Flexographic ink containing a polymer or copolymer of a 3, 4-dialkoxythiophene

Abstract

A non-dye containing flexographic ink containing a polymer or copolymer of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge, a polyanion and a latex binder in a solvent or aqueous medium, characterized in that the polymer or copolymer of a 3,4-dialkoxythiophene is present in a concentration of at least 0.1% by weight in the ink and that the ink is capable of producing a colorimetrically additive transparent print; a method of preparing the flexographic ink; and a flexographic printing process therewith.

Description

FIELD OF THE INVENTION

[0002] The present invention relates to flexographic inks containing a polymer or copolymer of a 3,4-dialkoxythiophene.

BACKGROUND OF THE INVENTION

[0003] Flexographic inking systems are used for printing a wide variety of substrates both porous such as paper and paperboard and non-porous such as polymer films and foils and are based on a two or three-roll system or a system that uses enclosed doctor blades. The three-roll system uses a rubber pickup roll that picks up the ink and transfers it to an anilox roll (engraved metal or ceramic roll). The ink fills the engraved cells and is then transferred to plates (either rubber or plastic), where the image is raised in relief from the background, non-image area. A final transfer then occurs from the plate to the substrate. Flexographic presses run at speeds in the range of 0.25 to 10.2 m/s.

[0004] Flexographic inks may be water- or solvent-based and are suitable for overprinting colour on colour, water-based inks typically having a pH of at least 8.5. Flexographic inks are known as liquid inks because of their low viscosity: 10 to 100 mPa.s under printing conditions. Prints produced by flexography can fulfil a wide range of functional effects other than the provision of information such as antistatic properties, e.g. for packaging for electronic components sensitive to electrical discharges, and electroconductive properties.

[0005] Flexographic inks containing electroconductive agents are reported in the patent literature. These are based upon metal particles, see for example WO 00/29208, U.S. Pat. No. 5,189,952, U.S. Pat. No. 4,221,830, U.S. Pat. No. 4,282,692, U.S. Pat. No. 5,286,415, U.S. Pat. No. 5,389,403 and U.S. Pat. No. 5,656,081, or carbon blacks particles, see for example JP 49-068807A, WO 00/77408, U.S. Pat. No. 5,286,415 and U.S. Pat. No. 5,389,403. Metallic inks are made from aluminum or bronze powders mixed with a suitable resin soluble. Such inks cannot be integrated into colour work due to the non-transparency of the prints made therewith.

[0006] Flexographic inks containing electroconductive agents capable of producing prints which can be incorporated into the informational attributes of flexible packaging, but also fulfilling an additional functional role are therefore required.

[0007] WO 99/34371 discloses a silk screen paste with a viscosity of 1 to 200 dpa.s (102 to 2×104 mpa.s) containing a solution or dispersion of a conductive polymer paste and optionally binders, thickeners and fillers. WO 99/34371 further discloses a process for preparing silk screen pastes in which a solution or dispersion with a content of <2% by weight of poly(3,4-ethylenedioxythiophene) [PEDOT]/poly(styrenesulfonate) [PSS] is concentrated to a solids content of >2% by removing the solvent and in which subsequently binder and/or filler are optionally added. Example 1 discloses evaporation of water from a 1.3% by weight solids dispersion of PEDOT/PSS in water to a 3% by weight solids dispersion in a rotary evaporator at 45° C. and 20 mbar.

[0008] EP-A 1 081 549 discloses a coating composition comprising a solution of a substituted or unsubstituted thiophene-containing electrically-conductive polymer, a film-forming binder, and an organic solvent media; the media having a water content of less than 37 weight percent. Coating dispersions with 0.1% by weight of PEDOT/PSS, i.e. 0.0294% by weight of PEDOT since BAYTRON™ P contains a weight ratio PEDOT to PSS of 1:2.4, and with between 8 and 25% by weight of water were disclosed in the invention examples using BAYTRON™ P, a 1.22% by weight dispersion of PEDOT/PSS in water, as the starting material.

[0009] EP-A 1 081 546 discloses a coating composition comprising a solution of an electrically-conductive polymer and an organic solvent media wherein the solvents are selected from the group consisting of alcohols, ketones, cycloalkanes, arenes, esters, glycol ethers and their mixtures; the media having a water content of less than 12 weight percent. Coating dispersions with PEDOT/PSS concentrations between 0.02 and 0.1% by weight, i.e. between 0.00588 and 0.0294% by weight of PEDOT since BAYTRON™ P contains a weight ratio PEDOT to PSS of 1:2.4, and with between 2 and 8% by weight of water were disclosed in the invention examples using BAYTRON™ P, a 1.22% by weight dispersion of PEDOT/PSS in water, as the starting material.

[0010] EP-A 1 081 548 discloses a coating composition comprising a substituted or unsubstituted thiophene-containing electrically-conductive polymer and an organic solvent media; the media having a water content of less than 12 weight percent. Coating dispersions with PEDOT/PSS concentrations between 0.02 and 0.1% by weight, i.e. between 0.00588 and 0.0294% by weight of PEDOT since BAYTRON™ P contains a weight ratio PEDOT to PSS of 1:2.4, and with between 2 and 8% by weight of water were disclosed in the invention examples using BAYTRON™ P, a 1.22% by weight dispersion of PEDOT/PSS in water, as the starting material.

[0011] EP-A 593 111 discloses a sheet or web material comprising a water resistant support or paper support coated with at least one water resistant resin layer wherein said resin support or resin layer is coated with an outermost antistatic layer containing as an essential component a polythiophene with conjugated polymer backbone in the presence of a polymeric polyanion compound, characterized in that said antistatic layer contains also a hydrophobic organic polymer having a glass transition value (Tg) of at least 40° C., said polythiophene being present at a coverage of at least 0.001 g/m2 and the weight ratio of said polythiophene organic polymer being in the range if 1/10 to 1/1000.

[0012] EP-A 821 025 discloses a thermal and mechanical formable polymer foil characterized by a transparent antistatic layer of a mixture of 3,4-polyethylenedioxythiophene with a thermally or mechanically formable binder.

[0013] WO 01/65903 discloses a method of forming an EMI shield comprising the steps of: (a) providing a thermoformable film comprising a first side and a second side; (b) applying an extensible conductive coating to the thermoformable film by printing or coating processes comprising flexographic printing, screen printing, gravure printing, offset printing, letter press printing, pad printing, slot coating, flood coating, spray coating and jet printing; (c) cutting the thermoformable film into a three-dimensional shape; and (e) applying a compressible EMI gasket to the thermoformable film, wherein steps (b) through (e) may be performed in any order.

[0014] Commercially non-transparent conductive flexographic inks on the basis of carbon black, e.g. THERMOKETT™ Conductive Ink and Black VX7011 from Akzo Nobel Inks, and metallic pigments are available. There is a need for flexographic inks capable of producing transparent conductive prints.

ASPECTS OF THE INVENTION

[0015] It is therefore an aspect of the present invention to provide a flexographic ink containing an electroconductive agent and capable of producing a transparent print.

[0016] It is a further aspect of the present invention to provide a method of preparing a flexographic ink containing an electroconductive agent capable of producing a transparent print.

[0017] It is also an aspect of the present invention to provided a flexographic printing process using a flexographic ink containing an electroconductive agent and capable of providing a transparent print on an optionally subbed substrate.

[0018] Further aspects and advantages of the invention will become apparent from the description hereinafter.

SUMMARY OF THE INVENTION

[0019] In fulfilling the need for a flexographic ink containing an electroconductive agent and capable of producing a transparent print, inorganic semiconductors transparent to visible light (400 to 750 nm) such as vanadium pentoxide, cuprous iodide and indium tin dioxide pigments are obvious candidates as electroconductive agents together with intrinsically conductive polymers such as polypyrroles, polyanilines, polyacetylene, polyparaphenylene, polythiophenes, polyphenylenevinylene, polythienylenevinylene and polyphenylenesulphide etc. However, it has been found that flexographic inks containing inorganic semiconductors exhibit poor resistance to abrasion and poor adhesion upon flexing/bending of the substrate and that flexographic inks containing polyanilines produce prints that are transparent but insufficiently conductive (e.g. a surface resistance of 107 Ω/square at an optical density of 0.01) or conductive and dominated by a high optical density green background (e.g. a surface resistance of 1000 Ω/square at an optical density >1.0), the intrinsic green colour of polyanilines, whereas flexographic inks containing polythiophenes surprisingly produced transparent prints which were readily overprintable and exhibited surface resistances down to 5000 Ω/square for non-coloured transparent prints and down to 6000 Ω/square for differently coloured transparent prints with optical density of up to 0.7. Furthermore, such layers exhibited excellent adhesion to a variety of substrates and excellent resistance to abrasion, water, alkali and organic solvents.

[0020] Aspects of the present invention are realized by a non-dye containing flexographic ink containing a polymer or copolymer of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge, a polyanion and a latex binder in an organic solvent or aqueous medium, characterized in that the polymer or copolymer of a 3,4-dialkoxythiophene is present in a concentration of at least 0.1% by weight in the ink and that the ink is capable of producing a colorimetrically additive transparent print.

[0021] Aspects of the present invention are also realized by a method for preparing the above-described flexographic ink comprising the steps of: i) concentrating an aqueous dispersion of the polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion; and ii) adding the latex binder.

[0022] Aspects of the present invention are also provided by a flexographic printing process comprising the steps of: providing the above-described flexographic ink; and printing the printing ink on an optionally subbed substrate thereby producing a colorimetrically additive transparent print.

[0023] Aspects of the present invention are also provided by a non-dye containing flexographic ink containing at least 0.1% by weight of a polymer or copolymer of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge, a polyanion and a latex binder in a solvent or aqueous medium and the ink is capable of producing a colorimetrically additive transparent print obtainable by the above-described method.

[0024] Preferred embodiments are disclosed in the dependent claims.

DETAILED DESCRIPTION OF THE INVENTION

Definitions

[0025] The term alkoxy means all variants possible for each number of carbon atoms in the alkoxy group i.e. for three carbon atoms: n-propyl and isopropyl; for four carbon atoms: n-butyl, isobutyl and tertiary-butyl; for five carbon atoms: n-pentyl, 1,1-dimethyl-propyl, 2,2-dimethylpropyl and 2-methyl-butyl etc.

