.3 to 0.9 mm. Most preferably, 0.5 to 0.8-mm-thick expanded graphite sheets are subjected to purification treatment. As the “desired shape” so referred to herein, there may be mentioned, for example, the shape shown in FIG. 2 or FIG. 3 and, further, figures of line symmetry, such as ellipses, stars and the Imperial crest of chrysanthemum, and asymmetric figures.

[0015] In a fifth aspect (claim 5), the invention provides a modification of the method specified above which modification comprises forming a plurality of expanded graphite sheets each into one and the same desired shape simultaneously in a laminate form, followed by purification treatment. This modification is preferred since the mass productivity in manufacturing expanded graphite sheets having one and the same desired, complicated shape can be improved by laying a plurality of expanded graphite sheets one upon another and working them simultaneously in one operation according to the method mentioned above. Preferably, a plurality of expanded graphite sheets each having a thickness of 0.2 to 1.0 mm are laid one upon another. When each expanded graphite sheet is less than 0.2 mm in thickness, the expanded graphite sheet cannot acquire flexibility or strength but becomes susceptible to cracking, for instance. When each sheet is thicker than 10 mm, the impurity content cannot be reduced to a satisfactory extent by purification treatment; this is unfavorable. It is desirable that the bulk density of expanded graphite sheets prior to purification treatment be 0.7 to 1.3 g/cm3.

[0016] In a sixth aspect (claim 6), the invention provides a method of producing such expanded graphite sheets as mentioned above in which the shaping of expanded graphite sheets is carried out by at least one method selected from among such methods as slitting, punching using a Thomson die, water jet working, and laser working. From the mass productivity viewpoint, however, punching with a Thomson die and water jet working are preferred since they can reduce the working tine, are less likely to decrease the purity of expanded graphite sheets and, further, are excellent in mass productivity. It is to be added that when expanded graphite sheets are shaped by punching using a Thomson die, the purification treatment should preferably be carried out after removing working dust from the worked surface (cut surface) by ultrasonic cleaning in a state immersed in water, alcohol or the like and the subsequent drying for evaporation of the moisture

[0017] In a seventh aspect (claim 7), the invention provides the use of the flexible, high-purity expanded graphite sheet as defined in any one of claims 1 to 3 as a carbon crucible liner. When such a high-purity expanded graphite sheet having flexibility and a low impurity content is used as a carbon crucible liner, the stability of the quartz crucible is good and the intrusion of silicon monoxide gas can be prevented, so that the carbon crucible can be inhibited from being converted to silicon carbide and the life of the expensive carbon crucible can be prolonged

BRIEF DESCRIPTION OF TEE DRAWINGS

[0018] FIG. 1 is a schematic sectional view of a single crystal puller.

[0019] FIG. 2 is an illustration of shaping of a high-purity expanded graphite sheet suited for use as an intervening liner in a single crystal pulling apparatus.

[0020] FIG. 3 is an illustration of shaping of another high-purity expanded graphite sheet suited for use as a liner in a single crystal puller.

[0021] FIG. 4 is a schematic representation of a flexibility measuring apparatus.

[0022] In FIGS. 1 and 4, the numerical symbols respectively denote the following: 1—quartz crucible, 2—heater, 3—silicon melt, 4—silicon single crystal, 5—carbon crucible, 6—upper ring, 7—inner shield, 8—lower zing, 9—bottom heater, 10—heat insulator, 11—spill tray, 21—sample (of high-purity expanded graphite sheet), 22—weight, 23—directions of bending, 24—benders

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0023] The following examples illustrate the present invention more specifically. These examples are, however, by no means limitative of the scope of the present invention.

EXAMPLE 1

[0024] An expanded graphite sheet made by Toyo Tanso Co. Ltd. grade name: PF-50, size: 1,000×1,000×0.5 (mm), bulk density: 1.3 g/cm3, ash content: 0.2% by mass) was obtained. This sheet was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 10 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 2

[0025] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Example 1. This laminate was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 50 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 3

[0026] An expanded graphite sheet made by Toyo Tanso Co. Ltd. Grade name: PF-40, thickness: 0.4 man, bulk dety: 1.0 g/cm3, ash content: 0.2% by mass) was obtained This sheet was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 10 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed

EXAMPLE 4

[0027] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Example 3. Tis laminate was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 50 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 5

[0028] An expanded graphite sheet made by Toyo Tanso Co. Ltd. (grade name: PF-40, thickness: 0.4 mm, bulk density; 0.7 g/cm3, ash content: 0.2% by mass) was obtained This sheet was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 10 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed

