Flow agent-dispersant composition

Abstract

Flow agent-dispersant composition for ink systems and the like comprising montan wax having from 3 to 10% of lecithin uniformly dispersed therein and a process for forming the same.

Description

This invention relates to improved dispersant and flow agent wax compositions for inclusion in mixtures of finely divided solids materials in readily liquifiable vehicles and particularly to improved dispersant-flow wax compositions for inks such as carbon paper inks and the like and to a process for making the same.

BACKGROUND OF THE INVENTION

Certain vegetable waxes, such as carnauba or ouricury wax or certain mineral waxes, such as montan wax, both basic and modified, have long been conventionally utilized to impart highly beneficial hardness and oil retention properties to ink systems, such as carbon paper inks, as well as to enhance the dispersion of solid particulate matter in diverse products incorporating readily liquifiable carrier vehicles. The continually increasing price of such vegetable and mineral wax materials, coupled with the uncertainties attendant their common sources of supply, has forced manufacturers to utilize continually decreasing amounts thereof in carbon paper inks and similar materials for selective functioning as "flow waxes" to obtain satisfactory dispersion properties therein, with other and less expensive materials being substituted therefor to impart the desired hardness and oil retention properties to the product. Even in such reduced amounts, however, the material costs for such vegetable and mineral waxes have risen to such an extent as to pose serious economic problems for the manufacturers of carbon paper inks and similar products.

The problem is one of long standing. Prior efforts in the art have been directed to the provision of domestically available synthetic waxes that are possessed of at least some desirable flow agent properties. While such synthetic waxes have provided some advantageous flow agent properties, they have not, as yet, provided the highly beneficial hardness and oil retention properties that are normally required in inks and like products that include a normally solid but readily liquifiable carrier vehicle. Exemplary of the foregoing are the modified synthetic waxes disclosed in U.S. Pat. Nos. 2,890,124, 2,890,125 and 3,163,548. These synthetic waxes, unfortunately, have likewise been characterized by progressively increasing costs for the resultant product and such has operated to accentuate rather than to alleviate the basic problem.

A more recent synthetic wax base product is disclosed in U.S. Pat. No. 3,941,608. Here again however, continually increasing raw material and processing costs have resulted in progressively increasing costs for the resultant product.

Apart from the increasing cost factor as above noted, the resultant economically dictated utilization of increasing amounts of paraffin wax and other substitutes for the above named vegetable and mineral waxes has increased the likelihood of detrimental gelling of the ink systems and other products being formulated therefrom.

As noted above, montan waxes, of both the basic and modified type, have been long recognized as having the ability to impart beneficial hardness and oil retention properties to, as well as the ability to enhance the dispersion of solid particulate matter in, diverse products utilizing readily liquifiable carrier vehicles. Basic montan wax is a mineral wax, solvent extracted from lignite, and is made up of a complex mixture of high molecular esters of long-chain aliphatic acids and wax alcohols. Both basic montan wax and chemically treated or modified montan waxes are hard waxes of microcrystalline structure and are commercially available products.

SUMMARY OF THE INVENTION

This invention may be briefly described as a chemically modified montan wax that can be advantageously employed as a dispersant-flow agent wax composition for ink systems and particularly for carbon paper inks and to methods of forming the same. In its broader aspects, the chemically modified montan wax product is obtained by the reaction of a montan wax with lecithin. In a narrower aspect, the invention includes the provision of a lecithin modified montan wax containing from three to about ten percent of lecithin.

Among the advantages of the subject invention is the provision of an effective dispersant for finely divided solids in liquifiable carrier vehicles, such as ink systems and particularly in carbon paper inks, that has flow imparting properties superior to those of natural vegetable waxes such as carnauba and ouricury, and available montan waxes, and which, in addition to markedly reducing the hazards of detrimental gelling, can be made available at a fraction of the cost of any of the presently available dispersant materials conventionally employed as flow agents in such environments. A further advantage is the provision of a simple and economic method of forming such improved dispersant-flow agents characterized by significantly low operating temperatures and markedly reduced raw material costs as compared to those attendant presently available modified natural and synthetic wax dispersants of the type identified above. A still further advantage of this invention is the provision of an improved wax like dispersant and flow agent to beneficially enhance the properties of liquifiable carrier vehicles for diverse products and permit the use of fillers and lower cost wax materials therein.