[0026] The term oxyalkylenealkoxy means two oxygen atoms linked by an alkylene group. An alkylene group is a substituted or unsubstituted hydrocarbon group e.g. a —(CH2)n— group where n is an integer between 1 and 5, which may be substituted with an alkoxy, aryloxy, alkyl, aryl, alkaryl, alkyloxyalkyl, alkyloxyalkaryl, alkyloxyaryl, hydroxy, carboxy, carboxyalkyl, carboxyamino, sulfo or alkylsulfo group.

[0027] The term derivatives as used in connection with a particular polymer refers to variants thereof substituted with alkyl, alkoxy, alkyloxyalkyl, carbbxy, alkylsulfonato and carboxy ester groups.

[0028] The term transparent layer as used in disclosing the present invention means permitting the passage of light in such a way that objects can be clearly seen through the layer.

[0029] The term colorimetrically additive as used in disclosing the present invention means having a colour whose component standard colours are additive with the component standard colours of adjacent layers.

[0030] The term aqueous medium means a medium containing water and water-miscible organic solvents containing between 50% by weight of water and 100% by weight of water.

[0031] The term solvent medium means a medium containing organic solvents and may also contain dissolved water in a concentration of less than 50% by weight.

[0032] The term dye, according to the present invention, means a coloring agent having a solubility of 10 mg/L or more in the medium in which it is applied and under the ambient conditions pertaining.

[0033] The term pigment is defined in DIN 55943, herein incorporated by reference, as an inorganic or organic, chromatic or achromatic coloring agent that is practically insoluble in the application medium under the pertaining ambient conditions, hence having a solubility of less than 10 mg/L therein.

[0034] Freeze drying according to the present invention is a lyophilization process in which a substance is first frozen and then the quantity of solvent (generally water) is reduced, first by sublimation (=primary drying process) and then by desorption (=secondary drying process) until the temperature of the shelves becomes equal to the atmospheric temperature in the freeze dryer. The freeze-drying process is enabled by the ability of solid materials such as ice to sublime (change directly into a gas without passing through a liquid phase) under the right conditions.

[0035] The term “dry product”, according to the present invention, means dry to touch and is associated with no apparent liquid phase.

[0036] The term paste, according to the present invention, means a soft plastic mixture or composition.

[0037] The term Newtonian behaviour refers to a viscosity with no more than 10% variation in the shear rate range 1 to 80 s−1 measured with increasing shear rate for concentrations in the medium concerned up to 2% by weight in the absence of other ingredients.

[0038] The term non-Newtonian behaviour refers to a viscosity with more than 10% variation in the shear rate range 1 to 80 s−1 measured with increasing shear rate for concentrations in the medium concerned below 2% by weight and in the absence of other ingredients.

[0039] The term layer according to the present invention means a continuous or discontinuous coating.

[0040] The term pattern according to the present invention means a discontinuous coating.

[0041] The term flexible as used in disclosing the present invention means capable of following the curvature of a curved object such as a drum e.g. without being damaged.

[0042] The electric resistance of a layer is generally expressed in terms of surface resistance Rs (unit Ω; often specified as Ω/square). Alternatively, it may be expressed in terms of volume resistivity Rv−Rs·d, wherein d is the thickness of the layer, volume conductivity kv=1/Rv [unit: S(iemens)/cm] or surface conductance ks=1/Rs [unit: S(iemens).square].

[0043] The term ‘electroconductive’ according to the present invention means having a surface resistivity below 106 Ω/square. 106 Ω/square is typically regarded as a value of surface resistivity which distinguishes electroconductive materials from antistatic materials. Antistatic materials typically have a surface resistivity in the range from 106 to 1011 Ω/square and are not suitable as an electrode.

[0044] Conductivity enhancement refers to a process in which contact with high boiling point liquids such as di- or polyhydroxy- and/or carboxy groups or amide or lactam group containing organic compound optionally followed by heating at elevated temperature, preferably between 100 and 250° C., during preferably 1 to 90 seconds, results in conductivity increase. Alternatively in the case of aprotic compounds with a dielectric constant ≧15, e.g. N-methyl-pyrrolidinone, temperatures below 100° C. can be used. Such conductivity enhancement is observed with polythiophenes and can take place during the preparation of a layer or subsequently. Particularly preferred liquids for such treatment are N-methyl-pyrrolidinone and diethylene glycol such as disclosed in EP-A 686 662 and EP-A 1 003 179.

[0045] PEDOT as used in the present disclosure represents poly(3,4-ethylenedioxythiophene).

[0046] PSS as used in the present disclosure represents poly(styrene sulphonic acid) or poly(styrenesulphonate).

[0047] PET as used in the present disclosure represents poly(ethylene terephthalate).

Flexographic Ink

[0048] Aspects of the present invention are realized by a non-dye containing flexographic ink containing a polymer or copolymer of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge, a polyanion and a latex binder, characterized in that the polymer or copolymer of a 3,4-dialkoxythiophene is present in a concentration of at least 0.1% by weight in the flexographic ink and that the flexographic ink is capable of producing a colorimetrically additive transparent print.

[0049] According to a first embodiment of the flexographic ink, according to the present invention, the flexographic ink contains at least 0.2% by weight of a polymer or copolymer of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge.

[0050] According to a second embodiment of the flexographic ink, according to the present invention, the flexographic ink contains at least 0.3% by weight of a polymer or copolymer of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge.

[0051] According to a third embodiment of the flexographic ink, according to the present invention, the flexographic ink has a viscosity at 25° C. after stirring to constant viscosity of at least 100 mPa.s as measured according to DIN 53211 i.e. until successive measurements according to DIN 53211 are reproducible.

[0052] According to a fourth embodiment of the flexographic ink, according to the present invention, the flexographic ink has a viscosity at 25° C. after stirring to constant viscosity of at least 200 mPa.s as measured according to DIN 53211 i.e. until successive measurements according to DIN 53211 are reproducible.

[0053] According to a fifth embodiment of the flexographic ink, according to the present invention, the flexographic ink has a viscosity at 25° C. after stirring to constant viscosity of less than 1000 mPa.s as measured according to DIN 53211 i.e. until successive measurements according to DIN 53211 are reproducible.

[0054] According to a sixth embodiment of the flexographic ink, according to the present invention, the flexographic ink has a pH between 1.5 and 5.5.

[0055] Polymer or copolymer of a 3,4-dialkoxythiophene According to a seventh embodiment of the flexographic ink, according to the present invention, the polymer or copolymer of a (3,4-dialkoxythiophene) has the formula 1

[0056] in which, each of R1 and R2 independently represents hydrogen or a C1-5-alkyl group or together represent an optionally substituted C1-5 alkylene group or a cycloalkylene group.

[0057] According to an eighth embodiment of the flexographic ink, according to the present invention, the polymer or copolymer of a (3,4-dialkoxythiophene) is a polymer or copolymer of a (3,4-dialkoxythiophene)in which the two alkoxy groups together represent an optionally substituted oxy-alkylene-oxy bridge.

[0058] According to a ninth embodiment of the flexographic ink, according to the present invention, the polymers or copolymers of a (3,4-dialkoxy-thiophenes) are polymers or copolymers of a (3,4-dialkoxy-thiophenes)in which the two alkoxy groups together represent an optionally substituted oxy-alkylene-oxy bridge are selected from the group consisting of: poly(3,4-methylenedioxy-thiophene), poly(3,4-methylenedioxythiophene) derivatives, poly(3,4-ethylenedioxythiophene), poly(3,4-ethylenedioxythiophene) derivatives, poly(3,4-propylenedioxythiophene), poly(3,4-propylene-dioxythiophene) derivatives, poly(3,4-butylenedioxythiophene) and poly(3,4-butylenedioxythiophene) derivatives and copolymers thereof.

[0059] According to a tenth embodiment of the flexographic ink, according to the present invention, the polymers or copolymers of a (3,4-dialkoxythiophenes), the substituents for the oxy-alkylene-oxy bridge are alkyl, alkoxy, alkyloxyalkyl, carboxy, alkylsulphonato and carboxy ester groups.

[0060] According to an eleventh embodiment of the flexographic ink, according to the present invention, in the poly(3,4-dialkoxythiophenes) the two alkoxy groups together represent an optionally substituted oxy-alkylene-oxy bridge which is a 1,2-ethylene group, an optionally alkyl-substituted methylene group, an optionally C1-12-alkyl- or phenyl-substituted 1,2-ethylene group, a 1,3-propylene group or a 1,2-cyclohexylene group.

[0061] Such polymers are disclosed in Handbook of Oligo- and Polythiophenes Edited by D. Fichou, Wiley-VCH, Weinheim (1999); by L. Groenendaal et al. in Advanced Materials, volume 12, pages 481-494 (2000); L. J. Kloeppner et al. in Polymer Preprints, volume 40(2), page 792 (1999); P. Schottland et al. in Synthetic Metals, volume 101, pages 7-8 (1999); and D. M. Welsh et al. in Polymer Preprints, volume 38(2), page 320 (1997,).

Polyanion

[0062] According to an twelfth embodiment of the flexographic ink, according to the present invention, polyanions include the polyanions of polymeric carboxylic acids, e.g. polyacrylic acids, polymethacrylic acids, or polymaleic acids, and polysulphonic acids, e.g. poly(styrene sulphonic acid). These polycarboxylic acids and polysulphonic acids can also be copolymers of vinylcarboxylic acids and vinylsulphonic acids with other polymerizable monomers, e.g. acrylic acid esters, methacrylic acid esters and styrene.

[0063] According to a thirteenth embodiment of the flexographic ink, according to the present invention, the polyanion is poly(styrenesulphonate) or a polyanion of a copolymer of poly(styrenesulphonic acid) with styrene.

[0064] According to a fourteenth embodiment of the flexographic ink, according to the present invention, the molar ratio of polymer or copolymer of a 3,4-dialkoxythiophene, in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge, to polyanion is in the range of 1:0.95 to 1:6.5.

[0065] According to a fifteenth embodiment of the flexographic ink, according to the present invention, the molar ratio of polymer or s copolymer of a 3,4-dialkoxythiophene, in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge, to polyanion is in the range of 1:0.95 to 1:3.0.

Latex Binder

[0066] Aspects of the present invention are realized by a non-dye containing flexographic ink containing a polymer or copolymer of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge, a polyanion and a latex binder.