EXAMPLE 6

[0029] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Example 5. This laminate was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 50 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 7

[0030] An expanded graphite sheet made of the same material and having the same size as that used in Example 1 was obtained. This sheet was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 one at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 8

[0031] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Example 1. This laminate was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed

EXAMPLE 9

[0032] An expanded graphite sheet made by Toyo Tanso Co. Ltd. (grade name: PF-40, thickness: 0.4 nm, bulk density: 1.0 g/cm3, ash content: 0.2% by mass) was obtained. This sheet was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 10

[0033] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Example 3. This laminate was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was heated to and maintained at 2,000° C. for 10 hours while gaseous chorine was fed.

EXAMPLE 11

[0034] An expanded graphite sheet made by Toyo Tanso Co. Ltd. (grade name: PF-40, thickness: 0.4 mm, bulk density: 0.7 g/cm3, ash content: 0.2% by mass) was obtained. This sheet was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0-1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 12

[0035] Alaminate was prepared by laying, one upon another, 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Example 5. Tis laminate was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 13

[0036] An expanded graphite sheet made by Toyo Tanso Co. Ltd. (grade name: PF-20, size: 1,000×1,000×0.2 (mm), bulk deity: 1.3 g/cm3, ash content: 0.2% by mass) was obtained. This sheet was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 10 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 14

[0037] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Example 13. This laminate was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 50 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 15

[0038] An expanded graphite sheet made by Toyo Tanso Co. Ltd. (grade name: PF-20, thickness: 0.2 mm, bulk density: 1.0 g/cm3, ash content: 0.2% by mass) was obtained This sheet was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 10 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 16

[0039] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Example 15. This laminate was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 50 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed

EXAMPLE 17

[0040] An expanded graphite sheet made by Toyo Tanso Co. Ltd. (grade name: PF-20, thickness: 0.2 mm, bulk density: 0.7 g/cm3, ash content 0.2% by mass) was obtained. This sheet was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 10 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 18

[0041] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Example 17. This laminate was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 50 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 19

[0042] An expanded graphite sheet made by Toyo Tanso Co. Ltd. (grade name: PF-100, size: 1,000×1,000×1.0 (mm), bulk density: 1.3 g/cm3, ash content: 0.2% by mass) was obtained. This sheet was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed

EXAMPLE 20

[0043] A laminate was prepared by laying, one upon another 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Example 19. This laminate was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was heated to and maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 21

[0044] An expanded graphite sheet made by Toyo Tanso Co. Ltd. (grade name: PF-100, thickness: 1.0 mm, bulk density: 1.0 g/cm3 ash content: 0.2% by mass) was obtained. This sheet was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

Example 22

[0045] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Example 21. This laminate was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was heated to and maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 23

[0046] An expanded graphite sheet made by Toyo Tanso Co. Ltd. (grade name: PF-100, thickness: 1.0 mm, bulk density: 0.7 g/cm8, ash content: 0.2% by mass) was obtained. This sheet was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 24

[0047] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Example 23. This laminate was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was heated to and maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

EXAMPLE 25

[0048] A laminate was prepared by laying, one upon another, 5 expanded graphite sheets made of the same material and having the same size as the sheet used in Example 1. This laminate was formed into the shape shown in FIG. 2 by subject to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The time required for the shaping was 5 minutes. The shaped article was subjected to 3 minutes of ultrasonic cleaning at 43 kHz to thereby remove cut dust derived from the expanded graphite laminate. Then, the shaped article was dried at 100° C. for 30 minutes to evaporate the moisture and then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

COMPARATIVE EXAMPLE 1

[0049] An expanded graphite sheet made by Toyo Tanso Co. Ltd. grade name; PF-50, size: 1,000×1,000×0.5 (mm), bulk density: 1.5 g/cm3, ash content: 0.2% by mass) was obtained. This sheet was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 10 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed

COMPARATIVE EXAMPLE 2

[0050] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Comparative Example 1. This laminate was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 50 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

COMPARATIVE EXAMPLE 3

[0051] An expanded graphite sheet made by Toyo Tanso Co. Ltd. (grade name: PF-10, size: 1,000×1,000×0.1 (mm), bulk density: 1.3 g/cm3, ash content: 0.2% by mass) was obtained. This sheet was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 10 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

COMPARATIVE EXAMPLE 4

[0052] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Comparative Example 3. Tis laminate was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 50 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

