Patent Application
20210191322
This application claims priority to European Patent Application No. 19218863.9 filed Dec. 20, 2019, the entire contents of which are incorporated herein by reference.
The present invention relates to timepiece components, in particular for an oscillator mechanism or for the barrel of a horological movement.
The invention also relates to a horological movement including such a component.
Mechanical horological movements generally comprise a barrel, an escapement mechanism and a mechanical oscillator mechanism. The barrel comprises a spring to supply energy to the oscillator mechanism. The escapement mechanism includes, in particular, an anchor and an escapement wheel, while the oscillator mechanism generally comprises a spiral spring associated with an oscillating inertial mass called a balance.
Technical progress in composite materials allows some components from innovative and high-performance materials to be manufactured, which allow, at least partly, purely metallic materials not to be used. Today, an attempt is made to use, for example, carbon nanotubes to manufacture components. Such materials provide advantages in terms of lightness, strength, and simplicity of manufacture. Thus, document JP2008116205A describes a spiral spring comprising a matrix of graphite and amorphous carbon, reinforced by carbon nanotubes which are dispersed in the matrix and aligned in the longitudinal direction of the spiral, that is to say in the direction of the main elastic stresses.
In the publication by N. Hutchison and al (MEMS 2009), a composite material is formed, on the one hand, of a forest of vertically aligned carbon nanotubes (VACNT), and on the other hand, of a second filling material between the nanotubes, mainly carbon, secondarily silicon, or even silicon nitride. The filling material mainly determines the mechanical properties of the composite material.
Nevertheless, these materials are limited to the use of nanotubes, which are usually empty. However, it is not always easy to manufacture nanotubes from materials other than carbon.
A purpose of the invention is, consequently, to provide a timepiece component which avoids the aforementioned problems.
To this end, the invention relates to a flexible timepiece component, in particular for an oscillator mechanism or for a barrel of a horological movement, the component extending along a main plane (P) and including at least a part made of a composite material.
The component is remarkable in that the composite material comprises a matrix and a multitude of nanowires distributed in the matrix, the nanowires being juxtaposed, the matrix including a material for filling the interstices between the nanowires to join them to each other, each nanowire forming a solid one-piece tube.
Thus, thanks to such a composite material, solid one-piece nanowires are obtained, so that all kinds of materials can be used to manufacture these nanowires. In addition, it is possible to manufacture nanowires easily, in a simpler manner than nanotubes made of some materials. Consequently, it is possible to produce some elements of a horological movement, which must be able to flex, such as a spiral spring or a barrel spring.
According to an advantageous embodiment, the nanowires are disposed substantially parallel to an axis substantially perpendicular to the plane of the component.
According to an advantageous embodiment, the nanowires are made of an element to be selected from the following list: gold, palladium, silicon, poly-crystalline diamond, boron nitride, gallium nitride, silicon nitride, zinc oxide, gallium arsenide, tungsten sulphide, silver, copper, manganese arsenide, indium arsenide, nickel, platinum, germanium, cobalt-graphene, phosphorus-germanium, copper-silver, gold-silver alloys, phosphorus-indium, nitrogen-gallium, nitrogen-indium-gallium, nitrogen-arsenic-gallium, arsenic-gallium, phosphorus-indium-gallium, sulphur-cadmium, sulphur-cadmium-selenium, nitrogen-aluminium-gallium, caesium-lead, antimony telluride, bismuth telluride, silicon oxide, titanium oxide, tungsten oxide, indium oxide, aluminium oxide, magnesium oxide, tin oxide, zinc oxide, lithium niobate, manganese oxide compounds, inorganic compounds such as Li2Mo6Se6 or Mo6S9-xIx. It is also possible to produce nanowires from an amorphous or partially amorphous metal alloy.
According to an advantageous embodiment, the nanowires have a diameter comprised within a range from 1 to 50 nm, preferably within a range from 3 to 15 nm, or even from 5 to 10 nm.
According to an advantageous embodiment, the nanowires have a length comprised within a range from 100 to 500 microns, preferably within a range from 100 to 300 microns, or even from 150 to 200 microns.