[0067] The suitability of latex binders was assessed by adding 0.1% by weight of the particular binder to a typical dispersion medium for the PEDOT/PSS-containing compositions of the present invention such as 87% by weight of 1,2-propandiol, 9% by weight of diethylene glycol, 3% by weight of deionized water, 0.5% by weight of ZONYL™ FSO and 0.5% by weight of silicone antifoam agent X50860A. A binder which dissolved in such a dispersion medium to the extent of 0.1% by weight was regarded as suitable for the compositions according to the present invention.

[0068] According to a sixteenth embodiment of the flexographic ink, according to the present invention, the latex binder is a carboxylated polyolefin or a homo- or co-polymer of a monomer selected from the group consisting of styrene, acrylates, methacrylates, and dienes e.g. isoprene and butadiene.

[0069] Suitable latex binders, according to the present invention, are:

LATEX01 = poly(methyl methacrylate) latex with a particle size of
          90 nm, available as a 20% by weight aqueous dispersion;
LATEX02 = copolyester latex of 26.5 mol % terephthalic acid, 20
          mol % isophthalic acid, 3.5 mol % sulfo-isophthalic acid
          and 50 mol % ethylene glycol, available as a 20% by
          weight aqueous dispersion;
LATEX03 = vinylidene chloride, methyl methacrylate, itaconic acid
          (88/10/2) terpolymer, available as 30% by weight aqueous
          dispersion;
LATEX04 = a copolymer of 80% ethyl acrylate and 20% methacrylic
          acid, available as a 27% by weight aqueous dispersion;
LATEX05 = a copolymer of 49% methyl methacrylate, 49% of butadiene
          and 2% itaconic acid, available as a 30% by weight
          aqueous dispersion;
LATEX06 = a poly(ethyl acrylate), available as a 30% by weight
          aqueous dispersion.
LATEX07 = CARBOPOL ™ Aqua 30, a latex of a copolymer of acrylic
          acid and ethyl acrylate from B. F. Goodrich;
LATEX08 = NEOCRYL ™ BT24, an acrylate-based aqueous latex from
          Zenica;
LATEX09 = AQUACER ™ 503, an acrylate-based aqueous latex from
          BYC Cera;
LATEX10 = POLYPHOBE ™ TR117, an acrylate-based aqueous latex
          from Union Carbide;
LATEX11 = AMOREX ™ CR2900, an acrylate-based aqueous latex
          from Westvaco Corporation;
LATEX12 = CRX-8057-45, an acrylate-based aqueous latex from
          Westvaco Corporation;
LATEX13 = PRIMAL ™ EP-5380, a 54% by weight acrylate-based
          aqueous latex from Rohm and Haas;
LATEX14 = JAGOTEX ™ KEM1020, a 58% by weight acrylate-based
          aqueous latex from Ernst Jager Chem. Rohstoffe GmbH;
LATEX15 = PERMUTEX ™ PS-34 = 320, a 54% by weight acrylate-
          based aqueous latex from Stahl Holland BV;
LATEX16 = JAGOTEX ™ KEM4009, a 55% by weight acrylate
          copolymer aqueous latex from Ernst Jager Chem. Rohstoffe
          GmbH;
LATEX17 = GOOD RITE ™ K797, a 50% by weight acrylic acid-
          AMPS copolymer aqueous latex from B. F. Goodrich;
LATEX18 = NARLEX ™ DX2020, an acrylic acid/styrene copolymer
          latex from Alco Chemical;
LATEX19 = ALCOPERSE ™ 725, an acrylic acid/styrene copolymer
          latex from Alco Chemical;
LATEX20 = CARBOPOL ™ EP2, a 18.1% by weight non-crosslinked
          methacrylate acid/ethyl acrylate copolymer latex from
          B. F. Goodrich
LATEX21 = NEOCRYL ™ BT-9, a 40% by weight aqueous poly-
          acrylate latex from ZENICA Resins
LATEX22 = TANACOTE ™ FG3, a 30% by weight aqueous dispersion
          of a carboxylated polypropylene from SYBRON Chemical
          Division
Latexes 7 and 20 have a very strong influence upon the viscosity of the dispersion independent of the PEDOT/PSS-content. LATEX03, LATEX04, LATEX05 and LATEX06 all have glass transition temperatures below 25° C.

[0070] Binders can be Newtonian or non-Newtonian as defined above.

Additional Binders

[0071] According to a seventeenth embodiment of the flexographic ink, according to the present invention, the flexographic ink further comprises at least one additional binder. Such binders can have a thickening effect on the flexographic ink.

[0072] According to an eighteenth embodiment of the flexographic ink, according to the present invention, the flexographic ink further comprises a binder having a glass transition temperature above 25° C.

[0073] Suitable additional binders for use in the present invention are described in EP-A 564 911, which is hereby incorporated by reference, and include water-soluble polymers, such as poly(vinyl alcohol), water-soluble homo- and co-polymers of acrylic acid and homo- and co-polymers of methacrylic acid, and latex binders. Suitable additional binders with a thickening effect are polyacrylates and polysaccharides. Preferred polyacrylate thickeners are high molecular weight homo- and copolymers of acrylic acid crosslinked with a polyalkenyl polyether such as the CARBOPOL™ resins of B. F. Goodrich with CARBOPOL™ ETD-2623 being particularly preferred. Preferred polysaccharide thickeners include cellulose, cellulose derivatives e.g. carboxymethyl cellulose, silica, guar gum and xanthan gum, with xanthan gum being particularly preferred e.g. BIOSAN™ S from Hercules Inc., USA and Kelzan™ T from MERCK & Co., Kelco Division, USA.

[0074] Particularly preferred additional binders for use in the flexographic ink, according to the present invention, are:

ERCOL ™ 48 20 =      a poly(vinyl alcohol) from Acetex Europe
CARBOPOL ™ ETD2623 = an acrylic acid copolymer crosslinked with
                     a polyalkenyl polyether from B. F.
                     Goodrich;
CERIDUST ™ 130 =     a polyethylene wax from Hoechst;
JONREZ ™ SM700 =     a rosin based resin from Johnson Polymer;
JONREZ ™ SM705 =     a rosin based resin from Johnson Polymer;
JONREZ ™ SM729 =     a rosin based resin from Johnson Polymer;
KLUCEL ™ H =         a hydroxypropylcellulose from Hercules
                     Inc.;
NEOCRYL ™ BT24 =     an alkaline-soluble acrylic copolymer from
                     Zenica Resins

[0075] According to a nineteenth embodiment of the flexographic ink, according to the present invention, the flexographic ink further comprises a water-soluble binder selected from the group consisting of: poly(vinyl alcohol), homo- and co-polymers of hydroxyethyl methacrylate, copolymers of 2-propenoic acid 2-(phosphonooxy)ethyl ester and copolymers of 2-methyl-2-propenoic acid 2-(phosphonooxy)ethyl ester.

Newtonian Binders

[0076] According to a twentieth embodiment of the flexographic ink, according to the present invention, the flexographic ink contains a Newtonian binder, see above definition. This Newtonian binder may be the latex binder or an additional binder.

[0077] Addition of the Newtonian binder to the aqueous composition, according to the present invention, may improve the coating quality on non-planar structures. Such binders may also increase the viscosity of aqueous solutions, but not substantially.

[0078] According to a twenty-first embodiment of the flexographic ink, according to the present invention, the flexographic ink contains a Newtonian binder selected from the group consisting of polyacrylates, carboxymethylcellulose, polyvinylpyrrolidone, hydroxyethylcellulose (e.g. TYLOSE™ H4000P), hydroxypropyl-cellulose (e.g. KLUCEL™ H from Hercules), carboxylate-containing copolymers with sulphonic acid groups, hydroxy-modified acrylic acid copolymers and poly(vinyl alcohol).

[0079] Suitable Newtonian binders are:

Non-Newtonian binders
MIROX ™ TBN = a 20% by weight aqueous solution of a copolymer of
              sodium acrylate and NP 14-methacrylate by
              Stockhausen GmbH, Krefeld, Germany;
LATEX 21 =    Neocryl ™ BT-9, a 40% by weight aqueous
              polyacrylate latex from ZENICA Resins;
LATEX 22 =    Tanacote ™ FG3, a 30% by weight aqueous
              dispersion of a carboxylated polypropylene from
              SYBRON Chemical Division

[0080] According to an twenty-second embodiment of the flexographic ink, according to the present invention, the flexographic ink contains a non-Newtonian binder. This non-Newtonian binder may be the latex binder or an additional binder.

[0081] Non-Newtonian binders bind the ingredients of the electroconductive layers together and substantially increase the viscosity of aqueous solutions at concentrations by weight of less than 2%.

[0082] Polyacrylates and polysaccharides exhibiting non-Newtonian behaviour in aqueous solution are suitable non-Newtonian binders for use in the aqueous compositions according to the present invention. Polysaccharides which substantially increase the viscosity of aqueous solutions include cellulose, cellulose derivatives, e.g. carboxymethyl cellulose, guar gum and xanthan gum.

[0083] The difference in rheological behaviour for non-Newtonian and Newtonian binders is evident from the dependence of the viscosity of their solutions upon shear rate. Table 1 gives the viscosity as a function of shear rate determined using an AR1000 plate and cone rheometer (diameter 4 cm; cone angle 2°) at 20° C. with increasing shear rate for 1% by weight solutions of CARBOPOL™ ETD 2623, a non-Newtonian polyacrylate binder, 0.2% by weight solutions of the copolymer of sodium polyacrylate and NP 14-methacrylate in MIROX™ TBN, a Newtonian polyacrylate binder, at different pH's and 2% by weight solutions of MIROX™ TBN in Table 1.

	TABLE 1
	Viscosity [mPa · s] at 20° C.
		ag. solution of copolymer
	1% by weight	of sodium polyacrylate & NP
Shear	CARBOPOL ™ ETD 2623	14-methacrylate in MIROX ™ TBN
rate	solution in water	0.2% by weight	2% by weight
[s−1]	pH = 3.2	pH = 5.2	pH = 8.0	pH = 7.2
0.10				375.9
0.25				365.8
0.40				363.0
0.63				358.9
1.00				357.0
1.18			4.9
1.20	7897	68620
1.59				353.9
2.30			4.8
2.38	3296	42610
2.51				349.8
3.98				346.2
4.67			4.8
4.75		26710
4.76	1520
5.89				372.0
7.29			4.9
7.54	994.2	19530
10.0				352.8
14.95			4.7
15.04	565.9	12070
15.85				372.0
25.12				394.9
30.00	337.5	7554
30.21			4.7
39.81				396.6
63.10				365.7
75.36	177.4	4180
77.15			4.6

[0084] Non-Newtonian binders for use in the present invention include high molecular weight homo- and copolymers of acrylic acid crosslinked with a polyalkenyl polyether, such as the CARBOPOL™ resins of B. F. Goodrich e.g. CARBOPOL™ ETD 2623, and xanthan gum, e.g. BIOSAN™ S from Hercules Inc., USA and Kelzan™ T from MERCK & Co., Kelco Division, USA.