The primary object of this invention is the provision of a lecithin modified montan wax dispersant-flow agent for ink systems and particularly for carbon paper inks.

A further object of this invention is the provision of an economic method of producing an improved lecithin modified dispersant-flow wax for carbon paper inks.

Other objects and advantages of the subject invention will become apparent from the following portions of this specification and appended claims which, in accord with the mandate of the patent statutes, discloses the principles of the invention as embodied in presently preferred chemically modified montan wax dispersant-flow agent products and a process for forming the same.

DETAILED DESCRIPTION OF THE INVENTION

As previously pointed out, montan wax is a natural mineral wax obtained by solvent extraction from lignite and is the base constituent of the improved product. Montan wax is a naturally occurring fossil hard wax made up of a variety of waxes and is a complex mixture of high molecular esters of long chain aliphatic acids and alcohols in association with small amounts of color intensive asphaltic resins. Montan wax is available in basic solvent extracted form and as modified by various chemical aftertreatments. A primary producer of montan waxes is the VEB Braunkohlenwerk "Gustav Sobottka" DDR-4256 Roblingen am See, GDR which produces and sells both basic montan wax and modified or chemically aftertreated montan waxes under the trademark ROMONTA. Another producer of montan waxes is the American Lignite Products Co. of Ione, California which produces and sells both basic and modified or chemically aftertreated montan waxes under the trademark ALPCO. Preferred montan waxes of both the basic or modified types for use in the practice of this invention include, by way of example, the following:

______________________________________ Saponification Solidification Value Acid Value Point (ASTM (ASTM (ASTMMontan Wax DF1389) D1386) F766)______________________________________ROMONTA 85-100 27-33 167-185.degree. F.(Standard)ROMONTA 76 85-95 14-20 172-181.degree. F.ROMONTA C 90-105 23-28 172-182.degree. F.ROMONTA 6715 92-102 23-28 174-183.degree. F.ALPCO 16 85-115 40-60 178-185.degree. F.(Standard)ALPCO 1600 85-115 22-30 178-186.degree. F.ALPCO 1650 23-28 179-188.degree. F.______________________________________

The modifier reactant is lecithin. Lecithin is a phosphoglyceride or phosphotide or, more usually, a mixture of the diglycerides of stearic, palmitic and oleic acids linked to the choline ester of phosphoric acid. One of the most common and abundant phosphoglycerides is choline phosphoglyceride which, when pure, is a waxy white solid. Lecithin is commercially produced from soya bean oil and usually consists of a mixture of phosphatides, largely phosphatidyl-choline; phosphatidyl-ethanolamine and phosphatidyl-serine.

The dispersant-flow agent wax embodying the subject invention is generally formed by heating the montan wax base constituent to a temperature between 220.degree. and 350.degree. F., preferably about 235.degree. F., in a mixing vessel with good agitation to render it highly fluid. Lecithin is slowly added, with continued agitation, in an amount in the range of from a minimum of about 3 to a maximum of about 10% by weight. If desired, the lecithin can be incrementally added to the molten montan wax. After lecithin addition has been completed the reaction, under continued agitation, is continued for at least one hour. After the reaction has been completed, the improved dispersant-flow agent in the nature of a lecithin modified montan wax may be flaked, prilled or otherwise cooled and mechanically processed to desired form.

By way of further example, two formulations of carbon paper ink employing varying amounts of the improved dispersant-flow agent were formulated and their comparative viscosities measured through use of a No. 2 Zahn cup having a delivery aperture of predetermined size therein. The inks were all heated to 200.degree. F. and measured amounts thereof were introduced into the No. 2 Zahn cup. The time required to drain the cup, measured in seconds, is generally indicative of the relative viscosity of the particular carbon paper ink being tested. The lower the drain time period, the lower is the viscosity and vice versa. The two carbon paper ink formulations subjected to test and differing in the main wax vehicle were constituted as follows:

