The present disclosure relates to a technique for manufacturing a float glass, and more particularly, to a float bath which allows easy temperature control according to an internal position, and a glass manufacturing apparatus and glass manufacturing method including the same.
Many kinds of flat glasses are being used in various fields like window panes, window screens of vehicles and mirrors. Such a flat glass may be manufactured in various ways. Among them, a representative method is a production method using a float method. For example, thin glass planes or glass films for TFT displays are frequently manufactured by the float method. The glass manufactured by the float method is called a float glass.
As shown in
In the float bath 10, a molten glass G having a lower viscosity than the molten metal M and lighter than the molten metal M by about ⅔ is successively supplied into the float bath 10 through an inlet thereof. In addition, the molten glass moves to the downstream of the float bath 10 while floating and spreading on the molten metal M. In this process, the molten glass nearly reaches an equivalent thickness according to its surface tension and gravity to form a glass strip or ribbon which is solidified to some extent. In the float bath 10, the thickness of a produced glass ribbon may be changed by adjusting or changing an amount of glass put through the inlet, a pulling speed determined by a rotation speed of rollers, a molding component such as top rollers installed in a float chamber, or the like.
Meanwhile, the molten glass ribbon formed in the float bath 10 as above is transferred to an annealing furnace by a roller 30 adjacent to the outlet of the float bath 10 and experiences an annealing process.
The float glass manufacturing method includes cyclic successive processes and may operate constantly without a cessation, which allows flat glasses to be manufactured for several years without a pause. For this reason, the float glass manufacturing method is in the limelight as a representative flat glass manufacturing method.
When manufacturing a float glass by using the float bath 10, temperature control in the float bath 10 is very important. In particular, since a molten metal M is contained in the float bath 10 and a molten glass G floats on the molten metal M, the inside of the float bath may be maintained in a high temperature state, for example 1300° C. to 600° C. In addition, since the molten glass on the molten metal spreads into a flat plate while progressing to the downstream of the float bath and should be solidified to some extent, the float bath 10 is configured so that its temperature gradually lowers from the upstream to the downstream.
As described above, the inside of the float bath 10 has a high temperature and may also have local temperature differences. In addition, since the float glass is successively formed, the internal temperature of the float bath 10 needs to be constantly controlled.
In general, the internal temperature of the float bath 10 may be controlled by a heater 20 and a cooler. Here, a plurality of heaters 20 may be provided at a loop portion 11 of the float bath 10 to supply heat into the float bath 10. In particular, the heaters 20 may supply different heat quantities individually or by group, so that a temperature difference is formed according to a location of the float bath 10. For example, the inside of the float bath 10 may be classified into a plurality of areas, namely control zones, and at least one heater 20 may be installed in each control zone to supply heat to the corresponding area.
However, in the case individual heaters 20 or individual heater groups give different heat quantities to form a temperature difference according to locations of the float bath 10, it is not easy to control temperature according to locations of the float bath 10. In particular, one of the most important factors which make it difficult to control temperature according to locations of the float bath 10 is heat transfer such as heat radiation transferred from another adjacent heater 20. For example, even though the inside of the float bath 10 is divided into several control zones and different heat quantities are supplied by heaters 20 installed in the control zones, a specific control zone may be supplied with heat not only from a heater 20 installed in the corresponding control zone but also from a heater 20 installed in another adjacent control zone.
Therefore, in the existing float bath 10, it is very difficult to control temperature according to locations of the float bath 10. In addition, if the temperature of the float bath 10 is not suitably controlled, a bad influence may be given to the quality of a glass, which may lower a glass production yield and increase manufacture time and costs.
The present disclosure is designed to solve the problems of the related art, and therefore the present disclosure is directed to providing a float bath which may allow easy temperature control according to positions, a glass manufacturing apparatus including the floating bath, and a glass manufacturing method using the float bath.
Other objects and advantages of the present disclosure will be understood by the following description and become more apparent from the embodiments of the present disclosure, which are set forth herein. It will also be apparent that objects and advantages of the present disclosure can be embodied easily by the means defined in claims and combinations thereof.
In one aspect of the present disclosure, there is provided a float bath, which includes a plurality of heaters provided at an upper portion of the float bath to supply heat into the float bath; and a shield provided between predetermined heaters among the plurality of heaters to block heat transfer therebetween.