COMPARATIVE EXAMPLE 5

[0053] An expanded graphite sheet made by Toyo Tanso Co. Ltd. (grade name: PF-120, size: 1.000×1,000×1.2 (min), bulk density: 1.3 g/cm3, ash content: 0.2% by mass) was obtained. This sheet was formed into the shape shown in FIG. 2 by punching using a hydraulic press and a Thomson die at a pressure of 10 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

COMPARATIVE EXAMPLE 6

[0054] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made of the same material and having the same size as the sheet used in Comparative Example 5. His laminate was formed into the shape shown in FIG. 2 by punching us-mg a hydraulic press and a Thomson die at a pressure of 50 MPa. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

COMPARATIVE EXAMPLE 7

[0055] A laminate was prepared by laying, one upon another, 5 expanded graphite sheets made of the same material and having the same size as the sheet used in Example 1. This laminate was formed into the shape shown in FIG. 2 by manual working using a cutter. The time required for the shaping was 1 hour. The shaped article was subjected to 3 minutes of ultrasonic cleaning at 43 kHz to thereby remove cut dust derived from the expanded graphite laminate. Then, the shaped article was dried at 100° C. for 30 minutes to evaporate the moisture and then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

COMPARATIVE EXAMPLE 8

[0056] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made by Toyo Tanso Co. Ltd. (grade name: PF-40, size: 1,000×1,000×0.4 (mm), bulk density 0.6 glens, ash content: 0.2% by mass). This laminate was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10-hours while gaseous chlorine was fed.

COMPARATIVE EXAMPLE 9

[0057] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made by Toyo Tanso Co. Ltd. grade name: PF-40, size: 1,000×1,000×0.4 (mm), bulk density: 0.3 g/cm3, ash content: 0.2% by mass). This laminate was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

COMPARATIVE EXAMPLE 10

[0058] A laminate was prepared by laying, one upon another, 10 expanded graphite sheets made by Toyo Tanso Co. Ltd. (grade name: PF-40, size: 1,000×1,000×0.4 (mm), bull density: 0-2 g/cm3, ash content: 0.2% by mass). This laminate was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed

COMPARATIVE EXAMPLE 11

[0059] An expanded graphite sheet made by Toyo Tanso Co. Ltd. (grade name: PF-40, size 1,000×1,000×0.4 (mm), bulk density: 0.6 g/cm3, ash content: 0.2% by mass) was obtained. This sheet was formed into the shape shown in FIG. 2 by subjecting to water jet working using a nozzle having an orifice diameter of 0.1 mm at a water pressure of 3,000 kg/cm2. The shaped article was then treated for purification; thus, it was maintained at 2,000° C. for 10 hours while gaseous chlorine was fed.

[0060] For each of Examples 1 to 25 and Comparative Examples 1 to 11, the bulk density of the expanded graphite sheet, the thickness per sheet, the number of sheets in the laminate, the method of shaping, the flexibility in the longitudinal direction, and the purity after purification treatment are summarized in Table 1. The expanded graphite sheets after purification treatment showed little changes in bulk density or in sheet thickness and thus were comparable in these respects to the sheets before purification treatment.

[0061] The impurity content of each expanded graphite sheet after purification treatment was determined by weighing at least 15 g of the high-purity expanded graphite sheet in a porcelain crucible, placing the crucible in an electric furnace, beating it at 850° C. for 48 hours, and calculating the impurity content from the mass before heating and the mass after heating.