[0085] According to a twenty-third embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains a non-Newtonian binder which is selected from the group consisting of polyacrylates and polysaccharides. According to an twenty-fourth embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains a non-Newtonian binder which is a homopolymer or copolymer of acrylic acid crosslinked with a polyalkenyl polyether.

Organic Solvents

[0086] According to a twenty-fifth embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains an organic solvent.

[0087] According to a twenty-sixth embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains a water-miscible organic solvent.

[0088] According to a twenty-seventh embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains a water-miscible organic solvent which is selected from the group consisting of aliphatic alcohols, ketones, arenes, esters, glycol ethers, cyclic ethers, such as tetrahydrofuran, and their mixtures.

[0089] The presence of certain organic solvents in layers containing polymers or copolymers of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge together with a subsequent heat treatment enhances the conductivity of the layers as disclosed in EP-A 686 662 and EP-A 1 003 179, herein included by reference.

[0090] According to a twenty-eighth embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains a di- or polyhydroxy- and/or carboxy groups or amide or lactam group containing organic compound, for example diethylene glycol, 1,2-propandiol, glycerol, hexylene glycol, propylene glycol, di(ethylene glycol)ethyl ether acetate (carbitol™ acetate), N-methylacetamide, N-methyl pyrrolidinone and sugar alcohols, such as sorbitol, mannitol, saccharose and fructose.

[0091] According to a twenty-ninth embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains an aprotic compound with a dielectric constant ≧15, such as N-methyl pyrrolidinone, 2-pyrrolidinone, 1,3-dimethyl-2-imidazolidone, N,N,N′,N′-tetramethylurea, formamide, N,N-dimethylformamide, N,N-dimethylacetamide, tetramethylene sulphone, dimethyl sulphoxide and hexamethylphosphoramide.

[0092] According to a thirtieth embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains a di- or polyhydroxy- and/or carboxy groups or amide or lactam group containing organic compound selected from the group consisting of 1,2-propandiol, propylene glycol, diethylene glycol, N-methyl pyrrolidinone and di(ethylene glycol)ethyl ether acetate (carbitol™ acetate).

[0093] The suitability of particular non-aqueous solvents can be evaluated by mixing 8 g of a 1.2% by weight aqueous dispersion of PEDOT/PSS with 12 g of solvent. If miscibility is observed without gel formation, the non-aqueous solvent is regarded as suitable. Tetrahydrofuran is miscible, but the dispersions are very viscous. Suitability according to the above miscibility test does not rule out phase separation upon further dilution of the PEDOT/PSS-dispersion with the same solvent, as is observed with tetrahydrofuran. It will be understood by one skilled in the art that a PEDOT/PSS-dispersion cannot be diluted to an unlimited extent without the possibility of phase separation.

[0094] Ethyl lactate induces gel-formation and hence is unsuitable. Benzyl alcohol, furfuryl alcohol and cyclohexane produced phase separation and hence are unsuitable.

Pigments

[0095] According to a thirty-first embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains a pigment.

[0096] Transparent coloured compositions can be realized by incorporating pigments e.g. azo pigments e.g. DALMAR™ Azo Yellow and LEVANYL™ Yellow HRLF, dioxazine pigments e.g. LEVANYL™ Violet BNZ, phthalocyanine blue pigments, phthalocyanine green pigments, Molybdate Orange pigments, Chrome Yellow pigments, Quinacridone pigments, barium precipitated Permanent Red 2B, manganese precipitated BON Red, Rhodamine B pigments and Rhodamine Y pigments.

[0097] Suitable pigments according to the present invention are:

Pig-		Manu-
ment		fact-
nr.	Pigment	urer
PIG01	LEVANYL ™VIOLET BNZ as an aqueous paste	BAYER	2
PIG02	LEVANYL ™Yellow HR- LF as an aqueous paste	BAYER	3
PIG03	FLEXONYL ™Blue B2G as an aqueous paste	CLARIANT	4
PIG04	LEVANYL ™RED BBZ as an aqueous paste	BAYER	5
PIG05	LEVANYL ™BLUE GZ as an aqueous paste	BAYER	6
PIG06	NOVOPERM ™Yellow HR02 as a aqueous paste	CLARIANT	7
PIG07	LEVANYL ™Blue G-LF as an aqueous paste	BAYER	8
PIG08	HOSTAPERM ™Blue B2G as an aqueous paste	CLARIANT	9
PIG09	HOSTAPERM ™Blue B2G-L as an aqueous paste	CLARIANT	10

Crosslinking Agents

[0098] According to a thirty-second embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains a cross-linking agent. Suitable cross-linking agents are epoxysilane (e.g. 3-glycidoxypropyltrimethoxysilane), hydrolysis products of silanes (e.g. hydrolysis products of tetraethyoxysilane or tetramethoxysilane) as disclosed in EP 564 911, herein incorporated by reference, and di- or oligo-isocyanates optionally in blocked form.

Anti-foaming Agents

[0099] According to a thirty-third embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains an anti-foaming agent.

[0100] A suitable anti-foaming agent is the silicone antifoam agent X50860A from Shin-Etsu.

Surfactants

[0101] According to a thirty-fourth embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains a surfactant.

[0102] According to a thirty-fifth embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains a non-ionic surfactant e.g. ethoxylated/fluroralkyl surfactants, polyethoxylated silicone surfactants, polysiloxane/polyether surfactants, ammonium salts of perfluro-alkylcarboxylic acids, polyethoxylated surfactants and fluorine-containing surfactants.

[0103] Suitable non-ionic surfactants are:

NON01	SURFYNOL ™ 440	a di(polyethylene oxide)-substituted
		alkyne from Air Products;
NON02	SYNPERONIC ™	a tridecylpolyethylene-glycol from
	13/6.55	UNIQEMA;
NON03	ZONYL ™ FSO-100:	a mixture of ethoxylated fluoro-
		surfactants with the formula:
		F(CF2CF2)1-7CH2CH2O(CH2CH2O)yH
		where y = 0 to ca. 15 from DuPont;
NON04	ARKOPAL ™ N060	a nonylphenylpolyethylene-glycol from
		HOECHST
NON05	FLUORAD ™ FC129	a fluoroaliphatic polymeric ester from
		3M
NON06	PLURONIC ™ L35	a polyethylene-glycol/propylene-glycol
		from BASF
NON07	Tegoglide ™ 410:	a polysiloxane-polymer copolymer
		surfactant, from Goldschmidt;
NON08	Tegowet ™:	a polysiloxane-polyester copolymer
		surfactant, from Goldschmidt;
NON09	FLUORAD ™ FC126:	a mixture of ammonium salts of
		perfluorocarboxylic acids, from 3M;
NON10	FLUORAD ™ FC430:	a 98.5% active fluoroaliphatic ester
		from 3M;
NON11	FLUORAD ™ FC431:	CF3(CF2)7SO2(C2H5)N—CH2CO—
		(OCH2CH2)nOH from 3M;
NON12		Polyoxyethylene-10-lauryl ether
NON13	ZONYL ™ PSN:	a 40% by weight solution of
		F(CF2CF2)1-9CH2CH2O(CH2CH2O)xH
		in a 50% by weight solution of iso-
		propanol in water where x = 0 to about
		25, from DuPont;
NON14	ZONYL ™ FSN-100:	F(CF2CF2)1-9CH2CH2O(CH2CH2O)xH
		where x = 0 to about 25, from DuPont;
NON15	ZONYL ™ PS300:	a 40% by weight aqueous solution of a
		fluorinated surfactant, from Dupont;
NON16	ZONYL ™ FSO:	a 50% by weight solution of a mixture
		of ethoxylated fluorosurfactants with the
		formula:
		F(CF2CF2)1-7CH2CH2O(CH2CH2O)yH
		where y = 0 to ca. 15 in a 50% by
		weight solution of ethylene glycol in
		water, from DuPont;

[0104] According to a thirty-sixth embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains an anionic surfactant. Suitable anionic surfactants are:

AN01	HOSTAPON ™ T	a 95% concentrate of purified sodium salt of N-
		methyl-N-2-sulfoethyl-oleylamide, from HOECHST
AN02	LOMAR ™ D	11
AN03	AEROSOL ™ OT	an aqueous solution of 10 g/L of the sodium salt of
		the di-2-ethylhexyl ester of sulphosuccinic acid
		from American Cyanamid
AN04	DOWFAX ™ 2A1	a 45% by weight aqueous solution of a mixture of
		the sodium salt of bis (p-dodecyl,sulpho-phenyl)-
		ether and the sodium salt of (p-dodecyl,sulpho-
		phenyl)(sulpho-phenyl)ether from Dow Corning
AN05	FT 248	an aqueous solution of 49.5 g/L tetraethylammonium
		perfluoro-octylsulphonate from BAYER
AN06	NIAPROOF	an aqueous solution of 50 mL/L sodium 1-isobutyl,4-
	ANIONIC ™ 4	ethyl-n-octylsulphate from Niacet;
AN07	ZONYL ™ 7950:	a fluorinated surfactant, from DuPont;
AN08	ZONYL ™ FSA:	25% by weight solution of
		F(CF2CF2)1-9CH2CH2SCH2CH2COOLi in a 50% by weight
		solution of isopropanol in water, from DuPont;
AN09	ZONYL ™ FSE:	14% by weight solution of
		[F(CF2CF2)1-7CH2CH2O]xP(O) (ONH4)y where x = 1 or 2;
		y = 2 or 1; and x + y = 3 in a 70% by weight
		solution of ethylene glycol in water, from DuPont;
AN10	ZONYL ™ FSJ:	40% by weight solution of a blend of
		F(CF2CF2)1-7CH2CH2O]xP(O) (ONH4)y where x = 1 or 2;
		y = 2 or 1; and x + y = 3 with a hydrocarbon
		surfactant in 25% by weight solution of
		isopropanol in water, from DuPont;
AN11	ZONYL ™ FSP	35% by weight solution of
		[F(CF2CF2)1-7CH2CH2O]xP(O) (ONH4)y where x = 1 or 2;
		y = 2 or 1 and x + y = 3 in 69.2% by weight
		solution of isopropanol in water, from DuPont;
AN12	ZONYL ™ UR:	[F(CF2CF2)1-7CH2CH2O]xP(O) (OH)y where x = 1 or 2;
		y = 2 or 1 and x + y = 3, from DuPont;
AN13	ZONYL ™ TBS:	33% by weight solution of F(CF2CF2)3-8CH2CH2SO3H in
		a 4.5% by weight solution of acetic acid in water,
		from DuPont;
AN14	FLUORAD ™ FX-	ammonium salt of perfluoro-octanoic acid, from 3M.
	1006

[0105] According to a thirty-seventh embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains an amphoteric surfactant. Suitable amphoteric surfactants are:

AMP01	AMBITERIC H:	a 20% by weight solution of hexadecyldi-
		methylammonium acetic acid in ethanol

Further Additives

[0106] According to a thirty-eighth embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains a wax. Wax improves the scuff, rub and abrasion resistance of the prints. Particularly suitable waxes are polyethylene wax, polyethylene oxide wax, polypropylene wax and fatty amides.