Preferably, among the plurality of heaters, every one or more heaters may supply different heat quantities.
Also preferably, the shield may be provided between heaters which supply different heat quantities.
Also preferably, the shield may have an adjustable length in the vertical direction.
Also preferably, the shield has an adjustable angle in at least a part thereof.
Also preferably, the shield has a bent lower end.
Also preferably, the float bath may further include a temperature measuring unit for measuring an internal temperature of the float bath.
In another aspect of the present disclosure, there is also provided a glass manufacturing apparatus, which includes the float bath.
In another aspect of the present disclosure, there is also provided a glass manufacturing method, which manufactures a glass by using the float bath.
According to the present disclosure, an internal temperature of a float bath may be effectively controlled.
In particular, according to the present disclosure, it is possible to prevent any unnecessary heat from being transferred from a heater installed at another adjacent location. Therefore, it is easier to control temperature differently according to internal locations of the float bath.
For example, when an internal region of the float bath is divided into a plurality of areas, namely a plurality of control zones so that the control zones supply different heat quantities to form a temperature gradient according to locations of the float bath, the transfer of radiant heat from a heater installed in another control zone may be prevented or decreased.
Therefore, according to the present disclosure, it is easier to differentially control heat quantities supplied to a molten metal or molten glass according to locations. Therefore, according to the present disclosure, quality and yield of the float glass may be improved, and manufacture costs or time of the float glass may be reduced.
The accompanying drawings illustrate preferred embodiments of the present disclosure and, together with the foregoing disclosure, serve to provide further understanding of the technical spirit of the present disclosure. However, the present disclosure is not to be construed as being limited to the drawings in which:
Hereinafter, preferred embodiments of the present disclosure will be described in detail with reference to the accompanying drawings. Prior to the description, it should be understood that the terms used in the specification and the appended claims should not be construed as limited to general and dictionary meanings, but interpreted based on the meanings and concepts corresponding to technical aspects of the present disclosure on the basis of the principle that the inventor is allowed to define terms appropriately for the best explanation.
Therefore, the description proposed herein is just a preferable example for the purpose of illustrations only, not intended to limit the scope of the disclosure, so it should be understood that other equivalents and modifications could be made thereto without departing from the spirit and scope of the disclosure.
Referring to
The heater 110 supplies heat into the float bath 100 to control an internal temperature of the float bath 100. In particular, the heater 110 supplies suitable heat to a molten metal contained in the float bath 100 and a molten glass floating thereon.
The heater 110 may be provided at an upper side of the float bath 100 in consideration of several aspects such as good heat transfer into the float bath 100 and convenient installation. In other words, in the float bath 100, the heater 110 may be installed at a position spaced apart from an upper surface of the molten metal or the molten glass by a predetermined distance in the upper direction.
The heater 110 may be composed of a plurality of heaters 110 in order to supply heat to the entire inside of the float bath 100 and also form a temperature gradient to have local temperature differences. For example, several hundred or several thousand heaters 110 may be arranged at the upper portion of the float bath 100 to be spaced apart from each other on a single horizontal plane.
The shield 120 may be provided between predetermined heaters 110 among the plurality of heaters 110 provided in the float bath 100 to block heat transfer between them. In other words, the shield 120 may prevent or decrease any interference phenomenon caused by the transfer of radiant heat between heaters 110 located at both sides thereof.
For example, as shown in
In this case, the shield 120 may prevent or minimize the supply of heat from a heater 110 located in another area. In other words, the heat from the heater 110 located in the area a1 may be supplied to the molten glass located in the area b1, and the heat from heaters 110 located in the areas a2 to a4 may be blocked or reduced. For this, the float bath 100 according to an embodiment of the present disclosure may include the shield 120 between the area a1 and the area a2. Like this, in the present disclosure, the shield 120 may be provided between predetermined heaters 110 to prevent or decrease heat transfer through the shield 120.
Preferably, the plurality of heaters 110 provided at the float bath 100 may supply heat of different temperatures by every one or more heaters 110. At this time, the entire region of the float bath 100 is divided into a plurality of areas, namely control zones, and at least one heater 110 may be included in each control zone, so that heaters 110 in different control zones have different heat quantities.
