Patent Grant
10689304
This application is the National Stage of International Application No. PCT/EP2014/075848, filed on Nov. 27, 2014, entitled FLOWABLE CONCRETE WITH SECONDARY ACCELERATOR, which claims priority to and the benefit of Great Britain Patent Application No. 1320942.4 filed on Nov. 27, 2013. The entire disclosure of both of the above documents are hereby incorporated by reference in their entirety.
This invention relates to an accelerator for flowable concrete or mortar, particularly but not exclusively for sprayable concrete and flowable grout, particularly backfill grout. This invention also relates to a method of producing flowable concrete.
Fast setting and early strength development are important requirements for sprayable concrete. For example, as applied to a rock surface in a tunnel and for backfill grouts, particularly as used to fill a void created by a tunnel boring machine (TBM).
Alkali-free accelerators have been added to the spray nozzle of sprayed concrete equipment immediately before the concrete is applied to a rock substrate. Examples are disclosed in WO99/18045, WO05/028398 and WO08/006410. Aqueous sodium silicate, commonly called water glass, has been added to backfill grout shortly before it is pumped into a void. Alkali carbonates have been used to shorten the setting time and to speed up strength development. However, alkali carbonates decompose when added to weakly acidic alkali free accelerators. Addition of carbonate to silicates causes precipitation of silica gel.
According to a first aspect of the present invention, a concrete, mortar or grout formulation comprises two separate components:
1. a concrete mixture comprising:
2. a main accelerator mixture comprising:
The concrete composition may comprise a typical concrete mix as used for sprayable concrete or shot mortar applications, generally consisting of cement and aggregates, plus fillers and other components such as superplasicisers or other concrete admixtures and water. The sprayable concrete or shot mortar composition may be conveniently referred to as flowable concrete compositions.
The alkali carbonate serves as a secondary accelerator and may be selected from the group consisting of potassium carbonate, sodium carbonate, or mixtures thereof. Hydrated or anhydrous salts may be employed. Use of potassium carbonate is preferred. Lithium carbonate or ammonium carbonate may also be used.
The amount of alkali carbonate by dry weight of the cement component of the concrete composition may be from 0.1% to 2%, preferably 0.2% to 1.5%, more preferably 0.25% to 0.8%, most preferably 0.35% to 0.4% by dry weight.
The carbonate may be added as an aqueous solution, for example, as 5-50% solution.
Percentages, ratios and other proportions used in the specification are by dry weight unless indicated otherwise. Percentages and other proportions are selected from any ranges quoted to total 100%.
The retarder serves to maintain flowability of the concrete or mortar mixture before combination with the main accelerator and application to a substrate. The retarder may be selected from materials used as conventional retarders.
Preferred retarders are selected from:
Hydroxycarboxylic acids are particularly preferred.
The components of the concrete mixture are preferably selected so that the mixture is not acidic, having a pH greater than about pH 7. A preferred pH is within the range of about pH 7 to about pH 14. A non-acidic mixture is preferred to prevent decomposition of the carbonate.
In preferred embodiments, the ratio of the carbonate to retarder may be in the range of about 4:1 to about 1:1, preferably about 3:1 to about 1.5:1, more preferably about 2.2:1 by weight.
A wide range of accelerator components may be employed in sprayed concrete and grout formulations as the main accelerator. Non-alkaline accelerators containing wholly or partially aluminium sulphate are preferred, for example, Mapequick AF 2000, TamShot 90AF or TamShot 100AF. Non-alkaline accelerators may also contain aluminium hydroxide, carboxylic acids, phosphoric acids, alkanolamines, stabilisers such as sepiolite and water.
Sodium silicate accelerators are preferred for backfill grout applications and may also be used for sprayed concrete applications.
According to a second aspect of the present invention, a method of applying a concrete, mortar or grout composition comprises the steps of:
providing a mixture comprising alkali carbonate and retarder;
adding the mixture to a concrete mixture to provide a cementitous composition comprising;
combining the concrete mixture and accelerator component to initiate curing of the concrete composition;
immediately applying the concrete composition to a substrate; and
allowing the concrete composition to cure.
The main accelerator is typically supplied to the spray head using a separate feed.
The present invention confers several advantages. Combination of the alkali carbonate and retarder prevents activation of the carbonate as secondary accelerator. The carbonate and retarder may be combined before addition of the concrete. Alternatively, retarder may be added to the concrete followed by addition of the carbonate.
The applied concrete or grout has an excellent set time and early strength characteristics in comparison to compositions which do not include carbonate in accordance with this invention.
For sprayable concrete an early strength of 1 MPa or higher may be achieved after one hour. This is important for such applications as tunnelling.
The composition and method of the present invention facilitate use of blended cements which may contain supplementary materials selected from: fly ash; ground granulated blast furnace slag (GGBS) or silica fume or mixtures thereof. For example, up to 20% fly ash may be employed. In such an application the early strength provided by the cement needs to be increased due to the less reactive supplementary material.
A further advantage is that the secondary accelerator does not need to be supplied to the spray head using a separate feed, so that modification of existing spray equipment is not necessary.
The invention is further described by means of examples, but not in any imitative sense, with reference to the accompanying tables, of which:
Table 1 shows compressive strength values versus time for two sprayed concrete compositions; and
Table 2 shows compressive strength values after 2 hours for two TBM backfill grouts.
Table 1: Shows the effect of a secondary accelerator on early age compressive strength of a sprayed concrete measured according to standard test methods used in-situ.
The concrete used was, Norwegian sprayed concrete mix design with 480 kg CEM II per m3 concrete.
The retarder referred to was a standard ‘Consistence control admixture’ meeting EN 934-5, and is a blend of citric acid and PBTC. The retarder including a secondary accelerator was the same retarder made slightly alkaline using sodium hydroxide and with an additional portion of potassium carbonate.
Table 2: shows the effect of a secondary accelerator on the compressive strength of a two-component TBM backfill grout two hours after mixing component 1 (cementitious mixture) and component 2 (sodium silicate accelerator).
The measurements were performed according to standard test methods used in-situ. The weights referred to are kg per m3 of hardened material. The water content is not shown. The retarder referred to is a standard sugar/gluconate retarder used for backfill grouts, while the retarder incl. a secondary accelerator is the same retarder with an additional portion of potassium carbonate.
The difference in cement and sodium silicate content (the two most costly ingredients in TBM backfill grouts) illustrates the economic gain obtained by the secondary accelerator.
| Number | Date | Country | Kind |
|---|---|---|---|
| 1320942.4 | Nov 2013 | GB | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2014/075848 | 11/27/2014 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2015/078985 | 6/4/2015 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4904503 | Hilton et al. | Feb 1990 | A |
| 20030106464 | Yamashita | Jun 2003 | A1 |
| 20120227630 | Gray | Sep 2012 | A1 |
| Number | Date | Country |
|---|---|---|
| 0508158 | Oct 1992 | EP |
| 0769482 | Apr 1997 | EP |
| 0128955 | Apr 2001 | WO |
| Entry |
|---|
| International Searching Authority, “Search Report & Written Opinion.” issued in connection with International Patent Application No. PCT/EP2014/075848, dated Mar. 23, 2015, 13 pages. |
| Jennifer A. Grubb, et al., Testing pH of Concrete Need for a standard procedure, Concrete international, Apr. 2007, pp. 76-83. |
| EFNARC, European Specification for Sprayed Concrete Guidelines for Specifiers and Contractors, 1999, 35 pages. |
| EFNARC, European Specification for Sprayed Concrete, 1996, 35 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20170008811 A1 | Jan 2017 | US |