According to an advantageous embodiment, the filling material is produced from an element to be selected from the following list: tungsten, organic materials such as parylene, hexagonal boron nitride, poly-crystalline ruby of the Al2O3 type, diamond, tungsten or molybdenum disulphides, graphite, lead, silicon carbide, nickel, indium phosphide, titanium oxide, poly-silicone, amorphous carbon, amorphous carbon of the DLC (Diamond-like-carbon) type, hafnium oxide, silicon oxide, poly-crystalline silicon, strontium titanate, zinc oxide, indium oxide, tungsten oxide, niobium oxide, cadmium oxide, magnesium fluoride, titanium nitride, silicon nitride, aluminium nitride, gallium nitride, hafnium nitride, calcium nitride, silver nitride, oxidised silicon nitride, platinum, palladium, molybdenum, tantalum, zinc sulphide, molybdenum sulphide, germanium, hydrofluorocarbon, compounds of the AlP, AlN, AlGaSb, AlGaAs, AlGaInP, AlGaN, AlGaP, GaSb, GaAsP, GaAs, GaN, GaP, InAlAs, InAlP, InSb, InGaSb, InGaN, GaInAlAs, GaInAlN, GaInAsN, GaInAsP, GaInAs, GaInP, InN, InP, InAs, InAsSb, ZnSe, HgCdTe, GeSbTe type.
According to an advantageous embodiment, the component is a spiral spring of an oscillator mechanism.
According to an advantageous embodiment, the component is a barrel spring.
According to an advantageous embodiment, the component is an anti-shock device.
The invention also relates to a horological movement comprising a flexible timepiece component according to the invention.
Other features and advantages of the present invention will become apparent upon reading several embodiments given only by way of non-limiting examples, with reference to the appended drawings wherein:
The description presents components for a horological movement. The component is a flexible component to be selected from a list comprising, for example, an oscillator mechanism spiral spring or a barrel spring.
The flexible component is preferably flat and extends along a main plane P. The component includes at least a part made of a composite material 1, shown in
The composite material 1 comprises a filling matrix 2 and a multitude of nanowires 3 distributed in said matrix 2. The matrix 2, for example, has a generally flat shape extending in a plane A.
The nanowires 3 form a structure of the composite material 1, wherein they are juxtaposed. They are regularly distributed so as to be homogeneously spaced from one another in the matrix 2. The term “nanowires” means one-piece tubes which are generally solid. Thus, the interior 16 of the nanowires 3 comprises the same material as the outer sheath.
The nanowires 3 are preferably disposed substantially parallel to one another. They are substantially perpendicular to the main plane P of the component. They are disposed substantially parallel to an axis A, perpendicular to the main plane P of the component. Substantially parallel means that the wires are oriented substantially in the same direction.
Advantageously, the composite material is produced in such a way that nanowires 3 are present throughout the mass of the matrix 2.
The nanowires 3 have, for example, a diameter D comprised within a range from 2 to 50 nm. Preferably, the nanowires 3 have a diameter comprised within a range from 3 to 15 nm, or even from 5 to 10 nm.
The nanowires 3 can have a length L comprised within a range from 100 to 500 microns. Preferably, the nanowires 3 have a length comprised within a range from 100 to 300 microns, or even from 150 to 200 microns.
The nanowires 3 are made of a material to be selected from the following list: gold, palladium, silicon, diamond, boron nitride, gallium nitride, silicon nitride, zinc oxide, gallium arsenide, tungsten sulphide, silver, copper, manganese arsenide, indium arsenide, nickel, platinum, germanium, cobalt-graphene, phosphorus-germanium, copper-silver, gold-silver alloys, phosphorus-indium, nitrogen-gallium, nitrogen-indium-gallium, nitrogen-arsenic-gallium, arsenic-gallium, phosphorus-indium-gallium, sulphur-cadmium, sulphur-cadmium-selenium, nitrogen-aluminium-gallium, caesium-lead, antimony telluride, bismuth telluride, silicon oxide, titanium oxide, tungsten oxide, indium oxide, aluminium oxide, magnesium oxide, tin oxide, zinc oxide, lithium niobate, manganese oxide compounds, inorganic compounds of the Li2Mo6Se6 or Mo6S9-xIx type. It is also possible to produce nanowires from an amorphous or partially amorphous metal alloy. This list is not exhaustive, other materials are also possible.
The matrix 2 includes a filling material 4 for filling the interstices 5 between the nanowires 3. The filling material 4 can advantageously include the nanowires 3, by being injected into the interstices 5 between the nanowires 3. This material 4 mainly determines the mechanical properties of the composite material 1, in particular to make the flexible matrix 2.