[0107] According to a thirty-ninth embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains a silicone. Silicone increases slip on packaging lines.

[0108] According to a fortieth embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains silica. Silica reduces slip on heavy duty sacks that must stack safely.

[0109] According to a forty-first embodiment of the flexographic ink, according to the present invention, the flexographic ink further contains a placticizer. Plasticizers increase flexibility of the ink film and thus assist in maintaining adhesion.

Method for Preparing a Flexographic Ink

[0110] Aspects of the present invention are also realized by a method for preparing a non-dye containing flexographic ink, containing at least 0.1% by weight of a polymer or copolymer of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge, a polyanion and a latex binder in a solvent or aqueous medium and having a viscosity at 25° C. after stirring to constant viscosity of at least 130 mPa.s as measured according to DIN 53211, comprising the steps of: i) concentrating an aqueous dispersion of the polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion; and ii) adding the latex binder.

[0111] According to a first embodiment of the method, according to the present invention, the method further comprises the step of adding at least one the di- or polyhydroxy- and/or carboxy groups or amide or lactam group containing organic compound for example sugar alcohols, such as sorbitol, mannitol, saccharose and fructose, diethylene glycol, 1,2-propandiol, propylene glycol N-ethyl pyrrolidinone and conductive coatings therefrom which are tempered to increase their resistance preferably to <300 ohm/square as disclosed in EP-A 686 662, hereby incorporated by reference.

[0112] According to a second embodiment of the method, according to the present invention, the method further comprises the step of adding a non-aqueous solvent.

[0113] According to a third embodiment of the method, according to the present invention, the step of concentrating the aqueous dispersion of a polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion is carried out by evaporation of water, evaporation of water after addition of at least one organic solvent or evaporation of water by freeze drying.

[0114] According to a fourth embodiment of the method, according to the present invention, the method further comprises the step of adding a pigment.

Evaporation of Water After Addition of at Least One Organic Solvent

[0115] According to a fifth embodiment of the method, according to the present invention, in the concentration of the aqueous polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion the evaporation of water after addition of at least one organic solvent proceeds until the content of water therein is reduced by at least 65% by weight.

[0116] According to a sixth embodiment of the method, according to the present invention, in the concentration of the aqueous polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion the evaporation of water after addition of at least one organic solvent proceeds until the content of water therein is reduced by at least 70% by weight.

[0117] According to a seventh-embodiment of the method, according to the present invention, in the concentration of the aqueous polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion the evaporation of water after addition of at least one organic solvent proceeds until the content of water therein is reduced by at least 80% by weight.

[0118] According to an eighth embodiment of the method, according to the present invention, in the concentration of the aqueous polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion the evaporation of water after addition of at least one organic solvent proceeds until the content of water therein is reduced by at least 90% by weight.

[0119] According to a ninth embodiment of the method, according to the present invention, in the concentration of the aqueous polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion the evaporation of water after addition of at least one organic solvent proceeds until the content of water therein is reduced by at least 95% by weight.

[0120] According to a tenth embodiment of the method, according to the present invention, in the concentration of the aqueous polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion the evaporation of water after addition of at least one organic solvent proceeds until the content of water therein is reduced by at least 99% by weight.

[0121] According to an eleventh embodiment of the method, according to the present invention, in the concentration of the aqueous polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion the evaporation of water after addition of at least one organic solvent at least 30% by weight of the flexographic ink is non-aqueous solvent.

[0122] According to a twelfth embodiment of the method, according to the present invention, in the concentration of the aqueous polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion the evaporation of water after addition of at least one organic solvent at least 65% by weight of the flexographic ink is non-aqueous solvent.

[0123] According to a thirteenth embodiment of the method, according to the present invention, in the concentration of the aqueous polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion the evaporation of water after addition of at least one organic solvent at least 80% by weight of the flexographic ink is non-aqueous solvent.

[0124] In general the degree to which water can be removed in the process, according to the present invention, will depend upon the ability of the water to diffuse through the dispersion to the surface, which is dependent upon the viscosity of the PEDOT/PSS-dispersion under the evaporation conditions. However, the viscosity of PEDOT/PSS-dispersions is strongly dependent upon the PEDOT/PSS-content in the final dispersion. Water-contents of 1 to 5% by weight can be easily realized with dispersions of 0.8% by weight PEDOT/PSS with a weight ratio of PEDOT to PSS of 1:2.4, but just increasing the content of PEDOT/PSS, with a weight ratio of PEDOT to PSS of 1:2.4, to 1.0% by weight has such a strong influence on the viscosity of the dispersion that the easily realisable water-content increases to 10 to 15% by weight.

[0125] It should be pointed out that the viscoelastic properties of the PEDOT/PSS-dispersions obtained with the method, according to the present invention, are stable upon storage under ambient conditions.

Evaporation of Water by Freeze Drying

[0126] According to a fourteenth embodiment of the method, according to the present invention, wherein in the concentration of the aqueous polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion the evaporation of water by freeze drying a redispersible or soluble product is prepared as a dry product or as a paste.

[0127] The first step in freeze drying a product is to convert it into a frozen state. During the freezing process the solvent (water) is preferably crystallized. The formation of ice crystals results in a separation of the solutes and the solvent. Then the ice crystals are removed by sublimation under vacuum conditions. While the sublimation or primary drying process removes most of the water from the frozen matrix, there can still be greater than 5% moisture weight/weight with respect to the freeze-dried product in the cake. Thereafter the remaining water is removed by desorption. It has been found that the water content of the freeze-dried product, according to the present invention, has a strong effect on the redispersibility thereof. The products are highly hygroscopic. For example, the weight of PEDOT/PSS obtained by drying a 1.2% by weight aqueous dispersion at 102° C. increased by 16 to 23% at room temperature, whereas the weight increase in an exicator was only 8%. Products freeze-dried at room temperature, according to the present invention, typically have a water content of 15 to 20% by weight. Further drying of the freeze-dried product in a vacuum drying cupboard at 110° C. and a drying cupboard at 110° C. results in products, which are more difficult to disperse.

[0128] The redispersible or soluble product prepared by freeze drying is a dry, spongy, woolly powder or a paste. A paste can be obtained instead of a powder by incomplete freeze drying of the aqueous dispersion. The redispersible or soluble product as a powder or paste can be dissolved or redispersed by adding water, organic solvent or mixtures of water/solvent optionally with other ingredients such as surfactants and dispersants.

[0129] According to a fifteenth embodiment of the method, according to the present invention, wherein in the concentration of the aqueous polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion the evaporation of water by freeze drying a redispersible or soluble product is prepared, which is a concentrated dispersion or a paste with a solids content higher than 10% by weight.

[0130] According to a sixteenth embodiment of the method, according to the present invention, wherein in the concentration of the aqueous polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion the evaporation of water by freeze drying a redispersible or soluble product is prepared, which is a concentrated dispersion or a paste with a solids content higher than 20% by weight.

[0131] According to a seventeenth embodiment of the method, according to the present invention, wherein in the concentration of the is aqueous polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion the evaporation of water by freeze drying a redispersible or soluble product is prepared, which is a concentrated dispersion or a paste with a solids content higher than 50% by weight.

[0132] A concentrated dispersion in an organic solvent such as diethylene glycol or N-methyl-pyrrolidinone, can, for example, be realized by freeze drying a mixture of the organic solvent and the aqueous dispersion or solution of polythiophene/polyanion to a dispersion of polythiophene/polyanion in the organic solvent.

[0133] This concentrated dispersion or paste can be diluted or redispersed to obtain any desired concentration in a similar manner to the powder.

Flexographic Printing Process

[0134] Aspects of the present invention are realized by a printing process comprising the steps of: providing a non-dye containing flexographic ink containing at least 0.1% by weight of a polymer or copolymer of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge, a polyanion and a latex binder in a solvent or aqueous medium and a viscosity at 25° C. after stirring to constant viscosity of at least 130 mPa.s as measured according to DIN 53211; and printing ink the printing ink on an optionally subbed substrate thereby producing a colorimetrically additive transparent print.

[0135] According to a first embodiment of the printing process according to the present invention, the substrate is a flexible substrate. According to a second embodiment of the printing process according to the present invention, the substrate is paper, polymer film, glass or ceramic.

[0136] A substrate may be translucent, transparent or opaque. It may be rigid or flexible and consist of a glass, a glass-polymer laminate, a polymer laminate, a thermoplastic polymer or a duroplastic polymer. Examples of thin flexible supports are those made of a cellulose ester, cellulose triacetate, polypropylene, polycarbonate or polyester, with poly(ethylene terephthalate) or poly(ethylene naphthalene-1,4-dicarboxylate) being particularly preferred.

Industrial Application

[0137] The flexographic ink according to the present invention can, for example, be used to apply antistatic and electroconductive patterns to an optionally subbed support, a dielectric layer, a phosphor layer and a transparent conductive layer. This can, for example, be a step in the production of electrical circuitry for single and limited use items such as toys, in capacitive antennae as part of radiofrequency tags, in electroluminescent devices which can be used in lamps, displays, back-lights e.g. LCD, automobile dashboard and keyswitch backlighting, emergency lighting, cellular phones, personal digital assistants, home electronics, indicator lamps and other applications in which light emission is required.

