Fluid activated disintegrating metal system

Information

  • Patent Grant
  • 11613952
  • Patent Number
    11,613,952
  • Date Filed
    Thursday, December 17, 2020
    3 years ago
  • Date Issued
    Tuesday, March 28, 2023
    a year ago
Abstract
An engineered composite system designed to be passive or inert under one set of conditions, but becomes active when exposed to a second set of conditions. This system can include a dissolving or disintegrating core, and a surface coating that has higher strength or which only dissolves under certain temperature and pH conditions, or in selected fluids. These reactive materials are useful for oil and gas completions and well stimulation processes, enhanced oil and gas recovery operations, as well as in defensive and mining applications requiring high energy density and good mechanical properties, but which can be stored and used for long periods of time without degradation.
Description
FIELD OF THE INVENTION

The present invention relates to the formation of disintegrating components and materials that can be stored indefinitely or near indefinitely unless activated. The present invention also relates to the production of a reactive composite having controlled reaction kinetics catalyzed by an external stimulus. The invention further relates to a reactive composite system that is inert unless initiated by a certain temperature, pH, and/or other external stimulus after, which it disintegrates in a controlled and repeatable manner.


BACKGROUND OF THE INVENTION

Reactive materials, which dissolve or corrode when exposed to acid, salt, or other wellbore conditions, have been proposed for some time. Generally, these consist of materials that are engineered to dissolve or corrode. Dissolving polymers have been disclosed and are also used extensively in the pharmaceutical industry for controlled-release drugs. In addition, reactive metal matrix composites have been proposed for use in disintegrating metallic systems, primarily consisting of magnesium-graphite systems, but also magnesium-calcium and other material systems that do not passivate and hence corrode in a rapid manner when in contact with a cathode material, such as graphite or iron.


While some of these systems have enjoyed modest success in reducing well completion costs, they have significant drawbacks, including limited strength and poor reliability, Ideally, components could be used, stored, and handled for long periods of time prior to use and, once activated, can undergo highly reliable disintegration or some other action.


SUMMARY OF THE INVENTION

The present invention relates to the formation of disintegrating components and materials that can be stored for long periods of time (e.g., at least a month, at least a year, etc.) unless activated. The present invention also relates to the production of a reactive composite having controlled reaction kinetics that can be catalyzed by an external stimulus. The invention further relates to a reactive composite system that is inert or essentially inert unless initiated by a certain temperature, pH, and/or other external stimulus after which it disintegrates in a controlled and repeatable manner. In one non-limiting application of the present invention, the components of the present invention can be used in the forming of wells used in, but not limited to, the oil and gas fracking industry. During the formation of wells, various metal components used to form the well are left in the well. These components must either be removed from the well or destroyed before the well can be fully and/or properly operational. The present invention is directed to components that can be used during the well forming operation and, once the component has completed its intended used, the component can be caused to disintegrate and/or fracture, thus sufficiently removing and/or fracturing the component so that the well can be fully and/or properly operational.


In one non-limiting aspect of the present invention relates to a hierarchically-designed component or system that includes a core and a surface which are designed to react and/or activate under different conditions. The core material is designed to have a high reaction rate that disintegrates over a period of 0.001 minutes to 100 hours (e.g., 0.001 min., 0.0011 min., 0.0012 min. . . . 99.99998 hours, 99.99999 hours, 100 hours, and all time values and ranges therebetween), and typically 30 minutes to 100 hours when exposed to certain environments (e.g., saltwater, electrolyte solutions, water, air, electromagnetic waves, sound waves, etc.). The core is typically designed to generate heat when exposed to various environments (e.g., saltwater, electrolyte solutions, water, air, electromagnetic waves, sound waves, etc.). The core can be formed of one or more layers. The shape of the core is non-limiting. The core is partially or fully surrounded by one or more surface or protective layers that inhibits or prevents the core from reacting and/or disintegrating until a desired time or event. The one or more surfaces or protective layers are designed to be inert unless exposed to an activation conditions such as, but not limited to, temperature, electromagnetic waves, sound waves, certain chemicals, and/or pH. Once the one or more surface or protective layers are removed and/or breached, the core material is activated to cause it to dissolve, corrode, react, fracture, etc. when exposed to certain surrounding conditions. For example, in a well application, the component is partially or fully submersed in a liquid environment that commonly includes water and/or saltwater/electrolytes. The core can be designed to dissolve, corrode, react, fracture, etc. when exposed to the water and/or to saltwater/electrolytes (e.g., HCl, KCl, CaCl2, CaBr2, ZnBr2, brine solutions) in the well once the one or more surface or protective layers about the core are removed and/or breached, thereby causing the component to dissolve or disintegrate in the well. The one or more surface or protective layers can also or alternatively be used to provide structural strength to the hierarchically-designed component.


In another non-limiting aspect of the present invention, the hierarchically-designed component or system can include one or more outer surface or protective layers and a core that is formed of two or more layers. Each layer can have a different function in the component or system; however, this is not required. In one non-limiting configuration, the component or system can include a surface or protective layer that encapsulates a core which is formed of at least two layers. In such an arrangement, the inner layer of the core can be a syntactic or very low-density core; the layer about the inner core layer can be a disintegrating high-strength functional layer; and the surface or protective layer is one or more layers that function as a surface modification layer and/or treatment which is inert unless activated.


In still another non-limiting aspect of the present invention, there is provided a surface-inhibited multilayer, multifunctional component comprising (a) a primary or core unit which includes one or more selected properties of density, dissolution rate, disintegration rate, reaction rate, strength; (b) a reactive surface layer having a complimentary set of properties of one or more of strength, temperature-dependent solubility, pH solubility, and density; and wherein the core unit and surface layer create an inhibited system that is relatively inert until exposed to an initial condition, after which it is activated. In one non-limiting embodiment, at least 70 weight percent of the core includes a core material selected from the group consisting of a metal, a metal alloy or a metal composite, typically at least 90 weight percent of the core includes a core material selected from the group consisting of a metal, a metal alloy or a metal composite, more typically at least 95 weight percent of the core includes a core material selected from the group consisting of a metal, a metal alloy or a metal composite, and even more typically 100 weight percent of the core includes a core material selected from the group consisting of a metal, a metal alloy or a metal composite. The core can be a magnesium, magnesium alloy or magnesium composite having a dissolution rate in salt-containing water of 0.1-100 mm/hr (e.g., 0.1 mm/hr, 0.101 mm/hr, 0.102 mm/hr 99.998 mm/hr, 99.999 mm/hr, 100 min/hr and all dissolution values and ranges therebetween) at 100-300° F. (and all temperature values and ranges therebetween). When the core is formed of magnesium, the core includes at least 99 wt % magnesium, and typically at least 99.5 wt % magnesium. When the core is formed of a magnesium alloy, the magnesium content of the magnesium alloy is at least 30 wt %, typically greater than 50%, and more typically at least about 70%. The metals that can be included in the magnesium alloy can include, but are not limited to, aluminum, calcium, lithium, manganese, rare earth metal, silicon, SiC, yttrium, zirconium and/or zinc. As can be appreciated, the core can be formed of other metals and/or non-metals that react, corrode, dissolve or disintegrate at a rate of 0.1-100 min/hr at 100-300° F. in water or salt water. Non-limiting examples of metals or metal alloys other than magnesium that can be used include aluminum alloys (e.g., aluminum alloys including 75+% aluminum and one or more of bismuth, copper, gallium, magnesium, indium, silicon, tin, and/or zinc); calcium; Ca—Mg, Ca—Al; and Ca—Zn. The core can be formulated and/or designed to be relatively insoluble at one temperature (e.g., room temperature: 60-80° F.), but highly soluble above a certain temperature (e.g., 100° F. or greater). Likewise, the core can also or alternatively be formulated and/or designed to be relatively insoluble in a solution having a certain pH (e.g., acidic pH, basic pH, etc.), but highly soluble in a solution having a different pH. When the component includes a surface coating, the surface coating can be designed to be relatively insoluble at a first temperature (e.g., room temperature, etc.), but highly soluble above or below above the first temperature. The surface layer can be formed of a metal coating (e.g., zinc, zinc alloy, etc.) and/or a polymer coating. In one non-limiting example, a surface layer that is relatively insoluble has a dissolution rate of about 0-0.1 mm/day (all dissolution values and ranges therebetween). In another non-limiting example, a surface layer that is highly soluble has a dissolution rate of 0.1 mm/hr or greater (e.g., 0.1 mm/hr 50 mm/hr and all dissolution values and ranges therebetween). Likewise, the surface layer (when used) can also or alternatively be formulated and/or designed to be relatively insoluble in a solution having a certain pH (e.g., acidic pH, basic pH, etc.), but highly soluble in a solution having a different pH. Non-limiting examples of polymers that can be used include ethylene-α-olefin copolymer; linear styrene-isoprene-styrene copolymer; ethylene-butadiene copolymer; styrene-butadiene-styrene copolymer; copolymer having styrene endblocks and ethylene-butadiene or ethylene-butene midblocks; copolymer of ethylene and alpha olefin; ethylene-octene copolymer; ethylene-hexene copolymer; ethylene-butene copolymer; ethylene-pentene copolymer; ethylene-butene copolymer; polyvinyl alcohol (PVA); and/or polyvinyl butyral (PVB). Also or alternatively, when the component includes a surface layer, the surface layer can include a chemistry that enables the surface layer to be an insoluble layer and then become a soluble layer when reacted with one or more compounds. For example, when the surface layer includes PVA, PVB, and/or similar polymers, the surface layer can be modified using a reversible chemical reaction to be insoluble in high-temperature water, acidic water solutions and/or salt water solutions, and which is soluble in high-temperature water, acidic water solutions and salt water solutions when a chemical trigger is applied. The reversible chemical reaction to make the surface layer insoluble can use trimethylsilyl group or similar silicon-containing organic chemicals. The reversible chemical reaction to make the surface layer soluble again can use ammonium fluoride or a similar compound. This non-limiting type of reversible chemistry is illustrated below:




embedded image


As set forth above, PVA, a compound that is soluble in water, can be made insoluble in water by reacting the PVA with trimethylsilyl group or some similar compound to form an insoluble compound in water. This reaction can take place prior to, during, and/or after the PVA (i.e., surface layer) is applied to the core of the component. The core of the component or a portion of the core of the component can be formed of a material (e.g., magnesium, magnesium alloy, etc.) that reacts, corrodes, dissolves, fractures, etc. when exposed to water. The modified surface layer that is insoluble to water protects the core from the water and inhibits or prevents the core from interacting with the water while the component is being used in the presence of water. Once the function or task of the component is completed, the component can be simply dissolved, corroded, fractured, disintegrated, etc. by exposing the water-insoluble surface layer to ammonium fluoride or a similar compound. Such exposure causes the surface layer to once again become a water-soluble compound. When the component is in the presence of water, the surface layer dissolves and the core is eventually exposed to the water. Upon exposure to water, the core dissolves, corrodes, fractures, disintegrates, etc. thereby causing the component to also dissolve, fracture, corrode, disintegrate, etc. The thickness of the surface layer and/or degree of solubility of the surface layer can be selected to control the rate at which the component dissolves, corrodes, fractures, disintegrates, etc. Likewise, the type of material used for the core and/or structure of the core can be selected to control the rate at which the component dissolves, corrodes, fractures, disintegrates, etc.


In yet another non-limiting aspect of the present invention, the surface layer can optionally be formed of a material that that resists degradation and/or dissolving when exposed to HCl (e.g., 0.1-3M HCl), KCl (e.g., 0.1-3M KCl), CaCl2 (e.g., 0.1-3M CaCl2), CaBr2 (e.g., 0.1-3M CaBr2), ZnBr2 (e.g., 0.1-3M ZnBr2), or brine solutions (1000-300,000 ppm) at a temperature of up to 60° F., but degrades and/or dissolves at a higher temperature of at least 100° F. In one specific surface layer, the surface layer resists HCl, KCl, and/or brine solutions up to 300° F., but degrades when a trigger (e.g., chemical ion source, fluorine ion source, etc.) is introduced to the solution in contact with the coating. One such coating is silicone-based coating (e.g., polymer-based siloxane two-part coating, 2-part epoxy-siloxane coating cured with amino silane, etc.). When the trigger is a fluorine ion source, the source of the fluorine ion can optionally be HF, ammonium fluoride, or other ionic compound where the fluorine ion will appear in a water solution.


In still yet another non-limiting aspect of the present invention, the surface layer can be applied to the core in a variety of ways (gas deposition, sublimation, solvent application, powder coating, plasma spraying, spraying, dipping, brushing, etc.).


In another non-limiting aspect of the present invention, the surface layer can be a polyurethane base system.


In still another non-limiting aspect of the present invention, the surface layer can be colored using dies for identification of the type of coating, type of core, type of trigger required, and/or type of hierarchically-designed component or system. In one non-limiting coating application process, an electrostatic coating and thermal curing using either a thermoset or thermoplastic polymer coating is used. Such a coating process is known in the industry as a type of “powder coating.”


In still yet another non-limiting aspect of the present invention, there is provided a hierarchically-designed component or system in the form of a low-density reactive hierarchically-designed component or system that includes (a) a core having a compression strength above about 5000 psig (e.g., 5000-30,000 psig and all values or ranges therebetween), but having a low density and tensile strength below 30,000 psig (e.g., magnesium composite, aluminum composite, manganese composite, zinc composite, etc.); and (b) a high-strength surface layer that has a higher density and higher strength than the core, but is also reactive (e.g., zinc or zinc alloy composite, etc.) and wherein the core and surface layer are designed to provide a high strength reactive system that also has an overall density of no more than about 5 glee (e.g., 0.5-5 g/cc and all values and ranges therebetween) and a tensile strength in the surface layer at least 32 ksi (e.g., 32-90 ksi and all values and rages therebetween). In one non-limiting configuration, the core has a density of about 0.9-1.4 g/cc. When the core is a magnesium composite, aluminum composite, manganese composite, or a zinc composite, the core can be formed of particles that are connected together by a binder. The core particles can include iron particles, carbon particles, tungsten particles, silicon particles, boron particles, tantalum particles, aluminum particles, zinc particles, iron particles, copper particles, molybdenum particles, silicon particles, ceramic particles, cobalt particles, nickel particles, rhenium particles, SiC particles, etc. (includes oxides and carbides thereof) having an average particle diameter size of about 5 to 50 microns (e.g., 5 microns, 5.01 microns, 5.02 microns . . . 49.98 microns, 49.99 microns, 50 microns) and any value or range therebetween, that are coated with about 0.3 to 3 microns coating thickness (e.g., 0.3 microns, 0.301 microns, 0.302 microns . . . 2.998 microns, 2.999 microns, 3 microns) and any value or range therebetween, of a matrix of magnesium, magnesium alloy, aluminum, aluminum alloy, manganese, manganese alloy, zinc and/or zinc alloy. The magnesium composite, aluminum composite, manganese composite, or zinc composite can be formulated to react when activated by an electrolyte (e.g., HCl, KCl, CaCl2, CaBr2, ZnBr2, or brine solutions), heat, etc., with the reactive binder dissolving at a controlled rate. In one non-limiting configuration, the surface layer is a high-strength zinc alloy. In another non-limiting configuration, the core can have a dissolution rate in salt-containing water of 0.1-100 mm/hr at 100-300° F. In another non-limiting configuration, the surface layer can include a fiber-reinforced metal (e.g., steel wire, graphite fiber reinforced magnesium, etc.) to obtain the desired strength of the surface layer.


In another non-limiting aspect of the present invention, there is provided a reactive hierarchically-designed component or system that includes (a) a core having an active material, and a material that is reactive in a fluid; (b) a selectively reactive surface layer that is unreactive in the a first fluid or first fluid conditions, but dissolves or reacts in a second fluid or a condition different from the first fluid condition; and wherein the core is coated with the selectively reactive surface layer, and wherein the core is formed of a different material from the selectively reactive surface layer, and the coating thickness of the selectively reactive surface layer is less than a diameter of the core. The core can include propellant. In one non-limiting configuration, the core includes a water-reactive material such as lithium, sodium, potassium, lithium aluminum hydride, sodium aluminum hydride, potassium aluminum hydride, magnesium aluminum hydride, lithium borohydride, sodium borohydride, calcium borohydride, magnesium hydride, n-Al, borohydride mixed with alanates, metal hydrides, borohydrides, divalent cation alanates, and/or other water-reactive materials. The surface layer is formulated to protect or insulate the core from external environments wherein the core would be reactive to the external environment. In one non-limiting configuration, the coating is insoluble at room temperature, but soluble at a higher temperature. In another or alternative non-limiting configuration, the surface is or includes PVA or PVB. In another and/or alternative non-limiting configuration, the core includes a reactive binder having a metal fuel and/or oxidizer composite which includes one or more of the following metals: magnesium, zirconium, tantalum, titanium, hafnium, calcium, tungsten, molybdenum, chrome, manganese, silicon, germanium and/or aluminum that is mixed with an oxidizer or thermite pair (e.g., fluorinated or chlorinated polymers such as polytetrafluoroethylene, polyvinylidene difluoride, oxidizers such as bismuth oxide, potassium perchlorate, potassium or silver nitrate, iron oxide, tungsten or molybdenum oxide, and/or intermetallic thermite such as boron, aluminum, or silicon). In another and/or alternative non-limiting configuration, the binder can include an intermetallic reactive material such as iron-aluminum, nickel-aluminum, titanium-boron, and/or other high energy intermetallic couple. In another and/or alternative non-limiting configuration, the binder can include a fuel, oxidizer, and/or a reactive polymeric material. In another and/or alternative non-limiting configuration, the reactive polymeric material can include aluminum-potassium perchlorate-polyvinylidene difluoride and/or tetrafluoroethylene (THV) polymer. The core can be formed by powder metallurgy techniques (e.g., solid state powder sinter-forging, solid state sinter-extrusion, and spark plasma or field assisted sintering in the solid or semi-solid state). The core can alternatively be formed from melt casting, with or without subsequent deformation and heat treatment. The reactive hierarchically-designed component or system can be used to form a variety of structural components (e.g., valve, plug, ball, sleeve, casing etc.) that are designed to corrode/disintegrate or deflagrate under a controlled external stimulus. The reactive hierarchically-designed component or system can be designed to disintegrate over a controlled period of one hour to three weeks (and all values and ranges therebetween), and/or equivalently at a rate of about 0.05-100 mm/hr upon the imparting of a controlled external stimulus of pH, salt content, electrolyte content, electromagnetic waves, sound waves, vibrations, magnetism, pressure, electricity, and/or temperature. The reactive hierarchically-designed component or system can be designed to deflagrate or otherwise combust or react over a certain time period (e.g., one second to 24 hours and all time values or ranges therebetween) upon exposure to an external trigger (e.g., electrical, thermal, magnetic, or hydraulic signal). The trigger can optionally be direct or through a secondary interaction such as, but not limited to, piezoelectric device, breakable capsule, timer, or other intermediate device to convert an external signal to an initiation electrical and/or thermal event. The deflagration of the reactive hierarchically-designed component or system can be utilized to provide thermal energy, clear obstructions, and/or provide local pressure to a location about the hierarchically-designed component or system in a controlled manner. The reaction of the reactive hierarchically-designed component or system can optionally be designed to generate a physical dimensional change, such as swelling (change in density), deformation, bending, and/or shrinkage in the hierarchically-designed component or system during the reaction. In non-limiting application of the reactive hierarchically-designed component or system, composite matrix material and consolidation process used to form the core and/or the complete structure of the hierarchically-designed component or system can be used to enable simultaneous control of compression yield strength and/or control of compressibility modulus for crush and/or extrusion resistance when the hierarchically-designed component or system is contained in an entrapping orifice, and simultaneously also allow for control over the triggering event and the reaction rate of the reactive hierarchically-designed component or system.