	TABLE 1
			Number
	Bulk	Sheet	of sheets			Impurity
	density	thickness	in	Shaping	Flexibility	content
	(g/cm8)	(mm/sheet)	laminate	method	(times)	(ppm)
Example 1	1.3	0.5	1	Thomson die	12	4
Example 2	1.3	0.5	10	Thomson die	12	4
Example 3	1.0	0.4	1	Thomson die	10	3
Example 4	1.0	0.4	10	Thomson die	10	3
Example 5	0.7	0.4	1	Thomson die	10	2
Example 6	0.7	0.4	10	Thomson die	10	2
Example 7	1.3	0.5	1	Water jet	12	3
Example 8	1.3	0.5	10	Water jet	12	3
Example 9	1.0	0.4	1	Water jet	10	2
Example 10	1.0	0.4	10	Water jet	10	2
Example 11	0.7	0.4	1	Water jet	10	1
Example 12	0.7	0.4	10	Water jet	10	1
Example 13	1.8	0.2	1	Thomson die	20	3
Example 14	1.3	0.2	10	Thomson die	20	3
Example 15	1.0	0.2	1	Thomson die	18	2
Example 16	1.0	0.2	10	Thomson die	18	2
Example 17	0.7	0.2	1	Thomson die	10	1
Example 18	0.7	0.2	10	Thomson die	10	1
Example 19	1.3	1.0	1	Water jet	10	5
Example 20	1.3	1.0	10	Water jet	10	5
Example 21	1.0	1.0	1	Water jet	10	4
Example 22	1.0	1.0	10	Water jet	10	4
Example 23	0.7	1.0	1	Water jet	10	2
Example 24	0.7	1.0	10	Water jet	10	2
Example 25	1.3	0.5	5	Water jet	12	1
Compar. Ex. 1	1.5	0.5	1	Thomson die	30	50
Compar. Ex. 2	1.5	0.5	10	Thomson die	30	50
Compar. Ex. 3	1.3	0.1	1	Thomson die	1	1
Compar. Ex. 4	1.3	0.1	10	Thomson die	1	1
Compar. Ex. 5	1.3	1.2	1	Thomson die	5	30
Compar. Ex. 6	1.8	1.2	10	Thomson die	5	30
Compar. Ex. 7	1.3	0.5	5	Cutter	12	30
Compar. Ex. 8	0.6	0.4	10	Water jet	1	2
Compar. Ex. 9	0.3	0.4	10	Water jet	1	1
Compar. Ex. 10	0.2	0.4	10	Water jet	1	1
Compar. Ex. 11	0.6	0.4	1	Water jet	1	2

[0062] As is evident from Table 1, those expanded graphite sheets having a bulk density of 0.7 to 1.3 g/cm3 and a thickness of 0.2 to 1.0 mm per sheet showed only slight decreases in flexibility after purification treatment and could be prevented from decreasing in purity.

[0063] A silicon single crystal growth experiment was carried out using the high-purity expanded graphite sheet obtained in Example 25 and Comparative Example 3 each as an intervening liner in a CZ apparatus. When the liner produced in Example 25 was used, it was confirmed by the eye that the area of yellowed portions suggesting the formation of silicon carbide was smaller as compared with the case of the liner produced in Comparative Example 3. This resulted from cracking of the high-purity expanded graphite sheet of Comparative Example 3 due to lack of flexibility.

[0064] When a plurality of expanded graphite sheets having a bulk density of 0.7 to 1.3 g/cm3 and a thickness of 0.2 to 1.0 mm per sheet are formed into a laminate and the laminate is worked into a desired shape, no impairment in flexibility is found after treatment for attaining high purity. In addition, when the laminate is shaped by water jet working, the working time can be reduced to {fraction (1/10)} or shorter as compared with that in the prior art and the impurity content can also be reduced to {fraction (1/10)} or below. Therefore, the products are useful in the semiconductor-related industries as those carbon crucible liners for use in CZ apparatus, CVD ovens and the like which are required to have high purity and flexibility and, in the nuclear industry-related fields, as in-core or in-pile parts required to be flexible and highly pure.

Claims

1. A flexible, high-purity expanded graphite sheet which has an impurity content not exceeding 10 ppm and such a degree of flexibility that a sample thereof, 10×100 mm in size, can withstand at least 10 times of bending in a flexibility test comprising repeatedly bending the sample, with a 50-g weight suspended from one end thereof, by means of bending bodies with a diameter of 6 mm.

2. A flexible, high-purity expanded graphite sheet as defined in claim 1 which has a bulk density of 0.5 to 1.3 g/cm3.

3. A flexible, high-purity expanded graphite sheet as defined in claim 1 or 2 which has a thickness of 0.2 to 1.0 mm.

4. A method of producing flexible, high-purity expanded graphite sheets which comprises forming an expanded graphite sheet having a bulk density of 0.7 to 1.3 g/cm3 into a desired shape and then subjecting the shaped sheet to treatment for attaining high purity.

5. A method of producing flexible, high-purity expanded graphite sheets which comprises forming a plurality of expanded graphite sheets each having a bulk density of 0.7 to 1.3 g/cm3 into one and the same desired shape simultaneously in a laminate form, followed by treatment for attaining high purity.

6. A method of producing flexible, high-purity expanded graphite sheets as defined in claim 4 or 5, wherein the shaping of expanded graphite sheets is carried out by at least one method selected from among such methods as working on a slitting machine, punching using a Thomson die, water jet working, and laser working.

7. A carbon crucible liner comprising a flexible, high-pity expanded graphite sheet as defined any one of claims 1 to 3.