[0138] The invention is illustrated hereinafter by way of COMPARATIVE EXAMPLES and INVENTION EXAMPLES. The percentages and ratios given in these examples are by weight unless otherwise indicated.

[0139] The following substrates were used in the COMPARATIVE and INVENTION EXAMPLES:

substrate nr
1 PET with subbing layer 1
2 polyethylene (RC) coated paper, roll nr. GM 279
3 cellulose triacetate film
4 transparent 100 μm thick PVC-foil, roll nr. 107 × 08 from
  Staufen
5 TRANSPAREX ™ T787 film from
  AGFA-GEVAERT N.V.
6 AUTOSTAT ™ CT7: a 175 μm thick heat-stabilized
  poly(ethylene terephthalate) [PET] subbed on both sides
  supplied by AUTOTYPE INTERNATIONAL LTD
7 copy paper: SYMBIO ™ BRONZE GRAPHICS (80 g/m2)
  from SYMBIOPAPER
8 coated paper: ALLEGRO ™ GLOSS (115 g/m2)

[0140] Subbing layer Nr. 01 has the composition:

copolymer of 88% vinylidene chloride, 10% methyl 79.1%
acrylate and 2% itaconic acid
Kieselsol ™ 100F, a colloidal silica from BAYER 18.6%
Mersolat ™ H, a surfactant from BAYER 0.4%
Ultravon ™ W, a surfactant from CIBA-GEIGY 1.9%

[0141] The following not previously mentioned ingredients were used in the COMPARATIVE and INVENTION EXAMPLES:

anti-foaming agent:
X-50-860A =                      X-50-860A, a silicone defoaming agent from Shin-
                                 Etsu
liquids:
DW =                             deionized water
PD =                             1,2-propandiol (189° C.)
DEG =                            diethylene glycol (245° C.)
DEG-MME =                        diethylene glycol monomethyl ether (193° C.)
dyes:
Acid Yellow 23 (Tartra- phenine) (from Clariant, Germany) = 12
Reactive Red 180 (from Aakash, USA) = 13
Direct Yellow 86 (from Farbenchem, Germany) = 14
Direct Blue 199 (from Farbenchem, Germany) = 15

Aqueous PEDOT/PSS Dispersion

[0142] The starting material for the preparation of the flexographic inks described in the INVENTION EXAMPLES was a 1.2% by weight aqueous dispersion of PEDOT/PSS containing a weight ratio PEDOT to PSS of 1:2.4 prepared as disclosed in EP-A 440 957 and having a typical viscosity measured using an AR1000 plate and cone rheometer (diameter 4 cm; cone angle 2°) at 20° C. of 38 mPa.s at a shear rate of 5 s−1 decreasing to 33.5 mPa.s at a shear rate of 35 mPa.s and has a typical pH of 1.9. A 3% by weight dispersion of PEDOT/PSS was then prepared from this 1.2% by weight dispersion by evaporating 60.7% by weight of the water with stirring at a temperature of 75° C. and a pressure of 50 mbar.

COMPARATIVE EXAMPLES 1 to 7

[0143] The flexographic inks of COMPARATIVE EXAMPLES 1 to 7 were prepared by adding with mixing the ingredients in the quantities given in Table 1 to 45 g of a 3% by weight dispersion of PEDOT/PSS in water after mixing with the deionized water.

	TABLE 1
	Comparative Example nr
	1	2	3	4	5	6	7
1.14 wt % aq.	81.0	81.0	81.0	81.0	81.0	81.0	81.0
PEDOT/PSS
disp.[g]
CARBOPOL ™	0.6	0.6	0.6	0.6	0.6	0.6	0.6
ETD2623 [g]
LATEX14 [g]	1.8	1.8	1.8	1.8	1.8	1.8	1.8
LATEX22 [g]	1.4	1.4	1.4	1.4	1.4	1.4	1.4
PD [g]	2.5	2.5	2.5	2.5	2.5	2.5	2.5
DEG-MME [g]	4.5	4.5	4.5	4.5	4.5	4.5	4.5
DEG [g]	7.0	7.0	7.0	7.0	7.0	7.0	7.0
SURFYNOL ™	0.7	0.7	0.7	0.7	0.7	0.7	0.7
440 [g]
X-50-860A [g]	0.1	0.1	0.1	0.1	0.1	0.1	0.1
Isopropanol [g]	10	10	10	10	10	10	10
Acid Yellow 23 [g]	0.1	—	—	—	—	—	—
Direct Yellow 86 [g]	—	0.1	—	—	—	—	—
Reactive Red 180 [g]	—	—	0.1	—	—	—	—
Direct Blue 199 [g]	—		—	0.1	0.6	1.1	2.0
Total [g]:	99.7	99.7	99.7	99.7	100.2	100.7	101.6
wt % water in	81.0	81.0	81.0	81.0	80.6	80.2	79.5
aq. medium
Viscosity [mPa · s]	680	700	690	720	750	760	750

[0144] The colorants: Acid Yellow 23, Direct Yellow 86, Reactive Red 180 and Direct Blue 199 all had solubilities in water at 25° C. above 10 g/L and hence are classified, according to the present invention, as dyes. Increasing the dye concentration did not produce a proportional increase in optical density in the print and the surface resistance increased disproportionately with an increase in dye concentration. Furthermore, the mottle and graininess of the print also increased with increasing dye concentration in the ink. Flocking of the PEDOT/PSS was observed which may include displacement of PSS in PEDOT/PSS by these anionic dyes.

Flexographic Printing

[0145] The flexographic inks of INVENTION EXAMPLES 1 to 6 were printed using a RK Esiproof handtester from RK Print Coat Instruments Ltd, UK provided with a 140 cells/inch chrome-plated anilox drum.

[0146] The compositions of the printed layers are given in Table 2, together with the surface resistance of the layers and their optical densities as determined using a MacBeth™ RD918 SB with the colour filters given with the optical density values in Table 2.

	TABLE 2
	Comparative Example nr
	1	2	3	4	5	6	7
wt % PEDOT/PSS	23.7	23.7	23.7	23.7	21.0	18.0	15.9
wt % binder	53.1	53.1	53.1	53.1	47.0	42.2	35.6
wt % dye	2.6	2.6	2.6	2.6	13.7	22.5	34.6
wt % SURFYNOL ™ 440	18.0	18.0	18.0	18.0	16.0	14.3	12.1
wt % X-50-860A	2.6	2.6	2.6	2.6	2.3	2.1	1.7
Surface resistance	7.2	11.0	8.1	14	63	1400	non-con-
[kΩ/square]							ductive
OD [Macbeth ™ RD918SB]	0.16	0.18	0.12	0.23	0.41	0.69	0.8
	[Dblue]	[Dblue]	[Dred]	[Dred]	[Dred]	[Dred]	[Dred]

INVENTION EXAMPLES 1 to 6

[0147] The flexographic inks of INVENTION EXAMPLES 1 to 6 were prepared by adding with mixing the ingredients in the quantities given in Table 3 to 45 g of a 3% by weight dispersion of PEDOT/PSS in water after mixing with the deionized water.

	TABLE 3
	Invention Example nr
	1	2	3	4	5	6
3wt % aq. disp. PEDOT/	45	45	45	45	45	45
PSS [g]
DW [g]	23.4	23.4	23.1	25.1	23.1	24.1
LATEX14 [g]	1.8	1.8	1.8	1.8	1.8	1.8
LATEX22 [g]	1.4	1.4	1.4	1.4	1.4	1.4
PD [g]	2.5	2.5	2.5	2.5	2.5	2.5
DEG-MME [g]	4.5	4.5	4.5	4.5	4.5	4.5
DEG [g]	7.0	7.0	7.0	7.0	7.0	7.0
SURFYNOL ™ 440 [g]	0.7	0.7	0.7	0.7	0.7	0.7
X-50-860A [g]	0.1	0.1	0.1	0.1	0.1	0.1
Isopropanol [g]	10	10	10	10	10	10
PIG01 (30%) [g]	—	3.7	—	—	—	—
PIG02 (30%) [g]	—	—	4.0	—	—	—
PIG03 (30%) [g]	—	—	—	2.0	—	—
PIG04 (30%) [g]	—	—	—	—	4.0	—
PIG05 (30%) [g]	—		—		—	3.0
Total [g]:	96.4	100.1	100.1	100.1	100.1	100.1
wt % water in aq. medium	70.2	71.2	71.1	71.3	71.1	71.2
Viscosity [mPa · s]	200	745	470	215	320	615

[0148] The flexographic inks of INVENTION EXAMPLE 1 was non-pigmented and those of INVENTION EXAMPLES 2 to 6 were pigmented. The flexographic ink of INVENTION EXAMPLE 2 was coloured violet, that of INVENTION EXAMPLE 3 was coloured yellow, those of INVENTION EXAMPLES 4 and 6 were coloured cyan, and that of INVENTION EXAMPLE was coloured red.

[0149] The viscosity of the flexographic inks was determined at 25° C. according to DIN 53211 using a DIN 4 cup by stirring the flexographic ink until a constant emptying time is measured. Standard conversion tables are used to convert the emptying times into dynamic viscosities (cSt) and a density of 1 is assumed in converting the dynamic viscosities values into mPa.s.

Flexographic Printing

[0150] The flexographic inks of INVENTION EXAMPLES 1 to 6 were printed using a RK Esiproof handtester from RK Print Coat Instruments Ltd, UK provided with a 140 cells/inch chrome-plated anilox drum.

[0151] The compositions of the printed layers as solids after drying are given in Table 4, together with the surface resistance of the layers and their optical densities as determined using a MacBeth™ RD918 SB with the colour filters given with the optical density values in Table 4.

	TABLE 4
	Invention Example nr
	1	2	3	4	5	6
wt % PEDOT/PSS	37.4	28.7	28.1	32.1	28.1	29.9
wt % binder	40.5	31.0	30.4	34.7	30.4	32.5
wt % pigment	—	23.3	24.9	14.2	24.9	19.9
wt % SURFYNOL ™	19.4	14.9	14.5	16.6	14.5	15.5
440
wt % X-50-860A	2.7	2.1	2.1	2.4	2.1	2.2
Surface resistance	10.5	8.2	10	6.7	6.6	6.1
[kΩ/square]
OD [Macbeth ™	—	0.65	0.72	0.52	0.62	0.67
RD918SB]		[Dgreen]	[Dblue]	[Dred]	[Dgreen ]	[Dred]

[0152] The surface resistance of the non-pigmented print produced with the flexographic ink of INVENTION EXAMPLE 1 was 10,500 Ω/square. Coloured prints with optical densities between 0.52 and 0.72 were obtained with the flexographic inks of INVENTION EXAMPLES 2 to 6 with surface resistances between 6100 and 8200 Ω/square. The prints exhibited excellent adhesion to the substrate, excellent solvent resistance and excellent water resistance.