In still another non-limiting aspect of the present invention, there is provided a reactive hierarchically-designed component or system that includes a) a core, the core dissolvable, reactive, or combinations thereof in the presence of a fluid environment; and, h) a surface layer that partially or fully encapsulates the core, and wherein the surface layer has a different composition from the core, and wherein the surface layer forms a protective layer about the core to inhibit or prevent the core from dissolving, reacting, or combinations thereof when the component is exposed to the fluid environment, and wherein the surface layer is non-dissolvable in the fluid environment until the surface layer is exposed to an activation event which thereafter causes the surface layer to controllably dissolve and/or degrade in the fluid environment, and wherein the core dissolving, reacting, or combinations thereof after the surface layer dissolves and exposes the core to the fluid environment. At least 70 weight percent of the core optionally includes one or more core materials selected from the group consisting of a metal, a metal alloy, a metal composite and a metal compound. The core material optionally including one or more metals or compounds selected from the group consisting of aluminum, calcium, lithium, magnesium, potassium, sodium, lithium aluminum hydride, sodium aluminum hydride, potassium aluminum hydride, magnesium aluminum hydride, lithium borohydride, sodium borohydride, calcium borohydride, magnesium hydride, n-Al, borohydride mixed with alanates, metal hydrides, borohydrides, and divalent cation alanates. The fluid environment optionally is a water-containing environment. The activation event optionally includes one or more events selected from the group consisting of a temperature change of the fluid environment, a pH change of the fluid environment, exposure of the surface layer with an activation compound, a change in composition of fluid environment, exposure of the surface layer to an electrical charge, exposure to of the surface layer to certain electromagnetic waves, a change in salt content of the fluid environment, a change in electrolyte content of the fluid environment, exposure of the surface layer to certain sound waves, exposure of the surface layer to certain vibrations, exposure of the surface layer to certain magnetic waves, and exposure of the surface layer to a certain pressure. The core optionally has a dissolution rate in the fluid environment of 0.1 and 100 mm/hr at 100-300° F. The surface layer is optionally formulated to be relatively insoluble at a first temperature in the fluid environment and highly soluble in the fluid environment at a second temperature. The surface layer is optionally formulated to be relatively insoluble at a first pH in the fluid environment and highly soluble in the fluid environment at a second pH. The surface layer optionally is chemically modified using a reversible chemical reaction to be insoluble in the fluid environment and soluble in the fluid environment when the chemically modified surface layer is exposed to a chemical compound that is a chemical trigger. The surface layer is optionally chemically modified with a silicon-containing compound. The chemical trigger is optionally a fluorine ion source. There is optionally provided a method for forming the reactive hierarchically-designed component or system as set forth above. There is optionally a method for forming the reactive hierarchically-designed component or system into a structure that can be used for a) separating hydraulic fracturing systems and zones for oil and gas drilling, b) structural support or component isolation in oil and gas drilling and completion systems, or combinations thereof.


In yet another non-limiting aspect of the present invention, there is provided a reactive hierarchically-designed component or system that includes (a) a core having a compression strength above 5000 psig, a density of no more than 1.7 glee and a tensile strength of less than 30,000 psig; (b) a high-strength surface layer that has a greater density and higher strength than the core, the surface layer partially of fully encapsulating the core; and wherein the core and the surface layer are provide a high-strength reactive system that also has an overall lower density than approximately 4 glee and a strength in the surface layer of at least 35 ksi. The core is optionally a magnesium composite or aluminum composite having a density of 0.9-1.4 g/cc. The surface layer is optionally a zinc alloy. The core optionally has a dissolution rate in a salt water environment of 0.1 and 100 mm/hr at 100-300° F. The surface layer optionally includes a fiber-reinforced metal. There is optionally provided a method for forming the reactive hierarchically-designed component or system as set forth above. There is optionally a method for forming the reactive hierarchically-designed component or system into a structure that can be used for a) separating hydraulic fracturing systems and zones for oil and gas drilling, b) structural support or component isolation in oil and gas drilling and completion systems, or combinations thereof.


In still yet another non-limiting aspect of the present invention, there is provided a reactive hierarchically-designed component or system that includes (a) a core that includes an active material that is reactive in a fluid environment; (b) a propellant located in she core, about the core, or combinations thereat and, (c) a surface layer that partially or fully encapsulates the core, the propellant, or combinations thereof, and wherein the surface layer has a different composition from the core and the propellant, and wherein the propellant has a different composition from the core, and wherein the surface layer forms a protective layer about the core and the propellant to inhibit or prevent the core and the propellant from dissolving, reacting, or combinations thereof when the component is exposed to the fluid environment, and wherein the surface layer is non-dissolvable in the fluid environment until the surface layer is exposed to an activation event which thereafter causes the surface layer to controllably dissolve and/or degrade in the fluid environment and the core and the propellant dissolving, reacting, or combinations thereof after the surface layer dissolves and/or degrades and exposes the core and/or the propellant to the fluid environment. The propellant optionally includes one or more water-reactive material selected from the group consisting of lithium, sodium, potassium, lithium aluminum hydride, sodium aluminum hydride, potassium aluminum hydride, magnesium aluminum hydride, lithium borohydride, sodium borohydride, calcium borohydride, magnesium hydride, n-Al, borohydride mixed with alanates, metal hydrides, borohydrides, divalent cation alanates, and/or other water-reactive materials. The reaction of the propellant with the fluid environment optionally causes rapid heat generation which in turn causes the core to ignite. The fluid environment optionally is a water-containing environment. The activation event optionally includes one or more events selected from the group consisting of a temperature change of the fluid environment, a pH change of the fluid environment, exposure of the surface layer with an activation compound, a change in composition of fluid environment, exposure of the surface layer to an electrical charge, exposure to of the surface layer to certain electromagnetic waves, a change in salt content of the fluid environment, a change in electrolyte content of the fluid environment, exposure of the surface layer to certain sound waves, exposure of the surface layer to certain vibrations, exposure of the surface layer to certain magnetic waves, and exposure of the surface layer to a certain pressure. The surface layer is optionally formulated to be relatively insoluble at a first temperature in the fluid environment and highly soluble in the fluid environment at a second temperature. The surface layer is optionally formulated to be relatively insoluble at a first pH in the fluid environment and highly soluble in the fluid environment at a second pH. The surface layer is optionally chemically modified using a reversible chemical reaction to be insoluble in the fluid environment and soluble in the fluid environment when the chemically-modified surface layer exposed to a chemical compound that is a chemical trigger. The surface layer optionally is chemically modified with a silicon containing compound. The chemical trigger is optionally a fluorine ion source. The core optionally includes a metal fuel and oxidizer composite which includes one or more mixtures of a reactive metal, an oxidizer, or thermite pair, the reactive metal including one or more metals selected from the group consisting of magnesium, zirconium, tantalum, titanium, hafnium, calcium, tungsten, molybdenum, chrome, manganese, silicon, germanium and aluminum, the oxidizer or thermite pair including one or more compounds selected from the group consisting of fluorinated or chlorinated polymer, oxidizer, and intermetallic thermite. The core optionally includes a binder that includes an intermetallic reactive material that includes a metal material selected from the group consisting of iron-aluminum, nickel-aluminum, titanium-boron, high energy intermetallic couple, or combinations thereof. The binder optionally includes a fuel, an oxidizer, and a reactive polymeric material. The reactive polymeric material optionally includes aluminum-potassium perchlorate-polyvinylidene difluoride or tetrafluoroethylene (THY) polymer. There is optionally provided a method for forming the reactive hierarchically-designed component or system as set forth above. There is optionally a method for forming the reactive hierarchically-designed component or system into a structure that can be used for a) separating hydraulic fracturing systems and zones for oil and gas drilling, b) structural support or component isolation in oil and gas drilling and completion systems, or combinations thereof.


In another non-limiting aspect of the present invention, there is provided a reactive hierarchically-designed component or system that is formed in to structural material that is designed to corrode/disintegrate or deflagrate under a controlled external stimulus. The structural material is optionally designed to disintegrate over a controlled period of one hour to one month or at a rate of about 0.1 to 100 mm/hr upon the imparting of a controlled external stimulus to the structural component. The structural material is optionally designed to deflagrate or otherwise combust or react over a one-second to one-hour period upon an external trigger, and wherein the deflagration is utilized to provide thermal energy, clear obstructions, provide local pressure, or combinations thereof in a controlled manner. The reaction is optionally designed to generate a physical dimensional change, deformation, bending, shrinkage, or combinations thereof.


In one non-limiting object of the present invention, there is provided a component or system that can be controllably disintegrated.


In another and/or alternative non-limiting object of the present invention, there is provided a component or system that can be used in a well operation that can be controllably disintegrated.


In still another and/or alternative non-limiting object of the present invention, there is provided a component or system that can include a core material having a surface or protective layer and which component or system can be stored for long periods of time unless activated.


In yet another and/or alternative non-limiting object of the present invention, there is provided a component or system that can include a core material having a surface or protective layer and which component or system has controlled reaction kinetics that can be catalyzed by an external stimulus.


In still yet another and/or alternative non-limiting object of the present invention, there is provided a component or system that can include a core material having a surface or protective layer and which component or system has a reactive composite system that is inert or essentially inert unless initiated by a certain temperatures, electromagnetic waves, sound waves, vibrations, chemicals, liquids, gasses, electromagnetic waves, pH, salt content, exposure electrolyte content, magnetism, pressure, and/or exposure to electricity and/or other external stimulus after which it disintegrates in a controlled and repeatable manner.


In another and/or alternative non-limiting object of the present invention, there is provided a component or system that can include a core material having a surface or protective layer and which component or system has a hierarchically-designed component or system that includes a core and a surface which are designed to react and/or activate under different conditions.


In still another and/or alternative non-limiting object of the present invention, there is provided a component or system that can include a core material having a surface or protective layer and which component or system has a core material is designed to have a high reaction rate that disintegrates when exposed to certain environments (liquids, gasses, temperatures, electromagnetic waves, vibrations, and/or sound waves, pH, salt content, electrolyte content, magnetism, pressure, and/or temperature, etc.).


In yet another and/or alternative non-limiting object of the present invention, there is provided a component or system that can include a core material having a surface or protective layer and which component or system has a core material is designed to generate heat when exposed to various environments (e.g., liquids, gasses, temperatures, electromagnetic waves, vibrations, and/or sound waves, pH, salt content, electrolyte content, magnetism, pressure, electricity, and/or temperature, etc.).


In still yet another and/or alternative non-limiting object of the present invention, there is provided a component or system that can include a core material having a surface or protective layer and which component or system has a core material is formed of one or more layers.


In another and/or alternative non-limiting object of the present invention, there is provided a component or system that can include a core material having a surface or protective layer and which component or system has a core material that is partially or fully surrounded by one or more surface or protective layers that inhibits or prevents the core from reacting and/or disintegrating until a desired time or event.


In still another and/or alternative non-limiting object of the present invention, there is provided a component or system that can include a core material having a surface or protective layer and which component or system has one or more surfaces or protective layers that are designed to be inert unless exposed to an activation event or condition, which activation event or condition could be, but are not limited to, temperature, electromagnetic waves, sound waves, certain chemicals, and/or pH.


In yet another and/or alternative non-limiting object of the present invention, there is provided a component or system that can include a core material having a surface or protective layer and in which each layer of the component or system has a different function in the component or system.


In still yet another and/or alternative non-limiting object of the present invention, there is provided a component or system that can be used as a dissolvable, degradable and/or reactive structure in oil drilling. For example, the component or system of the present invention can be used to form a frac ball or other structure in a well drilling or completion operation such as a structure that is seated in a hydraulic operation that can be dissolved away after use so that that no drilling or removal of the structure is necessary. Other types of structures can include, but are not limited to, sleeves, valves, hydraulic actuating tooling and the like. Such non-limiting structures or additional non-limiting structure are illustrated in U.S. Pat. Nos. 8,905,147; 8,717,268; 8,663,401; 8,631,876; 8,573,295; 8,528,633; 8,485,265; 8,403,037; 8,413,727; 8,211,331; 7,647,964; US 2013/0199800; US 2013/0032357; US 2013/0029886; US 2007/0181224; and WO 2013/122712; all of which are incorporated herein by reference.


These and other objects, features and advantages of the present invention will become apparent in light of the following detailed description of preferred embodiments thereof, as illustrated in the accompanying drawings.





BRIEF DESCRIPTION OF THE DRAWINGS


FIGS. 1-2 are a cross-sectional illustration of layered ball actuators in accordance with the present invention wherein the core represents a disintegrating high strength material.





DETAILED DESCRIPTION OF THE INVENTION

Referring now to the figures wherein the showings illustrate non-limiting embodiments of the present invention, the present invention is directed to the formation and use of disintegrating components and materials that can be stored for long periods of time until activated. The present invention also relates to the production of a reactive hierarchically-designed component or system having controlled reaction kinetics that can be catalyzed by an external stimulus. The invention further relates to a reactive hierarchically-designed component or system that is inert or essentially inert unless initiated by a certain temperature, pH, and/or other external stimulus after which it disintegrates in a controlled and repeatable manner. The components of the present invention have particular applicability to components used in the forming of wells; however, it will be appreciated that the components of the present invention can be used in many other industries and applications.


Referring to FIGS. 1-2, there are cross-sectional illustrations of layered composite ball actuators in accordance with the present invention wherein the core represents a disintegrating high strength composite. The cross-sectional shape of the core illustrated as being circular; however, it can be appreciated that the core can have any shape.


In one non-limiting configuration, the core can be formed of a metal such as, but not limited to, lithium, sodium, magnesium, magnesium-carbon-iron composite system, and the like. As can be appreciated, the core can also or alternatively include a polymer material. The core can be formed or more than one type of material; however, that is not required. The core can be formed of one or more layers. When the core includes two or more layers, the layers are generally formed of different materials; however, this is not required. The surface layer of the composite ball actuator can include a protective or delay coating. The surface layer can be a metal layer, a polymer layer, and/or a ceramic layer. The surface layer can be formed of one or more layers. When the surface layer includes two or more layers, the layers are generally formed of different materials; however, this is not required.


In one non-limiting arrangement, the surface layer can be a temperature-sensitive polymer such as, but not limited to, PVA, that is inert and insoluble until exposed to certain environmental conditions. For example, when the surface layer is PVA, and when the PVA reaches a critical temperature in water, the PVA dissolves to expose the underlying reactive core, thereby causing the core to react. Surface layers that activate under exposure to specific temperatures, pressures, fluids, electromagnetic waves and/or mechanical environments to delay the initiation of a dissolution reaction are envisioned by the present invention.


In accordance with the present invention, a metal, metal alloy, metal matrix composite, polymer, or polymer composite having a specified reactive function can form all or part of the core. One of the primary functions of the core is for the material of the core to partially or fully disintegrate in a controlled and uniform manner upon exposure an environmental condition (e.g., exposure to saltwater, etc.). On the surface of the core (which core can be a casting, forging, extrusion, pressed, molded, or machined part), a surface layer is included to modify the conditions to which the core will react. In one non-limiting configuration, the core has a strength above 25,000 psig, and is selected to respond to a set of environmental conditions to perform a function (e.g., react, dissolve, corrode, fracture, generate heat, etc.).