In addition, in this case, the shield 120 may be provided between heaters 10 supplying heat of different temperatures. In other words, the shield 120 may be provided between control zones to which heat of different temperatures may be supplied, so that thermal interference between the control zones by the heaters 110 may be reduced.
Referring to
However, on occasions, the same power may yet be supplied to different control zones. For example, the heater 110 included in the control zone c4 and the heater 110 included in the control zone c5 may be supplied with the same power to generate the same heat quantity.
As described above, the heaters 110 provided at the float bath 100 may be classified into several control zones and supply different heat quantities, and in this case, the shield 120 may be provided between heaters 110 supplying different heat quantities. In other words, the shield 120 may be installed between every adjacent control zones. For example, in the embodiment of
Meanwhile, even though
Referring to
Each control zone may include at least one heater 110. Therefore, the control zones may be supplied with different heat quantities by means of heaters 110 included therein. In addition, the shield 120 may be installed between adjacent control zones. However, in order to avoid complication of the figure, a part of the shields 120 are designated by a reference symbol 120 in
As described above, if the shield 120 is provided between the control zones, it is possible to reduce thermal interference caused by the transfer of radiant heat between the control zones.
Therefore, in this embodiment, since temperature may be easily adjusted for each control zone, it is possible to precisely control temperature of the float bath 100, which may form an optimal temperature gradient suitable for manufacturing a float glass in the float bath 100.
Meanwhile, the configuration and number of the control zones and the shields 120 depicted in
Preferably, the shield 120 may have a plate shape.
As shown in
Referring to
If the lower end of the shield 120 moves to the upper portion of the float bath 100, in view of the heater 110, the vertical length of the shield 120 may be regarded as decreasing. In this case, the heat transfer blocking effect between the control zone c6 and the control zone c7 by the shield 120 may relatively deteriorate. Meanwhile, if the lower end of the shield 120 moves to the lower portion of the float bath 100, in view of the heater 110, the vertical length of the shield 120 may be regarded as increasing. In this case, the heat transfer blocking effect between the control zone c6 and the control zone c7 by the shield 120 may relatively increase.
In this embodiment, by adjusting the vertical length of the shield 120, the internal temperature of the float bath 100 may be controlled more easily.
For example, in order to further clarify a temperature difference between the control zone c6 and the control zone c7, the lower end of the shield 120 may be moved to the lower portion of the float bath 100, so that the vertical length of the shield 120 increases, thereby further blocking heat transfer between the control zone c7 and the control zone c6. At this time, radiant heat by the heaters 110 included in the control zone c6 may be more effectively prevented from transferring to the control zone c7, and also radiant heat by the heaters 110 included in the control zone c7 may be prevented effectively prevented from transferring to the control zone c6.
On the contrary, if a temperature difference between the control zone c6 and the control zone c7 is excessive or such a temperature difference is not needed, the vertical length of the shield 120 may be decreased so as to ensure good heat transfer between the control zone c7 and the control zone c6. For example, if the temperature of the control zone c6 is higher than that of the control zone c7 and the temperature of the control zone c7 needs to be raised, the lower end of the shield 120 may be moved upwards so that the heat from the heaters included in the control zone c6 is transferred to the control zone c7.
Referring to
For example, the angle between the vertical direction of the shield 120 and the surface of the molten glass may be a right angle. However, on occasions, the shield 120 may be inclined toward the control zone c8 or the control zone c9.
In this embodiment, a heat quantity supplied from the heater 110 to each control zone may be controlled by adjusting the angle of the shield 120. For example, as the shield 120 is inclined further to the control zone c8, it is possible to more effectively block the heat supplied from the heaters 110 included in the control zone c8 from transferring to the control zone c9. Moreover, it is also possible to more effectively block the heat supplied from the heaters 110 included in control zone c8 from transferring to the control zone c8. This is because the shield 120 inclined further to the control zone c8 may more effectively block paths of radiant heat supplied from the heaters 110 included in the control zone c8. Meanwhile, if the shield 120 is inclined toward the control zone c8 as described above, the radiant heat from the heaters 110 included in the control zone c9 may be more effectively supplied to the control zone c8.
Meanwhile, even though
As shown in
In this embodiment, due to the bent lower end, the heat transfer between control zones of the shield 120 may be more effectively blocked.
Referring to
Preferably, the float bath 100 according to the present disclosure may further include a temperature measuring unit.