INVENTION EXAMPLE 7

[0153] The non-pigmented flexographic ink of INVENTION EXAMPLE 7 was prepared by adding with mixing the ingredients in the quantities given in Table 5 to 450 g of a 3% by weight dispersion of PEDOT/PSS in water after mixing with the deionized water.

TABLE 5
3 wt % aqueous PEDOT/PSS dispersion [g]	450	13.5 (solids)
DW [g]	172.5	—
LATEX21 [g]	37.5	15.0 (solids)
LATEX22 [g]	14	4.2 (solids)
PD [g]	25	—
DEG-MME [g]	45	—
DEG [g]	70	—
SYNPERONIC ™ 13/6.55 (100%) [g]	10	10 (solids)
X-50-860A [g]	1.0	1.0 (solids)
isopropanol [g]	200	—
Total [g]:	1025	43.7 (solids)
wt % water in aqueous medium	60.1
Viscosity [mPa · s]	750

[0154] The viscosity of the flexographic inks was determined at 25° C. according to DIN 53211 using a DIN 4 cup by stirring the flexographic ink until a constant emptying time is measured. Standard conversion tables are used to convert the emptying times into dynamic viscosities (cSt) and a density of 1 is assumed in converting the dynamic viscosities values into mPa.s.

Flexographic Printing

[0155] The flexographic inks of INVENTION EXAMPLE 7 was printed on different supports using a RK Esiproof handtester from RK Print Coat Instruments Ltd, UK provided with a 140 cells/inch chrome-lated anilox drum. The compositions of the printed layers as solids after drying are given in Table 6, together with the surface resistance of the layers and their optical densities in reflection as determined using a MacBeth™ RD918 SB densitometer with a visible filter or in transmission as determined using a MacBeth™ TR904 densitometer with an ortho filter.

[0156] The flexographic ink of INVENTION EXAMPLE 7 exhibited excellent or very good wetting behaviour on all eight substrates investigated, six non-porous (substrates 1 to 6) and two porous (substrates 7 and 8). The surface resistances observed varied strongly with support, markedly higher surface resistances being observed with substrates 3 and 5: cellulose triacetate film and TRANSPAREX™ film.

	TABLE 6
	Invention Example nr 7
substrate nr	1	2	3	4	5	6	7	8
wt % PEDOT/	30.9
PSS
wt % binder	43.9
wt % pigment	—
wt %	22.9
SYNPERONIC ™
13/6.55
wt % X-50-860A	2.3
Surface resistance	6.5	12.8	150	9.7	160	5.9	5.4	1.2
[kΩ/square]
wetting behaviour	excel-	very	excel-	excel-	very	excel-	very	excel-
	lent	good	lent	lent	good	lent	good	lent
adhesion	excel-	excel-	excel-	excel-	excel-	excel-	excel-	excel-
	lent	lent	lent	lent	lent	lent	lent	lent
overprintability	excel-	excel-	—	—	—	—	—	—
	lent	lent
OD [MacBeth ™	<0.01	—	<0.01	<0.01	<0.01	<0.01	—	—
TD904]
OD [MacBeth ™	—	0.07	—	—	—	—	0.18	0.09
RD918SB]

[0157] Upon coating substrate 2 twice with intermediate drying the surface resistance decreased from 12,800 to just below 5,000 Ω/square.

INVENTION EXAMPLES 8 to 19

[0158] The non-pigmented flexographic ink of INVENTION EXAMPLES 8 to 19 were prepared by adding with mixing the ingredients in the quantities given in Table 7 to 45 g of a 3% by weight dispersion of PEDOT/PSS in water after mixing with the deionized water.

[0159] The viscosity of the flexographic inks was determined at 25° C. according to DIN 53211 using a DIN 4 cup by stirring the flexographic ink until a constant emptying time is measured. Standard conversion tables were used to convert the emptying times into dynamic viscosities (cSt) and a density of 1 was assumed in converting the dynamic viscosities values into mpa.s.

	TABLE 7
	Invention Example nr
	8	9	10	11	12	13
3% aq. PEDOT/PSS disp. [g]	45	45	45	45	45	45
DW [g]	24.2	11.7	24.2	11.7	24.2	11.7
LATEX14 [g]	1.8	1.8	1.8	1.8	1.8	1.8
LATEX22 [g]	1.4	1.4	1.4	1.4	1.4	1.4
PD [g]	2.5	2.5	2.5	2.5	2.5	2.5
DEG-MME [g]	4.5	4.5	4.5	4.5	4.5	4.5
DEG [g]	7.0	7.0	7.0	7.0	7.0	7.0
ZONYL ™ FSO100 [g]	1.05	1.05	1.05	1.05	1.05	1.05
X50-860A [g]	0.1	0.1	0.1	0.1	0.1	0.1
isopropanol [g]	12.5	25	—	—	—	—
n-propanol [g]	—	—	12.5	25	—	—
isobutanol [g]	—	—	—	—	12.5	25
	100.05	100.05	100.05	100.05	100.05	100.05
wt % water in aqueous medium	68.4	53.5	68.4	53.5	68.4	53.5
viscosity [mPa · s]	230	700	300	600	230	125
Invention Example nr	14	15	16	17	18	19
3% aq. PEDOT/PSS disp. [g]	45	45	45	45	45	45
DW [g]	24.2	11.7	24.2	11.7	11.5	11.4
LATEX14 [g]	1.8	1.8	1.8	1.8	1.8	1.8
LATEX22 [g]	1.4	1.4	1.4	1.4	1.4	1.4
PD [g]	2.5	2.5	2.5	2.5	2.5	2.5
DEG-MME [g]	4.5	4.5	4.5	4.5	4.5	4.5
DEG [g]	7.0	7.0	7.0	7.0	7.0	7.0
ZONYL ™ FSO100 [g]	1.05	1.05	1.05	1.05	1.05	1.05
ascorbic acid [g]	—	—	—	—	0.15	0.3
X50-860A [g]	0.1	0.1	0.1	0.1	0.1	0.1
isopropanol [g]	—	—	—	—	25	25
ethanol [g]	12.5	25	—	—	—	—
methanol [g]	—	—	12.5	25	—	—
	100.05	100.05	100.05	100.05	100	100.05
wt % water in aqueous medium	68.4	53.5	68.4	53.5	53.3	53.2
viscosity [mPa · s]	210	600	175	325	325	325

Flexographic Printing

[0160] The flexographic inks of INVENTION EXAMPLES 8 to 19 were printed on substrate 2 using a RK Esiproof handtester from RK Print Coat Instruments Ltd, UK provided with a 140 cells/inch chrome-plated anilox drum.

[0161] The compositions of the printed layers as solids after drying are given in Table 8, together with the surface resistance of the layers and their optical densities as determined using a MacBeth™ RD918 SB with a visible filter. Table 8 also includes the surface resistances of several of the prints after 1, 2 and 7 days exposure to daylight.

	TABLE 8
	Invention Example nr
	8	9	10	11	12	13	14	15	16	17	18	19
wt % PEDOT/	34.1	34.1	34.1	34.1	34.1	34.1	34.1	34.1	34.1	34.1	32.8	31.7
PSS in layer
wt % binder	36.9	36.9	36.9	36.9	36.9	36.9	36.9	36.9	36.9	36.9	35.6	34.4
wt % pigment	—	—	—	—	—	—	—	—	—	—	—	—
wt % ZONYL ™ FSO100	26.5	26.5	26.5	26.5	26.5	26.5	26.5	26.5	26.5	26.5	25.5	24.6
wt % X-50-860A	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.4	2.3
wt % ascorbic acid	—	—	—	—	—	—	—	—	—	—	3.7	7.0
Initial surface	9.0	3.2	—	—	—	—	—	—	—	—	4.2	3.8
resistance
[kΩ/square]
Surface resistance	20.0	5.7	—	—	—	—	—	—	—	—	6.0	5.6
after 1d daylight
[kΩ/square]
Surface resistance	25.0	6.8	—	—	—	—	—	—	—	—	6.5	5.9
after 2d daylight
[kΩ/square]
Surface resistance	65.0	11.0	—	—	—	—	—	—	—	—	8.5	6.5
after 7d daylight
[kΩ/square]
R(after 7d daylight)/	7.22	3.44	—	—	—	—	—	—	—	—	2.02	1.71
R(initial)

[0162] Comparison of the R(after 7d daylight)/R(initial) value for prints produced with the flexographic inks of INVENTION EXAMPLES 8 and 9 show that higher dilution with isopropanol improved the stability of the prints to daylight exposure: 3.44 compared with 7.22. Comparison of the R(after 7d daylight)/R(initial) value for prints produced with the flexographic inks of INVENTION EXAMPLES 9, 18 and 19, shows that a further improvement in stability to daylight exposure could be obtained by incorporating ascorbic acid: 2.02 and 1.71 for prints containing 3.7 and 7.0% by weight ascorbic acid respectively compared with 3.44 for prints without ascorbic acid.

INVENTION EXAMPLES 20 to 31

[0163] The flexographic inks of INVENTION EXAMPLES 20 to 31 were prepared by adding with mixing the ingredients in the quantities given in Table 9 to 45 g of a 3% by weight dispersion of PEDOT/PSS in water after mixing with the deionized water.

[0164] The viscosity of the flexographic inks was determined at 25° C. according to DIN 53211 using a DIN 4 cup by stirring the flexographic ink until a constant emptying time is measured. Standard conversion tables were used to convert the emptying times into dynamic viscosities (cSt) and a density of 1 was assumed in converting the dynamic viscosities values into mPa.s.