In one non-limiting formulation, the core can be or include magnesium or magnesium alloy that has a temperature-dependent dissolution or disintegration rate. This disintegration rate of the core can be designed such that the core dissolves, corrodes, reacts, and/or chemically reacts in a certain period of time at a given temperature. One non-limiting application that can use such a core is a frac ball. The composite system can be designed such that the core does not disintegration at a temperature of less than about 100° F. via protection from the surface layer. As can be appreciated, the temperature can be any temperature (e.g., below 10° F., below 50° F., below 100° F., below 150° F., below 200° F., etc.). In one embodiment, wherein the hierarchically-designed component or system is designed to inhibit or prevent reaction of the core at a temperature below 100° F., the core would have a near-infinite life at conditions below 100° F. To accomplish this non-limiting embodiment, the hierarchically-designed component or system has a surface layer that is applied to the surface of the core, wherein the surface layer is inert under conditions wherein the temperature is below 100° F., but dissolves, corrodes, or degrades once the temperature exceeds 100° F. (e.g., dissolves, corrodes, or degrades in the presence of water that exceeds 100° F., dissolves, corrode, or degrades in the present of air that exceeds 100° F., etc.) In this non-limiting embodiment, the kinetics of the reaction can be changed by inhibiting the initial reaction, and then accelerating the reaction once specific conditions are met. As can be appreciated, the surface layer can be caused to dissolve, corrode, or degrade upon exposure to other conditions (e.g., certain liquids, certain gasses, certain temperatures, certain electromagnetic waves, certain vibrations, and/or certain sound waves, certain pH, certain salt content, certain electrolyte content, certain magnetism, certain pressure, electricity, and/or certain temperature, etc.).


Because the surface layer may be exposed to high stress, surface layer can be thin (e.g., 0.01-50 mils, typically 0.01-10 mils, more typically 0.01-5 mils, etc.); however, this is not required. Alternatively, the surface layer can be designed to be strong and to contribute mechanically to the system, such as through the use of fiber, flakes, metals, metal alloys, and/or whisker reinforcement in the layer. The thickness of the surface layer about the core can be uniform or vary.


Example 1

A magnesium frac ball is produced having a disintegration rate of about 0.7-1.4 mm/hr at 200° F. and about 0.01-0.04 mm/hr at 100° F. The frac ball is designed to able to withstand at least a 24-hour exposure to 80° F. water in a ball drop system. The magnesium core can be magnesium, magnesium alloy or a magnesium composite. As can be appreciated, the core can be formed of other metals and/or non-metals that react, dissolve, corrode, or disintegrate at a rate of 0.1-100 mm hr at 100-300° F. in water or salt water. The magnesium frac ball can be undermachined by 0.001-0.2″ (e.g., 0.005″, etc.) from final dimensions, and a 0.001-0.2″ coating (e.g., 0.005″ coating, etc.) of PVA can be applied to the surface through a spray-coating process. FIG. 1 illustrates one non-limiting configuration of the frac ball. Although not illustrated in FIG. 1, the core can be formed of multiple layers of material wherein each layer has a different composition from the adjacently positioned layer. For example, the first or central layer of the core could include a magnesium composite material, and a second layer that is applied about the first layer could be magnesium or magnesium alloy. Likewise, the surface layer can include one or more different layers wherein each layer has a different composition from the adjacently positioned layer. The thickness of the two or more layers of the surface layer (when used) can be the same or different. Likewise, the thickness of the two or more layers of the core (when used) can be the same or different. The PVA is very insoluble in water up to about 130-150° F. At temperatures above 150° F., the PVA becomes dissolvable and ultimately exposes the magnesium core. The magnesium frac ball has excellent mechanical properties (e.g., generally above 30 ksi strength), and when the magnesium frac ball is exposed to slightly acidic or salt solutions, the magnesium frac ball corrodes at a rate of about 0.1-15 mm/day. However, when the magnesium frac ball is exposed to temperatures below about 130° F., the magnesium frac ball does not dissolve or corrode. As can be appreciated, the thickness of the coating of PVA can be selected to control the time needed for the PVA to dissolve and thereby expose the core to the surrounding environment.


Example 2

A high-strength frac ball is produced using a low-density core, which frac ball is selected for having good compressive strength and low density, and having a surface layer of a higher tensile strength and a denser material than the core. The core is selected from a magnesium composite that uses a high corrosion magnesium alloy matrix with carbon, glass, and/or ceramic microballoons or balls to reduce its density to below 1.7 g/cc (e.g., 0.5-1.66 g/cc and all values and ranges therebetween) and typically below about 1.3 g/cc. As can be appreciated, other densities of the core can be used. This composite core has very good compressive strengths, but tensile strengths may, in some applications, be inadequate for the intended application. For example, the tensile strength of the composite core may be less than 35 ksi, typically less than 32 ksi, and more typically less than 30 ksi. As such, the composite core can be surrounded by another layer having a greater tensile strength. This surrounding layer can have a thickness of about 0.035-0.75″ (and all values and ranges therebetween) and typically about 0.1-0.2″. The surrounding layer can be formed of magnesium, magnesium alloy or a high-strength magnesium composite. The high strength outer layer is designed to have adequate tensile strength and toughness for the applications, and generally has a tensile strength that is greater than 33 ksi, typically greater than 35 ksi, and more typically greater than 45 ksi; however, the tensile strength can have other values. The resultant component can have an overall density of about 5-45% lower (and all values and ranges therebetween) than a pure magnesium alloy ball, and typically about 30% lower than a pure magnesium alloy ball, but also has the high tensile and shear strengths needed to perform the desired ball actuator application.


The core of the high-strength frac ball can be heat treated and machined after fabrication. A surface layer can optionally be applied to the core using thermal spray, co-extrusion, casting, or through power metallurgy techniques suitable for its fabrication as discussed in Example 1.


Example 3

A magnesium frac ball is produced having a disintegration rate of about 0.7-1.4 mm/hr at 200° F. and about 0.01-0.04 mm/hr at 100° F. The frac ball is designed to be able to withstand at least a 24-hour exposure to 80° F. water in a ball drop system. The magnesium frac ball can be undermachined by 0.001-0.2″ (e.g., 0.005″, etc.) from final dimensions, and a 0.001-0.2″ coating (e.g., 0.005″ coating, etc.) of zinc metal can be applied to the surface of the magnesium core. The magnesium core can be magnesium, magnesium alloy or a magnesium composite. As can be appreciated, the core can be formed of other metal and/or non-metals that react, corrode, dissolve or disintegrate at a rate of 0.1-100 mm/hr at 100-300° F. in water or salt water. The resultant compact has high mechanical properties, generally about 28 ksi and typically above 30 ksi strength (e.g., 30-45 ksi and all values and ranges therebetween). When the core of the magnesium frac ball is exposed to salt solutions, the magnesium frac ball corrodes at a rate of about 0.1-15 mm/day depending on the environment and temperature. The magnesium frac ball is designed to not react or corrode until activated with an acid exposure that removes the zinc surface layer and exposes the underlying magnesium core.


Example 4

A high-strength frac ball is produced using a low-density core, which frac ball is selected for having good compressive strength and low density, and having a surface layer of a higher tensile strength, and a denser material than the core. The core is selected from a magnesium composite that uses a high corrosion magnesium alloy matrix with carbon, glass, and/or ceramic microballoons or balls to reduce its density to below 1.7 g/cc (e.g., 0.5-1.66 g/cc and all values and ranges therebetween) and typically below about 1.3 g/cc. As can be appreciated, other densities of the core can be used. This composite core has very good compressive strengths, but tensile strengths may, in some applications, be inadequate for the intended application. For example, the tensile strength of the composite core may be less than 35 ksi, typically less than 32 ksi, and more typically less than 30 ksi. As such, the composite core can be surrounded by another layer having a greater tensile strength. Surrounding the composite core is high-strength metal or metal alloy (e.g., zinc, etc.) that has a layer thickness of about 0.035-0.75″, and typically about 0.1-0.2″. The high-strength metal or metal alloy outer layer is designed to have adequate tensile strength and toughness for certain the applications, and is generally greater than 33 ksi, typically greater than 35 ksi, and more typically greater than 45 ksi; however, the tensile strength can have other values. The resultant component can have an overall density of about 5-60% lower (and all values and ranges therebetween) than a pure zinc alloy ball, and typically about 50% lower than a pure zinc alloy ball, but also has the high tensile and shear strengths needed to perform the desired ball actuator application.


Example 5

A reactive material containing a water-reactive substance such as, but not limited to, lithium, is formed into a particle. The lithium is added to a propellant mixture. The propellant mixture can include polyvinylidene difluoride (PVDF), ammonium nitrate, and/or aluminum to form a gas-generating composition. The lithium particle can optionally include a polymer coating (e.g., PVA, etc.) that is applied to its surface to protect it from contact with water. The polymer coating is formulated to be insoluble at room temperature, but can dissolve in hot water (e.g., +140° F.). Once the coating is dissolved to expose the lithium, the lithium reacts with water and releases heat, thus igniting the propellant (e.g., aluminum-ammonium nitrate-PVDF propellant, etc.) to generate heat and gas pressure. As can be appreciated, other reactive particles can be used (e.g., lithium, sodium, potassium, lithium aluminum hydride, sodium aluminum hydride, potassium aluminum hydride, magnesium aluminum hydride, lithium borohydride, sodium borohydride, calcium borohydride, magnesium hydride, n-Al, borohydride mixed with alanates, metal hydrides, borohydrides, divalent cation alanates, and/or other water-reactive materials, etc.).


Example 6

A reactive material containing a water-reactive substance such as, but not limited to, sodium, is formed into a particle. The sodium is added to a propellant mixture. The propellant mixture can include PVDF, ammonium nitrate, and/or aluminum to form a gas-generating composition. The sodium particle can optionally include a polymer coating (e.g., PVAP, etc.) that is applied to its surface to protect it from contact with water. The polymer can optionally be a polymer that is insoluble in water-containing environments having an acidic pH, but is soluble in neutral or basic water containing environments; however, this is not required. One such polymer is polyvinyl acetate phthalate (PVAP). As can be appreciated, the polymer can optionally be selected to be insoluble in water-containing environments having a basic or neutral pH, but is soluble in an acidic water-containing environments; however, this is not required. The reactive material can be pumped into a formation using a solution having a pH wherein the polymer does not dissolve or degrade. Once the reactive material is in position, the pH solution can be changed to cause the polymer to dissolve or degrade, thereby exposing the sodium to the water and thus igniting the propellant by the heat generated by the sodium exposure to water to thereby generate localized heat and pressure. As can be appreciated, other reactive particles can be used (e.g., lithium, sodium, potassium, lithium aluminum hydride, sodium aluminum hydride, potassium aluminum hydride, magnesium aluminum hydride, lithium borohydride, sodium borohydride, calcium borohydride, magnesium hydride, n-Al, borohydride mixed with alanates, metal hydrides, borohydrides, divalent cation alanates, and/or other water-reactive materials, etc.).


Example 7

A magnesium frac ball is produced having a disintegration rate of about 0.7-1.4 mm/hr at 200° F. and about 0.01-0.04 mm/hr at 100° F. The frac ball is designed to able to withstand at least one day, typically at least seven days, and more typically at least 14 days exposure to 80° F.+ water or a water system having an acidic pH in a ball drop system or a down hole application (e.g., ball/ball seat assemblies, fracture plugs, valves, sealing elements, well drilling tools, etc.). The magnesium core can be magnesium, magnesium alloy or a magnesium composite. As can be appreciated, the core can be formed of other metal and/or non-metals that react, corrode, dissolve or disintegrate at a rate of 0.1-100 mm/hr at 100-300° F. in water or salt water. The magnesium frac ball can be undermachined by 0.001-0.2″ (e.g., 0.005″, etc.) from final dimensions, and a 0.001-0.2″ coating (e.g., 0.005″ coating, etc.) of PVA can be applied to the surface through a spray-coating process. The PVA is very insoluble in water up to about 130-150° F. At temperatures above 150° F., the PVA becomes dissolvable. To prevent dissolution of the PVA above 150° F., the PVA coating is modified with a silicone component such as, but not limited to, trimethylsilyl group to convert the PVA to a protected ether silyl layer that is insoluble in water, salt water, and acidic water solutions, even when such solutions exceed 150° F. Non-limiting examples of compounds that include the trimethylsilyl group include trimethylsilyl chloride, bis(trimethylsilyl)acetamide, trimethylsilanol, and tetramethylsilane. FIG. 2 illustrates an example of a surface treatment layer such as compound having a trimethylsilyl group that is applied to the outer surface of a surface layer of PVA, and wherein the PVA surrounds a core. The converted PVA can be converted back to PVA (e.g., the protected ether silyl is removed from the PVA) by exposing the converted PVA to an ammonium fluoride solution or similar solution which thereby converts the surface back to PVA. At temperatures above 150° F., the PVA becomes dissolvable and ultimately exposes the magnesium core. The magnesium frac ball has excellent mechanical properties (e.g., generally above 30 ksi strength), and when the magnesium frac ball is exposed to slightly acidic or salt solutions, the magnesium frac ball corrodes at a rate of about 0.1-15 mm/day. However, when the magnesium frac ball is exposed to temperatures below about 130° F., the magnesium frac ball does not dissolve or corrode. As can be appreciated, the thickness of the coating of PVA can be selected to control the time needed for the PVA to dissolve and thereby expose the core to the surrounding environment. Also as can be appreciated, the modification of the coating of PVA can be selected to achieve control of exposure of the core to the surrounding environment.


Example 8

A silicone coating (e.g., polymer-based siloxane two-part coating) was sprayed onto a dissolvable metal sphere and cured for seven days. The dissolvable metal sphere can be formed of magnesium, magnesium alloy, a magnesium composite or metal and/or non-metals that react, corrode, dissolve or disintegrate at a rate of 0.1-100 mm/hr at 100-300° F. in water or salt water. The coating thickness was about 0.003″; however, the coating thickness can be other thicknesses (e.g., 0.001-0.1″ and any value or range therebetween, etc.). The coated ball was then submersed in 200° F. of HCl (e.g., 0.1-3M HCl) for 65 min with no evidence of reaction of the metal sphere. 0.1 M HF was thereafter added to the 200° F. HCl solution (e.g., 0.1-3M HCl) and the silicone coating separated from the metal sphere in less than 30 minutes (e.g., 0.1-30 minutes and all values and ranges therebetween), The silicone coating is generally formulated to separate from the metal sphere when exposed to certain solutions in about 0.1-180 minutes (and all values and ranges therebetween), depending on the type, concentration and temperature of the solution. The metal that was dissolvable then started dissolving in the HCl solution. In another example, the same silicone polymer was sprayed onto a dissolvable metal plate and cured for seven days. The dissolvable metal plate can be formed of magnesium, magnesium alloy, a magnesium composite or metal and/or non-metals that react, corrodes, dissolves or disintegrate at a rate of 0.1-100 mm/hr at 100-300° F. in water or salt water. The coating thickness was about 0.006″. The coated plate was then subjected to a simulated pipe line sliding wear equivalent to 5000 feet of sliding wear. The silicone coating exhibited little or no removal of material and the dissolvable metal plate was not exposed to any sliding wear.


Example 9

A polymer-based polyurethane coating (e.g., one-or two-part coating) was applied (e.g., electrostatically, etc.) to the surface of a dissolvable metal sphere and cured above 300° F. for about 15 min. The dissolvable metal sphere can be formed of magnesium, magnesium alloy, a magnesium composite or metal and/or non-metals that react, corrode, dissolve or disintegrate at a rate of 0.1-100 mm/hr at 100-300° F. in water or salt water. The coated sphere was cooled to room temperature and submerged in 80° F. 15% HCl solution (i.e., 2.75M HCl) for 60 min. No degradation of the coating or ball was observed and no dimensions changed. The coated sphere was then moved to a 200° F. 3% KCl solution (i.e., 0.4M KCl). The coating started to degrade after about 30 minutes at the elevated temperature and the dissolvable metal sphere thereafter degraded with the removal of the silicone coating. The silicone coating is generally formulated to separate from the metal sphere when exposed to certain solutions in about 0.1-180 minutes (and all values and ranges therebetween), depending on the type, concentration and temperature of the solution.


Example 10

A polymer-based PVB coating was coated (e.g., electrostatically applied, etc.) to the surface of a dissolvable metal sphere and cured above 300° F. for about 30 minutes. The dissolvable metal sphere can be formed of magnesium, magnesium alloy, a magnesium composite or metal and/or non-metals that reacts, corrode, dissolves or disintegrates at a rate of 0.1-100 mm/hr at 100-300° F. in water or salt water. The coating was abrasion resistant and had excellent adhesion to the sphere. The coated sphere was cooled to room temperature and submerged in 80° F. 15% HCl solution for about 60 minutes. No degradation of the coating or metal sphere was observed and the coated sphere did not exhibit any dimensional changes. The coated sphere was then moved to a 200° F. 3% KCl solution. The coating on the metal sphere started to degrade after about 30 min at the elevated temperature and the dissolvable metal sphere degraded with the removal of the PVB. The PVB coating is generally formulated to separate from the metal sphere when exposed to certain solutions in about 0.1-180 minutes (and all values and ranges therebetween), depending on the type, concentration and temperature of the solution.


Example 11

A polymer-based. PVB coating was coated (e.g., coated using a solvent, etc.) to the surface of a dissolvable metal sphere and cured above 300° F. for about 30 minutes. The dissolvable metal sphere can be formed of magnesium, magnesium alloy, a magnesium composite or metal and/or non-metals that react, corrode, dissolve or disintegrate at a rate of 0.1-100 mm/hr at 100-300° F. in water or salt water. The coating was abrasion resistant and had excellent adhesion to the sphere. The coated sphere was cooled to room temperature and submerged in 80° F. 15% HCl solution for about 60 minutes. No degradation of the coating or metal sphere was observed and the coated sphere did not exhibit any dimensional changes. The coated sphere was then moved to a 200° F. 3% KCl solution. The coating on the metal sphere started to degrade after about 30 minutes at the elevated temperature and the dissolvable metal sphere degraded with the removal of the PVB. The PVB coating is generally formulated to separate from the metal sphere when exposed to certain solutions in about 0.1-180 minutes (and all values and ranges therebetween), depending on the type, concentration and temperature of the solution.