______________________________________Formula A Formula B______________________________________Montan Wax Constituent 6% Montan Wax Constituent 6%Paraffin type slack wax 42% Microcrystalline type 42%Petrolatum 15% slack wax100 second paraffin oil 12% Petrolatum 15%Carbon black 20% 100 second paraffin oil 12%Clay 5% Carbon black 20% Clay 5%______________________________________

The following viscosity tabulation clearly indicates the beneficial characteristics of lecithin modified montan waxes:

______________________________________Specific MontanWax Constituent Formula A Formula B______________________________________Alpco 16 (standard) no exit flow no exit flowAlpco 16 + 7% lecithin 43 seconds 60 seconds +Alpco 1600 no exit flow no exit flowAlpco 1600 + 7% lecithin 38 seconds 55 secondsAlpco 1650 29 seconds 45 secondsAlpco 1650 + 7% lecithin 23 seconds 32 secondsRomonta (Standard) no exit flow no exit flowRomonta + 7% lecithin 43 seconds 60 seconds +Romonta 6715 38 seconds 60 seconds +Romonta 6715 + 7% lecithin 30 seconds 55 secondsRomonta 76 33 seconds 47 secondsRomonta 76 + 7% lecithin 20 seconds 22 secondsRomonta C 27 seconds 45 secondsRomonta C + 7% lecithin 18 seconds 21 seconds______________________________________

As will be apparent from the foregoing, the utilization of the lecithin modified montan wax has, in every instance, resulted in a marked decrease in the viscosity of the carbon paper ink at 200.degree. F.

Beneficial properties derived from the use of the lecithin modified wax montan waxes have generally been obtained where the percentage of lecithin has varied between about three up to about ten percent by weight. A preferred percentage range for lecithin content is about 5 to 8% and optimum results appear to be obtained where the lecithin percentage is about seven percent. Lecithin addition of as little as 3 percent clearly improves the product, while lecithin additions of over ten percent do not appear to further markedly improve the viscosity and also may result in adverse effects on the hardness and oil retention characteristics of the finished product.

Generally indicative of the foregoing are the following viscosity values with variations in lecithin content in the Formula A composition utilizing Romonta C wax as the basic montan wax constituent:

______________________________________Romonta C 27 sec.Romonta C + 3% lecithin 29Romonta C + 5% lecithin 25Romonta C + 7% lecithin 18Romonta C + 10% lecithin 18______________________________________

Further examples of viscosity reduction through lecithin addition to montan waxes, again employing the No. 2 Zahn cup and 200.degree. F. wax, have been attained as follows:

______________________________________ LecithinWax 0% 3% 7% 10%______________________________________Alpco 1650 45 40 32 31Romonta 6715 no flow 60 55 54Romonta 76 47 38 22 23______________________________________

In general, it appears that the amount of lecithin to be used is dependent, at least in part, upon the nature of the ink vehicle and the amount of pigment being utilized. Ink formulations with reduced pigment content appear to require less lecithin with permitted usage of a harder wax base. If larger amounts of pigment than that specified in Formula B are employed in the ink formulation, increased percentage of lecithin and/or increased percentage of montan wax constituent would appear to be required.

A further carbon black ink identified as Formula C, and comprising

______________________________________Montan Wax Constituent 5%Carnauba Wax 2%Slack Wax 56%70 Sec. Paraffin Oil 12%Carbon Black 20%Clay 5%______________________________________ was made up in five samples that included the montan wax constituent as follows: ______________________________________Sample #1 Romonta CSample #2 Alpco 1650Sample #3 Romonta C + 7% lecithinSample #4 Romonta C + 7% lecithinSample #5 Romonta C + 7% lecithin______________________________________

These samples were subjected to the above described viscosity testing under various aging conditions without agitation with the following results:

______________________________________Aging #1 #2 #3 #4 #5______________________________________Initial 40 44 23 22 20 1 Hour 42 52 30 33 30 2 Hours 42 52 32 34 37 4 Hours 43 over 60 29 43 3924 Hours 45 over 60 38 45 40______________________________________

It appears from the above that the lecithin modified samples have generally improved aging qualities or stability, which facilitates the usage thereof in the commercial fabrication of diverse products.