The filling material 4 composing the matrix 2 is made of an element from the following list: tungsten, organic materials such as parylene, hexagonal boron nitride, poly-crystalline ruby of the Al2O3 type, poly-crystalline diamond, tungsten or molybdenum disulphides, graphite, lead, silicon carbide, nickel, indium phosphide, titanium oxide, poly-silicone, amorphous carbon, amorphous carbon of the DLC (Diamond-like-carbon) type, hafnium oxide, silicon oxide, poly-crystalline silicon, strontium titanate, zinc oxide, indium oxide, tungsten oxide, niobium oxide, cadmium oxide, magnesium fluoride, titanium nitride, silicon nitride, aluminium nitride, gallium nitride, hafnium nitride, calcium nitride, silver nitride, oxidised silicon nitride, platinum, palladium, molybdenum, tantalum, zinc sulphide, molybdenum sulphide, germanium, hydrofluorocarbon, compounds of the AlP, AlN, AlGaSb, AlGaAs, AlGaInP, AlGaN, AlGaP, GaSb, GaAsP, GaAs, GaN, GaP, InAlAs, InAlP, InSb, InGaSb, InGaN, GaInAlAs, GaInAlN, GaInAsN, GaInAsP, GaInAs, GaInP, InN, InP, InAs, InAsSb, ZnSe, HgCdTe, GeSbTe type. The filling material 4 can advantageously also consist of carbon. This list is not exhaustive, other materials are also possible.
The filling material 4 is flexible, the material 4 having mechanical properties allowing an elastic deformation of the component. The flexibility is further achieved thanks to the geometry of the component, in particular by the thickness of the component. Flexible material means a material which can be used to form a flexible timepiece component, such as a spiral or a spring. The flexibility also depends on the geometry of the component and the stiffness to density ratio.
For some filling materials, for example a metal, the material has a high modulus of elasticity, greater than 100 Gpa, preferably greater than 200 GPa, and also has a high tensile strength, greater than 1 GPa, preferably greater than 2 GPa.
In other examples of filling materials, for example parylene, the material has a lower modulus of elasticity, comprised between 0.1 Mpa and 100 Gpa, and has a lower tensile strength, comprised between 200 MPa and 1 GPa.
The component is for example a spiral spring 6 of an oscillator mechanism 8 of a horological movement, or a spring 7 of a barrel 10 of a horological movement.
Examples of combinations of filler materials and nanowires with particularly advantageous properties will be mentioned.
A first example relates to copper nanowires and an alumina filling material (ruby, Al2O3), the copper allowing to evacuate the electrostatic charges, while keeping the properties of rigidity and high resistance of alumina for the component.
In a second example, the nanowires are made of metal and the filling material of Al2O3, the metal allowing to modify the colour of the component.
Silicon nanowires and a silicon oxide filler material allow the thermal dependence of elasticity to be modified, in particular to adjust the thermal compensation of the natural frequency of a mechanical oscillator.
Finally, a filling material made of parylene or another polymer (Teflon, POM, etc) allows a sliding component having a reduced coefficient of dry friction to be obtained, which is useful for some of the applications where the friction between two mobiles must be reduced, and/or the addition of a standard lubricant would only degrade friction and increase wear, for example in an anti-shock component.
Depending on the combinations, the composite material allows in particular springs to be manufactured.
Regarding the manufacture of nanowires, conventional techniques related to the material selected from the list are used, such as catalytic growth, chemical etching, electrochemical deposition (electrodeposition), or deep etching by reactive plasma. The deposition of thin layers is preferably used, for example by CVD (Chemical Vapour Deposition) type chemical deposition or by PVD (Physical Vapour Deposition) type physical deposition. As in the first embodiment, photolithography methods are used to define the contours of the component on a substrate, for example made of silicon, where the nanowires are grown. After obtaining the nanowires, the flexible material is inserted between the nanowires. Finally, the component is detached from the substrate when it is finished.
International patent application WO 2014/172660 gives an embodiment of silica nanowires.
The nanowires 3 can also be produced by techniques other than catalytic growth, such as those described in the publication by N. Hutchison (MEMS 2009).
The filling material is inserted between the nanowires by methods of the ALD (atomic layer deposition), LPCVD (Low Pressure Chemical Vapour Deposition), MOCVD (moderate pressure CVD) type, by electrochemical deposition (electro-deposition), by CVD or by soaking in a liquid or gas phase.
Naturally, the invention is not limited to the embodiments described with reference to the figures and variants could be considered without departing from the scope of the invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 19218863.9 | Dec 2019 | EP | regional |