It will thus be seen that the objects set forth above, among those made apparent from the preceding description, are efficiently attained, and since certain changes may be made in the constructions set forth without departing from the spirit and scope of the invention, it is intended that all matter contained in the above description and shown in the accompanying drawings shall be interpreted as illustrative and not in a limiting sense. The invention has been described with reference to preferred and alternate embodiments. Modifications and alterations will become apparent to those skilled in the art upon reading and understanding the detailed discussion of the invention provided herein. This invention is intended to include all such modifications and alterations insofar as they come within the scope of the present invention. It is also to be understood that the following claims are intended to cover all of the generic and specific features of the invention herein described and all statements of the scope of the invention, which, as a matter of language, might be said to fall there between. The invention has been described with reference to the preferred embodiments. These and other modifications of the preferred embodiments as well as other embodiments of the invention will be obvious from the disclosure herein, whereby the foregoing descriptive matter is to be interpreted merely as illustrative of the invention and not as a limitation. It is intended to include all such modifications and alterations insofar as they come within the scope of the appended claims.

Claims
  • 1. A method for controlling the dissolving, degrading, reacting, and/or fracturing of a component for use in down-hole applications comprising: a. providing a down-hole component for use in down-hole applications, said down-hole component at least partially formed of a hierarchically-designed reactive component, said hierarchically-designed reactive component includes: i. a core, said core dissolvable and/or reactive in the presence of a down-hole fluid environment, at least 70 wt. % of said core including a core material that includes one or more water-reactive materials selected from the group consisting of lithium, sodium, potassium, lithium aluminum hydride, sodium aluminum hydride, potassium aluminum hydride, magnesium aluminum hydride, lithium borohydride, sodium borohydride, calcium borohydride, magnesium hydride, n-Al, borohydride mixed with alanates, metal hydrides, borohydrides, and divalent cation alanates; and,ii. a surface layer partially or fully encapsulatings said core, said surface layer having a different composition from said core, said surface layer includes polymer, said polymer formulated to have a chemical reaction when exposed to a chemical trigger, said surface layer formulated to be insoluble in said down-hole fluid environment and soluble in said down-hole fluid environment when chemically modified by said chemical trigger; said surface layer forming a protective layer about said core to inhibit or prevent said core from degrading, dissolving, and/or reacting when said component is exposed to said down-hole fluid environment in said down-hole applications, said surface layer is not degradable, dissolvable, and/or reactable in said down-hole fluid environment until said surface layer is exposed to an activation event which thereafter causes said surface layer to controllably dissolve in said down-hole fluid environment;b. inserting said down-hole component into a well, said surface layer of said hierarchically-designed reactive component does not or substantially does not dissolve, degrade, and/or react when exposed to said down-hole fluid environment in said well;c. exposing said surface layer of said hierarchically-designed reactive component to said activation event in the form of said chemical trigger to cause said surface layer to degrade, dissolve, and/or react to thereby expose said core to said down-hole fluid environment; and,d. causing said exposed core to degrade, dissolve, react, and/or fracture when exposed to said down-hole fluid environment, said degradation, dissolving, reacting, and/or fracturing of said core thereby causing said down-hole component to at least partially degrade, dissolve, react, and/or fracture.
  • 2. The method as defined in claim 1, wherein said down-hole component is selected from the group consisting of a frac ball, a valve, a plug, a ball, a sleeve, a casing, a hydraulic actuating tool, a ball/ball seat assembly, a fracture plug, sealing elements, and a well drilling tool.
  • 3. The method as defined in claim 1, wherein said down-hole fluid environment is a water-containing environment, said core having a dissolution rate in said down-hole fluid environment of 0.1-100 mm/hr at 100-300° F.
  • 4. The method as defined in claim 1, wherein said activation event further includes a temperature increase of said down-hole fluid environment to facilitate in causing said surface layer to degrade, dissolve, or combinations thereof.
  • 5. The method as defined in claim 1, wherein said activation event further includes a change in pH of said down-hole fluid environment to facilitate in causing said surface layer to degrade, dissolve, or combinations thereof.
  • 6. The method as defined in claim 1, wherein said surface layer includes a silicon-containing compound.
  • 7. The method as defined in claim 6, wherein said chemical trigger is a fluorine ion source.
  • 8. The method as defined in claim 1, wherein said core has a compression strength above 5000 psig, a density of no more than 1.7 g/cc, and a tensile strength of less than 30,000 psig.
  • 9. The method as defined in claim 1, wherein said surface layer includes a fiber-reinforced metal.
  • 10. The method as defined in claim 1, wherein said core is formulated to react with said down-hole fluid environment to cause rapid heat generation which in turn causes said core to ignite.
  • 11. The method as defined in claim 1, wherein said core includes a metal fuel and oxidizer composite which includes one or more mixtures of a reactive metal, an oxidizer, or thermite pair, said reactive metal including one or more metals selected from the group consisting of magnesium, zirconium, tantalum, titanium, hafnium, calcium, tungsten, molybdenum, chrome, manganese, silicon, germanium, and aluminum, said oxidizer or thermite pair including one or more compounds selected from the group consisting of fluorinated or chlorinated polymer, oxidizer, and intermetallic thermite.
  • 12. The method as defined in claim 11, wherein said surface layer includes polyvinyl alcohol, polyvinyl alcohol modified with a silicone component, polyvinyl acetate phthalate, silicone, polymer-based polyurethane, and polymer-based polyvinyl butyral.
  • 13. The method as defined in claim 1, wherein said core includes a reactive polymeric material including one or more materials selected from the group consisting of aluminum-potassium perchlorate-polyvinylidene difluoride and tetrafluoroethylene (THV) polymer.
  • 14. The method as defined in claim 1, wherein said surface layer includes one or more materials selected from the group consisting of zinc, zinc alloy, ethylene-α-olefin copolymer, linear styrene-isoprene-styrene copolymer, ethylene-butadiene copolymer, styrene-butadiene-styrene copolymer, copolymer having styrene endblocks and ethylene-butadiene or ethylene-butene midblocks, copolymer of ethylene and alpha olefin, ethylene-octene copolymer, ethylene-hexene copolymer, ethylene-butene copolymer, ethylene-pentene copolymer, ethylene-butene copolymer, polyvinyl alcohol, polyvinyl butyral, silicone-based coating, and polyurethane-based coating.
  • 15. A method for controlling the dissolving, degrading, reacting, and/or fracturing of a component for use in down-hole applications comprising: a. providing a down-hole component for use in down-hole applications, said down-hole component selected from the group consisting of a frac ball, a valve, a plug, a ball, a sleeve, a casing, a hydraulic actuating tool, a ball/ball seat assembly, a fracture plug, sealing elements, and a well drilling tool, said down-hole component at least partially formed of a hierarchically-designed reactive component, said hierarchically-designed reactive component includes: i. a core, said core dissolvable and/or reactive in the presence of a down-hole fluid environment, at least 70 wt. % of said core including a core material selected from the group consisting of lithium, potassium, lithium aluminum hydride, sodium aluminum hydride, potassium aluminum hydride, magnesium aluminum hydride, lithium borohydride, sodium borohydride, calcium borohydride, magnesium hydride, n-Al, borohydride mixed with alanates, metal hydrides, borohydrides, and divalent cation alanates; and,ii. a surface layer partially or fully encapsulating said core, said surface layer having a different composition from said core, said surface layer formulated to have a chemical reaction when exposed to said chemical trigger, said surface layer formulated to be insoluble in said down-hole fluid environment and soluble in said down-hole fluid environment when chemically modified by said chemical trigger; said surface layer forming a protective layer about said core to inhibit or prevent said core from degrading, dissolving, and/or reacting when said component is exposed to a down-hole fluid environment in said down-hole applications, said surface layer is not degradable, dissolvable, and/or reactable in said down-hole fluid environment until said surface layer is exposed to said chemical trigger which thereafter causes said surface layer to controllably dissolve in said down-hole fluid environment;b. inserting said down-hole component into a well, said surface layer of said hierarchically-designed reactive component does not or substantially does not dissolve, degrade, and/or react when exposed to said down-hole fluid environment in said well;c. exposing said surface layer of said hierarchically-designed reactive component to said chemical trigger to cause said surface layer to degrade, dissolve, and/or react to thereby expose said core to said down-hole fluid environment; and,d. causing said exposed core to degrade, dissolve, react, and/or fracture when exposed to said down-hole fluid environment, said degradation, dissolving, reacting, and/or fracturing of said core thereby causing said down-hole component to at least partially degrade, dissolve, react, and/or fracture.
  • 16. The method as defined in claim 15, wherein said surface layer includes one or more materials selected from the group consisting of ethylene-α-olefin copolymer, linear styrene-isoprene-styrene copolymer, ethylene-butadiene copolymer, styrene-butadiene-styrene copolymer, copolymer having styrene endblocks and ethylene-butadiene or ethylene-butene midblocks, copolymer of ethylene and alpha olefin, ethylene-octene copolymer, ethylene-hexene copolymer, ethylene-butene copolymer, ethylene-pentene copolymer, ethylene-butene copolymer, polyvinyl alcohol, polyvinyl butyral, silicone-based coating, and polyurethane-based coating.
  • 17. The method as defined in claim 15, wherein said surface layer includes polyvinyl alcohol, polyvinyl alcohol modified with a silicone component, polyvinyl acetate phthalate, silicone, polymer-based polyurethane, and polymer-based polyvinyl butyral.
  • 18. The method as defined in claim 15, wherein said down-hole fluid environment is a water-containing environment, said core having a dissolution rate in said down-hole fluid environment of 0.1-100 mm/hr at 100-300° F.
  • 19. The method as defined in claim 15, wherein said surface layer includes a silicon-containing compound.
  • 20. The method as defined in claim 19, wherein said chemical trigger is a fluorine ion source.
  • 21. The method as defined in claim 15, wherein said core has a compression strength above 5000 psig, a density of no more than 1.7 g/cc, and a tensile strength of less than 30,000 psig.
  • 22. A method for controlling the dissolving, degrading, reacting, and/or fracturing of a component for use in down-hole applications, said method comprises: a. providing a down-hole component for use in down-hole applications, said down-hole component selected from the group consisting of a frac ball, a valve, a plug, a ball, a sleeve, a casing, a hydraulic actuating tool, a ball/ball seat assembly, a fracture plug, sealing elements, and a well drilling tool, said down-hole component at least partially formed of a hierarchically-designed reactive component, said hierarchically-designed reactive component includes: i. a core, said core dissolvable and/or reactive in the presence of a down-hole fluid environment, at least 70 wt. % of said core including a core material selected from the group consisting of lithium, potassium, lithium aluminum hydride, sodium aluminum hydride, potassium aluminum hydride, magnesium aluminum hydride, lithium borohydride, sodium borohydride, calcium borohydride, magnesium hydride, n-Al, borohydride mixed with alanates, metal hydrides, borohydrides, and divalent cation alanates; and,ii. a surface layer partially or fully encapsulating said core, said surface layer having a different composition from said core, said surface layer including one or more materials selected from the group consisting of ethylene-α-olefin copolymer, linear styrene-isoprene-styrene copolymer, ethylene-butadiene copolymer, styrene-butadiene-styrene copolymer, copolymer having styrene endblocks and ethylene-butadiene or ethylene-butene midblocks, copolymer of ethylene and alpha olefin, ethylene-octene copolymer, ethylene-hexene copolymer, ethylene-butene copolymer, ethylene-pentene copolymer, ethylene-butene copolymer, polyvinyl alcohol, polyvinyl butyral, silicone-based coating, and polyurethane-based coating, said surface layer formulated to have a chemical reaction when exposed to a chemical trigger, said surface layer formulated to be insoluble in said down-hole fluid environment and soluble in said down-hole fluid environment when chemically modified by said chemical trigger; said surface layer forming a protective layer about said core to inhibit or prevent said core from degrading, dissolving, and/or reacting when said component is exposed to said down-hole fluid environment in said down-hole applications, said surface layer is not degradable, dissolvable, and/or reactable in said down-hole fluid environment until said surface layer is exposed to said chemical trigger which thereafter causes said surface layer to controllably dissolve in said down-hole fluid environment;b. inserting said down-hole component into a well, said surface layer of said hierarchically-designed reactive component does not or substantially does not dissolve, degrade, and/or react when exposed to said down-hole fluid environment in said well;c. exposing said surface layer of said hierarchically-designed reactive component to said chemical trigger to cause said surface layer to degrade, dissolve, and/or react to thereby expose said core to said down-hole fluid environment; and,d. causing said exposed core to degrade, dissolve, react, and/or fracture when exposed to said down-hole fluid environment, said degradation, dissolving, reacting, and/or fracturing of said core thereby causing said down-hole component to at least partially degrade, dissolve, react, and/or fracture.
  • 23. The method as defined in claim 22, wherein said surface layer includes one or more materials selected from the group consisting of polyvinyl alcohol and polyvinyl butyral.
  • 24. The method as defined in claim 22, wherein said down-hole fluid environment is a water-containing environment in a down hole, said core having a dissolution rate in said down-hole fluid environment of 0.1-100 mm/hr at 100-300° F.
  • 25. The method as defined in claim 22, wherein said chemical trigger is a fluorine ion source.
  • 26. The method as defined in claim 22, wherein said core has a compression strength above 5000 psig, a density of no more than 1.7 g/cc, and a tensile strength of less than 30,000 psig.
  • 27. A method for controlling the dissolving, degrading, reacting, and/or fracturing of a component for use in down-hole applications, said method comprises: a. providing a down-hole component for use in down-hole applications; said down-hole component selected from the group consisting of a frac ball, a valve, a plug, a ball, a sleeve, a casing, a hydraulic actuating tool, a ball/ball seat assembly, a fracture plug, sealing elements, and a well drilling tool; said down-hole component at least partially formed of a hierarchically-designed reactive component said hierarchically-designed reactive component includes: i. a core, said core dissolvable and/or reactive in the presence of a down-hole fluid environment at least 70 wt. % of said core including a core material selected from the group consisting of aluminum, calcium, lithium, magnesium, potassium, sodium, lithium aluminum hydride, sodium aluminum hydride, potassium aluminum hydride, magnesium aluminum hydride, lithium borohydride, sodium borohydride, calcium borohydride, magnesium hydride, n-Al, borohydride mixed with alanates, metal hydrides, borohydrides, and divalent cation alanates; and,ii. a surface layer partially or fully encapsulating said core; said surface layer having a different composition from said core; said surface layer including one or more materials selected from the group consisting of ethylene-α-olefin copolymer, linear styrene-isoprene-styrene copolymer, ethylene-butadiene copolymer, styrene-butadiene-styrene copolymer, copolymer having styrene endblocks and ethylene-butadiene or ethylene-butene midblocks, copolymer of ethylene and alpha olefin, ethylene-octene copolymer, ethylene-hexene copolymer, ethylene-butene copolymer, ethylene-pentene copolymer, ethylene-butene copolymer, polyvinyl alcohol, polyvinyl butyral, silicone-based coating, and polyurethane-based coating; said surface layer includes polyvinyl alcohol modified with a silicone component said surface layer formulated to have a chemical reaction when exposed to a chemical trigger; said surface layer formulated to be insoluble in said down-hole fluid environment and soluble in said down-hole fluid environment when chemically modified by said chemical trigger; said surface layer forming a protective layer about said core to inhibit or prevent said core from degrading, dissolving, and/or reacting when said component is exposed to said down-hole fluid environment in said down-hole applications; said surface layer is not degradable, dissolvable, and/or reactable in said down-hole fluid environment until said surface layer is exposed to said chemical trigger which thereafter causes said surface layer to controllably dissolve in said down-hole fluid environment;b. inserting said down-hole component into a well, said surface layer of said hierarchically-designed reactive component does not or substantially does not dissolve, degrade, and/or react when exposed to said down-hole fluid environment in said well;c. exposing said surface layer of said hierarchically-designed reactive component to said chemical trigger to cause said surface layer to degrade, dissolve, and/or react to thereby expose said core to said down-hole fluid environment and,d. causing said exposed core to degrade, dissolve, react, and/or fracture when exposed to said down-hole fluid environment, said degradation, dissolving, reacting, and/or fracturing of said core thereby causing said down-hole component to at least partially degrade, dissolve, react, and/or fracture.
Parent Case Info

The present invention is a continuation application of Serial No. U.S. application Ser. No. 16/110,550 filed Aug. 23, 2018, which in turn is a continuation of U.S. application Ser. No. 14/627,189 filed Feb. 20, 2015 (now U.S. Pat. No. 10,150,713 on Dec. 11, 2018), which in turn claims priority on U.S. Provisional Application Ser. No. 61/942,870 filed Feb. 21, 2014 and 62/054,597 filed Sep. 24, 2014, both of which are incorporated herein by reference.