It has been found that reaction time and temperature may be varied somewhat for different montan wax base constituents. By way of specific example, 465 grams of Romonta Type C wax having the typical specification:

______________________________________melting point .degree.F. 172-181acid value 22-28saponification value 92-110specific gravity @ 77.degree. F. 1.00______________________________________ was heated in an agitated vessel to about 235.degree. F. After the montan wax reached 235.degree. F., 35 grams of Archer Daniels Midland lecithin was added and the reaction was allowed to proceed for at least 30 minutes under continuing agitation. The molten material was then cooled into the desired form. The resultant lecithin modified wax had the following properties: ______________________________________melting point .degree.F. 175-185acid value 8-14saponification value 78-86specific gravity @ 77.degree. F. 1.08______________________________________

As further illustrative of reaction temperature criticality, a fourth carbon black ink formulation constituted of

______________________________________Formula D______________________________________Montan Wax Constituent 5%Carnauba Wax 2%Slack Wax #3 41%Petrolatum 15%120 sec paraffin oil 12%Carbon black 20%Clay 5%______________________________________ was made up in five samples with the montan wax constituent as follows: ______________________________________Sample 1 Alpco 1650Sample 2 Romonta 76 + 7% lecithin reacted at 300.degree. F.Sample 3 Romonta 76 + 7% lecithin reacted at 275.degree. F.Sample 4 Romonta 76 + 7% lecithin reacted at 235.degree. F.Sample 5 Romonta C + 7% lecithin reacted at 235.degree. F.______________________________________

These samples were subjected to the above described viscosity test under various aging conditions without agitation with the following results:

______________________________________Aging #1 #2 #3 #4 #5______________________________________Initial 26 27 28 20 1 Hour 48 27 33 35 24 2 Hours 50 29 35 38 26 4 Hours 52 29 36 42 2724 Hours 55 32 38 47 29______________________________________

The herein described lecithin modified montan wax products maintain or improve the properties of montan wax with respect to hardness and oil retention and greatly enhances the flow and dispersion properties thereof. While the contemplated principle use of this product will be in the carbon paper industry, the lecithin modified montan wax product may well have significant application in other normally solid but liquifiable carrier vehicle products which require pigment dispersion. Some possible applications would be in printing inks, carbon ribbon inks, plastics, paint and polishes.

Claims

1. A discrete lecithin modified montan wax dispersant-flow agent product for inclusion in mixtures of finely divided solid materials in liquifiable carrier vehicles to enhance the hardness and oil retention properties thereof, comprising the solidified residue of the reaction product of reagents consisting essentially of agitated molten montan wax with 3 to 10% of introduced lecithin dispersed therewithin.

2. A dispersant-flow agent product as set forth in claim 1 with 5 to 8% of introduced lecithin therewithin.

3. A dispersant-flow agent product as set forth in claim 1 with about 8% of introduced lecithin therewithin.

4. A dispersant-flow agent product as set forth in claim 1 wherein said montan wax has a solidification point of between 165.degree. and 190.degree. F.; an acid value of between 5 and 80 and a saponification value of between 75 and 125.

5. A dispersant-flow agent product as set forth in claim 4 with about 5 to 8% of introduced lecithin therewithin.

6. A method of forming an improved, lecithin modified montan wax dispersant-flow agent product for inclusion in mixtures of finely divided solid materials in liquifiable carrier vehicles to enhance the hardness and oil retention properties thereof, consisting essentially of the steps of

maintaining montan wax in a liquid condition at a temperature between 220.degree. and 350.degree. F. with continuous agitation thereof,

adding from 3 to 10% of lecithin to said continuously agitated montan wax; and

continuously agitating and maintaining the temperature of said liquified intermixture within said temperature range of 220.degree. and 350.degree. F. during lecithin addition and thereafter for a period of time sufficient to permit interreaction of the added lecithin with said montan wax,

whereby said lecithin modified montan wax dispersant-flow agent product is a reaction product from reagents consisting essentially of lecithin and said montan wax.

7. A method as set forth in claim 6 wherein the temperature of said liquid montan wax is maintained within said stated range and at about 235.degree. F.

8. A method as set forth in claim 6 wherein said lecithin is slowly added to the liquified and continuously agitated montan wax.

9. A dispersant-flow agent product that results from the method of claim 6.