The temperature measuring unit may measure an internal temperature of the float bath 100. In particular, the temperature measuring unit may measure a temperature of each area classified by the shield 120. For example, as in the embodiment of
In this case, the heater 110 may control a heat quantity supplied to a specific area according to the temperature measured by the temperature measuring unit. For example, if the temperature measuring unit measures that a specific control zone has a temperature lower than a criterion, the heater 110 included in the corresponding control zone may increase a supplied heat quantity so that the temperature of the corresponding control zone raises. On the contrary, if the temperature measuring unit measures that a specific control zone has a temperature higher than a criterion, the heater 110 included in the corresponding control zone may decrease a supplied heat quantity so that the temperature of the corresponding control zone lowers.
In this case, the float bath 100 according to the present disclosure may further include a control unit for controlling a heat quantity supplied by the heater 110 according to the temperature measured by the temperature measuring unit.
In the float bath 100 according to the present disclosure, the shield 120 may be made of various materials. Preferably, the shield 120 may be made of a material which is agreeably maintained and does not easily deform in an interior circumstance of the float bath 100 kept at a high temperature of, for example, 1300° C. to 600° C. For example, the shield 120 may be made of refractory material.
The float bath 100 may be included in a glass manufacturing apparatus and used for manufacturing a float glass. In other words, the float glass manufacturing apparatus according to the present disclosure may include the float bath 100 described above. In addition, the float glass manufacturing apparatus may further include a melting furnace for supplying a molten glass to the float bath 100, an annealing furnace for annealing a glass ribbon formed in the float bath 100 or the like, in addition to the float bath 100.
A glass manufacturing method according to the present disclosure manufactures a glass by using the float bath 100 described above.
In other words, the glass manufacturing method according to the present disclosure may include preparing a plurality of heaters 110 provided at the upper portion of a float bath 100 to supply heat into the float bath 100, and preparing a shield 120 between predetermined heaters 110 among the plurality of heaters 110 to block heat transfer between them.
In addition, the glass manufacturing method according to the present disclosure may further include supplying a molten glass to the float bath 100 and annealing a glass formed in the float bath 100.
The present disclosure has been described in detail. However, it should be understood that the detailed description and specific examples, while indicating preferred embodiments of the disclosure, are given by way of illustration only, since various changes and modifications within the spirit and scope of the disclosure will become apparent to those skilled in the art from this detailed description.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2012-0036720 | Apr 2012 | KR | national |
The present application is a continuation of International Application No. PCT/KR2013/002962 filed on Apr. 9, 2013, which claims priority to Korean Patent Application No. 10-2012-0036720 filed in the Republic of Korea on Apr. 9, 2012, the disclosures of which are incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3215516 | Pilkington | Nov 1965 | A |
| 3333936 | Warren | Aug 1967 | A |
| 3485617 | Lawrenson | Dec 1969 | A |
| 3520669 | Greenler | Jul 1970 | A |
| 3679389 | Kanai | Jul 1972 | A |
| 3809543 | Gaskell et al. | May 1974 | A |
| 3934994 | Muhlstadt et al. | Jan 1976 | A |
| 4217125 | Dickinson | Aug 1980 | A |
| 4319908 | Sensi | Mar 1982 | A |
| 4340411 | May | Jul 1982 | A |
| 4402786 | Little | Sep 1983 | A |
| 4693740 | Noiret | Sep 1987 | A |
| 5656052 | Boardman | Aug 1997 | A |
| 8448469 | Na et al. | May 2013 | B2 |
| 20070022783 | Ban | Feb 2007 | A1 |
| 20080282736 | Filippov et al. | Nov 2008 | A1 |
| 20100257900 | Yajima | Oct 2010 | A1 |
| 20110294645 | Kim et al. | Dec 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 688051 | Apr 1967 | BE |
| 2272958 | Dec 1975 | FR |
| 1074094 | Jun 1967 | GB |
| 59128222 | Jul 1984 | JP |
| 11-021137 | Jan 1999 | JP |
| 10-2010-0032379 | Mar 2010 | KR |
| 10-2010-0037990 | Apr 2010 | KR |
| 10-2011-0132143 | Dec 2011 | KR |
| Number | Date | Country | |
|---|---|---|---|
| 20140174130 A1 | Jun 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/KR2013/002962 | Apr 2013 | US |
| Child | 14189522 | US |