US Referenced Citations (1064)
Number Name Date Kind
1468905 Herman Jul 1923 A
1558066 Veazey et al. Oct 1925 A
1880614 Wetherill et al. Oct 1932 A
2352993 Albertson Jul 1933 A
2011613 Brown et al. Aug 1935 A
2094578 Blumenthal et al. Oct 1937 A
2189697 Baker Feb 1940 A
2222233 Mize Nov 1940 A
2225143 Baker et al. Dec 1940 A
2238895 Gage Apr 1941 A
2261292 Salnikov Nov 1941 A
2294648 Ansel et al. Sep 1942 A
2301624 Holt Nov 1942 A
2394843 Cook et al. Feb 1946 A
2672199 McKenna Mar 1954 A
2753941 Hebard et al. Jul 1956 A
2754910 Derrick et al. Jul 1956 A
2933136 Ayers et al. Apr 1960 A
2983634 Budininkas et al. May 1961 A
3057405 Mallinger Oct 1962 A
3066391 Vordahl et al. Dec 1962 A
3106959 Huitt et al. Oct 1963 A
3142338 Brown Jul 1964 A
3152009 DeLong Oct 1964 A
3180728 Pryor et al. Apr 1965 A
3180778 Rinderspacher et al. Apr 1965 A
3196949 Thomas Jul 1965 A
3226314 Wellington et al. Dec 1965 A
3242988 McGuire, Jr. et al. Mar 1966 A
3295935 Pflumm et al. Jan 1967 A
3298440 Current Jan 1967 A
3316748 Lang et al. May 1967 A
3326291 Zandemer Jun 1967 A
3347714 Broverman et al. Oct 1967 A
3385696 Hitchcock et al. May 1968 A
3390724 Caldwell Jul 1968 A
3395758 Kelly et al. Aug 1968 A
3406101 Kilpatrick Oct 1968 A
3416918 Roberts Dec 1968 A
3434539 Merritt Mar 1969 A
3445148 Harris et al. May 1969 A
3445731 Saeki et al. May 1969 A
3465181 Colby et al. Sep 1969 A
3489218 Means Jan 1970 A
3513230 Rhees et al. May 1970 A
3600163 Badia et al. Aug 1971 A
3602305 Kisling Aug 1971 A
3637446 Elliott et al. Jan 1972 A
3645331 Maurer et al. Feb 1972 A
3660049 Benjamin May 1972 A
3765484 Hamby, Jr. et al. Oct 1973 A
3768563 Blount Oct 1973 A
3775823 Adolph et al. Dec 1973 A
3816080 Bomford et al. Jun 1974 A
3823045 Hielema Jul 1974 A
3878889 Seabourne Apr 1975 A
3894850 Kovalchuk et al. Jul 1975 A
3905147 Snipes et al. Sep 1975 A
3924677 Prenner et al. Dec 1975 A
3957483 Suzuki May 1976 A
4010583 Highberg Mar 1977 A
4039717 Titus Aug 1977 A
4050529 Tagirov et al. Sep 1977 A
4157732 Fonner Jun 1979 A
4248307 Silberman et al. Feb 1981 A
4264362 Sergev et al. Apr 1981 A
4284137 Taylor Aug 1981 A
4292377 Petersen et al. Sep 1981 A
4368788 Drake Jan 1983 A
4372384 Kinney Feb 1983 A
4373584 Silberman et al. Feb 1983 A
4373952 Parent Feb 1983 A
4374543 Richardson Feb 1983 A
4384616 Dellinger May 1983 A
4395440 Abe et al. Jul 1983 A
4399871 Adkins et al. Aug 1983 A
4407368 Erbstoesser Oct 1983 A
4422508 Rutledge, Jr. et al. Dec 1983 A
4450136 Dudek et al. May 1984 A
4452311 Speegle et al. Jun 1984 A
4475729 Costigan Oct 1984 A
4498543 Pye et al. Feb 1985 A
4499048 Hanejko Feb 1985 A
4499049 Hanejko Feb 1985 A
4524825 Fore Jun 1985 A
4526840 Jerabek Jul 1985 A
4534414 Pringle Aug 1985 A
4539175 Lichti et al. Sep 1985 A
4554986 Jones Nov 1985 A
4619699 Petkovic-Luton et al. Oct 1986 A
4640354 Boisson Feb 1987 A
4648901 Murray et al. Mar 1987 A
4655852 Rallis Apr 1987 A
4664962 DesMarais, Jr. May 1987 A
4668470 Gilman et al. May 1987 A
4673549 Ecer Jun 1987 A
4674572 Gallus Jun 1987 A
4678037 Smith Jul 1987 A
4681133 Weston Jul 1987 A
4688641 Knieriemen Aug 1987 A
4690796 Paliwal Sep 1987 A
4693863 Del Corso et al. Sep 1987 A
4703807 Weston Nov 1987 A
4706753 Ohkochi et al. Nov 1987 A
4708202 Sukup et al. Nov 1987 A
4708208 Halbardier Nov 1987 A
4709761 Setterberg, Jr. Dec 1987 A
4714116 Brunner Dec 1987 A
4716964 Erbstoesser et al. Jan 1988 A
4719971 Owens Jan 1988 A
4721159 Ohkochi et al. Jan 1988 A
4738599 Shilling Apr 1988 A
4741973 Condit et al. May 1988 A
4768588 Kupsa Sep 1988 A
4775598 Jaeckel Oct 1988 A
4784226 Wyatt Nov 1988 A
4805699 Halbardier Feb 1989 A
4817725 Jenkins Apr 1989 A
4834184 Streich et al. May 1989 A
H635 Johnson et al. Jun 1989 H
4853056 Hoffman Aug 1989 A
4869324 Holder Sep 1989 A
4869325 Halbardier Sep 1989 A
4875948 Vemnecker Oct 1989 A
4880059 Brandell et al. Nov 1989 A
4889187 Terrell et al. Dec 1989 A
4890675 Dew Jan 1990 A
4901794 Baugh et al. Feb 1990 A
4909320 Hebert et al. Mar 1990 A
4916029 Nagle et al. Apr 1990 A
4917966 Wilde et al. Apr 1990 A
4921664 Couper May 1990 A
4929415 Okazaki May 1990 A
4932474 Schroeder, Jr. et al. Jun 1990 A
4934459 Baugh et al. Jun 1990 A
4938309 Emdy Jul 1990 A
4938809 Das et al. Jul 1990 A
4944351 Eriksen et al. Jul 1990 A
4949788 Szarka et al. Aug 1990 A
4952902 Kawaguchi et al. Aug 1990 A
4975412 Okazaki et al. Dec 1990 A
4977958 Miller Dec 1990 A
4981177 Carmody et al. Jan 1991 A
4986361 Muuller et al. Jan 1991 A
4997622 Regazzoni et al. Mar 1991 A
5006044 Walker, Sr. et al. Apr 1991 A
5010955 Springer Apr 1991 A
5036921 Pittard et al. Aug 1991 A
5048611 Cochran Sep 1991 A
5049165 Tselesin Sep 1991 A
5061323 DeLuccia Oct 1991 A
5063775 Walker, Sr. et al. Nov 1991 A
5073207 Faure et al. Dec 1991 A
5074361 Brisco et al. Dec 1991 A
5076869 Bourell et al. Dec 1991 A
5084088 Okazaki Jan 1992 A
5087304 Chang et al. Feb 1992 A
5090480 Pittard et al. Feb 1992 A
5095988 Bode Mar 1992 A
5103911 Heijnen Apr 1992 A
5106702 Walker et al. Apr 1992 A
5117915 Mueller et al. Jun 1992 A
5143795 Das et al. Sep 1992 A
5161614 Wu et al. Nov 1992 A
5171734 Sanjurjo et al. Dec 1992 A
5178216 Giroux et al. Jan 1993 A
5181571 Mueller et al. Jan 1993 A
5183631 Kugimiya et al. Feb 1993 A
5188182 Echols, III et al. Feb 1993 A
5188183 Hopmann et al. Feb 1993 A
5204055 Sachs et al. Apr 1993 A
5222867 Walker, Sr. et al. Jun 1993 A
5226483 Williamson, Jr. Jul 1993 A
5228518 Wilson et al. Jul 1993 A
5234055 Cornette Aug 1993 A
5238646 Tarcy et al. Aug 1993 A
5240742 Johnson et al. Aug 1993 A
5252365 White Oct 1993 A
5253714 Davis et al. Oct 1993 A
5271468 Streich et al. Dec 1993 A
5273569 Gilman et al. Dec 1993 A
5282509 Schurr, III Feb 1994 A
5285798 Banerjee et al. Feb 1994 A
5292478 Scorey Mar 1994 A
5293940 Hromas et al. Mar 1994 A
5304260 Aikawa et al. Apr 1994 A
5304588 Boysen et al. Apr 1994 A
5309874 Willermet et al. May 1994 A
5310000 Arterbury et al. May 1994 A
5316598 Chang et al. May 1994 A
5318746 Lashmore et al. Jun 1994 A
5336466 Iba Aug 1994 A
5342576 Whitehead Aug 1994 A
5352522 Kugimiya et al. Oct 1994 A
5380473 Bogue et al. Jan 1995 A
5387380 Cima et al. Feb 1995 A
5392860 Ross Feb 1995 A
5394236 Murnick Feb 1995 A
5394941 Venditto et al. Mar 1995 A
5398754 Dinhoble Mar 1995 A
5407011 Layton Apr 1995 A
5409555 Fujita et al. Apr 1995 A
5411082 Kennedy May 1995 A
5417285 Van Buskirk et al. May 1995 A
5425424 Reinhardt et al. Jun 1995 A
5427177 Jordan, Jr. et al. Jun 1995 A
5435392 Kennedy Jul 1995 A
5439051 Kennedy et al. Aug 1995 A
5454430 Kennedy et al. Oct 1995 A
5456317 Hood, III et al. Oct 1995 A
5456327 Denton et al. Oct 1995 A
5464062 Blizzard, Jr. Nov 1995 A
5472048 Kennedy Dec 1995 A
5474131 Jordan, Jr. et al. Dec 1995 A
5476632 Shivanath et al. Dec 1995 A
5477923 Jordan, Jr. et al. Dec 1995 A
5479986 Gano et al. Jan 1996 A
5494538 Kirillov et al. Feb 1996 A
5506055 Dorfman et al. Apr 1996 A
5507439 Story Apr 1996 A
5511620 Baugh et al. Apr 1996 A
5524699 Cook Jun 1996 A
5526880 Jordan, Jr. et al. Jun 1996 A
5526881 Martin et al. Jun 1996 A
5529746 Knoss et al. Jun 1996 A
5531735 Thompson Jul 1996 A
5533573 Jordan, Jr. et al. Jul 1996 A
5536485 Kume et al. Jul 1996 A
5552110 Iba Sep 1996 A
5558153 Holcombe et al. Sep 1996 A
5601924 Beane et al. Feb 1997 A
5607017 Owens et al. Mar 1997 A
5623993 Van Buskirk et al. Apr 1997 A
5623994 Robinson Apr 1997 A
5641023 Ross et al. Jun 1997 A
5636691 Hendrickson et al. Jul 1997 A
5647444 Williams Jul 1997 A
5665289 Chung et al. Sep 1997 A
5677372 Yamamoto et al. Oct 1997 A
5685372 Gano Nov 1997 A
5701576 Fujita et al. Dec 1997 A
5707214 Schmidt Jan 1998 A
5709269 Head Jan 1998 A
5720344 Newman Feb 1998 A
5722033 Carden Feb 1998 A
5728195 Eastman et al. Mar 1998 A
5765639 Muth Jun 1998 A
5767562 Yamashita Jun 1998 A
5772735 Sehgal et al. Jun 1998 A
5782305 Hicks Jul 1998 A
5797454 Hipp Aug 1998 A
5820608 Luzio et al. Oct 1998 A
5826652 Tapp Oct 1998 A
5826661 Parker et al. Oct 1998 A
5829520 Johnson Nov 1998 A
5836396 Norman Nov 1998 A
5857521 Ross et al. Jan 1999 A
5881816 Wright Mar 1999 A
5896819 Turila et al. Apr 1999 A
5902424 Fujita et al. May 1999 A
5934372 Muth Aug 1999 A
5941309 Appleton Aug 1999 A
5960881 Allamon et al. Oct 1999 A
5964965 Schulz et al. Oct 1999 A
5894007 Yuan et al. Nov 1999 A
5980602 Carden Nov 1999 A
5985466 Atarashi et al. Nov 1999 A
5988287 Jordan, Jr. et al. Nov 1999 A
5990051 Ischy et al. Nov 1999 A
5992452 Nelson, II Nov 1999 A
5992520 Schultz et al. Nov 1999 A
6007314 Nelson, II Dec 1999 A
6024915 Kume et al. Feb 2000 A
6030637 Whitehead Feb 2000 A
6032735 Echols Mar 2000 A
6033622 Maruyama Mar 2000 A
6036777 Sachs Mar 2000 A
6040087 Kawakami Mar 2000 A
6047773 Zeltmann et al. Apr 2000 A
6050340 Scott Apr 2000 A
6069313 Kay May 2000 A
6076600 Vick, Jr. et al. Jun 2000 A
6079496 Hirth Jun 2000 A
6085837 Massinon et al. Jul 2000 A
6095247 Streich et al. Aug 2000 A
6119783 Parker et al. Sep 2000 A
6126898 Butler Oct 2000 A
6142237 Christmas et al. Nov 2000 A
6161622 Robb et al. Dec 2000 A
6167970 Stout et al. Jan 2001 B1
6170583 Boyce Jan 2001 B1
6171359 Levinski et al. Jan 2001 B1
6173779 Smith Jan 2001 B1
6176323 Weirich et al. Jan 2001 B1
6189616 Gano et al. Feb 2001 B1
6189618 Beeman et al. Feb 2001 B1
6213202 Read, Jr. Apr 2001 B1
6220349 Vargus et al. Apr 2001 B1
6220350 Brothers et al. Apr 2001 B1
6220357 Carmichael et al. Apr 2001 B1
6228904 Yadav et al. May 2001 B1
6230799 Slaughter et al. May 2001 B1
6237688 Burleson et al. May 2001 B1
6238280 Ritt et al. May 2001 B1
6241021 Bowling Jun 2001 B1
6248399 Hehmann Jun 2001 B1
6250392 Muth Jun 2001 B1
6261432 Huber et al. Jul 2001 B1
6265205 Hitchens et al. Jul 2001 B1
6273187 Voisin, Jr. et al. Aug 2001 B1
6276452 Davis et al. Aug 2001 B1
6276457 Moffatt et al. Aug 2001 B1
6279656 Sinclair et al. Aug 2001 B1
6287332 Bolz et al. Sep 2001 B1
6287445 Lashmore et al. Sep 2001 B1
6302205 Ryll Oct 2001 B1
6315041 Carlisle et al. Nov 2001 B1
6315050 Vaylnshteyn et al. Nov 2001 B2
6325148 Trahan et al. Dec 2001 B1
6328110 Joubert Dec 2001 B1
6341653 Fermaniuk et al. Jan 2002 B1
6341747 Schmidt et al. Jan 2002 B1
6349766 Bussear et al. Feb 2002 B1
6354372 Carisell et al. Mar 2002 B1
6354379 Miszewski et al. Mar 2002 B2
6371206 Mills Apr 2002 B1
6372346 Toth Apr 2002 B1
6382244 Vann May 2002 B2
6390195 Nguyen et al. May 2002 B1
6390200 Allamon et al. May 2002 B1
6394180 Berscheidt et al. May 2002 B1
6394185 Constien May 2002 B1
6395402 Lambert et al. May 2002 B1
6397950 Streich et al. Jun 2002 B1
6401547 Hatfield et al. Jun 2002 B1
6403210 Stuivinga et al. Jun 2002 B1
6408946 Marshall et al. Jun 2002 B1
6419023 George et al. Jul 2002 B1
6422314 Todd et al. Jul 2002 B1
6439313 Thomeer et al. Aug 2002 B1
6444316 Reddy et al. Sep 2002 B1
6446717 White et al. Sep 2002 B1
6457525 Scott Oct 2002 B1
6467546 Allamon et al. Oct 2002 B2
6470965 Winzer Oct 2002 B1
6491097 Oneal et al. Dec 2002 B1
6491116 Berscheidt et al. Dec 2002 B2
6513598 Moore et al. Feb 2003 B2
6513600 Ross Feb 2003 B2
6527051 Reddy et al. Mar 2003 B1
6540033 Sullivan et al. Apr 2003 B1
6543543 Muth Apr 2003 B2
6554071 Reddy et al. Apr 2003 B1
6561275 Glass et al. May 2003 B2
6581681 Zimmerman et al. Jun 2003 B1
6588507 Dusterhoft et al. Jul 2003 B2
6591915 Burris et al. Jul 2003 B2
6601648 Ebinger Aug 2003 B2
6601650 Sundararajan Aug 2003 B2
6609569 Howlett et al. Aug 2003 B2
6612826 Bauer et al. Sep 2003 B1
6613383 George et al. Sep 2003 B1
6619400 Brunet Sep 2003 B2
6630008 Meeks, III et al. Oct 2003 B1
6634428 Krauss et al. Oct 2003 B2
6662886 Russell Dec 2003 B2
6675889 Mullins et al. Jan 2004 B1
6699305 Myrick Mar 2004 B2
6712153 Turley et al. Mar 2004 B2
6712797 Southern, Jr. Mar 2004 B1
6713177 George et al. Mar 2004 B2
6715541 Pedersen et al. Apr 2004 B2
6737385 Todd et al. May 2004 B2
6779599 Mullins et al. Aug 2004 B2
6799638 Butterfield, Jr. Oct 2004 B2
6810960 Pia Nov 2004 B2
6817414 Lee Nov 2004 B2
6831044 Constien Dec 2004 B2
6883611 Smith et al. Apr 2005 B2
6887297 Winter et al. May 2005 B2
6896049 Moyes May 2005 B2
6896061 Hriscu et al. May 2005 B2
6899777 Vaidyanathan et al. May 2005 B2
6908516 Hehmann et al. Jun 2005 B2
6913827 George et al. Jul 2005 B2
6926086 Patterson et al. Aug 2005 B2
6932159 Hovem Aug 2005 B2
6939388 Angeliu Sep 2005 B2
6945331 Patel Sep 2005 B2
6951331 Haughom et al. Oct 2005 B2
6959759 Doane et al. Nov 2005 B2
6973970 Johnston et al. Dec 2005 B2
6973973 Howard et al. Dec 2005 B2
6983796 Bayne et al. Jan 2006 B2
6986390 Doane et al. Jan 2006 B2
7013989 Hammond et al. Mar 2006 B2
7013998 Ray et al. Mar 2006 B2
7017664 Walker et al. Mar 2006 B2
7017677 Keshavan et al. Mar 2006 B2
7021389 Bishop et al. Apr 2006 B2
7025146 King et al. Apr 2006 B2
7028778 Krywitsky Apr 2006 B2
7044230 Starr et al. May 2006 B2
7048812 Bettles et al. May 2006 B2
7049272 Sinclair et al. May 2006 B2
7051805 Doane et al. May 2006 B2
7059410 Bousche et al. Jun 2006 B2