	TABLE 9
	Invention Example nr
	20	21	22	23	24	25	26	27	28	29	30	31
3wt % aq. PEDOT/	45	45	45	45	45	45	45	45	45	45	45	45
PSS disp. [g]
DW [g]	18.3	17.3	16.3	10.3	16.3	10.3	17.5	15.3	15.1	5.5	17.3	14.3
LATEX21 [g]	3.75	3.75	3.75	3.75	3.75	3.75	3.75	3.75	3.75	3.75	3.75	3.75
LATEX22 [g]	1.4	1.4	1.4	1.4	1.4	1.4	1.4	1.4	1.4	1.4	1.4	1.4
PD [g]	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5
DEG-MME [g]	4.5	4.5	4.5	4.5	4.5	4.5	4.5	4.5	4.5	4.5	4.5	4.5
DEG [g]	7.0	7.0	7.0	7.0	7.0	7.0	7.0	7.0	7.0	7.0	7.0	7.0
NON03 [g]	0.4	1.6	—	—	—	—	—	—	—	—	—	—
AMP01 [g]	—	—	2.0	8.0	—	—	—	—	—	—	—	—
N0N04 (20%) [g]	—	—	—	—	2.0	8.0	—	—	—	—	—	—
NON05 (50%) [g]	—	—	—	—	—	—	0.8	3.2	—	—	—	—
AN01 (12.5%) [g]	—	—	—	—	—	—	—	—	3.2	12.8	—	—
AN02 [g]	—	—	—	—	—	—	—	—	—	—	1.0	4.0
X-50-860A [g]	0.1	0.1	0.1	0.1	0.1	0.1	0.1	0.1	0.1	0.1	0.1	0.1
Isopropanol [g]	20	20	20	20	20	20	20	20	20	20	20	20
Total [g]:	102.95	103.15	102.55	102.55	102.55	102.55	102.55	102.75	102.55	102.55	102.55	102.55
wt % water in aq.	65.7	65.4	65.0	62.7	65.6	65.2	65.6	65.2	65.6	65.2	65.6	65.0
medium
Viscosity [mPa · s]	300	375	225	<60	450	700	300	350	350	450	375	300

[0165] The flexographic inks of INVENTION EXAMPLES 20 to 31 all exhibited excellent wetting behaviour on porous and non-porous substrates.

INVENTION EXAMPLES 32 to 43

[0166] The flexographic inks of INVENTION EXAMPLES 32 to 43 were prepared by adding with mixing the ingredients in the quantities given in Table 10 to 45 g of a 3% by weight dispersion of PEDOT/PSS in water after mixing with the deionized water.

[0167] The viscosity of the flexographic inks was determined at 25° C. according to DIN 53211 using a DIN 4 cup by stirring the flexographic ink until a constant emptying time is measured. Standard conversion tables are used to convert the emptying times into dynamic viscosities (cSt) and a density of 1 is assumed in converting the dynamic viscosities values into mPa.s.

	TABLE 10
	Invention Example nr
	32	33	34	35	36	37	38	39	40	41	42	43
3wt % aq. PEDOT/	45	45	45	45	45	45	45	45	45	45	45	45
PSS disp. [g]
DW [g]	12.0	—	15.1	12.4	15.6	14.4	15.6	14.4	12.0	—	12.0	—
LATEX21 [g]	3.75	3.75	3.75	3.75	3.75	3.75	3.75	3.75	3.75	3.75	3.75	3.75
LATEX22 [g]	1.4	1.4	1.4	1.4	1.4	1.4	1.4	1.4	1.4	1.4	1.4	1.4
PD [g]	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5
DEG-MME [g]	4.5	4.5	4.5	4.5	4.5	4.5	4.5	4.5	4.5	4.5	4.5	4.5
DEG [g]	7.0	7.0	7.0	7.0	7.0	7.0	7.0	7.0	7.0	7.0	7.0	7.0
AN03 [g]	4.0	16.0	—	—	—	—	—	—	—	—	—	—
AN04 [g]	—	—	0.89	3.56	—	—	—	—	—	—	—	—
N0N02 [g]	—	—	—	—	0.4	1.6	—	—	—	—	—	—
NON06 [g]	—	—	—	—	—	—	0.4	1.6	—	—	—	—
AN05 (5%) [g]	—	—	—	—	—	—	—	—	4.0	16.0	—	—
AN06 (1.44%) [g]	—	—	—	—	—	—	—	—	—	—	4.0	16.0
X-50-860A [g]	0.1	0.1	0.1	0.1	0.1	0.1	0.1	0.1	0.1	0.1	0.1	0.1
Isopropanol [g]	20	20	20	20	20	20	20	20	20	20	20	20
Total [g]:	100.25	100.25	100.24	100.21	100.25	100.25	100.25	100.25	100.25	100.25	100.25	100.25
wt % water in aq.	64.9	64.9	64.8	64.3	64.8	64.3	64.8	64.3	64.8	64.6	64.9	64.8
medium
Viscosity [mPa · s]	>1250	800	400	250	350	500	500	500	600	500	450	500

[0168] The flexographic inks of INVENTION EXAMPLES 32 to 43 all exhibited excellent wetting behaviour on both porous and non-porous substrates.

[0169] The present invention may include any feature or combination of features disclosed herein either implicitly or explicitly or any generalisation thereof irrespective of whether it relates to the presently claimed invention. In view of the foregoing description it will be evident to a person skilled in the art that various modifications may be made within the scope of the invention.

Claims

1. A non-dye containing flexographic ink containing a polymer or copolymer of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge, a polyanion and a latex binder in an organic solvent or aqueous medium, characterized in that said polymer or copolymer of a 3,4-dialkoxythiophene is present in a concentration of at least 0.1% by weight in said ink and that said ink is capable of producing a colorimetrically additive transparent print.

2. Flexographic ink according to claim 1, wherein said polymer or copolymer of a 3,4-dialkoxythiophene is present in a concentration of at least 0.2% by weight in said ink.

3. Flexographic ink according to claim 1, wherein said flexographic ink further contains a water-miscible organic solvent which is selected from the group consisting of aliphatic alcohols, ketones, arenes, esters, glycol ethers, cyclic ethers and their mixtures.

4. Flexographic ink according to claim 1, wherein said flexographic ink further contains a di- or polyhydroxy- and/or carboxy groups or amide or lactam group containing organic compound.

5. Flexographic ink according to claim 3, wherein said di- or polyhydroxy- and/or carboxy groups or amide or lactam group containing organic compound is selected from the group consisting of 1,2-propandiol, propylene glycol, diethylene glycol, N-methyl pyrrolidinone and di(ethylene glycol)ethyl ether acetate.

6. Flexographic ink according to claim 1, wherein said flexographic ink further contains an aprotic compound with a dielectric constant ≧15.

7. Flexographic ink according to claim 1, wherein said flexographic ink further contains a pigment.

8. Flexographic ink according to claim 1, wherein said flexographic ink contains a non-Newtonian binder.

9. Flexographic ink according to claim 1, wherein said polymer or copolymer of a (3,4-dialkoxythiophene) is selected from the group consisting of: poly(3,4-methylenedioxy-thiophene), poly(3,4-methylenedioxythiophene) derivatives, poly(3,4-ethylenedioxythiophene), poly(3,4-ethylenedioxy-thiophene) derivatives, poly[3,4-(propylene-dioxy)thiophene], poly[3,4-(propylenedioxy)thiophene] derivatives, poly(3,4-butylenedioxythiophene), poly(3,4-butylenedioxythiophene) derivatives and copolymers therewith.

10. Flexographic ink according to claim 1, wherein said polyanion is poly(styrenesulfonate).

11. Flexographic ink according to claim 1, wherein said ink has a viscosity at 25° C. after stirring to constant viscosity of at least 130 mPa.s as measured according to DIN 53211.

12. Flexographic ink according to claim 1, wherein said flexographic ink has a pH between 1.5 and 5.5.

13. A method for preparing a non-dye containing flexographic ink, containing a polymer or copolymer of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge, a polyanion and a latex binder in an organic solvent or aqueous medium, characterized in that said polymer or copolymer of a 3,4-dialkoxythiophene is present in a concentration of at least 0.1% by weight in said ink and that said ink is capable of producing a colorimetrically additive transparent print, comprising the steps of: i) concentrating an aqueous dispersion of said polymer or copolymer of (3,4-dialkoxythiophene) and said polyanion; and iii) adding said latex binder.

14. Method according to claim 13, wherein said step of concentrating said aqueous dispersion of a polymer or copolymer of (3,4-dialkoxythiophene) and said polyanion is carried out by evaporation of water, evaporation of water after addition of at least one organic solvent or evaporation of water by freeze drying.

15. Method according to claim 14, wherein in the evaporation of water after addition of at least one organic solvent said evaporation of water is continued until the content of water therein is reduced by at least 65% by weight.

16. Method according to claim 14, wherein in the evaporation of water after addition of at least one organic solvent said evaporation of water is continued until the content of water therein is reduced by at least 80% by weight.

17. Method according to claim 14, wherein in the concentration of the aqueous polymer or copolymer of (3,4-dialkoxythiophene) and the polyanion the evaporation of water by freeze drying a redispersible or soluble product is prepared as a dry product or as a paste.

18. A flexographic printing process comprising the steps of: providing a non-dye containing flexographic ink, containing a polymer or copolymer of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge, a polyanion and a latex binder in an organic solvent or aqueous medium, characterized in that said polymer or copolymer of a 3,4-dialkoxythiophene is present in a concentration of at least 0.1% by weight in said ink and that said ink is capable of producing a colorimetrically additive transparent print, printing said printing ink on an optionally subbed substrate thereby producing a colorimetrically additive transparent print.

19. Flexographic printing process according to claim 18, wherein said support is a flexible substrate.

20. Flexographic printing process according to claim 18, wherein said substrate is paper, polymer film, glass or ceramic.

21. A non-dye containing flexographic ink containing at least 0.1% by weight of a polymer or copolymer of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge, a polyanion and a latex binder in a solvent or aqueous medium and said ink is capable of producing a colorimetrically additive transparent print obtainable by a method for preparing a non-dye containing flexographic ink, containing a polymer or copolymer of a 3,4-dialkoxythiophene in which the two alkoxy groups may be the same or different or together represent an optionally substituted oxy-alkylene-oxy bridge, a polyanion and a latex binder in an organic solvent or aqueous medium, characterized in that said polymer or copolymer of a 3,4-dialkoxythiophene is present in a concentration of at least 0.1% by weight in said ink and that said ink is capable of producing a colorimetrically additive transparent print, comprising the steps of: i) concentrating an aqueous dispersion is of said polymer or copolymer of (3,4-dialkoxythiophene) and said polyanion; and iii) adding said latex binder.