7063748 Talton Jun 2006 B2
7090027 Williams Aug 2006 B1
7093664 Todd et al. Aug 2006 B2
7096945 Richards et al. Aug 2006 B2
7096946 Jasser et al. Aug 2006 B2
7097807 Meeks, III et al. Aug 2006 B1
7097906 Gardner Aug 2006 B2
7108080 Tessari et al. Sep 2006 B2
7111682 Blaisdell Sep 2006 B2
7128145 Mickey Oct 2006 B2
7141207 Jandeska, Jr. et al. Nov 2006 B2
7150326 Bishop et al. Dec 2006 B2
7163066 Lehr Jan 2007 B2
7165622 Hirth et al. Jan 2007 B2
7168494 Starr et al. Jan 2007 B2
7174963 Bertelsen Feb 2007 B2
7182135 Szarka Feb 2007 B2
7188559 Vecchio Mar 2007 B1
7210527 Walker et al. May 2007 B2
7210533 Starr et al. May 2007 B2
7217311 Hong et al. May 2007 B2
7234530 Gass Jun 2007 B2
7250188 Dodelet et al. Jul 2007 B2
7252162 Akinlade et al. Aug 2007 B2
7255172 Johnson Aug 2007 B2
7255178 Slup et al. Aug 2007 B2
7264060 Wills Sep 2007 B2
7267172 Hofman Sep 2007 B2
7267178 Krywitsky Sep 2007 B2
7270186 Johnson Sep 2007 B2
7287592 Surjaatmadja et al. Oct 2007 B2
7311152 Howard et al. Dec 2007 B2
7316274 Xu et al. Jan 2008 B2
7320365 Pia Jan 2008 B2
7322412 Badalamenti et al. Jan 2008 B2
7322417 Rytlewski et al. Jan 2008 B2
7325617 Murray Feb 2008 B2
7328750 Swor et al. Feb 2008 B2
7331388 Vilela et al. Feb 2008 B2
7337854 Horn et al. Mar 2008 B2
7346456 Le Bemadjiel Mar 2008 B2
7350582 McKeachnie et al. Apr 2008 B2
7353867 Carter et al. Apr 2008 B2
7353879 Todd et al. Apr 2008 B2
7360593 Constien Apr 2008 B2
7360597 Blaisdell Apr 2008 B2
7363970 Corre et al. Apr 2008 B2
7373978 Barry et al. May 2008 B2
7380600 Willberg et al. Jun 2008 B2
7384443 Mirchandani Jun 2008 B2
7387158 Murray et al. Jun 2008 B2
7387165 Lopez de Cardenas et al. Jun 2008 B2
7392841 Murray et al. Jul 2008 B2
7401648 Richard Jul 2008 B2
7416029 Telfer et al. Aug 2008 B2
7422058 O'Malley Sep 2008 B2
7426964 Lynde et al. Sep 2008 B2
7441596 Wood et al. Oct 2008 B2
7445049 Howard et al. Nov 2008 B2
7451815 Hailey, Jr. Nov 2008 B2
7451817 Reddy et al. Nov 2008 B2
7461699 Richard et al. Dec 2008 B2
7464752 Dale et al. Dec 2008 B2
7464764 Xu Dec 2008 B2
7472750 Walker et al. Jan 2009 B2
7478676 East, Jr. et al. Jan 2009 B2
7491444 Smith et al. Feb 2009 B2
7503390 Gomez Mar 2009 B2
7503392 King et al. Mar 2009 B2
7503399 Badalamenti et al. Mar 2009 B2
7509993 Turng et al. Mar 2009 B1
7510018 Williamson et al. Mar 2009 B2
7513311 Gramstad et al. Apr 2009 B2
7516791 Bryant et al. Apr 2009 B2
7520944 Johnson Apr 2009 B2
7527103 Huang et al. May 2009 B2
7531020 Woodfield et al. May 2009 B2
7531021 Woodfield et al. May 2009 B2
7537825 Wardle et al. May 2009 B1
7552777 Murray et al. Jun 2009 B2
7552779 Murray Jun 2009 B2
7559357 Clem Jul 2009 B2
7575062 East, Jr. Aug 2009 B2
7579087 Maloney et al. Aug 2009 B2
7591318 Tilghman Sep 2009 B2
7600572 Slup et al. Oct 2009 B2
7604049 Vaidya et al. Oct 2009 B2
7604055 Richard et al. Oct 2009 B2
7607476 Tom et al. Oct 2009 B2
7617871 Surjaatmadja et al. Nov 2009 B2
7635023 Goldberg et al. Dec 2009 B2
7640988 Phi et al. Jan 2010 B2
7647964 Akbar et al. Jan 2010 B2
7661480 Al-Anazi Feb 2010 B2
7661481 Todd et al. Feb 2010 B2
7665537 Patel et al. Feb 2010 B2
7686082 Marsh Mar 2010 B2
7690436 Turley et al. Apr 2010 B2
7699101 Fripp et al. Apr 2010 B2
7700038 Soran et al. Apr 2010 B2
7703511 Buyers et al. Apr 2010 B2
7708078 Stoesz May 2010 B2
7709421 Jones et al. May 2010 B2
7712541 Loretz et al. May 2010 B2
7723272 Crews et al. May 2010 B2
7726406 Xu Jun 2010 B2
7735578 Loehr et al. Jun 2010 B2
7743836 Cook et al. Jun 2010 B2
7752971 Loehr Jul 2010 B2
7757773 Rytlewski Jul 2010 B2
7762342 Richard et al. Jul 2010 B2
7770652 Barnett Aug 2010 B2
7771289 Palumbo et al. Aug 2010 B2
7775284 Richard et al. Aug 2010 B2
7775285 Surjaatmadja et al. Aug 2010 B2
7775286 Duphorne Aug 2010 B2
7784543 Johnson Aug 2010 B2
7793714 Johnson Sep 2010 B2
7793820 Hirano et al. Sep 2010 B2
7798225 Giroux et al. Sep 2010 B2
7798226 Themig Sep 2010 B2
7798236 McKeachnie et al. Sep 2010 B2
7806189 Frazier Oct 2010 B2
7806192 Foster et al. Oct 2010 B2
7810553 Cruickshank et al. Oct 2010 B2
7810567 Daniels et al. Oct 2010 B2
7819198 Birckhead et al. Oct 2010 B2
7828055 Willauer et al. Nov 2010 B2
7833944 Munoz et al. Nov 2010 B2
7849927 Herrera Dec 2010 B2
7851016 Arbab et al. Dec 2010 B2
7855168 Fuller et al. Dec 2010 B2
7861779 Vestavik Jan 2011 B2
7861781 D'Arcy Jan 2011 B2
7874365 East, Jr. et al. Jan 2011 B2
7878253 Stowe et al. Feb 2011 B2
7879367 Heublein et al. Feb 2011 B2
7896091 Williamson et al. Mar 2011 B2
7897063 Perry et al. Mar 2011 B1
7900696 Nish et al. Mar 2011 B1
7900703 Clark et al. Mar 2011 B2
7909096 Clark et al. Mar 2011 B2
7909104 Bjorgum Mar 2011 B2
7909110 Sharma et al. Mar 2011 B2
7909115 Grove et al. Mar 2011 B2
7913765 Crow et al. Mar 2011 B2
7918275 Clem Apr 2011 B2
7931093 Foster et al. Apr 2011 B2
7938191 Vaidya May 2011 B2
7946335 Bewlay et al. May 2011 B2
7946340 Surjattmadja et al. May 2011 B2
7958940 Jameson Jun 2011 B2
7963331 Surjattmadja et al. Jun 2011 B2
7963340 Gramstad et al. Jun 2011 B2
7963342 George Jun 2011 B2
7980300 Roberts et al. Jul 2011 B2
3002821 Stinson Aug 2011 A1
7987906 Troy Aug 2011 B1
7992763 Vecchio et al. Aug 2011 B2
7999987 Dellinger et al. Aug 2011 B2
3020619 Robertson et al. Sep 2011 A1
3020620 Daniels et al. Sep 2011 A1
3025104 Cooke, Jr. Sep 2011 A1
8028767 Radford et al. Oct 2011 B2
8033331 Themig Oct 2011 B2
8039422 Al-Zahrani Oct 2011 B1
8056628 Whitsitt et al. Nov 2011 B2
8056638 Clayton et al. Nov 2011 B2
8109340 Doane et al. Feb 2012 B2
8114148 Atanasoska et al. Feb 2012 B2
8119713 Dubois et al. Feb 2012 B2
8127856 Nish et al. Mar 2012 B1
8153052 Jackson et al. Apr 2012 B2
8163060 Imanishi et al. Apr 2012 B2
8167043 Willberg et al. May 2012 B2
8211247 Marya et al. Jul 2012 B2
8211248 Marya Jul 2012 B2
8211331 Jorgensen et al. Jul 2012 B2
8220554 Jordan et al. Jul 2012 B2
8226740 Chaumonnot et al. Jul 2012 B2
8230731 Dyer et al. Jul 2012 B2
8231947 Vaidya et al. Jul 2012 B2
8263178 Boulos et al. Sep 2012 B2
8267177 Vogel et al. Sep 2012 B1
8276670 Patel Oct 2012 B2
8277974 Kumar et al. Oct 2012 B2
8297364 Agrawal et al. Oct 2012 B2
8327931 Agrawal et al. Dec 2012 B2
8403037 Agrawal et al. Mar 2013 B2
8413727 Holmes Apr 2013 B2
8425651 Xu et al. Apr 2013 B2
8459347 Stout Jun 2013 B2
8485265 Marya et al. Jul 2013 B2
8490674 Stevens et al. Jul 2013 B2
8490689 McClinton et al. Jul 2013 B1
8528633 Agrawal et al. Sep 2013 B2
8535604 Baker et al. Sep 2013 B1
8573295 Johnson et al. Nov 2013 B2
8579023 Nish et al. Nov 2013 B1
8613789 Han et al. Dec 2013 B2
8631876 Xu et al. Jan 2014 B2
8663401 Marya et al. Mar 2014 B2
8695684 Chen et al. Apr 2014 B2
8695714 Xu Apr 2014 B2
8714268 Agrawal et al. May 2014 B2
8715339 Atanasoska et al. May 2014 B2
8723564 Kim et al. May 2014 B2
8734564 Kim et al. May 2014 B2
8734602 Li et al. May 2014 B2
8746342 Nish et al. Jun 2014 B1
8770261 Marya Jul 2014 B2
8776884 Xu Jul 2014 B2
8789610 Oxford Jul 2014 B2
8808423 Kim et al. Aug 2014 B2
8950504 Xu et al. Feb 2015 B2
8956660 Launag et al. Feb 2015 B2
8978734 Stevens Mar 2015 B2
8991485 Chenault et al. Mar 2015 B2
8998978 Wang Apr 2015 B2
9010416 Xu et al. Apr 2015 B2
9016363 Xu et al. Apr 2015 B2
9016384 Xu Apr 2015 B2
9022107 Agrawal et al. May 2015 B2
9027655 Xu May 2015 B2
9033041 Baihly et al. May 2015 B2
9033060 Xu et al. May 2015 B2
9044397 Choi et al. Jun 2015 B2
9057117 Harrison et al. Jun 2015 B2
9057242 Mazyar et al. Jun 2015 B2
9068428 Mazyar et al. Jun 2015 B2
9010424 Xu Jul 2015 B2
9079246 Xu et al. Jul 2015 B2
9080098 Xu et al. Jul 2015 B2
9080403 Xu et al. Jul 2015 B2
9080439 O'Malley Jul 2015 B2
9089408 Xu Jul 2015 B2
9090955 Xu et al. Jul 2015 B2
9090956 Xu Jul 2015 B2
9109429 Xu et al. Aug 2015 B2
9119906 Fomantschager et al. Sep 2015 B2
9127515 Xu et al. Sep 2015 B2
9163467 Gaudette et al. Oct 2015 B2
9187686 Crews Nov 2015 B2
9211586 Lavernia et al. Dec 2015 B1
9217319 Frazier et al. Dec 2015 B2
9227243 Xu Jan 2016 B2
9243475 Xu Jan 2016 B2
9260935 Murphree et al. Feb 2016 B2
9284803 Stone et al. Mar 2016 B2
9309733 Xu et al. Apr 2016 B2
9309744 Frazier Apr 2016 B2
9366106 Xu et al. Jun 2016 B2
9447482 Kim et al. Sep 2016 B2
9458692 Fripp et al. Oct 2016 B2
9500061 Frazier et al. Nov 2016 B2
9528343 Jordan et al. Dec 2016 B2
9587156 Crews Mar 2017 B2
9643250 Mazyar et al. May 2017 B2
9682425 Xu et al. Jun 2017 B2
9689227 Fripp et al. Jun 2017 B2
9689231 Fripp et al. Jun 2017 B2
9789663 Zhang et al. Oct 2017 B2
9790763 Fripp et al. Oct 2017 B2
9802250 Xu Oct 2017 B2
9803439 Xu et al. Oct 2017 B2
9833838 Mazyar et al. Dec 2017 B2
9835016 Zhang et al. Dec 2017 B2
9863201 Fripp et al. Jan 2018 B2
9925589 Xu Mar 2018 B2
9926763 Mazyar et al. Mar 2018 B2
9938451 Crews Apr 2018 B2
9970249 Zhang et al. May 2018 B2
10016810 Salinas et al. Jul 2018 B2
10059092 Welch et al. Aug 2018 B2
10059867 Crews Aug 2018 B2
10081853 Wilks et al. Sep 2018 B2
10082008 Robey et al. Sep 2018 B2
10092953 Mazyar et al. Oct 2018 B2
10119358 Walton et al. Nov 2018 B2
10119359 Frazier Nov 2018 B2
10125565 Fripp et al. Nov 2018 B2
10167691 Zhang et al. Jan 2019 B2
10202820 Xu et al. Feb 2019 B2
10221637 Xu et al. Mar 2019 B2
10221641 Zhang et al. Mar 2019 B2
10221642 Zhang et al. Mar 2019 B2
10221643 Zhang et al. Mar 2019 B2
10227841 Fripp et al. Mar 2019 B2
10253590 Xu et al. Apr 2019 B2
10266923 Wilks et al. Apr 2019 B2
10316601 Walton et al. Jun 2019 B2
10329643 Wilks et al. Jun 2019 B2
10335855 Welch et al. Jul 2019 B2
10337086 Wilks et al. Jul 2019 B2
10344568 Murphree et al. Jul 2019 B2
10364630 Xu et al. Jul 2019 B2
10364631 Xu et al. Jul 2019 B2
10364632 Xu et al. Jul 2019 B2
10450840 Xu Oct 2019 B2
10472909 Xu et al. Nov 2019 B2
10533392 Walton et al. Jan 2020 B2
10544652 Fripp et al. Jan 2020 B2
10597965 Allen Mar 2020 B2
10612659 Xu et al. Apr 2020 B2
10619438 Fripp et al. Apr 2020 B2
10619445 Murphree et al. Apr 2020 B2
10626695 Fripp et al. Apr 2020 B2
10633947 Fripp et al. Apr 2020 B2
10655411 Fripp et al. May 2020 B2
10669797 Johnson et al. Jun 2020 B2
10724321 Leonard et al. Jul 2020 B2
10737321 Xu Aug 2020 B2
10781658 Kumar et al. Sep 2020 B1
10807355 Welch et al. Oct 2020 B2
20020020527 Kilaas et al. Feb 2002 A1
20020047058 Verhoff et al. Apr 2002 A1
20020092654 Coronado et al. Jul 2002 A1
20020104616 De et al. Aug 2002 A1
20020108756 Harrall et al. Aug 2002 A1
20020121081 Cesaroni et al. Sep 2002 A1
20020139541 Sheffield et al. Oct 2002 A1
20020197181 Osawa et al. Dec 2002 A1
20030019639 Mackay Jan 2003 A1
20030060374 Cooke, Jr. Mar 2003 A1
20030104147 Bretschneider et al. Jun 2003 A1
20030111728 Thai et al. Jun 2003 A1
20030127013 Zavitsanos et al. Jul 2003 A1
20030141060 Hailey, Jr. et al. Jul 2003 A1
20030150614 Brown et al. Aug 2003 A1
20030155114 Pedersen et al. Aug 2003 A1
20030173005 Higashi Sep 2003 A1
20040005483 Lin Jan 2004 A1
20040055758 Brezinski et al. Mar 2004 A1
20040069502 Luke Apr 2004 A1
20040089449 Walton et al. May 2004 A1
20040094297 Malone et al. May 2004 A1
20040154806 Bode et al. Aug 2004 A1
20040159446 Haugen et al. Aug 2004 A1
20040216868 Owens, Sr. Nov 2004 A1
20040231845 Cooke, Jr. Nov 2004 A1
20040244968 Cook et al. Dec 2004 A1
20040256109 Johnson Dec 2004 A1
20040261993 Nguyen Dec 2004 A1
20040261994 Nguyen et al. Dec 2004 A1
20050064247 Sane et al. Mar 2005 A1
20050074612 Eklund et al. Apr 2005 A1
20050098313 Atkins et al. May 2005 A1
20050102255 Bultman May 2005 A1
20050106316 Rigney et al. May 2005 A1
20050161212 Leismer et al. Jul 2005 A1
20050165149 Chanak et al. Jul 2005 A1
20050194141 Sinclair et al. Sep 2005 A1
20050235757 De Jonge et al. Oct 2005 A1
20050241824 Burris, II et al. Nov 2005 A1
20050241825 Burris, II et al. Nov 2005 A1
20050268746 Abkowitz et al. Dec 2005 A1
20050269097 Towler Dec 2005 A1
20050275143 Toth Dec 2005 A1
20050279427 Park et al. Dec 2005 A1
20050279501 Surjaatmadja et al. Dec 2005 A1
20060012087 Matsuda et al. Jan 2006 A1
20060013350 Akers Jan 2006 A1
20060057479 Niimi et al. Mar 2006 A1
20060102871 Wang et al. May 2006 A1
20060108114 Johnson May 2006 A1
20060110615 Karim et al. May 2006 A1
20060113077 Willberg et al. Jun 2006 A1
20060116696 Odermatt et al. Jun 2006 A1
20060131031 McKeachnie Jun 2006 A1
20060131081 Mirchandani et al. Jun 2006 A1
20060144515 Tada et al. Jul 2006 A1
20060150770 Freim, III et al. Jul 2006 A1
20060153728 Schoenung et al. Jul 2006 A1
20060169453 Savery et al. Aug 2006 A1
20060175059 Sinclair et al. Aug 2006 A1
20060186602 Martin et al. Aug 2006 A1
20060207387 Soran et al. Sep 2006 A1
20060269437 Pandey Nov 2006 A1
20060278405 Turley Dec 2006 A1
20060283592 Sierra et al. Dec 2006 A1
20070017675 Hammami et al. Jan 2007 A1
20070134496 Katagiri et al. Jan 2007 A1
20070039161 Garcia Feb 2007 A1
20070044958 Rytlewski et al. Mar 2007 A1
20070044966 Davies et al. Mar 2007 A1
20070051521 Fike et al. Mar 2007 A1
20070053785 Hetz et al. Mar 2007 A1
20070054101 Sigalas et al. Mar 2007 A1
20070057415 Katagiri et al. Mar 2007 A1
20070062644 Nakamura et al. Mar 2007 A1
20070102199 Smith et al. May 2007 A1
20070107899 Werner et al. May 2007 A1
20070108060 Park May 2007 A1
20070131912 Simone et al. Jun 2007 A1
20070151009 Conrad, III et al. Jul 2007 A1
20070151769 Slutz et al. Jul 2007 A1
20070181224 Marya et al. Aug 2007 A1
20070187095 Walker et al. Aug 2007 A1
20070207182 Weber et al. Sep 2007 A1
20070221373 Murray Sep 2007 A1
20070227745 Roberts et al. Oct 2007 A1
20070259994 Tour et al. Nov 2007 A1
20070270942 Thomas Nov 2007 A1
20070284112 Magne et al. Dec 2007 A1
20070299510 Venkatraman et al. Dec 2007 A1
20080011473 Wood et al. Jan 2008 A1
20080020923 Debe et al. Jan 2008 A1
20080041500 Bronfin Feb 2008 A1
20080047707 Boney et al. Feb 2008 A1
20080060810 Nguyen et al. Mar 2008 A9
20080081866 Gong et al. Apr 2008 A1
20080093073 Bustos et al. Apr 2008 A1
20080105438 Jordan May 2008 A1
20080121436 Slay et al. May 2008 A1
20080127475 Griffo Jun 2008 A1
20080149325 Crawford Jun 2008 A1
20080149345 Marya et al. Jun 2008 A1
20080149351 Marya et al. Jun 2008 A1
20080169130 Norman et al. Jul 2008 A1
20080175744 Motegi Jul 2008 A1
20080179104 Zhang et al. Jul 2008 A1
20080196801 Zhao et al. Aug 2008 A1
20080202764 Clayton et al. Aug 2008 A1
20080202814 Lyons et al. Aug 2008 A1
20080210473 Zhang et al. Sep 2008 A1
20080216383 Pierick et al. Sep 2008 A1
20080220991 Slay et al. Sep 2008 A1
20080223587 Cherewyk Sep 2008 A1
20080236829 Lynde Oct 2008 A1
20080236842 Bhavsar et al. Oct 2008 A1
20080248205 Blanchet et al. Oct 2008 A1
20080248413 Ishii et al. Oct 2008 A1
20080264205 Zeng et al. Oct 2008 A1
20080264594 Lohmueller et al. Oct 2008 A1
20080277980 Koda et al. Nov 2008 A1
20080282924 Saenger et al. Nov 2008 A1
20080296024 Huang et al. Dec 2008 A1
20080302538 Hofman Dec 2008 A1
20080314581 Brown Dec 2008 A1
20080314588 Langlais et al. Dec 2008 A1
20090038858 Griffo et al. Feb 2009 A1
20090044946 Shasteen et al. Feb 2009 A1
20090044955 King et al. Feb 2009 A1
20090050334 Marya et al. Feb 2009 A1
20090056934 Xu Mar 2009 A1
20090065216 Frazier Mar 2009 A1
20090068051 Gross Mar 2009 A1
20090074603 Chan et al. Mar 2009 A1
20090084600 Severance Apr 2009 A1
20090090440 Kellett Apr 2009 A1
20090107684 Cooke, Jr. Apr 2009 A1
20090114381 Stroobants May 2009 A1
20090116992 Lee May 2009 A1
20090126436 Fly et al. May 2009 A1
20090151949 Marya et al. Jun 2009 A1
20090152009 Slay et al. Jun 2009 A1
20090155616 Thamida Jun 2009 A1
20090159289 Avant et al. Jun 2009 A1
20090194745 Tanaka Aug 2009 A1
20090205841 Kluge et al. Aug 2009 A1
20090211770 Nutley et al. Aug 2009 A1
20090226340 Marya Sep 2009 A1
20090226704 Kauppinen et al. Sep 2009 A1
20090242202 Rispler et al. Oct 2009 A1
20090242208 Bolding Oct 2009 A1
20090255667 Clem et al. Oct 2009 A1
20090255684 Bolding Oct 2009 A1
20090255686 Richard et al. Oct 2009 A1
20090260817 Gambier et al. Oct 2009 A1
20090266548 Olsen et al. Oct 2009 A1
20090272544 Giroux et al. Nov 2009 A1
20090283270 Langeslag Nov 2009 A1
20090293672 Mirchandani et al. Dec 2009 A1
20090301730 Gweily Dec 2009 A1
20090308588 Howell et al. Dec 2009 A1
20090317556 Macary Dec 2009 A1
20090317622 Huang et al. Dec 2009 A1
20100003536 Smith et al. Jan 2010 A1
20100012385 Drivdahl et al. Jan 2010 A1
20100015002 Barrera et al. Jan 2010 A1
20100015469 Romanowski Jan 2010 A1
20100025255 Su et al. Feb 2010 A1
20100038076 Spray et al. Feb 2010 A1
20100038595 Imholt et al. Feb 2010 A1
20100040180 Kim et al. Feb 2010 A1
20100044041 Smith et al. Feb 2010 A1
20100051278 Mytopher et al. Mar 2010 A1
20100055492 Baroum et al. Mar 2010 A1
20100089583 Xu et al. Apr 2010 A1
20100116495 Spray May 2010 A1
20100119405 Okamoto et al. May 2010 A1
20100139930 Patel et al. Jun 2010 A1
20100161031 Papirov et al. Jun 2010 A1
20100200230 East, Jr. et al. Aug 2010 A1
20100236793 Bjorgum Sep 2010 A1
20100236794 Duan et al. Sep 2010 A1
20100243254 Murphy et al. Sep 2010 A1
20100252273 Duphorne Oct 2010 A1
20100252280 Swor et al. Oct 2010 A1
20100270031 Patel Oct 2010 A1
20100276136 Evans et al. Nov 2010 A1
20100276159 Mailand et al. Nov 2010 A1
20100282338 Gerrard et al. Nov 2010 A1
20100282469 Richard et al. Nov 2010 A1
20100297432 Sherman et al. Nov 2010 A1
20100304178 Dirscherl Dec 2010 A1
20100304182 Facchini et al. Dec 2010 A1
20100314105 Rose Dec 2010 A1
20100314127 Swor et al. Dec 2010 A1
20100319427 Lohbeck et al. Dec 2010 A1
20100326650 Tran et al. Dec 2010 A1
20110005773 Dusterhoft et al. Jan 2011 A1
20110036592 Fay Feb 2011 A1
20110048743 Stafford et al. Mar 2011 A1
20110052805 Bordere et al. Mar 2011 A1
20110067872 Agrawal Mar 2011 A1
20110067889 Marya et al. Mar 2011 A1
20110091660 Dirscherl Apr 2011 A1
20110094406 Marya et al. Apr 2011 A1
20110094737 Chen Apr 2011 A1
20110135530 Xu et al. Jun 2011 A1
20110135805 Doucet et al. Jun 2011 A1
20110139465 Tibbles et al. Jun 2011 A1
20110147014 Chen et al. Jun 2011 A1
20110186306 Marya et al. Aug 2011 A1
20110192613 Garcia et al. Aug 2011 A1
20110214881 Newton et al. Sep 2011 A1
20110221137 Obi et al. Sep 2011 A1
20110236249 Kim et al. Sep 2011 A1
20110247833 Todd et al. Oct 2011 A1
20110253387 Ervin Oct 2011 A1
20110259610 Shkurti et al. Oct 2011 A1
20110277987 Frazier Nov 2011 A1
20110277989 Frazier Nov 2011 A1
20110277996 Cullick et al. Nov 2011 A1
20110284232 Huang Nov 2011 A1
20110284240 Chen et al. Nov 2011 A1
20110284243 Frazier Nov 2011 A1
20110300403 Vecchio et al. Dec 2011 A1
20110314881 Hatcher et al. Dec 2011 A1
20120046732 Sillekens et al. Feb 2012 A1
20120067426 Soni et al. Mar 2012 A1
20120080189 Marya et al. Apr 2012 A1
20120090839 Rudic Apr 2012 A1
20120097384 Valencia et al. Apr 2012 A1
20120103135 Xu et al. May 2012 A1
20120125642 Chenault May 2012 A1
20120130470 Agnew et al. May 2012 A1
20120145378 Frazier Jun 2012 A1
20120145389 Fitzpatrick, Jr. Jun 2012 A1
20120156087 Kawabata Jun 2012 A1
20120168152 Casciaro Jul 2012 A1
20120177905 Seals et al. Jul 2012 A1
20120190593 Soane et al. Jul 2012 A1
20120205120 Howell Aug 2012 A1
20120205872 Reinhardt et al. Aug 2012 A1
20120211239 Kritzler et al. Aug 2012 A1
20120234546 Xu Sep 2012 A1
20120234547 O'Malley et al. Sep 2012 A1
20120247765 Agrawal et al. Oct 2012 A1
20120267101 Cooke, Jr. Oct 2012 A1
20120269673 Koo et al. Oct 2012 A1
20120273229 Xu Nov 2012 A1
20120318513 Mazyar et al. Dec 2012 A1
20130000985 Agrawal et al. Jan 2013 A1
20130008671 Booth Jan 2013 A1
20130017610 Roberts et al. Jan 2013 A1
20130022816 Smith et al. Jan 2013 A1
20130029886 Mazyar et al. Jan 2013 A1
20130032357 Mazyar et al. Feb 2013 A1
20130043041 McCoy et al. Feb 2013 A1
20130047785 Xu Feb 2013 A1
20130052472 Xu Feb 2013 A1
20130056215 Crews Mar 2013 A1
20130062049 Ren Mar 2013 A1
20130068411 Forde et al. Mar 2013 A1
20130068461 Maerz et al. Mar 2013 A1
20130084643 Commarieu et al. Apr 2013 A1
20130105159 Alvarez et al. May 2013 A1
20130112429 Crews May 2013 A1
20130126190 Mazyar et al. May 2013 A1
20130133897 Bailhly et al. May 2013 A1
20130144290 Schiffl et al. Jun 2013 A1
20130146144 Joseph et al. Jun 2013 A1
20130160992 Agrawal et al. Jun 2013 A1
20130167502 Wilson et al. Jul 2013 A1
20130168257 Mazyar et al. Jul 2013 A1
20130186626 Aitken et al. Jul 2013 A1
20130199800 Kellner et al. Aug 2013 A1
20130209308 Mazyar et al. Aug 2013 A1
20130220496 Inoue et al. Aug 2013 A1
20130240200 Frazier Sep 2013 A1
20130240203 Frazier Sep 2013 A1
20130261735 Pacetti et al. Oct 2013 A1
20130277044 King et al. Oct 2013 A1
20130310961 Velez Nov 2013 A1
20130048289 Mazyar Dec 2013 A1
20130319668 Tschetter et al. Dec 2013 A1
20130327540 Hamid et al. Dec 2013 A1
20130333899 Xu Dec 2013 A1
20140018489 Johnson Jan 2014 A1
20140020712 Benson Jan 2014 A1
20140027128 Johnson Jan 2014 A1
20140060834 Quintero Mar 2014 A1
20140093417 Liu Apr 2014 A1
20140110112 Jordan, Jr. Apr 2014 A1
20140116711 Tang May 2014 A1
20140124216 Fripp et al. May 2014 A1
20140154341 Manuel et al. Jun 2014 A1
20140186207 Bae et al. Jul 2014 A1
20140190705 Fripp Jul 2014 A1
20140196889 Jordan et al. Jul 2014 A1
20140202284 Kim et al. Jul 2014 A1
20140202708 Jacob et al. Jul 2014 A1
20140219861 Han Aug 2014 A1
20140224477 Wiese et al. Aug 2014 A1
20140236284 Stinson Aug 2014 A1
20140271333 Kim et al. Sep 2014 A1
20140286810 Marya Sep 2014 A1
20140305627 Manke Oct 2014 A1
20140311731 Smith Oct 2014 A1
20140311752 Streich et al. Oct 2014 A1
20140360728 Tashiro et al. Dec 2014 A1
20140374086 Agrawal et al. Dec 2014 A1
20150060085 Xu Mar 2015 A1
20150065401 Xu et al. Mar 2015 A1
20150102179 McHenry et al. Apr 2015 A1
20150184485 Xu et al. Jul 2015 A1
20150240337 Sherman et al. Aug 2015 A1
20150247376 Tolman Sep 2015 A1
20150299838 Doud Oct 2015 A1
20150354311 Okura et al. Dec 2015 A1
20160024619 Wilkes et al. Jan 2016 A1
20160128849 Yan et al. May 2016 A1
20160201425 Walton Jul 2016 A1
20160201427 Fripp Jul 2016 A1
20160201435 Fripp et al. Jul 2016 A1
20160209391 Zhang et al. Jul 2016 A1
20160230494 Fripp et al. Aug 2016 A1
20160251934 Walton et al. Sep 2016 A1
20160258242 Hayter et al. Sep 2016 A1
20160265091 Walton et al. Sep 2016 A1
20160272882 Stray et al. Sep 2016 A1
20160279709 Xu et al. Sep 2016 A1
20170050159 Xu et al. Feb 2017 A1
20170266923 Guest et al. Sep 2017 A1
20170356266 Arackakudiyil et al. Dec 2017 A1
20180010217 Wilks et al. Jan 2018 A1
20180023359 Xu Jan 2018 A1
20180178289 Xu et al. Jun 2018 A1
20180187510 Xu et al. Jul 2018 A1
20180216431 Walton et al. Aug 2018 A1
20180274317 Hall Sep 2018 A1
20190054523 Wolf et al. Feb 2019 A1
20190093450 Walton et al. Mar 2019 A1
20190203563 Gano et al. Jul 2019 A1
20190249510 Deng et al. Aug 2019 A1
Foreign Referenced Citations (128)
Number Date Country
2783241 Jun 2011 CA
2783346 Jun 2011 CA
2886988 Oct 2015 CA
1076968 Oct 1993 CN
1079234 Dec 1993 CN
1255879 Jun 2000 CN
1668545 Sep 2005 CN
1882759 Dec 2006 CN
101050417 Oct 2007 CN
101351523 Jan 2009 CN
101381829 Mar 2009 CN
101392345 Mar 2009 CN
101454074 Jun 2009 CN
101457321 Jun 2009 CN
101605963 Dec 2009 CN
101720378 Jun 2010 CN
102517489 Jun 2012 CN
102796928 Nov 2012 CN
103343271 Oct 2013 CN
103602865 Feb 2014 CN
103898384 Jul 2014 CN
104152775 Nov 2014 CN
104480354 Apr 2015 CN
201532089 Apr 2015 CN
10577976 Jul 2016 CN
106086559 Nov 2016 CN
200600343 Jun 2006 EA
200870227 Feb 2009 EA
0033625 Aug 1981 EP
0400574 May 1990 EP
0470599 Feb 1998 EP
1006258 Jan 2000 EP
1174385 Jan 2002 EP
1412175 Apr 2004 EP
1493517 Jan 2005 EP
1798301 Jun 2007 EP
1857570 Nov 2007 EP
2088217 Aug 2009 EP
912956 Dec 1962 GB
1046330 Oct 1966 GB
1280833 Jul 1972 GB
1357065 Jun 1974 GB
2095288 Sep 1982 GB
2529062 Feb 2016 GB
H10147830 Jun 1998 JP
2000073152 Mar 2000 JP
2000185725 Jul 2000 JP
2002053902 Feb 2002 JP
2004154837 Jun 2004 JP
2004225084 Aug 2004 JP
2004225765 Aug 2004 JP
2005076052 Mar 2005 JP
2008266734 Nov 2008 JP
2008280565 Nov 2008 JP
2009144207 Jul 2009 JP
2010502840 Jan 2010 JP
2012197491 Oct 2012 JP
2013019030 Jan 2013 JP
2014043601 Mar 2014 JP
2014174013 Sep 2014 JP
20130023707 Mar 2013 KR
2373375 Jul 2006 RU
9111587 Aug 1881 WO
1990002655 Mar 1990 WO
9200961 Jan 1992 WO
1992013978 Aug 1992 WO
9857347 Dec 1998 WO
9909227 Feb 1999 WO
9947726 Sep 1999 WO
2001001087 Jan 2001 WO
2004001087 Dec 2003 WO
2004073889 Sep 2004 WO
2005065281 Jul 2005 WO
2007044635 Apr 2007 WO
2007095376 Aug 2007 WO
2008017156 Feb 2008 WO
2008034042 Mar 2008 WO
2008057045 May 2008 WO
2008079485 Jul 2008 WO
2008079777 Jul 2008 WO
2008142129 Nov 2008 WO
2009055354 Apr 2009 WO
2009079745 Jul 2009 WO
2010012184 Feb 2010 WO
2010038016 Apr 2010 WO
2010083826 Jul 2010 WO
2010110505 Sep 2010 WO
2011071902 Jun 2011 WO
2011071907 Jun 2011 WO
2011071910 Jun 2011 WO
2011130063 Oct 2011 WO
2012015567 Feb 2012 WO
2012047370 Apr 2012 WO
2012071449 May 2012 WO
2012091984 Jul 2012 WO
2012149007 Nov 2012 WO
2012164236 Dec 2012 WO
2012174101 Dec 2012 WO
2012175665 Dec 2012 WO
2013019410 Feb 2013 WO
2013019421 Feb 2013 WO
2013053057 Apr 2013 WO
2013078031 May 2013 WO
2013109287 Jul 2013 WO
2013122712 Aug 2013 WO
2013154634 Oct 2013 WO
20131544634 Oct 2013 WO
2014100141 Jun 2014 WO
2014113058 Jul 2014 WO
2014121384 Aug 2014 WO
2014210283 Dec 2014 WO
2015127177 Aug 2015 WO
2015142862 Sep 2015 WO
2015161171 Oct 2015 WO
2015171126 Nov 2015 WO
2015171585 Nov 2015 WO
2016032490 Mar 2016 WO
2016032493 Mar 2016 WO
2016032619 Mar 2016 WO
2016032620 Mar 2016 WO
2016032621 Mar 2016 WO
2016032758 Mar 2016 WO
2016032761 Mar 2016 WO
2016036371 Mar 2016 WO
2016085798 Jun 2016 WO
2016165041 Oct 2016 WO
2020018110 Jan 2020 WO
2020109770 Jun 2020 WO
Non-Patent Literature Citations (87)
Entry
State Intellectual Property Office of People's Republic of China, First Office Action for corresponding China Patent Application No. 201580020103.7 (dated Aug. 11, 2017).
Terves LLC, Response to First Office Action for China Patent Application No. 201580020103.7 (Official Translation dated Jul. 2, 2020).
Medlin, Dana, “Expert Report of Dana J. Medlin, Phd, PE, FASM in the Matter of Terves LLC v. Yueyang Aerospace New Materials Co., Ltd., et al. ”, US District Court for the Northern District of Ohio, Eastern Division, Case No. 1:19-cv-1661 (Jul. 27, 2021.
Medlin, Dana,“Expert Rebuttal Report of Dana J. Medlin, Phd, PE, FASM”, US District Court for the Northern District of Ohio, Eastern Division, Case No. 1:19-cv-1661 (Aug. 27, 2021).
Yueyang Aerospace New Materials Co, Ltd, et al, “The Ecometal Defendant's Final Invalidity, Non-Infringement, and Unenforceability Contentions”, US District Court for the Northern District of Ohio, Eastern Division, Case No. 1:19-cv-1661 (Jul. 6, 2020 ).
Ralston and Birbilis, “Effect of Grain Size on Corrosion: A Review”, Corrosion, vol. 66, No. 7, pp. 075005-01 thru 13 (2010).
Sherman, Andrew, “Declaration of Andrew J. Sherman Under 37 CFR § 1.132” in Ex Parte Reexamination of U.S. Appl. No. 90/014,795 (Jan. 14, 2021).
Swanger, Lee A., “Declaration of Lee A. Swanger, PhD, PE Under 37 CFR § 1.132” in Ex Parte Reexamination of U.S. Appl. No. 90/014,795 (Jan. 14, 2021).
Saravanan et al., “Fabrication and characterization of pure magnesium-30 vol SiCP particle composite”, Material Science and Eng., vol. 276, pp. 108-116 (2000).
Song et al., Texture evolution and mechanical properties of AZ31B magnesium alloy sheets processed by repeated unidirectional bending, Journal of Alloys and Compounds, vol. 489, pp. 475-481 (2010).
Blawert et al., “Magnesium secondary alloys: Alloy design for magnesium alloys with improved tolerance limits against impurities”, Corrosion Science, vol. 52, No. 7, pp. 2452-2468 (Jul. 1, 2010).
Wang et al., “Effect of Ni on microstructures and mechanical properties of AZ1 02 magnesium alloys” Zhuzao Foundry, Shenyang Zhuzao Yanjiusuo, vol. 62, No. 1, pp. 315-318 (Jan. 1, 2013).
Kim et al., “Effect of aluminum on the corrosions characteristics of Mg—4Ni—xAl alloys”, Corrosion, vol. 59, No. 3, pp. 228-237 (Jan. 1, 2003).
Unsworth et al., “A new magnesium alloy system”, Light Metal Age, vol. 37, No. 7-8., pp. 29-32 (Jan. 1, 1979).
Geng et al., “Enhanced age-hardening response of Mg—Zn alloys via Co additions”, Scripta Materialia, vol. 64, No. 6, pp. 506-509 (Mar. 1, 2011).
Zhu et al., “Microstructure and mechanical properties of Mg6ZnCuO.6Zr (wt.%) alloys”, Journal of Alloys and Compounds, vol. 509, No. 8, pp. 3526-3531 (Dec. 22, 2010).
International Search Authority, International Search Report and Written Opinion for PCT/GB2015/052169 (dated Feb. 17, 2016).
Search and Examination Report for GB 1413327.6 (dated Jan. 21, 2015).
Magnesium Elektron Test Report (Mar. 8, 2005).
New England Fishery Management Counsel, “Fishery Management Plan for American Lobster Amendment 3” (Jul. 1989).
Emly, E.F., “Principles of Magnesium Technology” Pergamon Press, Oxford (1966).
Shaw, “Corrosion Resistance of Magnesium Alloys”, ASM Handbook, vol. 13A, pp. 692-696 (2003).
Hanawalt et al., “Corrosion studies of magnesium and its alloys”, Metals Technology, Technical Paper 1353 (1941).
The American Foundry Society, Magnesium alloys, casting source directory 8208, available at www.afsinc.org/files/magnes.pdf.
Rokhlin, “Magnesium alloys containing rare earth metals structure and properties”, Advances in Metallic Alloys, vol. 3, Taylor & Francis (2003).
Ghali, “Corrosion Resistance of Aluminum and Magnesium Alloys” pp. 382-389, Wiley Publishing (2010).
Kim et al., “High Mechanical Strengths of Mg—Ni—Y and MG—Cu Amorphous Alloys with Significant Supercooled Liquid Region”, Materials Transactions, vol. 31, No. 11, pp. 929-934 (1990).
Tekumalla et al., “Mehcanical Properties of Magnesium-Rare Earth Alloy Systems”, Metals, vol. 5, pp. 1-39 (2014).
Hassan et al., “Development of high strength magnesium based composites using elemental nickel particulates as reinforcement”, Journal of Materials Science, vol. 37, pp. 2467-2474 (2002).
Metals Handbook, Desk Edition, edited by J.R. Davis, published by ASM International, pp. 559-574 (1998).
National Physical Laboratory, “Bimetallic Corrosion” Crown (C) p. 1-14 (2000).
Shaw, “Corrosion Resistance of Magnesium Alloys”, ASM Handbook, vol. 13A, pp. 602-606 (2003).
Ye et al., “Review of recent studies in magnesium matrix composites”, Journal of Material Sciences, vol. 39, pp. 6153-6171 (2004).
Hassan et al., “Development of a novel magnesium-copper based composite with improved mechanical properties”, Materials Research Bulletin, vol. 37, pp. 377-389 (2002).
Ye et al., “Microstructure and tensile properties of Ti6A14V/AM60B magnesium matrix composite”, Journal of Alloys and Composites, vol. 402, 00. 162-169 (2005).
Kumar et al., “Mechanical and Tribological Behavior of Particulars Reinforced Aluminum metal Matrix Composite”, Journal of Minerals & Materials Characterization and Engineering, vol. 10, pp. 59-91 (2011).
Majumdar, “Micromechanics of Discontinuously Reinforced MMCs”, Engineering Mechanics and Analysis of Metal-Matrix Composites, vol. 21, pp. 395-406 (2001).
Hemanth, “Fracture Behavior of Cryogenically solidifed aluminum-alloy reinforced with Nano-ZrO2 Metal Matrix Composites (CNMMCs)”, Journal of Chemical Engineering and Materials Science, vol. 2(8), pp. 110-121 (Aug. 2011).
Ashby, “Teach Yourself Phase Diagrams and Phase Transformations”, Cambridge, 5th Edition, pp: unknown (Mar. 2009).
Callister, Materials Science and Engineering an Introduction:, 6th Edition, New York, pp: unknown (2003).
Hanson et al. Constitution of Binary Alloys:, McGraw-Hill Book Co. Inc., pp: unknown (1958).
MSE 2090: Introduction to Materials Science, Chapter 9, pp: unknown (date unknown).
Metals Handbook, “Metallography, Structures and Phase Diagrams”, Aluminum-Magnesium, American Society for Metals, 8th Edition, vol. 8, pp: unknown (1973).
Metals Handbook, “Metallography, Structures and Phase Diagrams”, Magnesium-Nickel, American Society for Metals, 8th Edition, vol. 8, pp: unknown (1973).
Principles and Prevention of Corrosion, “Volts versus saturated calomel reference electrobe”, D.A. Jones, p. 170 (1996).
Medlin, “Mass Balance”, handwritten notes (Nov. 2020).
Metals Handbook, “Metallography, Structures and Phase Diagrams”, Aluminum-Iron, American Society for Metals, 8th Edition, vol. 8, p. 260 (1973).
Metals Handbook, “Metallography, Structures and Phase Diagrams”, Aluminum-Nickel, American Society for Metals, 8th Edition, vol. 8, p. 261 (1973).
Metals Handbook, “Metallography, Structures and Phase Diagrams”, Aluminum-Copper, American Society for Metals, 8th Edition, vol. 8, p. 259 (1973).
Metals Handbook, “Metallography, Structures and Phase Diagrams”, Silver-Aluminum, American Society for Metals, 8th Edition, vol. 8, p. 252 (1973).
Medlin, Declaration of Dona J. Medlin Ph D., P.E., FASM Under 37 CFR Section 1.68 in Support of Petition for Inter Partes Review of U.S. Pat. No. 9,903,010 (Sep. 2020).
Li, Qiang, “Translation Declaration and Translation of China Patent Publication No. 103343271” (Jun. 2020).
Ho et al., The mechanical behavior of magnesium alloy AZ91 reinforced with fine copper particulates:, Materials Science and Engineering A369, pp. 302-308 (2004).
Trojanova et al., “Mechanical and fracture properties of an AZ91 Magnesium alloy reinforced by Si and SiC particles”, Composites Science and Technology, vol. 69, pp. 2256-2264 (2009).
Lin et al., “Formation of Magnesium Metal Matrix Composites Al2O3p/AZ91D and Their Mechanical Properties After Heat Treatment” Acta Metallurgica Slovaca, vol. 16, pp. 237-245 (2010).
United States District Court/Northern District of Ohio/Eastern Division, Supplemental Declaration of Dana J. Medlin, Ph D. in Support of Opposition to Terves LLC'S Motion for Preliminary Injunction in related Case 1:19-CV-1611 (filedOct. 15, 2020).
United States District Court/Northern District of Ohio/Eastern Division, Declaration of Andrew Sherman in Support of Terves' Preliminary Injunction Motion in related Case 1:19-CV-1611 (filed May 1, 2020).
Sigworth et al. “Grain Refinement of Aluminum Castings Alloys” American Foundry Society; Paper 07-67; pp. 5-7 (2007).
Momentive, “Titanium Diborid Powder” condensed product brochure; retrieved from https /www.momentive.com/WorkArea/DownloadAsset.aspx?id+27489.; p. 1 (2012).
Durbin, “Modeling Dissolution in Aluminum Alloys” Dissertation for Georgia Institute of Technology; retrieved from https://smartech;gatech/edu/bitstream/handle/1853/6873/durbin_tracie_L_200505_phd.pdf> (2005).
Pegeut et al.., “Influence of cold working on the pitting corrosion resistance of stainless steel” Corrosion Science, vol. 49, pp. 1933-1948 (2007).
Elemental Charts from chemicalelements.com; retrieved Jul. 27, 2017.
Song et al., “Corrosion Mechanisms of Magnesium Alloys” Advanced Engg Materials, vol. 1, No. 1 (1999).
Zhou et al., “Tensile Mechanical Properties and Strengthening Mechanism of Hybrid Carbon Nanotubes . . . ” Journal of Nanomaterials, 2012; 2012:851862 (doi: 10 1155/2012/851862) Figs. 6 and 7.
Trojanova et al., “Mechanical and Acoustic Properties of Magnesium Alloys . . . ” Light Metal Alloys Application, Chapter 8, Published Jun. 11, 2014 (doi: 10.5772/57454) p. 163, para. [0008], [0014-0015]; [0041-0043].
AZoNano “Silicon Carbide Nanoparticles-Properties, Applications” http://www.amazon.com/articles.aspx?ArticleD=3396) p. 2, Physical Properties, Thermal Properties (May 9, 2013).
AZoM “Magnesium AZ91D-F Alloy” http://www.amazon.com/articles.aspx?ArticleD=8670) p. 1, Chemical Composition; p. 2 Physical Properties (Jul. 31, 2013.
Elasser et al., “Silicon Carbide Benefits and Advantages . . . ” Proceedings of the IEEE, 2002; 906(6):969-986 (doi: 10.1109/JPROC.2002.1021562) p. 970, Table 1.
Lan et al., “Microstructure and Microhardness of SiC Nanoparticles . . . ” Materials Science and Engineering A; 386:284-290 (2004).
Casati et al., “Metal Matrix Composites Reinforced by Nanoparticles”, vol. 4:65-83 (2014).
United States District Court/Northern District of Ohio/Eastern Division, Memorandum Opinion and Order in related Case 1:19-CV-1611 (issued Mar. 29, 2021).
United States District Court/Northern District of Ohio/Eastern Division, Second Rebuttal Rule 26 Report of Lee A. Swanger, Ph.D., P.E. in related Case 1:19-CV-1611 (filed Nov. 24, 2020).
U.S. Patent and Trademark Office, Declaration of Dana J. Medlin in Support of Request for Ex Parte Reexamination of U.S. Pat. No. 10,329,653 (filed Jul. 6, 2021).
Shimizu et al., “Multi-walled carbon nanotube-reinforced magnesium alloy composites”, Scripta Materialia, vol. 58, pp. 267-270 (2008).
Zhan et al., “Single-wall carbon nanotubes as attractive toughening agents in alumina-based nanocomposites”, Mature Materials, vol. 2, pp. 38-42 (Jan. 2003).
Curtin et al., “CNT-reinforced ceramics and metals”, Materials Today, vol. 7, pp. 44-49 (2004).
Pardo et al., “Corrosion behavior of magnesium/aluminum alloys in 3.5 wt.% NaCI”, Corrosion Science, vol. 50, pp. 823-834 (2008).
Song et L., “Influence of microstructure on the corrosion of diecast AZ91D”, Corrosion Science, vol. 41, pp. 249-273 (1999).
Watarai, “Trend of Research and Development for Magnesium Alloys—Reducing the Weight of Structural Materials in Motor Vehicles”, Science & Technology Trends, Quarterly Review, No. 18, pp. 84-97 (Jan. 2006).
Saravanan et al., “Mechanically Alloyed Carbon Nanotubes (CNT) Reinforced Nanocrystalline AA 4032: Synthesis and Characterization”, Journal of Minerals & Materials Characterization & Engineering, vol. 9, No. 11, pp. 1027-1035 (2010).
Tsipas et al., “Effect of high energy ball milling on titanium-hydroxyapatite powders”, Powder Metallurgy, vol. 46, No. 1 pp. 73-77 (2003).
Xie et al., “TEM Observation of Interfaces between Particles in Al—Mg Powder Compacts Prepared by Pulse Electric Current Sintering”, Materials Transactions, vol. 43, No. 9, pp. 2177-2180 (2002).
Elsayed et al., “Effect of Consolidation and Extrusion Temperatures on Tensile Properties of Hot Extruded ZK61 Magnesium Alloy Gas Atomized Powders via Spark Plasma Sintering”, Tranasctions of JWRI, vol. 38, No. 2, pp. 31.
Shigematsu et al., “Surface treatment of AZ91D magnesium alloy by aluminum diffusion coating”, Journal of Materials Science Letters, vol. 19, pp. 473-475 (2000).
Spencer et al., “Fluidized Bed Polymer Particle ALD Process for Producing HDPE/Alumina Nanocomposites”, 12th International Conference on Fluidization, vol. RP4 (2007).
Maisano, “Cryomilling of Aluminum-Based and Magnesium-Based Metal Powders”, Thesis, Virginia Tech (Jan. 2006).
Walters et al., “A Study of Jets from Unsintered-Powder Metal Lined Nonprecision Small-Caliber Shaped Charges”, Army Research Laboratory, Aberdeen Proving Group, MC 21005-5066 (Feb. 2001).
Related Publications (1)
Number Date Country
20210101849 A1 Apr 2021 US
Provisional Applications (2)
Number Date Country
61942870 Feb 2014 US
62054597 Sep 2014 US
Continuations (2)
Number Date Country